电学参数对胶体中工业纯钛微弧氧化膜特性的影响

陈根余 吴汉华 李乐 常鸿 唐元广

引用本文:
Citation:

电学参数对胶体中工业纯钛微弧氧化膜特性的影响

陈根余, 吴汉华, 李乐, 常鸿, 唐元广

Effect of electrical parameters on characteristics of microarc oxidation coatings of commercially pure titanium in colloid

Chen Gen-Yu, Wu Han-Hua, Li Yue, Chang Hong, Tang Yuan-Guang
PDF
导出引用
  • 利用自制多功能微弧氧化(MAO)电源对处在胶体中的工业纯钛表面进行了MAO处理,比较系统地研究了电压脉冲的峰值(U)和占空比(d)对膜层的生长特性、微观结构、相结构和处理后试样耐腐蚀性能的影响.结果表明,随着U的增加或d的加大,膜厚几乎呈线性增加,膜表面微孔尺寸和粗糙度逐渐增大,微孔密度逐渐减小.膜层主要由致密层组成,除U=450 V, d=10%时制备试样的膜层中含有少量锐钛矿相TiO2外,其他试样
    The effects of the pulse voltage amplitude (U) and duty cycle (d) on the growth characteristics, microstructure, phase component and corrosion resistance of the coating formed by microarc oxidation (MAO) on commercially pure titanium substrates in colloid have been systematically studied. The results show that, with the increase of U or d, the coating thickness increases almost linearly, the pore size and the roughness of the surface increases gradually, while the pore density decreases. The coatings almost entirely consist of dense layer, and they are completely composed of rutile TiO2 except the one formed at the duty cycle of 10% (U=450 V), which contains a small amount of anatase TiO2 The corrosion resistance test in sulfuric acid solution (30%) shows that the corrosion resistance of the samples is closely related to U and d, with the increase of U or d, the corrosion resistance of the samples increases gradually.
    • 基金项目: 国家基础科学人才培养基金(批准号: J0730311)资助的课题.
    [1]

    [1]Yerokhin A L, Nie X, Leyland A, Matthews A, Dowey S J 1999 Surf. Coat. Tech. 122 73

    [2]

    [2]Wu H H, Wang J B, Long B Y, Lü X Y, Long B H, Jin Z S, Bai Y Z, Bi D M 2005 Acta Phys. Sin. 54 5743(in Chinese)[吴汉华、汪剑波、龙北玉、吕宪义、龙北红、金曾孙、白亦真、毕冬梅 2005 物理学报 54 5743]

    [3]

    [3]Wei D Q, Zhou Y, Wang Y M, Jia D C 2007 Appl. Surf. Sci. 253 5045

    [4]

    [4]Wang J B, Wu H H, Li Q J, Li Z K, Gu G R, Lü X Y, Zheng W T, Jin Z S 2005 Chin.Phys. 14 2598

    [5]

    [5]Wu H H, Long B H, Long B Y, Tang Y G, Chang H, Bai Y Z 2007 Acta Phys. Sin. 56 6537 (in Chinese)[吴汉华、龙北红、龙北玉、唐元广、常鸿、白亦真 2007 物理学报 56 6537]

    [6]

    [6]Wang Y M, Jia D C, Guo L X, Lei T Q, Jiang B L 2005 Mater. Chem. Phys. 90 128

    [7]

    [7]Jin F Y, Chua P K, Wang K, Zhao J, Huang A P, Tong H H 2008 Mat. Sci.Eng. A 476 78

    [8]

    [8]Wei D Q, Zhou Y, Jia D C, Wang Y M 2007 Mater.Chem.Phys. 104 177

    [9]

    [9]Liu J, Xiong D S, Shen C J 2006 Electroplating&Finishing 12 0041 (in Chinese)[刘君、熊党生、沈承金 2006 电镀与涂饰 12 0041]

    [10]

    ]Zhang R H, Shan D Y, Chen R S, Han E H 2007 T. Nonferr. Metal. Soc. 10 1577 (in Chinese)[张荣发、单大勇、陈荣石、韩恩厚 2007 中国有色金属学报 10 1577]

    [11]

    ]Wang Y M, Jiang B L, Lei T Q, Guo L X, Cao Y P 2003 J. Inorg. Mater. 6 1325 (in Chinese)[王亚明、蒋百灵、雷廷权、郭立新、曹跃平 2003 无机材料学报 6 1325]

    [12]

    ]Wu H H, Long B H, Lu X Y, Wang J B, Jin Z S 2005 Acta Phys. Sin. 54 1697 (in Chinese)[吴汉华、龙北红、吕宪义、汪剑波、金曾孙 2005 物理学报 54 1697]

  • [1]

    [1]Yerokhin A L, Nie X, Leyland A, Matthews A, Dowey S J 1999 Surf. Coat. Tech. 122 73

    [2]

    [2]Wu H H, Wang J B, Long B Y, Lü X Y, Long B H, Jin Z S, Bai Y Z, Bi D M 2005 Acta Phys. Sin. 54 5743(in Chinese)[吴汉华、汪剑波、龙北玉、吕宪义、龙北红、金曾孙、白亦真、毕冬梅 2005 物理学报 54 5743]

    [3]

    [3]Wei D Q, Zhou Y, Wang Y M, Jia D C 2007 Appl. Surf. Sci. 253 5045

    [4]

    [4]Wang J B, Wu H H, Li Q J, Li Z K, Gu G R, Lü X Y, Zheng W T, Jin Z S 2005 Chin.Phys. 14 2598

    [5]

    [5]Wu H H, Long B H, Long B Y, Tang Y G, Chang H, Bai Y Z 2007 Acta Phys. Sin. 56 6537 (in Chinese)[吴汉华、龙北红、龙北玉、唐元广、常鸿、白亦真 2007 物理学报 56 6537]

    [6]

    [6]Wang Y M, Jia D C, Guo L X, Lei T Q, Jiang B L 2005 Mater. Chem. Phys. 90 128

    [7]

    [7]Jin F Y, Chua P K, Wang K, Zhao J, Huang A P, Tong H H 2008 Mat. Sci.Eng. A 476 78

    [8]

    [8]Wei D Q, Zhou Y, Jia D C, Wang Y M 2007 Mater.Chem.Phys. 104 177

    [9]

    [9]Liu J, Xiong D S, Shen C J 2006 Electroplating&Finishing 12 0041 (in Chinese)[刘君、熊党生、沈承金 2006 电镀与涂饰 12 0041]

    [10]

    ]Zhang R H, Shan D Y, Chen R S, Han E H 2007 T. Nonferr. Metal. Soc. 10 1577 (in Chinese)[张荣发、单大勇、陈荣石、韩恩厚 2007 中国有色金属学报 10 1577]

    [11]

    ]Wang Y M, Jiang B L, Lei T Q, Guo L X, Cao Y P 2003 J. Inorg. Mater. 6 1325 (in Chinese)[王亚明、蒋百灵、雷廷权、郭立新、曹跃平 2003 无机材料学报 6 1325]

    [12]

    ]Wu H H, Long B H, Lu X Y, Wang J B, Jin Z S 2005 Acta Phys. Sin. 54 1697 (in Chinese)[吴汉华、龙北红、吕宪义、汪剑波、金曾孙 2005 物理学报 54 1697]

  • [1] 丁智松, 高巍, 魏敬鹏, 金耀华, 赵晨, 杨巍. TaC微粒对Ti-6Al-4V合金微弧氧化层结构和性能的影响. 物理学报, 2022, 71(2): 028102. doi: 10.7498/aps.71.20210835
    [2] 丁智松, 高巍, 魏敬鹏, 金耀华, 赵晨, 杨巍. TaC 微粒对 Ti-6Al-4V 合金微弧氧化层结构和性能的影响. 物理学报, 2021, (): . doi: 10.7498/aps.70.20210835
    [3] 刘心卓, 王华光. 椭球胶体在圆球胶体体系中扩散行为的实验研究. 物理学报, 2020, 69(23): 238201. doi: 10.7498/aps.69.20201301
    [4] 贝帮坤, 王华光, 张泽新. 有限尺寸胶体体系的二维结晶. 物理学报, 2019, 68(10): 106401. doi: 10.7498/aps.68.20190304
    [5] 陈科. 胶体在非晶研究中的应用. 物理学报, 2017, 66(17): 178201. doi: 10.7498/aps.66.178201
    [6] 王理林, 王志军, 林鑫, 王锦程, 黄卫东. 冷却速率对温敏聚N-异丙基丙烯酰胺胶体结晶过程的影响. 物理学报, 2016, 65(10): 106403. doi: 10.7498/aps.65.106403
    [7] 马红孺. 胶体排空相互作用理论与计算. 物理学报, 2016, 65(18): 184701. doi: 10.7498/aps.65.184701
    [8] 张天辉, 曹镜声, 梁颖, 刘向阳. 胶体在基础物理研究中的应用. 物理学报, 2016, 65(17): 176401. doi: 10.7498/aps.65.176401
    [9] 吴赛, 李伟斌, 石峰, 蒋世春, 蓝鼎, 王育人. 受限胶体液滴蒸发过程中胶体颗粒沉积过程观察. 物理学报, 2015, 64(9): 096101. doi: 10.7498/aps.64.096101
    [10] 山磊, 田煜, 孟永钢, 张向军. 分散介质和温度对纳米二氧化硅胶体剪切增稠行为的影响. 物理学报, 2015, 64(6): 068301. doi: 10.7498/aps.64.068301
    [11] 于松楠, 吴汉华, 陈根余, 袁鑫, 李乐. Al(OH)3溶胶浓度对TC4钛合金微弧氧化膜特性的影响. 物理学报, 2011, 60(2): 028104. doi: 10.7498/aps.60.028104
    [12] 张欣盟, 田修波, 巩春志, 杨士勤. 约束阴极微弧氧化放电特性研究. 物理学报, 2010, 59(8): 5613-5619. doi: 10.7498/aps.59.5613
    [13] 黄立新, 高海峡, 肖长明. 胶体中排空作用的耦合效应. 物理学报, 2009, 58(8): 5864-5870. doi: 10.7498/aps.58.5864
    [14] 刘忍肖, 陈胜利, 董鹏. 旋涂法快速制备双层二元胶体微球有序薄膜. 物理学报, 2009, 58(4): 2820-2828. doi: 10.7498/aps.58.2820
    [15] 唐元广, 吴汉华, 常鸿, 陈根余, 桑勇, 白亦真. 阴极电压脉冲占空比对钛合金微弧氧化膜特性的影响. 物理学报, 2009, 58(7): 4840-4845. doi: 10.7498/aps.58.4840
    [16] 李春树, 肖长明. 带电胶体系统中的排空作用. 物理学报, 2007, 56(4): 2434-2441. doi: 10.7498/aps.56.2434
    [17] 吴汉华, 龙北红, 龙北玉, 唐元广, 常 鸿, 白亦真. 钛合金微弧氧化过程中电学参量的特性研究. 物理学报, 2007, 56(11): 6537-6542. doi: 10.7498/aps.56.6537
    [18] 刘 蕾, 徐升华, 刘 捷, 段 俐, 孙祉伟, 刘忍肖, 董 鹏. 带电胶体粒子结晶过程的实验研究. 物理学报, 2006, 55(11): 6168-6174. doi: 10.7498/aps.55.6168
    [19] 吴汉华, 龙北红, 吕宪义, 汪剑波, 金曾孙. 铝合金微弧氧化过程中电学参量的特性研究. 物理学报, 2005, 54(4): 1697-1701. doi: 10.7498/aps.54.1697
    [20] 吴汉华, 汪剑波, 龙北玉, 吕宪义, 龙北红, 金曾孙, 白亦真, 毕冬梅. 电流密度对铝合金微弧氧化膜物理化学特性的影响. 物理学报, 2005, 54(12): 5743-5749. doi: 10.7498/aps.54.5743
计量
  • 文章访问数:  7378
  • PDF下载量:  1979
  • 被引次数: 0
出版历程
  • 收稿日期:  2009-06-02
  • 修回日期:  2009-07-14
  • 刊出日期:  2010-03-15

/

返回文章
返回