激光钝化对熔石英修复后损伤性能影响的实验研究

李熙斌 袁晓东 贺少勃 吕海兵 王海军 向霞 郑万国

引用本文:
Citation:

激光钝化对熔石英修复后损伤性能影响的实验研究

李熙斌, 袁晓东, 贺少勃, 吕海兵, 王海军, 向霞, 郑万国

Influence of laser passivation on fused silica damage after CO2 laser mitigation

Li Xi-Bin, Yuan Xiao-Dong, He Shao-Bo, Lü Hai-Bing, Wang Hai-Jun, Xiang Xia, Zheng Wan-Guo
PDF
导出引用
  • 采用10.6 m 的CO2激光, 对单次激光脉冲辐照修复熔石英存在的烧蚀采用大光斑钝化去除. 经过辐照修复的区域置于前表面测试初始损伤阈值, 结果表明调制造成的损伤得到了一定程度的抑制; 辐照区域置于后表面修复后熔石英的初始损伤阈值超过了基底的初始损伤阈值. 实验观察到了应力分布外扩, 同时明显减弱. 对损伤增长的测试说明, 经过激光熔融辐照后的损伤点, 当应力释放以后, 损伤扩展初期表现出指数增长趋势, 后期随着辐照次数的增加, 损伤增长不再明显, 并且趋于恒定值.
    A 10.6 m CO2 big size laser beam is used to passivate the ablation deposit on surface of damage site which is repaired with single laser pulse. When the irradiated region is placed on front surface, modulation by 355 nm UV ns laser pulse is inhibited effectively; when the irradiated region is situated on rear surface, the initial damage threshold exceeds the substrate initial damage threshold. Second repair makes the thermal stress distribution enlarged obviously and the thermal stress magnitude weakened. The damage growth examination shows that once thermal stress is released, the initial phase damage growth exhibits an exponential tendency and as shoot number increases the damage size approaches to a constant value.
      通信作者: 李熙斌, lixibin2003@126.com
    • 基金项目: 国家高技术研究发展计划(863计划) (批准号:2008AA8040508) 和国防预研基金(批准号:426020606)资助的课题.
      Corresponding author: Li Xi-Bin, lixibin2003@126.com
    • Funds: Project supported by the National High Technology Research and Development Program of China (Grant No.2008AA8040508) and the National Defense Pre-Research Foundation of China (Grant No.406020606).
    [1]

    Temple P A,Milam D,Lowdermilk W H 1979 Natl.Bur.Stand.(U.S.) Spec.Publ.568 229

    [2]

    Wang F R,Huang J,Liu H J,Zhou X D,Jiang X D,Wu W D,Zheng W G 2010 Acta Phys.Sin.59 5122 (in Chinese) [王凤蕊,黄进,刘红婕,周信达,蒋晓东,吴卫东,郑万国 2010 物理学报 59 5122]

    [3]

    Hua J R,Zu X T,Li L,Xiang X,Chen M,Jiang X D,Yuan X D,Zheng W G 2010 Acta Phys.Sin.59 2519 (in Chinese) [花金荣,祖小涛,李莉,向霞,陈猛,蒋晓东,袁晓东,郑万国 2010 \物理学报 59 2519]

    [4]

    Mendez E,Nowak K M,Baker H J,Villarreal F J,Hall D R 2006 Opt.Express 45 5358

    [5]

    Palmier S,Gallais L,Commandré M,Cormont P,Courchinoux R,Lamaignère L,Rullier J L,Legros P 2008 Appl.Surface Science 255 5532

    [6]

    Feit M D,Rubenchik A M 2003 Proc.SPIE 4932 91

    [7]

    Feit M D,Rubenchik A M,Boley C D,Rotter M 2004 Proc.SPIE 5273 145

    [8]

    Bass I L,Guss G M,Hackel R P 2005 Proc.SPIE 59910C

    [9]

    Bass I L,Draggoo V G,Guss G M,Hackel R P,Norton M A,2006 Proc.SPIE 62612A

    [10]

    Li X B,L¨u H B,Xiang X,Wang H J,Chen M,Wang C C,Yuan X D,Zheng W G 2010 High Power Laser Part.Beams 22 2209 (in Chinese) [李熙斌,吕海兵,向霞,王海军,陈猛,王成程,袁晓东,郑万国\ 2010 强激光与粒子束 22 2209]

    [11]

    Huang J,Zhao S N,Wang H J,Lü H B,Ye L,Jiang X D,Yuan X D,Zheng W G 2009 Chinese Journal of Lasers 36 1282 (in Chinese)[黄进,赵松楠,王海军,吕海兵,叶琳,蒋晓东,袁晓东,郑万国\ 2009 中国激光 36 1282]

    [12]

    Laurent G,Philippe C,Jean-Luc R 2009 Opt.Express 17 23488

    [13]

    Li X B,Wang H J,Yuan X D,He S B,Xiang X,L¨u H B,Zheng WG,2011 Chinese Journal of Lasers 38 0903002 (in Chinese) [李熙斌,王海军,袁晓东,贺少勃,向霞,吕海兵,郑万国 2011 \中国激光 38 0903002]

    [14]

    Liu H J,Huang J,Wang F R,Zhou X D,Jiang X D,WuWD 2010 Acta Phys.Sin.59 1308 (in Chinese) [刘红婕,黄进,王凤蕊,周信达,蒋晓东,吴卫东 2010 物理学报 59 1308]

  • [1]

    Temple P A,Milam D,Lowdermilk W H 1979 Natl.Bur.Stand.(U.S.) Spec.Publ.568 229

    [2]

    Wang F R,Huang J,Liu H J,Zhou X D,Jiang X D,Wu W D,Zheng W G 2010 Acta Phys.Sin.59 5122 (in Chinese) [王凤蕊,黄进,刘红婕,周信达,蒋晓东,吴卫东,郑万国 2010 物理学报 59 5122]

    [3]

    Hua J R,Zu X T,Li L,Xiang X,Chen M,Jiang X D,Yuan X D,Zheng W G 2010 Acta Phys.Sin.59 2519 (in Chinese) [花金荣,祖小涛,李莉,向霞,陈猛,蒋晓东,袁晓东,郑万国 2010 \物理学报 59 2519]

    [4]

    Mendez E,Nowak K M,Baker H J,Villarreal F J,Hall D R 2006 Opt.Express 45 5358

    [5]

    Palmier S,Gallais L,Commandré M,Cormont P,Courchinoux R,Lamaignère L,Rullier J L,Legros P 2008 Appl.Surface Science 255 5532

    [6]

    Feit M D,Rubenchik A M 2003 Proc.SPIE 4932 91

    [7]

    Feit M D,Rubenchik A M,Boley C D,Rotter M 2004 Proc.SPIE 5273 145

    [8]

    Bass I L,Guss G M,Hackel R P 2005 Proc.SPIE 59910C

    [9]

    Bass I L,Draggoo V G,Guss G M,Hackel R P,Norton M A,2006 Proc.SPIE 62612A

    [10]

    Li X B,L¨u H B,Xiang X,Wang H J,Chen M,Wang C C,Yuan X D,Zheng W G 2010 High Power Laser Part.Beams 22 2209 (in Chinese) [李熙斌,吕海兵,向霞,王海军,陈猛,王成程,袁晓东,郑万国\ 2010 强激光与粒子束 22 2209]

    [11]

    Huang J,Zhao S N,Wang H J,Lü H B,Ye L,Jiang X D,Yuan X D,Zheng W G 2009 Chinese Journal of Lasers 36 1282 (in Chinese)[黄进,赵松楠,王海军,吕海兵,叶琳,蒋晓东,袁晓东,郑万国\ 2009 中国激光 36 1282]

    [12]

    Laurent G,Philippe C,Jean-Luc R 2009 Opt.Express 17 23488

    [13]

    Li X B,Wang H J,Yuan X D,He S B,Xiang X,L¨u H B,Zheng WG,2011 Chinese Journal of Lasers 38 0903002 (in Chinese) [李熙斌,王海军,袁晓东,贺少勃,向霞,吕海兵,郑万国 2011 \中国激光 38 0903002]

    [14]

    Liu H J,Huang J,Wang F R,Zhou X D,Jiang X D,WuWD 2010 Acta Phys.Sin.59 1308 (in Chinese) [刘红婕,黄进,王凤蕊,周信达,蒋晓东,吴卫东 2010 物理学报 59 1308]

  • [1] 李奋飞, 周晓燕, 张魁宝, 石兆华, 陈进湛, 叶鑫, 吴卫东, 李波. 中子辐照对掺镱光纤材料光学特性的影响. 物理学报, 2021, 70(19): 190201. doi: 10.7498/aps.70.20210083
    [2] 刘娅丽, 戚磊, 郑梦珂, 张蓉竹. 划痕缺陷对熔融石英光诱导损伤特性的影响分析. 物理学报, 2021, 70(13): 134203. doi: 10.7498/aps.70.20202174
    [3] 蒋勇, 袁晓东, 王海军, 廖威, 刘春明, 向霞, 邱荣, 周强, 高翔, 杨永佳, 郑万国, 祖小涛, 苗心向. 退火对熔石英表面损伤修复点损伤增长的影响. 物理学报, 2016, 65(4): 044209. doi: 10.7498/aps.65.044209
    [4] 韩伟, 冯斌, 郑奎兴, 朱启华, 郑万国, 巩马理. 高功率激光装置熔石英紫外损伤增长研究. 物理学报, 2016, 65(24): 246102. doi: 10.7498/aps.65.246102
    [5] 林圆圆, 姜有恩, 韦辉, 范薇, 李学春. 基于飞秒激光微加工的介质膜损伤修复研究. 物理学报, 2015, 64(15): 154207. doi: 10.7498/aps.64.154207
    [6] 蒋勇, 贺少勃, 袁晓东, 王海军, 廖威, 吕海兵, 刘春明, 向霞, 邱荣, 杨永佳, 郑万国, 祖小涛. CO2激光光栅式扫描修复熔石英表面缺陷的实验研究与数值模拟. 物理学报, 2014, 63(6): 068105. doi: 10.7498/aps.63.068105
    [7] 张明兰, 杨瑞霞, 李卓昕, 曹兴忠, 王宝义, 王晓晖. GaN厚膜中的质子辐照诱生缺陷研究. 物理学报, 2013, 62(11): 117103. doi: 10.7498/aps.62.117103
    [8] 卢喜瑞, 崔春龙, 张东, 陈梦君, 杨岩凯. 锆英石的抗γ射线辐照能力和Rietveld结构精修. 物理学报, 2011, 60(7): 078901. doi: 10.7498/aps.60.078901
    [9] 肖志强, 李蕾蕾, 张波, 徐静, 陈正才. 基于SOI技术的单层多晶EEPROM和SONOS EEPROM抗总剂量辐照特性研究. 物理学报, 2011, 60(2): 028502. doi: 10.7498/aps.60.028502
    [10] 江微微, 范林勇, 赵瑞峰, 卫延, 裴丽, 简水生. 基于双芯光纤耦合器的梳状滤波器及其CO2激光调节. 物理学报, 2011, 60(4): 044214. doi: 10.7498/aps.60.044214
    [11] 李蕾蕾, 于宗光, 肖志强, 周昕杰. SOI SONOS EEPROM 总剂量辐照阈值退化机理研究. 物理学报, 2011, 60(9): 098502. doi: 10.7498/aps.60.098502
    [12] 喻军, 周朋, 赵衡煜, 吴锋, 夏海平, 苏良碧, 徐军. γ射线辐照诱导Bi:α-BaB2O4单晶近红外宽带发光的研究. 物理学报, 2010, 59(5): 3538-3541. doi: 10.7498/aps.59.3538
    [13] 黄进, 蒋晓东, 刘红婕, 吕海兵, 王海军, 袁晓东, 郑万国. 真空环境中紫外脉冲激光对熔石英抗损伤能力的影响. 物理学报, 2010, 59(7): 4677-4681. doi: 10.7498/aps.59.4677
    [14] 王文鹏, 许周速, 徐军, 陈钢. 封离式He-N2-CO2激光器横模特性的测量与分析. 物理学报, 2009, 58(8): 5423-5428. doi: 10.7498/aps.58.5423
    [15] 朱涛, 宋韵, 饶云江, 朱永. CO2激光写入旋转折变型长周期光纤光栅的制作及理论分析. 物理学报, 2009, 58(7): 4738-4745. doi: 10.7498/aps.58.4738
    [16] 彭绍泉, 杜 磊, 庄奕琪, 包军林, 何 亮, 陈伟华. 基于辐照前1/f噪声的金属-氧化物-半导体场效应晶体管辐照退化模型. 物理学报, 2008, 57(8): 5205-5211. doi: 10.7498/aps.57.5205
    [17] 赵兴海, 高 杨, 徐美健, 段文涛, 於海武. 纳秒激光诱导石英光纤端面损伤特性研究. 物理学报, 2008, 57(8): 5027-5034. doi: 10.7498/aps.57.5027
    [18] 朱 涛, 饶云江, 莫秋菊, 王久玲. 高频CO2激光脉冲写入超长周期光纤光栅特性研究. 物理学报, 2007, 56(9): 5287-5292. doi: 10.7498/aps.56.5287
    [19] 张可言. 金属材料在中强度激光辐照下的相变速度研究. 物理学报, 2004, 53(6): 1815-1819. doi: 10.7498/aps.53.1815
    [20] 程 成. 优化封离型CO2激光工作气体的动力学机理研究. 物理学报, 2003, 52(12): 3068-3074. doi: 10.7498/aps.52.3068
计量
  • 文章访问数:  5998
  • PDF下载量:  561
  • 被引次数: 0
出版历程
  • 收稿日期:  2011-05-26
  • 修回日期:  2011-07-01
  • 刊出日期:  2012-03-05

/

返回文章
返回