Synthesis of nanoparticles in SiO2 by implantation of Cu and Zn ions and their thermal stability in oxygen atmoshphere

Xu Rong Jia Guang-Yi Liu Chang-Long

Citation:

Synthesis of nanoparticles in SiO2 by implantation of Cu and Zn ions and their thermal stability in oxygen atmoshphere

Xu Rong, Jia Guang-Yi, Liu Chang-Long
PDF
Get Citation

(PLEASE TRANSLATE TO ENGLISH

BY GOOGLE TRANSLATE IF NEEDED.)

  • Cu nanoparticles (NPs) embedded in silica were synthesized by implantation of 45 keV Cu ions at a fluence of 1.01017 cm-2, and then subjected to post irradiation with 50 keV Zn ions at fluences of 0.51017 cm-2 and 1.01017 cm-2, respectively. Zn post ion implantation induced modifications in structures, optical absorption properties of Cu NPs as well as their thermal stability in oxygen ambient have been investigated in detail. Results clearly show that Cu-Zn alloy NPs could be formed in the Cu pre-implanted silica followed by Zn ion irradiation at a fluence of 0.51017 cm-2, which causes an unique surface plasmon resonance (SPR) absorption peak at about 516 nm. Subsequent annealing in oxygen atmosphere results in the decomposition of Cu-Zn alloy NPs, at 450 ℃, and thus, ZnO and Cu NPs appear in the substrate. Further increase of annealing temperature to 550 ℃ could transform all the Zn and Cu into ZnO and CuO. Moreover, results also demonstrate that introduction of Zn into SiO2 substrate could effectively suppress the oxidation of Cu NPs, meanwhile, the existence of Cu could promote thermal diffusion of Zn towards substrate surface, which enhances the oxidation of Zn. The underlying mechanism has been discussed.
    • Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 11175129, 11175235), and the Natural Science Foundation of Tianjin, China (Grant No. 12JCZDJC26900).
    [1]

    Zhao C H, Zhang B P, Shang P P 2009 Chin. Phys. B 18 5539

    [2]

    Daniel M C, Astruc D 2004 Chem. Rev. 104 293

    [3]

    Inouye H, Tanaka K, Tanahashi I, Hattori T, Nakatsuka H 2000 Jpn. J. Appl. Phys. 39 5132

    [4]

    Huang Q, Zhang X D, Zhang H, Xiong S Z, Geng W D, Geng X H, Zhao Y 2010 Chin. Phys. B 19 047304

    [5]

    Stepanov A L 2010 Rev. Adv. Mater. Sci. 26 1

    [6]

    Liu X F, Jiang C Z, Ren F, Fu Q 2005 Acta Phys. Sin. 54 4633 (in Chinese)[刘向绯, 蒋昌忠, 任峰, 付强2005 物理学报54 4633]

    [7]

    Ferrando R, Jellinek J, Johnston R L 2008 Chem. Rev. 108 845

    [8]

    Peña O, Pal U, Rodríguez-Fernández L, Silva-Pereyra H G, Rodríguez-Iglesias V, Cheang-Wong J C, Arenas-Alatorre J, Oliver A 2009 J. Phys. Chem. C 113 2296

    [9]

    Mattei G, Maurizio C, Mazzoldi P, D’Acapito F, Battaglin G, Cattaruzza E, de Julián Fernández C, Sada C 2005 Phys. Rev. B 71 195418

    [10]

    Mattei G, De Marchi G, Maurizio C, Mazzoldi P, Sads C, Bello V, Battaglin G 2003 Phys. Rev. Lett. 90 085502

    [11]

    Zhang L, Jiang C Z, Ren F, Chen H B, Shi Y, Fu Q 2004 Acta Phys. Sin. 53 2910 (in Chinese)[张丽, 蒋昌忠, 任峰, 陈海波, 石瑛, 付强2004 物理学报53 2910]

    [12]

    Wang J, Zhang L H, Zhang X D, Shen Y Y, Liu C L 2013 J. Alloy. Compd. 549 231

    [13]

    Tang Q G, Meng J P, Liang J S, Nie L, Li Y X 2010 J. Alloy. Compd. 491 242

    [14]

    Xi J Y, Wang Z F, Lu G X 2002 Appl. Catal. A 225 77

    [15]

    Stepanov A L, Zhikharev V A, Hole D E, Townsend P D, Khaibullin I B 2000 Nucl. Instrum. Methods Phys. Res. B 166-167 26

    [16]

    Gnaser H, Brodyanski A, Reuscher B 2008 Surf. Interface Anal. 40 1415

    [17]

    Zhang X D, Xi J F, Shen Y Y, Zhang L H, Zhu F, Wang Z, Xue Y H, Liu C L 2011 Opt. Mater. 33 570

    [18]

    Shen Y Y, Zhang X D, Zhang D C, Xue Y H, Zhang L H, Liu C L 2011 Mater. Lett. 65 2966

    [19]

    Wang Y H, Li H Q, Lu J D, Wang R W 2011 Chin. Phys. Lett. 28 116101

    [20]

    Marshall C D, Speth J A, Payne S A 1997 J. Non-Cryst. Solids 212 59

    [21]

    Hume-Rothery W, Mabbott G W, Evans K M C 1934 Phil. Trans. R. Soc. 233 1

    [22]

    Pickering H W, Wagner C 1967 J. Electrochem. Soc. 114 698

    [23]

    Yazawa A, Gubčová A 1970 Trans. JIM 11 419

    [24]

    Amekura H, Kono K, Takeda Y, Kishimoto N 2005 Appl. Phys. Lett. 87 153105

    [25]

    Amekura H, Umeda N, Sakuma Y, Plaksin O A, Takeda Y, Kishimoto N, Buchal C 2006 Appl. Phys. Lett. 88 153119

    [26]

    Sun X F, Wei C P, Li Q Y 2009 Acta Phys. Sin. 58 5816 (in Chinese)[孙小飞, 魏长平, 李启源2009 物理学报 58 5816]

    [27]

    Volkert C A, Minor A M 2007 MRS Bull. 32 389

    [28]

    Chao L C, Lin S J, Chang W C 2010 Nucl. Instrum. Methods Phys. Res. B 268 1581

  • [1]

    Zhao C H, Zhang B P, Shang P P 2009 Chin. Phys. B 18 5539

    [2]

    Daniel M C, Astruc D 2004 Chem. Rev. 104 293

    [3]

    Inouye H, Tanaka K, Tanahashi I, Hattori T, Nakatsuka H 2000 Jpn. J. Appl. Phys. 39 5132

    [4]

    Huang Q, Zhang X D, Zhang H, Xiong S Z, Geng W D, Geng X H, Zhao Y 2010 Chin. Phys. B 19 047304

    [5]

    Stepanov A L 2010 Rev. Adv. Mater. Sci. 26 1

    [6]

    Liu X F, Jiang C Z, Ren F, Fu Q 2005 Acta Phys. Sin. 54 4633 (in Chinese)[刘向绯, 蒋昌忠, 任峰, 付强2005 物理学报54 4633]

    [7]

    Ferrando R, Jellinek J, Johnston R L 2008 Chem. Rev. 108 845

    [8]

    Peña O, Pal U, Rodríguez-Fernández L, Silva-Pereyra H G, Rodríguez-Iglesias V, Cheang-Wong J C, Arenas-Alatorre J, Oliver A 2009 J. Phys. Chem. C 113 2296

    [9]

    Mattei G, Maurizio C, Mazzoldi P, D’Acapito F, Battaglin G, Cattaruzza E, de Julián Fernández C, Sada C 2005 Phys. Rev. B 71 195418

    [10]

    Mattei G, De Marchi G, Maurizio C, Mazzoldi P, Sads C, Bello V, Battaglin G 2003 Phys. Rev. Lett. 90 085502

    [11]

    Zhang L, Jiang C Z, Ren F, Chen H B, Shi Y, Fu Q 2004 Acta Phys. Sin. 53 2910 (in Chinese)[张丽, 蒋昌忠, 任峰, 陈海波, 石瑛, 付强2004 物理学报53 2910]

    [12]

    Wang J, Zhang L H, Zhang X D, Shen Y Y, Liu C L 2013 J. Alloy. Compd. 549 231

    [13]

    Tang Q G, Meng J P, Liang J S, Nie L, Li Y X 2010 J. Alloy. Compd. 491 242

    [14]

    Xi J Y, Wang Z F, Lu G X 2002 Appl. Catal. A 225 77

    [15]

    Stepanov A L, Zhikharev V A, Hole D E, Townsend P D, Khaibullin I B 2000 Nucl. Instrum. Methods Phys. Res. B 166-167 26

    [16]

    Gnaser H, Brodyanski A, Reuscher B 2008 Surf. Interface Anal. 40 1415

    [17]

    Zhang X D, Xi J F, Shen Y Y, Zhang L H, Zhu F, Wang Z, Xue Y H, Liu C L 2011 Opt. Mater. 33 570

    [18]

    Shen Y Y, Zhang X D, Zhang D C, Xue Y H, Zhang L H, Liu C L 2011 Mater. Lett. 65 2966

    [19]

    Wang Y H, Li H Q, Lu J D, Wang R W 2011 Chin. Phys. Lett. 28 116101

    [20]

    Marshall C D, Speth J A, Payne S A 1997 J. Non-Cryst. Solids 212 59

    [21]

    Hume-Rothery W, Mabbott G W, Evans K M C 1934 Phil. Trans. R. Soc. 233 1

    [22]

    Pickering H W, Wagner C 1967 J. Electrochem. Soc. 114 698

    [23]

    Yazawa A, Gubčová A 1970 Trans. JIM 11 419

    [24]

    Amekura H, Kono K, Takeda Y, Kishimoto N 2005 Appl. Phys. Lett. 87 153105

    [25]

    Amekura H, Umeda N, Sakuma Y, Plaksin O A, Takeda Y, Kishimoto N, Buchal C 2006 Appl. Phys. Lett. 88 153119

    [26]

    Sun X F, Wei C P, Li Q Y 2009 Acta Phys. Sin. 58 5816 (in Chinese)[孙小飞, 魏长平, 李启源2009 物理学报 58 5816]

    [27]

    Volkert C A, Minor A M 2007 MRS Bull. 32 389

    [28]

    Chao L C, Lin S J, Chang W C 2010 Nucl. Instrum. Methods Phys. Res. B 268 1581

  • [1] Liu Jun-Hang, Zhu Zhao-Zhao, Bi Lin-zhu, Wang Peng-Ju, Cai Jian-Wang. Magnetic properties and thermal stability of ultrathin TbFeCo films encapsulated by heavy metals Pt and W. Acta Physica Sinica, 2023, 72(7): 077501. doi: 10.7498/aps.72.20222239
    [2] Kang Ya-Bin, Yuan Xiao-Peng, Wang Xiao-Bo, Li Ke-Wei, Gong Dian-Qing, Cheng Xu-Dong. Microstructure building and thermal stability of cermet-based photothermal conversion coatings with layered structures. Acta Physica Sinica, 2023, 72(5): 057103. doi: 10.7498/aps.72.20221693
    [3] Liu Na, Wang Yi, Li Wen-Bo, Zhang Li-Yan, He Shi-Kun, Zhao Jian-Kun, Zhao Ji-Jun. Thermal stability study of Weyl semimetal WTe2/Ti heterostructures by Raman scattering. Acta Physica Sinica, 2022, 71(19): 197501. doi: 10.7498/aps.71.20220712
    [4] Wang Xiao-Bo, Li Ke-Wei, Gao Li-Juan, Cheng Xu-Dong, Jiang Rong. Preparation and thermal stability of CrAlON based spectrally selective absorbing coatings. Acta Physica Sinica, 2021, 70(2): 027103. doi: 10.7498/aps.70.20200845
    [5] Zhu Xiao-Qin, Hu Yi-Feng. Application of Ge50Te50/Zn15Sb85 nanocomposite multilayer films in high thermal stability and low power phase change memory. Acta Physica Sinica, 2020, 69(14): 146101. doi: 10.7498/aps.69.20200502
    [6] Liu Le, Tang Jian, Wang Qin-Qin, Shi Dong-Xia, Zhang Guang-Yu. Thermal stability of MoS2 encapsulated by graphene. Acta Physica Sinica, 2018, 67(22): 226501. doi: 10.7498/aps.67.20181255
    [7] Lu Shun-Shun, Zhang Jin-Min, Guo Xiao-Tian, Gao Ting-Hong, Tian Ze-An, He Fan, He Xiao-Jin, Wu Hong-Xian, Xie Quan. Thermal stability of compound stucture of silicon nanowire encapsulated in carbon nanotubes. Acta Physica Sinica, 2016, 65(11): 116501. doi: 10.7498/aps.65.116501
    [8] Lu Dong, Jin Dong-Yue, Zhang Wan-Rong, Zhang Yu-Jie, Fu Qiang, Hu Rui-Xin, Gao Dong, Zhang Qing-Yuan, Huo Wen-Juan, Zhou Meng-Long, Shao Xiang-Peng. Novel microwave power sige heterojunction bipolar transistor with high thermal stability over a wide temperature range. Acta Physica Sinica, 2013, 62(10): 104401. doi: 10.7498/aps.62.104401
    [9] Zhou Guang-Hong, Pan Xuan, Zhu Yu-Fu. Exchange bias in BiFeO3/Ni81Fe19 magnetic films and its thermal stability. Acta Physica Sinica, 2013, 62(9): 097501. doi: 10.7498/aps.62.097501
    [10] Cui Xiao, Xu Bao-Chen, Wang Zhi-Zhi, Wang Li-Fang, Zhang Bo, Zu Fang-Qiu. On glass forming ability and thermal stability of Zr57Cu20Al10Ni8Ti5 bulk metallic glass by substituting each component with 1 at% Ag. Acta Physica Sinica, 2013, 62(1): 016101. doi: 10.7498/aps.62.016101
    [11] Zhang Zhang, Xiong Xian-Zhong, Yi Jiao-Jiao, Li Jin-Fu. Crystallization behavior and thermal stability of Al-Ni-RE metallic glasses. Acta Physica Sinica, 2013, 62(13): 136401. doi: 10.7498/aps.62.136401
    [12] Zhang Yang, Song Xiao-Yan, Xu Wen-Wu, Zhang Zhe-Xu. Thermodynamic study and cellular automaton simulation of thermal stability of nanocrystalline SmCo7 alloy. Acta Physica Sinica, 2012, 61(1): 016102. doi: 10.7498/aps.61.016102
    [13] Zhang Ying, He Zhi-Bing, Li Ping, Yan Jian-Cheng. Thermal stability of Si-doped glow discharge polymer films. Acta Physica Sinica, 2011, 60(12): 126501. doi: 10.7498/aps.60.126501
    [14] Xu Xue-Qin, Tang Chen-Yi, Wang Xuan, Cheng Ling, Yao Xin. In-plane and out-of-plane orientation influence on thermal stabilities of RBa2Cu3Oz thin film. Acta Physica Sinica, 2010, 59(2): 1294-1301. doi: 10.7498/aps.59.1294
    [15] Yan Jian-Cheng, He Zhi-Bing, Yang Zhi-Lin, Chen Zhi-Mei, Tang Yong-Jian, Wei Jian-Jun. Thermal stability of glow discharge polymer coatings on glass microspheres. Acta Physica Sinica, 2010, 59(11): 8005-8009. doi: 10.7498/aps.59.8005
    [16] Zhang Kai-Wang, Meng Li-Jun, Li Jun, Liu Wen-Liang, Tang Yi, Zhong Jian-Xin. Structure and thermal stability of gold nanowire encapsulated in carbon nanotube. Acta Physica Sinica, 2008, 57(7): 4347-4355. doi: 10.7498/aps.57.4347
    [17] Zhang Xu-Dong, Xu Tie-Feng, Nie Qiu-Hua, Dai Shi-Xun, Shen Xiang, Lu Long-Jun, Zhang Xiang-Hua. Investigation of spectral properties and thermal stability of Er3+/Yb3+ co-doped TeO2-B2O3-SiO2 glasses. Acta Physica Sinica, 2007, 56(3): 1758-1764. doi: 10.7498/aps.56.1758
    [18] Shen Xiang, Nie Qiu-Hua, Xu Tie-Feng, Gao Yuan. Investigation of spectral properties and thermal stability of Er3+/Yb3+ co-doped tungsten-tellurite glasses. Acta Physica Sinica, 2005, 54(5): 2379-2384. doi: 10.7498/aps.54.2379
    [19] Teng Jiao, Cai Jian-Wang, Xiong Xiao-Tao, Lai Wu-Yan, Zhu Feng-Wu. The establishment and thermal stability of exchange bias in NiFe/FeMn bilayers. Acta Physica Sinica, 2004, 53(1): 272-275. doi: 10.7498/aps.53.272
    [20] Yang Shen-Dong, Ning Zhao-Yuan, Huang Feng, Cheng Shan-Hua, Ye Chao. . Acta Physica Sinica, 2002, 51(6): 1321-1325. doi: 10.7498/aps.51.1321
Metrics
  • Abstract views:  5115
  • PDF Downloads:  642
  • Cited By: 0
Publishing process
  • Received Date:  22 November 2013
  • Accepted Date:  01 January 2014
  • Published Online:  05 April 2014

/

返回文章
返回