OPTIMIZATION OF Tc IN EPITAXIAL GdBaCuO SUPERCONDUCTING THIN FILM BY INVERTED CYLINDRICAL SPUTTERING

LI YAN-RONG LIU XIN-ZHAO XU JIN J.GEERK R.SMITHY

Citation:

OPTIMIZATION OF Tc IN EPITAXIAL GdBaCuO SUPERCONDUCTING THIN FILM BY INVERTED CYLINDRICAL SPUTTERING

LI YAN-RONG, LIU XIN-ZHAO, XU JIN, J.GEERK, R.SMITHY
PDF
Get Citation

(PLEASE TRANSLATE TO ENGLISH

BY GOOGLE TRANSLATE IF NEEDED.)

  • Thin films of GdBaCuO(GBCO) compound have been deposited in situ onto LaAlO3 single crystal substrates by inverted cylindrical sputtering.The variation of superconductive properties of the thin films with the substrate temperature and sputtering pressure has been systematic investigated.By the optimization of deposition parameter,high quality c-axis epitaxial GBCO thin films of Tc0>92K were reproducibly grown at the substrate temperature of 720—820℃ with a low deposition total pressure (40Pa).The Tc0 of the best sample is as high as 93.2K.Only by changing the target composition into GdBa2Cu4Oy (Gd124),was it observed that the samples always contain some a-axis oriented films,impling that excess copper would favour a-axis growth in thin films,and the Tc of the samples is lower than that with Gd123 target.The superconductivity of the thin films under high substrate temperature was clearly improved by the procedure of special post oxygenization at 400℃ in ozone atmosphere.These results are very useful to further prepare large area thin films of GBCO.
Metrics
  • Abstract views:  6013
  • PDF Downloads:  446
  • Cited By: 0
Publishing process
  • Received Date:  15 January 1997
  • Accepted Date:  01 April 1997
  • Published Online:  05 May 1997

/

返回文章
返回