声发射特性与材料断裂韧性相关性研究

朱 波 蔡 珣 王成国 蔡华甦

引用本文:
Citation:

声发射特性与材料断裂韧性相关性研究

朱 波, 蔡 珣, 王成国, 蔡华甦

Studies on the relationship between acoustic emission characteristics and fractu re toughness of materials

Zhu Bo, Cai Xun, Wang Cheng-Guo, Cai Hua-Su
PDF
导出引用
  • 以高强度铝合金的断裂过程为研究对象,利用先进的声发射试验系统,考察了拉伸试样和带有预制疲劳裂纹的DCB试样在断裂时的声发射事件特性,揭示了材料断裂韧性和声发射特性 间的关系.试验结果表明,材料稳态裂纹扩展起始于K1C并发射出许多幅值超过 阈值35 dB的信号,材料裂纹失稳扩展时爆发出强烈的声发射信号,材料断裂的累积声发射能与宏 观断裂能呈线性关系.
    The corelation between acoustic emission characteristics and their fracture toughness has been investigated in this paper based on the study of high-strength al uminum alloy cracking process by using advanced acoustic emission experiment sys tem and smooth tensile specimens as well as DCB specimens with premade cracks. E xperimental results showed that the specimens emitted strong signals with an amp litude above 35 dB when a stable crack extension started at K1C. Stro nger and more complicated acoustic emission signals were found during unstable crack extension, and the cumulative energy of acoustic emission events were found to b e linearly related with the macroscopic fracture energy.
    • 基金项目: 国家高技术研究发展计划(批准号:2002AA304090)资助的课题.
计量
  • 文章访问数:  3690
  • PDF下载量:  854
  • 被引次数: 0
出版历程
  • 收稿日期:  2002-12-26
  • 修回日期:  2003-04-10
  • 刊出日期:  2003-04-05

声发射特性与材料断裂韧性相关性研究

  • 1. (1)山东大学材料科学与工程学院,济南 250061; (2)山东大学计算机科学与技术学院,济南 250014
    基金项目: 

    国家高技术研究发展计划(批准号:2002AA304090)资助的课题.

摘要: 以高强度铝合金的断裂过程为研究对象,利用先进的声发射试验系统,考察了拉伸试样和带有预制疲劳裂纹的DCB试样在断裂时的声发射事件特性,揭示了材料断裂韧性和声发射特性 间的关系.试验结果表明,材料稳态裂纹扩展起始于K1C并发射出许多幅值超过 阈值35 dB的信号,材料裂纹失稳扩展时爆发出强烈的声发射信号,材料断裂的累积声发射能与宏 观断裂能呈线性关系.