利用固相反应法制备了Sr和Ba替代的Ca2.955-xMxSi2O7: 0.045Eu2+ (M= Sr, Ba, x= 0.10.5)系列荧光粉, 利用较大离子半径的Sr和Ba元素替代Eu掺杂Ca2.955-xMxSi2O7 中的Ca元素,研究Sr和Ba替代对样品结构和发光特性的影响. X射线衍射测试结果表明,少量Sr和Ba替代不会改变基质的晶体结构, 样品仍然为单斜晶系.未替代前, Ca2.955Si2O7: 0.045Eu2+ 样品的发射峰在574 nm左右,随着Sr含量的增加,样品的发射峰发生蓝移; 而Ba含量在x= 0.10.4时不会引起发射峰位置的移动, 但x= 0.5样品的发射峰发生蓝移.同等含量的Sr和Ba部分替代样品中的Ca元素, Ba替代样品的光谱强度较强.
[1] Zhang H X, Buddhudu S, Kam C H, Zhou Y, Lam Y L, Wong K S, Ooi B L, Ng S L, Que W X 2001 Mater. Chem. Phys. 68 31
[2] Bachmann V, Ronda C, Oeckler O, Schnick W, Meijerink A 2009 Chem. Mater. 21 316
[3] Kim J S, Jeon P E, Choi J C, Park H L 2005 Solid State Commun. 133 187
[4] Jang H S, Jeon D Y 2007 Appl. Phys. Lett. 90 041906
[5] Park J K, Cho K J, Yeon J H 2006 Appl. Phys. Lett. 88 043511
[6] Cui Z G, Jia G H, Deng D G, Hua Y J, Zhao S L, Huang L H, Wang H P, Ma H P, Xu S Q 2012 J. Lumin. 132 153
[7] Park W J, Song Y H, Yoon D H 2010 Mater. Sci. Eng. B 173 76
[8] Yang Z P, Liu Y F 2006 Acta Phys. Sin. 55 4946 (in Chinese) [杨志平, 刘玉峰 2006 物理学报 55 4946]
[9] Qian F J, Fu R L, Agathopoulos S, Gu X G, Song X F 2012 J. Lumin. 132 71
[10] Park W J, Jung M K, Kang S M, Masaki T, Yoon D H 2008 J. Phys. Chem. Sol. 69 1505
[11] Jiang L, Chang C, Mao D 2003 J. Alloys Compds. 360 193
[12] Wu H Y, Wang Y H, Hu Y H, Chen X H 2010 J. Guangdong Univ. Technol. 27 20 (in Chinese) [吴浩怡, 王银海, 胡义华, 陈雪花 2010 广东工业大学学报 27 20]
[13] Xie W, Wang Y H, Hu Y H, Wu H Y, Deng L Y, Liao F 2010 Acta Phys. Sin. 59 1148 [谢伟, 王银海, 胡义华, 吴浩怡, 邓柳咏, 廖峰 2010 物理学报 59 1148]
[14] Xu S Y, Zhang X S, Zhou Y L, Xi Q, Li L 2011 Chin. Phys. B 20 037804
[15] Kim J S, Park Y H, Kim S M, Choi J C, Park H L 2005 Solid State Commun. 133 445
[16] Mikhailik V B, Kraus H, Wahl D 2004 Phys. Rev. B 69 205110
-
[1] Zhang H X, Buddhudu S, Kam C H, Zhou Y, Lam Y L, Wong K S, Ooi B L, Ng S L, Que W X 2001 Mater. Chem. Phys. 68 31
[2] Bachmann V, Ronda C, Oeckler O, Schnick W, Meijerink A 2009 Chem. Mater. 21 316
[3] Kim J S, Jeon P E, Choi J C, Park H L 2005 Solid State Commun. 133 187
[4] Jang H S, Jeon D Y 2007 Appl. Phys. Lett. 90 041906
[5] Park J K, Cho K J, Yeon J H 2006 Appl. Phys. Lett. 88 043511
[6] Cui Z G, Jia G H, Deng D G, Hua Y J, Zhao S L, Huang L H, Wang H P, Ma H P, Xu S Q 2012 J. Lumin. 132 153
[7] Park W J, Song Y H, Yoon D H 2010 Mater. Sci. Eng. B 173 76
[8] Yang Z P, Liu Y F 2006 Acta Phys. Sin. 55 4946 (in Chinese) [杨志平, 刘玉峰 2006 物理学报 55 4946]
[9] Qian F J, Fu R L, Agathopoulos S, Gu X G, Song X F 2012 J. Lumin. 132 71
[10] Park W J, Jung M K, Kang S M, Masaki T, Yoon D H 2008 J. Phys. Chem. Sol. 69 1505
[11] Jiang L, Chang C, Mao D 2003 J. Alloys Compds. 360 193
[12] Wu H Y, Wang Y H, Hu Y H, Chen X H 2010 J. Guangdong Univ. Technol. 27 20 (in Chinese) [吴浩怡, 王银海, 胡义华, 陈雪花 2010 广东工业大学学报 27 20]
[13] Xie W, Wang Y H, Hu Y H, Wu H Y, Deng L Y, Liao F 2010 Acta Phys. Sin. 59 1148 [谢伟, 王银海, 胡义华, 吴浩怡, 邓柳咏, 廖峰 2010 物理学报 59 1148]
[14] Xu S Y, Zhang X S, Zhou Y L, Xi Q, Li L 2011 Chin. Phys. B 20 037804
[15] Kim J S, Park Y H, Kim S M, Choi J C, Park H L 2005 Solid State Commun. 133 445
[16] Mikhailik V B, Kraus H, Wahl D 2004 Phys. Rev. B 69 205110
| 引用本文: |
|
| Citation: |
|
计量
- 文章访问数: 2583
- PDF下载量: 650
- 被引次数: 0
下载: