Zn-22%Al合金共析转变的动态力学性质研究

刘军民 张进修

引用本文:
Citation:

Zn-22%Al合金共析转变的动态力学性质研究

刘军民, 张进修

THE DYNAMICALLY MECHANICAL PROPERTIES OF Zn-22%Al ALLOYS IN EUTECTOID DECOMPOSITION

LIU JUN-MIN, ZHANG JIN-XIU
PDF
导出引用
  • 用低频强迫振动模式测量了Zn-22%Al合金的动态力学性质(实模量、虚模量和内耗),观察到共析转变时具有典型的一级相变特征的内耗峰及共析转变温度以下的Al原子沿α/β相界以及α/α晶界扩散的弛豫过程.结合实验结果,对界面的稳定性和模量的变化进行了讨论
    The mechanical properties of Zn-22% Al alloys were measured with the low-frequency forced vibration mode. It was observed that a typical transformation internal friction peak was associated with eutectoid decomposition. A relaxation peak in the complex elastic modulus M2-T curves with an activation energy of 100±1.2kJ/mol was observed at the low-temperature side of the eutectoid decomposition peak. It was deduced that the relaxation process was related to the diffusion process of Al atom along the α/β phase boundary and α/α crystal boundary.
    • 基金项目: 中国科学院固体物理研究所固体缺陷与内耗开放研究实验室资助的课题.
计量
  • 文章访问数:  6388
  • PDF下载量:  421
  • 被引次数: 0
出版历程
  • 收稿日期:  1995-09-25
  • 修回日期:  1996-03-22
  • 刊出日期:  1996-11-20

/

返回文章
返回