掺杂Y2O3和BaCeO3提高MOD-YBCO超导性能的研究

丁发柱 古宏伟 张腾 王洪艳 屈飞 彭星煜 周微微

引用本文:
Citation:

掺杂Y2O3和BaCeO3提高MOD-YBCO超导性能的研究

丁发柱, 古宏伟, 张腾, 王洪艳, 屈飞, 彭星煜, 周微微

Enhanced flux pinning in MOD-YBCO films with co-doping of BaCeO3 and Y2O3 nanoparitcles

Ding Fa-Zhu, Gu Hong-Wei, Zhang Teng, Wang Hong-Yan, Qu Fei, Peng Xing-Yu, Zhou Wei-Wei
PDF
导出引用
  • 本文通过在前驱液中添加过量钇盐和铈的有机盐,采用三氟乙酸盐-金属有机沉积法(TFA-MOD) 在铝酸镧单晶基体上制备了含有纳米氧化钇和纳米铈酸钡的YBCO薄膜. 与纯YBCO薄膜相比,掺杂Y2O3/BaCeO3的YBCO膜的临界转变温度几乎保持不变,为91 K左右. 而掺杂Y2O3/BaCeO3的YBCO膜的临界电流密度达到5.0 MA/cm2 (77 K, 0T), 是纯YBCO膜临界电流密度的1.5倍.薄膜中的Y2O3和BaCeO3可能在YBCO内部起到了 有效的钉扎磁通作用.
    Enhancing the critical-current density of YBCO films is essential to gain a deeper understanding of the vortex pinning mechanisms and enable commercial applications of high-temperature superconductivity. Combined BaCeO3 and Y2O3 nanoparticles have been achieved to be co-doped in YBa2Cu3O7-x (YBCO) films by metalorganic deposition using trifluoroacetates (TFA-MOD). The formation of integrated nanoparticles increases the critical current density (Jc) of Y2O3/BaCeO3 doped-YBCO films while keeping the critical transition temperature (Tc) close to that in the pure YBCO films. YBCO film containing BaCeO3 and Y2O3 showed Tc value of 91 K and Jc value of 5 MA/cm2 at self-field (0 T, 77 K). The strongly enhanced flux pinning over a wide range of magnetic field may be attributed to the combined BaCeO3 and Y2O3 created by optimized TFA-MOD conditions.
    • 基金项目: 国家重点基础研究发展计划(批准号: 2011CBA00105); 国家自然科学基金(批准号: 51002149, 51272250)资助的课题.
    • Funds: Project supported by the National Basic Research Program of China (Grant No. 2011CBA00105), and the National Natural Science Foundation of China (Grant Nos. 51002149, 51272250).
    [1]

    Dimos D, Chaudhari P Mannhart J 1990 Phys. Rev. B 41 4038

    [2]

    Larkin A I Ovchinnikov, Yu N 1979 J. Low Temp. Phys. 34 409

    [3]

    Crisan A, Fujiwara S, Nie J C, Sundaresan A, Ihara H 2001 Appl. Phys. Lett. 79 4547

    [4]

    Sparing M, Backen E, Freudenberg T, Hhnel R, Rellinghaus B, Schultz L, Holzapfe B 2007 Supercond. Sci. Technol. 20 S239

    [5]

    Gutierrez J, Puig T, Gibert M, Moreno C, Roma N, Pomar A, Obradors X 2009 Appl. Phys. Lett. 94 172513

    [6]

    Vanpoucke D, Cottenier S, Speybroeckc V V, Bultinck P, Driessche I V 2012 Appl. Surf. Sci. 260 32

    [7]

    Maiorov B, Baily S A, Zhou H, Ugurlu O, Kennison J A, Dowden P C, Holesinger T G, Foltyn S R, Civale L 2009 Nature Mater. 8 398

    [8]

    Engel S, Thersleff T, Hhne R, Schultz L, Holzapfel B 2007 Appl. Phys. Lett. 90 102505

    [9]

    Samoilenkov S V, Boytsova O V, Amelichev V A, Kaul A R 2011 Supercond. Sci. Technol. 24 055003

    [10]

    Varanasi C V, Burke J, Brunke L, Wang H, Sumption M, Barnes P N 2007 J. Appl. Phys. 102 063909

    [11]

    Ding F Z, Gu H W 2010 Acta Phys. Sin. 59 8142 (in Chinese) [丁发柱, 古宏伟 2010 物理学报 59 8142]

    [12]

    Ding F Z, Gu H W, Zhang T, Dai S T, Xiao L Y 2011 Chin. Phys. B 20 027402

    [13]

    Ding F, Gu H, Zhang T, Wang H, Qu F, Dai S, Peng X, Cao J 2012 J. Alloys Compd. 513 277

    [14]

    Hanisch J, Cai C, Huhne R, Schultz L, Holzapfel B 2005 Appl. Phys. Lett. 86 122508

    [15]

    Kiessling A, Hänisch J, Thersleff T, Reich E, Weigand M, Hhne R, Sparing M, Holzapfel B, Durrell J H, Schultz1 L 2011 Supercond. Sci. Technol. 24 055018

    [16]

    Ishii Y, Shimoyama J, Tazaki Y, Nakashima T, Horii S, Kishio K 2006 Appl. Phys. Lett. 89 202514

    [17]

    Song X, Chen Z, Kim S, Matthew F D, Larbalestier D, Reeves J, Xie Y, Selvamanickam V 2006 Appl. Phys. Lett. 88 212508

    [18]

    Develos-Bagarinao K, Yamasaki H 2011 Supercond. Sci. Technol. 24 065017

    [19]

    Haugan T, Barnes P N, Wheeler R, Meisenkothen F, Sumption M 2004 Nature 430 867

  • [1]

    Dimos D, Chaudhari P Mannhart J 1990 Phys. Rev. B 41 4038

    [2]

    Larkin A I Ovchinnikov, Yu N 1979 J. Low Temp. Phys. 34 409

    [3]

    Crisan A, Fujiwara S, Nie J C, Sundaresan A, Ihara H 2001 Appl. Phys. Lett. 79 4547

    [4]

    Sparing M, Backen E, Freudenberg T, Hhnel R, Rellinghaus B, Schultz L, Holzapfe B 2007 Supercond. Sci. Technol. 20 S239

    [5]

    Gutierrez J, Puig T, Gibert M, Moreno C, Roma N, Pomar A, Obradors X 2009 Appl. Phys. Lett. 94 172513

    [6]

    Vanpoucke D, Cottenier S, Speybroeckc V V, Bultinck P, Driessche I V 2012 Appl. Surf. Sci. 260 32

    [7]

    Maiorov B, Baily S A, Zhou H, Ugurlu O, Kennison J A, Dowden P C, Holesinger T G, Foltyn S R, Civale L 2009 Nature Mater. 8 398

    [8]

    Engel S, Thersleff T, Hhne R, Schultz L, Holzapfel B 2007 Appl. Phys. Lett. 90 102505

    [9]

    Samoilenkov S V, Boytsova O V, Amelichev V A, Kaul A R 2011 Supercond. Sci. Technol. 24 055003

    [10]

    Varanasi C V, Burke J, Brunke L, Wang H, Sumption M, Barnes P N 2007 J. Appl. Phys. 102 063909

    [11]

    Ding F Z, Gu H W 2010 Acta Phys. Sin. 59 8142 (in Chinese) [丁发柱, 古宏伟 2010 物理学报 59 8142]

    [12]

    Ding F Z, Gu H W, Zhang T, Dai S T, Xiao L Y 2011 Chin. Phys. B 20 027402

    [13]

    Ding F, Gu H, Zhang T, Wang H, Qu F, Dai S, Peng X, Cao J 2012 J. Alloys Compd. 513 277

    [14]

    Hanisch J, Cai C, Huhne R, Schultz L, Holzapfel B 2005 Appl. Phys. Lett. 86 122508

    [15]

    Kiessling A, Hänisch J, Thersleff T, Reich E, Weigand M, Hhne R, Sparing M, Holzapfel B, Durrell J H, Schultz1 L 2011 Supercond. Sci. Technol. 24 055018

    [16]

    Ishii Y, Shimoyama J, Tazaki Y, Nakashima T, Horii S, Kishio K 2006 Appl. Phys. Lett. 89 202514

    [17]

    Song X, Chen Z, Kim S, Matthew F D, Larbalestier D, Reeves J, Xie Y, Selvamanickam V 2006 Appl. Phys. Lett. 88 212508

    [18]

    Develos-Bagarinao K, Yamasaki H 2011 Supercond. Sci. Technol. 24 065017

    [19]

    Haugan T, Barnes P N, Wheeler R, Meisenkothen F, Sumption M 2004 Nature 430 867

  • [1] 闻海虎. 高温超导体磁通钉扎和磁通动力学研究简介. 物理学报, 2021, 70(1): 017405. doi: 10.7498/aps.70.20201881
    [2] 梁超, 张洁, 赵可, 羊新胜, 赵勇. 拓扑超导体FeSexTe1–x单晶超导性能与磁通钉扎. 物理学报, 2020, 69(23): 237401. doi: 10.7498/aps.69.20201125
    [3] 陈桢妮, 刘胜利, 王海云, 程杰. Gd掺杂对无氟金属有机物沉积法制备Y1-xGdxBCO薄膜的应力调控. 物理学报, 2017, 66(15): 156101. doi: 10.7498/aps.66.156101
    [4] 王妙, 邬华春, 杨万民, 杨芃焘, 王小梅, 郝大鹏, 党文佳, 张明, 胡成西. BaO掺杂对单畴GdBCO超导块材性能的影响(二). 物理学报, 2017, 66(16): 167401. doi: 10.7498/aps.66.167401
    [5] 王春雷, 易晓磊, 姚超, 张谦君, 林鹤, 张现平, 王栋樑, 马衍伟. Ba1-xKxFe2As2单晶(Tc=38.5K)磁通钉扎力与钉扎机理研究. 物理学报, 2015, 64(11): 117401. doi: 10.7498/aps.64.117401
    [6] 于红云. 超导磁体剩余磁场对软磁材料测试的影响. 物理学报, 2014, 63(4): 047502. doi: 10.7498/aps.63.047502
    [7] 王银博, 薛驰, 冯庆荣. 钛离子辐照对MgB2超导薄膜的载流能力和磁通钉扎能力的影响. 物理学报, 2012, 61(19): 197401. doi: 10.7498/aps.61.197401
    [8] 丁发柱, 古宏伟. 前驱液成分对TFA-MOD法制备YBa2Cu3O7-x薄膜超导性能的影响. 物理学报, 2010, 59(11): 8142-8147. doi: 10.7498/aps.59.8142
    [9] 杨帆, 马瑾, 孔令沂, 栾彩娜, 朱振. 金属有机物化学气相沉积法生长Ga2(1-x)In2xO3薄膜的结构及光电性能研究. 物理学报, 2009, 58(10): 7079-7082. doi: 10.7498/aps.58.7079
    [10] 陈昌兆, 蔡传兵, 刘志勇, 应利良, 高 波, 刘金磊, 鲁玉明. NdBa2Cu3O7-δ/YBa2Cu3O7-δ多层膜体系的外延结构和磁通钉扎的研究. 物理学报, 2008, 57(7): 4371-4378. doi: 10.7498/aps.57.4371
    [11] 胡立发, 周廉, 张平祥, 王金星. 高温超导体的磁化与磁滞损耗. 物理学报, 2001, 50(7): 1359-1365. doi: 10.7498/aps.50.1359
    [12] 冯 勇, 周 廉, 杨万民, 张翠萍, 汪京荣, 于泽铭, 吴晓祖. PMP法YGdBaCuO超导体的磁通钉扎研究. 物理学报, 2000, 49(1): 146-152. doi: 10.7498/aps.49.146
    [13] 王智河, 曹效文, 陈敬林, 李可斌. YBa2Cu3O7-δ外延薄膜的有效钉扎势. 物理学报, 1998, 47(10): 1720-1726. doi: 10.7498/aps.47.1720
    [14] 姜建义, 胡安明, 孙玉平, 张发培, 杜家驹. 高JcBi-2223银包套带材的电阻转变展宽与磁通钉扎. 物理学报, 1996, 45(2): 283-290. doi: 10.7498/aps.45.283
    [15] 孙玉平, 张发培, 姜建义, 胡安明, 王迎枫, 杜家驹, 张裕恒, 盛正直. 高Jc Tl系2223相银包套带材的磁通钉扎和耗散. 物理学报, 1994, 43(7): 1166-1171. doi: 10.7498/aps.43.1166
    [16] 胡刚进, 方明虎, 李钟贤, 曾兴斌, 陈南松, 焦正宽, 张其瑞, 张贻瞳, 金新, 姚希贤. YBa2Cu3Oy中氧缺位的磁通钉扎效应. 物理学报, 1993, 42(10): 1669-1673. doi: 10.7498/aps.42.1669
    [17] 金新, 张贻瞳, 鹿牧, 张长贵, 颜涌, 于杨, 沈剑沧, 姚希贤. (BiPb)-Sr-Ca-Cu-O2223相高Tc超导体磁通钉扎与蠕动. 物理学报, 1991, 40(4): 630-633. doi: 10.7498/aps.40.630
    [18] 丁世英, 史可信, 曾朝阳, 余正, 施智祥, 邱里. Tl2Ba2Ca2Cu3Oy超导体磁通钉扎能的分布. 物理学报, 1991, 40(6): 985-989. doi: 10.7498/aps.40.985
    [19] 丁世英, 余正, 史可信. 非理想平面散射中心的磁通钉扎. 物理学报, 1987, 36(12): 1635-1639. doi: 10.7498/aps.36.1635
    [20] 陆怀先, 都有为, 王挺祥, 张毓昌. 有机物包裹的Fe3O4颗粒表面自旋钉扎效应研究. 物理学报, 1985, 34(1): 121-125. doi: 10.7498/aps.34.121
计量
  • 文章访问数:  5203
  • PDF下载量:  564
  • 被引次数: 0
出版历程
  • 收稿日期:  2013-02-27
  • 修回日期:  2013-03-18
  • 刊出日期:  2013-07-05

/

返回文章
返回