GIANT TUNNELING MAGNETORESISTANCE IN NANOSTRUCTURED ZnxFe3-xO4-α-Fe2O3 POLYCRYSTALLINE MATERIAL

DU YOU-WEI CHEN PENG ZHU JIAN-MIN XING DING-YU

GIANT TUNNELING MAGNETORESISTANCE IN NANOSTRUCTURED ZnxFe3-xO4-α-Fe2O3 POLYCRYSTALLINE MATERIAL

DU YOU-WEI, CHEN PENG, ZHU JIAN-MIN, XING DING-YU
PDF
Get Citation

(PLEASE TRANSLATE TO ENGLISH

BY GOOGLE TRANSLATE IF NEEDED.)

Metrics
  • Abstract views:  3181
  • PDF Downloads:  738
  • Cited By: 0
Publishing process
  • Received Date:  28 August 2001
  • Published Online:  20 November 2001

GIANT TUNNELING MAGNETORESISTANCE IN NANOSTRUCTURED ZnxFe3-xO4-α-Fe2O3 POLYCRYSTALLINE MATERIAL

  • 1. 南京大学固体微结构物理国家重点实验室物理系,南京210093

Abstract: Giant tunneling magnetoresistance effect (TMR) as large as 1280% at 4.2K and 158% at 300K was observed in Zn0.41Fe2.59O4-α-Fe2O3 polycrystalline sample. The Zn0.41Fe2.59O4 grains are separated by insulating α-Fe2O3 thin layer boundaries, The pattern of nanostructure has been verified by TEM and HREM and the thickness of α-Fe2O3 boundary is about 6-7nm. The huge TMR is attributed to the high spin-polarization of Zn0.41Fe2.59O4 grains and insulating antiferromagnetic α-Fe2O3 thin layer. The ZnxFe3-xO4 ferrite is a new type half-metallic material with a huge TMR at room temperature is interesting to further study in future.