金属材料界面与辐照缺陷的交互作用机理

刘思冕 韩卫忠

引用本文:
Citation:

金属材料界面与辐照缺陷的交互作用机理

刘思冕, 韩卫忠

Mechanism of interaction between interface and radiation defects in metal

Liu Si-Mian, Han Wei-Zhong
PDF
HTML
导出引用
  • 高能粒子辐照在材料内部产生大量的辐照缺陷, 如间隙原子、空位、位错环、空洞和气泡等. 大量辐照缺陷的形成和演化引起材料微观结构的失稳并造成严重的辐照硬化和脆化. 界面工程是一种调控材料抗辐照性能的有效方法. 通过引入高密度的晶界、相界、自由表面等来增加空位和间隙原子的复合概率, 能有效降低辐照缺陷的积聚, 提高材料的结构稳定性, 消除或减弱辐照的有害效应. 本文简述了几种典型金属材料界面与不同类型辐照缺陷的交互作用机理, 分析了界面结构、缺陷类型和辐照条件对交互作用过程的影响, 最后讨论了本领域需进一步关注的热点问题, 期望运用多学科知识和研究方法更好地揭示辐照损伤过程并设计新型抗辐照损伤材料.
    High-energy particles’ radiation produces a large number of radiation defects in material, such as interstitial atoms, vacancies, dislocation loops, voids and helium bubbles. The formation and evolution of massive radiation defects cause the instability of microstructure in metal, which further degrades its mechanical performance. Interface engineering is an effective method to tune the radiation resistance of metal and alloy. By introducing a large number of grain boundaries, phase interfaces, free surfaces, etc., the recombination probability of radiation-induced vacancies and interstitial atoms increases, thereby reducing the accumulation of radiation defects, improving the structural stability of the metal and eliminating the harmful effects of radiation. In this paper, we briefly review the recent progress of the mechanisms of interactions between several typical interfaces and various types of irradiation defects. The influence of interface structure, irradiation condition and defect character on their interaction behavior are reviewed and discussed. We also propose some critical questions about the radiation damage to material which remain to be understood. It is necessary to combine multidisciplinary techniques, knowledge and theories in order to fully understand the mechanism of radiation damage and design the advanced radiation-tolerant materials.
      通信作者: 韩卫忠, wzhanxjtu@mail.xjtu.edu.cn
    • 基金项目: 国家重点研发计划(批准号: 2017YFB0702301)、国家自然科学基金(批准号: 51471128, 51621063)和陕西省共享平台建设项目(批准号: 2017KTPT-12)资助的课题.
      Corresponding author: Han Wei-Zhong, wzhanxjtu@mail.xjtu.edu.cn
    • Funds: Project supported by the State Key Research and Development Program of China (Grant No.2017YFB0702301), the National Natural Science Foundation of China (Grant No. 51471128, 51621063), and the Innovation Project of Shaanxi Province, China (Grant No. 2017KTPT-12).
    [1]

    Zinkle S J, Was G S 2013 Acta Mater. 61 735Google Scholar

    [2]

    Zinkle S, Sindelar R 1988 J. Nucl. Mater. 155 1196

    [3]

    Kiritani M 2000 J. Nucl. Mater. 276 41Google Scholar

    [4]

    Griffiths M 1988 J. Nucl. Mater. 159 190Google Scholar

    [5]

    Silcox J, Hirsch P B 1959 Philos. Mag. 4 72Google Scholar

    [6]

    Kadoyoshi T, Kaburaki H, Shimizu F, Kimizuka H, Jitsukawa S, Li J 2007 Acta Mater. 55 3073Google Scholar

    [7]

    Wirth B D, Bulatov V, Diaz de la Rubia T 2000 J. Nucl. Mater. 283 773

    [8]

    Mansur L K 1978 Nucl. Technol. 40 5Google Scholar

    [9]

    Stubbins J, Garner F 1992 J. Nucl. Mater. 191 1295

    [10]

    Han W Z, Fu E, Demkowicz M J, Wang Y, Misra A 2013 J. Mater. Res. 28 2763Google Scholar

    [11]

    Yu K Y, Liu Y, Sun C, Wang H, Shao L, Fu E G, Zhang X 2012 J. Nucl. Mater. 425 140Google Scholar

    [12]

    Mazey D J, Evans J H 1986 J. Nucl. Mater. 138 16Google Scholar

    [13]

    Holt R A, Ibtahim E F 1979 Acta Metall. 27 1319Google Scholar

    [14]

    Fidleris V 1978 Atom. Energy Rev. 13 51

    [15]

    Carpenter G J C, Zee R H, Rogerson A 1988 J. Nucl. Mater. 159 86Google Scholar

    [16]

    Hu X X, Koyanagi T, Fukuda M, Kumar N A P K, Snead L L, Wirth B D, Katoh Y 2016 J. Nucl. Mater. 480 235Google Scholar

    [17]

    Pokor C, Brechet Y, Dubuisson P, Massoud J P, Avertye X 2004 J. Nucl. Mater. 326 30

    [18]

    Odette G R, Lucas G E 1998 Radiat. Eff. Defects Solids 44 189

    [19]

    Odette G R, Lucas G E 2001 JOM 53 18

    [20]

    Zinkle S J, Busby J T 2009 Mater. Today 12 12

    [21]

    Lu L, Shen Y F, Chen X H, Qian L H, Lu K 2004 Science 304 422Google Scholar

    [22]

    Han W Z, Demkowicz M J, Mara N A, Fu E, Sinha S, Rollett A D, Wang Y Q, Carpenter J S, Beyerlein I J, Misra A 2013 Adv. Mater. 25 6975Google Scholar

    [23]

    Han W Z, Demkowicz M J, Fu E G, Wang Y Q, Misra A 2012 Acta Mater. 60 6341Google Scholar

    [24]

    Hsiung L L, Fluss M J, Tumey S J, Choi B W, Serruys Y, Willaime F, Kimura A 2010 Phys. Rev. B 82 184103Google Scholar

    [25]

    Hsiung L, Fluss M, Tumey S, Kuntz J, El-Dasher B, Wall M, Choi B, Kimura A, Willaime F, Serruys Y 2011 J. Nucl. Mater. 409 72Google Scholar

    [26]

    Han W Z, Mara N A, Wang Y Q, Misra A, Demkowicz M J 2014 J. Nucl. Mater. 452 57Google Scholar

    [27]

    Fu E G, Caro M, Zepeda-Ruiz L A, Wang Y Q, Baldwin K, Bringa E, Nastasi M, Caro A 2012 Appl. Phys. Lett. 101 191607Google Scholar

    [28]

    Bringa E M, Monk J D, Caro A, Misra A, Zepeda-Ruiz L, Duchaineau M, Abraham F, Nastasi M, Picraux S T, Wang Y Q, Farkas D 2012 Nano Lett. 7 3351

    [29]

    Bai X M, Voter A F, Hoagland R G, Nastasi M, Uberuaga B P 2010 Science 327 1631Google Scholar

    [30]

    Chen D, Wang J, Chen T, Shao L 2013 Sci. Rep. 3 1450Google Scholar

    [31]

    Sun C, Zheng S, Wei C C, Wu Y, Shao L, Yang Y, Hartwig K T, Maloy S A, Zinkle S J, Allen T R, Wang H, Zhang X 2015 Sci. Rep. 5 7801Google Scholar

    [32]

    Zinkle S J, Farrell K 1989 J. Nucl. Mater. 168 262Google Scholar

    [33]

    Siegel R W, Chang S M, Balluffi R W 1980 Acta Metall. 28 249Google Scholar

    [34]

    Klueh R L, Nelson A T 2007 J. Nucl. Mater. 371 37Google Scholar

    [35]

    Demkowicz M J, Misra A, Caro A 2012 Curr. Opin. Solid State Mater. Sci. 16 101Google Scholar

    [36]

    Zhang X, Fu E G, Li N, Misra A, Wang Y Q, Shao L, Wang H 2012 J. Eng. Mater. Technol. 134 041010Google Scholar

    [37]

    Lu C Y, Zheng Lyu, Li Y P, Liu C M 2014 J. Notheastern U. (Nat. Sci. Ed) 35 1133

    [38]

    Beyerlein I J, Demkowicz M J, Misra A, Uberuaga B P 2015 Prog. Mater. Sci. 74 125Google Scholar

    [39]

    Demkowicz M J, Hoagland R G, Hirth J P 2008 Phys. Rev. Lett. 100 136102Google Scholar

    [40]

    Tschopp M A, Mcdowell D L 2007 Philos. Mag. 87 3147Google Scholar

    [41]

    Wang J, Beyerlein I J, Mara N A, Bhattacharyya D 2011 Scr. Mater. 64 1083Google Scholar

    [42]

    Wang M, Beyerlein I J, Zhang J, Han W Z 2018 Acta Mater. 160 211Google Scholar

    [43]

    Han W Z, Carpenter J S, Wang J, Beyerlein I J, Mara N A 2012 Appl. Phys. Lett. 100 011911Google Scholar

    [44]

    Demkowicz M J, Anderoglu O, Zhang X, Misra A 2011 J. Mater. Res. 26 1666Google Scholar

    [45]

    Barnes R S, Redding G B, Cottrell A H 1958 Philos. Mag. 3 97Google Scholar

    [46]

    Uberuaga B P, Choudhury S, Caro A 2015 J. Nucl. Mater. 462 402Google Scholar

    [47]

    Embury J D, Nicholson R B 1965 Acta Metall. 13 403Google Scholar

    [48]

    Mao S, Shu S, Zhou J, Averback R S, Dillon S J 2015 Acta Mater. 82 328Google Scholar

    [49]

    Mitchell T E, Lu Y C, Griffin A J, Nastasi M, Kung H 1997 J. Am. Ceram. Soc. 80 1673

    [50]

    Fu E G, Li N, Misra A, Hoagland R G, Wang H, Zhang X 2008 Mater. Sci. Eng. A 493 283Google Scholar

    [51]

    Misra A, Verdier M, Lu Y C, Kung H, Mitchell T E, Nastasi M 1998 Scr. Mater. 39 555Google Scholar

    [52]

    Gao F, Chen D, Hu W, Weber W J 2010 Phys. Rev. B 81 184101Google Scholar

    [53]

    Balluffi R W 1978 J. Nucl. Mater. 69-70 9

    [54]

    Bai X M, Uberuaga B P 2013 JOM 65 360Google Scholar

    [55]

    Bai X M, Vernon L J, Hoagland R G, Voter A F, Nastasi M, Uberuaga B P 2012 Phys. Rev. B 85 214103Google Scholar

    [56]

    Borovikov V, Tang X Z, Perez D, Bai X M, Uberuaga B P, Voter A F 2013 Nucl. Fusion 53 063001Google Scholar

    [57]

    Singh B N, Leffers T 1974 Scr. Metall. Mater. 8 1974

    [58]

    Liu X Y, Uberuaga B P, Demkowicz M J, Germann T C, Misra A, Nastasi M 2012 Phys. Rev. B 85 012103

    [59]

    Zhang L, Lu C, Tieu K, Shibuta Y 2018 Scripta Mater. 144 78Google Scholar

    [60]

    Xu J, Liu J B, Li S N, Liu B X, Jiang Y 2016 Phys. Chem. Phys. 18 17930Google Scholar

    [61]

    Demkowicz M J, Thilly L 2011 Acta Mater. 59 7744Google Scholar

    [62]

    Uberuaga B P, Bai X M, Dholabhai P P, Moore N, Duffy D M 2013 J. Phys. Condens. Matter 25 355001Google Scholar

    [63]

    Uberuaga B P, Vernon L J, Martinez E, Voter A F 2015 Sci. Rep. 5 09095Google Scholar

    [64]

    Demkowicz M J, Hoagland R G 2009 Intern. J. Appl. Mechan. 1 421Google Scholar

    [65]

    Nomura M, Adams J B 1995 J. Mater. Res. 10 2916Google Scholar

    [66]

    Zheng S, Shao S, Zhang J, Wang Y Q, Demkowicz M J, Beyerlein I J, Mara N A 2015 Sci. Rep. 5 15428Google Scholar

    [67]

    Lao Y X, Hu S L, Deng Y, Wang F, Du H, Zhang H B, Wang Y 2016 Sci. Rep. 7 40044

    [68]

    Zinkle S J, Seitzman L E, Wolfer W G I 1987 Philos. Mag. A 55 111Google Scholar

    [69]

    Kiener D, Hosemann P, Maloy S A, Minor A M 2011 Nat. Mater. 10 608Google Scholar

    [70]

    Niewczas M, Hoagland R G 2009 Philos. Mag. 89 727Google Scholar

    [71]

    Yu K Y, Bufford D, Sun C, Liu Y, Wang H, Kirk M A, Li M, Zhang X 2013 Nat. Commun. 4 1377Google Scholar

    [72]

    Chen Y, Li J, Yu K Y, Wang H, Kirk M A, Li M, Zhang X 2016 Acta Mater. 111 148Google Scholar

    [73]

    Wang J, Li N, Anderoglu O, Zhang X, Misra A, Huang J Y, Hirth J P 2010 Acta Mater. 58 2262Google Scholar

    [74]

    Wang J, Li N, Misra A 2013 Philos. Mag. 93 315Google Scholar

    [75]

    Wang J, Anderoglu O, Hirth J P 2009 Appl. Phys. Lett. 95 021908Google Scholar

    [76]

    Li J, Yu K Y, Chen Y, Song M, Wang H, Kirk M A, Li M, Zhang X 2015 Nano Lett. 15 2922Google Scholar

    [77]

    Sun C, Song M, Yu K Y, Kirk M, Li M, Wang H, Zhang X 2013 Metall. Mater. Trans. A 44 1966Google Scholar

    [78]

    Chen Y, Zhang X, Wang J 2016 JOM 68 235Google Scholar

    [79]

    Sun C, Bufford D, Chen Y, Kirk M A, Wang Y Q, Li M, Wang H, Maloy S A, Zhang X 2014 Sci. Rep. 4 3737

    [80]

    Thorsen P A, Bilde-Sørensen J B, Singh B N 2004 Scr. Mater. 51 557Google Scholar

    [81]

    Zhang L, Fu C C, Lu G H 2013 Phys. Rev. B 87 134107Google Scholar

    [82]

    Ding M S, Du J P, Wan L, Ogata S, Tian L, Ma E, Han W Z, Li J, Shan Z W 2016 Nano Lett. 16 4118Google Scholar

    [83]

    Ding M S, Tian L, Han W Z, Li J, Ma E, Shan Z W 2016 Phys. Rev. Lett. 117 215501Google Scholar

    [84]

    Han W Z, Ding M S, Shan Z W 2018 Scr. Mater. 147 1Google Scholar

    [85]

    Grimes R W, Kinungs R J M, Edwards L 2008 Nat. Mater. 7 683Google Scholar

    [86]

    Hochbauer T, Misra A, Hattar K, Hoagland R G 2005 J. Appl. Phys. 98 123516Google Scholar

    [87]

    Zhang X, Li N, Anderoglu O, Wang H, Swadener J G, Hochbauer T 2007 Nucl. Instrum. Methods Phys. Res. Sect. B 261 1129Google Scholar

    [88]

    Kashinath A, Misra A, Demkowicz M J 2013 Phys. Rev. Lett. 110 086101Google Scholar

    [89]

    Demkowicz M J, Bhattacharyya D, Usov I, Wang Y Q, Nastasi M, Misra A 2010 Appl. Phys. Lett. 97 161903Google Scholar

    [90]

    Di Z F, Bai X M, Wei Q M, Won J, Hoagland R G, Wang Y Q, Misra A, Uberuaga B P, Nastasi M 2011 Phys. Rev. B 84 052101

    [91]

    Lane P L, Goodhew P J 1983 Philos. Mag. A 48 965Google Scholar

    [92]

    Kashinath A, Demkowicz M J 2011 Model Simul. Mater. Sci. Eng. 19 035007Google Scholar

    [93]

    Singh B N, Leffers T, Green W V, Victoria M 1984 J. Nucl. Mater. 125 287Google Scholar

    [94]

    Bollmann W 1974 Phys. Status Solidi A 21 543Google Scholar

    [95]

    Bollmann W 1970 The Meaning of Dislocations in Crystalline Interfaces Washington, DC, USA, April 21-25, 1971 p465.

    [96]

    Chen D, Li N, Yuryev D, Baldwin J K, Wang Y Q, Demkowicz M J 2017 Sci. Adv. 3 eaao2710Google Scholar

  • 图 1  金属材料中的几种典型的界面结构 (a)经过200 keV, 剂量为2 × 1017 ions cm–2的氦离子在450 ℃辐照后的铜中的晶界; (b)经24.18 MeV 8价铁离子和1.7 MeV氦离子在430 ℃辐照后的ODS钢中高密度第二相和基体之间的界面; (c)经过200keV, 剂量为2 × 1021 ions cm–2的氦离子在450 ℃辐照后的铜-铌异质金属间的相界面; (d)经过400 keV, 剂量为8.64 × 1014 ions cm–2的氖离子在室温下辐照后的纳米多孔金中的自由表面(数据来源于文献[23,24,26,27],有改动)

    Fig. 1.  Typical interfaces in metals[23,24,26,27]: (a) Grain boundary in Cu which irradiated at 450 ℃ by 200 keV He ions with a fluence of 2 × 1017 ions cm–2; (b) interfaces between oxides and matrix in ODS steel which irradiated with 24.18 MeV Fe8+ ions and 1.7 MeV He+ ions at nearly 430 ℃; (c) Cu-Nb interface which irradiated at 450 ℃ by 200 keV He ions with a fluence of 2 × 1021 ions cm–2; (d) free surface in nanoporous gold (NPG) which irradiated at room temperature by 400 keV Ne++ ions with a fluence of 8.64 × 1014 ions/cm–2.

    图 2  (a)不同界面在相同的辐照条件下形成的无缺陷区的宽度随界面类型的变化; (b)经过200 keV, 剂量为2 × 1017 ions cm–2的氦离子在450 ℃辐照后的铜中大角晶界的无缺陷区域; (c)相同辐照条件下的K-S铜-铌相界面的无缺陷区域 (数据来源于文献[22,23],有改动)

    Fig. 2.  (a) Variation of the width of the void-denuded zone (VDZ) with the character of interfaces. The large angle grain boundary in (b) Cu which irradiated at 450 ℃ by 200 keV He ions with a fluence of 2 × 1017 ions cm–2. and in (c) Cu-Nb interface in the same irradiation condition[22,23].

    图 3  分子动力学模拟铜中Σ11对称倾斜晶界在吸收间隙原子前后对空位和间隙原子的形成能和迁移能的影响 (a)原始晶界的空位形成能; (b)级联碰撞发生后, 晶界吸收10个间隙原子的空位形成能, 虚线框代表容易被无障碍间隙原子发射复合掉的不稳定空位位点; (c)缺陷扩散能垒随着晶界距离的变化. 1代表原始晶界附近空位扩散的能垒; 2代表块体中空位扩散的能垒; 3代表原始晶界附近间隙原子扩散的能垒; 4代表块体中间隙原子扩散的能垒; 5代表吸收间隙原子的晶界附近空位扩散的能垒; 6代表吸收间隙原子的晶界附近间隙原子释放的能垒. 显而易见, 与原始晶界相比, 吸收间隙原子的晶界附近空位扩散和间隙原子释放的能垒都明显降低(数据来源于文献[29])

    Fig. 3.  The influence of grain boundaries loading with interstitials on the defect properties in Σ11 GB of copper: (a) Vacancy formation energy profile of a pristine GB; (b)vacancy formation energy profile of a GB loaded with 10 interstitials after a collision cascade. Vacancy sites denoted by dashed box are unstable sites that are annihilated via barrier-free interstitial emission; (c) defect diffusion barriers as a function of distance from a pristine and an interstitial-loaded GB. Line 1 represents vacancy diffusion barriers near the pristine GB. Line 2 represents vacancy diffusion barriers in the bulk. Line 3 represents interstitial diffusion barriers near the pristine GB. Line 4 represents interstitial diffusion barriers in the bulk. Line 5 represents vacancy diffusion barriers near the interstitial loaded GB. Line 6 represents interstitial emission near the interstitial loaded GB. Clearly, barriers for vacancy diffusion and interstitial emission near the interstitial-loaded GB are greatly reduced compared with the vacancy diffusion barriers near the pristine GB.

    图 4  铜–银界面“空位泵”的工作机理 (a) 400 keV, 2 × 1017 ion/cm2氦离子400 ℃辐照后的纳米层状共晶铜–银复合材料表面形成了富铜的凸起物; (b)距表面约200 nm深度形成大量纳米氦泡, 且银层氦泡密度和尺寸显著高于铜层中的氦泡; (c)距表面约1400 nm深度形成大量的空洞; (d)距表面约1800 nm深度形成位错结构; (e)铜–银界面上界面位错由于在铜侧产生压应力捕获铜空位到界面偏聚; (f)铜侧的空位自发转移至银层中; (g)银间隙原子由于界面拉应力偏聚到界面处, 并在铜–银界面处与部分界面空位复合; (h)铜层中的间隙原子浓度越来越高, 而银层中的空位浓度越来越高, 最终在表面形成富铜的凸起物(数据来源于文献[42], 有改动)

    Fig. 4.  Mechanism of vacancy pump in Cu/Ag interface: (a) A surface bump enriched copper formed on surface of the Cu/Ag nanocomposites after 400 keV, 2 × 1017 ion/cm2 helium ions implantation at 400 ℃; (b) high density of helium bubbles formed at the depth of 200 nm. The density and diameter of helium bubbles in Ag are larger than that in Cu; (c) high density of voids formed at the depth of 1400 nm; (d) high density of dislocation lines formed at the depth of 1800 nm; (e) Cu vacancies segregate to the MDI due to compressive stress field; (f) Cu vacancies at MDI transfer into Ag layer and attach to interface; (g) Ag interstitials migrate to non-MDI area because of tensile stress; (h) a state of interstitials enriched in Cu and vacancies enriched in Ag is achieved due to the vacancy pump effect of Cu/Ag interface.

    图 5  层错四面体与共格孪晶界的交互作用 (a)两种典型的四边形层错四面体, 层错四面体a从顶点削去一角, 层错四面体b从底角削去一角; (b)层错四面体和孪晶界交互作用沿着孪晶界形成大量层错; (c)对应(a)中共格孪晶界和层错四面体发交互作用的两种情况. 第一种, 由于层错四面体顶点先接触孪晶界而被削去一角, 在{111}面形成位错环; 另一种情况, 可动位错和压杆位错发生位错反应(如AB和AC), 在层错面形成两个新的可动位错, 分位错的进一步扩展消除整个层错四面体(数据来源于文献[71], 有改动)

    Fig. 5.  The mechanism of the interaction between the SFTs and the coherent twin boundaries: (a) The two truncated SFTs during their interactions with CTBs. SFT-a was truncated from its apex, whereas SFT-b was destructed from its base; (b) HRTEM micrograph showing the formation of groups of stacking faults during SFTs interactions with CTBs; (c) schematics of two types of interactions between SFTs and twin boundaries corresponding to the two cases in (a). The removal of SFT initiated from its apex (in contact with a twin boundary) results in the formation of dislocation loops on {111} plane in the twin lattices. In the lower case, the interaction of a mobile partial with stair-rod dislocations, AB and AC, results in two new mobile partials that can migrate on the surface of SFT and lead to its decomposition.

    图 6  银中的共格孪晶界在原位辐照过程与间隙型位错环的交互作用机制 (a)初始平直的共格孪晶界; (b)分子动力学模拟辐照产生了间隙型位错环, 在原位辐照下移动, 撞到共格孪晶界, 形成凸起; (c)共格孪晶界由于吸收间隙原子形成小凸起; (d)凸起的共格孪晶界遇到两个层错四面体; (e)分子动力学模拟拱起的共格孪晶界吸收邻近辐照产生的空位, 而后空位和孪晶界上的间隙原子复合, 使共格孪晶界恢复平直状态, 实现自愈合; (f)凸起的共格孪晶界恢复成平直状态(数据来源于文献[76], 有改动)

    Fig. 6.  The mechanism of interaction between CTBs and interstitial dislocation loops in Ag under in situ radiation: (a) An initially straight CTB; (b) the monocular dynamic simulation for the formation, movement and diffusion of an interstitial loop near a CTB; (c) the formation of puddle at the CTB; (d) Two SFTs adjacent to the puddle were gradually absorbed by the CTB; (e) the annihilation of interstitials with SFTs leads to the self-healing of the CTB; (f) the CTB was nearly recovered to a straight line.

    图 7  镍中Kr离子辐照产生的位错环向晶界运动、缩小并被最终被界面复合的机理. 在远离晶界的区域2中, 空位浓度达到饱和, 位错环持续吸收空位导致半径收缩; 在接近晶界的区域1中, 空位浓度梯度使位错环的一侧吸收空位, 另一侧释放空位, 使位错环向晶界迁移得以进行(数据来源于文献[77])

    Fig. 7.  Illustration of the shrinkage and migration of dislocation loops toward GBs in Ni irradiated by Kr ions. In region 2, further away from the GB, the concentration of vacancy induced by radiation approaches a plateau and the continuous absorption of vacancy leads to the gradual reduction of interstitial loop diameter. In region 1, adjacent to the GB, there is a concentration gradient of vacancies. The absorption of vacancy by one side of dislocation loop and the corresponding emission of vacancy from the other side (facing GB) lead to rapid migration (climb) of the loop toward the GB.

    图 8  铜铌界面既可作为障碍物阻碍位错滑移, 也作为缺陷陷阱愈合辐照缺陷. 在相同的辐照条件下, 纯铜晶粒内部形成了大量的氦泡, 而铜-铌纳米层状材料内观察不到任何的辐照缺陷. 说明纳米层状复合物比块体材料的强度更高, 抗辐照损伤能力更强(数据来源于文献[85])

    Fig. 8.  Cu-Nb interfaces act as obstacles to slip and sinks for radiation-induced defects. Under the same radiation condition, helium bubbles form in bulk Copper but not in Cu/Nb heterostructures. Hence, nanolayered composites not only increase strength but enhance radiation-damaged tolerance as well, compared with bulk materials.

    图 9  金中的辐照氦泡 (a)辐照后金薄膜中形成了大量纳米氦泡; (b)纳米氦泡分布在金的小角度扭转晶界的螺位错节点处; (c)分子动力学模拟沿着(001)小角度扭转晶界上不同原子位置的空位形成能和固溶能(数据来源于文献[90], 有改动)

    Fig. 9.  Helium bubbles in irradiated Au: (a) Nanoscale helium bubbles in Au film; (b) nanoscale helium bubbles are formed in the point of misfit dislocations in twist boundary of Au; (c) formation and solution energies of vacancy for different atom sites along (001) twist boundary.

    图 10  临界储氦量与界面失配位错密度与K-S界面取向的关系. 图中呈现了三种典型的FCC/BCC界面(K-S铜-铌界面, K-S铜-钒界面, K-S铜-钼界面)(数据来源于文献[35])

    Fig. 10.  The relationship of critical He concentration and MIDs densities for interfaces with Kurdjumov-Sachs interface orientation. As plotted are three typical FCC/BCC interface such as Cu-Nb, Cu-V, Cu-Mo.

  • [1]

    Zinkle S J, Was G S 2013 Acta Mater. 61 735Google Scholar

    [2]

    Zinkle S, Sindelar R 1988 J. Nucl. Mater. 155 1196

    [3]

    Kiritani M 2000 J. Nucl. Mater. 276 41Google Scholar

    [4]

    Griffiths M 1988 J. Nucl. Mater. 159 190Google Scholar

    [5]

    Silcox J, Hirsch P B 1959 Philos. Mag. 4 72Google Scholar

    [6]

    Kadoyoshi T, Kaburaki H, Shimizu F, Kimizuka H, Jitsukawa S, Li J 2007 Acta Mater. 55 3073Google Scholar

    [7]

    Wirth B D, Bulatov V, Diaz de la Rubia T 2000 J. Nucl. Mater. 283 773

    [8]

    Mansur L K 1978 Nucl. Technol. 40 5Google Scholar

    [9]

    Stubbins J, Garner F 1992 J. Nucl. Mater. 191 1295

    [10]

    Han W Z, Fu E, Demkowicz M J, Wang Y, Misra A 2013 J. Mater. Res. 28 2763Google Scholar

    [11]

    Yu K Y, Liu Y, Sun C, Wang H, Shao L, Fu E G, Zhang X 2012 J. Nucl. Mater. 425 140Google Scholar

    [12]

    Mazey D J, Evans J H 1986 J. Nucl. Mater. 138 16Google Scholar

    [13]

    Holt R A, Ibtahim E F 1979 Acta Metall. 27 1319Google Scholar

    [14]

    Fidleris V 1978 Atom. Energy Rev. 13 51

    [15]

    Carpenter G J C, Zee R H, Rogerson A 1988 J. Nucl. Mater. 159 86Google Scholar

    [16]

    Hu X X, Koyanagi T, Fukuda M, Kumar N A P K, Snead L L, Wirth B D, Katoh Y 2016 J. Nucl. Mater. 480 235Google Scholar

    [17]

    Pokor C, Brechet Y, Dubuisson P, Massoud J P, Avertye X 2004 J. Nucl. Mater. 326 30

    [18]

    Odette G R, Lucas G E 1998 Radiat. Eff. Defects Solids 44 189

    [19]

    Odette G R, Lucas G E 2001 JOM 53 18

    [20]

    Zinkle S J, Busby J T 2009 Mater. Today 12 12

    [21]

    Lu L, Shen Y F, Chen X H, Qian L H, Lu K 2004 Science 304 422Google Scholar

    [22]

    Han W Z, Demkowicz M J, Mara N A, Fu E, Sinha S, Rollett A D, Wang Y Q, Carpenter J S, Beyerlein I J, Misra A 2013 Adv. Mater. 25 6975Google Scholar

    [23]

    Han W Z, Demkowicz M J, Fu E G, Wang Y Q, Misra A 2012 Acta Mater. 60 6341Google Scholar

    [24]

    Hsiung L L, Fluss M J, Tumey S J, Choi B W, Serruys Y, Willaime F, Kimura A 2010 Phys. Rev. B 82 184103Google Scholar

    [25]

    Hsiung L, Fluss M, Tumey S, Kuntz J, El-Dasher B, Wall M, Choi B, Kimura A, Willaime F, Serruys Y 2011 J. Nucl. Mater. 409 72Google Scholar

    [26]

    Han W Z, Mara N A, Wang Y Q, Misra A, Demkowicz M J 2014 J. Nucl. Mater. 452 57Google Scholar

    [27]

    Fu E G, Caro M, Zepeda-Ruiz L A, Wang Y Q, Baldwin K, Bringa E, Nastasi M, Caro A 2012 Appl. Phys. Lett. 101 191607Google Scholar

    [28]

    Bringa E M, Monk J D, Caro A, Misra A, Zepeda-Ruiz L, Duchaineau M, Abraham F, Nastasi M, Picraux S T, Wang Y Q, Farkas D 2012 Nano Lett. 7 3351

    [29]

    Bai X M, Voter A F, Hoagland R G, Nastasi M, Uberuaga B P 2010 Science 327 1631Google Scholar

    [30]

    Chen D, Wang J, Chen T, Shao L 2013 Sci. Rep. 3 1450Google Scholar

    [31]

    Sun C, Zheng S, Wei C C, Wu Y, Shao L, Yang Y, Hartwig K T, Maloy S A, Zinkle S J, Allen T R, Wang H, Zhang X 2015 Sci. Rep. 5 7801Google Scholar

    [32]

    Zinkle S J, Farrell K 1989 J. Nucl. Mater. 168 262Google Scholar

    [33]

    Siegel R W, Chang S M, Balluffi R W 1980 Acta Metall. 28 249Google Scholar

    [34]

    Klueh R L, Nelson A T 2007 J. Nucl. Mater. 371 37Google Scholar

    [35]

    Demkowicz M J, Misra A, Caro A 2012 Curr. Opin. Solid State Mater. Sci. 16 101Google Scholar

    [36]

    Zhang X, Fu E G, Li N, Misra A, Wang Y Q, Shao L, Wang H 2012 J. Eng. Mater. Technol. 134 041010Google Scholar

    [37]

    Lu C Y, Zheng Lyu, Li Y P, Liu C M 2014 J. Notheastern U. (Nat. Sci. Ed) 35 1133

    [38]

    Beyerlein I J, Demkowicz M J, Misra A, Uberuaga B P 2015 Prog. Mater. Sci. 74 125Google Scholar

    [39]

    Demkowicz M J, Hoagland R G, Hirth J P 2008 Phys. Rev. Lett. 100 136102Google Scholar

    [40]

    Tschopp M A, Mcdowell D L 2007 Philos. Mag. 87 3147Google Scholar

    [41]

    Wang J, Beyerlein I J, Mara N A, Bhattacharyya D 2011 Scr. Mater. 64 1083Google Scholar

    [42]

    Wang M, Beyerlein I J, Zhang J, Han W Z 2018 Acta Mater. 160 211Google Scholar

    [43]

    Han W Z, Carpenter J S, Wang J, Beyerlein I J, Mara N A 2012 Appl. Phys. Lett. 100 011911Google Scholar

    [44]

    Demkowicz M J, Anderoglu O, Zhang X, Misra A 2011 J. Mater. Res. 26 1666Google Scholar

    [45]

    Barnes R S, Redding G B, Cottrell A H 1958 Philos. Mag. 3 97Google Scholar

    [46]

    Uberuaga B P, Choudhury S, Caro A 2015 J. Nucl. Mater. 462 402Google Scholar

    [47]

    Embury J D, Nicholson R B 1965 Acta Metall. 13 403Google Scholar

    [48]

    Mao S, Shu S, Zhou J, Averback R S, Dillon S J 2015 Acta Mater. 82 328Google Scholar

    [49]

    Mitchell T E, Lu Y C, Griffin A J, Nastasi M, Kung H 1997 J. Am. Ceram. Soc. 80 1673

    [50]

    Fu E G, Li N, Misra A, Hoagland R G, Wang H, Zhang X 2008 Mater. Sci. Eng. A 493 283Google Scholar

    [51]

    Misra A, Verdier M, Lu Y C, Kung H, Mitchell T E, Nastasi M 1998 Scr. Mater. 39 555Google Scholar

    [52]

    Gao F, Chen D, Hu W, Weber W J 2010 Phys. Rev. B 81 184101Google Scholar

    [53]

    Balluffi R W 1978 J. Nucl. Mater. 69-70 9

    [54]

    Bai X M, Uberuaga B P 2013 JOM 65 360Google Scholar

    [55]

    Bai X M, Vernon L J, Hoagland R G, Voter A F, Nastasi M, Uberuaga B P 2012 Phys. Rev. B 85 214103Google Scholar

    [56]

    Borovikov V, Tang X Z, Perez D, Bai X M, Uberuaga B P, Voter A F 2013 Nucl. Fusion 53 063001Google Scholar

    [57]

    Singh B N, Leffers T 1974 Scr. Metall. Mater. 8 1974

    [58]

    Liu X Y, Uberuaga B P, Demkowicz M J, Germann T C, Misra A, Nastasi M 2012 Phys. Rev. B 85 012103

    [59]

    Zhang L, Lu C, Tieu K, Shibuta Y 2018 Scripta Mater. 144 78Google Scholar

    [60]

    Xu J, Liu J B, Li S N, Liu B X, Jiang Y 2016 Phys. Chem. Phys. 18 17930Google Scholar

    [61]

    Demkowicz M J, Thilly L 2011 Acta Mater. 59 7744Google Scholar

    [62]

    Uberuaga B P, Bai X M, Dholabhai P P, Moore N, Duffy D M 2013 J. Phys. Condens. Matter 25 355001Google Scholar

    [63]

    Uberuaga B P, Vernon L J, Martinez E, Voter A F 2015 Sci. Rep. 5 09095Google Scholar

    [64]

    Demkowicz M J, Hoagland R G 2009 Intern. J. Appl. Mechan. 1 421Google Scholar

    [65]

    Nomura M, Adams J B 1995 J. Mater. Res. 10 2916Google Scholar

    [66]

    Zheng S, Shao S, Zhang J, Wang Y Q, Demkowicz M J, Beyerlein I J, Mara N A 2015 Sci. Rep. 5 15428Google Scholar

    [67]

    Lao Y X, Hu S L, Deng Y, Wang F, Du H, Zhang H B, Wang Y 2016 Sci. Rep. 7 40044

    [68]

    Zinkle S J, Seitzman L E, Wolfer W G I 1987 Philos. Mag. A 55 111Google Scholar

    [69]

    Kiener D, Hosemann P, Maloy S A, Minor A M 2011 Nat. Mater. 10 608Google Scholar

    [70]

    Niewczas M, Hoagland R G 2009 Philos. Mag. 89 727Google Scholar

    [71]

    Yu K Y, Bufford D, Sun C, Liu Y, Wang H, Kirk M A, Li M, Zhang X 2013 Nat. Commun. 4 1377Google Scholar

    [72]

    Chen Y, Li J, Yu K Y, Wang H, Kirk M A, Li M, Zhang X 2016 Acta Mater. 111 148Google Scholar

    [73]

    Wang J, Li N, Anderoglu O, Zhang X, Misra A, Huang J Y, Hirth J P 2010 Acta Mater. 58 2262Google Scholar

    [74]

    Wang J, Li N, Misra A 2013 Philos. Mag. 93 315Google Scholar

    [75]

    Wang J, Anderoglu O, Hirth J P 2009 Appl. Phys. Lett. 95 021908Google Scholar

    [76]

    Li J, Yu K Y, Chen Y, Song M, Wang H, Kirk M A, Li M, Zhang X 2015 Nano Lett. 15 2922Google Scholar

    [77]

    Sun C, Song M, Yu K Y, Kirk M, Li M, Wang H, Zhang X 2013 Metall. Mater. Trans. A 44 1966Google Scholar

    [78]

    Chen Y, Zhang X, Wang J 2016 JOM 68 235Google Scholar

    [79]

    Sun C, Bufford D, Chen Y, Kirk M A, Wang Y Q, Li M, Wang H, Maloy S A, Zhang X 2014 Sci. Rep. 4 3737

    [80]

    Thorsen P A, Bilde-Sørensen J B, Singh B N 2004 Scr. Mater. 51 557Google Scholar

    [81]

    Zhang L, Fu C C, Lu G H 2013 Phys. Rev. B 87 134107Google Scholar

    [82]

    Ding M S, Du J P, Wan L, Ogata S, Tian L, Ma E, Han W Z, Li J, Shan Z W 2016 Nano Lett. 16 4118Google Scholar

    [83]

    Ding M S, Tian L, Han W Z, Li J, Ma E, Shan Z W 2016 Phys. Rev. Lett. 117 215501Google Scholar

    [84]

    Han W Z, Ding M S, Shan Z W 2018 Scr. Mater. 147 1Google Scholar

    [85]

    Grimes R W, Kinungs R J M, Edwards L 2008 Nat. Mater. 7 683Google Scholar

    [86]

    Hochbauer T, Misra A, Hattar K, Hoagland R G 2005 J. Appl. Phys. 98 123516Google Scholar

    [87]

    Zhang X, Li N, Anderoglu O, Wang H, Swadener J G, Hochbauer T 2007 Nucl. Instrum. Methods Phys. Res. Sect. B 261 1129Google Scholar

    [88]

    Kashinath A, Misra A, Demkowicz M J 2013 Phys. Rev. Lett. 110 086101Google Scholar

    [89]

    Demkowicz M J, Bhattacharyya D, Usov I, Wang Y Q, Nastasi M, Misra A 2010 Appl. Phys. Lett. 97 161903Google Scholar

    [90]

    Di Z F, Bai X M, Wei Q M, Won J, Hoagland R G, Wang Y Q, Misra A, Uberuaga B P, Nastasi M 2011 Phys. Rev. B 84 052101

    [91]

    Lane P L, Goodhew P J 1983 Philos. Mag. A 48 965Google Scholar

    [92]

    Kashinath A, Demkowicz M J 2011 Model Simul. Mater. Sci. Eng. 19 035007Google Scholar

    [93]

    Singh B N, Leffers T, Green W V, Victoria M 1984 J. Nucl. Mater. 125 287Google Scholar

    [94]

    Bollmann W 1974 Phys. Status Solidi A 21 543Google Scholar

    [95]

    Bollmann W 1970 The Meaning of Dislocations in Crystalline Interfaces Washington, DC, USA, April 21-25, 1971 p465.

    [96]

    Chen D, Li N, Yuryev D, Baldwin J K, Wang Y Q, Demkowicz M J 2017 Sci. Adv. 3 eaao2710Google Scholar

  • [1] 董烨, 朱特, 宋亚敏, 叶凤娇, 张鹏, 杨启贵, 刘福雁, 陈雨, 曹兴忠. 低活化马氏体钢中位错对氦辐照缺陷的影响. 物理学报, 2023, 72(18): 187801. doi: 10.7498/aps.72.20230694
    [2] 王甫, 周毅, 高士鑫, 段振刚, 孙志鹏, 汪俊, 邹宇, 付宝勤. 碳化硅中点缺陷对热传导性能影响的分子动力学研究. 物理学报, 2022, 71(3): 036501. doi: 10.7498/aps.71.20211434
    [3] 王甫, 周毅, 高士鑫, 段振刚, 孙志鹏, 汪俊(Jun Wang), 邹 宇, 付宝勤(Baoqin Fu). 碳化硅中点缺陷对热传导性能影响的分子动力学研究. 物理学报, 2021, (): . doi: 10.7498/aps.70.20211434
    [4] 李翔, 尹益辉, 张元章. α-Fe中氦泡极限压强的分子动力学模拟. 物理学报, 2021, 70(7): 076101. doi: 10.7498/aps.70.20201409
    [5] 李明阳, 张雷敏, 吕沙沙, 李正操. 离子辐照和氧化对IG-110核级石墨中的点缺陷的影响. 物理学报, 2019, 68(12): 128102. doi: 10.7498/aps.68.20190371
    [6] 谢修华, 李炳辉, 张振中, 刘雷, 刘可为, 单崇新, 申德振. 点缺陷调控: 宽禁带II族氧化物半导体的机遇与挑战. 物理学报, 2019, 68(16): 167802. doi: 10.7498/aps.68.20191043
    [7] 张越, 赵剑, 董鹏, 田达晰, 梁兴勃, 马向阳, 杨德仁. 掺杂剂对重掺n型直拉硅片的氧化诱生层错生长的影响. 物理学报, 2015, 64(9): 096105. doi: 10.7498/aps.64.096105
    [8] 梁力, 谈效华, 向伟, 王远, 程焰林, 马明旺. 温度及深度对钛中氦泡释放过程影响的分子动力学研究. 物理学报, 2015, 64(4): 046103. doi: 10.7498/aps.64.046103
    [9] 杜洋洋, 李炳生, 王志光, 孙建荣, 姚存峰, 常海龙, 庞立龙, 朱亚滨, 崔明焕, 张宏鹏, 李远飞, 王霁, 朱卉平, 宋鹏, 王栋. He离子辐照6H-SiC引入缺陷的光谱研究. 物理学报, 2014, 63(21): 216101. doi: 10.7498/aps.63.216101
    [10] 王飞, 刘望, 邓爱红, 朱敬军, 安竹, 汪渊. 界面对ZrN/TaN纳米多层膜固氦性能的影响. 物理学报, 2013, 62(18): 186801. doi: 10.7498/aps.62.186801
    [11] 吉川, 徐进. 点缺陷对硼掺杂直拉硅单晶p/p+ 外延片中铜沉淀的影响. 物理学报, 2012, 61(23): 236102. doi: 10.7498/aps.61.236102
    [12] 曹永军, 谭伟, 刘燕. 二维磁振子晶体中点缺陷模的耦合性质研究. 物理学报, 2012, 61(11): 117501. doi: 10.7498/aps.61.117501
    [13] 刘望, 邬琦琦, 陈顺礼, 朱敬军, 安竹, 汪渊. 氦对铜钨纳米多层膜界面稳定性的影响. 物理学报, 2012, 61(17): 176802. doi: 10.7498/aps.61.176802
    [14] 魏琦, 程营, 刘晓峻. 点缺陷阵列对声子晶体波导定向辐射性能的影响. 物理学报, 2011, 60(12): 124301. doi: 10.7498/aps.60.124301
    [15] 温才, 李方华, 邹进, 陈弘. AlSb/GaAs(001)失配位错的高分辨电子显微学研究. 物理学报, 2010, 59(3): 1928-1937. doi: 10.7498/aps.59.1928
    [16] 敖冰云, 汪小琳, 陈丕恒, 史鹏, 胡望宇, 杨剑瑜. 嵌入原子法计算金属钚中点缺陷的能量. 物理学报, 2010, 59(7): 4818-4825. doi: 10.7498/aps.59.4818
    [17] 王海燕, 祝文军, 邓小良, 宋振飞, 陈向荣. 冲击加载下铝中氦泡和孔洞的塑性变形特征研究. 物理学报, 2009, 58(2): 1154-1160. doi: 10.7498/aps.58.1154
    [18] 马新国, 江建军, 梁 培. 锐钛矿型TiO2(101)面本征点缺陷的理论研究. 物理学报, 2008, 57(5): 3120-3125. doi: 10.7498/aps.57.3120
    [19] 宜晨虹, 慕青松, 苗天德. 带有点缺陷的二维颗粒系统离散元模拟. 物理学报, 2008, 57(6): 3636-3640. doi: 10.7498/aps.57.3636
    [20] 王海燕, 祝文军, 宋振飞, 刘绍军, 陈向荣, 贺红亮. 氦泡对铝的弹性性质的影响. 物理学报, 2008, 57(6): 3703-3708. doi: 10.7498/aps.57.3703
计量
  • 文章访问数:  13751
  • PDF下载量:  309
  • 被引次数: 0
出版历程
  • 收稿日期:  2019-01-23
  • 修回日期:  2019-04-22
  • 上网日期:  2019-06-06
  • 刊出日期:  2019-07-05

/

返回文章
返回