BiFeO3纳米粉的制备、结构表征及铁磁特性

张嬛 刘发民 丁芃 钟文武 周传仓

引用本文:
Citation:

BiFeO3纳米粉的制备、结构表征及铁磁特性

张嬛, 刘发民, 丁芃, 钟文武, 周传仓

Preparation,structure and ferromagnetic properties of BiFeO3 nano-power

Zhang Huan, Liu Fa-Min, Ding Peng, Zhong Wen-Wu, Zhou Chuan-Cang
PDF
导出引用
  • 采用溶胶-凝胶法成功地制备出BiFeO3纳米粉,利用X射线衍射仪(XRD)、扫描电子显微镜(SEM)和透射电子显微镜(TEM)测量分析了其结构与形貌,结果发现:胶体经700℃烧结2—25 h后,形成了30 nm左右的较纯相BiFeO3粉末,该样品为六角晶系,R3-m[166]空间群,晶胞参数为a=b=05580 nm,c=06939 nm,其(101)面晶面间距为0396 nm左右,(
    The BiFeO3 nano-powder has been synthesized by sol-gel method. The structure and morphology of BiFeO3 nano-powder have been characterized by X-ray diffraction (XRD),scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM). The results showed that the samples sintered at 700℃ for 2 h or 25 h is in the formed of pure BiFeO3 with the grain size about 30 nm,and the structure is hexagonal of R3-m[166] space group with lattice constants a=b=05580 nm,c=06939 nm,and the spacing of (101) and (110) are about 0396 nm and 0273 nm,respectively. The room temperature magnetic properties of samples have been measured on vibrating sample magnetometer (VSM). It was showed that the BiFeO3 nano-powder gives a complete hysteresis loop,which means that BiFeO3 nano-powder possesses weakly ferromagnetic at room temperature,its coercive force (Hc) could reach to over 700 Oe,and the magnetic mechanism comes from the double exchange of Fe3+-O-Fe2+. Moreover,with the increase of the sintering time,the grain size is influenced;the saturation magnetization (Ms) has a small change,however,the coercive force (Hc) of the BiFeO3 nano-powder decreased obviously.
    • 基金项目: 航天科学基金(批准号:373858)资助的课题.
    [1]

    [1]Hill N A 2000 J. Phys. Chem.B 104 6694

    [2]

    [2]Zhou J P,Shi Z,Liu G,He H C,Nan C W 2006 Acta Phys. Sin. 55 3766 (in Chinese)[周剑平、施展、刘刚、何泓材、南策文 2006 物理学报 55 3766]

    [3]

    [3]Fillippetti A,Hill N A 2001 J. Magn. Magn. Mater. 236 176

    [4]

    [4]Murashav V A,Rakov D N,Ionov V M,Dubenko I S,Titov 1994 Ferroelectrics 162 11

    [5]

    [5]Fischer P,Polomska M,Sosnowska I,Szymanski M 1980 J. Phys. 13 1931

    [6]

    [6]Ruette B,Zvyagin S,Pyatakov A P,Bush A,Li J F,Belotelov V I,Zvezdin A K,Viehland D 2004 Phys. Rev. B 69 064114

    [7]

    [7]Tang C H,Cai M Q,Yin Z,Zhang M S 2004 Acta Phys. Sin. 53 2931 (in Chinese)[唐春红、蔡孟秋、尹真、张明生 2004 物理学报 53 2931]

    [8]

    [8]Sun Y,Huang Z F,Fan H G,Ming X,Wang C Z,Chen G 2009 Acta Phys. Sin. 58 193 (in Chinese)[孙源、黄祖飞、范厚刚、明星、王春忠、陈岗 2009 物理学报 58 193]

    [9]

    [9]Qi X D,Dho J,Blamire M,Jia Q X,Lee J S,Foltyn S,MacManus-Driscoll J L 2004 J. Magn. Magn. Mater. 283 419

    [10]

    ]Kumar M M,Palkara V R,Srinivas K,Suryanarayana S V 2000 Appl. Phys. Lett. 76 2764

    [11]

    ]Wang Y P,Zhou L,Zhang M F,Chen X Y,Liu J M,Liu Z G 2004 Appl. Phys. Lett. 84 1731

    [12]

    ]Liu H R,Liu Z L,Liu Q,Yao K L 2006 Thin Solid Films. 500 105

    [13]

    ]Epifani M 2007 Mater. Lett. 61 3100

    [14]

    ]Matsui T,Taketani E,Fujimura N,Ito T,Morii K 2003 J. Appl. Phys. 93 6993

    [15]

    ]Taketani E,Matsui T,Fujimura N,Morii K 2004 IEEE Trans. Magn. 40 2736

    [16]

    ]Matsui T,Taketani E,Fujimura N,Tsuda H,Morii K 2005 Appl. Phys. Lett. 86 082902

    [17]

    ]Ren P,Guan J G,Cheng X D 2006 Mater. Chem. Phys. 98 93

    [18]

    ]Zhong C G,Jiang Q,Fang J H,Ge C W 2009 Acta Phys. Sin. 58 3491 (in Chinese)[仲崇贵、蒋青、方靖淮 2009 物理学报 58 3491]

    [19]

    ]Lu Y,Li Q A,Di N L,Cheng S H 2003 Acta. Phys. Sin. 52 1250 (in Chinese)[鲁毅、李庆安 邸乃力、成昭华 2003 物理学报 52 1250]

    [20]

    ]Han L A,Chen Ch L,Dong Y H,Wang J Y,Gao G M,Luo B C 2008 Acta. Phys. Sin. 57 541 (in Chinese)[韩立安、陈长乐、董慧迎、王建元、高国棉、罗炳成 2008 物理学报 57 541]

    [21]

    ]Liu Y Y,Liu F M,Shi X,Ding P,Zhou C C 2008 Acta Phys. Sin. 57 7275 (in Chinese)[刘妍妍、刘发民、石霞、丁芃、周传仓 2008 物理学报 57 7275]

  • [1]

    [1]Hill N A 2000 J. Phys. Chem.B 104 6694

    [2]

    [2]Zhou J P,Shi Z,Liu G,He H C,Nan C W 2006 Acta Phys. Sin. 55 3766 (in Chinese)[周剑平、施展、刘刚、何泓材、南策文 2006 物理学报 55 3766]

    [3]

    [3]Fillippetti A,Hill N A 2001 J. Magn. Magn. Mater. 236 176

    [4]

    [4]Murashav V A,Rakov D N,Ionov V M,Dubenko I S,Titov 1994 Ferroelectrics 162 11

    [5]

    [5]Fischer P,Polomska M,Sosnowska I,Szymanski M 1980 J. Phys. 13 1931

    [6]

    [6]Ruette B,Zvyagin S,Pyatakov A P,Bush A,Li J F,Belotelov V I,Zvezdin A K,Viehland D 2004 Phys. Rev. B 69 064114

    [7]

    [7]Tang C H,Cai M Q,Yin Z,Zhang M S 2004 Acta Phys. Sin. 53 2931 (in Chinese)[唐春红、蔡孟秋、尹真、张明生 2004 物理学报 53 2931]

    [8]

    [8]Sun Y,Huang Z F,Fan H G,Ming X,Wang C Z,Chen G 2009 Acta Phys. Sin. 58 193 (in Chinese)[孙源、黄祖飞、范厚刚、明星、王春忠、陈岗 2009 物理学报 58 193]

    [9]

    [9]Qi X D,Dho J,Blamire M,Jia Q X,Lee J S,Foltyn S,MacManus-Driscoll J L 2004 J. Magn. Magn. Mater. 283 419

    [10]

    ]Kumar M M,Palkara V R,Srinivas K,Suryanarayana S V 2000 Appl. Phys. Lett. 76 2764

    [11]

    ]Wang Y P,Zhou L,Zhang M F,Chen X Y,Liu J M,Liu Z G 2004 Appl. Phys. Lett. 84 1731

    [12]

    ]Liu H R,Liu Z L,Liu Q,Yao K L 2006 Thin Solid Films. 500 105

    [13]

    ]Epifani M 2007 Mater. Lett. 61 3100

    [14]

    ]Matsui T,Taketani E,Fujimura N,Ito T,Morii K 2003 J. Appl. Phys. 93 6993

    [15]

    ]Taketani E,Matsui T,Fujimura N,Morii K 2004 IEEE Trans. Magn. 40 2736

    [16]

    ]Matsui T,Taketani E,Fujimura N,Tsuda H,Morii K 2005 Appl. Phys. Lett. 86 082902

    [17]

    ]Ren P,Guan J G,Cheng X D 2006 Mater. Chem. Phys. 98 93

    [18]

    ]Zhong C G,Jiang Q,Fang J H,Ge C W 2009 Acta Phys. Sin. 58 3491 (in Chinese)[仲崇贵、蒋青、方靖淮 2009 物理学报 58 3491]

    [19]

    ]Lu Y,Li Q A,Di N L,Cheng S H 2003 Acta. Phys. Sin. 52 1250 (in Chinese)[鲁毅、李庆安 邸乃力、成昭华 2003 物理学报 52 1250]

    [20]

    ]Han L A,Chen Ch L,Dong Y H,Wang J Y,Gao G M,Luo B C 2008 Acta. Phys. Sin. 57 541 (in Chinese)[韩立安、陈长乐、董慧迎、王建元、高国棉、罗炳成 2008 物理学报 57 541]

    [21]

    ]Liu Y Y,Liu F M,Shi X,Ding P,Zhou C C 2008 Acta Phys. Sin. 57 7275 (in Chinese)[刘妍妍、刘发民、石霞、丁芃、周传仓 2008 物理学报 57 7275]

  • [1] 周攀钒, 袁欢, 徐小楠, 鹿轶红, 徐明. 过渡金属与F共掺杂ZnO薄膜结构及磁、光特性. 物理学报, 2015, 64(24): 247503. doi: 10.7498/aps.64.247503
    [2] 杨虹, 齐伟华, 纪登辉, 尚志丰, 张晓云, 徐静, 郎莉莉, 唐贵德. 钙钛矿锰氧化物La2/3Sr1/3FexMn1-xO3的结构与磁性研究. 物理学报, 2014, 63(8): 087503. doi: 10.7498/aps.63.087503
    [3] 齐智坚, 黄维刚. 白光LED用Ca3Si3O9:Dy3+荧光粉的制备及其发光性能. 物理学报, 2013, 62(19): 197801. doi: 10.7498/aps.62.197801
    [4] 张丽, 徐明, 余飞, 袁欢, 马涛. Fe, Co共掺杂ZnO薄膜结构及发光特性研究. 物理学报, 2013, 62(2): 027501. doi: 10.7498/aps.62.027501
    [5] 钟文武, 刘发民, 蔡鲁刚, 丁芃, 柳学全, 李一. Al和Sb共掺对ZnO有序阵列薄膜的结构和光学性能的影响. 物理学报, 2011, 60(11): 118102. doi: 10.7498/aps.60.118102
    [6] 曾乐贵, 刘发民, 钟文武, 丁芃, 蔡鲁刚, 周传仓. Nb/SnO2复合薄膜的制备、结构及光电性能. 物理学报, 2011, 60(3): 038203. doi: 10.7498/aps.60.038203
    [7] 王兴军, 董斌, 周治平. Er硅酸盐化合物薄膜的相转变和光致发光特性研究. 物理学报, 2010, 59(5): 3554-3557. doi: 10.7498/aps.59.3554
    [8] 彭英才, 范志东, 白振华, 马蕾. Si纳米线的固-液-固可控生长及其形成机理分析. 物理学报, 2010, 59(2): 1169-1174. doi: 10.7498/aps.59.1169
    [9] 刘吉地, 王育华. Mg2+掺杂Zn2SiO4:Mn2+的溶胶-凝胶法合成及真空紫外发光特性研究. 物理学报, 2010, 59(5): 3558-3563. doi: 10.7498/aps.59.3558
    [10] 胡林华, 戴俊, 刘伟庆, 王孔嘉, 戴松元. 锐钛矿相纳米TiO2晶体生长动力学及生长过程控制. 物理学报, 2009, 58(2): 1115-1119. doi: 10.7498/aps.58.1115
    [11] 罗炳成, 周超超, 陈长乐, 金克新. 单相Bi0.9Ba0.1Fe0.85Mn0.15O3陶瓷中的多铁性. 物理学报, 2009, 58(7): 4563-4566. doi: 10.7498/aps.58.4563
    [12] 武祥, 蔡伟, 曲凤玉. ZnO一维纳米结构的形貌调控与亲疏水性研究. 物理学报, 2009, 58(11): 8044-8049. doi: 10.7498/aps.58.8044
    [13] 向卫东, 唐珊珊, 张希艳, 杨昕宇, 张延华. 溶胶-凝胶法制备PbS量子点玻璃的研究. 物理学报, 2008, 57(7): 4607-4612. doi: 10.7498/aps.57.4607
    [14] 秦玉香, 胡 明. 钛碳化物改性碳纳米管的场发射性能. 物理学报, 2008, 57(6): 3698-3702. doi: 10.7498/aps.57.3698
    [15] 刘妍妍, 刘发民, 石 霞, 丁 芃, 周传仓. 钙钛矿型纳米BaFeO3的制备、结构表征及铁磁性研究. 物理学报, 2008, 57(11): 7274-7278. doi: 10.7498/aps.57.7274
    [16] 麻华丽, 李英兰, 杨保华, 王 锋. C60-聚甲基丙烯酸甲脂复合膜的结构、光学和电荷转移特性. 物理学报, 2005, 54(6): 2859-2862. doi: 10.7498/aps.54.2859
    [17] 胡林华, 戴松元, 王孔嘉. 纳米TiO2多孔膜的微结构对染料敏化纳米薄膜太阳电池性能的影响. 物理学报, 2005, 54(4): 1914-1918. doi: 10.7498/aps.54.1914
    [18] 贾建峰, 黄 凯, 潘清涛, 贺德衍. 溶胶-凝胶法制备(Ba0.7Sr0.3)TiO3/LaNiO3异质薄膜及其结构和介电性质研究. 物理学报, 2005, 54(9): 4406-4410. doi: 10.7498/aps.54.4406
    [19] 王 强, 沈明荣, 侯 芳, 甘肇强. 烘烤温度对溶胶-凝胶法制备镧掺杂钛酸铋薄膜结构与铁电性质的影响. 物理学报, 2004, 53(7): 2373-2377. doi: 10.7498/aps.53.2373
    [20] 徐润, 沈明荣, 葛水兵. 溶胶-凝胶法制备BaTiO3/SrTiO3多层膜的介电增强效应. 物理学报, 2002, 51(5): 1139-1143. doi: 10.7498/aps.51.1139
计量
  • 文章访问数:  7809
  • PDF下载量:  1729
  • 被引次数: 0
出版历程
  • 收稿日期:  2009-06-07
  • 修回日期:  2009-06-28
  • 刊出日期:  2010-03-15

/

返回文章
返回