非故意掺杂4H-SiC外延材料本征缺陷的热稳定性

程萍 张玉明 张义门 王悦湖 郭辉

引用本文:
Citation:

非故意掺杂4H-SiC外延材料本征缺陷的热稳定性

程萍, 张玉明, 张义门, 王悦湖, 郭辉

Stability of the intrinsic defects in unintentionally doped 4H-SiC epitaxial layer

Cheng Ping, Zhang Yu-Ming, Zhang Yi-Men, Wang Yue-Hu, Guo Hui
PDF
导出引用
  • 采用电子顺磁共振(ESR)和低温光致发光(PL)技术,研究了退火温度对低压化学气相沉积法(LPCVD)制备的非故意掺杂 4H-SiC材料中本征缺陷稳定性的影响.结果发现,当退火时间为10 min和30 min时,本征缺陷浓度均随着退火温度的升高而增大,当退火温度达到1573 K时材料中本征缺陷浓度达到最大,继续升高退火温度将使材料中本征缺陷浓度迅速降低.退火温度对材料中本征缺陷的影响主要是由于退火中本征缺陷的稳定化过程及本征缺陷之间发生强烈的相互作用引起的.
    The effects of high temperature annealing on the stability of the intrinsic defects in unintentionally doped epitaxial 4H-SiC prepared by low pressure chemical vapor deposition (LPCVD) are studied by electron spin resonance (ESR) and low-temperature photoluminescence (PL). The results showed that the concentration of intrinsic defects increases with increasing annealing temperature and reaches its maximum at 1573 K, then decreases with the gradually increasing annealing temperature when annealing time is 10 min or 30 min. The annealing temperature has an important effect on the concentration of intrinsic defects in epitaxial semi-insulating 4H-SiC prepared by LPCVD, whics is attributed to the process of intrinsic defects being stabilized and the strong interaction between the intrinsic defects during annealing.
    • 基金项目: 国家自然科学基金(批准号:60876061), 预研基金(批准号:9140A08050508),和陕西13115创新工程(批准号:2008ZDKG-30)资助的课题.
    [1]

    [1]Sriram S, Ward A, Henning J, Allen S T 2005 MRS Bull. 30 308

    [2]

    [2]Waldrop J R, Grant R W, Wang Y C, Davies R F 1992 J. Appl. Phys. 72 4757

    [3]

    [3]Cochran C J, Lenahan P M 2007 Appl. Phys. Lett. 90 123501

    [4]

    [4]Jenny J R, Müller St G, Powell A, Tsvetkov V F, Hobgood H M, Glass R C, Carter C H 2002 J. Electron. Mater. 31 366

    [5]

    [5]Ellison, Magnusson B, Hemmingsson C, Magnusson W, Iakimov T, Storasta L, Henry A, Henelius N H, Janzén E 2001 Mater. Res. Soc. Symp. Proc. 640 H1.21.1

    [6]

    [6]Son N T, Carlsson P, Gllstrm A, Magnusson B, Janzén E 2007 Physica B 401 67

    [7]

    [7]Janzén E, Son NT, Magnusson B, Ellison A 2006 Microelectronic Engineering 83 130

    [8]

    [8]Carlos W E, Garces N Y, Glaser E R 2006 Phys. Rev. B 74 235201

    [9]

    [9]Son N T, Magnusson B, Zolnai Z, Ellison A, Janzeén E 2004 Mater.Sci. Forum 457-460 437

    [10]

    ]Alfieri G, Kimoto T 2007 J. Phys. Condens. Matter 19 306204

    [11]

    ]Cheng P, Zhang Y M, Guo H, Zhang Y M,Liao Y L 2009 Acta Phys . Sin 58 4214 (in Chinese) [程萍、张玉明、郭辉、张义门、廖宇龙 2009 物理学报 58 4214]

    [12]

    ]Korsunska N E, Tarasov I, Kushnirenks V, Ostapenko S 2004 Semicond, Sci. Technol. 19 833

    [13]

    ]Lauer V 1999 Mater. Sci. Eng. B 61-62 248

    [14]

    ]Ivanov V Y 2008 Opt. Mater. 30 748

    [15]

    ]Jia R X, Zhang Y M, Zhang Y M, Guo H, Luan S Z 2008 Acta Phys. Sin. 57 4457(in Chinese) [贾仁需、张义门、张玉明、郭辉、栾苏珍 2008 物理学报 57 4457]

    [16]

    ]Carlos W E, Glaser E R, Shanabrook B V 2003 Physica B 151 340

    [17]

    ]Michel Bockstedte, Adam Gali, Alexander Mattausch, Pankratov O, Steeds J W 2008 J. Phys. Stat. Sol. B 7 1281

  • [1]

    [1]Sriram S, Ward A, Henning J, Allen S T 2005 MRS Bull. 30 308

    [2]

    [2]Waldrop J R, Grant R W, Wang Y C, Davies R F 1992 J. Appl. Phys. 72 4757

    [3]

    [3]Cochran C J, Lenahan P M 2007 Appl. Phys. Lett. 90 123501

    [4]

    [4]Jenny J R, Müller St G, Powell A, Tsvetkov V F, Hobgood H M, Glass R C, Carter C H 2002 J. Electron. Mater. 31 366

    [5]

    [5]Ellison, Magnusson B, Hemmingsson C, Magnusson W, Iakimov T, Storasta L, Henry A, Henelius N H, Janzén E 2001 Mater. Res. Soc. Symp. Proc. 640 H1.21.1

    [6]

    [6]Son N T, Carlsson P, Gllstrm A, Magnusson B, Janzén E 2007 Physica B 401 67

    [7]

    [7]Janzén E, Son NT, Magnusson B, Ellison A 2006 Microelectronic Engineering 83 130

    [8]

    [8]Carlos W E, Garces N Y, Glaser E R 2006 Phys. Rev. B 74 235201

    [9]

    [9]Son N T, Magnusson B, Zolnai Z, Ellison A, Janzeén E 2004 Mater.Sci. Forum 457-460 437

    [10]

    ]Alfieri G, Kimoto T 2007 J. Phys. Condens. Matter 19 306204

    [11]

    ]Cheng P, Zhang Y M, Guo H, Zhang Y M,Liao Y L 2009 Acta Phys . Sin 58 4214 (in Chinese) [程萍、张玉明、郭辉、张义门、廖宇龙 2009 物理学报 58 4214]

    [12]

    ]Korsunska N E, Tarasov I, Kushnirenks V, Ostapenko S 2004 Semicond, Sci. Technol. 19 833

    [13]

    ]Lauer V 1999 Mater. Sci. Eng. B 61-62 248

    [14]

    ]Ivanov V Y 2008 Opt. Mater. 30 748

    [15]

    ]Jia R X, Zhang Y M, Zhang Y M, Guo H, Luan S Z 2008 Acta Phys. Sin. 57 4457(in Chinese) [贾仁需、张义门、张玉明、郭辉、栾苏珍 2008 物理学报 57 4457]

    [16]

    ]Carlos W E, Glaser E R, Shanabrook B V 2003 Physica B 151 340

    [17]

    ]Michel Bockstedte, Adam Gali, Alexander Mattausch, Pankratov O, Steeds J W 2008 J. Phys. Stat. Sol. B 7 1281

  • [1] 徐思源, 张召富, 王俊, 刘雪飞, 郭宇铮. MoSi2N4的本征点缺陷以及掺杂特性的第一性原理计算研究. 物理学报, 2024, 0(0): 0-0. doi: 10.7498/aps.73.20231931
    [2] 王凯悦, 郭睿昂, 王宏兴. 金刚石氮-空位缺陷发光的温度依赖性. 物理学报, 2020, 69(12): 127802. doi: 10.7498/aps.69.20200395
    [3] 李香草, 刘宝安, 李猛, 闫春燕, 任杰, 刘畅, 巨新. 用光致发光研究不同通量辐照磷酸二氢钾晶体的缺陷. 物理学报, 2020, 69(17): 174208. doi: 10.7498/aps.69.20200482
    [4] 王强, 杨立学, 刘北云, 闫胤洲, 陈飞, 蒋毅坚. 本征富受主型ZnO微米管光致发光的温度调控机制. 物理学报, 2020, 69(19): 197701. doi: 10.7498/aps.69.20200655
    [5] 刘汝霖, 方粮, 郝跃, 池雅庆. 金红石TiO2中本征缺陷扩散性质的第一性原理计算. 物理学报, 2018, 67(17): 176101. doi: 10.7498/aps.67.20180818
    [6] 林俏露, 李公平, 许楠楠, 刘欢, 王苍龙. 金红石TiO2本征缺陷磁性的第一性原理计算. 物理学报, 2017, 66(3): 037101. doi: 10.7498/aps.66.037101
    [7] 张秀芝, 王凯悦, 李志宏, 朱玉梅, 田玉明, 柴跃生. 氮对金刚石缺陷发光的影响. 物理学报, 2015, 64(24): 247802. doi: 10.7498/aps.64.247802
    [8] 武志燕, 邝小渝, 李辉, 毛爱杰, 王振华. 蓝宝石(α-Al2O3:Fe3+)体系基态分裂与局域晶格畸变的研究. 物理学报, 2014, 63(1): 017102. doi: 10.7498/aps.63.017102
    [9] 王健, 谢自力, 张荣, 张韵, 刘斌, 陈鹏, 韩平. InN的光致发光特性研究. 物理学报, 2013, 62(11): 117802. doi: 10.7498/aps.62.117802
    [10] 彭丽萍, 夏正才, 尹建武. 金红石相和锐钛矿相TiO2本征缺陷的第一性原理计算. 物理学报, 2012, 61(3): 037103. doi: 10.7498/aps.61.037103
    [11] 王凯悦, 李志宏, 高凯, 朱玉梅. 电子辐照金刚石的光致发光研究. 物理学报, 2012, 61(9): 097803. doi: 10.7498/aps.61.097803
    [12] 任艳东, 吕树臣. 发光二极管用SrWO4:Eu3+红光荧光粉激发谱强度的调控. 物理学报, 2011, 60(8): 087804. doi: 10.7498/aps.60.087804
    [13] 李卓昕, 王丹妮, 王宝义, 薛德胜, 魏龙, 秦秀波. 水蒸气退火多孔硅发光性能的正电子谱学研究. 物理学报, 2010, 59(12): 8915-8919. doi: 10.7498/aps.59.8915
    [14] 黎兵, 刘才, 冯良桓, 张静全, 郑家贵, 蔡亚平, 蔡伟, 武莉莉, 李卫, 雷智, 曾广根, 夏庚培. CdS/CdTe薄膜太阳电池的深能级瞬态谱和光致发光研究. 物理学报, 2009, 58(3): 1987-1991. doi: 10.7498/aps.58.1987
    [15] 程萍, 张玉明, 郭辉, 张义门, 廖宇龙. LPCVD法制备的高纯半绝缘4H-SiC晶体ESR谱特性. 物理学报, 2009, 58(6): 4214-4218. doi: 10.7498/aps.58.4214
    [16] 成鹏飞, 李盛涛, 李建英. ZnO压敏陶瓷介电损耗的温度谱研究. 物理学报, 2009, 58(8): 5721-5725. doi: 10.7498/aps.58.5721
    [17] 李盛涛, 成鹏飞, 赵雷, 李建英. ZnO压敏陶瓷中缺陷的介电谱研究. 物理学报, 2009, 58(1): 523-528. doi: 10.7498/aps.58.523
    [18] 孙成伟, 刘志文, 张庆瑜. 退火温度对ZnO薄膜结构和发光特性的影响. 物理学报, 2006, 55(1): 430-436. doi: 10.7498/aps.55.430
    [19] 王 森, 俞国军, 巩金龙, 朱德彰, 何绥霞, 朱志远, 徐洪杰. 碳纳米管的氧化铝模板法合成及其退火效应研究. 物理学报, 2005, 54(10): 4949-4954. doi: 10.7498/aps.54.4949
    [20] 方泽波, 龚恒翔, 刘雪芹, 徐大印, 黄春明, 王印月. 退火对多晶ZnO薄膜结构与发光特性的影响. 物理学报, 2003, 52(7): 1748-1751. doi: 10.7498/aps.52.1748
计量
  • 文章访问数:  7016
  • PDF下载量:  650
  • 被引次数: 0
出版历程
  • 收稿日期:  2009-07-26
  • 修回日期:  2009-09-09
  • 刊出日期:  2010-05-15

/

返回文章
返回