超声强化合成MgFe2O4纳米颗粒及其机理研究

徐波; 王树林; 李生娟; 李来强

doi:10.7498/aps.61.030703

摘要

用超声水解方法制备MgO纳米颗粒,用化学沉淀法制备-Fe2O3纳米颗粒,将MgO/-Fe2O3混合体常温下超声活化2h,400℃固相合成制备出MgFe2O4纳米颗粒.通过X射线衍射和透射电子显微镜测试产品的化学成分、晶体结构和形貌尺寸,分析声化学反应机理及其影响因素.研究结果表明:所制备的MgFe2O4为尖晶石铁氧体,颗粒尺寸分布在2030nm之间,粒度分布均匀;超声空化效应提高了化学反应活性、增加反应物的比表面积和反应物之间的接触面积,促进固相合成反应速度,降低反应温度,实现了一般条件下难以完成的化学反应.

关键词:

Abstract

MgO nano-particles are prepared by ultrasonic cavitate, and-Fe2O3 nano-particles are prepared by chemical precipitation method, then MgO and-Fe2O3 are mixed in a beaker. After the ultrasonic dispersion for 2 h, MgO/-Fe2O3 admixture is calcined at 400℃ to synthesize MgFe2O4 nano-particles. TEM and XRD tests show that MgFe2O4 takes on a spinel structure and the particles sizes range from 20 to 30 nm. The theoretieal analysis indicates that the ultrasonic cavitate effect enhances the reaction activity of raw material, augmentes specific surface area and the contact area of reactant, which can promote reaction rate, reduce reaction temperature, and make possible the chemical reaction that is difficult to complete in common condition.

Keywords:

作者及机构信息

1.
上海理工大学能源与动力工程学院, 上海 200093;

2.
上海理工大学材料科学与工程学院, 上海 200093

基金项目: 上海市科委纳米专项(批准号: 1052nm02900)和上海理工大学博士启动费(批准号: 1D-11-301-002)资助的课题.

Authors and contacts

1.
College of Energy and Power Engineering, University of Shanghai for Science and Technology, Shanghai 200093, China;

2.
College of Material Science and Engineering, University of Shanghai for Science and Technology, Shanghai 200093, China

Funds: Project supported by the Shanghai Committee of Science and Technology, China (Grant No. 1052nm02900) and the University of Shanghai for Science and Technology, China (Grant No. 1D-11-301-002).

参考文献

[1]	Suslick K S 1990 Science 247 1144
[2]	Mason T J 1994 Chemical Industry 1 46
[3]	Tamura S, Tsunekawa Y, Okumiya M, Hatakeyama M 2008 J.Mater. Proces. Technol. 206 322
[4]	Wang X K, Yao Z Y, Wang J G, Guo W L, Li G Q 2008 Ultrason.Sonochem. 15 43
[5]	Lu Y G, Wu X H 2011 Acta Phys. Sin. 60 046202 (in Chinese) [卢义刚, 吴雄慧 2011 物理学报 60 046202]
[6]	Azhari A, Sharifsh M, Golestanifard F, Saberi A 2010 Mater.Chem. Phys. 124 658
[7]	Sivakumar N, Narayanasamy A, Greneche J M, Murugarajc R, LeeY S 2010 J. Alloys and Compounds 504 395
[8]	Ma Q, Jiang J J, Bie S W, Du G, Feng Z K, He H H 2008 ActaPhys. Sin. 57 6577 (in Chinese) [马强, 江建军, 别少伟, 杜刚, 冯则坤, 何华辉 2008 物理学报 57 6577]
[9]	Chen Z Q, Li F, Li Q 2006 Chin. Phys. 15 1075
[10]	Konishi M, Suda N, Kurihara S 1993 Biophys. J. 64 223
[11]	Hoffmann M R, Hua I, Hochemer R 1996 Ultrason. Sonochem. 3163
[12]	Suslick K S, Neis U 1989 Scientific American 43 80
[13]	Bogdan N 2007 Ultrason. Sonochemi. 14 13
[14]	Wang P H 2003 J. Hebei Institute of Technology 14 13 (in Chinese) [王萍辉 2003 河北理工学院学报 25 154]
[15]	Edward B 1991 Science 253 1397
[16]	Dalt S D, Takimi A S, Volkmer T M, Sousa V C, Bergmann C P2011 Powder Technology 210 103
[17]	Hong X G, Du L C, Ye M P, Wong Y X 2004 Chin. Phys. 13 720
[18]	Yuan Y H, Hou X, Gao H 2006 Acta Phys. Sin. 55 446 (in Chinese) [袁艳红, 侯洵, 高恒 2006 物理学报 55 446]

施引文献

[1]	Suslick K S 1990 Science 247 1144
[2]	Mason T J 1994 Chemical Industry 1 46
[3]	Tamura S, Tsunekawa Y, Okumiya M, Hatakeyama M 2008 J.Mater. Proces. Technol. 206 322
[4]	Wang X K, Yao Z Y, Wang J G, Guo W L, Li G Q 2008 Ultrason.Sonochem. 15 43
[5]	Lu Y G, Wu X H 2011 Acta Phys. Sin. 60 046202 (in Chinese) [卢义刚, 吴雄慧 2011 物理学报 60 046202]
[6]	Azhari A, Sharifsh M, Golestanifard F, Saberi A 2010 Mater.Chem. Phys. 124 658
[7]	Sivakumar N, Narayanasamy A, Greneche J M, Murugarajc R, LeeY S 2010 J. Alloys and Compounds 504 395
[8]	Ma Q, Jiang J J, Bie S W, Du G, Feng Z K, He H H 2008 ActaPhys. Sin. 57 6577 (in Chinese) [马强, 江建军, 别少伟, 杜刚, 冯则坤, 何华辉 2008 物理学报 57 6577]
[9]	Chen Z Q, Li F, Li Q 2006 Chin. Phys. 15 1075
[10]	Konishi M, Suda N, Kurihara S 1993 Biophys. J. 64 223
[11]	Hoffmann M R, Hua I, Hochemer R 1996 Ultrason. Sonochem. 3163
[12]	Suslick K S, Neis U 1989 Scientific American 43 80
[13]	Bogdan N 2007 Ultrason. Sonochemi. 14 13
[14]	Wang P H 2003 J. Hebei Institute of Technology 14 13 (in Chinese) [王萍辉 2003 河北理工学院学报 25 154]
[15]	Edward B 1991 Science 253 1397
[16]	Dalt S D, Takimi A S, Volkmer T M, Sousa V C, Bergmann C P2011 Powder Technology 210 103
[17]	Hong X G, Du L C, Ye M P, Wong Y X 2004 Chin. Phys. 13 720
[18]	Yuan Y H, Hou X, Gao H 2006 Acta Phys. Sin. 55 446 (in Chinese) [袁艳红, 侯洵, 高恒 2006 物理学报 55 446]

[1]	刘旺旺, 张克学, 王军, 夏国栋. 过渡区内纳米颗粒的曳力特性模拟研究. 物理学报, 2024, 73(7): 075101. doi: 10.7498/aps.73.20231861
[2]	雷照康, 武耀蓉, 黄晨阳, 莫润阳, 沈壮志, 王成会, 郭建中, 林书玉. 驻波场中环状空化泡聚集结构的稳定性分析. 物理学报, 2024, 73(8): 084301. doi: 10.7498/aps.73.20231956
[3]	许龙, 汪尧. 双泡耦合声空化动力学过程模拟. 物理学报, 2023, 72(2): 024303. doi: 10.7498/aps.72.20221571
[4]	马奥杰, 陈颂佳, 李玉秀, 陈颖. 纳米颗粒布朗扩散边界条件的分子动力学模拟. 物理学报, 2021, 70(14): 148201. doi: 10.7498/aps.70.20202240
[5]	崔杰, 苏俊杰, 王军, 夏国栋, 李志刚. 自由分子区内纳米颗粒的热泳力计算. 物理学报, 2021, 70(5): 055101. doi: 10.7498/aps.70.20201629
[6]	黄丛亮, 冯妍卉, 张欣欣, 李静, 王戈, 侴爱辉. 金属纳米颗粒的热导率. 物理学报, 2013, 62(2): 026501. doi: 10.7498/aps.62.026501
[7]	胡静, 林书玉, 王成会, 李锦. 超声波作用下泡群的共振声响应. 物理学报, 2013, 62(13): 134303. doi: 10.7498/aps.62.134303
[8]	黄小林, 侯丽珍, 喻博闻, 陈国良, 王世良, 马亮, 刘新利, 贺跃辉. Cu/C核/壳纳米结构的气相合成、形成机理及其光学性能研究. 物理学报, 2013, 62(10): 108102. doi: 10.7498/aps.62.108102
[9]	王新亮, 狄勤丰, 张任良, 丁伟朋, 龚玮, 程毅翀. 纳米颗粒吸附岩心表面的强疏水特征. 物理学报, 2012, 61(21): 216801. doi: 10.7498/aps.61.216801
[10]	陈慧敏, 刘恩隆. 纳米颗粒与纳米块材摩尔定压热容的理论计算. 物理学报, 2011, 60(6): 066501. doi: 10.7498/aps.60.066501
[11]	卢义刚, 吴雄慧. 双泡超声空化计算分析. 物理学报, 2011, 60(4): 046202. doi: 10.7498/aps.60.046202
[12]	臧渡洋, 张永建, Langevin Dominique. SiO2纳米颗粒单层膜流变特性的双Wilhelmy片法研究. 物理学报, 2011, 60(7): 076801. doi: 10.7498/aps.60.076801
[13]	刘演华, 干富军, 张凯. 平面射流场中纳米颗粒的成核与凝并. 物理学报, 2010, 59(6): 4084-4092. doi: 10.7498/aps.59.4084
[14]	林涛, 万能, 韩敏, 徐骏, 陈坤基. SnO2纳米晶体的制备、结构与发光性质. 物理学报, 2009, 58(8): 5821-5825. doi: 10.7498/aps.58.5821
[15]	孟利军, 张凯旺, 钟建新. 硅纳米颗粒在碳纳米管表面生长的分子动力学模拟. 物理学报, 2007, 56(2): 1009-1013. doi: 10.7498/aps.56.1009
[16]	李晖, 谢二庆, 张洪亮, 潘孝军, 张永哲. 火焰喷雾法合成ZnO和MgxZn1－xO纳米颗粒的光学性能研究. 物理学报, 2007, 56(6): 3584-3588. doi: 10.7498/aps.56.3584
[17]	刘锦宏, 张凌飞, 田庚方, 李济晨, 李发伸. 低温固相反应法制备的NiFe2O4纳米颗粒的结构与磁性. 物理学报, 2007, 56(10): 6050-6055. doi: 10.7498/aps.56.6050
[18]	陈谦, 邹欣晔, 程建春. 超声波声孔效应中气泡动力学的研究. 物理学报, 2006, 55(12): 6476-6481. doi: 10.7498/aps.55.6476
[19]	王丽, 王海波, 王涛, 李发伸. CoFe2O4纳米颗粒的结构、磁性以及离子迁移. 物理学报, 2006, 55(12): 6515-6521. doi: 10.7498/aps.55.6515
[20]	刘向绯, 蒋昌忠, 任峰, 付强. Ag离子注入非晶SiO2的光学吸收、拉曼谱和透射电镜研究. 物理学报, 2005, 54(10): 4633-4637. doi: 10.7498/aps.54.4633

计量

文章访问数: 12334
PDF下载量: 644
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板