高压处理对Cu75.15Al24.85合金组织与电阻率的影响

谌岩 刘琳 刘建华 张瑞军

引用本文:
Citation:

高压处理对Cu75.15Al24.85合金组织与电阻率的影响

谌岩, 刘琳, 刘建华, 张瑞军

Effect of high pressure treatment on microstructure and resistivity of Cu75.15Al24.85 alloy

Chen Yan, Liu Lin, Liu Jian-Hua, Zhang Rui-Jun
PDF
导出引用
  • 本文借助金相显微镜, XRD, SEM和DSC等手段对Cu75.15Al24.85合金经15 GPa压力, 750℃保温15 min处理前后的组织结构进行了分析,并用电阻率测试仪对合金的 电阻率进行测试,以此探讨了高压处理对Cu75.15Al24.85合金组织与电阻率的影响. 结果表明:高压处理能细化Cu75.15Al24.85合金的组织,增大合金的电阻率, 当压力为3 GPa时,该合金获得的组织最细小,电阻率最大.
    The microstructures of Cu75.15Al24.85 alloy before and after treatment at 15 GPa pressure and 750℃ for 15 min are analyzed by optical metallograph, X-ray diffraction, scanning electron microscopy and differential scanning calorimeter, and its resistivity is also obtained through resistivity measuring instrument. According to the obtained results, the effects of high pressure treatment on the microstructure and resistivity are investigated. The results show that high pressure treatment can refine the microstructure, and increase the resistivity of the alloy. When the pressure is 3 GPa, the refinement is more remarkable and the resistivity reaches a maximal value.
    • 基金项目: 河北省留学回国人员科研启动基金资助的课题.
    • Funds: Project supported by the Scientific Research Foundation for the Returned Overseas Chinese Scholars of Hebei Province.
    [1]

    Mu S G, Guo F A, Tang Y Q 2008 Materials Science and Engineering A 475 235

    [2]

    Zhang R J, Ren Y J, He M 2008 Journal of Materials Science and Engineering 2 31

    [3]

    Izadinia M, Dehghani K 2011 Transactions of Nonferrous Metals Society of China (English Edition) 21 2037

    [4]

    Yu F X, Cheng J Y, Ao X W 2011 Rare Metals 30 539

    [5]

    Wang M G, Zhao H Y, Ren J N, Mu Y Q, Wang W, Yang W M, Li A H, Ge H H, Hou H 2011 Acta Phys. Sin. 60 040507 (in Chinese) [王明光, 赵宇宏, 任娟娜, 穆彦青, 王伟, 杨伟明, 李爱红, 葛洪浩, 侯华 2011 物理学报 60 040507]

    [6]

    Xu J F, Fan Y F, Chen W, Zhai Q Y 2009 Acta Phys. Sin. 58 0644 (in Chinese) [徐锦锋, 范于芳, 陈娓, 翟秋亚 2009 物理学报 58 0644]

    [7]

    Yan N, Wang W L, Dai F P, Wei B B 2011 Acta Phys. Sin. 60 036402 (in Chinese) [闫娜, 王伟丽, 代富平, 魏炳波 2011 物理学报 60 036402]

    [8]

    Chen D N, Fan C L, Hu J W, Tan H, Wang H R, Wu S X and Yu Y Y 2009 Acta Phys. Sin. 58 2612 (in Chinese) [陈大年, 范春雷, 胡金伟, 吴善幸, 王焕然, 谭华, 俞宇颖 2009 物理学报 58 2612]

    [9]

    Wang H Y, Liu R P, Ma M Z, Gao M, Yao Y S, Wang W K 2004 Acta Phys. Sin. 53 2378 (in Chinese) [王海燕, 刘日平, 马明臻, 高明, 姚玉书, 王文魁 2004 物理学报 53 2378]

    [10]

    Wang H Y, Liu J H, Peng G R, Wang W K 2010 Chin. Phys. B 19 096203

    [11]

    Zhu R J, Xu W T, Yi L, Hao J S 2008 Chin. Phys. B 17 1088

    [12]

    Zhao J, Liu L, Yang J R 2008 Rare Metals 27 541

    [13]

    Wang H Y, Chen Y, Liu Y W 2009 Chin. Phys. Lett. 26 106201

    [14]

    Chen Y, Liu L, Wang Y H, Liu J H 2011 Trans. Nonferrous Met. Soc. China (English Edition) 21 2205

    [15]

    Wang Z T 2005 Copper Alloy and it's Processing Handbook (Changsha: Central South University press) p5 (in Chinese) [王祝堂 2005 铜合金及其加工手册 (长沙:中南大学出版社) 第5页]

    [16]

    Cui K 1986 Metallic and Nonferrous Metals Materials (Beijing: Mechanical Industry Press) p425 (in Chinese) [崔崑 1986 钢铁材料及有色金属材料 (北京: 机械工业出版社) 第425页]

    [17]

    Porter D, Easterling K 1981 Phase Transformation in Metals and Alloys (New York: Van Nostrand Reinhold Company) p263

    [18]

    Wang Z L, Wang H W, Wei Z J 2007 Transactions of Nonferrous Metals Society of China 17 384 (in Chinese) [王振玲, 王宏伟, 魏尊杰 2007 中国有色金属学报 17 384]

    [19]

    Song W, Guo J, Liu J H 2007 Journal of Materials Science and Engineering 1 55

    [20]

    Li Q R 2005 Journal of rare earths 23 437

    [21]

    Li C 1996 Principles of Metallography (Harbin: Harbin Institute of Technology Press) p278 (in Chinese) [李超 1996 金属学原理 (哈尔滨: 哈尔滨工业大学出版社) 第278页]

  • [1]

    Mu S G, Guo F A, Tang Y Q 2008 Materials Science and Engineering A 475 235

    [2]

    Zhang R J, Ren Y J, He M 2008 Journal of Materials Science and Engineering 2 31

    [3]

    Izadinia M, Dehghani K 2011 Transactions of Nonferrous Metals Society of China (English Edition) 21 2037

    [4]

    Yu F X, Cheng J Y, Ao X W 2011 Rare Metals 30 539

    [5]

    Wang M G, Zhao H Y, Ren J N, Mu Y Q, Wang W, Yang W M, Li A H, Ge H H, Hou H 2011 Acta Phys. Sin. 60 040507 (in Chinese) [王明光, 赵宇宏, 任娟娜, 穆彦青, 王伟, 杨伟明, 李爱红, 葛洪浩, 侯华 2011 物理学报 60 040507]

    [6]

    Xu J F, Fan Y F, Chen W, Zhai Q Y 2009 Acta Phys. Sin. 58 0644 (in Chinese) [徐锦锋, 范于芳, 陈娓, 翟秋亚 2009 物理学报 58 0644]

    [7]

    Yan N, Wang W L, Dai F P, Wei B B 2011 Acta Phys. Sin. 60 036402 (in Chinese) [闫娜, 王伟丽, 代富平, 魏炳波 2011 物理学报 60 036402]

    [8]

    Chen D N, Fan C L, Hu J W, Tan H, Wang H R, Wu S X and Yu Y Y 2009 Acta Phys. Sin. 58 2612 (in Chinese) [陈大年, 范春雷, 胡金伟, 吴善幸, 王焕然, 谭华, 俞宇颖 2009 物理学报 58 2612]

    [9]

    Wang H Y, Liu R P, Ma M Z, Gao M, Yao Y S, Wang W K 2004 Acta Phys. Sin. 53 2378 (in Chinese) [王海燕, 刘日平, 马明臻, 高明, 姚玉书, 王文魁 2004 物理学报 53 2378]

    [10]

    Wang H Y, Liu J H, Peng G R, Wang W K 2010 Chin. Phys. B 19 096203

    [11]

    Zhu R J, Xu W T, Yi L, Hao J S 2008 Chin. Phys. B 17 1088

    [12]

    Zhao J, Liu L, Yang J R 2008 Rare Metals 27 541

    [13]

    Wang H Y, Chen Y, Liu Y W 2009 Chin. Phys. Lett. 26 106201

    [14]

    Chen Y, Liu L, Wang Y H, Liu J H 2011 Trans. Nonferrous Met. Soc. China (English Edition) 21 2205

    [15]

    Wang Z T 2005 Copper Alloy and it's Processing Handbook (Changsha: Central South University press) p5 (in Chinese) [王祝堂 2005 铜合金及其加工手册 (长沙:中南大学出版社) 第5页]

    [16]

    Cui K 1986 Metallic and Nonferrous Metals Materials (Beijing: Mechanical Industry Press) p425 (in Chinese) [崔崑 1986 钢铁材料及有色金属材料 (北京: 机械工业出版社) 第425页]

    [17]

    Porter D, Easterling K 1981 Phase Transformation in Metals and Alloys (New York: Van Nostrand Reinhold Company) p263

    [18]

    Wang Z L, Wang H W, Wei Z J 2007 Transactions of Nonferrous Metals Society of China 17 384 (in Chinese) [王振玲, 王宏伟, 魏尊杰 2007 中国有色金属学报 17 384]

    [19]

    Song W, Guo J, Liu J H 2007 Journal of Materials Science and Engineering 1 55

    [20]

    Li Q R 2005 Journal of rare earths 23 437

    [21]

    Li C 1996 Principles of Metallography (Harbin: Harbin Institute of Technology Press) p278 (in Chinese) [李超 1996 金属学原理 (哈尔滨: 哈尔滨工业大学出版社) 第278页]

  • [1] 李鸿明, 董闯, 王清, 李晓娜, 赵亚军, 周大雨. 电阻率与强度性能的关联及铜合金性能分区. 物理学报, 2019, 68(1): 016101. doi: 10.7498/aps.68.20181498
    [2] 伍友成, 刘高旻, 戴文峰, 高志鹏, 贺红亮, 郝世荣, 邓建军. 冲击波作用下Pb(Zr0.95Ti0.05)O3铁电陶瓷去极化后电阻率动态特性. 物理学报, 2017, 66(4): 047201. doi: 10.7498/aps.66.047201
    [3] 李蕊, 左小伟, 王恩刚. 时效Ag-7wt.%Cu合金的微观组织、电阻率和硬度. 物理学报, 2017, 66(2): 027401. doi: 10.7498/aps.66.027401
    [4] 王天天, 葛昌纯, 贾崇林, 汪杰, 谷天赋, 吴海新. 喷射成形粉末高温合金FGH4095M的制备及组织特征. 物理学报, 2015, 64(10): 106103. doi: 10.7498/aps.64.106103
    [5] 刘雅洁. 直接利用磁场和温度精确确定磁性材料La0.67Ca0.33MnO3和Pr0.7Sr0.3MnO3的电阻率. 物理学报, 2013, 62(1): 017601. doi: 10.7498/aps.62.017601
    [6] 周鹏力, 史茹倩, 何静芳, 郑树凯. B-Al共掺杂3C-SiC的第一性原理研究. 物理学报, 2013, 62(23): 233101. doi: 10.7498/aps.62.233101
    [7] 吴宝嘉, 李燕, 彭刚, 高春晓. InSe的高压电输运性质研究. 物理学报, 2013, 62(14): 140702. doi: 10.7498/aps.62.140702
    [8] 罗晓东, 狄国庆. 溅射制备Ge,Nb共掺杂窄光学带隙和低电阻率的TiO2薄膜. 物理学报, 2012, 61(20): 206803. doi: 10.7498/aps.61.206803
    [9] 谌岩, 李雅莉, 刘建华, 张瑞军. 4 GPa压力处理对T8钢在加热过程中固态相变动力学的影响. 物理学报, 2012, 61(19): 196203. doi: 10.7498/aps.61.196203
    [10] 徐锦锋, 范于芳, 陈娓, 翟秋亚. 快速凝固Cu-Pb过偏晶合金的性能表征. 物理学报, 2009, 58(1): 644-649. doi: 10.7498/aps.58.644
    [11] 张明晓, 田学雷, 郭风祥. 电磁感应式液固态金属电阻率定性测量装置及应用. 物理学报, 2009, 58(9): 6080-6085. doi: 10.7498/aps.58.6080
    [12] 樊飞, 班春燕, 王洋, 巴启先, 崔建忠. 普通铸造和低频电磁铸造7050铝合金电阻率-温度特性的研究. 物理学报, 2009, 58(1): 638-643. doi: 10.7498/aps.58.638
    [13] 别少伟, 江建军, 马 强, 杜 刚, 袁 林, 邸永江, 冯则坤, 何华辉. 高电阻率多层纳米颗粒膜软磁特性及微波磁导率. 物理学报, 2008, 57(4): 2514-2518. doi: 10.7498/aps.57.2514
    [14] 翟秋亚, 杨 扬, 徐锦锋, 郭学锋. 快速凝固Cu-Sn亚包晶合金的电阻率及力学性能. 物理学报, 2007, 56(10): 6118-6123. doi: 10.7498/aps.56.6118
    [15] 周 昀, 龙云泽, 陈兆甲, 张志明, 万梅香. 水和乙醇对纳米管结构聚苯胺电阻率的影响. 物理学报, 2005, 54(1): 228-232. doi: 10.7498/aps.54.228
    [16] 徐锦锋, 魏炳波. 快速凝固Co-Cu包晶合金的电学性能. 物理学报, 2005, 54(7): 3444-3450. doi: 10.7498/aps.54.3444
    [17] 汪 渊, 徐可为. Cu-W薄膜表面形貌的分形表征与电阻率. 物理学报, 2004, 53(3): 900-904. doi: 10.7498/aps.53.900
    [18] 龙云泽, 陈兆甲, 张志明, 万梅香, 郑 萍, 王楠林, 贺朝会, 耿 斌, 杨海亮, 陈晓华, 王燕萍, 李国政. 纳米管结构聚苯胺的电阻率和磁化率. 物理学报, 2003, 52(1): 175-179. doi: 10.7498/aps.52.175
    [19] 李慧玲, 阮可青, 李世燕, 莫维勤, 樊荣, 罗习刚, 陈仙辉, 曹烈兆. MgB2和Mg0.93Li0.07B2的电阻率与霍尔效应研究. 物理学报, 2001, 50(10): 2044-2048. doi: 10.7498/aps.50.2044
    [20] 王强, 陆坤权, 李言祥. 液态InSb电阻率和热电势与温度的关系. 物理学报, 2001, 50(7): 1355-1358. doi: 10.7498/aps.50.1355
计量
  • 文章访问数:  5705
  • PDF下载量:  414
  • 被引次数: 0
出版历程
  • 收稿日期:  2011-11-30
  • 修回日期:  2012-01-25
  • 刊出日期:  2012-09-05

/

返回文章
返回