退火工艺对LaTiON和HfLaON存储层金属-氧化物-氮化物-氧化物-硅存储器特性的影响

朱剑云 刘璐 李育强 徐静平

引用本文:
Citation:

退火工艺对LaTiON和HfLaON存储层金属-氧化物-氮化物-氧化物-硅存储器特性的影响

朱剑云, 刘璐, 李育强, 徐静平

Effect of annealing atmosphere on characteristics of MONOS with LaTiON or HfLaON as charge storage layer

Zhu Jian-Yun, Liu Lu, Li Yu-Qiang, Xu Jing-Ping
PDF
导出引用
  • 采用反应溅射法, 分别制备以LaTiON, HfLaON为存储层的 金属-氧化物-氮化物-氧化物-硅 电容存储器, 研究了淀积后退火气氛(N2, NH3)对其存储性能的影响. 分析测试表明, 退火前LaTiON样品比HfLaON 样品具有更好的电荷保持特性, 但后者具有更大的存储窗口 (编程/擦除电压为+/-12 V时4.8 V); 对于退火样品, 由于NH3的氮化作用, NH3退火样品比N2退火样品表现出更快的编程/擦除速度、更好的电荷保持特性和疲劳特性. 当编程/擦除电压为+/-12 V时, NH3退火HfLaON样品的存储窗口为3.8 V, 且比NH3退火LaTiON样品具有更好的电荷保持特性和疲劳特性.
    Charge-trapping memory capacitor with LaTiON or HfLaON serving as charge storage layer is fabricated by reactive sputtering method, and influences of post-deposition annealing (PDA) in NH3 or N2 ambient on its memory characteristics are investigated. It is found that before PDA, the LaTiON sample exhibits better retention characteristic than the HfLaON sample, but the later shows larger memory window (4.8 V at +/-12 V/1 s), and after PDA, the NH3-annealed sample has faster program/erase speed, better retention and endurance properties than the N2-annealed sample, owing to nitridation role of NH3. Furthermore, the HfLaON sample with PDA in NH3achieves a large memory window of 3.8 V at +/-12 V/1 s, and also shows better retention and endurance properties than the LaTiON sample with PDA in NH3.
    • 基金项目: 国家自然科学基金 (批准号: 60976091) 资助的课题.
    • Funds: Project supported by the National Natural Science Foundation of China (Grant No. 60976091).
    [1]

    Fang S H, Cheng X L, Huang Y, Gu H H 2007 Acta Phys. Sin. 56 6634 (in Chinese) [房少华, 程秀兰, 黄晔, 顾怀怀 2007 物理学报 56 6634]

    [2]

    Li L L, Yu Z G, Xiao Z Q, Zhou X J 2011 Acta Phys. Sin. 60 098502 (in Chinese) [李蕾蕾, 于宗光, 肖志强, 周昕杰 2011 物理学报 60 098502]

    [3]

    Pan T M, Chen F H, Jung J S 2010 Appl. Phys. Lett. 96 102904

    [4]

    Pan T M, Yeh W W 2009 J. Vac. Sci. Technol. A 27 700

    [5]

    Pan T M, Yeh W W, Chang W T, Chen K M, Chen J W, Huang K C 2007 Semiconductor Device Research Symposium 2007 International College Park, MD, USA Dec. 12-14 2007 (Piscataway, NJ, USA: IEEE) p435

    [6]

    Huang X D, Sin J K O, Lai P T 2012 Device and Materials Reliability 12 306

    [7]

    Xu H X, Xu J P, Li C X, Liu L, Lai P T, Chan C L 2009 IEEE International Conference of Electron Devices and Solid-State Circuits Xi'an Dec. 25-27 2009 (Piscataway, NJ, USA: IEEE) p435

    [8]

    Arimura H, Kitano N, Naitou Y, Oku Y, Minami T, Kosuda M, Hosoi T, Shimura T, Watanabe H 2008 Appl. Phys. Lett. 92 212902

    [9]

    Tao Q B, Lai P T 2010 IEEE International Conference of Electron Devices and Solid-State Circuits Hongkong, China Dec. 15-17 2010 (Piscataway, NJ, USA: IEEE) p1

    [10]

    Xu H X, Xu J P, Li C X, Chan C L, Lai P T 2010 Appl. Phys. Lett. 99 903

    [11]

    Ji F, Xu J P, Zhang H Q, Li P T, Li C X, Guan J G 2008 Research & Progress of Solid State Electronics 28 330 (in Chinese) [季峰, 徐静平, 张洪强, 黎沛涛, 李春霞, 官建国 2008 固体电子学研究与进展 28 330]

    [12]

    Gavartin J L, Shluger A L, Foster A S, Bersuker G I 2005 J. Appl. Phys. 97 053704

    [13]

    van Dover R B 1999 Appl. Phys. Lett. 74 3041

    [14]

    Huang X D, Lai P T, Sin J K O 2012 Appl. Phys. A Mater. Sci. Proc. 106 6881

    [15]

    Huang X D, Lai P T 2010 2010 10th IEEE International Conference on Solid-State and Integrated Circuit Technology Shanghai Nov. 1-4 2010 (Piscataway, NJ, USA: IEEE) p900

    [16]

    Sato S, Tachi K, Kakushima K, Ahmet P, Tsutsui K, Sugii N, Hattori T, Iwai H 2007 Microelectronic Engineering 84 1894

    [17]

    Hamamura H, Itoh H, Shimogaki Y, Aoyama J, Yoshimi T, Ueda J, Komiyama H 1998 Thin Solid Films 320 31

    [18]

    Lee W G, Lee J G 2002 Journal of The Electrochemical Society 149 G1

  • [1]

    Fang S H, Cheng X L, Huang Y, Gu H H 2007 Acta Phys. Sin. 56 6634 (in Chinese) [房少华, 程秀兰, 黄晔, 顾怀怀 2007 物理学报 56 6634]

    [2]

    Li L L, Yu Z G, Xiao Z Q, Zhou X J 2011 Acta Phys. Sin. 60 098502 (in Chinese) [李蕾蕾, 于宗光, 肖志强, 周昕杰 2011 物理学报 60 098502]

    [3]

    Pan T M, Chen F H, Jung J S 2010 Appl. Phys. Lett. 96 102904

    [4]

    Pan T M, Yeh W W 2009 J. Vac. Sci. Technol. A 27 700

    [5]

    Pan T M, Yeh W W, Chang W T, Chen K M, Chen J W, Huang K C 2007 Semiconductor Device Research Symposium 2007 International College Park, MD, USA Dec. 12-14 2007 (Piscataway, NJ, USA: IEEE) p435

    [6]

    Huang X D, Sin J K O, Lai P T 2012 Device and Materials Reliability 12 306

    [7]

    Xu H X, Xu J P, Li C X, Liu L, Lai P T, Chan C L 2009 IEEE International Conference of Electron Devices and Solid-State Circuits Xi'an Dec. 25-27 2009 (Piscataway, NJ, USA: IEEE) p435

    [8]

    Arimura H, Kitano N, Naitou Y, Oku Y, Minami T, Kosuda M, Hosoi T, Shimura T, Watanabe H 2008 Appl. Phys. Lett. 92 212902

    [9]

    Tao Q B, Lai P T 2010 IEEE International Conference of Electron Devices and Solid-State Circuits Hongkong, China Dec. 15-17 2010 (Piscataway, NJ, USA: IEEE) p1

    [10]

    Xu H X, Xu J P, Li C X, Chan C L, Lai P T 2010 Appl. Phys. Lett. 99 903

    [11]

    Ji F, Xu J P, Zhang H Q, Li P T, Li C X, Guan J G 2008 Research & Progress of Solid State Electronics 28 330 (in Chinese) [季峰, 徐静平, 张洪强, 黎沛涛, 李春霞, 官建国 2008 固体电子学研究与进展 28 330]

    [12]

    Gavartin J L, Shluger A L, Foster A S, Bersuker G I 2005 J. Appl. Phys. 97 053704

    [13]

    van Dover R B 1999 Appl. Phys. Lett. 74 3041

    [14]

    Huang X D, Lai P T, Sin J K O 2012 Appl. Phys. A Mater. Sci. Proc. 106 6881

    [15]

    Huang X D, Lai P T 2010 2010 10th IEEE International Conference on Solid-State and Integrated Circuit Technology Shanghai Nov. 1-4 2010 (Piscataway, NJ, USA: IEEE) p900

    [16]

    Sato S, Tachi K, Kakushima K, Ahmet P, Tsutsui K, Sugii N, Hattori T, Iwai H 2007 Microelectronic Engineering 84 1894

    [17]

    Hamamura H, Itoh H, Shimogaki Y, Aoyama J, Yoshimi T, Ueda J, Komiyama H 1998 Thin Solid Films 320 31

    [18]

    Lee W G, Lee J G 2002 Journal of The Electrochemical Society 149 G1

  • [1] 孟绍怡, 郝奇, 吕国建, 乔吉超. La基非晶合金β弛豫行为: 退火和加载应变的影响. 物理学报, 2023, 72(7): 076101. doi: 10.7498/aps.72.20222389
    [2] 宋梦婷, 张悦, 黄文娟, 候华毅, 陈相柏. 拉曼光谱研究退火氧化镍中二阶磁振子散射增强. 物理学报, 2021, 70(16): 167201. doi: 10.7498/aps.70.20210454
    [3] 张金帅, 黄秋实, 蒋励, 齐润泽, 杨洋, 王风丽, 张众, 王占山. 低温退火的X射线W/Si多层膜应力和结构性能. 物理学报, 2016, 65(8): 086101. doi: 10.7498/aps.65.086101
    [4] 蒋勇, 袁晓东, 王海军, 廖威, 刘春明, 向霞, 邱荣, 周强, 高翔, 杨永佳, 郑万国, 祖小涛, 苗心向. 退火对熔石英表面损伤修复点损伤增长的影响. 物理学报, 2016, 65(4): 044209. doi: 10.7498/aps.65.044209
    [5] 陈剑辉, 杨静, 沈艳娇, 李锋, 陈静伟, 刘海旭, 许颖, 麦耀华. 后退火增强氢化非晶硅钝化效果的研究. 物理学报, 2015, 64(19): 198801. doi: 10.7498/aps.64.198801
    [6] 贾艳丽, 杨桦, 袁洁, 于和善, 冯中沛, 夏海亮, 石玉君, 何格, 胡卫, 龙有文, 朱北沂, 金魁. 浅析电子型掺杂铜氧化物超导体的退火过程. 物理学报, 2015, 64(21): 217402. doi: 10.7498/aps.64.217402
    [7] 张彬, 王伟丽, 牛巧利, 邹贤劭, 董军, 章勇. H2气氛退火处理对Nb掺杂TiO2薄膜光电性能的影响. 物理学报, 2014, 63(6): 068102. doi: 10.7498/aps.63.068102
    [8] 刘建朋, 朱彦旭, 郭伟玲, 闫微微, 吴国庆. ITO退火对GaN基LED电学特性的影响. 物理学报, 2012, 61(13): 137303. doi: 10.7498/aps.61.137303
    [9] 罗庆洪, 娄艳芝, 赵振业, 杨会生. 退火对AlTiN多层薄膜结构及力学性能影响. 物理学报, 2011, 60(6): 066201. doi: 10.7498/aps.60.066201
    [10] 张磊, 叶辉, 皇甫幼睿, 刘旭. 氧化硅缓冲层对于退火形成锗量子点的作用研究. 物理学报, 2011, 60(7): 076103. doi: 10.7498/aps.60.076103
    [11] 胡美娇, 李成, 徐剑芳, 赖虹凯, 陈松岩. 循环氧化/退火制备GeOI薄膜材料及其性质研究. 物理学报, 2011, 60(7): 078102. doi: 10.7498/aps.60.078102
    [12] 宋超, 陈谷然, 徐骏, 王涛, 孙红程, 刘宇, 李伟, 陈坤基. 不同退火温度下晶化硅薄膜的电学输运性质. 物理学报, 2009, 58(11): 7878-7883. doi: 10.7498/aps.58.7878
    [13] 杨帆, 马瑾, 孔令沂, 栾彩娜, 朱振. 金属有机物化学气相沉积法生长Ga2(1-x)In2xO3薄膜的结构及光电性能研究. 物理学报, 2009, 58(10): 7079-7082. doi: 10.7498/aps.58.7079
    [14] 周丽宏, 张崇宏, 李炳生, 杨义涛, 宋 银. 注入Ar+的蓝宝石晶体退火前后光致发光谱的分析. 物理学报, 2008, 57(4): 2562-2566. doi: 10.7498/aps.57.2562
    [15] 崔 灿, 马向阳, 杨德仁. 低起始温度的线性升温热处理对直拉硅中氧沉淀的影响. 物理学报, 2008, 57(2): 1037-1042. doi: 10.7498/aps.57.1037
    [16] 王 冲, 冯 倩, 郝 跃, 万 辉. AlGaN/GaN异质结Ni/Au肖特基表面处理及退火研究. 物理学报, 2006, 55(11): 6085-6089. doi: 10.7498/aps.55.6085
    [17] 吴世亮, 陈叶清, 吴奕初, 王少阶, 温熙宇, 翟同广. AA 2037新型连铸铝合金热轧板退火的正电子湮没研究. 物理学报, 2006, 55(11): 6129-6135. doi: 10.7498/aps.55.6129
    [18] 孙成伟, 刘志文, 张庆瑜. 退火温度对ZnO薄膜结构和发光特性的影响. 物理学报, 2006, 55(1): 430-436. doi: 10.7498/aps.55.430
    [19] 王永谦, 陈长勇, 陈维德, 杨富华, 刁宏伟, 许振嘉, 张世斌, 孔光临, 廖显伯. a-Si∶O∶H薄膜微结构及其高温退火行为研究. 物理学报, 2001, 50(12): 2418-2422. doi: 10.7498/aps.50.2418
    [20] 童六牛, 何贤美, 鹿 牧. 真空退火对周期性界面掺杂Ni80Co20薄膜磁性的影响. 物理学报, 2000, 49(11): 2290-2295. doi: 10.7498/aps.49.2290
计量
  • 文章访问数:  5289
  • PDF下载量:  538
  • 被引次数: 0
出版历程
  • 收稿日期:  2012-06-27
  • 修回日期:  2012-09-04
  • 刊出日期:  2013-02-05

/

返回文章
返回