量子限制受主远红外电致发光器件的制备与测量

刘静 郑卫民 宋迎新 初宁宁 李素梅 丛伟艳

引用本文:
Citation:

量子限制受主远红外电致发光器件的制备与测量

刘静, 郑卫民, 宋迎新, 初宁宁, 李素梅, 丛伟艳

Preparation and measurement of far-infrared electroluminescence emitter based on quantum confined acceptors

Liu Jing, Zheng Wei-Min, Song Ying-Xin, Chu Ning-Ning, Li Su-Mei, Cong Wei-Yan
PDF
导出引用
  • 采用分子束外延技术生长GaAs/AlAs三量子阱,并在中间的GaAs阱中δ-掺杂浅受主杂质Be原子,制作出量子限制受主远红外Teraherz原型电致发光器件.实验上测量得到4.5 K时器件的电致发光谱(EL)和电传输特性(I-V曲线).在EL发射谱中清楚地观察到222 cm-1处宽的尖峰,这来源于Be受主奇宇称激发态到其基态的辐射跃迁,而非辐射弛豫过程则使发射谱的信号很弱.另外在I-V曲线中072和186 V的位置出现两个共振隧道贯穿现象,分别对应于中间δ-掺杂量子阱受主能级1s3/2(Γ6+Γ7)到左边非掺GaAs量子阱中HH带,及右边非掺杂GaAs量子阱中HH重空穴带到中间掺杂GaAs量子阱中Be受主杂质原子奇宇称激发态2p5/2(Γ6+Γ7)能级的共振隧穿.
    GaAs/AlAs triple-quantum-well samples were grown by molecular beam epitaxy, and the middle GaAs quantum-well layer was delta-doped at the well centre with Be shallow acceptors. Then the far-infrared Teraherz prototype emitter was fabricated using the samples. Electroluminescence (EL) and current-voltage characteristics (I-V) were measured at 4.5 K. In the EL spectrum, a wide peak was observed clear 222 cm-1, which is attributed to the Be acceptor’s radiative transitions from the excited odd-parity states to the ground state. Nevertheless, the emission signal was weakened by non-radiative relaxation processes. In the I-V curve, the negative differential resistance characteristic at the position of 0.72 and 1.86 V was also observed clearly. This is attributed to the resonant tunneling between Be acceptor 1s3/2(Γ6+Γ7) energy level in the middle quantum-well and the HH1 band in the left-side non-doping quantum-well, as well as the resonant tunneling between the HH band in the right-side non-doping quantum-well and Be acceptor 2p5/2(Γ6+Γ7) energy level.
    • 基金项目: 国家自然科学基金(批准号:60776044)和山东省自然科学基金(批准号:2006ZRA10001)资助的课题.
    [1]

    [1]Ma S H, Shi Y L, Xu X L, Yan W, Yang Y P, Wang L 2006 Acta Phys. Sin. 55 4091 (in Chinese) [马士华、施宇蕾、徐新龙、严伟、杨玉平、汪力 2006 物理学报 55 4091]

    [2]

    [2]Zhang X B, Shi W 2008 Acta Phys. Sin. 57 4984 (in Chinese) [张显斌、施卫 2008 物理学报 57 4984]

    [3]

    [3]Lafaye D G, Boucaud P, Julien F H, Prazeres R, Glotin F, Ortega J M, Thierry-Mieg V, Planel R 1997 Appl. Phys. Lett. 70 3197

    [4]

    [4]Muravjov A V, Withers S H, Pavlov S G, Shastin V N, Peale R E 1999 J. Appl. Phys. 86 3512

    [5]

    [5]Zhang T Y, Zhao W 2008 Chin. Phys. B 17 4285

    [6]

    [6]Xu G Y, Li A Z 2007 Acta Phys. Sin. 56 500 (in Chinese) [徐刚毅、李爱珍 2007 物理学报 56 500]

    [7]

    [7]Lin G J, Zhou Z W, Lai H K, Li C, Chen S Y, Yu J Z 2007 Acta Phys. Sin. 56 4137 (in Chinese) [林桂江、周志文、赖虹凯、李成、陈松岩、余金中 2007 物理学报 56 4137]

    [8]

    [8]Ting D Z, Chang Y C, Bandara S V, Gunapala S D 2007 Appl. Phys. Lett. 91 073510

    [9]

    [9]MujagiDc' E, Austerer M, Schartner S, Nobile M, Hoffmann L K, Schrenk W, Strasser G, Semtsiv M P, Bayrakli I, Wienold M, Masselink W T 2008 J. Appl. Phys. 103 033104

    [10]

    ]Williams B S, Callebaut H, Kumar S, Hu Q, Reno J L 2003 Appl. Phys. Lett. 82 1015

    [11]

    ]Harrison P, Halsall M P, Zheng W M 2002 Mater. Sci. Forum 384—385 165

    [12]

    ]Harrison P, Kelsall R W 1997 J. Appl. Phys. 81 7135

    [13]

    ]Halsall M P, Harrison P, Wells J P R, Bradley I V, Pellemans H 2001 Phys. Rev. B 63 155314

    [14]

    ]Zheng W M, Halsall M P, Harmer P, Harrison P, Steer M J 2002 J. Appl. Phys. 92 6039

    [15]

    ]Orlova E E, Harrison P, Zhang W M, Halsall M P 2005 Semiconductors 39 67

    [16]

    ]Zheng W M, Halsall M P, Harmer P, Harrison P, Steer M J 2004 Appl. Phys. Lett. 84 735

    [17]

    ]Seliuta D, ACˇUechaviDcˇius B, Kavaliauskas J, Krivaite G, Grigelionis I, Balakauskas S, ValuDsˇis G, Sherliker B, Sherliker B, Halsall M P, Lachab M, Khanna S P, Harrison P, Linfieldc E H 2008 Acta Phys. Pol. A 113 909

    [18]

    ]Huber R, Kaindl R A, Schmid B A, Chemla D S 2005 Phys. Rev. B 72 161314

    [19]

    ]ACˇUechaviDcˇius B, Kavaliauskas J, Krivaite· G, Seliuta D, ValuDsˇis G, Halsall M P, Steer M J, Harrison P 2005 J. Appl. Phys. 98 023508

    [20]

    ]ACˇUechaviDcˇius B, Kavaliauskas J, Krivaite· G, Seliuta D, ASˇUirmulis E, Devenson J, ValuAsˇis G, Sherliker B, Halsall M P, Steer M J, Harrison P 2005 Acta Phys. Pol. A 107 328

    [21]

    ]Kundrotas J, ACˇUerDsˇkus A, ValuDsˇis G, Lachab M, Khanna S P, Harrison P, Linfield E H 2008 J. Appl. Phys. 103 123108

    [22]

    ]Holtz P O, Sundaram M, Doughty K, Merz J L, Gossard A C 1989 Phys. Rev. B 40 12338

    [23]

    ]Missous M 1995 J. Appl. Phys. 78 4467

    [24]

    ]Zheng W M, Halsall M P, Harrison P, Steer M J 2006 Sci. China Ser. G 49 702

    [25]

    ]Masselink W T, Chung C Y, Morkoc H 1985 Phys.Rev. B 32 5190

    [26]

    ]Zheng W M, Halsall M P, Harrison P, Wells J P R, Bradley I V, Steer M J 2003 Appl. Phys. Lett. 83 3719

    [27]

    ]Reeder A A, McCombe B D, Chambers F A, Devane G P 1988 Phys. Rev. B 38 4318

    [28]

    ]Xia J B, Huang K 1988 Acta Phys. Sin. 37 1 (in Chinese) [夏建白、黄昆 1988 物理学报 37 1]

  • [1]

    [1]Ma S H, Shi Y L, Xu X L, Yan W, Yang Y P, Wang L 2006 Acta Phys. Sin. 55 4091 (in Chinese) [马士华、施宇蕾、徐新龙、严伟、杨玉平、汪力 2006 物理学报 55 4091]

    [2]

    [2]Zhang X B, Shi W 2008 Acta Phys. Sin. 57 4984 (in Chinese) [张显斌、施卫 2008 物理学报 57 4984]

    [3]

    [3]Lafaye D G, Boucaud P, Julien F H, Prazeres R, Glotin F, Ortega J M, Thierry-Mieg V, Planel R 1997 Appl. Phys. Lett. 70 3197

    [4]

    [4]Muravjov A V, Withers S H, Pavlov S G, Shastin V N, Peale R E 1999 J. Appl. Phys. 86 3512

    [5]

    [5]Zhang T Y, Zhao W 2008 Chin. Phys. B 17 4285

    [6]

    [6]Xu G Y, Li A Z 2007 Acta Phys. Sin. 56 500 (in Chinese) [徐刚毅、李爱珍 2007 物理学报 56 500]

    [7]

    [7]Lin G J, Zhou Z W, Lai H K, Li C, Chen S Y, Yu J Z 2007 Acta Phys. Sin. 56 4137 (in Chinese) [林桂江、周志文、赖虹凯、李成、陈松岩、余金中 2007 物理学报 56 4137]

    [8]

    [8]Ting D Z, Chang Y C, Bandara S V, Gunapala S D 2007 Appl. Phys. Lett. 91 073510

    [9]

    [9]MujagiDc' E, Austerer M, Schartner S, Nobile M, Hoffmann L K, Schrenk W, Strasser G, Semtsiv M P, Bayrakli I, Wienold M, Masselink W T 2008 J. Appl. Phys. 103 033104

    [10]

    ]Williams B S, Callebaut H, Kumar S, Hu Q, Reno J L 2003 Appl. Phys. Lett. 82 1015

    [11]

    ]Harrison P, Halsall M P, Zheng W M 2002 Mater. Sci. Forum 384—385 165

    [12]

    ]Harrison P, Kelsall R W 1997 J. Appl. Phys. 81 7135

    [13]

    ]Halsall M P, Harrison P, Wells J P R, Bradley I V, Pellemans H 2001 Phys. Rev. B 63 155314

    [14]

    ]Zheng W M, Halsall M P, Harmer P, Harrison P, Steer M J 2002 J. Appl. Phys. 92 6039

    [15]

    ]Orlova E E, Harrison P, Zhang W M, Halsall M P 2005 Semiconductors 39 67

    [16]

    ]Zheng W M, Halsall M P, Harmer P, Harrison P, Steer M J 2004 Appl. Phys. Lett. 84 735

    [17]

    ]Seliuta D, ACˇUechaviDcˇius B, Kavaliauskas J, Krivaite G, Grigelionis I, Balakauskas S, ValuDsˇis G, Sherliker B, Sherliker B, Halsall M P, Lachab M, Khanna S P, Harrison P, Linfieldc E H 2008 Acta Phys. Pol. A 113 909

    [18]

    ]Huber R, Kaindl R A, Schmid B A, Chemla D S 2005 Phys. Rev. B 72 161314

    [19]

    ]ACˇUechaviDcˇius B, Kavaliauskas J, Krivaite· G, Seliuta D, ValuDsˇis G, Halsall M P, Steer M J, Harrison P 2005 J. Appl. Phys. 98 023508

    [20]

    ]ACˇUechaviDcˇius B, Kavaliauskas J, Krivaite· G, Seliuta D, ASˇUirmulis E, Devenson J, ValuAsˇis G, Sherliker B, Halsall M P, Steer M J, Harrison P 2005 Acta Phys. Pol. A 107 328

    [21]

    ]Kundrotas J, ACˇUerDsˇkus A, ValuDsˇis G, Lachab M, Khanna S P, Harrison P, Linfield E H 2008 J. Appl. Phys. 103 123108

    [22]

    ]Holtz P O, Sundaram M, Doughty K, Merz J L, Gossard A C 1989 Phys. Rev. B 40 12338

    [23]

    ]Missous M 1995 J. Appl. Phys. 78 4467

    [24]

    ]Zheng W M, Halsall M P, Harrison P, Steer M J 2006 Sci. China Ser. G 49 702

    [25]

    ]Masselink W T, Chung C Y, Morkoc H 1985 Phys.Rev. B 32 5190

    [26]

    ]Zheng W M, Halsall M P, Harrison P, Wells J P R, Bradley I V, Steer M J 2003 Appl. Phys. Lett. 83 3719

    [27]

    ]Reeder A A, McCombe B D, Chambers F A, Devane G P 1988 Phys. Rev. B 38 4318

    [28]

    ]Xia J B, Huang K 1988 Acta Phys. Sin. 37 1 (in Chinese) [夏建白、黄昆 1988 物理学报 37 1]

  • [1] 朱伟君, 陈金鑫, 高宇晗, 杨德仁, 马向阳. 硅基掺铒二氧化钛薄膜发光器件的电致发光: 共掺镱的增强发光作用. 物理学报, 2019, 68(12): 124204. doi: 10.7498/aps.68.20190300
    [2] 易有根, 王瑜英, 胡奇峰, 张彦彬, 彭勇宜, 雷红文, 彭丽萍, 王雪敏, 吴卫东. ZnCdO/ZnO单量子阱结构及其荧光发射特性. 物理学报, 2016, 65(5): 057802. doi: 10.7498/aps.65.057802
    [3] 毛清华, 刘军林, 全知觉, 吴小明, 张萌, 江风益. p型层结构与掺杂对GaInN发光二极管正向电压温度特性的影响. 物理学报, 2015, 64(10): 107801. doi: 10.7498/aps.64.107801
    [4] 林圳旭, 林泽文, 张毅, 宋超, 郭艳青, 王祥, 黄新堂, 黄锐. 基于纳米硅结构的氮化硅基发光器件电致发光特性研究. 物理学报, 2014, 63(3): 037801. doi: 10.7498/aps.63.037801
    [5] 何月娣, 徐征, 赵谡玲, 刘志民, 高松, 徐叙瑢. 混合量子点器件电致发光的能量转移研究. 物理学报, 2014, 63(17): 177301. doi: 10.7498/aps.63.177301
    [6] 刘博智, 黎瑞锋, 宋凌云, 胡炼, 张兵坡, 陈勇跃, 吴剑钟, 毕刚, 王淼, 吴惠桢. 氧化锌锡作为电子传输层的量子点发光二极管. 物理学报, 2013, 62(15): 158504. doi: 10.7498/aps.62.158504
    [7] 马小凤, 王懿喆, 周呈悦. a-Si ∶H/SiO2多量子阱材料制备及其光学性能和微结构研究. 物理学报, 2011, 60(6): 068102. doi: 10.7498/aps.60.068102
    [8] 朱海娜, 徐征, 赵谡玲, 张福俊, 孔超, 闫光, 龚伟. 量子阱结构对有机电致发光器件效率的影响. 物理学报, 2010, 59(11): 8093-8097. doi: 10.7498/aps.59.8093
    [9] 宋迎新, 郑卫民, 刘静, 初宁宁, 李素梅. 量子限制效应对δ掺杂GaAs/AlAs多量子阱中铍受主态寿命的影响. 物理学报, 2009, 58(9): 6471-6476. doi: 10.7498/aps.58.6471
    [10] 熊传兵, 江风益, 王 立, 方文卿, 莫春兰. 硅衬底垂直结构InGaAlN多量子阱发光二极管电致发光谱的干涉现象研究. 物理学报, 2008, 57(12): 7860-7864. doi: 10.7498/aps.57.7860
    [11] 张国辉, 华玉林, 吴晓明, 印寿根, 牛 霞, 惠娟利, 王 宇, 张丽娟. 一种多层白色磷光有机电致发光器件的制备及性能研究. 物理学报, 2007, 56(9): 5408-5412. doi: 10.7498/aps.56.5408
    [12] 锁 钒, 于军胜, 邓 静, 蒋亚东, 王 睿, 汪伟志, 刘天西. 芴-咔唑新型共聚物/PVK掺杂体系的电致发光特性研究. 物理学报, 2007, 56(11): 6685-6690. doi: 10.7498/aps.56.6685
    [13] 聂 海, 张 波, 唐先忠. 聚合物掺杂有机小分子发光二极管的电致发光与杂质陷阱效应. 物理学报, 2007, 56(1): 263-267. doi: 10.7498/aps.56.263
    [14] 姜 燕, 杨盛谊, 张秀龙, 滕 枫, 徐 征, 侯延冰. 基于ZnSe的有机-无机异质结电致发光器件. 物理学报, 2006, 55(9): 4860-4864. doi: 10.7498/aps.55.4860
    [15] 张 鹏, 周印华, 刘秀芬, 田文晶, 李 敏, 张 国. PVK:DBVP掺杂体系的能量转移及发光性质的研究. 物理学报, 2006, 55(10): 5494-5498. doi: 10.7498/aps.55.5494
    [16] 侯林涛, 侯 琼, 彭俊彪, 曹 镛. 三元共聚物饱和红色电致发光研究. 物理学报, 2005, 54(11): 5377-5381. doi: 10.7498/aps.54.5377
    [17] 曾中明, 韩秀峰, 杜关祥, 詹文山, 王 勇, 张 泽. 双势垒磁性隧道结的磁电阻效应及其在自旋晶体管中的应用. 物理学报, 2005, 54(7): 3351-3356. doi: 10.7498/aps.54.3351
    [18] 朱文清, 吴有智, 郑新友, 蒋雪茵, 张志林, 孙润光, 许少鸿. 双层有机电致发光器件中多成分激发态发射. 物理学报, 2004, 53(7): 2325-2329. doi: 10.7498/aps.53.2325
    [19] 许秀来, 徐 征, 侯延冰, 苏艳梅, 徐 叙. Gd3Ga5O12:Ag薄膜电致发光材料的制备及其发光性质. 物理学报, 2000, 49(7): 1390-1393. doi: 10.7498/aps.49.1390
    [20] 孙永科, 衡成林, 王孙涛, 秦国刚, 马振昌, 宗婉华. Au/(SiO2/Si/SiO2)纳米双势垒/n+-Si结构的电致发光研究. 物理学报, 2000, 49(7): 1404-1408. doi: 10.7498/aps.49.1404
计量
  • 文章访问数:  7921
  • PDF下载量:  1192
  • 被引次数: 0
出版历程
  • 收稿日期:  2009-07-06
  • 修回日期:  2009-08-06
  • 刊出日期:  2010-02-05

/

返回文章
返回