本文先应用分子动力学模拟BaTiO3体系在初级击出原子(primary knock-on atom, PKA)轰击下缺陷产生和复合的动力学过程, 模拟结果表明：PKA的方向和能量对缺陷数目有重要影响, 并计算了Ba， O和Ti原子的平均位移阈能分别为69 eV, 51 eV和123 eV, 远大于SRIM程序默认的位移阈能25 eV. 然后应用蒙特卡罗软件包SRIM, 模拟质子在BaTiO3薄膜中的能量损失过程, 比较位移阈能对模拟结果的影响, 分析质子能量和入射角度对空位数量以及分布的影响. 结果表明空位数量随着质子能量增加而增加, 增加的速率随能量的增加是降低的；当入射角度大于60°, 空位数量随入射角增大而明显减少.BaTiO3 is a kind of perovskite ferroelectric which has the advantages of ferroelectric property, piezoelectric property and radiation resistance. BaTiO3 thin films and devices have important applications in strong irradiation environment. The structure damage, especially the oxygen vacancy has a crucial influence on the response of ferroelectric under radiation. Molecular dynamics is used to simulate the formation process and the recovery process of defects in BaTiO3 under the impact of primary knock-on atom (PKA). The results show that the initial motion direction and energy of PKA have significant effects on the number of defects, and the averaged threshold displacement energies of Ba, O and Ti atom are 69 eV, 51 eV and 123 eV respectively. The calculated displacement energy is obviously larger than default value (25 eV) in SRIM code. Furthermore the SRIM code is used to simulate the proton irradiation damage in BaTiO3 thin film. The results show that the number of vacancy increases with the increase of proton energy, but the increase rate decreases, and the number of vacancy decreases obviously with the increase of incidence angle when it is more than 60°.
-
Keywords:
- molecular dynamics /
- ferroelectric thin film /
- irradiation damage
[1] Scott J F, Araujo C A, Brett H, McMillan L D, Shawabkeh A 1989 J. Appl. Phys. 66 1444
[2] Colc Y M, Musseau O, Leray J L 1994 IEEE Trans. Nucl. Sci. 41 495
[3] Scott J F 2004 Ferroelectric Memories(Beijing: Tsinghua Univerisy Press) (In Chinese) [朱劲松等译 2004 铁电存储器 (北京：清华大学出版社)]
[4] Gruverman A, Rodriguez B J, Nemanich R J, Kingon A I 2002 J. Appl. Phys. 92 2734
[5] Stanishevsky A, Nagaraj B,Melngailis J, Ramesh R, Khriachtchev L, McDaniel E 2002 J. Appl. Phys. 92 3275
[6] Li Y S, Ma Y, Zhou Y C 2009 Appl. Phys. Lett. 94 042903
[7] Cao H X, Zhang N 2008 Acta Phys. Sin. 57 6582 (in Chinese) [曹鸿霞, 张宁 2008 物理学报 57 6582]
[8] Ma Y, Sun L L, Zhou Y C 2011 Acta Phys. Sin. 60 046105 (in Chinese) [马颖, 孙玲玲, 周益春 2011 物理学报 60 046105]
[9] Xiao S Q, Xie G F 2010 Acta Phys. Sin. 59 4808 (in Chinese) [肖松青, 谢国锋 2010 物理学报 59 4808]
[10] Ziegler J F, Biersack J P, Littmark U 1985 The Stopping and Range of Ions in Solids. (Pergamon, New York)
[11] Thomas B S, Marks N A, Begg B D 2007 Nucl. Instr. and Meth. B 254 211
[12] Smith K L, Zaluzec N J 2005 J. Nucl. Mater. 336 261
[13] Smith K L, Colella M, Cooper R, Vance E R 2003 J. Nucl. Mater. 321 19
-
[1] Scott J F, Araujo C A, Brett H, McMillan L D, Shawabkeh A 1989 J. Appl. Phys. 66 1444
[2] Colc Y M, Musseau O, Leray J L 1994 IEEE Trans. Nucl. Sci. 41 495
[3] Scott J F 2004 Ferroelectric Memories(Beijing: Tsinghua Univerisy Press) (In Chinese) [朱劲松等译 2004 铁电存储器 (北京：清华大学出版社)]
[4] Gruverman A, Rodriguez B J, Nemanich R J, Kingon A I 2002 J. Appl. Phys. 92 2734
[5] Stanishevsky A, Nagaraj B,Melngailis J, Ramesh R, Khriachtchev L, McDaniel E 2002 J. Appl. Phys. 92 3275
[6] Li Y S, Ma Y, Zhou Y C 2009 Appl. Phys. Lett. 94 042903
[7] Cao H X, Zhang N 2008 Acta Phys. Sin. 57 6582 (in Chinese) [曹鸿霞, 张宁 2008 物理学报 57 6582]
[8] Ma Y, Sun L L, Zhou Y C 2011 Acta Phys. Sin. 60 046105 (in Chinese) [马颖, 孙玲玲, 周益春 2011 物理学报 60 046105]
[9] Xiao S Q, Xie G F 2010 Acta Phys. Sin. 59 4808 (in Chinese) [肖松青, 谢国锋 2010 物理学报 59 4808]
[10] Ziegler J F, Biersack J P, Littmark U 1985 The Stopping and Range of Ions in Solids. (Pergamon, New York)
[11] Thomas B S, Marks N A, Begg B D 2007 Nucl. Instr. and Meth. B 254 211
[12] Smith K L, Zaluzec N J 2005 J. Nucl. Mater. 336 261
[13] Smith K L, Colella M, Cooper R, Vance E R 2003 J. Nucl. Mater. 321 19
-
[1] 曾启昱, 陈博, 康冬冬, 戴佳钰. 大规模、量子精度的分子动力学模拟: 以极端条件液态铁为例. 物理学报, 2023, 72(18): 187102. doi: 10.7498/aps.72.20231258 [2] 张硕, 龙连春, 刘静毅, 杨洋. 分子动力学方法研究缺陷对铁单质薄膜磁致伸缩的影响. 物理学报, 2021, (): . doi: 10.7498/aps.70.20211177 [3] 梁晋洁, 高宁, 李玉红. 体心立方Fe中 ${ \langle 100 \rangle}$ 位错环对微裂纹扩展影响的分子动力学研究. 物理学报, 2020, 69(11): 116102. doi: 10.7498/aps.69.20200317[4] 刘强, 郭巧能, 钱相飞, 王海宁, 郭睿林, 肖志杰, 裴海蛟. 循环载荷下纳米铜/铝薄膜孔洞形核、生长及闭合的分子动力学模拟. 物理学报, 2019, 68(13): 133101. doi: 10.7498/aps.68.20181901 [5] 王云天, 曾祥国, 杨鑫. 高应变率下温度对单晶铁中孔洞成核与生长影响的分子动力学研究. 物理学报, 2019, 68(24): 246102. doi: 10.7498/aps.68.20190920 [6] 袁伟, 彭海波, 杜鑫, 律鹏, 沈扬皓, 赵彦, 陈亮, 王铁山. 分子动力学模拟钠硼硅酸盐玻璃电子辐照诱导的结构演化效应. 物理学报, 2017, 66(10): 106102. doi: 10.7498/aps.66.106102 [7] 王成龙, 王庆宇, 张跃, 李忠宇, 洪兵, 苏折, 董良. SiC/C界面辐照性能的分子动力学研究. 物理学报, 2014, 63(15): 153402. doi: 10.7498/aps.63.153402 [8] 姜少宁, 万发荣, 龙毅, 刘传歆, 詹倩, 大貫惣明. 氦、氘对纯铁辐照缺陷的影响. 物理学报, 2013, 62(16): 166801. doi: 10.7498/aps.62.166801 [9] 崔振国, 勾成俊, 侯氢, 毛莉, 周晓松. 低能中子在锆中产生的辐照损伤的计算机模拟研究. 物理学报, 2013, 62(15): 156105. doi: 10.7498/aps.62.156105 [10] 兰惠清, 徐藏. 掺硅类金刚石薄膜摩擦过程的分子动力学模拟. 物理学报, 2012, 61(13): 133101. doi: 10.7498/aps.61.133101 [11] 杨平, 吴勇胜, 许海锋, 许鲜欣, 张立强, 李培. TiO2/ZnO纳米薄膜界面热导率的分子动力学模拟. 物理学报, 2011, 60(6): 066601. doi: 10.7498/aps.60.066601 [12] 汪志刚, 吴亮, 张杨, 文玉华. 面心立方铁纳米粒子的相变与并合行为的分子动力学研究. 物理学报, 2011, 60(9): 096105. doi: 10.7498/aps.60.096105 [13] 汪俊, 张宝玲, 周宇璐, 侯氢. 金属钨中氦行为的分子动力学模拟. 物理学报, 2011, 60(10): 106601. doi: 10.7498/aps.60.106601 [14] 马颖, 陈尚达, 谢国锋. SiC晶界薄膜的变电荷分子动力学模拟. 物理学报, 2009, 58(11): 7792-7796. doi: 10.7498/aps.58.7792 [15] 刘美林, 张宗宁, 李蔚, 赵骞, 祁阳, 张林. MgO（001）表面上沉积MgO薄膜过程的分子动力学模拟. 物理学报, 2009, 58(13): 199-S203. doi: 10.7498/aps.58.199 [16] 王 磊, 张忠强, 张洪武. 双壁碳纳米管电浸润现象的分子动力学模拟. 物理学报, 2008, 57(11): 7069-7077. doi: 10.7498/aps.57.7069 [17] 王海燕, 祝文军, 宋振飞, 刘绍军, 陈向荣, 贺红亮. 氦泡对铝的弹性性质的影响. 物理学报, 2008, 57(6): 3703-3708. doi: 10.7498/aps.57.3703 [18] 邵建立, 王 裴, 秦承森, 周洪强. 铁冲击相变的分子动力学研究. 物理学报, 2007, 56(9): 5389-5393. doi: 10.7498/aps.56.5389 [19] 周耐根, 周 浪. 外延生长薄膜中失配位错形成条件的分子动力学模拟研究. 物理学报, 2005, 54(7): 3278-3283. doi: 10.7498/aps.54.3278 [20] 陶永梅, 蒋 青, 曹海霞. 用横场伊辛模型研究应力对铁电薄膜的热力学性质的影响. 物理学报, 2005, 54(1): 274-279. doi: 10.7498/aps.54.274
计量
- 文章访问数: 6600
- PDF下载量: 698
- 被引次数: 0
下载: