Gd0.55Sr0.45MnO3薄膜光诱导电阻变化特性研究

赵省贵; 金克新; 罗炳成; 王建元; 陈长乐

doi:10.7498/aps.61.047501

摘要

分别采用固相反应和脉冲激光沉积的方法制备了电荷-轨道有序态锰氧化物Gd0.55Sr0.45MnO3块材和多晶薄膜, 研究了薄膜在光诱导作用下的电阻变化特性. 实验结果表明该薄膜在整个测量温度范围内表现出了半导体型导电特性. 利用变程跳跃模型拟合电阻温度关系可知, 其电荷有序态转变温度为70 K. 激光作用致使薄膜电阻减小, 当激光功率度为40 mW/mm2时, 最大光致电阻相对变化值可达99.8%, 且在8 s的时间内达到了平衡态, 温度对其影响很小; 当激光功率度为6 mW/mm2时, 获得的最大光致电阻相对变化值为44%, 而且时间常数随温度的升高而增大, 这主要是由于光诱导和热扰动共同作用的结果.

关键词:

Abstract

The compound and the film of the critical charge-ordering Gd0.55Sr0.45MnO3 thin film are prepared using the solid state reaction technique and the pulsed laser deposition method respectively. The properties of the photoinduced relative change in the resistance of the film are investigated. Experimental results indicate that the film exhibits the semiconductive conduction and the charge-ordering temperature is about 70 K from the fitting of a variable-range hopping model. The maximum value of the photoinduced relative change in resistance is about 99.8% when the laser with a power density of 40 mW/mm2 irradiates the film, and the rise time is about 8s independent of temperature. The maximum value of the photoinduced relative change in resistance is about 44% at T=20 K when the laser with a power density of 6 mW/mm2 irradiates the film. The time constant is increased with the increase of temperature, which is attributed to the competition between photoinduced effect and thermal fluctuation.

Keywords:

作者及机构信息

1.
西安科技大学理学院, 西安 710054;

2.
西北工业大学凝聚态结构与性质陕西省重点实验室, 西安 710072

基金项目: 国家自然科学基金(批准号: 51172183, 61078057和50702046), 陕西省教育厅科研计划项目(批准号: 2010JK673), 西北工业大学基础研究基金(批准号: NPU-FFR-JC200821和JC201048)和西北工业大学翱翔之星项目资助的课题.

Authors and contacts

1.
School of Science, Xi’an University of Science and Technology, Xi’an 710054, China;

2.
Shannxi Key Laboratory of Condensed Matter Structural and Properties, Northwestern Polytechnical University, Xian 710072, China

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos: 51172183, 61078057, 50702046), the Scientific Research Program Funded by Shaanxi Provincial Education Commission (Grant No. 2010JK673), NPU Foundation for Fundamental Research (Grant No. NPU-FFR-JC201048), and NWPU Aoxiang Star.

参考文献

[1]	Helmholt R V, Wecker J , Holzapel B , Schultz L, Samwer K 1993 Phys. Rev. Lett. 71 2331
[2]	Jin K X, Chen C L, Wang S L, Wang Y L, Wang Y C, Song Z M 2004 J. Appl. Phys. 96 1537
[3]	Tomioka Y, Tokura Y 2004 Phys. Rev. B 70 014432
[4]	Dho Joonghoe, Hur N H 2003 Phys. Rev. B 67 214414
[5]	Gao T, Cao S X, LiWJ, Kang B J, Yuan S J, Zhang J C 2006 Acta Phys. Sin. 55 3692 (in Chinese) [高湉, 曹世勋, 李文娟, 康保娟, 袁淑娟, 张金仓 2006 物理学报 55 3692]
[6]	Zhang R L, Song W H, Ma Y Q, Yang J, Zhao B C, Zheng G H, Sheng Z G, LuWJ, Sun Y P 2006 J. Phys. D: Appl. Phys. 39 621
[7]	Jin K X, Zhao S G, Chen C L 2009 Acta Phys. Sin. 58 4953 (in Chinese) [金克新, 赵省贵, 陈长乐 2009 物理学报 58 4953]
[8]	Takubo N, Ogimoto Y, Nakamura M, Tamaru H, Izumi M, Miyano K 2005 Phys. Rev. Lett. 95 017404
[9]	Takubo N, Onishi I, Takubo K, Mizokawa T, Miyano K 2008 Phys. Rev. Lett. 101 177403
[10]	Matsubara M, Okimoto Y, Ogasawara T, Tomioka Y, Okamoto H, Tokura Y 2007 Phys. Rev. Lett. 99 207401
[11]	Beyreuther E, Thiessen A, Grafström S , Eng L M, Dekker M C, Dörr K 2009 Phys. Rev. B 80 075106
[12]	Hu L, Sun Y P, Wang B, Sheng Z G, Luo X, Zhu X B, Yang Z R, Song W H, Dai J M, Yin Z Z, Wu W B 2009 J. Appl. Phys. 106 083903
[13]	Hu L, Sun Y P, Wand B, Luo X, Sheng Z G, Zhu X B, Song W H, Yang Z R, Dai J M 2010 Chin. Phys. Lett. 27 097504
[14]	Zhao S G, Jin K X, Chen C L 2007 J. Appl. Phys. 101 083701
[15]	Liu J M, Wang K F 2005 Progress in Physics 25 82
[16]	Kézsmárki I, Tomioka Y, Miyasaka S, DemkóL, Okimoto Y, Tokura Y 2008 Phys. Rev. B 77 075117
[17]	Chamberlin R V, Mozurkewich G, Orbach R 1991 J. Appl. Phys. 56 1714

施引文献

[1]	Helmholt R V, Wecker J , Holzapel B , Schultz L, Samwer K 1993 Phys. Rev. Lett. 71 2331
[2]	Jin K X, Chen C L, Wang S L, Wang Y L, Wang Y C, Song Z M 2004 J. Appl. Phys. 96 1537
[3]	Tomioka Y, Tokura Y 2004 Phys. Rev. B 70 014432
[4]	Dho Joonghoe, Hur N H 2003 Phys. Rev. B 67 214414
[5]	Gao T, Cao S X, LiWJ, Kang B J, Yuan S J, Zhang J C 2006 Acta Phys. Sin. 55 3692 (in Chinese) [高湉, 曹世勋, 李文娟, 康保娟, 袁淑娟, 张金仓 2006 物理学报 55 3692]
[6]	Zhang R L, Song W H, Ma Y Q, Yang J, Zhao B C, Zheng G H, Sheng Z G, LuWJ, Sun Y P 2006 J. Phys. D: Appl. Phys. 39 621
[7]	Jin K X, Zhao S G, Chen C L 2009 Acta Phys. Sin. 58 4953 (in Chinese) [金克新, 赵省贵, 陈长乐 2009 物理学报 58 4953]
[8]	Takubo N, Ogimoto Y, Nakamura M, Tamaru H, Izumi M, Miyano K 2005 Phys. Rev. Lett. 95 017404
[9]	Takubo N, Onishi I, Takubo K, Mizokawa T, Miyano K 2008 Phys. Rev. Lett. 101 177403
[10]	Matsubara M, Okimoto Y, Ogasawara T, Tomioka Y, Okamoto H, Tokura Y 2007 Phys. Rev. Lett. 99 207401
[11]	Beyreuther E, Thiessen A, Grafström S , Eng L M, Dekker M C, Dörr K 2009 Phys. Rev. B 80 075106
[12]	Hu L, Sun Y P, Wang B, Sheng Z G, Luo X, Zhu X B, Yang Z R, Song W H, Dai J M, Yin Z Z, Wu W B 2009 J. Appl. Phys. 106 083903
[13]	Hu L, Sun Y P, Wand B, Luo X, Sheng Z G, Zhu X B, Song W H, Yang Z R, Dai J M 2010 Chin. Phys. Lett. 27 097504
[14]	Zhao S G, Jin K X, Chen C L 2007 J. Appl. Phys. 101 083701
[15]	Liu J M, Wang K F 2005 Progress in Physics 25 82
[16]	Kézsmárki I, Tomioka Y, Miyasaka S, DemkóL, Okimoto Y, Tokura Y 2008 Phys. Rev. B 77 075117
[17]	Chamberlin R V, Mozurkewich G, Orbach R 1991 J. Appl. Phys. 56 1714

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板