液Zn对Fe2Al5涂层侵蚀的相变过程研究

孙文秀 阎殿然 陈学广 董艳春 李香芝

引用本文:
Citation:

液Zn对Fe2Al5涂层侵蚀的相变过程研究

孙文秀, 阎殿然, 陈学广, 董艳春, 李香芝

Erosion phase transition of Fe2Al5 coating in molten zinc

Sun Wen-Xiu, Yan Dian-Ran, Chen Xue-Guang, Dong Yan-Chun, Li Xiang-Zhi
PDF
导出引用
  • 本文对Fe2Al5涂层在液态Zn中的侵蚀相变过程进行了研究,实验结果表明:在侵蚀初期,靠界面张力平衡的作用,先发生热侵蚀,在试样表面形成热蚀沟,当热蚀沟达到一定程度后, 液Zn与Fe2Al5相由不浸润变为浸润;同时Zn原子扩散进入Fe2Al5相并形成Fe2Al5-Znx固溶体相(η相);随着侵蚀时间的增加,发生在腐蚀界面上的液Zn对Fe2Al5涂层的侵蚀过程是恒温相变过程,相变过程使Fe2Al5涂层发生定向熔化. 相变的驱动力来自于相成分的改变所引起的各相自由能的变化及各相间的相平衡的重新建立.
    The mechanism of erosion phase transition of Fe2Al5 coating in molten zinc was investigated. Experimental results indicated that etched grooves caused by interfacial tension equilibrium driving formed on sample surface. The Fe2Al5 phase, on where zinc did not adhere at the early stage of erosion, was infiltrated by zinc and solid solution Fe2Al5-Znx (η phase) was formed due to zinc atoms diffusing into Fe2Al5 phase. The erosion process of Fe2Al5 in molten zinc is directed melt at the interface caused by phase transition to drive. There were three types of phase interface,η/L,η/(η+δ)/L and η /(η+δ)/δ+L,formed in corroded area .The solid (S) / liquid (L) interface was phase-equilibrium interface and the S/S interface like η/(η+δ) and (η+δ)/δ were non phase-equilibrium interfaces at erosion temperature. The demand of phase-equilibrium interfaces and phase transitions of non-equilibrium interfaces, η→(η+δ) and (η+δ) →δ, made the S/L interface move towards to solid phase and Fe2Al5 phase was corroded by molten zinc.
    • 基金项目: 天津市高技术研究计划资助的课题.
    [1]

    [1]Kato T, Nunome K, Kaneko K, Saka H 2000 Acta Mater. 48 2257

    [2]

    [2]Inagaki J, Sakurai Y, Nishimoto A 1993 Tetsu to Hagane 79 1273 (in Japanese)

    [3]

    [3]Urednieck M, Kirkaldy J S 1973 Z. Metal. Kd. 64 899

    [4]

    [4]Adachi Y, Arai M 1998 Mater. Sci. Enging. A 254 305

    [5]

    [5]Guttmmann M, Lepretre Y, Aubry A, Roch M J, Moreau T, Drillet P, Mataigne J M, Baudin H 1995 Proceeding of the 3rd International Conference on Zinc and Zinc Alloy Coated Steel Sheet (Galvatech’95) Warrendale 1995 P295

    [6]

    [6]Zhang J H, Liu Z S, Qin Y Z. 1992 Acta Phys. Sin. 41 1474 (in Chinese)(张建华、刘增山、秦永志 1992 物理学报 41 1474)

    [7]

    [7]Wang C P, Liu X J, Ohnuma I, Kainuma R, Ishida K 2002 Science 297 990

    [8]

    [8]Liu X R, Cao C D, Wei B B 2003 Chin. Phys. 12 1266

    [9]

    [9]Long W Y, Cai Q Z ,C L L,Wei B K 2005 Acta Phy. Sin. 54 256 (in Chinese) [龙文元、蔡启舟、陈立亮、魏伯康 2005 物理学报 54 256]

    [10]

    ]Yao W J, Wei B B, 2003 Chin. Phys. 12 1272

    [11]

    ]Yao W J, Yang C, Han X J, Chen M, Wei B B ,Guo Z Y 2003Acta Phys. Sin. 52 448 (in Chinese) [姚文静、杨春、 韩秀君、陈民、魏丙泼、郭增元 2003 物理学报 52 448]

    [12]

    ]Liu Y, Wang F, Zhu C S, Wang Z P 2006 Acta Phys. Sin. 55 780 (in Chinese) [路阳、王帆、朱昌盛、王智平 2006 物理学报 55 780]

    [13]

    ]Li M E,Yang G C, Zhou Y H 2005 Acta Phys. Sin. 54 454 (in Chinese) [李梅娥、杨根仓、周尧和 2005 物理学报 54 454]

    [14]

    ]Shigeaki K,Takao Y 2002 Mater. Sci. Engng. A 338 44

    [15]

    ]Wang D G, Shi Z Y, Zou L J 2003 Appl. Surf. Sci. 214 304

    [16]

    ]Feutelais Y, Legendre B, de Avillze R R 2002 J. Alloys Comp. 346 211

    [17]

    ]Su X P, Tang N Y, Toguri J M 2001 J. Alloys Comp. 325 129

    [18]

    ]Chen Z W, Sharp R M,Gregory J T 1990 Mater. Sci. Technol. 12 1173

    [19]

    ]Hu G X, Qian M G 1980 Metallography (Shanghai: Shanghai Scientific and Technical Publishers) p331—332(in Chinese)[胡庚祥、钱苗根 1980 金属学(上海:上海科学技术出版社)第331—332页]

    [20]

    ]Liu B J 1995 Hot Dip Aluminizing for Steel and Iron (Beijing: metallurgical industry press) p145(in Chinese) [刘邦津 1995 钢材的热浸镀铝 (北京:冶金工业出版社) 第145页]

  • [1]

    [1]Kato T, Nunome K, Kaneko K, Saka H 2000 Acta Mater. 48 2257

    [2]

    [2]Inagaki J, Sakurai Y, Nishimoto A 1993 Tetsu to Hagane 79 1273 (in Japanese)

    [3]

    [3]Urednieck M, Kirkaldy J S 1973 Z. Metal. Kd. 64 899

    [4]

    [4]Adachi Y, Arai M 1998 Mater. Sci. Enging. A 254 305

    [5]

    [5]Guttmmann M, Lepretre Y, Aubry A, Roch M J, Moreau T, Drillet P, Mataigne J M, Baudin H 1995 Proceeding of the 3rd International Conference on Zinc and Zinc Alloy Coated Steel Sheet (Galvatech’95) Warrendale 1995 P295

    [6]

    [6]Zhang J H, Liu Z S, Qin Y Z. 1992 Acta Phys. Sin. 41 1474 (in Chinese)(张建华、刘增山、秦永志 1992 物理学报 41 1474)

    [7]

    [7]Wang C P, Liu X J, Ohnuma I, Kainuma R, Ishida K 2002 Science 297 990

    [8]

    [8]Liu X R, Cao C D, Wei B B 2003 Chin. Phys. 12 1266

    [9]

    [9]Long W Y, Cai Q Z ,C L L,Wei B K 2005 Acta Phy. Sin. 54 256 (in Chinese) [龙文元、蔡启舟、陈立亮、魏伯康 2005 物理学报 54 256]

    [10]

    ]Yao W J, Wei B B, 2003 Chin. Phys. 12 1272

    [11]

    ]Yao W J, Yang C, Han X J, Chen M, Wei B B ,Guo Z Y 2003Acta Phys. Sin. 52 448 (in Chinese) [姚文静、杨春、 韩秀君、陈民、魏丙泼、郭增元 2003 物理学报 52 448]

    [12]

    ]Liu Y, Wang F, Zhu C S, Wang Z P 2006 Acta Phys. Sin. 55 780 (in Chinese) [路阳、王帆、朱昌盛、王智平 2006 物理学报 55 780]

    [13]

    ]Li M E,Yang G C, Zhou Y H 2005 Acta Phys. Sin. 54 454 (in Chinese) [李梅娥、杨根仓、周尧和 2005 物理学报 54 454]

    [14]

    ]Shigeaki K,Takao Y 2002 Mater. Sci. Engng. A 338 44

    [15]

    ]Wang D G, Shi Z Y, Zou L J 2003 Appl. Surf. Sci. 214 304

    [16]

    ]Feutelais Y, Legendre B, de Avillze R R 2002 J. Alloys Comp. 346 211

    [17]

    ]Su X P, Tang N Y, Toguri J M 2001 J. Alloys Comp. 325 129

    [18]

    ]Chen Z W, Sharp R M,Gregory J T 1990 Mater. Sci. Technol. 12 1173

    [19]

    ]Hu G X, Qian M G 1980 Metallography (Shanghai: Shanghai Scientific and Technical Publishers) p331—332(in Chinese)[胡庚祥、钱苗根 1980 金属学(上海:上海科学技术出版社)第331—332页]

    [20]

    ]Liu B J 1995 Hot Dip Aluminizing for Steel and Iron (Beijing: metallurgical industry press) p145(in Chinese) [刘邦津 1995 钢材的热浸镀铝 (北京:冶金工业出版社) 第145页]

  • [1] 冯妍卉, 冯黛丽, 褚福强, 邱琳, 孙方远, 林林, 张欣欣. 纳米组装相变储热材料的热设计前沿. 物理学报, 2022, 71(1): 016501. doi: 10.7498/aps.71.20211776
    [2] 黄艳, 孙继忠, 桑超峰, 胡万鹏, 王德真. 边界局域模引起钨偏滤器靶板侵蚀和形貌变化的数值模拟研究. 物理学报, 2017, 66(3): 035201. doi: 10.7498/aps.66.035201
    [3] 闫文超, 苏鲁宁, 林晓宣, 杜飞, 袁大伟, 廖国前, 刘成, 沈忠伟, 陈黎明, 李玉同, 马景龙, 鲁欣, 王瑄, 王兆华, 魏志义, 盛政明, 张杰. 高反射效率高定向性的热解石墨晶体X射线谱仪. 物理学报, 2014, 63(17): 170701. doi: 10.7498/aps.63.170701
    [4] 王文鹏, 刘福生, 张宁超. 冲击加载下液态水的结构相变. 物理学报, 2014, 63(12): 126201. doi: 10.7498/aps.63.126201
    [5] 尚慧琳, 韩元波, 李伟阳. 时滞位置反馈对一类非线性相对转动系统混沌运动和安全盆侵蚀的控制. 物理学报, 2014, 63(11): 110502. doi: 10.7498/aps.63.110502
    [6] 孙振月, 桑超峰, 胡万鹏, 王德真. 偏滤器等离子体中杂质对钨壁材料的侵蚀模拟研究. 物理学报, 2014, 63(14): 145204. doi: 10.7498/aps.63.145204
    [7] 孙健, 刘伟强. 内嵌定向高导热层疏导式结构热防护机理分析. 物理学报, 2012, 61(12): 124401. doi: 10.7498/aps.61.124401
    [8] 王军国, 刘福生, 李永宏, 张明建, 张宁超, 薛学东. 在石英界面处液态水的冲击结构相变. 物理学报, 2012, 61(19): 196201. doi: 10.7498/aps.61.196201
    [9] 张世来, 刘福生, 彭小娟, 张明建, 李永宏, 马小娟, 薛学东. 纳秒尺度金属熔化相变数值模拟及实验验证. 物理学报, 2011, 60(1): 014401. doi: 10.7498/aps.60.014401
    [10] 尚慧琳. 时滞位移反馈对Helmholtz振子系统的分形侵蚀安全域的控制. 物理学报, 2011, 60(7): 070501. doi: 10.7498/aps.60.070501
    [11] 徐京城, 赵纪军. 液态硝基甲烷热分解行为及压力效应的第一性原理研究. 物理学报, 2009, 58(6): 4144-4149. doi: 10.7498/aps.58.4144
    [12] 陈斌, 彭向和, 范镜泓, 孙士涛, 罗吉. 考虑相变的热弹塑性本构方程及其应用. 物理学报, 2009, 58(13): 29-S34. doi: 10.7498/aps.58.29
    [13] 王 祺, 赵华波, 张朝晖. 高定向热解石墨表面局域导电增强现象的扫描探针显微学研究. 物理学报, 2008, 57(5): 3059-3063. doi: 10.7498/aps.57.3059
    [14] 戎海武, 王向东, 徐 伟, 方 同. 多频谐和与噪声作用下Flickering振子的安全盆侵蚀与混沌. 物理学报, 2008, 57(3): 1506-1513. doi: 10.7498/aps.57.1506
    [15] 秦 莉, 张喜田, 梁 瑶, 张 锷, 高 红, 张治国. 氧化锌微米花的共振拉曼和“负热淬灭”效应. 物理学报, 2006, 55(6): 3119-3123. doi: 10.7498/aps.55.3119
    [16] 王 进, 赵志刚, 刘 楣, 邢定钰. 磁通格子的有序-无序相变和反向熔化. 物理学报, 2003, 52(12): 3162-3167. doi: 10.7498/aps.52.3162
    [17] 龚璞林, 徐健学, 孙政策. 弱的参数周期扰动对一非线性系统安全域的影响与分形侵蚀安全域的控制. 物理学报, 2001, 50(5): 841-846. doi: 10.7498/aps.50.841
    [18] 吴德昌, 王仁卉. 锌的X射线热漫散衍射及弹性系数. 物理学报, 1966, 22(5): 533-540. doi: 10.7498/aps.22.533
    [19] 郭常霖, 唐士鑫. 侵蚀法测定碳化硅结构极性的研究. 物理学报, 1966, 22(7): 831-835. doi: 10.7498/aps.22.831
    [20] 闵乃本, 吉光民, 冯端. 钨单晶体中位错的侵蚀斑. 物理学报, 1964, 20(11): 1182-1186. doi: 10.7498/aps.20.1182
计量
  • 文章访问数:  6971
  • PDF下载量:  1013
  • 被引次数: 0
出版历程
  • 收稿日期:  2009-09-25
  • 修回日期:  2009-10-12
  • 刊出日期:  2010-02-05

/

返回文章
返回