微结构对Eu掺杂Bi4Ti3O12铁电薄膜铁电性能的影响

吕业刚; 梁晓琳; 谭永宏; 郑学军; 龚跃球; 何林

doi:10.7498/aps.60.027701

摘要

采用金属有机物分解法在Pt/Ti/Si(111)基底上制备了退火温度分别为600℃,650℃,700℃的Bi3.15Eu0.85Ti3O12(BET)铁电薄膜,并对其结构及铁电性能进行了测试,再使用扫描探针显微镜对BET薄膜的电畴翻转进行了实时观测.BET薄膜c畴发生180°畴变的最小电压为+6V,而r畴由于其高四方性,即使极化电压增至+12V也不会发生翻转.薄膜的铁电性主要源于c畴的极化,随着退火温度的升高,c畴的区域面积增加,BET薄膜的剩余极化强度随之增大.退火温度为700℃的BET薄膜剩余极化强度达到84μC/cm2.

关键词:

Abstract

Eu-doped bismuth titanate Bi3.15Eu0.85Ti3O12 (BET) ferroelectric thin film was prepared on the Pt/Ti/Si(111) substrates by metal-organic decomposition (MOD) at different annealing temperatures of 600℃, 650℃ and 700℃. The structure and ferroelectric properties of BET thin film were analyzed. The nanoscale domain switching was investigated by scanning probe microscopy (SPM) via direct observation. When the polarizing voltage increases to +6V, the ferroelectric c-domain suffers 180° domain switching. The ferroelectric r-domain can not be reversed due to its highly tetragonal structure even if the polarized voltage value increases to +12V. The ferroelectric properties of the BET thin films are dependent on the polarization of ferroelectric c-domain. With the increasing annealing temperature, the area of c-domain becomes larger, and the remnant polarization (2Pr) values of BET films increase. The value of 2Pr reaches 84μC/cm for BET thin film annealed at the temperature of 700℃.

Keywords:

作者及机构信息

(1)湖南科技学院电子工程系,永州 425100; (2)湖南科技学院电子工程系,永州 425100;湘潭大学材料与光电物理学院,湘潭 411105; (3)湘潭大学材料与光电物理学院,湘潭 411105

基金项目: 湖南永州市科技局(批准号:永科发[2009]20号)资助的课题.

Authors and contacts

(1)Department of Electronic Engineering, Hunan University of Science and Engineering, Yongzhou 425100, China; (2)Department of Electronic Engineering, Hunan University of Science and Engineering, Yongzhou 425100, China;Faculty of Material and Photoelectronic Physics, Xiangtan University, Xiangtan 411105, China; (3)Faculty of Material and Photoelectronic Physics, Xiangtan University, Xiangtan 411105, China

参考文献

[1]	Funakubo H, Watanabe T, Kojima T, Sakai T, Noguchi Y, Miyayama M, Osada M, Kakihana M, Saito K 2003 J. Cryst. Growth 248 180
[2]	Lee H N, Hesse D, Zakharov N 2002 Science 296 2006
[3]	[刘洪、蒲朝辉、龚小刚、王志红、黄惠东、李言荣、肖定金、朱建国 2006 物理学报 55 6123]
[4]	Zhong X L, Wang J B, Zheng X J, Zhou Y C, Yang G W 2004 Appl. Phys. Lett. 85 5661
[5]	Wu Y Y, Wang X H, Li L T 2010 Chin. Phys. B 19 037701
[6]	Fu C, Huang Z, Li J, Guo D 2008 Sci. China Ser. E 51 1439
[7]	Wu X M, Chen H, Zhai Y, Lu X M, Liu Y F, Zhu J S 2010 Chin. Phys. B 19 036802
[8]	Chon U, Jang H M, Kim M G, Chang C H 2002 Phys. Rev. Lett. 89 087601
[9]	Lim K T, Kim K T, Kim D P, Kim C 2004 Thin Solid Films 447 337
[10]	Liu H, Pu C H, Gong X G, Wang Z H, Huang H D, Li Y R, Xiao D Q, Zhu J G 2006 Acta Phys. Sin. 55 6123 (in Chinese)
[11]	Zeng H R, Yu H F, Chu R Q, Li G R, Yin Q R, Tang X G 2005 Acta Phys. Sin. 54 1437 (in Chinese) [曾华荣、余寒峰、初瑞清、李国荣、殷庆瑞、唐新桂 2005 物理学报 54 1437]
[12]	Anbusathaiah V, Nagarajan V, Aggarwal S 2006 Appl. Phys. Lett. 89 132912
[13]	Wang L H, Yu J, Liu F, Zheng C D, Li J, Wang Y B, Gao J X, Wang Z H, Zeng H Z, Zhao S L 2006 Acta Phys. Sin. 55 2590 (in Chinese) [王龙海、于军、刘峰、郑朝丹、李佳、王耘波、高峻雄、王志红、曾慧中、赵素玲 2006 物理学报〖13] Tan C B, Zhong X L, Wang J B, Liao M, Zhon Y C, Pan W 2007 Acta Phys. Sin. 56 6084 (in Chinese) [谭丛兵、钟向丽、王金斌、廖敏、周益春、潘伟 2007 物理学报 56 6084]
[14]	Oh Y N, Yoon S G 2005 Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures 23 1029
[15]	Yau C Y, Palan R, Tran K, Buchanan R C 2005 Appl. Phys. Lett. 86 032907
[16]	Guo D Y, Wang Y B, Yu J, Gao J X, Li M Y 2006 Acta Phys. Sin. 55 5551 (in Chinese) [郭冬云、王耘波、于军、高俊雄、李美亚 2006 物理学报 55 5551]
[17]	Zheng X J, He L, Zhou Y C, Tang M H 2006 Appl. Phys. Lett. 89 252908
[18]	Kelman M B, Schloss L F, McIntyre P C, Hendrix B C, Bilodeau S M, Roeder J F 2002 Appl. Phys. Lett. 80 1258
[19]	Chen X, Zhu W, Tan O K, Yao X 2002 Mater. Chem. Phys. 75 90
[20]	Cheng S Y, Ho N J, Lu H Y 2008 J. Am. Ceram. Soc. 91 3721

施引文献

[1]	Funakubo H, Watanabe T, Kojima T, Sakai T, Noguchi Y, Miyayama M, Osada M, Kakihana M, Saito K 2003 J. Cryst. Growth 248 180
[2]	Lee H N, Hesse D, Zakharov N 2002 Science 296 2006
[3]	[刘洪、蒲朝辉、龚小刚、王志红、黄惠东、李言荣、肖定金、朱建国 2006 物理学报 55 6123]
[4]	Zhong X L, Wang J B, Zheng X J, Zhou Y C, Yang G W 2004 Appl. Phys. Lett. 85 5661
[5]	Wu Y Y, Wang X H, Li L T 2010 Chin. Phys. B 19 037701
[6]	Fu C, Huang Z, Li J, Guo D 2008 Sci. China Ser. E 51 1439
[7]	Wu X M, Chen H, Zhai Y, Lu X M, Liu Y F, Zhu J S 2010 Chin. Phys. B 19 036802
[8]	Chon U, Jang H M, Kim M G, Chang C H 2002 Phys. Rev. Lett. 89 087601
[9]	Lim K T, Kim K T, Kim D P, Kim C 2004 Thin Solid Films 447 337
[10]	Liu H, Pu C H, Gong X G, Wang Z H, Huang H D, Li Y R, Xiao D Q, Zhu J G 2006 Acta Phys. Sin. 55 6123 (in Chinese)
[11]	Zeng H R, Yu H F, Chu R Q, Li G R, Yin Q R, Tang X G 2005 Acta Phys. Sin. 54 1437 (in Chinese) [曾华荣、余寒峰、初瑞清、李国荣、殷庆瑞、唐新桂 2005 物理学报 54 1437]
[12]	Anbusathaiah V, Nagarajan V, Aggarwal S 2006 Appl. Phys. Lett. 89 132912
[13]	Wang L H, Yu J, Liu F, Zheng C D, Li J, Wang Y B, Gao J X, Wang Z H, Zeng H Z, Zhao S L 2006 Acta Phys. Sin. 55 2590 (in Chinese) [王龙海、于军、刘峰、郑朝丹、李佳、王耘波、高峻雄、王志红、曾慧中、赵素玲 2006 物理学报〖13] Tan C B, Zhong X L, Wang J B, Liao M, Zhon Y C, Pan W 2007 Acta Phys. Sin. 56 6084 (in Chinese) [谭丛兵、钟向丽、王金斌、廖敏、周益春、潘伟 2007 物理学报 56 6084]
[14]	Oh Y N, Yoon S G 2005 Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures 23 1029
[15]	Yau C Y, Palan R, Tran K, Buchanan R C 2005 Appl. Phys. Lett. 86 032907
[16]	Guo D Y, Wang Y B, Yu J, Gao J X, Li M Y 2006 Acta Phys. Sin. 55 5551 (in Chinese) [郭冬云、王耘波、于军、高俊雄、李美亚 2006 物理学报 55 5551]
[17]	Zheng X J, He L, Zhou Y C, Tang M H 2006 Appl. Phys. Lett. 89 252908
[18]	Kelman M B, Schloss L F, McIntyre P C, Hendrix B C, Bilodeau S M, Roeder J F 2002 Appl. Phys. Lett. 80 1258
[19]	Chen X, Zhu W, Tan O K, Yao X 2002 Mater. Chem. Phys. 75 90
[20]	Cheng S Y, Ho N J, Lu H Y 2008 J. Am. Ceram. Soc. 91 3721

[1]	田国, 樊贞, 陈德杨, 侯志鹏, 刘俊明, 高兴森. “针尖下的实验室”—扫描探针探测与调控铁电畴及其微观物性. 物理学报, 2023, 72(20): 207501. doi: 10.7498/aps.72.20230954
[2]	白刚, 韩宇航, 高存法. (111)取向无铅K_0.5Na_0.5NbO₃外延薄膜的相变和电卡效应: 外应力与错配应变效应. 物理学报, 2022, 71(9): 097701. doi: 10.7498/aps.71.20220234
[3]	白刚, 林翠, 刘端生, 许杰, 李卫, 高存法. 取向相关的Pb(Zr_0.52Ti_0.48)O₃外延薄膜的相图和介电性能. 物理学报, 2021, 70(12): 127701. doi: 10.7498/aps.70.20202164
[4]	石志鑫, 周大雨, 李帅东, 徐进, UweSchröder. 一阶回转曲线图谱法及其在HfO₂基铁电薄膜极化翻转行为研究中的应用. 物理学报, 2021, 70(12): 127702. doi: 10.7498/aps.70.20210115
[5]	包定华. 稀土发光铁电薄膜的研究进展. 物理学报, 2020, 69(12): 127712. doi: 10.7498/aps.69.20200738
[6]	佘彦超, 张蔚曦, 王应, 罗开武, 江小蔚. 氧空位缺陷对PbTiO3铁电薄膜漏电流的调控. 物理学报, 2018, 67(18): 187701. doi: 10.7498/aps.67.20181130
[7]	王歆钰, 储瑞江, 魏胜男, 董正超, 仲崇贵, 曹海霞. 应力作用下EuTiO3铁电薄膜电热效应的唯象理论研究. 物理学报, 2015, 64(11): 117701. doi: 10.7498/aps.64.117701
[8]	卢兆信. 参数修改对铁电薄膜相变性质的影响. 物理学报, 2013, 62(11): 116802. doi: 10.7498/aps.62.116802
[9]	文娟辉, 杨琼, 曹觉先, 周益春. 铁电薄膜漏电流的应变调控. 物理学报, 2013, 62(6): 067701. doi: 10.7498/aps.62.067701
[10]	华宝成, 钱建强, 王曦, 姚骏恩. 应用于扫描探针显微镜的石英音叉机械模型研究. 物理学报, 2011, 60(4): 040702. doi: 10.7498/aps.60.040702
[11]	朱杰, 张辉, 张鹏翔, 谢康, 胡俊涛. Pb(Zr0.3Ti0.7)O3铁电薄膜激光感生电压效应. 物理学报, 2010, 59(9): 6417-6422. doi: 10.7498/aps.59.6417
[12]	吕业刚, 梁晓琳, 龚跃球, 郑学军, 刘志壮. 外加电场对铁电薄膜相变的影响. 物理学报, 2010, 59(11): 8167-8171. doi: 10.7498/aps.59.8167
[13]	赵晓英, 刘世建, 褚君浩, 戴宁, 胡古今. 锆钛酸铅双层膜的铁电及光学特性研究. 物理学报, 2008, 57(9): 5968-5972. doi: 10.7498/aps.57.5968
[14]	王龙海, 于军, 王耘波, 高峻雄, 赵素玲. PbTiO3/PbZr0.3Ti0.7O3/PbTiO3夹心结构铁电薄膜子晶层的优化. 物理学报, 2008, 57(2): 1207-1213. doi: 10.7498/aps.57.1207
[15]	王英龙, 魏同茹, 刘保亭, 邓泽超. 外延PbZr0.4Ti0.6O3薄膜厚度对其铁电性能的影响. 物理学报, 2007, 56(5): 2931-2936. doi: 10.7498/aps.56.2931
[16]	王华, 任鸣放. Si基Bi3.25La0.75Ti3O12铁电薄膜的制备与特性研究. 物理学报, 2006, 55(6): 3152-3156. doi: 10.7498/aps.55.3152
[17]	黄平, 徐廷献, 崔彩娥. SrBi4Ti4O15铁电薄膜的制备工艺及薄膜生长机理研究. 物理学报, 2006, 55(3): 1464-1471. doi: 10.7498/aps.55.1464
[18]	王龙海, 于军, 刘锋, 郑朝丹, 李佳, 王耘波, 高峻雄, 王志红, 曾慧中, 赵素玲. PT/PZT/PT铁电薄膜的铁电畴和畴壁. 物理学报, 2006, 55(5): 2590-2595. doi: 10.7498/aps.55.2590
[19]	陶永梅, 蒋青, 曹海霞. 用横场伊辛模型研究应力对铁电薄膜的热力学性质的影响. 物理学报, 2005, 54(1): 274-279. doi: 10.7498/aps.54.274
[20]	王华. Si基Bi4Ti3O12铁电薄膜的制备与特性研究. 物理学报, 2004, 53(4): 1265-1270. doi: 10.7498/aps.53.1265

计量

文章访问数: 7904
PDF下载量: 732
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板