纳米VOx薄膜在空气中的电学特性退化研究

罗振飞 吴志明 许向东 王涛 蒋亚东

引用本文:
Citation:

纳米VOx薄膜在空气中的电学特性退化研究

罗振飞, 吴志明, 许向东, 王涛, 蒋亚东

Aging in the electrical properties of nanostructured vanadium oxide thin film exposed to air

Luo Zhen-Fei, Wu Zhi-Ming, Xu Xiang-Dong, Wang Tao, Jiang Ya-Dong
PDF
导出引用
  • 采用射频磁控溅射法在氮化硅衬底上沉积纳米VOx薄膜,利用X射线衍射、原子力显微镜分别对薄膜的结晶形态及表面形貌进行表征.研究了纳米VOx薄膜在空气中长时间暴露后的方块电阻、热滞回线等电学特性的变化情况,并分析这些变化给器件带来的影响.利用X射线光电子能谱仪、傅里叶变换红外光谱仪分析对比新制与久置薄膜的组分及分子结构差异.研究表明,暴露在空气中的纳米VOx薄膜方块电阻增大是因为低价钒离子被吸附氧原子氧
    Radio frequency magnetron sputtering method is used to grow nanostructured VOx thin film on silicon nitride layer. X-ray diffraction and atomic force microscope are used to characterize the crystal structure and surface morphology, respectively. The variations of square resistance and thermal hysteresis loop are studied when the film is exposed to air for a long period of time, and the effects of these variations on the performance of device are analyzed. X-ray photoelectron spectrometer and Fourier transform infrared spectroscopy are employed to investigate the differences in composition and molecular structure between the fresh and aged films. The results indicate that the increase of square resistance is due to the oxidation of vanadium ions with low oxidation states. The reason to cause the change of thermal hysteresis loop is that the molecular structure of nanostructured VOx thin film is affected by the adsorbed atoms and functional groups.
    [1]

    Yuan N Y, Li J H, Lin C L 2002 Acta Phys. Sin. 51 852 (in Chinese) [袁宁一、李金华、林成鲁 2002 物理学报 51 852]

    [2]

    Wang L X, Li J P, He X L, Gao X G 2006 Acta Phys. Sin. 55 2846 (in Chinese) [王利霞、李建平、何秀丽、高晓光 2006 物理学报 55 2846]

    [3]

    Chen C H, Huang D X, Zhu P 2007 Acta Phys. Sin. 56 5221 (in Chinese) [陈长虹、黄德修、朱 鹏 2007 物理学报 56 5221]

    [4]

    Verkelis J, Bliznikas Z, Breive K, Dikinis V, Sarmatis R 1998 Sens. Actuators A 68 338

    [5]

    Gentle A, Maaroof A I, Smith G B 2007 Nanotechnology 18 025202-1

    [6]

    Wang H C, Yi X J, Lai J J, Li Y 2005 Chin. Phys. Lett. 22 1746

    [7]

    Wang H C, Yi X J, Li Y 2005 Opt. Commun. 256 305

    [8]

    Fieldhouse N, Pursel S M, Carey R, Horn M W, Bharadwaja S S N 2009 J. Vac. Sci. Technol. A 27 951

    [9]

    Wang X J, Liang C J, Guan K P, Li D H, Nie Y X, Zhu S Q, Huang F, Zhang W W, Cheng Z W 2008 Chin. Phys. B 17 3512

    [10]

    Gurvitch M, Luryi S, Polyakov A, Shabalov A, Dudley M, Wang G, Ge S, Yakovlev V 2007 J. Appl. Phys. 102 033504

    [11]

    Ruzmetov D, Senanayake S D, Ramanathan S 2007 Phys. Rev. B 75 195102

    [12]

    Moshfegh A Z, Ignatiev A 1992 Surf. Sci. Lett. 275 L650

    [13]

    Bondarenka V, Grebinskij S, Kaciulis S, Mattogno G, Mickevicius S, Tvardauskas H, Volkov V, Zakharova G 2001 J. Electron. Spectrosc. Relat. Phenom. 120 131

    [14]

    Bullot J, Cordier P, Gallais O, Gauthier M 1984 J. Non-crystal. Sol. 68 123

    [15]

    Pan M X, Cao X Z, Li Y X, Wang B Y, Xue D S, Ma C X, Zhou C L, Wei L 2004 Acta Phys. Sin. 53 1956 (in Chinese) [潘梦霄、曹兴忠、李养贤、王宝义、薛德胜、马创新、周春兰、魏 龙 2004 物理学报 53 1956]

    [16]

    Bahgat A, Al-Hajry A, El-Desoky M M 2006 Phys. Status Solidi A 203 1999

    [17]

    Abello L, Husson E, Repelin Y, Lucazeau G 1983 Spectrochim. Acta A 39 641

    [18]

    Klimov V A, Timofeeva I O, Khanin S D, Shadrin E B, Il’inskii A V, Silva-Andrade F 2003 Semiconductors 37 370

  • [1]

    Yuan N Y, Li J H, Lin C L 2002 Acta Phys. Sin. 51 852 (in Chinese) [袁宁一、李金华、林成鲁 2002 物理学报 51 852]

    [2]

    Wang L X, Li J P, He X L, Gao X G 2006 Acta Phys. Sin. 55 2846 (in Chinese) [王利霞、李建平、何秀丽、高晓光 2006 物理学报 55 2846]

    [3]

    Chen C H, Huang D X, Zhu P 2007 Acta Phys. Sin. 56 5221 (in Chinese) [陈长虹、黄德修、朱 鹏 2007 物理学报 56 5221]

    [4]

    Verkelis J, Bliznikas Z, Breive K, Dikinis V, Sarmatis R 1998 Sens. Actuators A 68 338

    [5]

    Gentle A, Maaroof A I, Smith G B 2007 Nanotechnology 18 025202-1

    [6]

    Wang H C, Yi X J, Lai J J, Li Y 2005 Chin. Phys. Lett. 22 1746

    [7]

    Wang H C, Yi X J, Li Y 2005 Opt. Commun. 256 305

    [8]

    Fieldhouse N, Pursel S M, Carey R, Horn M W, Bharadwaja S S N 2009 J. Vac. Sci. Technol. A 27 951

    [9]

    Wang X J, Liang C J, Guan K P, Li D H, Nie Y X, Zhu S Q, Huang F, Zhang W W, Cheng Z W 2008 Chin. Phys. B 17 3512

    [10]

    Gurvitch M, Luryi S, Polyakov A, Shabalov A, Dudley M, Wang G, Ge S, Yakovlev V 2007 J. Appl. Phys. 102 033504

    [11]

    Ruzmetov D, Senanayake S D, Ramanathan S 2007 Phys. Rev. B 75 195102

    [12]

    Moshfegh A Z, Ignatiev A 1992 Surf. Sci. Lett. 275 L650

    [13]

    Bondarenka V, Grebinskij S, Kaciulis S, Mattogno G, Mickevicius S, Tvardauskas H, Volkov V, Zakharova G 2001 J. Electron. Spectrosc. Relat. Phenom. 120 131

    [14]

    Bullot J, Cordier P, Gallais O, Gauthier M 1984 J. Non-crystal. Sol. 68 123

    [15]

    Pan M X, Cao X Z, Li Y X, Wang B Y, Xue D S, Ma C X, Zhou C L, Wei L 2004 Acta Phys. Sin. 53 1956 (in Chinese) [潘梦霄、曹兴忠、李养贤、王宝义、薛德胜、马创新、周春兰、魏 龙 2004 物理学报 53 1956]

    [16]

    Bahgat A, Al-Hajry A, El-Desoky M M 2006 Phys. Status Solidi A 203 1999

    [17]

    Abello L, Husson E, Repelin Y, Lucazeau G 1983 Spectrochim. Acta A 39 641

    [18]

    Klimov V A, Timofeeva I O, Khanin S D, Shadrin E B, Il’inskii A V, Silva-Andrade F 2003 Semiconductors 37 370

  • [1] 洪梓凡, 陈海峰, 贾一凡, 祁祺, 刘英英, 过立新, 刘祥泰, 陆芹, 李立珺, 王少青, 关云鹤, 胡启人. 引入籽晶层的物理溅射生长Ga2O3外延薄膜特性研究. 物理学报, 2020, 69(22): 228103. doi: 10.7498/aps.69.20200810
    [2] 张传军, 邬云骅, 曹鸿, 高艳卿, 赵守仁, 王善力, 褚君浩. 不同衬底和CdCl2退火对磁控溅射CdS薄膜性能的影响. 物理学报, 2013, 62(15): 158107. doi: 10.7498/aps.62.158107
    [3] 江强, 毛秀娟, 周细应, 苌文龙, 邵佳佳, 陈明. 外加磁场对磁控溅射制备氮化硅陷光薄膜的影响. 物理学报, 2013, 62(11): 118103. doi: 10.7498/aps.62.118103
    [4] 杨铎, 钟宁, 尚海龙, 孙士阳, 李戈扬. 磁控溅射(Ti, N)/Al纳米复合薄膜的微结构和力学性能. 物理学报, 2013, 62(3): 036801. doi: 10.7498/aps.62.036801
    [5] 魏晓林, 陈元平, 王如志, 钟建新. 含孔缺陷石墨烯纳米条带的电学特性研究. 物理学报, 2013, 62(5): 057101. doi: 10.7498/aps.62.057101
    [6] 赵守仁, 黄志鹏, 孙雷, 孙朋超, 张传军, 邬云华, 曹鸿, 王善力, 褚君浩. 碲化镉薄膜太阳能电池电学特性参数分析. 物理学报, 2013, 62(18): 188801. doi: 10.7498/aps.62.188801
    [7] 苏元军, 徐军, 朱明, 范鹏辉, 董闯. 利用等离子体辅助脉冲磁控溅射实现多晶硅薄膜的低温沉积. 物理学报, 2012, 61(2): 028104. doi: 10.7498/aps.61.028104
    [8] 沈向前, 谢泉, 肖清泉, 陈茜, 丰云. 磁控溅射辉光放电特性的模拟研究. 物理学报, 2012, 61(16): 165101. doi: 10.7498/aps.61.165101
    [9] 李林娜, 陈新亮, 王斐, 孙建, 张德坤, 耿新华, 赵颖. H2 气对脉冲磁控溅射铝掺杂氧化锌薄膜性能的影响. 物理学报, 2011, 60(6): 067304. doi: 10.7498/aps.60.067304
    [10] 曹月华, 狄国庆. 磁控溅射制备Y2O3-TiO2薄膜形貌的研究. 物理学报, 2011, 60(3): 037702. doi: 10.7498/aps.60.037702
    [11] 狄国庆. 溅射制备Ta2O5薄膜的表面形貌与光学特性. 物理学报, 2011, 60(3): 038101. doi: 10.7498/aps.60.038101
    [12] 丁万昱, 徐军, 陆文琪, 邓新绿, 董闯. 微波ECR磁控溅射制备SiNx薄膜的XPS结构研究. 物理学报, 2009, 58(6): 4109-4116. doi: 10.7498/aps.58.4109
    [13] 刘 峰, 孟月东, 任兆杏, 舒兴胜. 感应耦合等离子体增强射频磁控溅射沉积ZrN薄膜及其性能研究. 物理学报, 2008, 57(3): 1796-1801. doi: 10.7498/aps.57.1796
    [14] 邱东江, 王 俊, 丁扣宝, 施红军, 郏 寅. 退火对Mn和N共掺杂的Zn0.88Mn0.12O:N薄膜特性的影响. 物理学报, 2008, 57(8): 5249-5255. doi: 10.7498/aps.57.5249
    [15] 张 辉, 刘应书, 刘文海, 王宝义, 魏 龙. 基片温度与氧分压对磁控溅射制备氧化钒薄膜的影响. 物理学报, 2007, 56(12): 7255-7261. doi: 10.7498/aps.56.7255
    [16] 刘志文, 谷建峰, 孙成伟, 张庆瑜. 磁控溅射ZnO薄膜的成核机制及表面形貌演化动力学研究. 物理学报, 2006, 55(4): 1965-1973. doi: 10.7498/aps.55.1965
    [17] 丁万昱, 徐 军, 李艳琴, 朴 勇, 高 鹏, 邓新绿, 董 闯. 微波ECR等离子体增强磁控溅射制备SiNx薄膜及其性能分析. 物理学报, 2006, 55(3): 1363-1368. doi: 10.7498/aps.55.1363
    [18] 李蕾蕾, 刘红侠, 于宗光, 郝 跃. 恒流应力下E2PROM隧道氧化层的退化特性研究. 物理学报, 2006, 55(5): 2459-2463. doi: 10.7498/aps.55.2459
    [19] 周小莉, 杜丕一. 磁控溅射法制备的CaCu3Ti4O12薄膜. 物理学报, 2005, 54(4): 1809-1813. doi: 10.7498/aps.54.1809
    [20] 张仁刚, 王宝义, 张 辉, 马创新, 魏 龙. 不同参数溅射的ZnO薄膜硫化后的特性. 物理学报, 2005, 54(5): 2389-2393. doi: 10.7498/aps.54.2389
计量
  • 文章访问数:  7054
  • PDF下载量:  682
  • 被引次数: 0
出版历程
  • 收稿日期:  2010-03-18
  • 修回日期:  2010-09-06
  • 刊出日期:  2011-03-05

/

返回文章
返回