H2 气对脉冲磁控溅射铝掺杂氧化锌薄膜性能的影响

李林娜 陈新亮 王斐 孙建 张德坤 耿新华 赵颖

引用本文:
Citation:

H2 气对脉冲磁控溅射铝掺杂氧化锌薄膜性能的影响

李林娜, 陈新亮, 王斐, 孙建, 张德坤, 耿新华, 赵颖

Effects of hydrogen flux on aluminum doped zinc thin films by pulsed magnetron sputtering

Li Lin-Na, Chen Xin-Liang, Wang Fei, Sun Jian, Zhang De-Kun, Geng Xin-Hua, Zhao Ying
PDF
导出引用
  • 实验采用脉冲磁控溅射法制备铝掺杂氧化锌(AZO)薄膜.为了进一步提高AZO薄膜的光电性能,在溅射过程中加入一定流量的氢气,以高纯ZnO ∶Al2O3陶瓷靶为溅射靶材,制备AZO/H透明导电薄膜.通过测试薄膜的结构特性、表面形貌及其光电性能,详细地研究了氢气流量对AZO薄膜性能的影响.溅射过程中引入氢气,可以促进薄膜的晶化,提高薄膜的迁移率和透过率(400—1100 nm).采用纯氩气溅射制备AZO薄膜的电阻率为5.664×10-4 Ω·cm
    Aluminum doped zinc oxide (AZO) thin films are prepared by pulsed magnetron sputtering in pure argon gas. In order to improve the properties of AZO thin films, we add hydrogen gas into vacuum during sputtering. High purity ceramic ZnO ∶Al2O3 target and hydrogen gas at various flow rates are used as source materials. The microstructure, the surface information, the optical and electrical properties of AZO/H film are investigated. The crystallization, the Hall mobility and the transmission between 400 nm and 1100 nm are enhanced by increasing H2 flow rate, and resistivity is decreased, the lowest resistivities of these films are all 4.435×10-4 Ω·cm, and AZO thin films with 5.664×10-4 Ω·cm are achieved. In this experiment, it is observed that Raman peak is related to defects due to O-vacancies (579 cm-1) in the AZO/H thin films grown at different H2 flow rates. With the increase of hydrogen flow rate, the intensity of Raman peak at 579 cm-1 decreases. Finally, AZO and AZO/H thin films are etched in 0.5% dilute hydrochloric acid. Compared with AZO thin films, AZO/H thin films can be relatively easy to achieve the light trapping structure with crater-type morphology.
    • 基金项目: 国家重点基础研究发展计划(批准号:2006CB202602,2006CB202603)、国家高技术研究发展计划(批准号:2009AA050602)、天津市应用基础及前沿技术研究计划(批准号:09JCYBJC06900)和中央高校基本科研业务费专项资金资助的课题.
    [1]

    Chen X L, Geng X H, Xue J M, Zhang D K, Hou G F, Zhao Y 2006 J. Crystal Growth 296 43

    [2]

    Meier J, Kroll U, Dubail S, Golay S, Fay S, Dubail J, Shah A 2000 Photovoltaic Specialists Conference (Conference Record of the 28th IEEE) AK: Anchorage, USA, September 15—22, 2000 p746

    [3]

    Chen X L, Xue J M, Zhang D K, Sun J, Ren H Z, Zhao Y, Geng X H 2007 Acta Phys. Sin. 56 1563(in Chinese) [陈新亮、薛俊明、张德坤、孙 建、任慧志、赵 颖、耿新华 2007 物理学报 56 1563]

    [4]

    Dewald W, Sittinger V, Werner W, Jacobs C, Szyszka B 2009 Thin Solid Films 518 1085

    [5]

    Duan L W, Xue J M, Yang R X, Zhao Y, Geng X H 2008 J. Optoelectron. Laser 19 1206 (in Chinese) [段苓伟、薛俊明、杨瑞霞、赵 颖、耿新华 2008 光电子·激光 19 1206]

    [6]

    Sittinger V, Ruske F, Werner W, Szyszka B, Rech B, Hüpkes J, Schöpe G, Stiebig H 2006 Thin Solid Films 496 16

    [7]

    Ellmer K, Klein A, Rech B 2008 Transparent Conductive Zinc Oxide (New York: Springer) p36

    [8]

    Müller J, Rech B, Springer J, Vanecek M 2004 Sol. Energ. 77 917

    [9]

    Patterson A L 1939 Phys. Rev. 56 978

    [10]

    Tark S J, Ok Y W, Kang M G, Lim W M, Kim D 2009 J. Electroceram. 23 548

    [11]

    Chris G, Walle V 2000 Phys. Rev. Lett. 85 1012

    [12]

    Liu E K, Zhu B S, Luo J S 2005 Semiconductor Physics (4th Ed.)(Beijing: National Defence Industry Press) p256 (in Chinese)[刘恩科、朱炳升、罗晋声 2005 半导体物理学(第4版)(北京: 国防工业出版社) 第256页]

    [13]

    Kluth O, Rech B, Houben L, Wieder S, Schöpe G, Beneking C, Wagner H, Löffl, A Schock H W 1999 Thin Solid Films 351 247

    [14]

    Springer J, Rech B, Reetz W, Müller J, Vanecek M 2005 Sol. Energ. Mat. Sol. C 85 1

    [15]

    Berginski M, Hüpkes J, Schulte M Schöpe G, Stiebig H, Rech B 2007 J. Appl. Phys. 101 074903

    [16]

    Beyer W, Hüpkes J, Stiebig H 2007 Thin Solid Films 516 147

  • [1]

    Chen X L, Geng X H, Xue J M, Zhang D K, Hou G F, Zhao Y 2006 J. Crystal Growth 296 43

    [2]

    Meier J, Kroll U, Dubail S, Golay S, Fay S, Dubail J, Shah A 2000 Photovoltaic Specialists Conference (Conference Record of the 28th IEEE) AK: Anchorage, USA, September 15—22, 2000 p746

    [3]

    Chen X L, Xue J M, Zhang D K, Sun J, Ren H Z, Zhao Y, Geng X H 2007 Acta Phys. Sin. 56 1563(in Chinese) [陈新亮、薛俊明、张德坤、孙 建、任慧志、赵 颖、耿新华 2007 物理学报 56 1563]

    [4]

    Dewald W, Sittinger V, Werner W, Jacobs C, Szyszka B 2009 Thin Solid Films 518 1085

    [5]

    Duan L W, Xue J M, Yang R X, Zhao Y, Geng X H 2008 J. Optoelectron. Laser 19 1206 (in Chinese) [段苓伟、薛俊明、杨瑞霞、赵 颖、耿新华 2008 光电子·激光 19 1206]

    [6]

    Sittinger V, Ruske F, Werner W, Szyszka B, Rech B, Hüpkes J, Schöpe G, Stiebig H 2006 Thin Solid Films 496 16

    [7]

    Ellmer K, Klein A, Rech B 2008 Transparent Conductive Zinc Oxide (New York: Springer) p36

    [8]

    Müller J, Rech B, Springer J, Vanecek M 2004 Sol. Energ. 77 917

    [9]

    Patterson A L 1939 Phys. Rev. 56 978

    [10]

    Tark S J, Ok Y W, Kang M G, Lim W M, Kim D 2009 J. Electroceram. 23 548

    [11]

    Chris G, Walle V 2000 Phys. Rev. Lett. 85 1012

    [12]

    Liu E K, Zhu B S, Luo J S 2005 Semiconductor Physics (4th Ed.)(Beijing: National Defence Industry Press) p256 (in Chinese)[刘恩科、朱炳升、罗晋声 2005 半导体物理学(第4版)(北京: 国防工业出版社) 第256页]

    [13]

    Kluth O, Rech B, Houben L, Wieder S, Schöpe G, Beneking C, Wagner H, Löffl, A Schock H W 1999 Thin Solid Films 351 247

    [14]

    Springer J, Rech B, Reetz W, Müller J, Vanecek M 2005 Sol. Energ. Mat. Sol. C 85 1

    [15]

    Berginski M, Hüpkes J, Schulte M Schöpe G, Stiebig H, Rech B 2007 J. Appl. Phys. 101 074903

    [16]

    Beyer W, Hüpkes J, Stiebig H 2007 Thin Solid Films 516 147

  • [1] 任程超, 周佳凯, 张博宇, 刘璋, 赵颖, 张晓丹, 侯国付. 基于隧穿氧化物钝化接触的高效晶体硅太阳电池的研究现状与展望. 物理学报, 2021, 70(17): 178401. doi: 10.7498/aps.70.20210316
    [2] 王延峰, 谢希成, 刘晓洁, 韩冰, 武晗晗, 连宁宁, 杨富, 宋庆功, 裴海林, 李俊杰. F, Al共掺杂ZnO透明导电薄膜的制备及掺杂机理研究. 物理学报, 2020, 69(19): 197801. doi: 10.7498/aps.69.20200580
    [3] 陈新亮, 陈莉, 周忠信, 赵颖, 张晓丹. Cu2O/ZnO氧化物异质结太阳电池的研究进展. 物理学报, 2018, 67(11): 118401. doi: 10.7498/aps.67.20172037
    [4] 赵其琛, 郝瑞亭, 刘思佳, 刘欣星, 常发冉, 杨敏, 陆熠磊, 王书荣. 单靶溅射制备铜锌锡硫薄膜及原位退火研究. 物理学报, 2017, 66(22): 226801. doi: 10.7498/aps.66.226801
    [5] 王延峰, 孟旭东, 郑伟, 宋庆功, 翟昌鑫, 郭兵, 张越, 杨富, 南景宇. V掺杂ZnO透明导电薄膜研究. 物理学报, 2016, 65(8): 087802. doi: 10.7498/aps.65.087802
    [6] 刘长文, 周讯, 岳文瑾, 王命泰, 邱泽亮, 孟维利, 陈俊伟, 齐娟娟, 董超. 金属氧化物基杂化型聚合物太阳电池研究. 物理学报, 2015, 64(3): 038804. doi: 10.7498/aps.64.038804
    [7] 马海林, 苏庆. 氧分压对溅射制备氧化镓薄膜结构及光学带隙的影响. 物理学报, 2014, 63(11): 116701. doi: 10.7498/aps.63.116701
    [8] 陈明, 周细应, 毛秀娟, 邵佳佳, 杨国良. 外加磁场对射频磁控溅射制备铝掺杂氧化锌薄膜影响的研究. 物理学报, 2014, 63(9): 098103. doi: 10.7498/aps.63.098103
    [9] 朱顺明, 顾然, 黄时敏, 姚峥嵘, 张阳, 陈斌, 毛昊源, 顾书林, 叶建东, 郑有炓. 金属有机源化学气相沉积法生长氧化锌薄膜中氢气的作用及其机理. 物理学报, 2014, 63(11): 118103. doi: 10.7498/aps.63.118103
    [10] 王利, 张晓丹, 杨旭, 魏长春, 张德坤, 王广才, 孙建, 赵颖. 高绒度掺硼氧化锌透明导电薄膜用作非晶硅太阳电池前电极的研究. 物理学报, 2014, 63(2): 028801. doi: 10.7498/aps.63.028801
    [11] 王利, 张晓丹, 杨旭, 魏长春, 张德坤, 王广才, 孙建, 赵颖. 非晶硅太阳电池BZO/p-a-SiC:H接触特性改善的研究. 物理学报, 2013, 62(5): 058801. doi: 10.7498/aps.62.058801
    [12] 王延峰, 张晓丹, 黄茜, 刘阳, 魏长春, 赵颖. 室温制备低电阻率高透过率H, W共掺杂ZnO薄膜. 物理学报, 2013, 62(1): 017803. doi: 10.7498/aps.62.017803
    [13] 王延峰, 张晓丹, 黄茜, 杨富, 孟旭东, 宋庆功, 赵颖. B掺杂ZnO透明导电薄膜的实验及理论研究. 物理学报, 2013, 62(24): 247802. doi: 10.7498/aps.62.247802
    [14] 王延峰, 黄茜, 宋庆功, 刘阳, 魏长春, 赵颖, 张晓丹. W掺杂ZnO透明导电薄膜的理论及实验研究. 物理学报, 2012, 61(13): 137801. doi: 10.7498/aps.61.137801
    [15] 丁万昱, 王华林, 巨东英, 柴卫平. O2流量对磁控溅射N掺杂TiO2薄膜成分及晶体结构的影响. 物理学报, 2011, 60(2): 028105. doi: 10.7498/aps.60.028105
    [16] 周春兰, 励旭东, 王文静, 赵雷, 李海玲, 刁宏伟, 曹晓宁. 氧化随机织构硅表面对单晶硅太阳电池性能的影响研究. 物理学报, 2011, 60(3): 038201. doi: 10.7498/aps.60.038201
    [17] 张坤, 刘芳洋, 赖延清, 李轶, 颜畅, 张治安, 李劼, 刘业翔. 太阳电池用Cu2ZnSnS4薄膜的反应溅射原位生长及表征. 物理学报, 2011, 60(2): 028802. doi: 10.7498/aps.60.028802
    [18] 张 辉, 刘应书, 刘文海, 王宝义, 魏 龙. 基片温度与氧分压对磁控溅射制备氧化钒薄膜的影响. 物理学报, 2007, 56(12): 7255-7261. doi: 10.7498/aps.56.7255
    [19] 王宝义, 张仁刚, 张 辉, 万冬云, 魏 龙. ZnO退火条件对硫化法制备的ZnS薄膜特性的影响. 物理学报, 2005, 54(4): 1874-1878. doi: 10.7498/aps.54.1874
    [20] 张仁刚, 王宝义, 张 辉, 马创新, 魏 龙. 不同参数溅射的ZnO薄膜硫化后的特性. 物理学报, 2005, 54(5): 2389-2393. doi: 10.7498/aps.54.2389
计量
  • 文章访问数:  8035
  • PDF下载量:  853
  • 被引次数: 0
出版历程
  • 收稿日期:  2010-08-06
  • 修回日期:  2010-09-15
  • 刊出日期:  2011-03-05

/

返回文章
返回