激光熔覆铜锰合金选择性脱合金制备纳米多孔涂层的研究

董长胜; 谷雨; 钟敏霖; 马明星; 黄婷; 刘文今

doi:10.7498/aps.61.094211

摘要

本文通过激光加工结合电化学腐蚀脱合金法, 成功实现了纳米多孔涂层的制备. 采用激光熔覆首先在45钢表面制备了成形良好、稀释率低的铜锰合金熔覆层, 并通过快速重熔工艺实现了初始材料组织细化. 研究表明, 在不同的电解液下,铜锰合金的临界腐蚀电位出现了明显的偏移; 在不同的腐蚀电流下,铜锰合金腐蚀后的形貌迥异. 最终,通过选择性腐蚀成功实现了纳米多孔铜和纳米多孔锰涂层的制备, 并利用电位-pH图对脱合金的选择性腐蚀进行了详细的理论解释.

关键词:

Abstract

The nanoporous metal is fabricated by means of hybrid laser processing in combination with electrochemical dealloying. Cu-Mn alloy coatings with fine shape, low dilute ratio and refined microstructure are fabricated on medium carbon steel by means of laser processing. Polarization curve indicates that the Cu-Mn alloy shows selective dissolution characteristics for different electrolytes. Nanoporous Cu and nanoporous Mn are fabricated with optimal electrochemically dealloying parameters. Nanoporous Cu has pore sizes rangeing from 30 to 50 nm, while the surface morphology of the porous Mn shows a ribbon-like structure with ultrahigh roughness factor up to 900. Finally, the potential-pH diagram is used to explain the mechanism of the dealloying.

Keywords:

作者及机构信息

1.
清华大学机械工程系, 先进成形制造教育部重点实验室, 北京 100084

基金项目: 国家自然科学基金(批准号: 90923021), 清华大学自主研究计划 (批准号: 2010THZ0) 和北京市教育委员会科技计划重点项目(批准号: KZ201110005001)资助的课题.

Authors and contacts

1.
Department of Mechanical Engineering, Key Laboratory for Advanced Materials Processing Technology, Ministry of Education, Tsinghua University, Beijing 100084, China

Funds: Project supported by the National Natural Science Foundation of China (Grant Nos. 90923021), the Independent Scientific Research Plan of Tsinghua University (Grant No. 2010THZ0), and the Key Program for Science and Technology Project of Beijing Municipal Education Commission (Grant No. KZ201110005001).

参考文献

[1]	Zhong M L, Fan P X 2011 Chinese J. Lasers 38 0601001 (in Chinese) [钟敏霖, 范培迅 2011 中国激光 38 0601001]
[2]	Zhang L D, Xie S S 2004 Nano Mateirals and Nano Structure (Beijing: Chemical Industry Press) p241 (in Chinese) [张立德, 谢思深 2004 纳米材料和纳米结构 (北京:化学工业出版社) 第241页]
[3]	Liu P S 2004 Introduction of Porous Materials (Beijing: Tsinghua University Press) p1 (in Chinese) [刘培生 2004 多孔材料引论 (北京:清华大学出版社) 第1页]
[4]	Ryoo R, Joo S H, Kruk M 2001 Adv. Mater. 13 667
[5]	Shin H J, Ko C H, Ryoo R 2001 J. Mater. Chem. 11 260
[6]	Ding Y, Kim Y J, Erlebacher J 2004 Adv. Mater. 16 1897
[7]	Erlebacher J, Aziz M J, Karma A, Dimitrov N, Sieradzki K 2001 Nature 410 450
[8]	Huang J F, Sun I W 2005 Adv. Funct. Mater. 15 989
[9]	Jia F, Yu C, Ai Z, Zhang L 2007 Chem. Mater. 19 3648
[10]	Pugh D, Dursun A, Corcoran S 2003 J. Mater. Res. 18 216
[11]	Pugh D, Dursun A, Corcoran S. 2005 J. Electrochem. Soc. 152 B455
[12]	Lu H B, Li Y, Wang F H 2007 Scripta Mater. 56 165
[13]	Huang J F, Sun I W 2005 Adv. Funct.Mater. 15 989
[14]	Thorp J C, Sieradzki K, Tang L, Crozier P A, Misra A, Nastasi M, Mitlin D, Picraux S T 2005 Appl. Phys. Lett. 88 033110
[15]	Jia Z, Dai C S, Chen L 2006 Electrochemical Measurement Techniques (Beijing: Chemical Industry Press) p238 (in Chinese) [贾铮, 戴长松, 陈玲 2006 电化学测量方法 (北京:化学工业出版社) 第238页]
[16]	Li S, Chien C L, Searson P C 2004 Chem. Mater. 16 3125
[17]	Chang J K, Hsu S H, Sun I W, Tsai W T 2008 J. Phys. Chem. C 112 1371
[18]	Dong C S, Gu Y, Zhong M L, Li L, Ma M X, Liu W J 2011 Appl. Surf. Sci. 257 2467
[19]	Senior N A, Newman R C 2006 Nanotechnology 17 2311
[20]	Kan Y D 2008 Ph. D. Dissertation (Beijing: Tsinghua University) (in Chinese) [阚义德 2008 激光制备介孔结构涂层的研究 (北京:清华大学)]
[21]	Erlebacher J 2004 J. Electrochem. Soc. 151 C614
[22]	Liu H T, He P, Li Z Y, Li J H 2006 Nanotechnology 17 2167
[23]	Li D 2008 Electrochemical Thoery (Beijing: Beijing University of Aeronautics & Astronautics Press) p54--56 (in Chinese) [李荻 2008 电化学原理(北京:北京航空航天大学出版社) 第54---56页]
[24]	Huang Y C 1989 Corrosion and Protection of Metals (Shanghai: Shanghai Jiao Tong University Press) p15--28 (in Chinese) [黄永昌 1989 金属腐蚀与防护原理 (上海:上海交通大学出版社)第15---28页]
[25]	Zhang C Z 1985 Corrosion and Protection of Metals (Beijing: Metallurgical Industry Press) p79--89 (in Chinese) [张承忠 1985 金属的腐蚀与防护(北京:冶金工业出版社)第79---89页]
[26]	Jiang J X, Zhang P F, Gao M T 1986 Metal Corrosion (Beijing: National Defense Industrial Press) p4--28 (in Chinese) [蒋金勋, 张佩芬, 高满同 1986 金属腐蚀学 (北京:国防工业出版社) 第4---28页]
[27]	Zhao W Z 1998 Materials Surface Engineering (Xi'an: Xi'an Jiao Tong University Press) p90--95 (in Chinese) [赵文轸 1998 材料表面工程(陕西:西安交通大学出版社)第90---95页]
[28]	Aksu S 2009 J. Eleltrochem. Soc. 156 C387
[29]	Tyurin A G 2005 Prot. Met. 41 69

施引文献

[1]	Zhong M L, Fan P X 2011 Chinese J. Lasers 38 0601001 (in Chinese) [钟敏霖, 范培迅 2011 中国激光 38 0601001]
[2]	Zhang L D, Xie S S 2004 Nano Mateirals and Nano Structure (Beijing: Chemical Industry Press) p241 (in Chinese) [张立德, 谢思深 2004 纳米材料和纳米结构 (北京:化学工业出版社) 第241页]
[3]	Liu P S 2004 Introduction of Porous Materials (Beijing: Tsinghua University Press) p1 (in Chinese) [刘培生 2004 多孔材料引论 (北京:清华大学出版社) 第1页]
[4]	Ryoo R, Joo S H, Kruk M 2001 Adv. Mater. 13 667
[5]	Shin H J, Ko C H, Ryoo R 2001 J. Mater. Chem. 11 260
[6]	Ding Y, Kim Y J, Erlebacher J 2004 Adv. Mater. 16 1897
[7]	Erlebacher J, Aziz M J, Karma A, Dimitrov N, Sieradzki K 2001 Nature 410 450
[8]	Huang J F, Sun I W 2005 Adv. Funct. Mater. 15 989
[9]	Jia F, Yu C, Ai Z, Zhang L 2007 Chem. Mater. 19 3648
[10]	Pugh D, Dursun A, Corcoran S 2003 J. Mater. Res. 18 216
[11]	Pugh D, Dursun A, Corcoran S. 2005 J. Electrochem. Soc. 152 B455
[12]	Lu H B, Li Y, Wang F H 2007 Scripta Mater. 56 165
[13]	Huang J F, Sun I W 2005 Adv. Funct.Mater. 15 989
[14]	Thorp J C, Sieradzki K, Tang L, Crozier P A, Misra A, Nastasi M, Mitlin D, Picraux S T 2005 Appl. Phys. Lett. 88 033110
[15]	Jia Z, Dai C S, Chen L 2006 Electrochemical Measurement Techniques (Beijing: Chemical Industry Press) p238 (in Chinese) [贾铮, 戴长松, 陈玲 2006 电化学测量方法 (北京:化学工业出版社) 第238页]
[16]	Li S, Chien C L, Searson P C 2004 Chem. Mater. 16 3125
[17]	Chang J K, Hsu S H, Sun I W, Tsai W T 2008 J. Phys. Chem. C 112 1371
[18]	Dong C S, Gu Y, Zhong M L, Li L, Ma M X, Liu W J 2011 Appl. Surf. Sci. 257 2467
[19]	Senior N A, Newman R C 2006 Nanotechnology 17 2311
[20]	Kan Y D 2008 Ph. D. Dissertation (Beijing: Tsinghua University) (in Chinese) [阚义德 2008 激光制备介孔结构涂层的研究 (北京:清华大学)]
[21]	Erlebacher J 2004 J. Electrochem. Soc. 151 C614
[22]	Liu H T, He P, Li Z Y, Li J H 2006 Nanotechnology 17 2167
[23]	Li D 2008 Electrochemical Thoery (Beijing: Beijing University of Aeronautics & Astronautics Press) p54--56 (in Chinese) [李荻 2008 电化学原理(北京:北京航空航天大学出版社) 第54---56页]
[24]	Huang Y C 1989 Corrosion and Protection of Metals (Shanghai: Shanghai Jiao Tong University Press) p15--28 (in Chinese) [黄永昌 1989 金属腐蚀与防护原理 (上海:上海交通大学出版社)第15---28页]
[25]	Zhang C Z 1985 Corrosion and Protection of Metals (Beijing: Metallurgical Industry Press) p79--89 (in Chinese) [张承忠 1985 金属的腐蚀与防护(北京:冶金工业出版社)第79---89页]
[26]	Jiang J X, Zhang P F, Gao M T 1986 Metal Corrosion (Beijing: National Defense Industrial Press) p4--28 (in Chinese) [蒋金勋, 张佩芬, 高满同 1986 金属腐蚀学 (北京:国防工业出版社) 第4---28页]
[27]	Zhao W Z 1998 Materials Surface Engineering (Xi'an: Xi'an Jiao Tong University Press) p90--95 (in Chinese) [赵文轸 1998 材料表面工程(陕西:西安交通大学出版社)第90---95页]
[28]	Aksu S 2009 J. Eleltrochem. Soc. 156 C387
[29]	Tyurin A G 2005 Prot. Met. 41 69

[1]	李腾, 邱文婷, 龚深. 基于相场方法的多孔合金马氏体相变模拟. 物理学报, 2023, 72(14): 148102. doi: 10.7498/aps.72.20230212
[2]	陈波, 杨詹詹, 王玉楹, 王寅岗. 退火时间对Fe₈₀Si₉B₁₀Cu₁非晶合金纳米尺度结构不均匀性和磁性能的影响. 物理学报, 2022, 71(15): 156102. doi: 10.7498/aps.71.20220446
[3]	蒋新安, 赵宇宏, 杨文奎, 田晓林, 侯华. 相场法研究Fe₈₄Cu₁₅Mn₁合金富Cu相析出的内磁能作用机理. 物理学报, 2022, 71(8): 080201. doi: 10.7498/aps.71.20212087
[4]	郭震, 赵宇宏, 孙远洋, 赵宝军, 田晓林, 侯华. 相场法研究Fe-Cu-Mn-Al合金富Cu相析出机制. 物理学报, 2021, 70(8): 086401. doi: 10.7498/aps.70.20201843
[5]	曹永青, 林鑫, 汪志太, 王理林, 黄卫东. 液氮冷却条件下激光快速熔凝Ni-28 wt%Sn合金组织演变. 物理学报, 2015, 64(10): 108103. doi: 10.7498/aps.64.108103
[6]	第伍旻杰, 胡晓棉. 高应变率压缩下纳米孔洞对金属铝塑性变形的影响研究. 物理学报, 2015, 64(17): 170201. doi: 10.7498/aps.64.170201
[7]	齐玉, 曲昌荣, 王丽, 方腾. Fe50Cu50合金熔体相分离过程的分子动力学模拟. 物理学报, 2014, 63(4): 046401. doi: 10.7498/aps.63.46401
[8]	姚洪斌, 李文亮, 张季, 彭敏. K2分子在强激光场下的量子调控：缀饰态选择性分布. 物理学报, 2014, 63(17): 178201. doi: 10.7498/aps.63.178201
[9]	汪礼锋, 贺新奎, 滕浩, 运晨霞, 张伟, 魏志义. 5fs驱动激光脉冲的高次谐波选择性优化. 物理学报, 2014, 63(22): 224103. doi: 10.7498/aps.63.224103
[10]	刘晓旭, 赵兴涛, 张颖, 朱岩, 吴光恒. 高矫顽力的Co70Cu30合金纳米线阵列的制备及磁性研究. 物理学报, 2012, 61(13): 137503. doi: 10.7498/aps.61.137503
[11]	唐林峰, 王楠, 管强, 姚文静. 单晶合金激光熔凝过程中晶向对单晶完整性的影响. 物理学报, 2010, 59(11): 7941-7948. doi: 10.7498/aps.59.7941
[12]	蔡从中, 裴军芳, 温玉锋, 朱星键, 肖婷婷. 选择性激光烧结成型件密度的支持向量回归预测. 物理学报, 2009, 58(13): 8-S14. doi: 10.7498/aps.58.8
[13]	王清周, 陆东梅, 崔春翔, 韩福生. 利用内耗研究淬火空位对Cu-11.9Al-2.5Mn(wt%)形状记忆合金逆马氏体相变温度的影响. 物理学报, 2008, 57(11): 7083-7087. doi: 10.7498/aps.57.7083
[14]	陈岁元, 刘常升, 李慧莉, 崔彤. 非晶Fe73.5Cu1Nb3Si13.5B9合金激光纳米化的超精细结构研究. 物理学报, 2005, 54(9): 4157-4163. doi: 10.7498/aps.54.4157
[15]	王振华, 胡响明. 修饰态布居的选择性激发对无反转激光的作用. 物理学报, 2004, 53(8): 2569-2575. doi: 10.7498/aps.53.2569
[16]	李健靓, 赵韦人, 张羊换, 王新林, 张建福, 郭世海. 熔体快淬对Ni-Mn-Ga合金马氏体相变特征及应变的影响. 物理学报, 2003, 52(11): 2849-2853. doi: 10.7498/aps.52.2849
[17]	杨森, 苏云鹏, 黄卫东, 周尧和. 激光快速凝固条件下Cu-31.4%Mn合金的微观组织特征. 物理学报, 2003, 52(1): 81-86. doi: 10.7498/aps.52.81
[18]	张思玉, 王必本, 郑克全. 激光熔敷WC-TiN-SiC-Co高硬质合金及机理初探. 物理学报, 1994, 43(4): 678-682. doi: 10.7498/aps.43.678
[19]	戴长建, 于长江. 脉冲激光场选择性光电离同位素原子. 物理学报, 1994, 43(3): 356-368. doi: 10.7498/aps.43.356
[20]	刘学东, 朱洁, 晁月盛, 姜健, 王景唐. Fe-Cu-Si-B纳米晶合金的结构与性能. 物理学报, 1993, 42(8): 1272-1277. doi: 10.7498/aps.42.1272

计量

文章访问数: 7049
PDF下载量: 819
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板