球形无规键无规场模型研究弛豫铁电体极化效应

屈少华; 曹万强

doi:10.7498/aps.63.047701

摘要

基于球形无规键无规场模型和电场作用下弛豫铁电体微畴-宏畴机理，利用模糊畴界观点以及电场对极化的分数维效应，分析了电场对畴的作用机理. 研究结果表明: 电场对畴的诱导偶极子增量的极化效应导致了电滞回线的不饱和及相关的大的电致伸缩效应；而畴的偶极子增量耦合时结合能的变化对低电场的电滞回线略有影响，但基本不会改变高电场时的极化状态. 初始微畴大小对电滞回线非常重要，细小的微畴会导致细长的电滞回线及电场与电致伸缩良好的线性关系.

关键词:

弛豫铁电体 /
极化 /
电致伸缩

Abstract

Based on spherical random bond-random field model, micro-macro domain mechanism under electric field, and the fuzzy domain boundary with fractal dimension of electric field, the mechanism of polarization effect is analyzed. The results show that the effect of electric field on polarization effect of increment of domain dipoles leads to an unsaturated electric hysteresis loop and its associated big electrostrictive effect. But the variation of binding energy, when dipole couples to the increment of domain dipoles induced by electric field, has a little influence on electric hysteresis loop in a low electric field, and has almost no influence in a high electric field. The initial size of the micro domain is very important for electric hysteresis loop: small micro domain can lead to a long electric hysteresis loop and better linear relationship between electric field and electrostriction.

Keywords:

作者及机构信息

屈少华¹,
曹万强²

1.
湖北文理学院物理与电子工程学院, 低维光电材料与器件湖北省重点实验室, 襄阳 441053;

2.
湖北大学材料科学与工程学院, 有机化工新材料湖北省协同创新中心, 武汉 430062

基金项目: 湖北省自然科学基金（批准号：2012FFC05101）资助的课题.

Authors and contacts

Qu Shao-Hua¹,
Cao Wan-Qiang²

1.
Key Laboratory of Low Dimension Photoelectric Material and Device of Hubei Province, School of Physics and Electronic Engineering, Hubei University of Arts and Science, Xiangyang 441053, China;

2.
Collaborative Innovation Center for Advanced Organic Chemical Materials of Hubei Province, School of Materials Science and Engineering, Hubei University, Wuhan 430062, China

Funds: Project supported by the Natural Science Foundation of Hubei Province, China (Grant No. 2012FFC05101).

参考文献

[1]	Chino K U 1986 Am. Ceram. Soc. Bull. 65 647
[2]	Uchino K, Nomura S, Cross L E, Jang S J, Newnham R E 1980 J. Appl. Phys. 51 1142
[3]	Cross L E, Jang S J, Newnham R E, Nomura S, Uchino K 1980 Ferroelectrics 23 187
[4]	Park S E, Shrout T R 1997 J. Appl. Phys. 82 1804
[5]	Zhang S T, Yan F, Yang B, Cao W W 2010 Appl. Phys. Lett. 97 122901
[6]	Cao W Q, Chen W, Shang Y L, Shu M F 2012 Ferroelectr. Lett. 39 71
[7]	Zhang Q M, Bharti V, Zhao X 1998 Science 280 2101
[8]	Wu Z Q 2003 Ph. D. Dissertation (Beijing: Tsinghu University) (in Chinese) [吴忠庆 2003 博士学位论文 (北京: 清华大学)]
[9]	Pirc R, Blinc R 1999 Phys. Rev. B 60 13470
[10]	Blinc R, Dolinšek J, Gregorovič A, Zalar B, Filipic C, Kutnjak Z, Levstik A, Pirc R 1999 Phys. Rev. Lett. 83 424
[11]	Blinc R, Gregorovic A, Zalar B, Pirc R 2000 Phys. Rev. B 61 253
[12]	Yao X, Chen Z L, Cross L E 1983 J. Appl. Phys. 54 3399
[13]	Wad S, Park S E, Cross L E, Shrout T R 1998 J. Korean Phys. Soc. 32 S1290
[14]	Kutnjak Z, Petzelt J, Blinc R 2006 Nature 441 956
[15]	Shang Y L, Shu M F, Chen W, Cao W Q 2012 Acta Phys. Sin. 61 197701 (in Chinese) [尚玉黎, 舒明飞, 陈威, 曹万强 2012 物理学报 61 197701]
[16]	Shang X Z, Chen W, Cao W Q 2012 Acta Phys. Sin. 61 217701 (in Chinese) [尚勋忠, 陈威, 曹万强 2012 物理学报61 217701]
[17]	Cao W Q, Chen W 2012 Ferroelectr. Lett. 39 56
[18]	Zhang X D, Rogers C A 1993 J. Intell. Mater. Syst. Struct. 4 307
[19]	Gan Y C, Cao W Q 2013 Acta Phys. Sin. 62 127701 (in Chinese) [甘永超, 曹万强 2013 物理学报 62 127701]
[20]	Wang X S, Yamada H, Xu C N 2005 Appl. Phys. Lett. 86 022905
[21]	Chen X F, Li H M, Li D J, Cao F, Dong X L 2008 Acta Phys. Sin. 57 7298 (in Chinese) [陈学锋, 李华梅, 李东杰, 曹菲, 董显林 2008 物理学报 57 7298]
[22]	Moura F, Simoes A Z, Stojanovic B D Zaghete M A, Longo E, Varela J A 2008 J. Alloys Compd. 462 129
[23]	Wang Z J, Li X Z, Long X F, Ye Z G 2009 Scripta Mater 60 830

施引文献

[1]	Chino K U 1986 Am. Ceram. Soc. Bull. 65 647
[2]	Uchino K, Nomura S, Cross L E, Jang S J, Newnham R E 1980 J. Appl. Phys. 51 1142
[3]	Cross L E, Jang S J, Newnham R E, Nomura S, Uchino K 1980 Ferroelectrics 23 187
[4]	Park S E, Shrout T R 1997 J. Appl. Phys. 82 1804
[5]	Zhang S T, Yan F, Yang B, Cao W W 2010 Appl. Phys. Lett. 97 122901
[6]	Cao W Q, Chen W, Shang Y L, Shu M F 2012 Ferroelectr. Lett. 39 71
[7]	Zhang Q M, Bharti V, Zhao X 1998 Science 280 2101
[8]	Wu Z Q 2003 Ph. D. Dissertation (Beijing: Tsinghu University) (in Chinese) [吴忠庆 2003 博士学位论文 (北京: 清华大学)]
[9]	Pirc R, Blinc R 1999 Phys. Rev. B 60 13470
[10]	Blinc R, Dolinšek J, Gregorovič A, Zalar B, Filipic C, Kutnjak Z, Levstik A, Pirc R 1999 Phys. Rev. Lett. 83 424
[11]	Blinc R, Gregorovic A, Zalar B, Pirc R 2000 Phys. Rev. B 61 253
[12]	Yao X, Chen Z L, Cross L E 1983 J. Appl. Phys. 54 3399
[13]	Wad S, Park S E, Cross L E, Shrout T R 1998 J. Korean Phys. Soc. 32 S1290
[14]	Kutnjak Z, Petzelt J, Blinc R 2006 Nature 441 956
[15]	Shang Y L, Shu M F, Chen W, Cao W Q 2012 Acta Phys. Sin. 61 197701 (in Chinese) [尚玉黎, 舒明飞, 陈威, 曹万强 2012 物理学报 61 197701]
[16]	Shang X Z, Chen W, Cao W Q 2012 Acta Phys. Sin. 61 217701 (in Chinese) [尚勋忠, 陈威, 曹万强 2012 物理学报61 217701]
[17]	Cao W Q, Chen W 2012 Ferroelectr. Lett. 39 56
[18]	Zhang X D, Rogers C A 1993 J. Intell. Mater. Syst. Struct. 4 307
[19]	Gan Y C, Cao W Q 2013 Acta Phys. Sin. 62 127701 (in Chinese) [甘永超, 曹万强 2013 物理学报 62 127701]
[20]	Wang X S, Yamada H, Xu C N 2005 Appl. Phys. Lett. 86 022905
[21]	Chen X F, Li H M, Li D J, Cao F, Dong X L 2008 Acta Phys. Sin. 57 7298 (in Chinese) [陈学锋, 李华梅, 李东杰, 曹菲, 董显林 2008 物理学报 57 7298]
[22]	Moura F, Simoes A Z, Stojanovic B D Zaghete M A, Longo E, Varela J A 2008 J. Alloys Compd. 462 129
[23]	Wang Z J, Li X Z, Long X F, Ye Z G 2009 Scripta Mater 60 830

[1]	韦宜政, 孙超, 朱启轩. 浅海矢量声场极化特性的深度分布规律. 物理学报, 2024, 73(9): 094302. doi: 10.7498/aps.73.20231767
[2]	李元, 李春鹏, 李林波, 袁磊, 王亚桢, 石亚轩, 张冠军. 电致伸缩效应下水中电子输运特性研究. 物理学报, 2024, 0(0): . doi: 10.7498/aps.73.20231893
[3]	陈昊鹏, 聂永杰, 李国倡, 魏艳慧, 胡昊, 鲁广昊, 李盛涛, 朱远惟. 聚合物分散液晶薄膜的极化特性及其对电光性能的影响. 物理学报, 2023, 72(17): 177701. doi: 10.7498/aps.72.20230664
[4]	李元, 李林波, 温嘉烨, 倪正全, 张冠军. 基于电致伸缩效应的水中纳秒脉冲放电起始机制. 物理学报, 2021, 70(2): 024701. doi: 10.7498/aps.70.20201048
[5]	黄建邦, 南虎, 张锋, 张佳乐, 刘来君, 王大威. 弛豫铁电体弥散相变与热滞效应的伊辛模型. 物理学报, 2021, 70(11): 110501. doi: 10.7498/aps.70.20202019
[6]	黄旭东, 冯玉军, 唐帅. 掺镧锆锡钛酸铅陶瓷极化强度变化量对电子发射电流强度的影响. 物理学报, 2012, 61(8): 087702. doi: 10.7498/aps.61.087702
[7]	陈龙天, 程用志, 聂彦, 龚荣洲. 人工异向介质调控电磁波极化特性的实验与仿真研究. 物理学报, 2012, 61(9): 094203. doi: 10.7498/aps.61.094203
[8]	尚勋忠, 陈威, 曹万强. 弛豫铁电体介电可调性的研究. 物理学报, 2012, 61(21): 217701. doi: 10.7498/aps.61.217701
[9]	赵静波, 杜红亮, 屈绍波, 张红梅, 徐卓. A位等价与非等价取代对(K0.5Na0.5)NbO3陶瓷极化的影响. 物理学报, 2011, 60(10): 107701. doi: 10.7498/aps.60.107701
[10]	周可余, 叶辉, 甄红宇, 尹伊, 沈伟东. 基于压电聚合物薄膜可调谐Fabry-Perot滤波器的研究. 物理学报, 2010, 59(1): 365-369. doi: 10.7498/aps.59.365
[11]	高剑森, 张宁. 异型磁体/铁电复合材料中的电致变磁导及电致变阻抗效应. 物理学报, 2009, 58(12): 8607-8611. doi: 10.7498/aps.58.8607
[12]	宋学平, 张永光, 罗晓婧, 徐玲芳, 曹万强, 杨昌平. (1-x)(K0.5Na0.5)NbO3-xSrTiO3陶瓷的弛豫铁电性能. 物理学报, 2009, 58(7): 4980-4986. doi: 10.7498/aps.58.4980
[13]	孙贤明, 哈恒旭. 基于反射太阳光反演气溶胶光学厚度和有效半径. 物理学报, 2008, 57(9): 5565-5570. doi: 10.7498/aps.57.5565
[14]	杨凤霞, 张端明, 邓宗伟, 姜胜林, 徐洁, 李舒丹. 基体电导率对0-3型铁电复合材料高压极化行为及损耗的影响. 物理学报, 2008, 57(6): 3840-3845. doi: 10.7498/aps.57.3840
[15]	顾晓玲, 郭霞, 吴迪, 徐丽华, 梁庭, 郭晶, 沈光地. GaN基多量子阱发光二极管的极化效应和载流子不均匀分布及其影响. 物理学报, 2007, 56(8): 4977-4982. doi: 10.7498/aps.56.4977
[16]	朱振业, 王彪, 郑跃, 王海, 李青坤, 李晨亮. 应力作用下铁电超晶格BaTiO3/SrTiO3的结构和极化的第一性原理研究. 物理学报, 2007, 56(10): 5986-5989. doi: 10.7498/aps.56.5986
[17]	徐任信, 陈文, 周静. 聚合物电导率对0-3型压电复合材料极化性能的影响. 物理学报, 2006, 55(8): 4292-4297. doi: 10.7498/aps.55.4292
[18]	刘洪, 蒲朝辉, 龚小刚, 王志红, 黄惠东, 李言荣, 肖定全, 朱建国. (111)取向(Pb,La)TiO3铁电薄膜中90°纳米带状畴与热释电性能的研究. 物理学报, 2006, 55(11): 6123-6128. doi: 10.7498/aps.55.6123
[19]	张春福, 郝跃, 游海龙, 张金凤, 周小伟. 界面电偶极子对GaN/AlGaN/GaN光电探测器紫外/太阳光选择比的影响. 物理学报, 2005, 54(8): 3810-3814. doi: 10.7498/aps.54.3810
[20]	郭冠军, 苏林, 毕思文. 风成海面的极化辐射. 物理学报, 2005, 54(5): 2448-2452. doi: 10.7498/aps.54.2448

计量

文章访问数: 5196
PDF下载量: 407
被引次数: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

搜索

留言板