Silicon carbide (SiC) is widely used due to the lower coefficient of thermal expansion (CTE), high thermal conductivity and excellent mechanical properties. However, the self-diffusion coefficient of SiC relative to that of oxide ceramics is very low, it is difficult to sinter at lower temperature. The β-spodumene has ultra low or even negative thermal expansion coefficient combined with good thermal and chemical durability, which melts at 1423 ℃. Accordingly, the present study focuses on the use of β-spodumene as a flux at lower sintering temperature and the preparation of lower CET composite ceramics. The effects of spodumene on the sintering behavior, phase relations, thermal expansion and mechanical properties of spodumene/silicon carbide composites are discussed. A high pure β-spodumene LiAlSi2O6 compound with nearly zero thermal expansion coefficient is synthesized via solid phase sintering. Spodumene/silicon carbide composites are fabricated by the adding 25, 30, 35 and 40 mass% synthesized β-spodumene powder to 75, 70, 65 and 60 mass% α-SiC matrix, respectively. Both β-spodumene and SiC are fabricated by conventional pressureless liquid sintering technique, and the batches are uniaxially pressed into discs and rectangular bars, then sintered at 1550 ℃ for 2 h in an Ar atmosphere. The results show that the SiC and β-spodumene do not react during sintering, and the β-spodumene changes from tetragonal phase into hexagonal phase, the cell volume has a considerable shrinkage. A certain amount of liquid phase can help to enhance the density, improve Young’s modulus and promote the sintering behavior of SiC. When the feedstock contains 35% β-spodumene, the Young’s modulus reaches to (204.2 ± 0.5) GPa. Excess porosity is formed when liquid phase is too much during sintering, The Young's modulus of the sample 40SP is (119.6 ± 0.5) GPa. It is determined that the Young’s modulus of these materials are affected by porosity and internal microcracks. This study indicates that the content of β-spodumene and porosity are the dominant factors to control the CET of composites, but the porosity has a stronger effect. Besides, the microcracks, which are formed by the interaction of various internal stresses, are also an impotant factor. The materials with nearly zero thermal expansion are developed in a lower temperature range from –150 ℃ to 25 ℃, the spodumene content in the most stable composite reaches 40 mass%, and the CET of composite is close to that of Si (α25 ℃ = 2.59 × 10–6 ℃–1) in a temperature range of 25–480 ℃. -
Keywords:
- silicon carbide /
- β-spodumene /
- thermal expansion /
- Young’s modulus
[1] Mandal S, Chakrabarti S, Das S K, Ghatak S 2007 Ceram. Int. 33 123
Google Scholar
[2] Abdel-Fattah W I, Abdellah R 1997 Ceram. Int. 23 463
Google Scholar
[3] Hummel F A 1951 J. Am. Ceram. Soc. 34 235
Google Scholar
[4] Roy R, Agrawal D K, Mckinstry H A 2003 Annu. Rev. Mater. Res. 19 59
Google Scholar
[5] Ramirez I J, Matsumaru K, Ishizaki K 2006 J. Ceram. Soc. Jpn. 114 1111
Google Scholar
[6] Ono T, Matsumaru K, Juárez-Ramírez I, Torres-Martínez L M, Ishizaki K 2009 Mater. Sci. Forum 620–622 715
Google Scholar
[7] Wang B, Yang X H, Zeng D J, Yang J F, Ishizaki K, Niihara K 2014 J. Eur. Ceram. Soc. 34 97
Google Scholar
[8] García-Moreno O, Fernández A, Torrecillas R 2010 J. Eur. Ceram. Soc. 30 3219
Google Scholar
[9] Iwashima M, Nakano H, Ogata T O, Tsurumi T, Urabe K 2003 J. Ceram. Soc. Jpn. 111 430
Google Scholar
[10] Iguchi M, Umezu M, Kataoka M, Nakamura H, Ishii M 2006 Key Eng. Mater. 317-318 177
Google Scholar
[11] Welsch A M, Murawski D, Prekajski M, Vulic P, Kremenovic A 2015 Phys. Chem. Miner. 42 413
Google Scholar
[12] Li C T 1968 Z. Kristallogr. Kristallgeom. Kristallphys. Kristallchem. 127 327
Google Scholar
[13] Ostertag W, Fischer G R, Williams J P 1968 J. Am. Ceram. Soc. 51 651
Google Scholar
[14] Manurung P, Low I M, O’Connor B H, Kennedy S 2005 Mater. Res. Bull. 40 2047
Google Scholar
[15] 曹爱红 2006 中国陶瓷 42 30
Google Scholar
Cao A H 2006 Chn. Ceram. 42 30
Google Scholar
[16] Awaad M, Mӧrtel H, Naga S M 2005 J. Mater. Sci. -Mater. Electron. 16 377
Google Scholar
[17] Bayuseno A P, Latella B A, O'Connor B H 1999 J. Am. Ceram. Soc. 82 819
Google Scholar
[18] Latella B A, Burton G R, O'Connort B H 1995 J. Am. Ceram. Soc. 78 1895
Google Scholar
[19] Naga S M, El-Maghraby A A, Hassan A M 2016 Ceram. Int. 42 12161
Google Scholar
[20] Low I M, Mathews E, Garrod T, Zhou D, Phillip D N, Pillai X M 1997 J. Mater. Sci. 32 3807
Google Scholar
[21] Shi C G, Low I M 1998 Mater. Lett. 36 118
Google Scholar
[22] Halbig M C, Singh M, Tsuda H 2012 Int. J. Appl. Ceram. Technol. 9 677
Google Scholar
[23] 赵赞良, 唐政维, 蔡雪梅, 李秋俊, 张宪力 2006 装备制造技术 4 81
Google Scholar
Zhao Z L, Tang Z W, Cai X M, Li Q J, Zhang X L 2006 Equip. Manuf. Technol. 4 81
Google Scholar
[24] 赵更一 2016 硕士学位论文 (黑龙江: 哈尔滨工业大学)
Zhao G Y 2016 M.S. Thesis (Harbin: Harbin Institute of Technology) (in Chinese)
[25] 吴清仁, 吴建青, 文壁璇 1994 94'全国结构陶瓷、功能陶瓷、金属/陶瓷封接学术会议论文集 (中国北京) 10月20—24日 1994 p174
Wu Q R, Wu J Q, Wen B X 1994 Proceedings of the 94' National symposium on Structural Ceramics, Functional Ceramics, Metal/Ceramic Sealing Beijing, China, October 20–24, 1994 p174 (in Chinese)
[26] 黄智恒, 贾德昌, 杨治华, 周玉 2004 材料科学与工艺 12 103
Google Scholar
Huang Z H, Jia D C, Yang Z H, Zhou Y 2004 Mater. Sci. Technol. 12 103
Google Scholar
[27] Liang H Q, Yao X M, Liu X J, Huang Z R 2014 Mater. Des. 56 1009
Google Scholar
[28] Li C T 1970 Z. Kristallogr. Kristallgeom. Kristallphys. Kristallchem. 132 118
Google Scholar
[29] Kobayashi H, Ishibashi N, Akiba T, Mitamura T 1990 J. Ceram. Soc. Jpn. 98 1023
Google Scholar
[30] Xia L, Wang X Y, Wen G W, Zhong B, Song L 2012 Ceram. Int. 38 5315
Google Scholar
[31] Okada Y, Tokumaru Y 1984 J. Appl. Phys. 56 314
Google Scholar
[32] 喻佑华, 刘映珍 1995 陶瓷研究 10 180
Yu Y H, Liu Y Z 1995 Ceram. Stud. J. 10 180
-
图 1 β-锂辉石XRD图谱 (a) β-LiAlSi2O6; (b) ICSD No. 01-071-2058
Fig. 1. XRD patterns of β-spodumene: (a) β-LiAlSi2O6; (b) ICSD No. 01-071-2058
图 3 1550 ℃烧结前后试样40SP的XRD图谱
Fig. 3. XRD patterns of 40SP sample in the starting and the sintered at 1550 ℃.
图 4 锂辉石/碳化硅复相陶瓷断面显微形貌 (a) 25SP; (b) 30SP; (c) 35SP; (d) 40SP
Fig. 4. SEM micrographs of the fracture surface of spodumene/silicon composites: (a) 25SP; (b) 30SP; (c) 35SP; (d) 40SP.
图 5 锂辉石/碳化硅复相陶瓷的气孔率和杨氏模量
Fig. 5. Apparent porosity and Young’s modulus of the spodumene/silicon carbide composites.
图 6 锂辉石/碳化硅复相陶瓷热膨胀率随温度的变化关系
Fig. 6. Expansion versus temperature of the spodumene/sili-con carbide composites.
表 1 LAS体系一些重要物质的平均线热膨胀系数
Table 1. Average linear thermal expansion coefficient (CET) of some important materials based on LAS system.
System/material CET/10–6 ℃–1 Temperature range/℃ Li2O·Al2O3·2SiO2 (LiAlSiO4, Eucryptite) –6.2 25—800 Li2O·Al2O3·3SiO2 (Solid solution of eucryptite) Negative near zero CET 25—1000 Li2O·Al2O3·4SiO2 (β-LiAlSi2O6, β-Spodumene) 0.9 25—1000 Li2O·Al2O3·6SiO2 (LiAlSi3O8, Virgilite) 0.5 25—1000 Li2O·Al2O3·8SiO2 (LiAlSi4O10, Petalite) 0.3 25—1000 Li2O·Al2O3·10SiO2 0.5 25—1000 LAS + TiO2 (Pyroceram) –0.07—0.30 LAS + TiO2 + ZrO2 (Cer-Vit) 0.05—0.30 Hercuvit (LAS-based transparentlow expanding glass-ceramic) 0—0.3 
下载: 导出CSV
表 2 四方相β-锂辉石和六方相锂辉石原子键长、晶胞体积和密度
Table 2. The atomic bond lengths, cell volume and density of tetragonal and hexagonal spodumene.
Phase Si, Al—O/Å Li—O/ Å Si, Al—Li/Å O—O (Li tetrahedra)/Å O—O (Si, Al tetrahedra)/Å V/Å3 Dc/g·cm–3 Te-SP 1.643 2.081 2.628/2.710 3.339 2.682 520.671 2.374 He-SP 1.641 2.068 2.609 3.337 2.679 128.790 2.399
下载: 导出CSV
表 3 锂辉石/碳化硅复相陶瓷材料的性能
Table 3. Characteristics of spodumene/ silicon carbide composites.
β–Spodumene content/
mass%Apparent porosity/
%Bulk density/
g·cm–3Young’s modulus/
GPaα (–150—25 ℃)/
℃–1α (25—480 ℃)/
℃–1SP25 38 1.81 95.3 ± 0.1 0.23 × 10–6 1.83 × 10–6 SP30 32 1.82 123.8 ± 0.4 0.60 × 10–6 2.95 × 10–6 SP35 19 2.24 204.2 ± 0.5 0.53 × 10–6 5.71 × 10–6 SP40 29 1.95 119.6 ± 0.5 1.14 × 10–6 2.50 × 10–6
下载: 导出CSV
-
[1] Mandal S, Chakrabarti S, Das S K, Ghatak S 2007 Ceram. Int. 33 123
Google Scholar
[2] Abdel-Fattah W I, Abdellah R 1997 Ceram. Int. 23 463
Google Scholar
[3] Hummel F A 1951 J. Am. Ceram. Soc. 34 235
Google Scholar
[4] Roy R, Agrawal D K, Mckinstry H A 2003 Annu. Rev. Mater. Res. 19 59
Google Scholar
[5] Ramirez I J, Matsumaru K, Ishizaki K 2006 J. Ceram. Soc. Jpn. 114 1111
Google Scholar
[6] Ono T, Matsumaru K, Juárez-Ramírez I, Torres-Martínez L M, Ishizaki K 2009 Mater. Sci. Forum 620–622 715
Google Scholar
[7] Wang B, Yang X H, Zeng D J, Yang J F, Ishizaki K, Niihara K 2014 J. Eur. Ceram. Soc. 34 97
Google Scholar
[8] García-Moreno O, Fernández A, Torrecillas R 2010 J. Eur. Ceram. Soc. 30 3219
Google Scholar
[9] Iwashima M, Nakano H, Ogata T O, Tsurumi T, Urabe K 2003 J. Ceram. Soc. Jpn. 111 430
Google Scholar
[10] Iguchi M, Umezu M, Kataoka M, Nakamura H, Ishii M 2006 Key Eng. Mater. 317-318 177
Google Scholar
[11] Welsch A M, Murawski D, Prekajski M, Vulic P, Kremenovic A 2015 Phys. Chem. Miner. 42 413
Google Scholar
[12] Li C T 1968 Z. Kristallogr. Kristallgeom. Kristallphys. Kristallchem. 127 327
Google Scholar
[13] Ostertag W, Fischer G R, Williams J P 1968 J. Am. Ceram. Soc. 51 651
Google Scholar
[14] Manurung P, Low I M, O’Connor B H, Kennedy S 2005 Mater. Res. Bull. 40 2047
Google Scholar
[15] 曹爱红 2006 中国陶瓷 42 30
Google Scholar
Cao A H 2006 Chn. Ceram. 42 30
Google Scholar
[16] Awaad M, Mӧrtel H, Naga S M 2005 J. Mater. Sci. -Mater. Electron. 16 377
Google Scholar
[17] Bayuseno A P, Latella B A, O'Connor B H 1999 J. Am. Ceram. Soc. 82 819
Google Scholar
[18] Latella B A, Burton G R, O'Connort B H 1995 J. Am. Ceram. Soc. 78 1895
Google Scholar
[19] Naga S M, El-Maghraby A A, Hassan A M 2016 Ceram. Int. 42 12161
Google Scholar
[20] Low I M, Mathews E, Garrod T, Zhou D, Phillip D N, Pillai X M 1997 J. Mater. Sci. 32 3807
Google Scholar
[21] Shi C G, Low I M 1998 Mater. Lett. 36 118
Google Scholar
[22] Halbig M C, Singh M, Tsuda H 2012 Int. J. Appl. Ceram. Technol. 9 677
Google Scholar
[23] 赵赞良, 唐政维, 蔡雪梅, 李秋俊, 张宪力 2006 装备制造技术 4 81
Google Scholar
Zhao Z L, Tang Z W, Cai X M, Li Q J, Zhang X L 2006 Equip. Manuf. Technol. 4 81
Google Scholar
[24] 赵更一 2016 硕士学位论文 (黑龙江: 哈尔滨工业大学)
Zhao G Y 2016 M.S. Thesis (Harbin: Harbin Institute of Technology) (in Chinese)
[25] 吴清仁, 吴建青, 文壁璇 1994 94'全国结构陶瓷、功能陶瓷、金属/陶瓷封接学术会议论文集 (中国北京) 10月20—24日 1994 p174
Wu Q R, Wu J Q, Wen B X 1994 Proceedings of the 94' National symposium on Structural Ceramics, Functional Ceramics, Metal/Ceramic Sealing Beijing, China, October 20–24, 1994 p174 (in Chinese)
[26] 黄智恒, 贾德昌, 杨治华, 周玉 2004 材料科学与工艺 12 103
Google Scholar
Huang Z H, Jia D C, Yang Z H, Zhou Y 2004 Mater. Sci. Technol. 12 103
Google Scholar
[27] Liang H Q, Yao X M, Liu X J, Huang Z R 2014 Mater. Des. 56 1009
Google Scholar
[28] Li C T 1970 Z. Kristallogr. Kristallgeom. Kristallphys. Kristallchem. 132 118
Google Scholar
[29] Kobayashi H, Ishibashi N, Akiba T, Mitamura T 1990 J. Ceram. Soc. Jpn. 98 1023
Google Scholar
[30] Xia L, Wang X Y, Wen G W, Zhong B, Song L 2012 Ceram. Int. 38 5315
Google Scholar
[31] Okada Y, Tokumaru Y 1984 J. Appl. Phys. 56 314
Google Scholar
[32] 喻佑华, 刘映珍 1995 陶瓷研究 10 180
Yu Y H, Liu Y Z 1995 Ceram. Stud. J. 10 180
下载:
计量
- 文章访问数: 8723
- PDF下载量: 119
- 被引次数: 0