核((Nd0.7, Ce0.3)2Fe14B)-壳(Nd2Fe14B)型磁体反磁化的微磁学模拟

李栋 董生智 李磊 徐吉元 陈红升 李卫

引用本文:
Citation:

核((Nd0.7, Ce0.3)2Fe14B)-壳(Nd2Fe14B)型磁体反磁化的微磁学模拟

李栋, 董生智, 李磊, 徐吉元, 陈红升, 李卫

Micromagnetic simulations of reversal magnetization in core ((Nd0.7, Ce0.3)2Fe14B)-shell (Nd2Fe14B) type

Li Dong, Dong Sheng-Zhi, Li Lei, Xu Ji-Yuan, Chen Hong-Sheng, Li Wei
PDF
HTML
导出引用
  • 以核((Nd0.7,Ce0.3)2Fe14B)-壳(Nd2Fe14B)型晶粒为研究对象, 利用C++语言进行编程建模, 通过微磁学模拟软件OOMMF进行计算仿真, 系统讨论了核的尺寸、壳层厚度以及壳层分布对单晶粒磁体反磁化过程的影响. 对于核((Nd0.7,Ce0.3)2Fe14B)-壳(Nd2Fe14B)型晶粒, 当壳层厚度不变时, 矫顽力随核的尺寸增加而单调递减. 当核的尺寸不变时, 壳层厚度的增加使得矫顽力先增加后降低. 当核的尺寸不变, 壳层总体积也不变时, 壳层的不同分布会影响矫顽力的大小, 其中当壳层仅平均分布于核的z面(垂直于z轴的两个面)时, 矫顽力达到最大值.
    The effects of core size, shell thickness and shell distribution on the coercivity of single-grain core ((Nd0.7,Ce0.3)2Fe14B)-shell (Nd2Fe14B) magnets are studied by programming and modeling them through using the C++ language. All the micromagnetic simulations are carried out via object oriented micro magnetic framework (OOMMF). The results show that the coercivity decreases with the increase of core size when the shell thickness is constant. It is considered that for the grain, the increase in the size of the core leads the average magnetocrystalline anisotropy field to increase and the total demagnetization energy to increase, thereby contributing to the magnetization reversal occurring under a smaller external field. When the core size is unchanged, as the shell thickness increases gradually, the coercivity first increases and then decreases. The analysis of the position of the nucleation point shows that the reason why the coercivity increases in the early period is mainly that the nucleation point is located at the core-shell junction and belongs to the core. As the thickness of the shell increases, the exchange interaction effect between the magnetic moment of the shell and the one of the nucleation point is strengthened, so a larger external field is needed in the nucleation process. As for the decrease of the coercivity in the later period, the main reason is that the nucleation points are exactly the vertices of the shell (also the vertices of the grain), and the increase of the shell thickness conduces to increasing the total demagnetization energy, so the nucleation points can be formed under a smaller external magnetic field. With core size and shell volume kept unchanged, when the shell is distributed on the two easy-axis planes (i.e. the planes perpendicular to the easy axis) of the core, the coercivity of the magnet reaches a largest value. It is because that the nucleation points are located at the vertices of the shell (also the vertices of the grain), of which the magnetocrystalline anisotropy field is larger, and the demagnetization field is smaller. Via magnetocrystalline anisotropy field, the demagnetization energy, nucleation point, etc, the changes of coercivity in above cases can be explained.
      通信作者: 董生智, dong_shengzhi@163.com
    • 基金项目: 国家级-国家自然科学基金重大项目(51590882)
      Corresponding author: Dong Sheng-Zhi, dong_shengzhi@163.com
    [1]

    Skomski R, Coey J M D 2016 Scr. Mater. 112 112

    [2]

    Sagawa M, Fujimura S, Togawa N, Yamamoto H, Matsuura Y 1984 J. Appl. Phys. 55 2083Google Scholar

    [3]

    Hono K, Sepehri-Amin H 2012 Scr. Mater. 67 530Google Scholar

    [4]

    Herbst J F, Meyer M S, Pinkerton F E 2012 J. Appl. Phys. 111 07A718Google Scholar

    [5]

    Zhang H W, Zhao T Y, Rong C B, Zhang S Y, Han B S, Shen B G 2003 J. Magn. Magn. Mater. 267 224Google Scholar

    [6]

    Gutfleisch O, Willard M A, Brück E, Chen C H, Sankar S G, Liu J P 2011 Adv. Mater. 23 821Google Scholar

    [7]

    Minowa T 2008 Resour. Geol. 58 414Google Scholar

    [8]

    Niu E, Chen Z A, Chen G A, Zhao Y G, Zhang J, Rao X L, Hu B P, Wang Z X 2014 J. Appl. Phys. 115 113912Google Scholar

    [9]

    Xing M Y, Han J Z, Lin Z, Wan F M, Li C, Liu S Q, Wang C S, Yang J B, Yang Y C 2013 J. Magn. Magn. Mater. 331 140Google Scholar

    [10]

    Boltich E B, Oswald E, Huang M Q, Hirosawa S, Wallace W E, Burzo E 1985 J. Appl. Phys. 57 4106Google Scholar

    [11]

    Zhou S X, Wang Y G, Hoier R 1994 J. Appl. Phys. 75 6268Google Scholar

    [12]

    Okada M, Sugimoto S, Ishizaka C, Tanaka T, Homma M 1985 J. Appl. Phys. 57 4146Google Scholar

    [13]

    Li D, Bogatin Y 1991 J. Appl. Phys. 69 5515Google Scholar

    [14]

    Yan C J, Guo S, Chen R J, Lee D, Yan A R 2014 IEEE Trans. Magn. 50 2102605

    [15]

    Zhu M G, Han R, Li W, Huang S L, Zheng D W, Song L W, Shi X N 2015 IEEE Trans. Magn. 51 2104604

    [16]

    Zhu M G, Li W, Wang J D, Zheng L Y, Li Y F, Zhang K, Feng H B, Liu T 2014 IEEE Trans. Magn. 50 1000104

    [17]

    Huang S L, Feng H B, Zhu M G, Li A H, Li Y F, Sun Y C, Zhang Y, Li W 2015 Int. J. Miner. Metall. Mater. 22 417Google Scholar

    [18]

    Li W, Li A H, Feng H B, Huang S L, Wang J D, Zhu M G 2015 IEEE Trans. Magn. 51 2103603

    [19]

    Huang S L, Feng H B, Zhu M G, Li A H, Zhang Y, Li W 2014 AIP Adv. 4 10727

    [20]

    Rong C B, Shen B G 2018 Chin. Phys. B 27 117502Google Scholar

    [21]

    Shang R X, Xiong J F, Liu D, Zuo S L, Zhao X, Li R, Zuo W L, Zhao T Y, Chen R J, Sun J R, Shen B G 2017 Chin. Phys. B 26 057502Google Scholar

    [22]

    Liu D, Zhao T Y, Li R, Zhang M, Shang R X, Xiong J F, Zhang J, Sun J R, Shen B G 2017 AIP Adv. 7 056201Google Scholar

    [23]

    Li R, Liu Y, Zuo S L, Zhao T Y, Hu F X, Sun J R, Shen B G 2018 Chin. Phys. B 27 047501Google Scholar

    [24]

    Li L, Dong S Z, Chen H S, Jiang R J, Li D, Han R, Zhou D, Zhu M G, Wei Li W, Sun W 2019 Chin. Phys. B 28 037502Google Scholar

    [25]

    Sagawa M, Fujimura S, Yamamoto H, Matsuura T, Hirosawa S 1985 J. Appl. Phys. 57 4094Google Scholar

    [26]

    Herbst J F 1991 Rev. Mod. Phys. 63 819Google Scholar

  • 图 1  壳层厚度为常数6 nm, 核的尺寸为变量的核((Nd0.7, Ce0.3)2Fe14B)-壳(Nd2Fe14B)模型

    Fig. 1.  The illustration of core ((Nd0.7, Ce0.3)2Fe14B) - shell (Nd2Fe14B) model of which the shell thickness is a constant of 6 nm while the core size is variable.

    图 2  (a) 矫顽力随核的尺寸(边长x)的变化规律; (b) t = 6 nm时不同核尺寸(边长x)的晶粒的退磁曲线

    Fig. 2.  (a) The relevance of the coercivity to the core size (side length x); (b) the demagnetization curves of grains with different core size (side length x) when t = 6 nm.

    图 3  不同核尺寸(边长)的晶粒总退磁能Ed的比较

    Fig. 3.  Comparisons of the total demagnetization energy Ed of grains with various core size (side length).

    图 4  核的尺寸为常数200 nm × 200 nm × 200 nm, 壳层厚度t为变量的核((Nd0.7, Ce0.3)2Fe14B)-壳(Nd2Fe14B)模型

    Fig. 4.  Illustration of core ((Nd0.7, Ce0.3)2Fe14B) - shell (Nd2Fe14B) model of which the core size is a constant of 200 nm × 200 nm × 200 nm while the shell thickness t is variable.

    图 5  (a) 不同核尺寸下矫顽力随壳层厚度的变化规律; (b) 核尺寸为200 nm × 200 nm × 200 nm时不同壳层厚度的晶粒的退磁曲线

    Fig. 5.  (a) The relevance of the coercivity to the shell thickness; (b) the demagnetization curves of grains with different shell thicknesses when the core size is kept at 200 nm × 200 nm × 200 nm.

    图 6  壳层厚度为2−20 nm时不同的形核点(x-z面视图)(虚线表示核与壳层的边界; 图中放大区域特别标出位置的点表示该模型的形核点; 蓝色箭头代表磁矩与初始磁化方向相同, 即磁矩未反生明显反转, 红色箭头磁矩已经发生反转)

    Fig. 6.  Illustration of the nucleation points for t = 2−20 nm (view of x-z plane) (The dotted lines represent the boundary between the core and the shelll; the point in the magnified area specifically indicates the nucleation point of the model; the blue arrow indicates that the magnetic moment is the same as the initial magnetization direction, that is, the magnetic moment is not reflected. Reversal, the magnetic moment of the red arrow has reversed).

    图 7  外场为48.25 kOe (与矫顽力大小相同)时, t = 6 nm晶粒的磁化反转过程(x-z面视图, y = 21 nm)(虚线表示核与壳层的边界; 蓝色箭头代表磁矩与初始磁化方向相同, 即磁矩未反生明显反转, 红色箭头磁矩已经发生反转)

    Fig. 7.  The reversal process for t = 6 nm (view of x-z plane at y = 21 nm) under external field of 48.25 kOe (equal to the coercivity) (The dotted lines represent the boundary between the core and the shelll; the blue arrow indicates that the magnetic moment is the same as the initial magnetization direction, that is, the magnetic moment is not reflected. Reversal, the magnetic moment of the red arrow has reversed).

    图 8  外场为50.25 kOe (与矫顽力大小相同)时, t = 16 nm晶粒的磁化反转过程(x-z面视图, y = 1 nm)(虚线表示核与壳层的边界; 蓝色箭头代表磁矩与初始磁化方向相同, 即磁矩未反生明显反转, 红色箭头磁矩已经发生反转)

    Fig. 8.  The reversal process for t =16 nm (view of x-z plane at y = 1 nm) under external field of 50.25 kOe (equal to the coercivity) (The dotted lines represent the boundary between the core and the shelll; the blue arrow indicates that the magnetic moment is the same as the initial magnetization direction, that is, the magnetic moment is not reflected. Reversal, the magnetic moment of the red arrow has reversed).

    图 9  不同壳层厚度的晶粒总退磁能Ed随外场的变化

    Fig. 9.  The change of the total demagnetization energy Ed for grains with different shell thicknesses under varying external field.

    图 10  6种核((Nd0.7, Ce0.3)2Fe14B)-壳(Nd2Fe14B)模型, 从左到右: ax型, 壳层只分布在核的x面(即与x轴垂直的面), 两面各一半; az型, 壳层只分布在核的z面(即与z轴垂直的面), 两面各一半; bxy型, 壳层均匀分布在核的x面和y面; bxz型, 壳层均匀分布在核的x面和z面; c型, 壳层均匀分布在核的x面、y面、z面(即均匀包覆); c'型, 壳层在核的x面和y面的厚度均为1 nm, 在核的z面厚度随壳层总体积可变 (图中标示尺寸以Vshell/Vgrain ≈ 50%为例)

    Fig. 10.  Illustration of six types of core ((Nd0.7, Ce0.3)2Fe14B)-shell (Nd2Fe14B) model, from left to right: ax type, the shell is evenly distributed on the two x-planes (the plane perpendicular to the x-axis) of the core; az type, the shell is evenly distributed on the two z-planes (the plane perpendicular to the z-axis) of the core; bxy type, the shell is evenly distributed on the x-planes and the y-planes of the core; bxz type, the shell is evenly distributed on the x-planes and the z-planes of the core; c type, the shell is evenly distributed on the x-planes, y-planes and the z-planes of the core (evenly distributed around the core); c' type, both the shell thicknesses for the x-planes and the y-planes of the core are 1 nm, and the shell thickness for the z-planes of the core is variable with changing total shell volume (The size shown in the figure takes Vshell/Vgrain ≈ 50% as an example).

    图 11  相同壳层体积下6种核壳结构矫顽力的比较

    Fig. 11.  Comparisons for the coercivity of six types of core-shell grain structure with the same shell volume.

    图 12  Vshell/Vgrain ≈ 50%时, 6种晶粒的磁化反转过程图(x-z面视图) (a) az型(x-z面位置: y = 0.5 nm; 外场为59.75 kOe, 与矫顽力大小相同); (b) c'型(x-z面位置: y = 0.5 nm; 外场为59.25 kOe, 与矫顽力大小相同); (c) bxz型(x-z面位置: y = 0.5 nm; 外场为58.75 kOe, 与矫顽力大小相同); (d) c型(x-z面位置: y = 0.5 nm; 外场为57.75 kOe, 与矫顽力大小相同); (e) bxy型(x-z面位置: y = 18.5 nm; 外场为54.75 kOe, 与矫顽力大小相同); (f) ax型(x-z面位置: y = 0.5 nm; 外场为51.25 kOe, 与矫顽力大小相同)

    Fig. 12.  The reversal magnetization processes of six types of grains when Vshell/Vgrain ≈ 50% (view of x-z plane): (a) az type (x-z plane position: y = 0.5 nm; external field is 59.75 kOe, same as coercive force); (b) c' type (x-z plane position: y = 0.5 nm; external field is 59.25 kOe, and the coercive force is the same); (c) bxz type (x-z plane position: y = 0.5 nm; the external field is 58.75 kOe, which is the same as the coercive force); (d) c type (x-z plane position: y = 0.5 nm; the external field is 57.75 kOe, which is the same as the coercive force; (e) bxy type (x-z plane position: y = 18.5 nm; the external field is 54.75 kOe, which is the same as the coercive force); (f) ax type (x-z plane position: y = 0.5 nm; the external field is 51.25 kOe, which is the same as the coercive force).

    图 13  4种晶粒的退磁曲线

    Fig. 13.  The demagnetization curves for four types of grains.

    图 14  4种晶粒 (a) 形核点处z轴方向退磁场Hdz的比较; (b) 总退磁能Ed的比较

    Fig. 14.  (a) Comparisons for the demagnetization field in z-axis direction Hdz of the nucleation points; (b) the total demagnetization energy Ed of four types of grains.

    表 1  壳层厚度保持为6 nm时, 不同核尺寸(边长)的晶粒的总Ce含量及内禀磁性参数

    Table 1.  The total Ce content and intrinsic magnetic parameters of the grain with the same shell thickness 6 nm but different core size (side length).

    Core size(x)/nmTotal Ce content/at.%Average K1 /MJ·m–3Average Ms /kA·m–1Average HA /kA·m–1·kOe–1
    207.324.281255.37(5428.72)/(68.2)
    4013.654.091233.21(5277.48)/(66.3)
    6017.363.981220.24(5189.92)/(65.2)
    8019.733.911211.96(5134.20)/(64.5)
    10021.353.861206.26(5094.40)/(64.0)
    12022.543.821202.11(5062.56)/(63.6)
    14023.443.801198.96(5038.68)/(63.3)
    16024.153.781196.48(5022.76)/(63.1)
    18024.723.761194.48(5006.84)/(62.9)
    20025.193.741192.84(4998.88)/(62.8)
    下载: 导出CSV

    表 2  核的尺寸保持为200 nm × 200 nm × 200 nm时, 不同壳层厚度t的晶粒的总Ce含量及内禀磁性参数

    Table 2.  The total Ce content and intrinsic magnetic parameters of the grain with the same core size 200 nm × 200 nm × 200 nm but different shell thicknesses t.

    t/nmTotal Ce content/at.%Average K1/MJ·m–3Average Ms/kA·m–1Average HA/kA·m–1·kOe–1
    228.273.651182.06(4919.28)/(61.8)
    426.673.701187.66(4959.08)/(62.3)
    625.193.741192.84(4998.88)/(62.8)
    823.813.791197.65(5030.72)/(63.2)
    1022.543.821202.11(5062.56)/(63.6)
    1221.353.861206.26(5094.40)/(64.0)
    1420.253.891210.13(5118.28)/(64.3)
    1619.223.921213.73(5150.12)/(64.7)
    1818.263.951217.09(5174.00)/(65.0)
    2017.363.981220.24(5189.92)/(65.2)
    下载: 导出CSV
  • [1]

    Skomski R, Coey J M D 2016 Scr. Mater. 112 112

    [2]

    Sagawa M, Fujimura S, Togawa N, Yamamoto H, Matsuura Y 1984 J. Appl. Phys. 55 2083Google Scholar

    [3]

    Hono K, Sepehri-Amin H 2012 Scr. Mater. 67 530Google Scholar

    [4]

    Herbst J F, Meyer M S, Pinkerton F E 2012 J. Appl. Phys. 111 07A718Google Scholar

    [5]

    Zhang H W, Zhao T Y, Rong C B, Zhang S Y, Han B S, Shen B G 2003 J. Magn. Magn. Mater. 267 224Google Scholar

    [6]

    Gutfleisch O, Willard M A, Brück E, Chen C H, Sankar S G, Liu J P 2011 Adv. Mater. 23 821Google Scholar

    [7]

    Minowa T 2008 Resour. Geol. 58 414Google Scholar

    [8]

    Niu E, Chen Z A, Chen G A, Zhao Y G, Zhang J, Rao X L, Hu B P, Wang Z X 2014 J. Appl. Phys. 115 113912Google Scholar

    [9]

    Xing M Y, Han J Z, Lin Z, Wan F M, Li C, Liu S Q, Wang C S, Yang J B, Yang Y C 2013 J. Magn. Magn. Mater. 331 140Google Scholar

    [10]

    Boltich E B, Oswald E, Huang M Q, Hirosawa S, Wallace W E, Burzo E 1985 J. Appl. Phys. 57 4106Google Scholar

    [11]

    Zhou S X, Wang Y G, Hoier R 1994 J. Appl. Phys. 75 6268Google Scholar

    [12]

    Okada M, Sugimoto S, Ishizaka C, Tanaka T, Homma M 1985 J. Appl. Phys. 57 4146Google Scholar

    [13]

    Li D, Bogatin Y 1991 J. Appl. Phys. 69 5515Google Scholar

    [14]

    Yan C J, Guo S, Chen R J, Lee D, Yan A R 2014 IEEE Trans. Magn. 50 2102605

    [15]

    Zhu M G, Han R, Li W, Huang S L, Zheng D W, Song L W, Shi X N 2015 IEEE Trans. Magn. 51 2104604

    [16]

    Zhu M G, Li W, Wang J D, Zheng L Y, Li Y F, Zhang K, Feng H B, Liu T 2014 IEEE Trans. Magn. 50 1000104

    [17]

    Huang S L, Feng H B, Zhu M G, Li A H, Li Y F, Sun Y C, Zhang Y, Li W 2015 Int. J. Miner. Metall. Mater. 22 417Google Scholar

    [18]

    Li W, Li A H, Feng H B, Huang S L, Wang J D, Zhu M G 2015 IEEE Trans. Magn. 51 2103603

    [19]

    Huang S L, Feng H B, Zhu M G, Li A H, Zhang Y, Li W 2014 AIP Adv. 4 10727

    [20]

    Rong C B, Shen B G 2018 Chin. Phys. B 27 117502Google Scholar

    [21]

    Shang R X, Xiong J F, Liu D, Zuo S L, Zhao X, Li R, Zuo W L, Zhao T Y, Chen R J, Sun J R, Shen B G 2017 Chin. Phys. B 26 057502Google Scholar

    [22]

    Liu D, Zhao T Y, Li R, Zhang M, Shang R X, Xiong J F, Zhang J, Sun J R, Shen B G 2017 AIP Adv. 7 056201Google Scholar

    [23]

    Li R, Liu Y, Zuo S L, Zhao T Y, Hu F X, Sun J R, Shen B G 2018 Chin. Phys. B 27 047501Google Scholar

    [24]

    Li L, Dong S Z, Chen H S, Jiang R J, Li D, Han R, Zhou D, Zhu M G, Wei Li W, Sun W 2019 Chin. Phys. B 28 037502Google Scholar

    [25]

    Sagawa M, Fujimura S, Yamamoto H, Matsuura T, Hirosawa S 1985 J. Appl. Phys. 57 4094Google Scholar

    [26]

    Herbst J F 1991 Rev. Mod. Phys. 63 819Google Scholar

  • [1] 张家滕, 徐吉元, 金佳莹, 孟睿阳, 董生智. 晶界添加PrCu合金对(Pr, Nd, Dy)32.2Co13Cu0.4FebalB0.98M1.05磁体磁性能与微观组织的影响. 物理学报, 2022, 71(16): 167502. doi: 10.7498/aps.71.20220406
    [2] 张浩杰, 张茹菲, 傅立承, 顾轶伦, 智国翔, 董金瓯, 赵雪芹, 宁凡龙. 一种具有“1111”型结构的新型稀磁半导体(La1–xSrx)(Zn1–xMnx)SbO. 物理学报, 2021, 70(10): 107501. doi: 10.7498/aps.70.20201966
    [3] 李柱柏, 李赟, 秦渊, 张雪峰, 沈保根. 稀土永磁体及复合磁体反磁化过程和矫顽力. 物理学报, 2019, 68(17): 177501. doi: 10.7498/aps.68.20190364
    [4] 肖俊儒, 刘仲武, 楼华山, 詹慧雄. 利用Pr70Cu30晶界扩散改善烧结钕铁硼废料矫顽力的研究. 物理学报, 2018, 67(6): 067502. doi: 10.7498/aps.67.20172551
    [5] 孙璐, 火炎, 周超, 梁建辉, 张祥志, 许子健, 王勇, 吴义政. 利用扫描透射X射线显微镜观测磁涡旋结构. 物理学报, 2015, 64(19): 197502. doi: 10.7498/aps.64.197502
    [6] 侯志鹏, 苏峰, 王文全. 三元Co79Zr18Cr3合金中高矫顽力. 物理学报, 2014, 63(8): 087501. doi: 10.7498/aps.63.087501
    [7] 张嵩波, 王方标, 李发铭, 温戈辉. 高温高压方法合成碳包覆-Fe2O3纳米棒及其磁学性能. 物理学报, 2014, 63(10): 108101. doi: 10.7498/aps.63.108101
    [8] 彭懿, 赵国平, 吴绍全, 斯文静, 万秀琳. 不同易轴取向下对Nd2Fe14B/Fe65Co35磁性双层膜的微磁学模拟. 物理学报, 2014, 63(16): 167505. doi: 10.7498/aps.63.167505
    [9] 郭子政, 胡旭波. 应力对铁磁薄膜磁滞损耗和矫顽力的影响. 物理学报, 2013, 62(5): 057501. doi: 10.7498/aps.62.057501
    [10] 夏静, 张溪超, 赵国平. 易轴取向对Nd2Fe14B/α-Fe双层膜退磁过程影响的微磁学分析. 物理学报, 2013, 62(22): 227502. doi: 10.7498/aps.62.227502
    [11] 侯志鹏, 张金宝, 徐世峰, 吴春姬, 王子涵, 杨坤隆, 王文全, 杜晓波, 苏峰. B元素添加对Co-Zr-Mo合金薄带的磁性能及结构的影响. 物理学报, 2012, 61(20): 207501. doi: 10.7498/aps.61.207501
    [12] 陆海鹏, 韩满贵, 邓龙江, 梁迪飞, 欧雨. Co纳米线磁矩反转动态过程的有限元微磁学模拟. 物理学报, 2010, 59(3): 2090-2096. doi: 10.7498/aps.59.2090
    [13] 杨秀会. W(110)基底上的铁纳米岛初始自发磁化态的微磁学模拟. 物理学报, 2008, 57(11): 7279-7286. doi: 10.7498/aps.57.7279
    [14] 邱学军, 张云鹏, 何正红, 白 浪, 刘国磊, 王 跃, 陈 鹏, 熊祖洪. 矫顽力可调的多孔硅基Fe膜. 物理学报, 2006, 55(11): 6101-6107. doi: 10.7498/aps.55.6101
    [15] 史慧刚, 司明苏, 薛德胜. 段化(A/B)m复合纳米线阵列的矫顽力机理. 物理学报, 2005, 54(7): 3402-3407. doi: 10.7498/aps.54.3402
    [16] 李 腾, 李 卫, 潘 伟, 李岫梅. Fe40—45Cr30—35Co20—25Mo0—4Zr0—2合金微观结构对矫顽力的影响. 物理学报, 2005, 54(9): 4389-4394. doi: 10.7498/aps.54.4389
    [17] 张宏伟, 荣传兵, 张绍英, 沈保根. 高性能纳米复合永磁材料的模拟计算研究. 物理学报, 2004, 53(12): 4347-4352. doi: 10.7498/aps.53.4347
    [18] 翁臻臻, 冯 倩, 黄志高, 都有为. 混合磁性薄膜矫顽力及阶梯效应的微磁学及Monte Carlo研究. 物理学报, 2004, 53(9): 3177-3185. doi: 10.7498/aps.53.3177
    [19] 高汝伟, 冯维存, 王 标, 陈 伟, 韩广兵, 张 鹏, 刘汉强, 李 卫, 郭永权, 李岫梅. 纳米复合永磁材料的有效各向异性与矫顽力. 物理学报, 2003, 52(3): 703-707. doi: 10.7498/aps.52.703
    [20] 张宏伟, 荣传兵, 张 健, 张绍英, 沈保根. 纳米晶永磁Pr2Fe14B微磁学有限元法的模拟计算研究. 物理学报, 2003, 52(3): 718-721. doi: 10.7498/aps.52.718
计量
  • 文章访问数:  5474
  • PDF下载量:  145
  • 被引次数: 0
出版历程
  • 收稿日期:  2020-03-23
  • 修回日期:  2020-04-28
  • 上网日期:  2020-05-08
  • 刊出日期:  2020-07-20

/

返回文章
返回