The defects in Hg1-xCdxTe crystals are observed using HREM. Two kinds of 60° dislocation as well as the twin dislocation in the twin-plane boundary are obserred directly. It is showed that twin dislocation is the activated step of the migration of twin-plane boundary during recrystallization.