Mechanical failures in solid-state lithium batteries and their solution

Liang Yu-Hao; Fan Li-Zhen

doi:10.7498/aps.69.20200713

Abstract

The mechanical properties of electrode materials and solid-state electrolytes in solid-state batteries (SSBs) have an important influence on the mechanical stabilties of SSBs. Mechanical failures in SSBs on different scales and in different components will occur once the stress inside SSBs exceeds the materials’ strengths, which seriously deteriorates the electrochemical performances of SSBs. From the perspective of stabilizing the mechanical stabilities of SSBs, in this review we describe the influences of the mechanical properties of each component in SSBs on the mechanical stabilites of SSBs, and we analyze the factors that affect the mechanical properties of materials. In addition, we also discuss the mechanical failures of SSBs during cycle, including electrode materials’ or solid-state electrolytes’ fractures, electrode-electrolyte contact losses, and short-circuits due to lithium dendrites. Finally, we summarize some common strategies to mitigate the mechanical failures in SSBs, and look forward to the future research directions in this field. Overall, the mechanical failures in SSBs and their strategies discussed in this review will help researchers build SSBs with higher energy density, longer life and higher safety.

Keywords:

Authors and contacts

Institute of Advanced Materials and Technology, Beijing University of Science and Technology, Beijing 100083, China

Corresponding author: Fan Li-Zhen, fanlizhen@ustb.edu.cn

FullText HTML : translate this paragraph

References

[1]	Ding Y, Cano Z P, Yu A, Lu J, Chen Z 2019 Electrochem. Energy Rev. 2 1 Google Scholar
[2]	Choi J W, Aurbach D 2016 Nat. Rev. Mater. 1 16013 Google Scholar
[3]	Li W, Erickson E M, Manthiram A 2020 Nat. Energy 5 26 Google Scholar
[4]	Tarascon J M, Armand M 2001 Nature 414 359 Google Scholar
[5]	Deng J, Bae C, Denlinger A, Miller T 2020 Joule 4 511 Google Scholar
[6]	Li H 2019 Joule 3 911 Google Scholar
[7]	Wu F, Maier J, Yu Y 2020 Chem. Soc. Rev. 49 1569 Google Scholar
[8]	Manthiram A, Yu X, Wang S 2017 Nat. Rev. Mater. 2 16103 Google Scholar
[9]	Lopez J, Mackanic D G, Cui Y, Bao Z 2019 Nat. Rev. Mater. 4 312 Google Scholar
[10]	Boaretto N, Meabe L, Martinez Ibañez M, Armand M, Zhang H 2020 J. Electrochem. Soc. 167 070524 Google Scholar
[11]	Zhao N, Khokhar W, Bi Z, Shi C, Guo X, Fan L Z, Nan C W 2019 Joule 3 1190 Google Scholar
[12]	Bachman J C, Muy S, Grimaud A, Chang H H, Pour N, Lux S F, Paschos O, Maglia F, Lupart S, Lamp P, Giordano L, Shao Horn Y 2016 Chem. Rev. 116 140 Google Scholar
[13]	Zhang Q, Cao D, Ma Y, Natan A, Aurora P, Zhu H 2019 Adv. Mater. 31 1901131 Google Scholar
[14]	Hu Y S 2016 Nat. Energy 1 16042 Google Scholar
[15]	Lu Y, Li L, Zhang Q, Niu Z, Chen J 2018 Joule 2 1747 Google Scholar
[16]	Cao Y, Li M, Lu J, Liu J, Amine K 2019 Nat. Nanotechnol. 14 200 Google Scholar
[17]	Du M, Liao K, Lu Q, Shao Z 2019 Energy Environ. Sci. 12 1780 Google Scholar
[18]	Zhao Q, Stalin S, Zhao C Z, Archer L A 2020 Nat. Rev. Mater. 5 229 Google Scholar
[19]	He Y, Lu C, Liu S, Zheng W, Luo J 2019 Adv. Energy Mater. 9 1901810 Google Scholar
[20]	Chen H, Ling M, Hencz L, Ling H Y, Li G, Lin Z, Liu G, Zhang S 2018 Chem. Rev. 118 8936 Google Scholar
[21]	Zhang F, Huang Q A, Tang Z, Li A, Shao Q, Zhang L, Li X, Zhang J 2020 Nano Energy 70 104545 Google Scholar
[22]	Stone G M, Mullin S A, Teran A A, Hallinan D T, Minor A M, Hexemer A, Balsara N P 2012 J. Electrochem. Soc. 159 222 Google Scholar
[23]	Monroe C, Newman J 2005 J. Electrochem. Soc. 152 396 Google Scholar
[24]	Famprikis T, Canepa P, Dawson J A, Islam M S, Masquelier C 2019 Nat. Mater. 18 1278 Google Scholar
[25]	Schnell J, Günther T, Knoche T, Vieider C, Köhler L, Just A, Keller M, Passerini S, Reinhart G 2018 J. Power Sources 382 160 Google Scholar
[26]	Liang J, Luo J, Sun Q, Yang X, Li R, Sun X 2019 Energy Storage Mater. 21 308 Google Scholar
[27]	Kato Y, Hori S, Saito T, Suzuki K, Hirayama M, Mitsui A, Yonemura M, Iba H, Kanno R 2016 Nat. Energy 1 16030 Google Scholar
[28]	Judez X, Eshetu G G, Li C, Rodriguez Martinez L M, Zhang H, Armand M 2018 Joule 2 2208 Google Scholar
[29]	Cho Y H, Wolfenstine J, Rangasamy E, Kim H, Choe H, Sakamoto J 2012 J. Mater. Sci. 47 5970
[30]	Kim Y, Jo H, Allen J L, Choe H, Wolfenstine J, Sakamoto J 2016 J. Am. Ceram. Soc. 99 1367 Google Scholar
[31]	Jackman S D, Cutler R A 2012 J. Power Sources 218 65
[32]	Yu S, Schmidt R D, Garcia Mendez R, Herbert E, Dudney N J, Wolfenstine J B, Sakamoto J, Siegel D J 2016 Chem. Mater. 28 197 Google Scholar
[33]	McGrogan F P, Swamy T, Bishop S R, Eggleton E, Porz L, Chen X, Chiang Y M, Van Vliet K J 2017 Adv. Energy Mater. 7 1602011 Google Scholar
[34]	Deng Z, Wang Z, Chu I H, Luo J, Ong S P 2015 J. Electrochem. Soc. 163 A67
[35]	Xie J, Duan R G, Han Y, Kerr J B 2004 Solid State Ionics 175 755 Google Scholar
[36]	Ji J, Li B, Zhong W H 2010 J. Phys. Chem. B 114 13637 Google Scholar
[37]	Chen Yang Y W, Chen H C, Lin F J, Chen C C 2002 Solid State Ionics 150 327 Google Scholar
[38]	Chung N K, Kwon Y D, Kim D 2003 J. Power Sources 124 148 Google Scholar
[39]	Mukhopadhyay A, Sheldon B W 2014 Prog. Mater Sci. 63 58 Google Scholar
[40]	Xu R C, Xia X H, Li S H, Zhang S Z, Wang X L, Tu J P 2017 J. Mater. Chem. A 5 6310 Google Scholar
[41]	Qi Y, Guo H, Hector L G, Timmons A 2010 J. Electrochem. Soc. 157 A558 Google Scholar
[42]	Beaulieu L Y, Eberman K W, Turner R L, Krause L J, Dahn J R 2001 Electrochem. Solid-State Lett. 4 A137 Google Scholar
[43]	Zhang W, Schröder D, Arlt T, Manke I, Koerver R, Pinedo R, Weber D A, Sann J, Zeier W G, Janek J 2017 J. Mater. Chem. A 5 9929 Google Scholar
[44]	Kim J, Lee H, Cha H, Yoon M, Park M, Cho J 2018 Adv. Energy Mater. 8 1702028 Google Scholar
[45]	Zhang W, Richter F H, Culver S P, Leichtweiss T, Lozano J G, Dietrich C, Bruce P G, Zeier W G, Janek J 2018 ACS Appl. Mater. Interfaces 10 22226 Google Scholar
[46]	Park K H, Bai Q, Kim D H, Oh D Y, Zhu Y, Mo Y, Jung Y S 2018 Adv. Energy Mater. 8 1800035 Google Scholar
[47]	Reimers J, Dahn J 1992 J. Electrochem. Soc. 139 2091 Google Scholar
[48]	Su L, Jing Y, Zhou Z 2011 Nanoscale 3 3967 Google Scholar
[49]	Yin S C, Rho Y H, Swainson I, Nazar L F 2006 Chem. Mater. 18 1901 Google Scholar
[50]	Padhi A K 1997 J. Electrochem. Soc. 144 1188 Google Scholar
[51]	Han F, Yue J, Fan X, Gao T, Luo C, Ma Z, Suo L, Wang C 2016 Nano Lett. 16 4521 Google Scholar
[52]	Ohzuku T 1995 J. Electrochem. Soc. 142 1431 Google Scholar
[53]	Nonemacher J F, Hüter C, Zheng H, Malzbender J, Krüger M, Spatschek R, Finsterbusch M 2018 Solid State Ionics 321 126 Google Scholar
[54]	Sharafi A, Haslam C G, Kerns R D, Wolfenstine J, Sakamoto J 2017 J. Mater. Chem. A 5 21491 Google Scholar
[55]	Li Y, Chen X, Dolocan A, Cui Z, Xin S, Xue L, Xu H, Park K, Goodenough J B 2018 J. Am. Chem. Soc. 140 6448 Google Scholar
[56]	Dai J, Yang C, Wang C, Pastel G, Hu L 2018 Adv. Mater. 30 1802068 Google Scholar
[57]	Sun H H, Ryu H H, Kim U H, Weeks J A, Heller A, Sun Y K, Mullins C B 2020 ACS Energy Lett. 5 1136 Google Scholar
[58]	Park K J, Hwang J Y, Ryu H H, Maglia F, Kim S J, Lamp P, Yoon C S, Sun Y K 2019 ACS Energy Lett. 4 1394 Google Scholar
[59]	Zhou H, Xin F, Pei B, Whittingham M S 2019 ACS Energy Lett. 4 1902 Google Scholar
[60]	Park K J, Jung H G, Kuo L Y, Kaghazchi P, Yoon C S, Sun Y K 2018 Adv. Energy Mater. 8 1801202 Google Scholar
[61]	Ryu H H, Park K J, Yoon D R, Aishova A, Yoon C S, Sun Y K 2019 Adv. Energy Mater. 9 1902698 Google Scholar
[62]	Kim H, Lee E J, Sun Y K 2014 Mater. Today 17 285 Google Scholar
[63]	Smith S, Thompson T, Sakamoto J, Allen J L, Baker D R, Wolfenstine J 2017 Solid State Ionics 300 38 Google Scholar
[64]	Dixit M B, Zaman W, Bootwala Y, Zheng Y, Hatzell M C, Hatzell K B 2019 ACS Appl. Mater. Interfaces 11 45087 Google Scholar
[65]	Troy S, Schreiber A, Reppert T, Gehrke H G, Finsterbusch M, Uhlenbruck S, Stenzel P 2016 Appl. Energy 169 757 Google Scholar
[66]	Sakuda A, Hayashi A, Tatsumisago M 2013 Sci. Rep. 3 2261 Google Scholar
[67]	Kato A, Yamamoto M, Sakuda A, Hayashi A, Tatsumisago M 2018 ACS Appl. Energy Mater. 1 1002 Google Scholar
[68]	Aidoud D, Etiemble A, Guy Bouyssou D, Maire E, Le Bideau J, Guyomard D, Lestriez B 2016 J. Power Sources 330 92 Google Scholar
[69]	Weston J E, Steele B C H 1982 Solid State Ionics 7 75 Google Scholar
[70]	Arya A, Sharma A L 2020 J. Mater. Sci. 55 6242 Google Scholar
[71]	Jiang G, Maeda S, Yang H, Saito Y, Tanase S, Sakai T 2005 J. Power Sources 141 143 Google Scholar
[72]	Lee W, Lyon C K, Seo J H, Lopez-Hallman R, Leng Y, Wang C Y, Hickner M A, Randall C A, Gomez E D 2019 Adv. Funct. Mater. 29 1807872 Google Scholar
[73]	Li S, Zhang S Q, Shen L, Liu Q, Ma J B, Lv W, He Y B, Yang Q H 2020 Adv. Sci. 7 1903088 Google Scholar
[74]	Hu X, Yan G, Cheng X, Malzbender J, Qiang W, Huang B 2019 J. Am. Ceram. Soc. 102 1953
[75]	Hu X, Cheng X, Qin S, Yan G, Malzbender J, Qiang W, Huang B 2018 Ceram. Int. 44 1902 Google Scholar
[76]	Ishidzu K, Oka Y, Nakamura T 2016 Solid State Ionics 288 176 Google Scholar
[77]	Kalluri S, Yoon M, Jo M, Park S, Myeong S, Kim J, Dou S X, Guo Z, Cho J 2017 Adv. Energy Mater. 7 1601507 Google Scholar
[78]	Xu X, Huo H, Jian J, Wang L, Zhu H, Xu S, He X, Yin G, Du C, Sun X 2019 Adv. Energy Mater. 9 1803963 Google Scholar
[79]	Zhang C, Xu S, Han B, Lin G, Huang Q, Ivey D G, Yang C, Wang P, Wei W 2019 J. Power Sources 431 40 Google Scholar
[80]	Wu B, Wang S, Evans Iv W J, Deng D Z, Yang J, Xiao J 2016 J. Mater. Chem. A 4 15266 Google Scholar
[81]	Li H, Liu A, Zhang N, Wang Y, Yin S, Wu H, Dahn J R 2019 Chem. Mater. 31 7574 Google Scholar
[82]	Cheng X B, Zhang R, Zhao C Z, Wei F, Zhang J G, Zhang Q 2016 Adv. Sci. 3 1500213 Google Scholar
[83]	Waetzig K, Rost A, Langklotz U, Matthey B, Schilm J 2016 J. Eur. Ceram. Soc. 36 1995 Google Scholar
[84]	Bucci G, Swamy T, Chiang Y M, Carter W C 2017 J. Mater. Chem. A 5 19422 Google Scholar
[85]	Koerver R, Aygün I, Leichtweiß T, Dietrich C, Zhang W, Binder J O, Hartmann P, Zeier W G, Janek J 2017 Chem. Mater. 29 5574 Google Scholar
[86]	Xiao Y, Wang Y, Bo S H, Kim J C, Miara L J, Ceder G 2019 Nat. Rev. Mater. 5 105
[87]	Kuang Y, Chen C, Kirsch D, Hu L 2019 Adv. Energy Mater. 9 1901457 Google Scholar
[88]	Devaux D, Harry K J, Parkinson D Y, Yuan R, Hallinan D T, MacDowell A A, Balsara N P 2015 J. Electrochem. Soc. 162 A1301 Google Scholar
[89]	Liu T, Zhang Y, Chen R, Zhao S X, Lin Y, Nan C W, Shen Y 2017 Electrochem. Commun. 79 1 Google Scholar
[90]	Huang W, Zhao N, Bi Z, Shi C, Guo X, Fan L, Nan C 2020 Mater. Today Nano 10 100075 Google Scholar
[91]	Dixit M B, Zaman W, Hortance N, Vujic S, Harkey B, Shen F, Tsai W Y, De Andrade V, Chen X C, Balke N, Hatzell K B 2020 Joule 4 207 Google Scholar
[92]	Zhao N, Fang R, He M H, Chen C, Li Y Q, Bi Z J, Guo X X 2018 Rare Met. 37 473 Google Scholar
[93]	Sakamoto J 2019 Nat. Energy 4 827 Google Scholar
[94]	Kim S H, Kim K, Choi H, Im D, Heo S, Choi H S 2019 J. Mater. Chem. A 7 13650 Google Scholar
[95]	Cheng X B, Zhang R, Zhao C Z, Zhang Q 2017 Chem. Rev. 117 10403 Google Scholar
[96]	Xia S, Wu X, Zhang Z, Cui Y, Liu W 2019 Chem. 5 753 Google Scholar
[97]	Khurana R, Schaefer J L, Archer L A, Coates G W 2014 J. Am. Chem. Soc. 136 7395 Google Scholar
[98]	Hatzell K B, Chen X C, Cobb C L, Dasgupta N P, Dixit M B, Marbella L E, McDowell M T, Mukherjee P P, Verma A, Viswanathan V, Westover A S, Zeier W G 2020 ACS Energy Lett. 5 922 Google Scholar
[99]	Liu H, Cheng X B, Huang J Q, Yuan H, Lu Y, Yan C, Zhu G L, Xu R, Zhao C Z, Hou L P, He C, Kaskel S, Zhang Q 2020 ACS Energy Lett. 5 833 Google Scholar
[100]	Ishiguro K, Nemori H, Sunahiro S, Nakata Y, Sudo R, Matsui M, Takeda Y, Yamamoto O, Imanishi N 2014 J. Electrochem. Soc. 161 A668 Google Scholar
[101]	Zhang X, Wang A, Liu X, Luo J 2019 Acc. Chem. Res. 52 3223 Google Scholar
[102]	Kasemchainan J, Zekoll S, Spencer Jolly D, Ning Z, Hartley G O, Marrow J, Bruce P G 2019 Nat. Mater. 18 1105 Google Scholar
[103]	Doux J M, Nguyen H, Tan D H S, Banerjee A, Wang X, Wu E A, Jo C, Yang H, Meng Y S 2019 Adv. Energy Mater. 10 1903253
[104]	Yan P, Zheng J, Liu J, Wang B, Cheng X, Zhang Y, Sun X, Wang C, Zhang J G 2018 Nat. Energy 3 600 Google Scholar
[105]	Jung S H, Kim U H, Kim J H, Jun S, Yoon C S, Jung Y S, Sun Y K 2019 Adv. Energy Mater. 10 1903360
[106]	Liu Y, Harlow J, Dahn J 2020 J. Electrochem. Soc. 167 020512 Google Scholar
[107]	Lee H, Oh P, Kim J, Cha H, Chae S, Lee S, Cho J 2019 Adv. Mater. 31 1900376 Google Scholar
[108]	Zeng H, Ji X, Tsai F, Zhang Q, Jiang T, Li R K Y, Shi H, Luan S, Shi D 2018 Solid State Ionics 320 92 Google Scholar
[109]	Ohta N, Takada K, Sakaguchi I, Zhang L, Ma R, Fukuda K, Osada M, Sasaki T 2007 Electrochem. Commun. 9 1486 Google Scholar
[110]	Bi Z, Zhao N, Ma L, Fu Z, Xu F, Wang C, Guo X 2020 Chem. Eng. J. 387 124089 Google Scholar
[111]	Bi Z, Zhao N, Ma L, Shi C, Fu Z, Xu F, Guo X 2020 J. Mater. Chem. A 8 4252 Google Scholar
[112]	Zhang X D, Shi J L, Liang J Y, Wang L P, Yin Y X, Jiang K C, Guo Y G 2019 J. Power Sources 426 242 Google Scholar
[113]	Yubuchi S, Ito Y, Matsuyama T, Hayashi A, Tatsumisago M 2016 Solid State Ionics 285 79 Google Scholar
[114]	Ito Y, Otoyama M, Hayashi A, Ohtomo T, Tatsumisago M 2017 J. Power Sources 360 328 Google Scholar
[115]	Koerver R, Zhang W, de Biasi L, Schweidler S, Kondrakov A O, Kolling S, Brezesinski T, Hartmann P, Zeier W G, Janek J 2018 Energy Environ. Sci. 11 2142 Google Scholar
[116]	Sakuda A, Hayashi A, Tatsumisago M 2013 Scientific Reports 3 2261
[117]	Shi T, Tu Q, Tian Y, Xiao Y, Miara L J, Kononova O, Ceder G 2019 Adv. Energy Mater. 10 1902881
[118]	Park K, Yu B C, Jung J W, Li Y, Zhou W, Gao H, Son S, Goodenough J B 2016 Chem. Mater. 28 8051 Google Scholar
[119]	Li Y, Wang Z, Li C, Cao Y, Guo X 2014 J. Power Sources 248 642 Google Scholar
[120]	Han F, Yue J, Chen C, Zhao N, Fan X, Ma Z, Gao T, Wang F, Guo X, Wang C 2018 Joule 2 497 Google Scholar
[121]	Liu Y, Sun Q, Wang D, Adair K, Liang J, Sun X 2018 J. Power Sources 393 193 Google Scholar
[122]	Guo J, Berbano S S, Guo H, Baker A L, Lanagan M T, Randall C A 2016 Adv. Funct. Mater. 26 7115 Google Scholar
[123]	Sun C, Liu J, Gong Y, Wilkinson D P, Zhang J 2017 Nano Energy 33 363 Google Scholar
[124]	Wang X, Zhang Y, Zhang X, Liu T, Lin Y H, Li L, Shen Y, Nan C W 2018 ACS Appl. Mater. Interfaces 10 24791 Google Scholar
[125]	Pervez S A, Ganjeh Anzabi P, Farooq U, Trifkovic M, Roberts E P L, Thangadurai V 2019 Adv. Mater. Interfaces 6 1900186
[126]	Huo H, Sun J, chen C, Meng X, He M, Zhao N, Guo X 2018 J. Power Sources 383 150 Google Scholar
[127]	Liu S, Imanishi N, Zhang T, Hirano A, Takeda Y, Yamamoto O, Yang J 2010 J. Power Sources 195 6847 Google Scholar
[128]	Gai J, Ma F, Zhang Z, Sun D, Jin Y, Guo Y, Kim W 2019 ACS Sustainable Chem. Eng. 7 15896 Google Scholar
[129]	Zhou W, Wang S, Li Y, Xin S, Manthiram A, Goodenough J B 2016 J. Am. Chem. Soc. 138 9385 Google Scholar
[130]	Huo H, Chen Y, Luo J, Yang X, Guo X, Sun X 2019 Adv. Energy Mater. 9 1804004 Google Scholar
[131]	Duan H, Fan M, Chen W P, Li J Y, Wang P F, Wang W P, Shi J L, Yin Y X, Wan L J, Guo Y G 2019 Adv. Mater. 31 1807789 Google Scholar
[132]	Stone G M, Mullin S A, Teran A A, Hallinan D T, Minor A M, Hexemer A, Balsara N P 2012 J. Electrochem. Soc. 159 A222
[133]	Xu B, Li W, Duan H, Wang H, Guo Y, Li H, Liu H 2017 J. Power Sources 354 68 Google Scholar
[134]	Choudhury S, Vu D, Warren A, Tikekar M D, Tu Z, Archer L A 2018 Proc. Natl. Acad. Sci. 115 6620 Google Scholar

Cited By

图 1 材料典型的应力-应变曲线

Figure 1. A typical stress-strain curve of materials.

DownLoad: Full-Size Img PowerPoint

图 2 NCA89和NCW90材料的　(a) a和c轴晶格参数; (b)晶胞体积随着电池电压的变化图; (c) NCA89和(d) NCW90材料在充电到4.3 V下截面的明场STEM-mosaic图^[61]

Figure 2. Changes in (a) a- and c-axis lattice parameters and (b) unit cell volumes for NCA89 and NCW90 as a function of the cell voltage; bright-filed STEM mosaic image of a cross-section of (c) NCA89 and (d) NCW90 at charged to 4.3 V^[61].

DownLoad: Full-Size Img PowerPoint

图 3 (100–y)(0.75 Li₂S·0.25 P₂S₅) ·yLiI(mol%)(y=0, 5, 10, 20, 和30)玻璃的杨氏模量和LiI含量的关系^[67]

Figure 3. Relationship between the Young’s moduli and LiI content of (100–y)(0.75 Li₂S·0.25 P₂S₅) ·yLiI(mol%)(y=0, 5, 10, 20, and 30) glasses^[67].

DownLoad: Full-Size Img PowerPoint

图 4 LiCoO₂在电池循环后破裂的SEM图^[45]

Figure 4. SEM images of fracturing of LiCoO₂ particles in cycled battery^[45].

DownLoad: Full-Size Img PowerPoint

图 5 NCM811/β-Li₃PS₄/In全固态电池首次循环不可逆容量损失的示意图^[85]

Figure 5. Schematic diagram of the irreversible first cycle capacity loss of the NCM811/β-Li₃PS₄/In all-solid-state battery^[85].

DownLoad: Full-Size Img PowerPoint

图 6 堆叠压力对锂金属固态电池短路行为的影响示意图　(a) 在电池制备期间, 在对电池施加压力之前, 电解质和锂金属之间的接触不良; (b)在25 MPa的压力下, 锂金属和电解质的物理接触得到改善; (c)即使随后将压力降低到5 MPa, 也会使锂对称电池的阻抗大幅降低; (d)在5 MPa的堆叠压力下进行沉积/剥离测试, 未观察到Li在电解质颗粒内部蠕变的现象; (e)在25 MPa的压力下, Li在电解质的晶粒之间缓慢蠕变, 并且在这些枝晶上产生沉积过程, 最终在48 h后电池发生短路; (f)当电池的堆叠压力过高时, Li会通过蠕变在电解质中形成树枝状枝晶, 从而使电池机械短路^[103]

Figure 6. Schematic of the effect of the stack pressure on the shorting behavior of Li metal solid-state batteries:　(a) During cell fabrication, the contact between the electrolyte and Li metal is poor before pressing the Li metal on the electrolyte pellet; (b) Pressing the Li metal at 25 MPa allows for proper wetting of the electrolyte and (c) induces a large drop in the symmetric cell impedance, even when the pressure is later released to 5 MPa; (d) plating and stripping at a stack pressure of 5 MPa, no creeping of Li inside the SSE pellet is observed; (e) at a stack pressure of 25 MPa, Li slowly creeps between the grains of the SSE and plating occurs on these dendrites, eventually shorting the cell after 48 h; (f) when the stack pressure is too high, Li creeps through the electrolyte and forms dendrites that mechanically short the cell^[103].

DownLoad: Full-Size Img PowerPoint

图 7 全固态电池中NCA80和FCG75电极的不同微观结构和界面演化示意图^[105]

Figure 7. Schematic diagram of the different microstructural and interfical evolutions in the NCA80 and FCG75 electrodes in all-solid-state batteries^[105].

DownLoad: Full-Size Img PowerPoint

图 8 PIC–5 μm, CIP–200 nm和多层“三明治”型复合固态电解质的示意图^[130]

Figure 8. The schematic illustration of the PIC–5 µm, CIP–200 nm, and hierarchical sandwich-type composite electrolytes^[130].

DownLoad: Full-Size Img PowerPoint

表 1 固态电池材料的力学性能

Table 1. Mechanical properties of solid-state battery materials.

电池材料		杨氏模量/GPa	剪切模量/GPa	硬度/GPa	泊松比(B/G)	K_c/MPa·m^1/2
氧化物电解质	Li_0.33La_0.57TiO₃^[29]	200	80	9.2	1.66	~1
	Li₇La₃Zr₂O₁₂^[30]	150	59.6	9.1	1.72	0.92–2.73
	Li_1.3Al_0.3Ti_1.7(PO₄)₃^[31]	115		7.1		1.10
	Li_6.5La₃Zr_1.5Ta_0.5O₁₂^[32]	153.8 ± 2.7	61.2 ± 1.1		1.59
硫化物电解质	Li₂S-P₂S₅^[33]	18.5	7.1 ± 0.3	1.9		0.23 ± 0.04
	Li₇P₃S₁₁^[34]
	Li₁₀GeP₂S₁₂^[34]	21.7	7.9		3.44
	Li₁₀SnP₂S₁₂^[34]	29.1	11.2		2.09
	Li₅PS₅Cl^[34]	22.1	8.1		3.57
聚合物电解质	PEO+LiTFSI^[35]	~10^–6
	PEO+ LiClO₄^[36]	14.5 × 10^–3
	PAN+LiClO₄^[37]	1.6 × 10³
	PVDF+LiBF₄^[38]	0.3 × 10^–3
电极材料	LiCoO₂^[33]	178—191		8.3		0.94
	LiFePO₄^[39]	125.9	48.9		2.02
	NCM^[40]	198		11
	石墨^[41]	32	12		2.34
	Si^[42]	113		16.6
	Li^[33]	5	4.25	10^–3

DownLoad: CSV

表 2 电极材料在电池循环过程中的体积变化

Table 2. Volume variation of electrode materials during battery cycle.

电极材料		嵌锂/锂化产物	体积变化/%
正极	LiCoO₂	Li_0.5CoO₂	2^[47]
	LiNiO₂	Li_0.5NiO₂	2.8^[48]
	LiMnO₂	Li_0.5MnO₂	5.6^[48]
	LiNi_1/3Co_1/3 Mn_1/3O₂	Li_0.04Ni_1/3Co_1/3 Mn_1/3O₂	7.2^[49]
	LiFePO₄	FePO₄	7^[50]
	S	Li₂S	76^[51]
负极	Si	Li₁₅Si₄	310^[42]
	石墨	LiC₆	13^[41]
	Li₄Ti₅O12	Li₂[Li_1/3Ti_5/3]O₄	0.2^[52]

DownLoad: CSV

[1]	Ding Y, Cano Z P, Yu A, Lu J, Chen Z 2019 Electrochem. Energy Rev. 2 1 Google Scholar
[2]	Choi J W, Aurbach D 2016 Nat. Rev. Mater. 1 16013 Google Scholar
[3]	Li W, Erickson E M, Manthiram A 2020 Nat. Energy 5 26 Google Scholar
[4]	Tarascon J M, Armand M 2001 Nature 414 359 Google Scholar
[5]	Deng J, Bae C, Denlinger A, Miller T 2020 Joule 4 511 Google Scholar
[6]	Li H 2019 Joule 3 911 Google Scholar
[7]	Wu F, Maier J, Yu Y 2020 Chem. Soc. Rev. 49 1569 Google Scholar
[8]	Manthiram A, Yu X, Wang S 2017 Nat. Rev. Mater. 2 16103 Google Scholar
[9]	Lopez J, Mackanic D G, Cui Y, Bao Z 2019 Nat. Rev. Mater. 4 312 Google Scholar
[10]	Boaretto N, Meabe L, Martinez Ibañez M, Armand M, Zhang H 2020 J. Electrochem. Soc. 167 070524 Google Scholar
[11]	Zhao N, Khokhar W, Bi Z, Shi C, Guo X, Fan L Z, Nan C W 2019 Joule 3 1190 Google Scholar
[12]	Bachman J C, Muy S, Grimaud A, Chang H H, Pour N, Lux S F, Paschos O, Maglia F, Lupart S, Lamp P, Giordano L, Shao Horn Y 2016 Chem. Rev. 116 140 Google Scholar
[13]	Zhang Q, Cao D, Ma Y, Natan A, Aurora P, Zhu H 2019 Adv. Mater. 31 1901131 Google Scholar
[14]	Hu Y S 2016 Nat. Energy 1 16042 Google Scholar
[15]	Lu Y, Li L, Zhang Q, Niu Z, Chen J 2018 Joule 2 1747 Google Scholar
[16]	Cao Y, Li M, Lu J, Liu J, Amine K 2019 Nat. Nanotechnol. 14 200 Google Scholar
[17]	Du M, Liao K, Lu Q, Shao Z 2019 Energy Environ. Sci. 12 1780 Google Scholar
[18]	Zhao Q, Stalin S, Zhao C Z, Archer L A 2020 Nat. Rev. Mater. 5 229 Google Scholar
[19]	He Y, Lu C, Liu S, Zheng W, Luo J 2019 Adv. Energy Mater. 9 1901810 Google Scholar
[20]	Chen H, Ling M, Hencz L, Ling H Y, Li G, Lin Z, Liu G, Zhang S 2018 Chem. Rev. 118 8936 Google Scholar
[21]	Zhang F, Huang Q A, Tang Z, Li A, Shao Q, Zhang L, Li X, Zhang J 2020 Nano Energy 70 104545 Google Scholar
[22]	Stone G M, Mullin S A, Teran A A, Hallinan D T, Minor A M, Hexemer A, Balsara N P 2012 J. Electrochem. Soc. 159 222 Google Scholar
[23]	Monroe C, Newman J 2005 J. Electrochem. Soc. 152 396 Google Scholar
[24]	Famprikis T, Canepa P, Dawson J A, Islam M S, Masquelier C 2019 Nat. Mater. 18 1278 Google Scholar
[25]	Schnell J, Günther T, Knoche T, Vieider C, Köhler L, Just A, Keller M, Passerini S, Reinhart G 2018 J. Power Sources 382 160 Google Scholar
[26]	Liang J, Luo J, Sun Q, Yang X, Li R, Sun X 2019 Energy Storage Mater. 21 308 Google Scholar
[27]	Kato Y, Hori S, Saito T, Suzuki K, Hirayama M, Mitsui A, Yonemura M, Iba H, Kanno R 2016 Nat. Energy 1 16030 Google Scholar
[28]	Judez X, Eshetu G G, Li C, Rodriguez Martinez L M, Zhang H, Armand M 2018 Joule 2 2208 Google Scholar
[29]	Cho Y H, Wolfenstine J, Rangasamy E, Kim H, Choe H, Sakamoto J 2012 J. Mater. Sci. 47 5970
[30]	Kim Y, Jo H, Allen J L, Choe H, Wolfenstine J, Sakamoto J 2016 J. Am. Ceram. Soc. 99 1367 Google Scholar
[31]	Jackman S D, Cutler R A 2012 J. Power Sources 218 65
[32]	Yu S, Schmidt R D, Garcia Mendez R, Herbert E, Dudney N J, Wolfenstine J B, Sakamoto J, Siegel D J 2016 Chem. Mater. 28 197 Google Scholar
[33]	McGrogan F P, Swamy T, Bishop S R, Eggleton E, Porz L, Chen X, Chiang Y M, Van Vliet K J 2017 Adv. Energy Mater. 7 1602011 Google Scholar
[34]	Deng Z, Wang Z, Chu I H, Luo J, Ong S P 2015 J. Electrochem. Soc. 163 A67
[35]	Xie J, Duan R G, Han Y, Kerr J B 2004 Solid State Ionics 175 755 Google Scholar
[36]	Ji J, Li B, Zhong W H 2010 J. Phys. Chem. B 114 13637 Google Scholar
[37]	Chen Yang Y W, Chen H C, Lin F J, Chen C C 2002 Solid State Ionics 150 327 Google Scholar
[38]	Chung N K, Kwon Y D, Kim D 2003 J. Power Sources 124 148 Google Scholar
[39]	Mukhopadhyay A, Sheldon B W 2014 Prog. Mater Sci. 63 58 Google Scholar
[40]	Xu R C, Xia X H, Li S H, Zhang S Z, Wang X L, Tu J P 2017 J. Mater. Chem. A 5 6310 Google Scholar
[41]	Qi Y, Guo H, Hector L G, Timmons A 2010 J. Electrochem. Soc. 157 A558 Google Scholar
[42]	Beaulieu L Y, Eberman K W, Turner R L, Krause L J, Dahn J R 2001 Electrochem. Solid-State Lett. 4 A137 Google Scholar
[43]	Zhang W, Schröder D, Arlt T, Manke I, Koerver R, Pinedo R, Weber D A, Sann J, Zeier W G, Janek J 2017 J. Mater. Chem. A 5 9929 Google Scholar
[44]	Kim J, Lee H, Cha H, Yoon M, Park M, Cho J 2018 Adv. Energy Mater. 8 1702028 Google Scholar
[45]	Zhang W, Richter F H, Culver S P, Leichtweiss T, Lozano J G, Dietrich C, Bruce P G, Zeier W G, Janek J 2018 ACS Appl. Mater. Interfaces 10 22226 Google Scholar
[46]	Park K H, Bai Q, Kim D H, Oh D Y, Zhu Y, Mo Y, Jung Y S 2018 Adv. Energy Mater. 8 1800035 Google Scholar
[47]	Reimers J, Dahn J 1992 J. Electrochem. Soc. 139 2091 Google Scholar
[48]	Su L, Jing Y, Zhou Z 2011 Nanoscale 3 3967 Google Scholar
[49]	Yin S C, Rho Y H, Swainson I, Nazar L F 2006 Chem. Mater. 18 1901 Google Scholar
[50]	Padhi A K 1997 J. Electrochem. Soc. 144 1188 Google Scholar
[51]	Han F, Yue J, Fan X, Gao T, Luo C, Ma Z, Suo L, Wang C 2016 Nano Lett. 16 4521 Google Scholar
[52]	Ohzuku T 1995 J. Electrochem. Soc. 142 1431 Google Scholar
[53]	Nonemacher J F, Hüter C, Zheng H, Malzbender J, Krüger M, Spatschek R, Finsterbusch M 2018 Solid State Ionics 321 126 Google Scholar
[54]	Sharafi A, Haslam C G, Kerns R D, Wolfenstine J, Sakamoto J 2017 J. Mater. Chem. A 5 21491 Google Scholar
[55]	Li Y, Chen X, Dolocan A, Cui Z, Xin S, Xue L, Xu H, Park K, Goodenough J B 2018 J. Am. Chem. Soc. 140 6448 Google Scholar
[56]	Dai J, Yang C, Wang C, Pastel G, Hu L 2018 Adv. Mater. 30 1802068 Google Scholar
[57]	Sun H H, Ryu H H, Kim U H, Weeks J A, Heller A, Sun Y K, Mullins C B 2020 ACS Energy Lett. 5 1136 Google Scholar
[58]	Park K J, Hwang J Y, Ryu H H, Maglia F, Kim S J, Lamp P, Yoon C S, Sun Y K 2019 ACS Energy Lett. 4 1394 Google Scholar
[59]	Zhou H, Xin F, Pei B, Whittingham M S 2019 ACS Energy Lett. 4 1902 Google Scholar
[60]	Park K J, Jung H G, Kuo L Y, Kaghazchi P, Yoon C S, Sun Y K 2018 Adv. Energy Mater. 8 1801202 Google Scholar
[61]	Ryu H H, Park K J, Yoon D R, Aishova A, Yoon C S, Sun Y K 2019 Adv. Energy Mater. 9 1902698 Google Scholar
[62]	Kim H, Lee E J, Sun Y K 2014 Mater. Today 17 285 Google Scholar
[63]	Smith S, Thompson T, Sakamoto J, Allen J L, Baker D R, Wolfenstine J 2017 Solid State Ionics 300 38 Google Scholar
[64]	Dixit M B, Zaman W, Bootwala Y, Zheng Y, Hatzell M C, Hatzell K B 2019 ACS Appl. Mater. Interfaces 11 45087 Google Scholar
[65]	Troy S, Schreiber A, Reppert T, Gehrke H G, Finsterbusch M, Uhlenbruck S, Stenzel P 2016 Appl. Energy 169 757 Google Scholar
[66]	Sakuda A, Hayashi A, Tatsumisago M 2013 Sci. Rep. 3 2261 Google Scholar
[67]	Kato A, Yamamoto M, Sakuda A, Hayashi A, Tatsumisago M 2018 ACS Appl. Energy Mater. 1 1002 Google Scholar
[68]	Aidoud D, Etiemble A, Guy Bouyssou D, Maire E, Le Bideau J, Guyomard D, Lestriez B 2016 J. Power Sources 330 92 Google Scholar
[69]	Weston J E, Steele B C H 1982 Solid State Ionics 7 75 Google Scholar
[70]	Arya A, Sharma A L 2020 J. Mater. Sci. 55 6242 Google Scholar
[71]	Jiang G, Maeda S, Yang H, Saito Y, Tanase S, Sakai T 2005 J. Power Sources 141 143 Google Scholar
[72]	Lee W, Lyon C K, Seo J H, Lopez-Hallman R, Leng Y, Wang C Y, Hickner M A, Randall C A, Gomez E D 2019 Adv. Funct. Mater. 29 1807872 Google Scholar
[73]	Li S, Zhang S Q, Shen L, Liu Q, Ma J B, Lv W, He Y B, Yang Q H 2020 Adv. Sci. 7 1903088 Google Scholar
[74]	Hu X, Yan G, Cheng X, Malzbender J, Qiang W, Huang B 2019 J. Am. Ceram. Soc. 102 1953
[75]	Hu X, Cheng X, Qin S, Yan G, Malzbender J, Qiang W, Huang B 2018 Ceram. Int. 44 1902 Google Scholar
[76]	Ishidzu K, Oka Y, Nakamura T 2016 Solid State Ionics 288 176 Google Scholar
[77]	Kalluri S, Yoon M, Jo M, Park S, Myeong S, Kim J, Dou S X, Guo Z, Cho J 2017 Adv. Energy Mater. 7 1601507 Google Scholar
[78]	Xu X, Huo H, Jian J, Wang L, Zhu H, Xu S, He X, Yin G, Du C, Sun X 2019 Adv. Energy Mater. 9 1803963 Google Scholar
[79]	Zhang C, Xu S, Han B, Lin G, Huang Q, Ivey D G, Yang C, Wang P, Wei W 2019 J. Power Sources 431 40 Google Scholar
[80]	Wu B, Wang S, Evans Iv W J, Deng D Z, Yang J, Xiao J 2016 J. Mater. Chem. A 4 15266 Google Scholar
[81]	Li H, Liu A, Zhang N, Wang Y, Yin S, Wu H, Dahn J R 2019 Chem. Mater. 31 7574 Google Scholar
[82]	Cheng X B, Zhang R, Zhao C Z, Wei F, Zhang J G, Zhang Q 2016 Adv. Sci. 3 1500213 Google Scholar
[83]	Waetzig K, Rost A, Langklotz U, Matthey B, Schilm J 2016 J. Eur. Ceram. Soc. 36 1995 Google Scholar
[84]	Bucci G, Swamy T, Chiang Y M, Carter W C 2017 J. Mater. Chem. A 5 19422 Google Scholar
[85]	Koerver R, Aygün I, Leichtweiß T, Dietrich C, Zhang W, Binder J O, Hartmann P, Zeier W G, Janek J 2017 Chem. Mater. 29 5574 Google Scholar
[86]	Xiao Y, Wang Y, Bo S H, Kim J C, Miara L J, Ceder G 2019 Nat. Rev. Mater. 5 105
[87]	Kuang Y, Chen C, Kirsch D, Hu L 2019 Adv. Energy Mater. 9 1901457 Google Scholar
[88]	Devaux D, Harry K J, Parkinson D Y, Yuan R, Hallinan D T, MacDowell A A, Balsara N P 2015 J. Electrochem. Soc. 162 A1301 Google Scholar
[89]	Liu T, Zhang Y, Chen R, Zhao S X, Lin Y, Nan C W, Shen Y 2017 Electrochem. Commun. 79 1 Google Scholar
[90]	Huang W, Zhao N, Bi Z, Shi C, Guo X, Fan L, Nan C 2020 Mater. Today Nano 10 100075 Google Scholar
[91]	Dixit M B, Zaman W, Hortance N, Vujic S, Harkey B, Shen F, Tsai W Y, De Andrade V, Chen X C, Balke N, Hatzell K B 2020 Joule 4 207 Google Scholar
[92]	Zhao N, Fang R, He M H, Chen C, Li Y Q, Bi Z J, Guo X X 2018 Rare Met. 37 473 Google Scholar
[93]	Sakamoto J 2019 Nat. Energy 4 827 Google Scholar
[94]	Kim S H, Kim K, Choi H, Im D, Heo S, Choi H S 2019 J. Mater. Chem. A 7 13650 Google Scholar
[95]	Cheng X B, Zhang R, Zhao C Z, Zhang Q 2017 Chem. Rev. 117 10403 Google Scholar
[96]	Xia S, Wu X, Zhang Z, Cui Y, Liu W 2019 Chem. 5 753 Google Scholar
[97]	Khurana R, Schaefer J L, Archer L A, Coates G W 2014 J. Am. Chem. Soc. 136 7395 Google Scholar
[98]	Hatzell K B, Chen X C, Cobb C L, Dasgupta N P, Dixit M B, Marbella L E, McDowell M T, Mukherjee P P, Verma A, Viswanathan V, Westover A S, Zeier W G 2020 ACS Energy Lett. 5 922 Google Scholar
[99]	Liu H, Cheng X B, Huang J Q, Yuan H, Lu Y, Yan C, Zhu G L, Xu R, Zhao C Z, Hou L P, He C, Kaskel S, Zhang Q 2020 ACS Energy Lett. 5 833 Google Scholar
[100]	Ishiguro K, Nemori H, Sunahiro S, Nakata Y, Sudo R, Matsui M, Takeda Y, Yamamoto O, Imanishi N 2014 J. Electrochem. Soc. 161 A668 Google Scholar
[101]	Zhang X, Wang A, Liu X, Luo J 2019 Acc. Chem. Res. 52 3223 Google Scholar
[102]	Kasemchainan J, Zekoll S, Spencer Jolly D, Ning Z, Hartley G O, Marrow J, Bruce P G 2019 Nat. Mater. 18 1105 Google Scholar
[103]	Doux J M, Nguyen H, Tan D H S, Banerjee A, Wang X, Wu E A, Jo C, Yang H, Meng Y S 2019 Adv. Energy Mater. 10 1903253
[104]	Yan P, Zheng J, Liu J, Wang B, Cheng X, Zhang Y, Sun X, Wang C, Zhang J G 2018 Nat. Energy 3 600 Google Scholar
[105]	Jung S H, Kim U H, Kim J H, Jun S, Yoon C S, Jung Y S, Sun Y K 2019 Adv. Energy Mater. 10 1903360
[106]	Liu Y, Harlow J, Dahn J 2020 J. Electrochem. Soc. 167 020512 Google Scholar
[107]	Lee H, Oh P, Kim J, Cha H, Chae S, Lee S, Cho J 2019 Adv. Mater. 31 1900376 Google Scholar
[108]	Zeng H, Ji X, Tsai F, Zhang Q, Jiang T, Li R K Y, Shi H, Luan S, Shi D 2018 Solid State Ionics 320 92 Google Scholar
[109]	Ohta N, Takada K, Sakaguchi I, Zhang L, Ma R, Fukuda K, Osada M, Sasaki T 2007 Electrochem. Commun. 9 1486 Google Scholar
[110]	Bi Z, Zhao N, Ma L, Fu Z, Xu F, Wang C, Guo X 2020 Chem. Eng. J. 387 124089 Google Scholar
[111]	Bi Z, Zhao N, Ma L, Shi C, Fu Z, Xu F, Guo X 2020 J. Mater. Chem. A 8 4252 Google Scholar
[112]	Zhang X D, Shi J L, Liang J Y, Wang L P, Yin Y X, Jiang K C, Guo Y G 2019 J. Power Sources 426 242 Google Scholar
[113]	Yubuchi S, Ito Y, Matsuyama T, Hayashi A, Tatsumisago M 2016 Solid State Ionics 285 79 Google Scholar
[114]	Ito Y, Otoyama M, Hayashi A, Ohtomo T, Tatsumisago M 2017 J. Power Sources 360 328 Google Scholar
[115]	Koerver R, Zhang W, de Biasi L, Schweidler S, Kondrakov A O, Kolling S, Brezesinski T, Hartmann P, Zeier W G, Janek J 2018 Energy Environ. Sci. 11 2142 Google Scholar
[116]	Sakuda A, Hayashi A, Tatsumisago M 2013 Scientific Reports 3 2261
[117]	Shi T, Tu Q, Tian Y, Xiao Y, Miara L J, Kononova O, Ceder G 2019 Adv. Energy Mater. 10 1902881
[118]	Park K, Yu B C, Jung J W, Li Y, Zhou W, Gao H, Son S, Goodenough J B 2016 Chem. Mater. 28 8051 Google Scholar
[119]	Li Y, Wang Z, Li C, Cao Y, Guo X 2014 J. Power Sources 248 642 Google Scholar
[120]	Han F, Yue J, Chen C, Zhao N, Fan X, Ma Z, Gao T, Wang F, Guo X, Wang C 2018 Joule 2 497 Google Scholar
[121]	Liu Y, Sun Q, Wang D, Adair K, Liang J, Sun X 2018 J. Power Sources 393 193 Google Scholar
[122]	Guo J, Berbano S S, Guo H, Baker A L, Lanagan M T, Randall C A 2016 Adv. Funct. Mater. 26 7115 Google Scholar
[123]	Sun C, Liu J, Gong Y, Wilkinson D P, Zhang J 2017 Nano Energy 33 363 Google Scholar
[124]	Wang X, Zhang Y, Zhang X, Liu T, Lin Y H, Li L, Shen Y, Nan C W 2018 ACS Appl. Mater. Interfaces 10 24791 Google Scholar
[125]	Pervez S A, Ganjeh Anzabi P, Farooq U, Trifkovic M, Roberts E P L, Thangadurai V 2019 Adv. Mater. Interfaces 6 1900186
[126]	Huo H, Sun J, chen C, Meng X, He M, Zhao N, Guo X 2018 J. Power Sources 383 150 Google Scholar
[127]	Liu S, Imanishi N, Zhang T, Hirano A, Takeda Y, Yamamoto O, Yang J 2010 J. Power Sources 195 6847 Google Scholar
[128]	Gai J, Ma F, Zhang Z, Sun D, Jin Y, Guo Y, Kim W 2019 ACS Sustainable Chem. Eng. 7 15896 Google Scholar
[129]	Zhou W, Wang S, Li Y, Xin S, Manthiram A, Goodenough J B 2016 J. Am. Chem. Soc. 138 9385 Google Scholar
[130]	Huo H, Chen Y, Luo J, Yang X, Guo X, Sun X 2019 Adv. Energy Mater. 9 1804004 Google Scholar
[131]	Duan H, Fan M, Chen W P, Li J Y, Wang P F, Wang W P, Shi J L, Yin Y X, Wan L J, Guo Y G 2019 Adv. Mater. 31 1807789 Google Scholar
[132]	Stone G M, Mullin S A, Teran A A, Hallinan D T, Minor A M, Hexemer A, Balsara N P 2012 J. Electrochem. Soc. 159 A222
[133]	Xu B, Li W, Duan H, Wang H, Guo Y, Li H, Liu H 2017 J. Power Sources 354 68 Google Scholar
[134]	Choudhury S, Vu D, Warren A, Tikekar M D, Tu Z, Archer L A 2018 Proc. Natl. Acad. Sci. 115 6620 Google Scholar

[1]	Xu Ji-Yuan, Zhang Jia-Teng, Meng Rui-Yang, Chen Hong-Sheng, Fang Yi-Kun, Dong Sheng-Zhi, Li Wei. Study on temperature stability and mechanical properties of sintered Nd_25.5Dy_6.5Co₁₃(Fe, M)_balB_0.98 magnet. Acta Physica Sinica, 2023, 72(7): 077502. doi: 10.7498/aps.72.20222045
[2]	Chen Jing-Jing, Qiu Xiao-Lin, Li Ke, Zhou Dan, Yuan Jun-Jun. Mechanical performance analysis of nanocrystalline CoNiCrFeMn high entropy alloy: atomic simulation method. Acta Physica Sinica, 2022, 71(19): 199601. doi: 10.7498/aps.71.20220733
[3]	Xin Yong, Bao Hong-Wei, Sun Zhi-Peng, Zhang Ji-Bin, Liu Shi-Chao, Guo Zi-Xuan, Wang Hao-Yu, Ma Fei, Li Yuan-Ming. Effects of Th doping on mechanical properties of U_1–_xTh_xO₂: An atomistic simulation. Acta Physica Sinica, 2021, 70(12): 122801. doi: 10.7498/aps.70.20202239
[4]	Li Xing-Xin, Li Si-Ping. Manipulations on mechanical properties of multilayer folded graphene by annealing temperature: a molecular dynamics simulation study. Acta Physica Sinica, 2020, 69(19): 196102. doi: 10.7498/aps.69.20200836
[5]	Li Jie-Jie, Lu Bin-Bin, Xian Yue-Hui, Hu Guo-Ming, Xia Re. Characterization of nanoporous silver mechanical properties by molecular dynamics simulation. Acta Physica Sinica, 2018, 67(5): 056101. doi: 10.7498/aps.67.20172193
[6]	Deng Shi-Jie, Zhao Yu-Hong, Hou Hua, Wen Zhi-Qin, Han Pei-De. Structural, mechanical and thermodynamic properties of Ti2AlX (X= C, N) at high pressure. Acta Physica Sinica, 2017, 66(14): 146101. doi: 10.7498/aps.66.146101
[7]	Chen Zhi-Peng, Ma Ya-Nan, Lin Xue-Ling, Pan Feng-Chun, Xi Li-Ying, Ma Zhi, Zheng Fu, Wang Yan-Qing, Chen Huan-Ming. Electronic structure and mechanical properties of Nb-doped -TiAl intermetallic compound. Acta Physica Sinica, 2017, 66(19): 196101. doi: 10.7498/aps.66.196101
[8]	Li Ming-Lin, Wan Ya-Ling, Hu Jian-Yue, Wang Wei-Dong. Molecular dynamics simulation of effects of temperature and chirality on the mechanical properties of single-layer molybdenum disulfide. Acta Physica Sinica, 2016, 65(17): 176201. doi: 10.7498/aps.65.176201
[9]	Wang Hai-Yan, Hu Qian-Ku, Yang Wen-Peng, Li Xu-Sheng. Influence of metal element doping on the mechanical properties of TiAl alloy. Acta Physica Sinica, 2016, 65(7): 077101. doi: 10.7498/aps.65.077101
[10]	Ma Bing-Yang, Zhang An-Ming, Shang Hai-Long, Sun Shi-Yang, Li Ge-Yang. Amorphizing and mechanical properties of co-sputtered Al-Zr alloy films. Acta Physica Sinica, 2014, 63(13): 136801. doi: 10.7498/aps.63.136801
[11]	Yang Duo, Zhong Ning, Shang Hai-Long, Sun Shi-Yang, Li Ge-Yang. Microstructures and mechanical properties of (Ti, N)/Al nanocomposite films by magnetron sputtering. Acta Physica Sinica, 2013, 62(3): 036801. doi: 10.7498/aps.62.036801
[12]	Yu Li-Hua, Ma Bing-Yang, Cao Jun, Xu Jun-Hua. Structures, mechanical and tribological properties of (Zr,V)N composite films. Acta Physica Sinica, 2013, 62(7): 076202. doi: 10.7498/aps.62.076202
[13]	Li Lan-Kai, Wang Hou-Sheng, Ni Zhi-Peng, Cheng Jun-Sheng, Wang Qiu-Liang. Mechanical stress in superconducting coils during winding process. Acta Physica Sinica, 2013, 62(5): 058403. doi: 10.7498/aps.62.058403
[14]	Wang Ying, Lu Tie-Cheng, Wang Yue-Zhong, Yue Shun-Li, Qi Jian-Qi, Pan Lei. Investigation of the electronic and mechanical properties of Al2O3-AlN solid solution by virtual crystal approximation. Acta Physica Sinica, 2012, 61(16): 167101. doi: 10.7498/aps.61.167101
[15]	Luo Qing-Hong, Lu Yong-Hao, Lou Yan-Zhi. Microstructure and mechanical properties of Ti-B-C-N nanocomposite coatings. Acta Physica Sinica, 2011, 60(8): 086802. doi: 10.7498/aps.60.086802
[16]	Luo Qing-Hong, Lou Yan-Zhi, Zhao Zhen-Ye, Yang Hui-Sheng. Effect of annealing on microstructure and mechanical propertiesof AlTiN multilayer coatings. Acta Physica Sinica, 2011, 60(6): 066201. doi: 10.7498/aps.60.066201
[17]	Yu Wei-Yang, Tang Bi-Yu, Peng Li-Ming, Ding Wen-Jiang. Electronic structure and mechanical properties of α-Mg3Sb2. Acta Physica Sinica, 2009, 58(13): 216-S223. doi: 10.7498/aps.58.216
[18]	Wang Li-Qun, Wang Ming-Xia, Li De-Jun, Yang Jin, Yu Da-Shu, Su Jie. Effect of N2 partial pressure on the defect properties and mechanical behaviors of nanoscale ZrN/WN multilayers. Acta Physica Sinica, 2007, 56(6): 3435-3439. doi: 10.7498/aps.56.3435
[19]	Zhai Qiu-Ya, Yang Yang, Xu Jin-Feng, Guo Xue-Feng. Electrical resistivity and mechanical properties of rapidly solidified Cu-Sn hypoperitectic alloys. Acta Physica Sinica, 2007, 56(10): 6118-6123. doi: 10.7498/aps.56.6118
[20]	Wei Lun, Mei Fang-Hua, Shao Nan, Dong Yun-Shan, Li Ge-Yang. The coherent growth and mechanical properties of non-isostructural TiN/TiB2 nanomultilayers. Acta Physica Sinica, 2005, 54(10): 4846-4851. doi: 10.7498/aps.54.4846

Catalog

Vol. 69, Issue 22 - 2020-11-20

Metrics

Abstract views: 10803
PDF Downloads: 647
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板