Bi-Pb-Sr-Ca-Cu-O系反应过程研究

奚正平 周廉 冀春霖

引用本文:
Citation:

Bi-Pb-Sr-Ca-Cu-O系反应过程研究

奚正平, 周廉, 冀春霖

REACTION PROCESS IN THE Bi-Pb-Sr-Ca-Cu-O SYSTEM

XI ZHENG-PING, ZHOU LIAN, JI CHUN-LIN
PDF
导出引用
  • 采用高温X射线和DTA技术研究了三步反应法合成Bi-Pb-Sr-Ca-Cu-O超导体的反应过程。实验结果表明样品在740℃能形成2212相,在825℃形成2223相.2212相在875℃左右异分熔化成2201相和液相,2223相在935℃左右同分熔化。2212相在晶化过程中容易形成强的c轴取向。
    The reaction process of formation of the Bi-Pb-Sr-Ca-Cu-O superconductor by means of a three-step reaction method was studied by high-temperature X-ray diffraction meansurement and DTA technique. The 2212 phase began to form at about 740℃ from the mixture of the Bi-Pb-Sr-Ca-O precursor-CuO, and the 2223 phase at about 825℃. The 2212 phase melted incongruently to the 2201 phase and a liquid phase at about 875℃ and the 2223 phase melted a liquid phase at about 935℃. In the crystallization of the 2212 phase, strong c-orientation forms easily.
    • 基金项目: 国家超导技术联合研究开发中心的资助
计量
  • 文章访问数:  3436
  • PDF下载量:  435
  • 被引次数: 0
出版历程
  • 收稿日期:  1990-04-04
  • 刊出日期:  2005-06-28

Bi-Pb-Sr-Ca-Cu-O系反应过程研究

  • 1. (1)东北工学院,沈阳,110006; (2)西北有色金属研究院,宝鸡,721014
    基金项目: 

    国家超导技术联合研究开发中心的资助

摘要: 采用高温X射线和DTA技术研究了三步反应法合成Bi-Pb-Sr-Ca-Cu-O超导体的反应过程。实验结果表明样品在740℃能形成2212相,在825℃形成2223相.2212相在875℃左右异分熔化成2201相和液相,2223相在935℃左右同分熔化。2212相在晶化过程中容易形成强的c轴取向。

English Abstract