In替代(La2/3Ca1/3)(Mn(3-2x)/3In2x/3)O3体系巨磁电阻效应的研究

徐明祥 焦正宽

引用本文:
Citation:

In替代(La2/3Ca1/3)(Mn(3-2x)/3In2x/3)O3体系巨磁电阻效应的研究

徐明祥, 焦正宽

STUDY OF GIANT MAGNETORESISTANCE IN THE In-SUBSTITUTED (La2/3Ca1/3)(Mn(3-2x)/3In2x/3)O3 SYSTEM

XU MING-XIANG, JIAO ZHENG-KUAN
PDF
导出引用
  • 采用固态反应法制备了In替代的(La2/3Ca1/3)(Mn(3-2x)/3In2x/3)O3(x=0.00,0.10,0.15)体系.通过测量其零场和1.6T磁场下样品的电阻-温度关系以及一定温度下磁电阻率与磁场的关系.发现随In3+替代量的增加其磁电阻峰和电阻峰均向低温方向移动,同时巨磁电阻效应减弱,磁电阻峰也展宽.这是由于In3+替代量的变化,引起
    The In-substituted system,(La2/3Ca1/3)(Mn(3-2x)/3In2x/3)O3(x=0.00,0.10,0.15),was synthesized by solid-state reaction method.Its temperature dependence of electrical resistance and magnetoresistance (H=0,1.6T) and field dependence of magnetoresistance were measured by the four-probe method.It was found that when x increases,both the peak of the electrical resistivity and the peak of magnetoresistance move to lower temperatures.However,the cusp is broadened by In-substitution.The authors suggested that the variation of the proportion of In3+ ions leads to the change of manganese valence and the magnetic moments,as well as magnetic structure of the (La2/3Ca1/3)(Mn(3-2x)/3In2x/3)O3 system.Such phenomena weaken the ferromagnetic double exchange effect.
    • 基金项目: 浙江省自然科学基金资助的课题.
计量
  • 文章访问数:  3481
  • PDF下载量:  457
  • 被引次数: 0
出版历程
  • 收稿日期:  1997-10-05
  • 修回日期:  1997-12-01
  • 刊出日期:  1998-03-05

In替代(La2/3Ca1/3)(Mn(3-2x)/3In2x/3)O3体系巨磁电阻效应的研究

  • 1. 浙江大学物理系,杭州 310027
    基金项目: 

    浙江省自然科学基金资助的课题.

摘要: 采用固态反应法制备了In替代的(La2/3Ca1/3)(Mn(3-2x)/3In2x/3)O3(x=0.00,0.10,0.15)体系.通过测量其零场和1.6T磁场下样品的电阻-温度关系以及一定温度下磁电阻率与磁场的关系.发现随In3+替代量的增加其磁电阻峰和电阻峰均向低温方向移动,同时巨磁电阻效应减弱,磁电阻峰也展宽.这是由于In3+替代量的变化,引起