N i50.5Mn24Ga25.5取向晶体相变应变性能的研究

梁 婷 蒋成保 徐惠彬

引用本文:
Citation:

N i50.5Mn24Ga25.5取向晶体相变应变性能的研究

梁 婷, 蒋成保, 徐惠彬

The property of transformation strain in the texturedNi50550.5Mn 2424Ga25525.5 alloy

Liang Ting, Jiang Cheng-Bao, Xu Hui-Bin
PDF
导出引用
  • 采用区熔法制备了Ni50550.5Mn2424Ga25525.5取向晶体,在底部、中部和顶部各切取一块样品进行相变应变测试.在中部样品中获得了高达14%的相变应变,应变随加热冷却循环次数的增加而逐步降低,第9次和第10次相变时应变为08%.在底部和顶部样品中,降温过程的应变随温度的变化呈现先收缩后膨胀或先膨胀后收缩的现象,我们认为这是由于样品中高度择优取向的马氏体变体竞争的结果所致.
    A large strain of 14% during the martensitic transformation has been observed in the textured Ni50550.5Mn2424Ga25525 .5 polycrystal prepared by vertical zone melting unidirectional solidification. This martensitic transformation strain decreases to 08% at the ninth and tenth thermal cycles. Expansion and shrinkage phenomenon during the martensitic transformation has been obtained, indicating the existence of a preferential orientation of martensitic variants.
    • 基金项目: 国家自然科学基金(批准号:50131010,50271002)资助的课题.
计量
  • 文章访问数:  3635
  • PDF下载量:  604
  • 被引次数: 0
出版历程
  • 收稿日期:  2004-07-23
  • 修回日期:  2004-12-13
  • 刊出日期:  2005-02-05

N i50.5Mn24Ga25.5取向晶体相变应变性能的研究

  • 1. (1)北京航空航天大学材料科学与工程学院,北京 100083; (2)北京航空航天大学材料科学与工程学院,北京 100083;中国人民解放军防化指挥工程学院装备系,北京 102205
    基金项目: 

    国家自然科学基金(批准号:50131010,50271002)资助的课题.

摘要: 采用区熔法制备了Ni50550.5Mn2424Ga25525.5取向晶体,在底部、中部和顶部各切取一块样品进行相变应变测试.在中部样品中获得了高达14%的相变应变,应变随加热冷却循环次数的增加而逐步降低,第9次和第10次相变时应变为08%.在底部和顶部样品中,降温过程的应变随温度的变化呈现先收缩后膨胀或先膨胀后收缩的现象,我们认为这是由于样品中高度择优取向的马氏体变体竞争的结果所致.