交换弹簧磁性多层膜的磁矩取向及磁滞回线的解析研究

邓娅 赵国平 薄鸟

引用本文:
Citation:

交换弹簧磁性多层膜的磁矩取向及磁滞回线的解析研究

邓娅, 赵国平, 薄鸟

The analytical investigation of the magnetic orientation and hysteresis loop in exchange-spring magnetic multilayers

Deng Ya, Zhao Guo-Ping, Bo Niao
PDF
导出引用
  • 本文以界面交换耦合常数Ji和软磁相厚度Ls为主要参变量,研究了易轴与膜面平行情况下的Nd2Fe14B/α-Fe磁性多层膜的磁矩随外场变化的取向及磁滞回线,并得到了成核场的解析公式.分析发现,Ji对磁矩取向、钉扎场和矫顽力机理有着较大的影响.当Ls较小时,钉扎场等于成核场,随着Ji的减小
    Using the interface coupling constant Ji and the soft layer thickness Ls as the main variables, the changes of the magnetic moments with the applied field and the hysteresis loops of Nd2Fe14B/α-Fe trilayers, whose easy axes of all layers lie in the film plane, have been investigated. Analysis shows that Ji has significant influence on the magnetic orientation, the pinning field HP and the coercivity mechanism. When Ls is small, HP equals to HN, where the coercivity mechanism transforms from nucleation to pinning as Ji decreases, whereas for large Ls this trend is reversed. The critical thickness, at which the nucleation field and pinning field detaches, decreases as Ji decreases. When the reduced exchange coupling is considered, the rigid composite magnet appears only when Ls is very small. The reduced exchange coupling leads to a sudden change of angle of magnetization at the interface, which results in the change of the behavior of the trilayers from the single-phase one to the two-phase one and in the decrease of HN, whereas HP increases when Ls is larger.
    • 基金项目: 国家自然科学基金(批准号: 10747007)和教育部留学归国人员启动基金资助的课题.
    [1]

    Kneller E F, Hawig R 1991 IEEE Trans. Magn. 27 3588

    [2]

    Skomski R, Coey J M D 1993 Phys. Rev. B 48 15812

    [3]

    Feng C, Zhan Q, Li B H, Teng J, Li M H, Jiang Y, Yu G H 2009 Acta Phys. Sin. 58 3503 (in Chinese) [冯 春、詹 倩、李宝河、滕 蛟、李明华、姜 勇、于广华 2009 物理学报 58 3503]

    [4]

    Liu W, Zhang Z D, Liu J P, Chen L J, He L L, Liu Y, Sun X K, Sellmyer D J 2002 Adv. Mater. 14 1832

    [5]

    Xin H L, Yuan W Z, Cheng J K, Lin H, Ruan J Z, Zhao Z J 2007 Acta Phys. Sin. 56 4152 (in Chinese) [辛宏梁、袁望治、程金科、林 宏、阮建中、赵振杰 2007 物理学报 56 4152]

    [6]

    Ao Q, Zhang W L, Zhang Y, Wu J S 2005 Acta Phys. Sin. 54 4889 (in Chinese) [敖 琪、张瓦利、张 熠、吴建生 2005 物理学报 54 4889]

    [7]

    Yan S S, Liu W J, Weston J L, Zangari G, Barnard J A 2001 Phys. Rev. B 63 174415

    [8]

    Yan S S, Elkawni M, Li D S, Garmestani H, Liu J P, Weston J L, Zangari G 2003 J. Appl. Phys. 94 4535

    [9]

    Wang S G, Ward R C C, Du G X, Han X F, Wang C, Kohn A 2008 Phys. Rev. B 78 18041(R)

    [10]

    Wang S G, Wang C, Kohn A, Lee S, Goff J P, Singh L J, Barber Z H, Ward R C C 2007 J. Appl. Phys. 101 09D103

    [11]

    Zhao G P, Bo N, Zhang H W, Feng Y P, Deng Y 2010 J. Appl. Phys. 107 083907

    [12]

    Xian C W, Zhao G P, Zhang Q X, Xu J S 2009 Acta Phys. Sin. 58 631 (in Chinese) [鲜承伟、赵国平、张庆香、徐劲松 2009 物理学报 58 631]

    [13]

    Leineweber T, Kronmüller H 1997 J. Magn. Magn. Mater. 176 145

    [14]

    Zhao G P, Wang X L 2006 Phys. Rev. B 74 012409

    [15]

    Zhao G P, Zhao M G, Lim H S, Feng Y P, Ong C K 2005 Appl. Phy. Lett. 87 162513

    [16]

    Asti G, Solzi M, Ghidini M, Neri F M 2004 Phys. Rev. B 69 174401

    [17]

    Liu Q Z, Jiang J H, Sun F, Wu J S 2007 Physics 36 301 [刘琼珍、蒋建华、孙 锋、吴建生 2007 物理 36 301]

    [18]

    Guslienko K Yu, Chubykalo-Fesenko O, Mryasov O, Chantrell R, Weller D 2004 Phys. Rev. B 70 104405

    [19]

    Asti G, Ghidini M, Pellicelli R, Pernechele C, Solzi M 2006 Phys. Rev. B 73 094406

    [20]

    Amato M, Pini M G, Rettori 1999 Phys. Rev. B 60 3414

    [21]

    Gao R W, Feng W C, Wang B, Chen W, Han G B, Zhang P, Liu H Q, Li W, Guo Y Q, Li Y M 2003 Acta Phys. Sin. 52 0703 (in Chinese) [高汝伟、冯维存、王 标、陈 伟、韩广兵、张 鹏、刘汉强、李 卫、郭永权、李岫梅 2003 物理学报52 0703 ]

    [22]

    Han B, Gao R W, Fu S, Feng W C, Liu H Q, Chen W, Li W, and Guo Y Q 2005Appl. Phys. A 81 579

    [23]

    Yin J H, Takao S, Pan L Q 2008 Chin. Phys. B 17 3907

    [24]

    Zhang H W, Rong C B, Zhang S Y, Shen B G 2004 Acta Phys. Sin. 53 4347 (in Chinese) [张宏伟、荣传兵、张绍英、沈保根 2004 物理学报 53 4347]

    [25]

    Brown W F Jr 1945 Rev. Mod. Phys. 17 15

    [26]

    Stoner E C, Wohlfarth E P 1948 Phil. Trans. R. Soc. A 240 599

  • [1]

    Kneller E F, Hawig R 1991 IEEE Trans. Magn. 27 3588

    [2]

    Skomski R, Coey J M D 1993 Phys. Rev. B 48 15812

    [3]

    Feng C, Zhan Q, Li B H, Teng J, Li M H, Jiang Y, Yu G H 2009 Acta Phys. Sin. 58 3503 (in Chinese) [冯 春、詹 倩、李宝河、滕 蛟、李明华、姜 勇、于广华 2009 物理学报 58 3503]

    [4]

    Liu W, Zhang Z D, Liu J P, Chen L J, He L L, Liu Y, Sun X K, Sellmyer D J 2002 Adv. Mater. 14 1832

    [5]

    Xin H L, Yuan W Z, Cheng J K, Lin H, Ruan J Z, Zhao Z J 2007 Acta Phys. Sin. 56 4152 (in Chinese) [辛宏梁、袁望治、程金科、林 宏、阮建中、赵振杰 2007 物理学报 56 4152]

    [6]

    Ao Q, Zhang W L, Zhang Y, Wu J S 2005 Acta Phys. Sin. 54 4889 (in Chinese) [敖 琪、张瓦利、张 熠、吴建生 2005 物理学报 54 4889]

    [7]

    Yan S S, Liu W J, Weston J L, Zangari G, Barnard J A 2001 Phys. Rev. B 63 174415

    [8]

    Yan S S, Elkawni M, Li D S, Garmestani H, Liu J P, Weston J L, Zangari G 2003 J. Appl. Phys. 94 4535

    [9]

    Wang S G, Ward R C C, Du G X, Han X F, Wang C, Kohn A 2008 Phys. Rev. B 78 18041(R)

    [10]

    Wang S G, Wang C, Kohn A, Lee S, Goff J P, Singh L J, Barber Z H, Ward R C C 2007 J. Appl. Phys. 101 09D103

    [11]

    Zhao G P, Bo N, Zhang H W, Feng Y P, Deng Y 2010 J. Appl. Phys. 107 083907

    [12]

    Xian C W, Zhao G P, Zhang Q X, Xu J S 2009 Acta Phys. Sin. 58 631 (in Chinese) [鲜承伟、赵国平、张庆香、徐劲松 2009 物理学报 58 631]

    [13]

    Leineweber T, Kronmüller H 1997 J. Magn. Magn. Mater. 176 145

    [14]

    Zhao G P, Wang X L 2006 Phys. Rev. B 74 012409

    [15]

    Zhao G P, Zhao M G, Lim H S, Feng Y P, Ong C K 2005 Appl. Phy. Lett. 87 162513

    [16]

    Asti G, Solzi M, Ghidini M, Neri F M 2004 Phys. Rev. B 69 174401

    [17]

    Liu Q Z, Jiang J H, Sun F, Wu J S 2007 Physics 36 301 [刘琼珍、蒋建华、孙 锋、吴建生 2007 物理 36 301]

    [18]

    Guslienko K Yu, Chubykalo-Fesenko O, Mryasov O, Chantrell R, Weller D 2004 Phys. Rev. B 70 104405

    [19]

    Asti G, Ghidini M, Pellicelli R, Pernechele C, Solzi M 2006 Phys. Rev. B 73 094406

    [20]

    Amato M, Pini M G, Rettori 1999 Phys. Rev. B 60 3414

    [21]

    Gao R W, Feng W C, Wang B, Chen W, Han G B, Zhang P, Liu H Q, Li W, Guo Y Q, Li Y M 2003 Acta Phys. Sin. 52 0703 (in Chinese) [高汝伟、冯维存、王 标、陈 伟、韩广兵、张 鹏、刘汉强、李 卫、郭永权、李岫梅 2003 物理学报52 0703 ]

    [22]

    Han B, Gao R W, Fu S, Feng W C, Liu H Q, Chen W, Li W, and Guo Y Q 2005Appl. Phys. A 81 579

    [23]

    Yin J H, Takao S, Pan L Q 2008 Chin. Phys. B 17 3907

    [24]

    Zhang H W, Rong C B, Zhang S Y, Shen B G 2004 Acta Phys. Sin. 53 4347 (in Chinese) [张宏伟、荣传兵、张绍英、沈保根 2004 物理学报 53 4347]

    [25]

    Brown W F Jr 1945 Rev. Mod. Phys. 17 15

    [26]

    Stoner E C, Wohlfarth E P 1948 Phil. Trans. R. Soc. A 240 599

  • [1] 何鑫鑫, 赵倩. 界面原子扩散对SmCo/Fe交换弹簧双层膜磁性能影响的微磁学研究. 物理学报, 2021, 70(19): 197502. doi: 10.7498/aps.70.20210623
    [2] 李柱柏, 李赟, 秦渊, 张雪峰, 沈保根. 稀土永磁体及复合磁体反磁化过程和矫顽力. 物理学报, 2019, 68(17): 177501. doi: 10.7498/aps.68.20190364
    [3] 肖俊儒, 刘仲武, 楼华山, 詹慧雄. 利用Pr70Cu30晶界扩散改善烧结钕铁硼废料矫顽力的研究. 物理学报, 2018, 67(6): 067502. doi: 10.7498/aps.67.20172551
    [4] 陈传文, 项阳. 正交各向异性双层交换弹簧薄膜的磁矩分布. 物理学报, 2016, 65(12): 127502. doi: 10.7498/aps.65.127502
    [5] 李正华, 李翔. L10-FePt合金单层磁性薄膜的微磁学模拟. 物理学报, 2014, 63(16): 167504. doi: 10.7498/aps.63.167504
    [6] 侯志鹏, 苏峰, 王文全. 三元Co79Zr18Cr3合金中高矫顽力. 物理学报, 2014, 63(8): 087501. doi: 10.7498/aps.63.087501
    [7] 朱洁, 苏垣昌, 潘靖, 封国林. 高斯型非均匀应力对铁磁薄膜磁化性质的影响. 物理学报, 2013, 62(16): 167503. doi: 10.7498/aps.62.167503
    [8] 郭子政, 胡旭波. 应力对铁磁薄膜磁滞损耗和矫顽力的影响. 物理学报, 2013, 62(5): 057501. doi: 10.7498/aps.62.057501
    [9] 王光建, 蒋成保. Sm(CobalFe0.1Cu0.1Zr0.033)6.9高温永磁合金的矫顽力. 物理学报, 2012, 61(18): 187503. doi: 10.7498/aps.61.187503
    [10] 鲜承伟, 赵国平, 张庆香, 徐劲松. 垂直取向Nd2Fe14B/α-Fe磁性三层膜的磁化反转. 物理学报, 2009, 58(5): 3509-3514. doi: 10.7498/aps.58.3509
    [11] 邱学军, 张云鹏, 何正红, 白 浪, 刘国磊, 王 跃, 陈 鹏, 熊祖洪. 矫顽力可调的多孔硅基Fe膜. 物理学报, 2006, 55(11): 6101-6107. doi: 10.7498/aps.55.6101
    [12] 李 腾, 李 卫, 潘 伟, 李岫梅. Fe40—45Cr30—35Co20—25Mo0—4Zr0—2合金微观结构对矫顽力的影响. 物理学报, 2005, 54(9): 4389-4394. doi: 10.7498/aps.54.4389
    [13] 史慧刚, 司明苏, 薛德胜. 段化(A/B)m复合纳米线阵列的矫顽力机理. 物理学报, 2005, 54(7): 3402-3407. doi: 10.7498/aps.54.3402
    [14] 张翠玲, 郑瑞伦, 滕 蛟. NiFeNb种子层对坡莫合金磁滞回线的影响. 物理学报, 2005, 54(11): 5389-5394. doi: 10.7498/aps.54.5389
    [15] 翁臻臻, 冯 倩, 黄志高, 都有为. 混合磁性薄膜矫顽力及阶梯效应的微磁学及Monte Carlo研究. 物理学报, 2004, 53(9): 3177-3185. doi: 10.7498/aps.53.3177
    [16] 张晓渝, 陈亚杰. 磁性颗粒复合体磁渗流区矫顽力异常的研究. 物理学报, 2003, 52(8): 2052-2056. doi: 10.7498/aps.52.2052
    [17] 高汝伟, 冯维存, 王 标, 陈 伟, 韩广兵, 张 鹏, 刘汉强, 李 卫, 郭永权, 李岫梅. 纳米复合永磁材料的有效各向异性与矫顽力. 物理学报, 2003, 52(3): 703-707. doi: 10.7498/aps.52.703
    [18] 荣传兵, 张宏伟, 张 健, 张绍英, 沈保根. 纳米晶永磁中面缺陷对畴壁钉扎机理的研究. 物理学报, 2003, 52(3): 708-712. doi: 10.7498/aps.52.708
    [19] 张宏伟, 荣传兵, 张 健, 张绍英, 沈保根. 纳米晶永磁Pr2Fe14B微磁学有限元法的模拟计算研究. 物理学报, 2003, 52(3): 718-721. doi: 10.7498/aps.52.718
    [20] 姜宏伟, 李明华, 于广华, 朱逢吾, 郑鹉. Bi对自旋阀钉扎场的影响及机理. 物理学报, 2002, 51(6): 1366-1370. doi: 10.7498/aps.51.1366
计量
  • 文章访问数:  6077
  • PDF下载量:  735
  • 被引次数: 0
出版历程
  • 收稿日期:  2010-04-22
  • 修回日期:  2010-06-14
  • 刊出日期:  2011-03-15

交换弹簧磁性多层膜的磁矩取向及磁滞回线的解析研究

  • 1. 四川师范大学物理与电子工程学院,成都 610068
    基金项目: 国家自然科学基金(批准号: 10747007)和教育部留学归国人员启动基金资助的课题.

摘要: 本文以界面交换耦合常数Ji和软磁相厚度Ls为主要参变量,研究了易轴与膜面平行情况下的Nd2Fe14B/α-Fe磁性多层膜的磁矩随外场变化的取向及磁滞回线,并得到了成核场的解析公式.分析发现,Ji对磁矩取向、钉扎场和矫顽力机理有着较大的影响.当Ls较小时,钉扎场等于成核场,随着Ji的减小

English Abstract

参考文献 (26)

目录

    /

    返回文章
    返回