采用高温固相法合成了Ba3Tb(BO3)3和Ba3Tb(BO3)3 ∶Ce3+两种绿色荧光粉,并研究了材料的发光性质.Ba3Tb(BO3)3材料呈多峰发射,发射峰位于439,493,547,589和629 nm,分别对应Tb3+的5D
-
关键词:
- 白光LED /
- Ba3Tb(BO3)3 /
- Ce3+ /
- 发光特性
Two green emitting phosphors, Ba3Tb(BO3)3 and Ba3Tb(BO3)3 ∶Ce3+, are synthesized by the high temperature solid-state method, and their luminescent characteristics are investigated. Ba3Tb(BO3)3 phosphor shows several emission peaks located at 439, 493, 547, 589 and 629 nm separately. The emission peaks correspond to the 5D3→7F4 and 5D4→7FJ=6. 5, 4, 3 transitions of Tb3+, respectively, and the maximal peak is 547 nm. For the 547 nm emission, the excitation spectrum consists of several bands, and the maximal peak is located at 380 nm. The Ce3+-activated Ba3Tb(BO3)3 phosphor is studied, and the result shows that the emission spectrum distribution of Ba3Tb(BO3)3 ∶Ce3+ is the same as that of Ba3Tb(BO3)3 phosphor, however, its emission intensity is higher than that of Ba3Tb(BO3)3,which is attributed to the sensitizing action of Ce3+ on Tb3+ in Ba3Tb(BO3)3. For the 547 nm emission, the excitation spectrum of Ba3Tb(BO3)3 ∶Ce3+presents a broad band, differing from that of Ba3Tb(BO3)3 phosphor. The effect of H3BO3 on the emission intensity of Ba3Tb(BO3)3 ∶Ce3+ phosphor is investigated, and the results show that the emission intensity can reach a maximum for 15 wt% excessive H3BO3. All the results show that Ba3Tb(BO3)3 ∶Ce3+ is a green emitting phosphor for white LED.-
Keywords:
- white LED /
- Ba3Tb(BO3)3 /
- Ce3+ /
- luminescent characteristics
[1] Nakamura S, Fasol G 1996 The Blue Laser Diode (Springer Berlin) p1
[2] Setlur A A, Heward W J, Gao Y, Srivastava, A M, Chandran R G, Shankar M V 2006 Chemical Materials 18 3314
[3] Kuo C H, Sheu J K, Chang S J, Su Y K, Wu L W, Tsai J M, Liu C H, Wu P K 2003 Japanese Journal of Applied Physics Part 1 42 2284
[4] Wang Z J, Li P L, Wang Y, Yang Z P, Guo Q L 2009 Acta Physica Sinica 58 1257 (in Chinese) [王志军、李盼来、王 颖、杨志平、郭庆林 2009 物理学报 58 1257]
[5] Song Y H, Jia G, Yang M, Huang Y J, You H P, Zhang H J 2009 Appl. Phys. Lett. 94 091902-1
[6] Li P L, Wang Z J, Yang Z P, Guo Q L 2010 Journal of The Electrochemical Society 157 H504
[7] Ma M X, Zhu D C, Tu M J 2009 Acta Phys. Sin. 58 5826 (in Chinese) [马明星、朱达川、涂铭旌 2009 物理学报 58 5826]
[8] Yang Z P, Liu Y F, Wang L W Yu Q M, Xiong Z J, Xu X L 2007 Acta Phy. Sin. 56 546 (in Chinese) [杨志平、刘玉峰、王利伟、余泉茂、熊志军、徐小岭 2007 物理学报 56 546]
[9] Liao J S, Liu B, Lai H S 2009 Journal of Luminescence 129 668
[10] Zhang J C, Wang Y H, Zhang Z Y, Xie P, Li H H, Jiang Y P 2008 Chin. Phys. Lett. 25 1453
[11] Zhang Z, Wang J, Zhang M, Zhang Q, Su Q 2008 Appl. Phys. B 91 529
[12] Li P L, Pang L B, Wang Z J, Yang Z P, Guo Q L, Li X 2009 Journal of Alloys and Compounds 478 813
[13] Liao J S, Qiu B, Wen H R, Chen J L, You W X 2009 Marerials Research Bulletin 44 1863
[14] Liu X R, Wang X J, Wang Z K 1989 Phys. Rev. B 39 10633
[15] Meng Q Y, Chen B J, Xu W, Zhao X X, Yang Y M, Di W H, Wang X J 2009 Spectroscopy and Spectral Analysis 29 151 (in Chinese) [孟庆裕、陈宝玖、许 武、赵晓霞、杨艳民、狄卫华、王晓君 2009 光谱学与光谱分析 29 151]
[1] Nakamura S, Fasol G 1996 The Blue Laser Diode (Springer Berlin) p1
[2] Setlur A A, Heward W J, Gao Y, Srivastava, A M, Chandran R G, Shankar M V 2006 Chemical Materials 18 3314
[3] Kuo C H, Sheu J K, Chang S J, Su Y K, Wu L W, Tsai J M, Liu C H, Wu P K 2003 Japanese Journal of Applied Physics Part 1 42 2284
[4] Wang Z J, Li P L, Wang Y, Yang Z P, Guo Q L 2009 Acta Physica Sinica 58 1257 (in Chinese) [王志军、李盼来、王 颖、杨志平、郭庆林 2009 物理学报 58 1257]
[5] Song Y H, Jia G, Yang M, Huang Y J, You H P, Zhang H J 2009 Appl. Phys. Lett. 94 091902-1
[6] Li P L, Wang Z J, Yang Z P, Guo Q L 2010 Journal of The Electrochemical Society 157 H504
[7] Ma M X, Zhu D C, Tu M J 2009 Acta Phys. Sin. 58 5826 (in Chinese) [马明星、朱达川、涂铭旌 2009 物理学报 58 5826]
[8] Yang Z P, Liu Y F, Wang L W Yu Q M, Xiong Z J, Xu X L 2007 Acta Phy. Sin. 56 546 (in Chinese) [杨志平、刘玉峰、王利伟、余泉茂、熊志军、徐小岭 2007 物理学报 56 546]
[9] Liao J S, Liu B, Lai H S 2009 Journal of Luminescence 129 668
[10] Zhang J C, Wang Y H, Zhang Z Y, Xie P, Li H H, Jiang Y P 2008 Chin. Phys. Lett. 25 1453
[11] Zhang Z, Wang J, Zhang M, Zhang Q, Su Q 2008 Appl. Phys. B 91 529
[12] Li P L, Pang L B, Wang Z J, Yang Z P, Guo Q L, Li X 2009 Journal of Alloys and Compounds 478 813
[13] Liao J S, Qiu B, Wen H R, Chen J L, You W X 2009 Marerials Research Bulletin 44 1863
[14] Liu X R, Wang X J, Wang Z K 1989 Phys. Rev. B 39 10633
[15] Meng Q Y, Chen B J, Xu W, Zhao X X, Yang Y M, Di W H, Wang X J 2009 Spectroscopy and Spectral Analysis 29 151 (in Chinese) [孟庆裕、陈宝玖、许 武、赵晓霞、杨艳民、狄卫华、王晓君 2009 光谱学与光谱分析 29 151]
[1] 严涌飚, 李霜, 丁双双, 张冰雪, 孙浩, 鞠泉浩, 姚露. 基质 ${\text{VO}}_4^{3 - }$ 与掺杂离子Pr3+荧光强度比的新型高灵敏度光学测温研究. 物理学报, 2024, 73(9): 097801. doi: 10.7498/aps.73.20240012[2] 高小钦, 卓宁泽, 王海波, 崔一平, 张家雨. 半导体量子点在白光LED器件上的应用研究. 物理学报, 2015, 64(13): 137801. doi: 10.7498/aps.64.137801 [3] 熊晓波, 袁曦明, 刘金存, 宋江齐. Na2SrMg(PO4)2: Ce3+, Mn2+荧光粉的发光性质及其能量传递机理. 物理学报, 2015, 64(1): 017801. doi: 10.7498/aps.64.017801 [4] 周仁迪, 黄雪飞, 齐智坚, 黄维刚. Ca2Si（O4-xNx）：Eu2+绿色荧光粉的制备及其发光性能. 物理学报, 2014, 63(19): 197801. doi: 10.7498/aps.63.197801 [5] 余阳, 刘自军, 陈乔乔, 戴能利, 李进延, 杨旅云. Dy3+掺杂硼硅酸盐玻璃的发光特性. 物理学报, 2013, 62(1): 017804. doi: 10.7498/aps.62.017804 [6] 齐智坚, 黄维刚. 白光LED用Ca3Si3O9：Dy3+荧光粉的制备及其发光性能. 物理学报, 2013, 62(19): 197801. doi: 10.7498/aps.62.197801 [7] 杨帆, 潘尚可, 丁栋舟, 吴云涛, 任国浩. 中子探测晶体Li6Gd(BO3)3:Ce的光谱特性研究. 物理学报, 2011, 60(11): 113301. doi: 10.7498/aps.60.113301 [8] 曹仕秀, 韩涛, 涂铭旌. Eu2+掺杂浓度对Ca2MgSi2O7∶Eu2+荧光粉发光特性的影响. 物理学报, 2011, 60(12): 127802. doi: 10.7498/aps.60.127802 [9] 韩颖, 侯蓝田, 夏长明, 周桂耀, 侯峙云. 镱铝共掺石英玻璃的制备及其发光特性的研究. 物理学报, 2011, 60(5): 054212. doi: 10.7498/aps.60.054212 [10] 苗瑞霞, 张玉明, 汤晓燕, 张义门. 4H-SiC中基面位错发光特性研究. 物理学报, 2011, 60(3): 037808. doi: 10.7498/aps.60.037808 [11] 冯晓辉, 孟庆裕, 孙江亭, 吕树臣, 孙立男. Eu3+掺杂Gd2W2O9和Gd2(WO4)3纳米荧光粉发光性质研究. 物理学报, 2011, 60(3): 037806. doi: 10.7498/aps.60.037806 [12] 薛正群, 黄生荣, 张保平, 陈朝. GaN基白光发光二极管失效机理分析. 物理学报, 2010, 59(7): 5002-5009. doi: 10.7498/aps.59.5002 [13] 杨志平, 马欣, 赵盼盼, 宋兆丰. SrAl2B2O7:Dy3+材料的制备及其发光性能. 物理学报, 2010, 59(8): 5387-5391. doi: 10.7498/aps.59.5387 [14] 刘元红, 庄卫东, 高文贵, 胡运生, 何涛, 何华强. 硼酸对亚微米级Ca3Sc2Si3O12:Ce绿色荧光粉的制备及发光性能的影响. 物理学报, 2010, 59(11): 8200-8204. doi: 10.7498/aps.59.8200 [15] 马明星, 朱达川, 涂铭旌. Eu2+的掺杂浓度对BaAl2Si2O8：Eu2+荧光粉发光特性的影响. 物理学报, 2009, 58(8): 5826-5830. doi: 10.7498/aps.58.5826 [16] 马明星, 朱达川, 涂铭旌. H3BO3对BaAl2Si2O8：Eu2+蓝色荧光粉物相组成和发光特性的影响. 物理学报, 2009, 58(9): 6512-6517. doi: 10.7498/aps.58.6512 [17] 李盼来, 王志军, 王颖, 杨志平, 郭庆林, 李旭, 杨艳民, 傅广生. Ce3+在LiBaBO3中的发光特性及晶体学格位. 物理学报, 2009, 58(8): 5831-5835. doi: 10.7498/aps.58.5831 [18] 王志军, 李盼来, 王颖, 杨志平, 郭庆林. 白光LED用LiBaBO3:Eu2+材料发光特性研究. 物理学报, 2009, 58(2): 1257-1260. doi: 10.7498/aps.58.1257 [19] 王志军, 李盼来, 王 刚, 杨志平, 郭庆林. Ca2SiO4:Dy3+材料的制备及其发光特性. 物理学报, 2008, 57(7): 4575-4579. doi: 10.7498/aps.57.4575 [20] 刘小兵, 史向华, 廖太长, 任 鹏, 柳 玥, 柳 毅, 熊祖洪, 丁训民, 侯晓远. 声空化物理化学综合法制备发光多孔硅薄膜的微结构与发光特性. 物理学报, 2005, 54(1): 416-421. doi: 10.7498/aps.54.416 计量
- 文章访问数: 9109
- PDF下载量: 699
- 被引次数: 0
留言板
尊敬的读者、作者、审稿人, 关于本刊的投稿、审稿、编辑和出版的任何问题, 您可以本页添加留言。我们将尽快给您答复。谢谢您的支持!
| 姓名 | |
|---|---|
| 邮箱 | |
| 手机号码 | |
| 标题 | |
| |
下载: