热压法制备的碲酸盐玻璃微盘

胡博 吴越豪 郑雨璐 戴世勋

引用本文:
Citation:

热压法制备的碲酸盐玻璃微盘

胡博, 吴越豪, 郑雨璐, 戴世勋

Fabrication of tellurite glass microdisks with thermal pressing method

Hu Bo, Wu Yue-Hao, Zheng Yu-Lu, Dai Shi-Xun
PDF
HTML
导出引用
  • 提出一种热压法制备微盘激光器的工艺, 仅使用实验室常用电阻加热炉具即可制备出不同直径/厚度的微盘激光器. 选用TeO2-ZnO-Na2O碲酸盐玻璃为基质材料, 制备出直径分布在100—400 μm范围内、最小厚度可达8 μm、典型品质因数(Q值)约为105的微盘激光器. 对碲酸盐玻璃基质材料掺入稀土离子Nd3+和Tm3+, 通过光纤锥耦合法开展微盘的抽运耦合实验, 即可在耦合系统的输出光谱中获得明显的荧光回廊模式和激光模式. 以一颗直径为105.74 μm、厚度为10.4 μm的Nd3+掺杂微盘为例, 当抽运光功率提升至1.364 mW以上时, 即可在1.06 μm附近获得激光峰. 同样实验表明, 对Tm3+掺杂的微盘进行抽运耦合实验可获得1.9 μm附近的激光峰.
    In this work, we report a two-step thermal pressing method of fabricating microdisk lasers that are suitable for processing thermally stable glass materials, and we utilize a tellurite glass (TeO2-ZnO-Na2O) to demonstrate the feasibility of this method. Compared with the conventional microdisk fabricating methods that rely on a series of complicated procedures, such as lithography, etching, thermal reflow, and ion implantation, this thermal pressing method involves only two heating procedures and can be accomplished with simple laboratory resistive heating furnaces. In the first heating procedure, we crush bulk tellurite glass into powders and drop those powders through a vertical heating furnace. Glass powders are transformed into microspheres by surface tension in the furnace. In the second heating procedure, microspheres are placed between two flat/smooth surfaces and are thermally treated when being pressed with suitable weights. With this procedure, the “flattened” microspheres turn into the microdisks. In this work, we demonstrate that our fabricated tellurite glass microdisks possess diameters of 100-400 μm, thinnest thickness of ~ 8 μm, and typical quality-factor (Q-factor) of ~ 105. We also dope tellurite glass with active dopants such as Nd3+ and Tm3+ to fabricate the active microdisk resonators. We couple those active microdisk resonators with fiber tapers and demonstrate that with appropriate pump power, apparent fluorescence whispering gallery mode and laser mode can be obtained. Taking a 105.74-μm-diameter, 10.4-μm-thickness, and Nd3+-doped tellurite glass microdisk for example, we show that as the pump power increases above a threshold of 1.364 mW, a lasing peak near 1.06 μm can be obtained. We also show that lasing peaks near 1.9 μm can be obtained by coupling/pumping Tm3+ doped microdisks.
      通信作者: 吴越豪, wuyuehao@nbu.edu.cn
    • 基金项目: 国家自然科学青年基金(批准号: 61605094)、国家自然科学基金重点项目(批准号: 61435009)和宁波大学王宽诚幸福基金资助的课题
      Corresponding author: Wu Yue-Hao, wuyuehao@nbu.edu.cn
    • Funds: Project supported by the Young Scientists Fund of the National Natural Science Foundation of China (Grant No. 61605094), the Key Program of the National Natural Science Foundation of China (Grant No., 61435009), and the K. C. Wong Magna Fund in Ningbo University
    [1]

    Sandoghdar V, Treussart F, Hare J, Lefevre-Seguin V, Raimond J, Haroche S 1996 Phys. Rev. A 54 R1777Google Scholar

    [2]

    Murugan G S, Zervas M N, Panitchob Y, Wilkinson J S 2011 Opt. Lett. 36 73Google Scholar

    [3]

    黄衍堂, 彭隆祥, 庄世坚, 李强龙, 廖廷俤, 许灿华, 段亚凡 2017 物理学报 66 244208Google Scholar

    Huang Y T, Peng L X, Zhuang S J, Li Q L, Liao Y D, Xu C H, Duan Y F 2017 Acta Phys. Sin. 66 244208Google Scholar

    [4]

    Gorajoobi S B, Murugan G S, Zervas M N 2019 Opt. Express 27 25493Google Scholar

    [5]

    Qian K, Tang J, Guo H, Zhang W, Liu J H, Liu J, Xue C Y, Zhang W D 2016 Chin. Phys. B 25 114209Google Scholar

    [6]

    Vernooy D W, Ilchenko V S, Mabuchi H, Streed E W, Kimble H J 1998 Opt. Lett. 23 247Google Scholar

    [7]

    Sasagawa K, Yonezawa Z, Iwai R, Ohta J, Nunoshita M 2004 Appl. Phys. Lett. 85 4325Google Scholar

    [8]

    Peng X, Song F, Jiang S, Peyghambarian N, Kuwata-Gonokami M, Xu L 2003 Appl. Phys. Lett. 82 1497Google Scholar

    [9]

    Elliott G R, Hewak D W, Murugan G S, Wilkinson J S 2007 Opt. Express 15 17542Google Scholar

    [10]

    Li C, Dai S, Zhang Q, Shen X, Wang X, Zhang P, Lu L, Wu Y, Lv S 2015 Chin. Phys. B 24 044208Google Scholar

    [11]

    胡博, 吴越豪, 郑雨璐, 戴世勋 2019 物理学报 68 064209Google Scholar

    Hu B, Wu Y H, Zheng Y L, Dai S X 2019 Acta Phys. Sin. 68 064209Google Scholar

    [12]

    Yang K, Dai S X, Wu Y H, Nie Q H 2018 Chin. Phys. B 27 117701Google Scholar

    [13]

    Spillane S M, Kippenberg T J, Vahala K J, Goh K W, Wilcut E, Kimble H J 2005 Phys. Rev. A 71 013817Google Scholar

    [14]

    Kippenberg T J, Spillane S M, Vahala K J 2004 Appl. Phys. Lett. 85 6113Google Scholar

    [15]

    Wang T J, He J Y, Lee C A, Niu H 2012 Opt. Express 20 028119Google Scholar

    [16]

    Tulek A, Akbulut D, Bayindir M 2009 Appl. Phys. Lett. 94 203302Google Scholar

    [17]

    Polman A, Min B, Kalkman J, Kippenberg T J, Vahala K J 2004 Appl. Phys. Lett. 84 1037Google Scholar

    [18]

    Zou L X, Liu B W, Lv X M, Yang Y D, Xiao J L, Huang Y Z 2015 Appl. Phys. Lett. 106 191107Google Scholar

    [19]

    Yang Z, Wu Y, Yang K, Xu P, Zhang W, Dai S, Xu T 2017 Opt. Mat. 72 524Google Scholar

    [20]

    Li A Z, Zhang J Q, Zhang M, Li W H, Wang S B, Lewis E, Brambilla G, Wang P F 2018 Opt. Lett. 43 4325Google Scholar

    [21]

    Jiang S S, Guo C L, Che K J, Luo Z Q, Du T J, Fu H Y, Xu H Y, Cai Z P 2019 Photon. Res. 7 566Google Scholar

  • 图 1  实验制备的一批典型的碲酸盐玻璃微球(内插图为一颗直径为92.13 μm的碲酸盐玻璃微球的SEM图)

    Fig. 1.  A typical batch of tellurite glass microspheres fabricated in this work. Inset: SEM image of a 92.13-μm diameter tellurite glass microdisk laser.

    图 2  第二次加热示意图

    Fig. 2.  Schematic drawing of the second heating procedure.

    图 3  由一个直径为101.56 μm的微球压出的直径为254.78 μm的微盘谐振腔的SEM照片 (a)俯视图; (b)侧视图

    Fig. 3.  (a) Top-view and (b) side-view of a 254.78-μm-diameter microdisk fabricated with a 101.56-μm-diameter microsphere.

    图 4  由一个直径为62.48 μm的微球压出的直径为101.52 μm的微盘谐振腔的SEM照片 (a)俯视图; (b)侧视图

    Fig. 4.  (a) Top-view and (b) side-view of a 101.52-μm-diameter microdisk fabricated with a 62.48-μm-diameter microsphere.

    图 5  (a)一颗直径为105.74 μm的微盘与一根锥腰直径为1.83 μm的光纤锥耦合图; (b)在1551.0058 nm处获取的吸收峰(Q值为6.2 × 105)

    Fig. 5.  (a) A 105.74-μm-diameter microdisk coupled with a 1.83-μm-waist-diameter fiber taper; (b) a typical absorption peak at 1551.0058 nm, representing a Q-factor of 6.2 × 105.

    图 6  (a)从一颗掺Nd3+的有源微盘谐振腔中获取的不同抽运功率下的回廊模; (b)微盘谐振腔的激光阈值现象(内插图为微盘谐振腔在抽运阈值附近(1.177 mW和1.364 mW)出现的激光峰)

    Fig. 6.  (a) Whispering gallery mode patterns obtained with a Nd3+-doped tellurite glass microdisk at different pump powers; (b) threshold behavior of the microdisk laser. Inset in panel (b) shows the transmission spectra of the coupling system at pump powers of 1.177 mW and 1.364 mW.

    图 7  从一颗掺Tm3+微盘(直径为104.34 μm, 厚度为15.86 μm)中测得的激光阈值现象(内插图为微盘谐振腔在抽运阈值(0.928 mW和1.306 mW)附近出现的位于1908.63 nm处的激光峰)

    Fig. 7.  Threshold behavior of a Tm3+-doped microdisk laser (diameter: 104.34 μm, thickness: 15.86 μm). Inset: transmission spectra of the coupling system at pump powers of 0.928 mW and 1.306 mW.

  • [1]

    Sandoghdar V, Treussart F, Hare J, Lefevre-Seguin V, Raimond J, Haroche S 1996 Phys. Rev. A 54 R1777Google Scholar

    [2]

    Murugan G S, Zervas M N, Panitchob Y, Wilkinson J S 2011 Opt. Lett. 36 73Google Scholar

    [3]

    黄衍堂, 彭隆祥, 庄世坚, 李强龙, 廖廷俤, 许灿华, 段亚凡 2017 物理学报 66 244208Google Scholar

    Huang Y T, Peng L X, Zhuang S J, Li Q L, Liao Y D, Xu C H, Duan Y F 2017 Acta Phys. Sin. 66 244208Google Scholar

    [4]

    Gorajoobi S B, Murugan G S, Zervas M N 2019 Opt. Express 27 25493Google Scholar

    [5]

    Qian K, Tang J, Guo H, Zhang W, Liu J H, Liu J, Xue C Y, Zhang W D 2016 Chin. Phys. B 25 114209Google Scholar

    [6]

    Vernooy D W, Ilchenko V S, Mabuchi H, Streed E W, Kimble H J 1998 Opt. Lett. 23 247Google Scholar

    [7]

    Sasagawa K, Yonezawa Z, Iwai R, Ohta J, Nunoshita M 2004 Appl. Phys. Lett. 85 4325Google Scholar

    [8]

    Peng X, Song F, Jiang S, Peyghambarian N, Kuwata-Gonokami M, Xu L 2003 Appl. Phys. Lett. 82 1497Google Scholar

    [9]

    Elliott G R, Hewak D W, Murugan G S, Wilkinson J S 2007 Opt. Express 15 17542Google Scholar

    [10]

    Li C, Dai S, Zhang Q, Shen X, Wang X, Zhang P, Lu L, Wu Y, Lv S 2015 Chin. Phys. B 24 044208Google Scholar

    [11]

    胡博, 吴越豪, 郑雨璐, 戴世勋 2019 物理学报 68 064209Google Scholar

    Hu B, Wu Y H, Zheng Y L, Dai S X 2019 Acta Phys. Sin. 68 064209Google Scholar

    [12]

    Yang K, Dai S X, Wu Y H, Nie Q H 2018 Chin. Phys. B 27 117701Google Scholar

    [13]

    Spillane S M, Kippenberg T J, Vahala K J, Goh K W, Wilcut E, Kimble H J 2005 Phys. Rev. A 71 013817Google Scholar

    [14]

    Kippenberg T J, Spillane S M, Vahala K J 2004 Appl. Phys. Lett. 85 6113Google Scholar

    [15]

    Wang T J, He J Y, Lee C A, Niu H 2012 Opt. Express 20 028119Google Scholar

    [16]

    Tulek A, Akbulut D, Bayindir M 2009 Appl. Phys. Lett. 94 203302Google Scholar

    [17]

    Polman A, Min B, Kalkman J, Kippenberg T J, Vahala K J 2004 Appl. Phys. Lett. 84 1037Google Scholar

    [18]

    Zou L X, Liu B W, Lv X M, Yang Y D, Xiao J L, Huang Y Z 2015 Appl. Phys. Lett. 106 191107Google Scholar

    [19]

    Yang Z, Wu Y, Yang K, Xu P, Zhang W, Dai S, Xu T 2017 Opt. Mat. 72 524Google Scholar

    [20]

    Li A Z, Zhang J Q, Zhang M, Li W H, Wang S B, Lewis E, Brambilla G, Wang P F 2018 Opt. Lett. 43 4325Google Scholar

    [21]

    Jiang S S, Guo C L, Che K J, Luo Z Q, Du T J, Fu H Y, Xu H Y, Cai Z P 2019 Photon. Res. 7 566Google Scholar

  • [1] 胡博, 吴越豪, 郑雨璐, 戴世勋. 2 μm波段硫系玻璃微球激光器的制备和表征. 物理学报, 2019, 68(6): 064209. doi: 10.7498/aps.68.20181817
    [2] 张兴迪, 吴越豪, 杨正胜, 戴世勋, 张培晴, 张巍, 徐铁锋, 张勤远. Tm3+掺杂Ge-Ga-S玻璃微球-石英光纤锥耦合系统的荧光回廊模特性. 物理学报, 2016, 65(14): 144205. doi: 10.7498/aps.65.144205
    [3] 刘丽莎, 吕树臣, 孙江亭. Er3+/Yb3+共掺TeO2-WO3-Bi2O3玻璃的光谱性质和上转换发光. 物理学报, 2010, 59(9): 6637-6641. doi: 10.7498/aps.59.6637
    [4] 陈敢新, 张勤远, 赵纯, 石冬梅, 姜中宏. 掺Tm3+和Tm3+/Ho3+共掺碲钨酸盐玻璃中能量转换过程和机理. 物理学报, 2010, 59(2): 1321-1327. doi: 10.7498/aps.59.1321
    [5] 王大刚, 周亚训, 王训四, 戴世勋, 沈祥, 陈飞飞, 王森. 应用于白光显示的Tm3+/Ho3+/Yb3+共掺碲酸盐玻璃上转换发光特性研究. 物理学报, 2010, 59(9): 6256-6260. doi: 10.7498/aps.59.6256
    [6] 周亚训, 戴世勋, 周灵, 徐铁峰, 聂秋华, 黄尚廉. 掺铒碲酸盐玻璃中的协作上转换能量转移. 物理学报, 2009, 58(2): 1261-1268. doi: 10.7498/aps.58.1261
    [7] 厉旭杰, 聂秋华, 戴世勋, 徐铁峰, 沈 祥, 章向华. 低温下Er3+/Yb3+共掺碲酸盐玻璃的发光特性研究. 物理学报, 2008, 57(5): 3001-3005. doi: 10.7498/aps.57.3001
    [8] 赵 纯, 张勤远, 陈东丹, 姜中宏. 激光二极管抽运下铥/镱共掺碲镓酸盐玻璃光谱特性研究. 物理学报, 2007, 56(7): 4194-4199. doi: 10.7498/aps.56.4194
    [9] 金 哲, 聂秋华, 徐铁峰, 戴世勋, 沈 祥, 章向华. Tm3+/Yb3+共掺碲铅锌镧玻璃的能量传递和上转换发光. 物理学报, 2007, 56(4): 2261-2267. doi: 10.7498/aps.56.2261
    [10] 戴世勋, 厉旭杰, 聂秋华, 徐铁峰, 沈 祥, 王训四. Yb3+敏化的Er3+/Ho3+共掺碲酸盐玻璃的上转换发光研究. 物理学报, 2007, 56(9): 5518-5525. doi: 10.7498/aps.56.5518
    [11] 陈敢新, 张勤远, 杨钢锋, 杨中民, 姜中宏. Tm3+/Ho3+共掺碲酸盐玻璃的2.0μm发光特性及能量传递. 物理学报, 2007, 56(7): 4200-4206. doi: 10.7498/aps.56.4200
    [12] 张 茹, 王 淼, 张 宁, Srinivasan G.. (Ni0.8Zn0.2Fe2O4)epoxy-PZT双层膜中的磁电效应. 物理学报, 2006, 55(5): 2548-2552. doi: 10.7498/aps.55.2548
    [13] 戴世勋, 徐铁峰, 聂秋华, 沈 祥, 张军杰, 胡丽丽. 荧光俘获效应对掺饵氧化物玻璃光谱性质的影响. 物理学报, 2006, 55(3): 1479-1485. doi: 10.7498/aps.55.1479
    [14] 汪国年, 戴世勋, 张军杰, 胡丽丽, 姜中宏. Yb:铅锌镧碲酸盐玻璃的热学、光谱和激光性质. 物理学报, 2005, 54(4): 1854-1858. doi: 10.7498/aps.54.1854
    [15] 陈炳炎, 刘粤惠, 陈东丹, 姜中宏. 一种新型掺铒碲酸盐玻璃的光谱性质研究. 物理学报, 2005, 54(5): 2374-2378. doi: 10.7498/aps.54.2374
    [16] 于春雷, 戴世勋, 周 刚, 张军杰, 胡丽丽, 姜中宏. 掺铒碲酸盐玻璃中的浓度猝灭机理研究. 物理学报, 2005, 54(8): 3894-3899. doi: 10.7498/aps.54.3894
    [17] 陈 鹤, 刘粤惠, 姚小旭, 冯洲明. 不同Tm3+浓度掺杂碲酸盐玻璃光谱性质研究. 物理学报, 2005, 54(9): 4427-4432. doi: 10.7498/aps.54.4427
    [18] 刘粤惠, 陈东丹, 侯志远, 陈 鹤, 张勤远, 邓再德, 姜中宏. 977nm抽运下掺铒碲酸盐基氧卤玻璃的光谱特性. 物理学报, 2005, 54(1): 422-428. doi: 10.7498/aps.54.422
    [19] 戴世勋, 杨建虎, 柳祝平, 温 磊, 胡丽丽, 姜中宏. 970nm抽运下Er3+/Yb3+/Tm3+共掺碲酸盐玻璃的发光特性. 物理学报, 2003, 52(3): 729-735. doi: 10.7498/aps.52.729
    [20] 林金谷, 刘承惠, 朱振和, 赖瑞生, 霍崇儒. 用非共线二次谐波法实现对锁模激光器超短脉冲宽度的测定. 物理学报, 1980, 29(3): 406-408. doi: 10.7498/aps.29.406
计量
  • 文章访问数:  7285
  • PDF下载量:  54
  • 被引次数: 0
出版历程
  • 收稿日期:  2019-07-09
  • 修回日期:  2019-09-29
  • 上网日期:  2019-11-27
  • 刊出日期:  2019-12-01

/

返回文章
返回