适用于2.79 μm波段的可饱和吸收材料一直是该波段被动调Q激光技术研究关注的重点. 乙醇作为一种流动性好、化学性质稳定、恢复性好、损伤阈值高的材料有成为良好可饱和吸收体的潜力. 本研究通过设计的微米级液体厚度调控装置控制乙醇溶液的厚度, 实现了2.79 μm Er, Cr:YSGG激光器被动调Q脉冲输出. 在液层厚度为45 μm, 重复频率为20 Hz时, 获得的多脉冲最大能量为11.64 mJ, 最窄单脉冲宽度为287.6 ns. 结果表明, 乙醇作为液相饱和吸收体在2.79 μm波段吸收暗区也具有良好的可饱和吸收特性, 为乙醇作为饱和吸收体的应用和其他羟基可饱和吸收体材料的研究提供了参考.
The search for suitable saturable absorption materials for the 2.79-μm wavelength range has been a key focus in the development of passive Q -switched laser technology at this wavelength. High-purity ethanol serving as a saturable absorber operating within its intrinsic absorption darkening region is comprehensively investigated in this work. Ethanol stands out due to its high damage threshold, excellent fluidity, and long-term chemical stability, thereby making it a promising candidate for mid-infrared applications. Using a custom-designed micrometer-precision liquid cell, the ethanol layer thickness is continuously modulated from 14 μm to 55 μm (±1 μm accuracy), and passive Q -switching can be achieved without the need for an external modulator. The laser system adopts a 248-mm planar resonator, which includes a $\varPhi $3 mm × 70 mm Er, Cr:YSGG rod (Cr3+ 3% (atomic percentage), Er3+ 30% (atomic percentage)), and a flashlamp pumped at 250 μs and 20 Hz. Under these conditions, the output pulse characteristics are governed almost entirely by the ethanol thickness. When the pump energy is fixed at 12.86 J, reducing the layer thickness from 55 μm to 14 μm will shorten the pulse duration from 366.1 ns to 257.9 ns and increase the single-pulse energy from 1.25 mJ to 3.48 mJ. Optimal performance, characterized by 287.6 ns pulses and 11.64 mJ energy, is achieved at a thickness of 45 μm. While maintaining this optimal thickness, increasing the pump energy from 7.01 J to 10.75 J will further compress the pulses from 629.1 ns to 287.6 ns and increases the output energy from 0.52 mJ to 11.64 mJ, none of which do not cause optical damage, indicating a damage threshold exceeding 10 J/cm2. At pump energies exceeding 8.4 J, the ethanol undergoes re-bleaching within its ~20 μs recovery time, resulting in the formation of 2–5 equally spaced nanosecond sub-pulses (6–12 μs spacing, effective repetition ≈ 100 kHz) within a single pump envelope, which is an operating regime highly favorable for precision laser ablation. The beam quality at maximum output is measured to be $ M_x^2 =7.51 $ and $ M_y^2 =7.51 $. These results are supported by rate-equation modeling combined with temperature-dependent absorption cross-sections from the HITRAN database, establishing ethanol as an adjustable, high-damage-threshold liquid saturable absorber for compact mid-infrared Q -switched lasers, and emphasizing the broader potential of hydroxyl-containing liquids for next-generation medical and spectroscopic applications. -
Keywords:
- solid-state lasers /
- Er /
- Cr:YSGG laser /
- passive Q-switching /
- saturable absorber
[1] Burikov S, Dolenko T, Patsaeva S, Starokurov Y, Yuzhakov V 2010 Mol. Phys. 108 2427
Google Scholar
[2] Wei C, Zhu X S, Norwood R A, Song F, Peyghambarian N 2013 Opt. Express 21 29488
Google Scholar
[3] Skorczakowski M, Swiderski J, Pichola W, Nyga P, Zajac A, Maciejewska M, Galecki L, Kasprzak J, Gross S, Heinrich A, Bragagna T 2010 Laser Phys. Lett. 7 498
Google Scholar
[4] Wang L, Wang J T, Yang J W, Wu X Y, Sun D L, Yin S T, Jiang H H, Wang J Y, Xu C Q 2013 Opt. Lett. 38 2150
Google Scholar
[5] Yang J W, Wang L, Wu X Y, Cheng T T, Jiang H H 2014 Opt. Express 22 15686
Google Scholar
[6] Huang L, Wang P, Wang Y, Cheng T, Wang L, Jiang H 2024 Photonics 11 432
Google Scholar
[7] Cui Q Z, Wei M G, Xiong Z D, et al. 2019 Infrared Phys. Technol. 98 256
Google Scholar
[8] Huang L, Wang Y Z, Zhang Y Y, Cheng T Q, Wang L, Jiang H H 2024 Opt. Laser Technol. 175 110743
Google Scholar
[9] Wang S W, Tang Y L, Yang J L, Zhong H Z, Fan D Y 2019 Laser Phys. 29 025101
Google Scholar
[10] Tang P H, Wu M, Wang Q K, Miao L L, Huang B, Liu J, Zhao C, Wen S 2016 IEEE Photonics Technol. Lett. 28 1573
Google Scholar
[11] Xiong Z D, Jiang L L, Cheng T Q, Jiang H H 2022 Infrared Phys. Technol. 122 104087
Google Scholar
[12] Li C, Liu J, Jiang S Z, Xu S C, Ma W W, Wang J Y, Xu X D, Su L B 2016 Opt. Mater. Express 6 1570
Google Scholar
[13] Qin Z P, Xie G Q, Ma J G, Yuan P, Qian L J 2018 Photonics Res. 6 1074
Google Scholar
[14] Vodopyanov K L, Shori R, Stafsudd O M 1998 Appl. Phys. Lett. 72 2211
Google Scholar
[15] Deàk J C, Rhea S T, Iwaki L K, Dlott D D 2000 J. Phys. Chem. A 104 4866
Google Scholar
[16] Flór M, Wilkins D M, De La Puente M, Laage D, Cassone G, Hassanali A, Roke S 2024 Science 386 eads4369
Google Scholar
[17] Vodop’yanov K L, Kulevskiǐ L, Pashinin P, Prokhorov A 1982 J. Exp. Theor. Phys. 55 1049
[18] Vodop’yanov L 1990 J. Exp. Theor. Phys. 70 114
[19] Shori R K, Walston A A, Stafsudd O M, Fried D, Walsh J T 2001 IEEE J. Sel. Top. Quantum Electron. 7 959
Google Scholar
[20] Dong J 2003 Opt. Commun. 226 337
Google Scholar
[21] Kucherov A N 2003 Dokl. Phys. 48 90
Google Scholar
[22] Vogel A, Venugopalan V 2003 Chem. Rev. 103 577
Google Scholar
[23] Xian T H, Zhan L, Gao L R, Zhang W Y, Zhang W C 2019 Opt. Lett. 44 863
Google Scholar
[24] 戴川生, 董志鹏, 林加强, 姚培军, 许立新, 顾春 2022 物理学报 71 174202
Google Scholar
Dai C S, Dong Z P, Lin J Q, Yao P J, Xu L X, Gu C 2022 Acta Phys. Sin. 71 174202
Google Scholar
-
图 1 不同泵浦功率下, 光子数密度随时间变化仿真结果
Fig. 1. Simulation results of photon number density changing with time under different pump power.
图 2 Er, Cr:YSGG被动调Q激光实验装置图
Fig. 2. Schematic diagram of a passively Q -switched Er, Cr:YSGG laser.
图 3 微米级液体厚度调控装置实物图
Fig. 3. Photograph of the micron-scale liquid thickness control device.
图 5 泵浦能量12.86 J、重复频率20 Hz时静态输出脉冲波形图
Fig. 5. Static output pulse waveform at a pump energy of 12.86 J and a repetition rate of 20 Hz.
图 6 输出能量和脉冲宽度随溶液厚度的变化
Fig. 6. Output energy and pulse duration as a function of thickness of the ethanol.
图 7 乙醇溶液厚度14 μm、泵浦能量12.86 J、重复频率20 Hz时调Q输出脉冲波形图
Fig. 7. Pulse waveform of ethanol Q -switched output with ethanol thickness of 14 μm, pump energy of 12.86 J, and repetition rate of 20 Hz.
图 8 输出能量和脉冲宽度随泵浦能量的变化
Fig. 8. Output energy and pulse duration as a function of pump energy.
-
[1] Burikov S, Dolenko T, Patsaeva S, Starokurov Y, Yuzhakov V 2010 Mol. Phys. 108 2427
Google Scholar
[2] Wei C, Zhu X S, Norwood R A, Song F, Peyghambarian N 2013 Opt. Express 21 29488
Google Scholar
[3] Skorczakowski M, Swiderski J, Pichola W, Nyga P, Zajac A, Maciejewska M, Galecki L, Kasprzak J, Gross S, Heinrich A, Bragagna T 2010 Laser Phys. Lett. 7 498
Google Scholar
[4] Wang L, Wang J T, Yang J W, Wu X Y, Sun D L, Yin S T, Jiang H H, Wang J Y, Xu C Q 2013 Opt. Lett. 38 2150
Google Scholar
[5] Yang J W, Wang L, Wu X Y, Cheng T T, Jiang H H 2014 Opt. Express 22 15686
Google Scholar
[6] Huang L, Wang P, Wang Y, Cheng T, Wang L, Jiang H 2024 Photonics 11 432
Google Scholar
[7] Cui Q Z, Wei M G, Xiong Z D, et al. 2019 Infrared Phys. Technol. 98 256
Google Scholar
[8] Huang L, Wang Y Z, Zhang Y Y, Cheng T Q, Wang L, Jiang H H 2024 Opt. Laser Technol. 175 110743
Google Scholar
[9] Wang S W, Tang Y L, Yang J L, Zhong H Z, Fan D Y 2019 Laser Phys. 29 025101
Google Scholar
[10] Tang P H, Wu M, Wang Q K, Miao L L, Huang B, Liu J, Zhao C, Wen S 2016 IEEE Photonics Technol. Lett. 28 1573
Google Scholar
[11] Xiong Z D, Jiang L L, Cheng T Q, Jiang H H 2022 Infrared Phys. Technol. 122 104087
Google Scholar
[12] Li C, Liu J, Jiang S Z, Xu S C, Ma W W, Wang J Y, Xu X D, Su L B 2016 Opt. Mater. Express 6 1570
Google Scholar
[13] Qin Z P, Xie G Q, Ma J G, Yuan P, Qian L J 2018 Photonics Res. 6 1074
Google Scholar
[14] Vodopyanov K L, Shori R, Stafsudd O M 1998 Appl. Phys. Lett. 72 2211
Google Scholar
[15] Deàk J C, Rhea S T, Iwaki L K, Dlott D D 2000 J. Phys. Chem. A 104 4866
Google Scholar
[16] Flór M, Wilkins D M, De La Puente M, Laage D, Cassone G, Hassanali A, Roke S 2024 Science 386 eads4369
Google Scholar
[17] Vodop’yanov K L, Kulevskiǐ L, Pashinin P, Prokhorov A 1982 J. Exp. Theor. Phys. 55 1049
[18] Vodop’yanov L 1990 J. Exp. Theor. Phys. 70 114
[19] Shori R K, Walston A A, Stafsudd O M, Fried D, Walsh J T 2001 IEEE J. Sel. Top. Quantum Electron. 7 959
Google Scholar
[20] Dong J 2003 Opt. Commun. 226 337
Google Scholar
[21] Kucherov A N 2003 Dokl. Phys. 48 90
Google Scholar
[22] Vogel A, Venugopalan V 2003 Chem. Rev. 103 577
Google Scholar
[23] Xian T H, Zhan L, Gao L R, Zhang W Y, Zhang W C 2019 Opt. Lett. 44 863
Google Scholar
[24] 戴川生, 董志鹏, 林加强, 姚培军, 许立新, 顾春 2022 物理学报 71 174202
Google Scholar
Dai C S, Dong Z P, Lin J Q, Yao P J, Xu L X, Gu C 2022 Acta Phys. Sin. 71 174202
Google Scholar
下载:
计量
- 文章访问数: 829
- PDF下载量: 12
- 被引次数: 0