溅射制备Ge,Nb共掺杂窄光学带隙和低电阻率的TiO2薄膜

罗晓东 狄国庆

引用本文:
Citation:

溅射制备Ge,Nb共掺杂窄光学带隙和低电阻率的TiO2薄膜

罗晓东, 狄国庆

Ge and Nb co-doped TiO2 films with narrow band gap and low resistivity prepared by sputtering

Luo Xiao-Dong, Di Guo-Qing
PDF
导出引用
  • 采用射频磁控溅射技术制备了Ge, Nb共掺杂的锐钛矿结构TiO2薄膜,详细探讨了薄膜的结构、 电阻率及光学带隙等性质随Ge, Nb掺杂量、溅射功率和热处理温度等参数的变化, 发现Ge, Nb共掺杂可以同时调节TiO2薄膜的光学带隙和电阻率. 体积分数约为6% Nb和20% Ge的共掺杂TiO2薄膜电阻率由104 Ω/cm减小至 10-1 Ω/cm,光学带隙由3.2 eV减小至1.9 eV. 退火后掺杂TiO2薄膜不仅显示更低的电阻率,还表现出更强的可见-红外光吸收. 结果表明,改变Ge, Nb的掺杂量和退火条件能够制备出电阻率和带隙都可调的TiO2薄膜.
    Ge and Nb co-doped anatase TiO2 films are prepared by using radio frequency magnetron sputtering. The structures, resistivities and band gap properties of the films, which depend on Ge and Nb doping amounts, sputtering power and annealing temperature, are discussed. It is found that the band gap and resistivity of TiO2 film can be simultaneously tailored by co-doping with Ge and Nb. With doping volume fractions of 6% Nb and 20% Ge, the resistivity of the film can be reduced from 104 Ω/cm to 10-1 Ω/cm, and the band gap from 3.2 eV to 1.9 eV. After annealing, the Ge and Nb co-doped TiO2 film shows not only a lower resistivity but also a stronger absorption for visible and infrared light. As a result, Ge and Nb co-doped TiO2 film with adjustable band gap and resistivity can be prepared with magnetron sputtering by choosing proper Ge and Nb doping amounts and annealing conditions.
    • 基金项目: 江苏省高校自然科学重大基础研究项目(批准号: 05KJA43006)资助的课题.
    • Funds: Project supported by the Basic Research Program of Jiangsu Province, China (Grant No. 05KJA43006).
    [1]

    Bach U, Lupo D, Comte P, Moser J E, Weissörtel F, Salbeck J, Spreitzer H, Grätzel M 1998 Nature 395 583

    [2]

    O'Hayre R, Nanu M, Schoonman J, Goossens A, Wang Q, Grätzel M 2006 Adv. Funct. Mater. 16 1566

    [3]

    Lin H, Huang C P, Li W, Ni C, Ismat Shah S, Tseng Y H 2006 Appl. Catal. B: Environ. 68 1

    [4]

    Albertin K F, Pereyra I 2009 Thin Solid Films 517 4548

    [5]

    Kurtz S R, Gordon R G 1997 Thin Solid Films 147 167

    [6]

    Cui Y F, Yuan Z H Acta Phys. Sin. 55 5127 (in Chinese) [崔永锋, 袁志好 2006 物理学报 55 5127]

    [7]

    Bu J L, Jiang Z Y, Jiao S H 2012 Adv. Mater. Res. 415-417 2036

    [8]

    Mwabora J M, Lindgren T, Avendano E, Jaramillo T F, Lu J, Lindquist S E, Granqvist C 2004 J. Phys. Chem. B 108 20193

    [9]

    Umebayashi T, Yamaki T, Itoh H, Asai K 2002 Appl. Phys. Lett. 81 454

    [10]

    Sakthivel S, Kisch H 2003 Angew. Chem. Int. Ed. 42 4908

    [11]

    Wu X W, Wu D J, Liu X J 2010 Acta Phys. Sin. 59 4788 (in Chinese) [吴雪炜, 吴大建, 刘晓峻 2010 物理学报 59 4788]

    [12]

    Zhang Y, Tang C Q, Dai J 2005 Acta Phys. Sin. 54 323 (in Chinese) [张勇, 唐超群, 戴君 2005 物理学报 54 323]

    [13]

    Chatterjee S, Goyal A, Ismat Shah S 2006 Mater. Lett. 60 3541

    [14]

    Chatterjee S 2008 Solar Energy 82 95

    [15]

    Gai Y Q, Li J B, Li S S, Xia J B, Wei S H 2009 Phys. Rev. Lett. 102 36402

    [16]

    Zhang X J, Gao P, Liu Q J 2010 Acta Phys. Sin. 59 4930 (in Chinese) [张学军, 高攀, 柳清菊 2010 物理学报 59 4930]

    [17]

    Luo H, Takata T, Lee Y, Zhao J F, Domen K, Yan Y S 2004 Chem. Mater. 16 846

    [18]

    Furubayashi Y, Hitosugi T, Yamamoto Y, Inana K, Kinoda G, Hirose Y, Shimada T, Hasegawa T 2005 Appl. Phys. Lett. 86 252101

    [19]

    Hitosugi T, Yamada N, Nakao S, Kirose Y, hasegawa T 2010 Phys. Status Solidi A 207 1529

    [20]

    Liu G A, Yang G J, Zheng F S 2007 Chin. J. Vacuum Sci. Technol. 27 254 (in Chinese) [刘贵昴, 杨贵进, 郑妃盛 2007 真空科学与技术学报 27 254]

    [21]

    Ghosh T B, Dhabal S, Datta A K 2003 J. Appl. Phys. 94 4577

    [22]

    Guo M L, Zhang X D, Liang C T 2011 Physica B: Condensed Matter 406 3354

    [23]

    Tang H, Prasad K, Sanjines R, Schmid P E, Levy F 1994 J. Appl. Phys. 75 1994

    [24]

    Sato Y, Akizuki H, Kamiyama T, Shigesato Y 2008 Thin Solid Films 516 5758

    [25]

    Hitosugi T, Kamisaka H, Yamashita K, Nogawa H, Furubayashi Y, Nakao S, Yamada N, Chikamatsu A, Kumigashira H, Oshima M, Hirose Y, Shimada T, Hasegawa T 2008 Appl. Phys. Express 1 111203

    [26]

    Hamberg I, Granqvist C G 1986 J. Appl. Phys. 60 123

    [27]

    Hitosugi T, Yamada N, Nakao S, Hirose Y, Hasegawa T 2010 Phys. Status Solidi A 207 1529

    [28]

    Khan A F, Mehmood M, Aslam M, Ismat Shah S 2010 J. Colloid Interf. Sci. 343 271

    [29]

    Tang H, Prasad, Sanjines R, Schmid P, Levy F 1994 J. Appl. Phys. 75 2042

  • [1]

    Bach U, Lupo D, Comte P, Moser J E, Weissörtel F, Salbeck J, Spreitzer H, Grätzel M 1998 Nature 395 583

    [2]

    O'Hayre R, Nanu M, Schoonman J, Goossens A, Wang Q, Grätzel M 2006 Adv. Funct. Mater. 16 1566

    [3]

    Lin H, Huang C P, Li W, Ni C, Ismat Shah S, Tseng Y H 2006 Appl. Catal. B: Environ. 68 1

    [4]

    Albertin K F, Pereyra I 2009 Thin Solid Films 517 4548

    [5]

    Kurtz S R, Gordon R G 1997 Thin Solid Films 147 167

    [6]

    Cui Y F, Yuan Z H Acta Phys. Sin. 55 5127 (in Chinese) [崔永锋, 袁志好 2006 物理学报 55 5127]

    [7]

    Bu J L, Jiang Z Y, Jiao S H 2012 Adv. Mater. Res. 415-417 2036

    [8]

    Mwabora J M, Lindgren T, Avendano E, Jaramillo T F, Lu J, Lindquist S E, Granqvist C 2004 J. Phys. Chem. B 108 20193

    [9]

    Umebayashi T, Yamaki T, Itoh H, Asai K 2002 Appl. Phys. Lett. 81 454

    [10]

    Sakthivel S, Kisch H 2003 Angew. Chem. Int. Ed. 42 4908

    [11]

    Wu X W, Wu D J, Liu X J 2010 Acta Phys. Sin. 59 4788 (in Chinese) [吴雪炜, 吴大建, 刘晓峻 2010 物理学报 59 4788]

    [12]

    Zhang Y, Tang C Q, Dai J 2005 Acta Phys. Sin. 54 323 (in Chinese) [张勇, 唐超群, 戴君 2005 物理学报 54 323]

    [13]

    Chatterjee S, Goyal A, Ismat Shah S 2006 Mater. Lett. 60 3541

    [14]

    Chatterjee S 2008 Solar Energy 82 95

    [15]

    Gai Y Q, Li J B, Li S S, Xia J B, Wei S H 2009 Phys. Rev. Lett. 102 36402

    [16]

    Zhang X J, Gao P, Liu Q J 2010 Acta Phys. Sin. 59 4930 (in Chinese) [张学军, 高攀, 柳清菊 2010 物理学报 59 4930]

    [17]

    Luo H, Takata T, Lee Y, Zhao J F, Domen K, Yan Y S 2004 Chem. Mater. 16 846

    [18]

    Furubayashi Y, Hitosugi T, Yamamoto Y, Inana K, Kinoda G, Hirose Y, Shimada T, Hasegawa T 2005 Appl. Phys. Lett. 86 252101

    [19]

    Hitosugi T, Yamada N, Nakao S, Kirose Y, hasegawa T 2010 Phys. Status Solidi A 207 1529

    [20]

    Liu G A, Yang G J, Zheng F S 2007 Chin. J. Vacuum Sci. Technol. 27 254 (in Chinese) [刘贵昴, 杨贵进, 郑妃盛 2007 真空科学与技术学报 27 254]

    [21]

    Ghosh T B, Dhabal S, Datta A K 2003 J. Appl. Phys. 94 4577

    [22]

    Guo M L, Zhang X D, Liang C T 2011 Physica B: Condensed Matter 406 3354

    [23]

    Tang H, Prasad K, Sanjines R, Schmid P E, Levy F 1994 J. Appl. Phys. 75 1994

    [24]

    Sato Y, Akizuki H, Kamiyama T, Shigesato Y 2008 Thin Solid Films 516 5758

    [25]

    Hitosugi T, Kamisaka H, Yamashita K, Nogawa H, Furubayashi Y, Nakao S, Yamada N, Chikamatsu A, Kumigashira H, Oshima M, Hirose Y, Shimada T, Hasegawa T 2008 Appl. Phys. Express 1 111203

    [26]

    Hamberg I, Granqvist C G 1986 J. Appl. Phys. 60 123

    [27]

    Hitosugi T, Yamada N, Nakao S, Hirose Y, Hasegawa T 2010 Phys. Status Solidi A 207 1529

    [28]

    Khan A F, Mehmood M, Aslam M, Ismat Shah S 2010 J. Colloid Interf. Sci. 343 271

    [29]

    Tang H, Prasad, Sanjines R, Schmid P, Levy F 1994 J. Appl. Phys. 75 2042

  • [1] 张鑫鑫, 靳映霞, 叶晓松, 王茺, 杨宇. 高速率沉积磁控溅射技术制备Ge点的退火生长研究. 物理学报, 2014, 63(15): 156802. doi: 10.7498/aps.63.156802
    [2] 马海林, 苏庆. 氧分压对溅射制备氧化镓薄膜结构及光学带隙的影响. 物理学报, 2014, 63(11): 116701. doi: 10.7498/aps.63.116701
    [3] 佟国香, 李毅, 王锋, 黄毅泽, 方宝英, 王晓华, 朱慧群, 梁倩, 严梦, 覃源, 丁杰, 陈少娟, 陈建坤, 郑鸿柱, 袁文瑞. 磁控溅射制备W掺杂VO2/FTO复合薄膜及其性能分析. 物理学报, 2013, 62(20): 208102. doi: 10.7498/aps.62.208102
    [4] 张传军, 邬云骅, 曹鸿, 高艳卿, 赵守仁, 王善力, 褚君浩. 不同衬底和CdCl2退火对磁控溅射CdS薄膜性能的影响. 物理学报, 2013, 62(15): 158107. doi: 10.7498/aps.62.158107
    [5] 李林娜, 陈新亮, 王斐, 孙建, 张德坤, 耿新华, 赵颖. H2 气对脉冲磁控溅射铝掺杂氧化锌薄膜性能的影响. 物理学报, 2011, 60(6): 067304. doi: 10.7498/aps.60.067304
    [6] 曹月华, 狄国庆. 磁控溅射制备Y2O3-TiO2薄膜形貌的研究. 物理学报, 2011, 60(3): 037702. doi: 10.7498/aps.60.037702
    [7] 狄国庆. 溅射制备Ta2O5薄膜的表面形貌与光学特性. 物理学报, 2011, 60(3): 038101. doi: 10.7498/aps.60.038101
    [8] 丁万昱, 徐军, 陆文琪, 邓新绿, 董闯. 微波ECR磁控溅射制备SiNx薄膜的XPS结构研究. 物理学报, 2009, 58(6): 4109-4116. doi: 10.7498/aps.58.4109
    [9] 贾璐, 谢二庆, 潘孝军, 张振兴. 溅射制备非晶氮化镓薄膜的光学性能. 物理学报, 2009, 58(5): 3377-3382. doi: 10.7498/aps.58.3377
    [10] 邓金祥, 汪旭洋, 姚 倩, 周 涛, 张晓康. 立方氮化硼薄膜的光学带隙. 物理学报, 2008, 57(10): 6631-6635. doi: 10.7498/aps.57.6631
    [11] 肖剑荣, 徐 慧, 郭爱敏, 王焕友. 含氮氟化类金刚石(FN-DLC)薄膜的研究:(Ⅱ)射频功率对薄膜光学带隙的影响. 物理学报, 2007, 56(3): 1809-1814. doi: 10.7498/aps.56.1809
    [12] 肖剑荣, 徐 慧, 李燕峰, 李明君. 氮分压对氮化铜薄膜结构及光学带隙的影响. 物理学报, 2007, 56(7): 4169-4174. doi: 10.7498/aps.56.4169
    [13] 梁丽萍, 张 磊, 盛永刚, 徐 耀, 吴 东, 孙予罕, 蒋晓东, 魏晓峰. 溶胶-凝胶ZrO2-TiO2高折射率光学膜层的抗激光损伤性能研究. 物理学报, 2007, 56(6): 3596-3601. doi: 10.7498/aps.56.3596
    [14] 汪 渊, 徐可为. Cu-W薄膜表面形貌的分形表征与电阻率. 物理学报, 2004, 53(3): 900-904. doi: 10.7498/aps.53.900
    [15] 马平, 刘乐园, 张升原, 王昕, 谢飞翔, 邓鹏, 聂瑞娟, 王守证, 戴远东, 王福仁. 直流磁控溅射一步法原位制备MgB2超导薄膜. 物理学报, 2002, 51(2): 406-409. doi: 10.7498/aps.51.406
    [16] 杨宏顺, 李鹏程, 柴一晟, 余旻, 李志权, 杨东升, 章良, 王喻宏, 李明德, 曹烈兆, 龙云泽, 陈兆甲. La2CuO4掺锌样品的低温电阻率与热导率研究. 物理学报, 2002, 51(3): 679-684. doi: 10.7498/aps.51.679
    [17] 叶超, 宁兆元, 程珊华, 王响英. 氟化非晶碳薄膜的光学带隙分析. 物理学报, 2002, 51(11): 2640-2643. doi: 10.7498/aps.51.2640
    [18] 杨慎东, 宁兆元, 黄峰, 程珊华, 叶超. a-C:F薄膜的热稳定性与光学带隙的关联. 物理学报, 2002, 51(6): 1321-1325. doi: 10.7498/aps.51.1321
    [19] 杨宏顺, 余旻, 李世燕, 李鹏程, 柴一晟, 章良, 陈仙辉, 曹烈兆. 新型超导体MgB2的热电势和电阻率研究. 物理学报, 2001, 50(6): 1197-1200. doi: 10.7498/aps.50.1197
    [20] 李慧玲, 阮可青, 李世燕, 莫维勤, 樊荣, 罗习刚, 陈仙辉, 曹烈兆. MgB2和Mg0.93Li0.07B2的电阻率与霍尔效应研究. 物理学报, 2001, 50(10): 2044-2048. doi: 10.7498/aps.50.2044
计量
  • 文章访问数:  4277
  • PDF下载量:  357
  • 被引次数: 0
出版历程
  • 收稿日期:  2012-03-02
  • 修回日期:  2012-05-08
  • 刊出日期:  2012-10-05

溅射制备Ge,Nb共掺杂窄光学带隙和低电阻率的TiO2薄膜

  • 1. 苏州大学物理科学与技术学院,薄膜材料江苏省重点实验室, 苏州 215006
    基金项目: 江苏省高校自然科学重大基础研究项目(批准号: 05KJA43006)资助的课题.

摘要: 采用射频磁控溅射技术制备了Ge, Nb共掺杂的锐钛矿结构TiO2薄膜,详细探讨了薄膜的结构、 电阻率及光学带隙等性质随Ge, Nb掺杂量、溅射功率和热处理温度等参数的变化, 发现Ge, Nb共掺杂可以同时调节TiO2薄膜的光学带隙和电阻率. 体积分数约为6% Nb和20% Ge的共掺杂TiO2薄膜电阻率由104 Ω/cm减小至 10-1 Ω/cm,光学带隙由3.2 eV减小至1.9 eV. 退火后掺杂TiO2薄膜不仅显示更低的电阻率,还表现出更强的可见-红外光吸收. 结果表明,改变Ge, Nb的掺杂量和退火条件能够制备出电阻率和带隙都可调的TiO2薄膜.

English Abstract

参考文献 (29)

目录

    /

    返回文章
    返回