高密度脉冲电流对非晶Fe-Ni-Si-B合金结构弛豫与晶化的促进效应

晁月盛 孙少权 滕功清 赖祖涵

引用本文:
Citation:

高密度脉冲电流对非晶Fe-Ni-Si-B合金结构弛豫与晶化的促进效应

晁月盛, 孙少权, 滕功清, 赖祖涵

ACCELERATING EFFECT OF HIGH DENSITY ELECTRO-PULSING UPON STRUCTURE RELAXATION AND CRYSTALLIZATION OF AMORPHOUS ALLOY

CHAO YUE-SHENG, SUN SHAO-QUAN, TENG GONG-QING, LAI ZU-HAN
PDF
导出引用
  • 对非晶Fe73Ni5Si8B14合金分别进行了高密度脉冲电流及真空退火处理.用穆斯堡尔谱学与透射电子显微镜技术研究了处理后非晶的微观结构与晶化行为.实验结果表明,与退火处理相比,高密度脉冲电流产生的“电子风”促进了非晶合金的结构弛豫与晶化.随电流密度显著增加,这一促进效应进一步增强
    High density electropulsing and vacuum annealing treatments of amorphous alloy Fe73Ni5Si8B14 have been carried out. The microstructural change and crystallization behavior after treating were investigated by M?ssbauer spectroscopy and TEM techniques. The experimental results show that the "electron wind " induced by high density current promotes the structure of amorphous alloy to be more relaxed and crystallized as compared with annealing treatment. And, The accelerating effect is further enhanced with an increase of current density.
    • 基金项目: 国家自然科学基金及冶金工业部科学技术司基金资助的课题.
计量
  • 文章访问数:  4920
  • PDF下载量:  598
  • 被引次数: 0
出版历程
  • 收稿日期:  1995-09-22
  • 修回日期:  1995-11-20
  • 刊出日期:  1996-09-20

高密度脉冲电流对非晶Fe-Ni-Si-B合金结构弛豫与晶化的促进效应

  • 1. 东北大学理学院
    基金项目: 国家自然科学基金及冶金工业部科学技术司基金资助的课题.

摘要: 对非晶Fe73Ni5Si8B14合金分别进行了高密度脉冲电流及真空退火处理.用穆斯堡尔谱学与透射电子显微镜技术研究了处理后非晶的微观结构与晶化行为.实验结果表明,与退火处理相比,高密度脉冲电流产生的“电子风”促进了非晶合金的结构弛豫与晶化.随电流密度显著增加,这一促进效应进一步增强