Bi2O3:BaF2 and BiF3:BaF2 crystals were prepared by TGT (temperature gradient method). Near-infrared broadband luminescence was observed in as-grown Bi2O3:BaF2 crystal. The emission band peaks at 961 nm in the range of 850—1250 nm，with FWHM about 202 nm. The luminescence of Bi2+ and Bi3+ ions in the visible region was observed in BiF3:BaF2 crystal, but there was no near-infrared emission. Then the BiF3: BaF2 crystal was exposed to γ-rays in order to reduce valence states of Bi ions. Near-infrared broadband luminescence was observed in γ-irradiated BiF3:BaF2 crystal. The emission band peaks at 1135 nm in the range of 850—1500 nm，with FWHM about 192 nm. The mechanisms of near-infrared luminescence in Bi2O3:BaF2 crystals and γ-irradiated BiF3:BaF2 crystals were discussed.
-
Keywords:
- near-infrared luminescence /
- bismuth /
- BaF2 crystal /
- γ-irradiation
[1] ［1］Flood F A 2000 Proceedings of Optical Fiber Communications Conference Baltimore, 5—10 March 2000, WG1-2
[2] ［2］Federighi M, Pasquale F D 1995 IEEE Photon. Technol. Lett. 7 303
[3] ［3］Mori A, Ohishi Y, Sudo S 1997 Electron. Lett. 33 863
[4] ［4］Yang J H, Dai S X, Zhou Y F, Wen L, Hu L L, Jiang Z H 2003 J . Appl. Phys. 93 977
[5] ［5］Yang J H, Dai S X, Wen L, Liu Z P, Hu L L, Jiang Z H 2003 Acta Phys. Sin. 52 508 (in Chinese) ［杨建虎、戴世勋、温磊、柳祝平、胡丽丽、姜中宏 2003 物理学报 52 508］
[6] ［6］Chen B Y, Lin Y H, Chen D D, Jiang Z H 2004 Acta Phys. Sin. 54 2374 (in Chinese) ［陈炳炎、刘粤惠、陈东丹、姜中宏 2004 物理学报 54 2374］
[7] ［7］Yamada M, Ono H, Ohishi Y 1998 Electron. Lett. 34 1490
[8] ［8］Fujimoto Y，Nakatsuka M 2001 Appl. Phys. Lett. 40 L279
[9] ［9］Fujimoto Y，Nakatsuka M 2003 Appl. Phys. Lett. 82 3325
[10] ］Okhrimchuk A G, Butvina L N, Dianov E M, Lichkova N V, Zagorodnev V N, Boldvrev K N 2008 Opt. Lett. 33 2182
[11] ］Ruan J, Su L B, Qiu J R, Chen D P, Xu J 2009 Opt. Exp. 17 5163
[12] ］Su L B, Dong Y J, Yang W Q, Zhou G Q, Zhou S M, Zhao G J, Xu J 2004 J. Synth. Cryst. 33 88 (in Chinese) ［苏良碧、董永军、杨卫桥、周国清、周圣明、赵广军、徐军 2004 人工晶体学报 33 88］
[13] ］Peng M Y, Qiu J R, Chen D P, Meng X G, Yang I Y, Jiang X W, Zhu C S 2008 Opt. Lett. 29 1998
[14] ］Blasse G, Bril A 1968 J. Chem. Phys. 48 217
[15] ］Srivastava A 1998 J. Lumin. 78 239
[16] ］Bao J X, Zhou S F, Feng G F, Wang X, Lin G, Qiu J R 2007 J. Lumin. 5 699 (in Chinese) ［鲍家兴、周时凤、冯高峰、王玺、林耿、邱建荣 2007 发光学报 5 699］
-
[1] ［1］Flood F A 2000 Proceedings of Optical Fiber Communications Conference Baltimore, 5—10 March 2000, WG1-2
[2] ［2］Federighi M, Pasquale F D 1995 IEEE Photon. Technol. Lett. 7 303
[3] ［3］Mori A, Ohishi Y, Sudo S 1997 Electron. Lett. 33 863
[4] ［4］Yang J H, Dai S X, Zhou Y F, Wen L, Hu L L, Jiang Z H 2003 J . Appl. Phys. 93 977
[5] ［5］Yang J H, Dai S X, Wen L, Liu Z P, Hu L L, Jiang Z H 2003 Acta Phys. Sin. 52 508 (in Chinese) ［杨建虎、戴世勋、温磊、柳祝平、胡丽丽、姜中宏 2003 物理学报 52 508］
[6] ［6］Chen B Y, Lin Y H, Chen D D, Jiang Z H 2004 Acta Phys. Sin. 54 2374 (in Chinese) ［陈炳炎、刘粤惠、陈东丹、姜中宏 2004 物理学报 54 2374］
[7] ［7］Yamada M, Ono H, Ohishi Y 1998 Electron. Lett. 34 1490
[8] ［8］Fujimoto Y，Nakatsuka M 2001 Appl. Phys. Lett. 40 L279
[9] ［9］Fujimoto Y，Nakatsuka M 2003 Appl. Phys. Lett. 82 3325
[10] ］Okhrimchuk A G, Butvina L N, Dianov E M, Lichkova N V, Zagorodnev V N, Boldvrev K N 2008 Opt. Lett. 33 2182
[11] ］Ruan J, Su L B, Qiu J R, Chen D P, Xu J 2009 Opt. Exp. 17 5163
[12] ］Su L B, Dong Y J, Yang W Q, Zhou G Q, Zhou S M, Zhao G J, Xu J 2004 J. Synth. Cryst. 33 88 (in Chinese) ［苏良碧、董永军、杨卫桥、周国清、周圣明、赵广军、徐军 2004 人工晶体学报 33 88］
[13] ］Peng M Y, Qiu J R, Chen D P, Meng X G, Yang I Y, Jiang X W, Zhu C S 2008 Opt. Lett. 29 1998
[14] ］Blasse G, Bril A 1968 J. Chem. Phys. 48 217
[15] ］Srivastava A 1998 J. Lumin. 78 239
[16] ］Bao J X, Zhou S F, Feng G F, Wang X, Lin G, Qiu J R 2007 J. Lumin. 5 699 (in Chinese) ［鲍家兴、周时凤、冯高峰、王玺、林耿、邱建荣 2007 发光学报 5 699］
计量
- 文章访问数: 9167
- PDF下载量: 1490
- 被引次数: 0
下载: