Directional textured dysprosium foils are fabricated by rapid solidification and sequential cold rolling, and the influences of their thickness values and magnetic structures on magnetic properties are analyzed and studied. The results show that magnetic properties of cold-rolled dysprosium foils are better than those of rapid solidification dysprosium foils, and the magnetization and permeability for each of the cold-rolled dysprosium foils are related to the thickness and temperature. Below Curie temperature, the cold-rolled dysprosium foils have obvious soft magnetic properties in a temperature range from 77 K to 4.2 K, the saturation magnetization for each of cold-rolled dysprosium foils increases by 5%－8%, and the saturation magnetization of 0.15-mm-thick cold-rolled dysprosium foil arrives at 2880 kA/m at 4.2 K, and the maximum permeability of cold-rolled 0.10-mm-thick dysprosium foil approaches to 30. The cryogenic magnetization of cold-rolled dysprosium foil with a strong external magnetic field is higher than that of conventional Co-V-Fe below 85 K. The cryogenic magnetic properties of textured dysprosium foils are related to the oxygen content and the orientation degree of (0001) crystal plane. The present study lays the foundation of technology and principle for preparing the chunky directional textured dysprosium soft magnet for cryogenic undulator.
-
Keywords:
- cryogenic undulator /
- texture Dy /
- cold rolling /
- magnetic properties.
[1] 麦振洪 2013 同步辐射光源及其应用 (北京: 科学出版社) 第 90 页
Mai Z H 2013 Synchrotron Radiation and its Applications (Beijing: Science Press) p90 (in Chinese)
[2] 何永周 2015 博士学位论文 (北京: 中国科学院大学)
He Y Z 2015 Ph. D. Dissertation (Beijing: University of Chinese Academy of Sciences) (in Chinese)
[3] Grau A, Casalbuoni S, Gerstl S, Glamann N, Holubek T, Saez de Jauregui D, Voutta R, Boffo C, Gerhard T, Turenne M, Walter W 2016 IEEE Trans. Appl. Supercond. 26 4100804
Google Scholar
[4] Bahrdt J, Gluskin E 2018 Nucl. Instr. Meth. Phys. Res. A 907 149
Google Scholar
[5] 周寿增, 董清飞 1999 超强永磁体 (北京: 冶金工业出版社) 第283页
Zhou S H, Dong Q F 1999 Super Power Permanent Magnet (Beijing: Metallurgical Industry Press) p283 (in Chinese)
[6] 钟文定 2008 技术磁学 (北京: 科学出版社) 第2页
Zhong W D 2008 Technical Magnetism. (Beijing: Science Press) p2 (in Chinese)
[7] Chen C W 1961 J. Appl. Phys. 32 S348
Google Scholar
[8] Barlow D B, Kraus R H, Lobb C T, Menzel M T, Walstrom P L 1992 Nucl. Instr. Meth. Phys. Res. A 313 311
Google Scholar
[9] Bird M D, Bole S, Dixon I, Eyssa Y M, Gao B J, Schneider-Muntau H J 2001 Phys. B: Condens. Matter. 294 639
Google Scholar
[10] Gottschalk S C, Pindroh A L, Quimby D C, Robinson K E, Slater J M 1991 Nucl. Instr. Meth. Phys. Res. A 304 732
Google Scholar
[11] Larbalestier D, Gurevich A, Feldmann D M, Polyanskii A 2001 Nature 414 368
Google Scholar
[12] Mishra S, Därmann C, Lücke K 1984 Acta. Metall. 32 2185
Google Scholar
[13] Murokn A, Solovyov V, Agustsson R, O'Shea F H, Chubar O, Chen Y, Grandsaert T 2014 Nucl. Instr. Meth. Phys. Res. A 735 521
Google Scholar
[14] Rhyne J J, Clark A E 1967 J. Appl. Phys 38 1379
Google Scholar
[15] Swift W, Mathur M 1974 IEEE Trans. Magn. 10 308
Google Scholar
[16] 戴闻 1995 河北师范大学学报 (自然科学版) 19 51
Dai W 1995 J. Hebei Normal Univ.: Nat. Sci. Ed. 19 51
-
图 1 实验Dy样品 (a) Dy轧制片; (b) 冷轧Dy薄片; (c) 速凝Dy薄片
Figure 1. Experiment Dy sample: (a) Dy rolled sheet; (b) cold-rolled Dy foils; (C) strip cooling Dy foils.
图 2 (a) 单晶Dy结构; (b) 冷轧态Dy; (c) 退火态Dy
Figure 2. (a) Three-dimensional structure of single crystal Dy; (b) cold-rolled Dy; (c) annealed Dy.
图 3 X射线衍射图
Figure 3. X-ray diffraction 2θ scans.
图 4 冷轧Dy薄片退火前后的背散射照片 (a) 轧制态Dy; (b) 0.05 mm退火态Dy; (c) 0.075 mm退火态Dy; (d) 0.10 mm退火态Dy
Figure 4. Backscatter photographs of cold-rolled Dy foils before and after annealing: (a) Rolled Dy; (b) 0.05 mm annealed Dy; (c) 0.075 mm annealed Dy; (d) 0.10 mm annealed Dy.
图 5 4.2 K时冷轧Dy薄片[0001]方向磁性能 (a) 磁化曲线; (b) 磁导率
Figure 5. Magnetic properties of [0001] direction for cold-rolled Dy foils at 4.2 K: (a) Magnetization curve; (b) permeability.
图 6 Dy薄片磁化曲线 (a) 77 K; (b) 4.2 K
Figure 6. Magnetization curves of Dy foils: (a) 77 K; (b) 4.2 K.
图 7 冷轧Dy薄片的磁性能 (a) M-T; (b) 磁导率@77 K
Figure 7. Magnetic properties of cold-rolled Dy foils: (a) M-T; (b) permeability @ 77 K.
图 8 77 K冷轧Dy薄片与常规软磁的磁化曲线. *1J22与DTC4磁化曲线测试样环: Φ28 mm × Φ20 mm × 5 mm, H ≤ 0.0125 T为实测数据, H ≥ 0.0125 T为推测数据
Figure 8. M-H curves of cold-rolled Dy foils and conventional soft magnet at 77 K. * ring for M-H curve of conventional 1J22 and DTC4: Φ28 mm × Φ20 mm × 5 mm, M-H curves with H ≤ 0.0125 T are measured data, and the M-H curves with H ≥ 0.0125 T are calculated data.
-
[1] 麦振洪 2013 同步辐射光源及其应用 (北京: 科学出版社) 第 90 页
Mai Z H 2013 Synchrotron Radiation and its Applications (Beijing: Science Press) p90 (in Chinese)
[2] 何永周 2015 博士学位论文 (北京: 中国科学院大学)
He Y Z 2015 Ph. D. Dissertation (Beijing: University of Chinese Academy of Sciences) (in Chinese)
[3] Grau A, Casalbuoni S, Gerstl S, Glamann N, Holubek T, Saez de Jauregui D, Voutta R, Boffo C, Gerhard T, Turenne M, Walter W 2016 IEEE Trans. Appl. Supercond. 26 4100804
Google Scholar
[4] Bahrdt J, Gluskin E 2018 Nucl. Instr. Meth. Phys. Res. A 907 149
Google Scholar
[5] 周寿增, 董清飞 1999 超强永磁体 (北京: 冶金工业出版社) 第283页
Zhou S H, Dong Q F 1999 Super Power Permanent Magnet (Beijing: Metallurgical Industry Press) p283 (in Chinese)
[6] 钟文定 2008 技术磁学 (北京: 科学出版社) 第2页
Zhong W D 2008 Technical Magnetism. (Beijing: Science Press) p2 (in Chinese)
[7] Chen C W 1961 J. Appl. Phys. 32 S348
Google Scholar
[8] Barlow D B, Kraus R H, Lobb C T, Menzel M T, Walstrom P L 1992 Nucl. Instr. Meth. Phys. Res. A 313 311
Google Scholar
[9] Bird M D, Bole S, Dixon I, Eyssa Y M, Gao B J, Schneider-Muntau H J 2001 Phys. B: Condens. Matter. 294 639
Google Scholar
[10] Gottschalk S C, Pindroh A L, Quimby D C, Robinson K E, Slater J M 1991 Nucl. Instr. Meth. Phys. Res. A 304 732
Google Scholar
[11] Larbalestier D, Gurevich A, Feldmann D M, Polyanskii A 2001 Nature 414 368
Google Scholar
[12] Mishra S, Därmann C, Lücke K 1984 Acta. Metall. 32 2185
Google Scholar
[13] Murokn A, Solovyov V, Agustsson R, O'Shea F H, Chubar O, Chen Y, Grandsaert T 2014 Nucl. Instr. Meth. Phys. Res. A 735 521
Google Scholar
[14] Rhyne J J, Clark A E 1967 J. Appl. Phys 38 1379
Google Scholar
[15] Swift W, Mathur M 1974 IEEE Trans. Magn. 10 308
Google Scholar
[16] 戴闻 1995 河北师范大学学报 (自然科学版) 19 51
Dai W 1995 J. Hebei Normal Univ.: Nat. Sci. Ed. 19 51
DownLoad:
Catalog
Metrics
- Abstract views: 3978
- PDF Downloads: 31
- Cited By: 0