In the paper, under 5.6 GPa and 1250−1450 ℃, the Ib-ype diamond single crystals chosen as the seed crystals with different sizes, are synthesized in a cubic anvil at high pressure and high temperature. High-purity Fe-Ni-Co solvents are chosen as the catalysts. High-purity graphite powder (99.99%, purity) is selected as the carbon source. Hexahedral abrasive grade high-quality diamonds of 0.8 mm, 1.5 mm or 2.2 mm in diameter are chosen as seed crystals. The effects of seed crystal size on the growth of gem-diamond single crystal are studied in detail. Firstly, the influence of the change of seed size on the cracking of diamond single crystal is investigated. The crystal growth law of increasing the probability of cracking crystal with larger seed crystal is obtained. It can be attributed to the following two points. i) The residual cross section at the separation of the main crystal from the larger seed crystal is too large, thus reducing the overall compressive strength of the crystal. ii) The growth rate of the diamond crystal synthesized by larger seed crystal is too fast, which leads to the increase of impurities and defects and the decrease of compressive strength of the crystal. The decrease of crystal compressive strength leads to cracks in diamond crystals during cooling and depressurizing. Secondly, in the growth time of 25 hours, the relationships between the growth time and the limit growth rate of the diamond single crystals synthesized by choosing three sizes of seed crystals are investigated. The results show that the high-quality single crystal synthesis efficiency can be improved and the synthesis period can be shortened by selecting large seed crystals. This is because the size of the seed crystal becomes larger at each stage of crystal growth, resulting in the enhancement of the ability of diamond single crystal to receive carbon, so that high-quality diamond single crystals can be grown at a faster growth rate. Thirdly, with the help of scanning electron microscope or optical microscope, we calibrate the surface morphologies of diamond single crystals grown with different-size seed crystals. Using the seed crystals of 0.8 mm, 1.5 mm or 2.2 mm in diameter, high-quality diamond single crystals with smooth surfaces can be synthesized. However, with the increase of seed crystal in size, the surface flatness of the grown crystals tends to decrease and the possibility with which surface defects occur and string inclusions increase. The growth rate of high-quality diamond single crystals grown with larger seed crystals must be strictly controlled. Finally, the N impurity content values of diamond single crystals grown with different seed crystals in size are characterized by Fourier transform infrared measurement. The results show that the N impurity content of the crystal increases with the diamond growing rapidly by selecting larger seed crystal.
[1] Bundy F P, Hall H T, Strong H M, Wentorf Jr R H 1955 Nature 176 51
Google Scholar
[2] Bovenkerk H P, Bundy F P, Hall H T, Strong H M, Wentorf Jr R H 1959 Nature 184 1094
Google Scholar
[3] Strong H M 1963 J. Phys. Chem. 39 2057
Google Scholar
[4] Traore A, Muret P, Fiori A, Eon D, Gheeraert E, Pernot J 2014 Appl. Phys. Lett. 104 052105
Google Scholar
[5] Sumiya H, Toda N, Satoh S 2002 J. Cryst. Growth 237-239 1281
[6] Kanda H 2001 Radiat. Eff. Defects Solids 156 163
Google Scholar
[7] 任泽阳, 张金风, 张进成, 许晟瑞, 张春福, 全汝岱, 郝跃 2017 物理学报 66 208101
Google Scholar
Ren Z Y, Zhang J F, Zhang J C, Xu S D, Zhang C F, Quan R D, Hao Y 2017 Acta Phys. Sin. 66 208101
Google Scholar
[8] 刘银娟, 贺端威, 王培, 唐明君, 许超, 王文丹, 刘进, 刘国端, 寇自立 2017 物理学报 66 038103
Liu Y J, He D W, Wang P, Tang M J, Xu C, Wang W D, Liu J, Liu G D, Kou Z L 2017 Acta Phys. Sin. 66 038103
[9] Liu G Q, Pan X Y 2018 Chin. Phys. B 27 020304
Google Scholar
[10] Wu K P, Ma W F, Sun C X, Chen C Z, Ling L Y, Wang Z G 2018 Chin. Phys. B 27 058101
Google Scholar
[11] Berman L E, Hastings J B, Siddons D P, Koike M, Stojanoffand V, Hart M 1993 Nucl. Instrum. Methods 329 555
Google Scholar
[12] Freund A K 1995 Opt. Eng. 34 432
Google Scholar
[13] Koizumi S, Watanabe K, Hasegawa M, Kanda H 2001 Science 292 1899
Google Scholar
[14] Makino T, Tanimoto S, Hayashi Y, Kato H, Tokuda N, Ogura M, Takeuchi D, Oyama K, Ohashi H, Okushi H, Yamasaki S 2009 Appl. Phys. Lett. 94 262101
Google Scholar
[15] Xiao J W, Yang H Z, Wu X Z, Younus F, Li P, Wen B, Zhang X Y, Wang Y B, Tian Y J 2018 Sci. Adv. 4 8195
[16] Sun S S, Xu Z Z, Cui W, Jia X P, Ma H A 2017 Chin. Phys. B 26 098101
Google Scholar
[17] Wang J K, Li S S, Jiang Q W, Song Y L, Yu K P, Han F, Su T C, Hu M H, Hu Q, Ma H A, Jia X P, Xiao H Y 2018 Chin. Phys. B 27 088102
Google Scholar
[18] Srimongkon K, Ohmagari S, Katoa Y, Amornkitbamrung V, Shikata S I 2016 Diam. Relat. Mater. 63 21
Google Scholar
[19] Palyanov Y N, Borzdov Y M, Kupriyanov I N, Bataleva Y V, Khohkhryakov A F 2015 Diam. Relat. Mater. 58 40
Google Scholar
[20] Li Y, Jia X P, Feng Y G, Fang C, Fan L J, Li Y D, Zeng X, Ma H A 2015 Chin. Phys. B 24 088104
Google Scholar
[21] Zhang H, Li S S, Su T C, Hu M H, Li G H, Man H A, Jia X P 2016 Chin. Phys. B 25 118104
Google Scholar
[22] Xiao H Y, Jia X P, Ma H A, Li S S, Li Y, Zhao M 2010 Chinese Sci. Bull. 55 1372
Google Scholar
[23] 肖宏宇, 秦玉琨, 刘利娜, 鲍志刚, 唐春娟, 孙瑞瑞, 张永胜, 李尚升, 贾晓鹏 2018 物理学报 67 140702
Google Scholar
Xiao H Y, Qin Y K, Liu L N, Bao Z G, Tang C J, Sun R R, Zhang Y S, Li S S, Jia X P 2018 Acta Phys. Sin. 67 140702
Google Scholar
-
图 1 宝石级金刚石单晶的生长组装示意图
Figure 1. Sample assembly to treat Gem-diamond single crystals.
图 2 不同直径的籽晶生长金刚石大单晶的光学显微照片 (a) 0.8 mm; (b) 1.5 mm; (c), (d) 2.2 mm
Figure 2. Optical photos of the diamonds using different seed-crystals in diameters: (a) 0.8 mm; (b) 1.5 mm; (c), (d) 2.2 mm.
图 3 金刚石大单晶及剩余碳源的光学显微照片
Figure 3. Optical photos of the diamonds and the carbon source.
图 4 不同尺寸籽晶生长优质金刚石单晶的极限生长速度与合成时间关系曲线 (a) 0.8 mm; (b) 1.5 mm; (c) 2.2 mm
Figure 4. Curves between the limit growth rate and the synthesis time of the high quality diamonds with different diameters of the seed-crystals: (a) 0.8 mm; (b) 1.5 mm; (c) 2.2 mm.
图 5 不同尺寸籽晶生长金刚石单晶的SEM测试结果
Figure 5. Scanning electron microscope photographs of diamond single crystals using different seed-crystals in diameters.
图 6 金刚石单晶的微区FTIR测试 (a) 图2(a)所示晶体; (b) 图2(b)所示晶体; (c) 图2(c)所示晶体
Figure 6. FTIR curves of diamond single crystals: (a) Diamond crystal of Fig. 2 (a); (b) diamond crystal of Fig. 2 (b); (c) diamond crystal of Fig. 2 (c).
表 1 宝石级金刚石单晶生长组装内各部件名称
Table 1. Part names of gem-diamond sample assembly.
序号 名称 序号 名称 1 叶蜡石块 6 导电金属片 2 白云石衬管 7 石墨发热管 3 反应容器 8 碳素源 4 触媒合金 9 金刚石单晶 5 导电石墨片 10 密封、导电堵头 
DownLoad: CSV
表 2 宝石级金刚石单晶的晶体参数及品质
Table 2. Parameters and quality of gem-diamond single crystals.
样品 籽晶尺寸/mm 晶体尺寸/mm 生长速度/mg·h−1 晶体品质 图2(a) 0.8 4.8 3.7 优质 图2(b) 1.5 4.4 4.2 优质 图2(c) 2.2 5.7 5.3 优质、少量包裹体 图2(d) 2.2 5.4 6.1 劣质、裂晶
DownLoad: CSV
-
[1] Bundy F P, Hall H T, Strong H M, Wentorf Jr R H 1955 Nature 176 51
Google Scholar
[2] Bovenkerk H P, Bundy F P, Hall H T, Strong H M, Wentorf Jr R H 1959 Nature 184 1094
Google Scholar
[3] Strong H M 1963 J. Phys. Chem. 39 2057
Google Scholar
[4] Traore A, Muret P, Fiori A, Eon D, Gheeraert E, Pernot J 2014 Appl. Phys. Lett. 104 052105
Google Scholar
[5] Sumiya H, Toda N, Satoh S 2002 J. Cryst. Growth 237-239 1281
[6] Kanda H 2001 Radiat. Eff. Defects Solids 156 163
Google Scholar
[7] 任泽阳, 张金风, 张进成, 许晟瑞, 张春福, 全汝岱, 郝跃 2017 物理学报 66 208101
Google Scholar
Ren Z Y, Zhang J F, Zhang J C, Xu S D, Zhang C F, Quan R D, Hao Y 2017 Acta Phys. Sin. 66 208101
Google Scholar
[8] 刘银娟, 贺端威, 王培, 唐明君, 许超, 王文丹, 刘进, 刘国端, 寇自立 2017 物理学报 66 038103
Liu Y J, He D W, Wang P, Tang M J, Xu C, Wang W D, Liu J, Liu G D, Kou Z L 2017 Acta Phys. Sin. 66 038103
[9] Liu G Q, Pan X Y 2018 Chin. Phys. B 27 020304
Google Scholar
[10] Wu K P, Ma W F, Sun C X, Chen C Z, Ling L Y, Wang Z G 2018 Chin. Phys. B 27 058101
Google Scholar
[11] Berman L E, Hastings J B, Siddons D P, Koike M, Stojanoffand V, Hart M 1993 Nucl. Instrum. Methods 329 555
Google Scholar
[12] Freund A K 1995 Opt. Eng. 34 432
Google Scholar
[13] Koizumi S, Watanabe K, Hasegawa M, Kanda H 2001 Science 292 1899
Google Scholar
[14] Makino T, Tanimoto S, Hayashi Y, Kato H, Tokuda N, Ogura M, Takeuchi D, Oyama K, Ohashi H, Okushi H, Yamasaki S 2009 Appl. Phys. Lett. 94 262101
Google Scholar
[15] Xiao J W, Yang H Z, Wu X Z, Younus F, Li P, Wen B, Zhang X Y, Wang Y B, Tian Y J 2018 Sci. Adv. 4 8195
[16] Sun S S, Xu Z Z, Cui W, Jia X P, Ma H A 2017 Chin. Phys. B 26 098101
Google Scholar
[17] Wang J K, Li S S, Jiang Q W, Song Y L, Yu K P, Han F, Su T C, Hu M H, Hu Q, Ma H A, Jia X P, Xiao H Y 2018 Chin. Phys. B 27 088102
Google Scholar
[18] Srimongkon K, Ohmagari S, Katoa Y, Amornkitbamrung V, Shikata S I 2016 Diam. Relat. Mater. 63 21
Google Scholar
[19] Palyanov Y N, Borzdov Y M, Kupriyanov I N, Bataleva Y V, Khohkhryakov A F 2015 Diam. Relat. Mater. 58 40
Google Scholar
[20] Li Y, Jia X P, Feng Y G, Fang C, Fan L J, Li Y D, Zeng X, Ma H A 2015 Chin. Phys. B 24 088104
Google Scholar
[21] Zhang H, Li S S, Su T C, Hu M H, Li G H, Man H A, Jia X P 2016 Chin. Phys. B 25 118104
Google Scholar
[22] Xiao H Y, Jia X P, Ma H A, Li S S, Li Y, Zhao M 2010 Chinese Sci. Bull. 55 1372
Google Scholar
[23] 肖宏宇, 秦玉琨, 刘利娜, 鲍志刚, 唐春娟, 孙瑞瑞, 张永胜, 李尚升, 贾晓鹏 2018 物理学报 67 140702
Google Scholar
Xiao H Y, Qin Y K, Liu L N, Bao Z G, Tang C J, Sun R R, Zhang Y S, Li S S, Jia X P 2018 Acta Phys. Sin. 67 140702
Google Scholar
DownLoad:
Catalog
Metrics
- Abstract views: 10707
- PDF Downloads: 108
- Cited By: 0