Recent progress of ion migration in organometal halide perovskite

Wang Ji-Fei; Lin Dong-Xu; Yuan Yong-Bo

doi:10.7498/aps.68.20190853

Abstract

In recent years, metal halide perovskite solar cells have attracted widespread attention due to their unique technological superiority. Remarkable progress of device performance has been achieved in last few years. The certified efficiency has reached 24.2%, which is close to the efficiency of the commercial crystalline silicon solar cells. Halide perovskite is a kind of semiconductor and ionic conductor material, which not only has the ability to transfer charges, but also exhibits the phenomenon of ion migration under an external electric field. Ion migration can directly change the local chemical ratio of perovskite crystals, and can also greatly affect the electrical properties of materials and the working mechanisms of corresponding devices. In this review, the formation mechanism, basic characteristics and effects of ion migration on the working mechanism of the device (such as giant switchable photovoltaic phenomenon, current hysteresis, etc.) are summarized, and then some recent advances in the suppression of ion migration are introduced. Since there exist still many doubts about ion migration in perovskite materials, it is very important to understand the phenomenon of ion migration in perovskite materials in order to promote the development and application of perovskite solar cells.

Keywords:

Authors and contacts

1.
Hunan Key Laboratory of Super Microstructure and Ultrafast Process, School of Physics and Electronics, Central South University, Changsha 410083, China
2.
School of Physics and Electronic Sciences, Hunan Institute of Science and Technology, Yueyang 414006, China

Corresponding author: Yuan Yong-Bo, yuanyb@csu.edu.cn

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 51673218).

FullText HTML : translate this paragraph

References

[1]	Huang J, Shao Y, Dong Q 2015 J. Phys. Chem. Lett. 6 3218 Google Scholar
[2]	Nazeeruddin M K, Snaith H 2015 Mrs. Bull. 40 641 Google Scholar
[3]	Lin Q, Armin A, Nagiri R C R, Burn P L, Meredith P 2015 Nat. Photon. 9 106
[4]	Gong J, Darling S B, You F 2015 Energy Environ. Sci. 8 1953 Google Scholar
[5]	Nrel. gov https://www.nrel.gov/pv/assets/images/efficiency-chart.png [2019-6-27]
[6]	Leo K 2015 Nat. Nanotechnol. 10 574 Google Scholar
[7]	Zhao X, Park N G 2015 Photonics 2 1139 Google Scholar
[8]	Shahbazi M, Wang H 2016 Sol. Energy 123 74 Google Scholar
[9]	Yang B, Dyck O, Ming W, Du M H, Das S, Rouleau C M, Duscher G, Geohegan D B, Xiao K 2016 CS Appl. Mater. Inter. 8 32333 Google Scholar
[10]	Park N G, Grätzel M, Miyasaka T, Zhu K, Emery K 2016 Nat. Energy 1 16152 Google Scholar
[11]	Leijtens T, Eperon G E, Pathak S, Abate A, Lee M M, Snaith H J 2013 Nat. Commun. 4 2885 Google Scholar
[12]	Cao D H, Stoumpos C C, Farha O K, Hupp J T, Kanatzidis M G 2015 J. Am. Chem. Soc. 137 7843 Google Scholar
[13]	Smith I C, Hoke E T, Solis-Ibarra D, McGehee M D, Karunadasa H I 2014 Angew. Chem. Int. Edit. 53 11232 Google Scholar
[14]	Gao P, Bin Mohd Yusoff A R, Nazeeruddin M K 2018 Nat. Commun. 9 5028 Google Scholar
[15]	Zheng F, Saldana-Greco D, Liu S, Rappe A M 2015 J. Phys. Chem. Lett. 6 4862 Google Scholar
[16]	Berry J, Buonassisi T, Egger D A, Hodes G, Kronik L, Loo Y L, Lubomirsky I, Marder S R, Mastai Y, Miller J S, Mitzi D B, Paz Y, Rappe A M, Riess I, Rybtchinski B, Stafsudd O, Stevanovic V, Toney M F, Zitoun D, Kahn A, Ginley D, Cahen D 2015 Adv. Mater. 27 5102 Google Scholar
[17]	Zhao Y, Liang C, Zhang H, Li D, Tian D, Li G, Jing X, Zhang W, Xiao W, Liu Q, Zhang F, He Z 2015 Energy Environ. Sci. 8 1256 Google Scholar
[18]	Egger D A, Edri E, Cahen D, Hodes G 2015 J. Phys. Chem. Lett. 6 279 Google Scholar
[19]	Shao Y, Xiao Z, Bi C, Yuan Y, Huang J 2014 Nat. Commun. 5 5784 Google Scholar
[20]	Snaith H J, Abate A, Ball J M, Eperon G E, Leijtens T, Noel N K, Stranks S D, Wang J T W, Wojciechowski K, Zhang W 2014 J. Phys. Chem. Lett. 5 1511 Google Scholar
[21]	Tress W, Marinova N, Moehl T, Zakeeruddin S M, Nazeeruddin M K, Graetzel M 2015 Energy Environ. Sci. 8 995 Google Scholar
[22]	Unger E L, Hoke E T, Bailie C D, Nguyen W H, Bowring A R, Heumueller T, Christoforo M G, McGehee M D 2014 Energy Environ. Sci. 7 3690 Google Scholar
[23]	Son D Y, Kim S G, Seo J Y, Lee S H, Shin H, Lee D, Park N G 2018 J. Am. Chem. Soc. 140 1358 Google Scholar
[24]	Kim H S, Jang I H, Ahn N, Choi M, Guerrero A, Bisquert J, Park N G 2015 J. Phys. Chem. Lett. 6 4633 Google Scholar
[25]	Wei J, Zhao Y, Li H, Li G, Pan J, Xu D, Zhao Q, Yu D 2014 J. Phys. Chem. Lett. 5 3937 Google Scholar
[26]	Kang D H, Park N G 2019 Adv. Mater. 1805214 Google Scholar
[27]	Liu P, Wang W, Liu S, Yang H, Shao Z 2019 Adv. Energy Mater. 9 1803017 Google Scholar
[28]	Jeon N J, Noh J H, Kim Y C, Yang W S, Ryu S, Seok S I 2014 Nat. Mater. 13 897 Google Scholar
[29]	Wei J, Li H, Zhao Y, Zhou W, Fu R, Leprince-Wang Y, Yu D, Zhao Q 2016 Nano Energy 26 139 Google Scholar
[30]	Zhao Y, Zhou W, Tan H, Fu R, Li Q, Lin F, Yu D, Walters G, Sargent E H, Zhao Q 2017 J. Phys. Chem. C 121 14517 Google Scholar
[31]	Jung H J, Kim D, Kim S, Park J, Dravid V P, Shin B 2018 Adv. Mater. 30 e1802769 Google Scholar
[32]	Wang Q, Shao Y, Dong Q, Xiao Z, Yuan Y, Huang J 2014 Energy Environ. Sci. 7 2359 Google Scholar
[33]	Kim H S, Park N G 2014 J. Phys. Chem. Lett. 5 2927 Google Scholar
[34]	Eames C, Frost J M, Barnes P R, O'Regan B C, Walsh A, Islam M S 2015 Nat. Commun. 6 7497 Google Scholar
[35]	Yuan Y, Wang Q, Shao Y, Lu H, Li T, Gruverman A, Huang J 2016 Adv. Energy Mater. 6 1501803 Google Scholar
[36]	Yang D, Ming W, Shi H, Zhang L, Du M H 2016 Chem. Mater. 28 4349 Google Scholar
[37]	Shao Y, Fang Y, Li T, Wang Q, Dong Q, Deng Y, Yuan Y, Wei H, Wang M, Gruverman A, Shield J, Huang J 2016 Energy Environ. Sci. 9 1752 Google Scholar
[38]	Calado P, Telford A M, Bryant D, Li X, Nelson J, O’Regan B C, Barnes P R F 2016 Nat. Commun. 7 13831 Google Scholar
[39]	Zhang Y, Liu M, Eperon G E, Leijtens T C, McMeekin D, Saliba M, Zhang W, de Bastiani M, Petrozza A, Herz L M, Johnston M B, Lin H, Snaith H J 2015 Mater. Horiz. 2 315 Google Scholar
[40]	Azpiroz J M, Mosconi E, Bisquert J, de Angelis F 2015 Energy Environ. Sci. 8 2118 Google Scholar
[41]	Mizusaki J, Arai K, Fueki K 1983 Solid State Ionics 11 203 Google Scholar
[42]	Xiao Z, Yuan Y, Shao Y, Wang Q, Dong Q, Bi C, Sharma P, Gruverman A, Huang J 2015 Nat. Mater. 14 193 Google Scholar
[43]	Yuan Y, Chae J, Shao Y, Wang Q, Xiao Z, Centrone A, Huang J 2015 Adv. Energy Mater. 5 1500615 Google Scholar
[44]	Zhang Y, Wang Y, Xu Z Q, Liu J, Song J, Xue Y, Wang Z, Zheng J, Jiang L, Zheng C, Huang F, Sun B, Cheng Y B, Bao Q 2016 ACS Nano 10 7031 Google Scholar
[45]	Almora O, Zarazua I, Mas-Marza E, Mora-Sero I, Bisquert J, Garcia-Belmonte G 2015 J. Phys. Chem. Lett. 6 1645 Google Scholar
[46]	Yang J H, Yin W J, Park J S, Wei S H 2016 J. Mater. Chem. A 4 13105 Google Scholar
[47]	Deng X, Wen X, Lau C F J, Young T, Yun J, Green M A, Huang S, Ho-Baillie A W Y 2016 J. Mater. Chem. C 4 9060 Google Scholar
[48]	Haruyama J, Sodeyama K, Han L, Tateyama Y 2015 J. Am. Chem. Soc. 137 10048 Google Scholar
[49]	Zhang T, Chen H, Bai Y, Xiao S, Zhu L, Hu C, Xue Q, Yang S 2016 Nano Energy 26 620 Google Scholar
[50]	Egger D A, Kronik L, Rappe A M 2015 Angew. Chem. Int. Edit. 54 12437 Google Scholar
[51]	Yin W J, Shi T, Yan Y 2014 Appl. Phys. Lett. 104 063903 Google Scholar
[52]	Xiao Z, Du K Z, Meng W, Wang J, Mitzi D B, Yan Y 2017 J. Am. Chem. Soc. 139 6054 Google Scholar
[53]	Polman A, Knight M, Garnett E C, Ehrler B, Sinke W C 2016 Science 35 aad4424
[54]	Ansari M I H, Qurashi A, Nazeeruddin M K 2018 J. Photoch. Photobio. C 35 1 Google Scholar
[55]	Nakazaki J, Segawa H 2018 J. Photoch. Photobio. C 35 74 Google Scholar
[56]	Chakraborty S, Xie W, Mathews N, Sherburne M, Ahuja R, Asta M, Mhaisalkar S G 2017 ACS Energy Lett. 2 837 Google Scholar
[57]	Sun J, Yang J, Lee J I, Cho J H, Kang M S 2018 J. Phys. Chem. Lett. 9 1573 Google Scholar
[58]	Zhang M, Lyu M, Chen P, Hao M, Yun J H, Wang L 2016 Asia-Pac. J. Chem. Eng. 11 392 Google Scholar
[59]	Liu C, Li W, Fan J, Mai Y 2018 J. Energy Chem. 27 1054 Google Scholar
[60]	Liang L, Gao P 2018 Adv. Sci. 5 1700331 Google Scholar
[61]	Pazoki M, Edvinsson T 2018 Sustain. Energ. Fuels 2 1430 Google Scholar
[62]	Ganose A M, Savory C N, Scanlon D O 2017 Chem. Commun. 53 20
[63]	Chatterjee S, Pal A J 2018 J. Mater. Chem. A 6 3793 Google Scholar
[64]	Yang B, Pan W, Wu H, Niu G, Yuan J H, Xue K H, Yin L, Du X, Miao X S, Yang X, Xie Q, Tang J 2019 Nat. Commun. 10 1989 Google Scholar
[65]	Li Q, Yin L, Chen Z, Deng K, Luo S, Zou B, Wang Z, Tang J, Quan Z 2019 Inorg. Chem. 58 1621 Google Scholar
[66]	Cheng Y, Li H W, Qing J, Yang Q D, Guan Z, Liu C, Cheung S H, So S K, Lee C S, Tsang S W 2016 J. Mater. Chem. A 4 12748 Google Scholar
[67]	Dhar J, Sil S, Dey A, Sanyal D, Ray P P 2017 J. Phys. Chem. C 121 5515
[68]	Kuku T A 1998 Thin Solid Films 325 246 Google Scholar
[69]	Leijtens T, Hoke E T, Grancini G, Slotcavage D J, Eperon G E, Ball J M, De Bastiani M, Bowring A R, Martino N, Wojciechowski K, McGehee M, Snaith H J, Petrozza A 2015 Adv. Energy Mater. 5 1500962 Google Scholar
[70]	Li C, Tscheuschner S, Paulus F, Hopkinson P E, Kiessling J, Kohler A, Vaynzof Y, Huettner S 2016 Adv. Mater. 28 2446 Google Scholar
[71]	de Bastiani M, Dell'Erba G, Gandini M, D'Innocenzo V, Neutzner S, Kandada A R S, Grancini G, Binda M, Prato M, Ball J M, Caironi M, Petrozza A 2016 Adv. Energy Mater. 6 1501453 Google Scholar
[72]	Zhang H M, Lin H, Liang C J, Liu H, Liang J J, Zhao Y, Zhang W G, Sun M J, Xiao W K, Li H, Polizzi S, Li D, Zhang F J, He Z Q, Choy W C H 2015 Adv. Funct. Mater. 25 7226 Google Scholar
[73]	Xu J, Buin A, Ip A H, Li W, Voznyy O, Comin R, Yuan M, Jeon S, Ning Z, McDowell J J, Kanjanaboos P, Sun J P, Lan X, Quan L N, Kim D H, Hill I G, Maksymovych P, Sargent E H 2015 Nat. Commun. 6 7081 Google Scholar
[74]	Liu N, Yam C 2018 Phys. Chem. Chem. Phys. 20 6800 Google Scholar
[75]	Zhao Y, Zhou W, Ma W, Meng S, Li H, Wei J, Fu R, Liu K, Yu D, Zhao Q 2016 ACS Energy Lett. 1 266 Google Scholar
[76]	Tian Y, Peter M, Unger E, Abdellah M, Zheng K, Pullerits T, Yartsev A, Sundström V, Scheblykin I G 2015 Phys. Chem. Chem. Phys. 17 24978 Google Scholar
[77]	Chen S, Wen X, Sheng R, Huang S, Deng X, Green M A, Ho-Baillie A 2016 ACS Appl. Mater. Inter. 8 5351 Google Scholar
[78]	Zhang W, Burlakov V M, Graham D J, Leijtens T, Osherov A, Bulović V, Snaith H J, Ginger D S, Stranks S D 2016 Nat. Commun. 7 11683 Google Scholar
[79]	Hu M, Bi C, Yuan Y, Bai Y, Huang J 2016 Adv. Sci. 3 1500301 Google Scholar
[80]	Walsh A, Scanlon D O, Chen S, Gong X, Wei S H 2015 Angew. Chem. 127 1811 Google Scholar
[81]	Johnston M B, Herz L M 2016 Accounts Chem. Res. 49 146
[82]	Xiao Z, Yuan Y, Wang Q, Shao Y, Bai Y, Deng Y, Dong Q, Hu M, Bi C, Huang J 2016 Mater. Sci. Engin. R-Reports 101 1 Google Scholar
[83]	Stranks S D, Nayak P K, Zhang W, Stergiopoulos T, Snaith H J 2015 Angew. Chem. Int. Edit. 54 3240 Google Scholar
[84]	Richardson G, O'Kane S E, Niemann R G, Peltola T A, Foster J M, Cameron P J, Walker A B 2016 Energy Environ. Sci. 9 1476 Google Scholar
[85]	van Reenen S, Kemerink M, Snaith H J 2015 J. Phys. Chem. Lett. 6 3808 Google Scholar
[86]	Hoke E T, Slotcavage D J, Dohner E R, Bowring A R, Karunadasa H I, McGehee M D 2015 Chem. Sci. 6 613 Google Scholar
[87]	Hentz O, Zhao Z, Gradecak S 2016 Nano Lett. 16 1485 Google Scholar
[88]	Bag M, Renna L A, Adhikari R Y, Karak S, Liu F, Lahti P M, Russell T P, Tuominen M T, Venkataraman D 2015 J. Am. Chem. Soc. 137 13130
[89]	Bae S, Kim S, Lee S W, Cho K J, Park S, Lee S, Kang Y, Lee H S, Kim D 2016 J. Phys. Chem. Lett. 7 3091 Google Scholar
[90]	Yuan Y, Huang J 2016 Accounts Chem. Res. 49 286 Google Scholar
[91]	Lee H, Ko D, Lee C 2019 ACS Appl. Mater. Inter. 11 11667 Google Scholar
[92]	Zhang H, Fu X, Tang Y, Wang H, Zhang C, Yu W W, Wang X, Zhang Y, Xiao M 2019 Nat. Commun. 10 1088 Google Scholar
[93]	Leijtens T, Eperon G E, Barker A J, Grancini G, Zhang W, Ball J M, Kandada A R S, Snaith H J, Petrozza A 2016 Energy Environ. Sci. 9 3472 Google Scholar
[94]	Zhang T, Meng X, Bai Y, Xiao S, Hu C, Yang Y, Chen H, Yang S 2017 J. Mater. Chem. A 5 1103 Google Scholar
[95]	Yuan H, Debroye E, Janssen K, Naiki H, Steuwe C, Lu G, Moris M, Orgiu E, Uji I H, de Schryver F, Samori P, Hofkens J, Roeffaers M 2016 J. Phys. Chem. Lett. 7 561 Google Scholar
[96]	Yang T Y, Jeon N J, Shin H W, Shin S S, Kim Y Y, Seo J 2019 Adv. Sci. 1900528 Google Scholar
[97]	Fedwa El-Mellouhi S N R, Marzouk A, Kabalan L, Belaidi A, Merzougui B, Tabet N, Alharbi F H 2019 J. Mater. Chem. C 7 5299 Google Scholar
[98]	Jiang L, Lu J, Raga S R, Sun J, Lin X, Huang W, Huang F, Bach U, Cheng Y B 2019 Nano Energy 58 687 Google Scholar
[99]	Wu Q, Wu Z Y, Rudd P N, Shao Y C, Dai X Z, Wei H T, Zhao J J, FangY J, Wang Q, Liu Y, Deng Y H, Xiao X, Feng Y X, Huang J S 2019 Sci. Adv. 5 eaav8925 Google Scholar
[100]	Ferdani D W, Pering S R, Ghosh D, Kubiak P, Walker A B, Lewis S E, Johnson A L, Baker P J, Islam M S, Cameron P J 2019 Energy Environ. Sci.Google Scholar
[101]	Fu W, Liu H, Shi X, Zuo L, Li X, Jen A K Y 2019 Adv. Funct. Mater. 29 1900221
[102]	Huang F, Jiang L, Pascoe A R, Yan Y, Bach U, Spiccia L, Cheng Y B 2016 Nano Energy 27 509 Google Scholar
[103]	Shi J, Xu X, Zhang H, Luo Y, Li D, Meng Q 2015 Appl. Phys. Lett. 107 163901 Google Scholar
[104]	Nie W, Blancon J C, Neukirch A J, Appavoo K, Tsai H, Chhowalla M, Alam M A, Sfeir M Y, Katan C, Even J, Tretiak S, Crochet J J, Gupta G, Mohite A D 2016 Nat. Commun. 7 11574 Google Scholar
[105]	Yang T Y, Gregori G, Pellet N, Gratzel M, Maier J 2015 Angew. Chem. 54 7905 Google Scholar
[106]	Jeangros Q, Duchamp M, Werner J, Kruth M, Dunin-Borkowski R E, Niesen B, Ballif C, Hessler-Wyser A 2016 Nano Lett. 16 7013 Google Scholar
[107]	Akbulatov A F, Frolova L A, Griffin M P, Gearba I R, Dolocan A, Vanden Bout D A, Tsarev S, Katz E A, Shestakov A F, Stevenson K J, Troshin P A 2017 Adv. Energy Mater. 7 1700476 Google Scholar
[108]	Carrillo J, Guerrero A, Rahimnejad S, Almora O, Zarazua I, Mas-Marza E, Bisquert J, Garcia-Belmonte G 2016 Adv. Energy Mater. 6 1502246 Google Scholar
[109]	Zohar A, Kedem N, Levine I, Zohar D, Vilan A, Ehre D, Hodes G, Cahen D 2016 J. Phys. Chem. Lett. 7 191
[110]	Kato Y, Ono L K, Lee M V, Wang S, Raga S R, Qi Y 2015 Adv. Mater. Interf. 2 1500195 Google Scholar
[111]	Zhao J, Zheng X, Deng Y, Li T, Shao Y, Gruverman A, Shield J, Huang J 2016 Energy Environ. Sci. 9 3650 Google Scholar
[112]	Dong X, Fang X, Lü M, Lin B, Zhang S, Ding J, Yuan N 2015 J. Mater. Chem. A 3 5360 Google Scholar
[113]	Soe Chan Myae M, Nie W, Stoumpos Constantinos C, Tsai H, Blancon J C, Liu F, Even J, Marks Tobin J, Mohite Aditya D, Kanatzidis Mercouri G 2018 Adv. Energy Mater. 8 1700979
[114]	Jiang Q, Zhang X, You J 2018 Small 14 e1801154 Google Scholar
[115]	Chen Q, de Marco N, Yang Y, Song T B, Chen C C, Zhao H, Hong Z, Zhou H, Yang Y 2015 Nano Today 10 355 Google Scholar
[116]	Yun J S, Seidel J, Kim J, Soufiani A M, Huang S, Lau J, Jeon N J, Seok S I, Green M A, Ho-Baillie A 2016 Adv. Energy Mater. 6 1600330 Google Scholar
[117]	Zhang T, Long M, Yan K, Qin M, Lu X, Zeng X, Cheng C M, Wong K S, Liu P, Xie W, Xu J 2017 Adv. Energy Mater. 7 1700118 Google Scholar
[118]	Meggiolaro D, Mosconi E, de Angelis F 2019 ACS Energy Lett. 4 779 Google Scholar
[119]	Xing J, Wang Q, Dong Q, Yuan Y, Fang Y, Huang J 2016 Phys.Chem. Chem. Phys. 18 30484 Google Scholar
[120]	Xiao Z, Dong Q, Bi C, Shao Y, Yuan Y, Huang J 2014 Adv. Mater. 26 6503 Google Scholar
[121]	Yang M, Zhang T, Schulz P, Li Z, Li G, Kim D H, Guo N, Berry J J, Zhu K, Zhao Y 2016 Nat. Commun. 7 12305 Google Scholar
[122]	Guo P, Ye Q, Yang X, Zhang J, Xu F, Shchukin D, Wei B, Wang H 2019 J. Mater. Chem. A 7 2497 Google Scholar
[123]	Xie C, Zhou C, Yang B, Shen L, Ke L, Ding L, Yuan Y 2019 Appl. Phys. Express 12 064006 Google Scholar
[124]	Bi C, Shao Y, Yuan Y, Xiao Z, Wang C, Gao Y, Huang J 2014 J. Mater. Chem. A 2 18508 Google Scholar
[125]	Zhao Y, Zhao Y, Zhou W, Li Q, Fu R, Yu D, Zhao Q 2018 ACS Appl. Mater. Inter. 10 33205 Google Scholar
[126]	Li X, Zhang W, Wang Y C, Zhang W, Wang H Q, Fang J 2018 Nat. Commun. 9 3806 Google Scholar
[127]	Wei D, Ma F, Wang R, Dou S, Cui P, Huang H, Ji J, Jia E, Jia X, Sajid S, Elseman A M, Chu L, Li Y, Jiang B, Qiao J, Yuan Y, Li M 2018 Adv. Mater. 30 e1707583 Google Scholar
[128]	Pan W, Wu H, Luo J, Deng Z, Ge C, Chen C, Jiang X, Yin W J, Niu G, Zhu L, Yin L, Zhou Y, Xie Q, Ke X, Sui M, Tang J 2017 Nat. Photon. 11 726 Google Scholar
[129]	Meloni S, Moehl T, Tress W, Franckevicius M, Saliba M, Lee Y H, Gao P, Nazeeruddin M K, Zakeeruddin S M, Rothlisberger U, Graetzel M 2016 Nat. Commun. 7 10334 Google Scholar
[130]	Shi E, Gao Y, Finkenauer B P, Akriti, Coffey A H, Dou L 2018 Chem. Soc. Rev. 47 6046 Google Scholar
[131]	Mosconi E, de Angelis F 2016 ACS Energy Lett. 1 182 Google Scholar
[132]	Eperon G E, Stranks S D, Menelaou C, Johnston M B, Herz L M, Snaith H J 2014 Energy Environ. Sci. 7 982 Google Scholar
[133]	Pang S, Hu H, Zhang J, Lü S, Yu Y, Wei F, Qin T, Xu H, Liu Z, Cui G 2014 Chem. Mater. 26 1485 Google Scholar
[134]	Lan C, Zhao S, Luo J, Fan P 2018 Phys. Chem. Chem. Phys. 20 24339 Google Scholar
[135]	Zhou W, Zhao Y, Zhou X, Fu R, Li Q, Zhao Y, Liu K, Yu D, Zhao Q 2017 J. Phys. Chem. Lett. 8 4122 Google Scholar
[136]	Li Z, Yang M, Park J S, Wei S H, Berry J J, Zhu K 2016 Chem. Mater. 28 284
[137]	Binek A, Hanusch F C, Docampo P, Bein T 2015 J. Phys. Chem. Lett. 6 1249 Google Scholar
[138]	Liao Y, Liu H, Zhou W, Yang D, Shang Y, Shi Z, Li B, Jiang X, Zhang L, Quan L N, Quintero-Bermudez R, Sutherland B R, Mi Q, Sargent E H, Ning Z 2017 J. Am. Chem. Soc. 139 6693
[139]	Jackson P, Wuerz R, Hariskos D, Lotter E, Witte W, Powalla M 2016 Phys. Status Solidi-R. 10 583 Google Scholar
[140]	Chirila A, Reinhard P, Pianezzi F, Bloesch P, Uhl A R, Fella C, Kranz L, Keller D, Gretener C, Hagendorfer H, Jaeger D, Erni R, Nishiwaki S, Buecheler S, Tiwari A N 2013 Nat. Mater. 12 1107 Google Scholar
[141]	Bu T, Liu X, Zhou Y, Yi J, Huang X, Luo L, Xiao J, Ku Z, Peng Y, Huang F, Cheng Y B, Zhong J 2017 Energy Environ. Sci. 10 2509 Google Scholar
[142]	Nam J K, Chai S U, Cha W, Choi Y J, Kim W, Jung M S, Kwon J, Kim D, Park J H 2017 Nano Lett. 17 2028 Google Scholar
[143]	Liu X, Zhang Y, Shi L, Liu Z, Huang J, Yun J S, Zeng Y, Pu A, Sun K, Hameiri Z, Stride J A, Seidel J, Green M A, Hao X 2018 Adv. Energy Mater. 8 1800138
[144]	Wang P, Wang J, Zhang X, Wang H, Cui X, Yuan S, Lu H, Tu L, Zhan Y, Zheng L 2018 J. Mater. Chem. A 6 15853 Google Scholar
[145]	Li Y, Duan J, Yuan H, Zhao Y, He B, Tang Q 2018 Solar. Rrl. 2 1800164 Google Scholar
[146]	Tsai H, Nie W, Blancon J C, Stoumpos C C, Asadpour R, Harutyunyan B, Neukirch A J, Verduzco R, Crochet J J, Tretiak S, Pedesseau L, Even J, Alam M A, Gupta G, Lou J, Ajayan P M, Bedzyk M J, Kanatzidis M G, Mohite A D 2016 Nature 536 312 Google Scholar
[147]	Wang Z, Lin Q, Chmiel F P, Sakai N, Herz L M, Snaith H J 2017 Nat. Energy 2 17135 Google Scholar
[148]	Grancini G, Roldán-Carmona C, Zimmermann I, Mosconi E, Lee X, Martineau D, Narbey S, Oswald F, de Angelis F, Graetzel M, Nazeeruddin M K 2017 Nat. Commun. 8 15684 Google Scholar
[149]	Chao L, Niu T, Xia Y, Ran X, Chen Y, Huang W 2019 J. Phys. Chem. Lett. 10 1173 Google Scholar
[150]	Ye T, Bruno A, Han G, Koh T M, Li J, Jamaludin N F, Soci C, Mhaisalkar S G, Leong W L 2018 Adv. Funct. Mater. 28 1801654 Google Scholar
[151]	Liu G, Zheng H, Xu X X, Zhu L, Alsaedi A, Hayat T, Pan X, Dai S 2018 J. Mater. Chem. A 6 18067 Google Scholar
[152]	Koh T M, Shanmugam V, Guo X T, Lim S S, Filonik O, Herzig E M, Müller-Buschbaum P, Swamy V, Chien S T, Mhaisalkar S G, Mathews N 2018 J. Mater. Chem. A 6 2122−2128 Google Scholar
[153]	Lin Y, Bai Y, Fang Y, Wang Q, Deng Y, Huang J 2017 ACS Energy Lett. 2 1571 Google Scholar
[154]	Xiao X, Dai J, Fang Y, Zhao J, Zheng X, Tang S, Rudd P N, Zeng X C, Huang J 2018 ACS Energy Lett. 3 684 Google Scholar
[155]	Song J, Li J, Li X, Xu L, Dong Y, Zeng H 2015 Adv. Mater. 27 7162 Google Scholar
[156]	Wang N, Cheng L, Ge R, Zhang S, Miao Y, Zou W, Yi C, Sun Y, Cao Y, Yang R 2016 Nat. Photon. 10 699 Google Scholar
[157]	Shang Q, Wang Y, Zhong Y, Mi Y, Qin L, Zhao Y, Qiu X, Liu X, Zhang Q 2017 J. Phys. Chem. Lett. 8 4431 Google Scholar
[158]	Zou W, Li R, Zhang S, Liu Y, Wang N, Cao Y, Miao Y, Xu M, Guo Q, Di D, Zhang L, Yi C, Gao F, Friend R H, Wang J, Huang W 2018 Nat. Commun. 9 608 Google Scholar
[159]	Yang X, Zhang X, Deng J, Chu Z, Jiang Q, Meng J, Wang P, Zhang L, Yin Z, You J 2018 Nat. Commun. 9 570 Google Scholar
[160]	Yan J, Qiu W, Wu G, Heremans P, Chen H 2018 J. Mater. Chem. A 6 11063 Google Scholar
[161]	Zhang X, Munir R, Xu Z, Liu Y, Tsai H, Nie W, Li J, Niu T, Smilgies D M, Kanatzidis M G, Mohite A D, Zhao K, Amassian A, Liu S F 2018 Adv. Mater. 30 e1707166 Google Scholar
[162]	Liu G, Zheng H, Xu X, Xu S, Zhang X, Pan X, Dai S 2019 Adv. Funct. Mater. 1807565 Google Scholar
[163]	Zheng H, Liu G, Zhu L, Ye J, Zhang X, Alsaedi A, Hayat T, Pan X, Dai S 2018 Adv. Energy. Mater. 8 1800051 Google Scholar
[164]	Cho Y, Soufiani A M, Yun J S, Kim J, Lee D S, Seidel J, Deng X, Green M A, Huang S, Ho-Baillie A W Y 2018 Adv. Energy Mater. 8 1703392
[165]	Li M H, Yeh H H, Chiang Y H, Jeng U S, Su C J, Shiu H W, Hsu Y J, Kosugi N, Ohigashi T, Chen Y A, Shen P S, Chen P, Guo T F 2018 Adv. Mater. 30 e1801401 Google Scholar
[166]	Wang F, Jiang X, Chen H, Shang Y, Liu H, Wei J, Zhou W, He H, Liu W, Ning Z 2018 Joule 2 2732 Google Scholar
[167]	Peng W, Yin J, Ho K T, Ouellette O, de Bastiani M, Murali B, El Tall O, Shen C, Miao X, Pan J, Alarousu E, He J H, Ooi B S, Mohammed O F, Sargent E, Bakr O M 2017 Nano Lett. 17 4759 Google Scholar
[168]	Liu M, Johnston M B, Snaith H J 2013 Nature 501 395 Google Scholar

Cited By

图 1 (a)典型的平面型钙钛矿电池正反扫I-V曲线图, 扫描速度为0.20 V/s, I-V曲线正反扫不重合, 表现出电流迟滞现象^[28]; (b)影响电流迟滞的因素和(c)导致电流迟滞的可能原因

Figure 1. (a) Typical I-V character of the planner structure perovskite solar cell with the scan rate was 0.20 V/s, which expressived the obvious hysteresis; (b) the parameters lead to the hysteresis and (c) the possible reasons responsible for the hysteresis.

DownLoad: Full-Size Img PowerPoint

图 2 (a), (b), 用于测试可翻转光伏效应的垂直结构钙钛矿器件示意图以及器件在–2.5 V到2.5 V之间以0.14 V/s速度扫描时的I-V曲线, 显示出可翻转的光伏效应; (c), (d)分别为原位观察横向结构器件电极化过程时的材料变化的设备示意图和极化过程中钙钛矿材料变化的光学显微镜图, 其中极化电场强度约为1.2 V/μm^[42]; (e)极化前后KPFM测试的钙钛矿薄膜的表面势图; (f) 横向器件Au/MAPbI₃/Au极化(1.2 V/µm, 100 s)前后材料的能级结构示意图^[43]; (g)第一性原理计算的I^–离子在MAPbI₃钙钛矿构成单元${\rm{Pb}}{{\rm{I}}_6^{4-}}$八面体中沿着I^–-I^–边界的迁移路径图^[34]

Figure 2. (a), (b) Diagram of the lateral structure perovskite device used to test the giant switchable photovoltaic effect and the I-V curve at a speed of 0.14 V/s between –2.5 V and 2.5 V, showing a switchable photovoltaic effect; (c), (d) illustration of the set-up used for in situ monitoring the material changes of perovskite films under electric poling process and the corresponding optical microscope photos of perovskite materials, in which the electric field applied on the perovskite film was about 1.2 V/μm^[42]; (e) KPFM potential images of the MAPbI₃ thin films before and after electrical poling (1.2 V/µm, 100 s); (f) schematic diagram of the energy level of the lateral device Au/MAPbI₃/Au before and after the polarization^[43]; (g) the migration path calculated by the first principle for I^– ions in the ${\rm{Pb}}{{\rm{I}}_6^{4-}}$ octahedron, which is the constituent unit of the MAPbI₃, along the I^–-I^– boundary^[34].

DownLoad: Full-Size Img PowerPoint

图 3 晶体中与离子移动相关的Schottky缺陷(a)和Frankel缺陷(b)的示意图

Figure 3. Illustrative diagrams of Schottky defects (a) and Frankel defect (b) related to ion migration in crystals.

DownLoad: Full-Size Img PowerPoint

图 4 MAPbI₃钙钛矿材料中的可迁移离子、缺陷、填隙和杂质离子及其可能迁移的路径示意图, 包括I空位(a), ${\rm{I}}_{\rm{i}}^ - $填隙(b), MA空位(c), ${\rm{MA}}_{\rm{i}}^ + $填隙(d), 以及I离子、MA离子和其他存在的杂质离子(e)

Figure 4. Schematic illustration ofmobile ions, defects, interstitial and impurity ions in MAPbI₃ and their possible migration paths, including, I vacancies (a), interstitialI ions (b), MA vacancies (c), interstitial MA ions (d), I ions, MA ions, and extrinsic impurities (e)

DownLoad: Full-Size Img PowerPoint

图 5 (a) 钙钛矿晶体结构图; (b) 钙钛矿中Pb-I平面中I^–离子移动路径和(c) MA-I平面中MA⁺离子移动的路径^[34]; 各种缺陷迁移路径(d) ${\rm{V}}_{\rm{I}}^ + $, (e) ${\rm{V}}_{{\rm{MA}}}^ - $, (f) ${\rm{V}}_{{\rm{Pb}}}^{2 - }$和碘填隙迁移路径(g) I_I^[40]

Figure 5. (a) Structure diagram of perovskite crystal; migration paths for I^– ion in Pb-I plane (b) and MA⁺ ion in MA-I plane (c)^[34]; diffusion pathsfor ${\rm{V}}_{\rm{I}}^ + $ (d), ${\rm{V}}_{{\rm{MA}}}^ - $ (e), ${\rm{V}}_{{\rm{Pb}}}^{2 - }$ (f) and interstitial iodine ion I_I (g) respectively^[40].

DownLoad: Full-Size Img PowerPoint

图 6 (a) PTIR显微镜下MAPbI₃薄膜在1.6 V/μm电场极化100和200 s前后, MA⁺离子的分布图, 其中电极间距为100 μm^[43]; (b)实验中用XPS方法于测试元素分布的横向器件和实验装置示意图及测得的从阳极到阴极之间的I/Pb比例分布图(c), 施加的直流电压为1 V, 持续时间30 min, 两电极间的横向距离为200 μm, 其中位置“0”为接近正极处, 位置“8”为接近阴极处^[70]; (d)横向器件中具有PbI₂条形区域的SEM和XRD分析, 对横向结构的MAPbI₃薄膜电场极化后具有典型的PbI₂条形区域的SEM图(d)和极化前后的XRD图(e); (f), (h)EDX测试下的具有PbI₂条形区域的横向钙钛矿器件的碘元素(f)和铅元素(h)分布图; (g), (i) 分别为碘元素和铅元素在(f), (h) 白线处的浓度变化曲线^[35]

Figure 6. (a) Corresponding PTIR images for the CH₃ asymmetric deformation absorption of the methylammonium ion (1468 cm^–1) obtained before, after 100 s and after 200 s electrical poling, respectively. The poling field was 1.6 V/µm and the distance between the electrode is 100 μm^[43]. (b) Illustration of the set-up for characterization of elements distribution using a lateral structure with XPS method and the obtained I/Pb ration against position from anode side to cathode side (c). The applied DC voltage is 1 V for 30 min. The lateral distance between two electrodes is 200 µm. Position 0 is near the anode and position 8 is near cathode side^[70]. (d) SEM and XRD study of the lateral devices with a PbI₂ thread. By electric polarization of MAPbI₃ films with lateral symmetric electrode structure, SEM image (d) of a typical PbI₂ thread, (e) XRD spectra of the MAPbI₃ film before and after the formation of a PbI₂ thread. (f), (h) The distribution diagram of iodine (f) and lead element (h) of lateral perovskite device with PbI₂ thread line under energy dispersion X-ray (EDX) test. (g), (i) The concentration curves of iodine (g) and lead (i) at the white line in Figs. (f) and (h), respectively^[35].

DownLoad: Full-Size Img PowerPoint

图 7 (a) MAPbI₃合成简图; (b) 红色区域为MAPbI₃中达到热力学平衡生长时的热力学稳定区域; (c) MAPbI₃中化学势在A, B, C (图7(b)中A, B, C处)位置时内部点缺陷的形成能, 虚线代表具有更高形成能的缺陷; (d), (e) 分别为通过计算得到的MAPbI₃钙钛矿中内部电子受体和给体的传输能级^[51]

Figure 7. (a) Schematic diagram of the MAPbI₃ unit cell. (b) The thermodynamic stability range for equilibriμm growth of MAPbI₃ is in the red region. The formation energies of intrinsic point defects in MAPbI₃ at chemical potentials A, B, and C shown in (c), where defects with much high formation energies have displayed as dashed lines. The calculated transition energy levels of (d) intrinsic acceptors and (e) intrinsic donors in MAPbI₃. Dashed lines stand for the defects that have much higher formation energy so that they cannot exist^[51].

DownLoad: Full-Size Img PowerPoint

图 8 (a) 短路时离子和带电缺陷迁移对p-i-n器件能带的影响, E_c为导带, E_v为价带, V_bi为内建电场; 带有加号的方格表示碘离子空位; (b)不同偏压条件和时间下计时光电流测量时假设的能级结构图, 导带和价带的变化对应于碘离子空位在不同外加偏压和作用时间下与界面之间的再分布^[34]

Figure 8. (a) Schematic representation indicating the impact of ion vacancy drift on the band energies of a p-i-n device at short circuit conditions. E_c is the conduction band energy, E_v is the valence band energy and V_bi is the built-in potential. The squares with “plus” signs indicate the iodide ion vacancies. Implicit in the diagram is that the vacancies with effective positive charges are balanced by immobile cation vacancies (not shown) with effective negative charges. (b) Hypothesized energy level configurations corresponding to different bias conditions and times during the chrono-photoamperometry measurements. The variation in the conduction and valence bands corresponds to the redistribution of iodide ion vacancies to and from interfaces with different applied potentials and times^[34].

DownLoad: Full-Size Img PowerPoint

图 9 (a)固态薄膜中不同数量外部缺陷情况下典型的离子电导$\ln {\sigma _{\rm{i}}}\text{ -} 1/T$曲线图, 其中E_A是离子迁移的活化能, E_D是热激发点缺陷的形成能; (b)通过变温测试MAPbI₃钙钛矿离子电导, 结合阿伦尼伍兹方程拟合离子迁移活化能E_A^[43]; (c)具有离子迁移过程的卤化物钙钛矿的电化学阻抗谱图, 在低频区域阻抗表现出线性变化, 说明具有离子传输特性, 其等效电路如图中插图, 虚线框中为低频区等效电路图, 图中的W_s是Warburg阻抗单元, R_ct是界面电荷传输阻抗, C_dl是所有在界面聚集的离子相关的德拜层电容^[88]; (d)通过瞬态光电流弛豫时间常数结合阿伦尼乌斯方程拟合离子迁移激活能^[34]

Figure 9. (a) Typical $\ln {\sigma _{\rm{i}}} \text{-} 1/T$ curves for ion conduction in solid with different amount of extrinsic defects, where E_A is the activation energy for ion migration, E_D is the formation energy for thermal-excited point defects. (b) Arrhenius plot of the conductivity of the MAPbI₃ film under dark (blue) and illμmination (red, the light intensity is 0.25 mW/cm)^[43]. (c) Typical Nyquist plot for mixed conductor system with Warburg diffusion as evidence by the linear portion of the low frequency regime. Equivalent circuit diagram was showedin the figure and the dashed line islowfrequency ionic elements. W_s is the Warburg component, R_ct is the interfacial charge transfer and C_dl is modeled as an interfacial an interfacial Debye-layer capacitance^[88]. (d) Calculation of activation energy of ion migration by transient photocurrent combined with Arius drawing method^[34].

DownLoad: Full-Size Img PowerPoint

图 10 (a) MAPb(Br_0.6I_0.4)₃的XRD和PL图, 左图表示MAPb(Br_0.6I_0.4)₃膜在光浸泡前(黑色)和在约50 mW·cm^–2下白光浸泡5 min (红色)以及置于暗态下2 h (蓝色)的XRD图谱, 右图通过打开(457 nm, 15 mW·cm^–2)和关闭激发光(黑暗中5 min后), 光谱可以在这两种状态之间重复循环^[86]; (b) 电场下MAPbI₃和PbI₂之间的可逆转换, 左边为横向MAPbI₃钙钛矿太阳能电池的横截面图, 其中在阳极下方形成PbI₂线, 右图具有PbI₂线移向阴极的侧向MAPbI₃器件的图示, 这是由“区域A/区域B”和“区域B/区域C”界面上分别发生的两组固态化学反应造成^[35]; (c) 极化前(左)和极化后(右)带银电极的钙钛矿横向结构的SEM俯视图; “ + ”和“－”符号表示不同的电极极化^[71]

Figure 10. (a) XRD and PL of MAPb(Br_0.6I_0.4)₃. The black line in the left XRD indicates that the MAPb(Br_0.6I_0.4)₃ film has not been soaked by light, the red line represents the sample soaked for 5 minutes in white light at ~50 mW·cm^–2, and the blue line indicates that it is placed in the dark state 2 hour. On the right, by turning on (457 nm, 15 mW·cm^–2) and turning off the excitation light (after 5 minutes in the dark), the spectrum can be repeated between two states^[86]. (b) Reversible conversion between MAPbI₃ and PbI₂ under electric field. On the left is a cross-sectional view of lateral MAPbI₃ perovskite solar cell in which PbI₂ line is formed below the anode. The image to the right shows a schematic representation of the lateral MAPbI₃ device with the PbI₂ line moving toward the cathode, which is caused by two sets of solid-state chemical reactions that occur at the “A/B” and “Region B/C” interfaces, respectively^[35]. (c) SEM top view of the perovskite transverse structure with silver electrodes before (left) and after polarization (right). The “ + ” and “–” symbols indicate different electrode polarizations^[71].

DownLoad: Full-Size Img PowerPoint

图 11 (a) 大晶粒尺寸(左)和小晶粒尺寸(右)薄膜的温度依赖离子电导性图^[119]; (b) 状态密度(DOS)的DFT计算表明, Pb-I抗静电缺陷引起的深陷阱态(黑色)减少, 并且当PCBM吸附在有缺陷的卤化物上时变得更浅(红色)^[73]; (c) NMR图示, PCBM中特征峰—CH₂—在PCBM + MAI和PCBM + PbI₂中均有位移, 表明碘和PCBM之间的相互作用^[75]; (d) 原位交联有机/钙钛矿薄膜的示意图, ①中具有显着羰基(蓝色)和烯基(红色)基团的TMTA的化学结构, ②在热条件下TMTA的交联聚合, ③TMTA化学锚定到MAPbI₃的晶界, 然后原位交联到连续的网络聚合物^[126]

Figure 11. (a) Temperature-dependent ion conductivity of large grain size (left) and small grain size (right) films figure^[119]. (b) DFT calculations show that the deep trap state (black) caused by Pb-I antistatic defects is reduced and becomes lighter (red) when PCBM is adsorbed on the defective halide^[73]. (c) NMR shows that the characteristic peak —CH₂— in PCBM is shifted in both PCBM + MAI and PCBM + PbI₂, indicating the interaction between iodine and PCBM^[75]. (d) Schematic diagram of in situ cross-linking of organic/perovskite films: ① Chemical structure of TMTA having significant carbonyl (blue) and alkenyl (red) groups; ② crosslinking polymerization of TMTA under hot conditions; ③ TMTA is chemically anchored to the grain boundaries of MAPbI₃ and then crosslinked in situ to the continuous network polymer^[126].

DownLoad: Full-Size Img PowerPoint

图 12 (a) MAPbI₃(黑色方块)和FAPbI₃(红色圆圈)装置下暗稳定性(～20%相对湿度(RH))^[94]; (b)在不同光强下, CsPbI₂Br薄膜的温度依赖离子电导性图, 拟合得离子迁移活化能为常数(～0.45 eV)^[135]; (c) FA_1–_xCs_xPbI₃的温度依赖性XRD图, 纯FAPbI₃的δ-α相转变在约165 ℃发生, 掺15% Cs则δ-α相转变温度降低至约125 ℃^[136]; (d) Cs_xR_1–_xPbBr₃ (R = Li⁺, Na⁺, K⁺和Rb⁺)的XRD图(左)及平均晶粒大小图(右)^[145]

Figure 12. (a) Dark stability (～20% RH) of MAPbI₃ (black squares) and FAPbI₃ (red circles) devices^[94]; (b) the ion mobility activation energy of CsPbI₂Br film is constant (～0.45 eV) under different light intensities^[135]; (c) the temperature-dependent XRD pattern of FA_1–_xCs_xPbI₃, the δ-α phase transition of FAPbI₃ occurs at about 165 ℃, and the δ-α phase transition temperature is reduced to about 125 ℃ when 15% Cs is doped^[136]; (d) XRD pattern (left) and average grain size map (right) of Cs_xR_1–_xPbBr₃ (R = Li⁺, Na⁺, K⁺ and Rb⁺)^[145].

DownLoad: Full-Size Img PowerPoint

表 1 理论计算和实验测试的MAPbI₃中可迁移离子的离子活化能对比

Table 1. Comparison of ion activation energies (E_A) between theoretical calculations and experimental measurements of the migration ions in the MAPbI₃ film.

离子种类	活化能E_A/eV
离子种类	理论计算值	实验测量值
I^–	0.58^[34]	0.60—0.68^[34]
MA⁺	0.84^[34]/0.55^[48]	0.36^[43]
Pb²⁺	2.31^[34]	—
${\rm{V}}_{\rm{i}}^ + $	0.08^[40]/0.32—0.45^[48]	0.60—0.68^[34]
${\rm{V}}_{{\rm{MA}}}^ - $	0.46^[40]/0.57—0.89^[48]	—
${\rm{V}}_{{\rm{pb}}}^{2 - }$	0.80^[40]	—
I_i	0.08(0.16)^[40]	—

DownLoad: CSV

表 2 在化学势分别为A, B, C, 如图7(c)中A, B, C处时, MAPbI₃钙钛矿材料中内部中性点缺陷的形成能(单位: eV)^[51]

Table 2. The formation energies (unit: eV) of the neutral defects in MAPbI₃ at chemical potential points A, B, and C^[51].

位置	I_i	MA_Pb	V_MA	V_Pb	I_MA	I_Pb	MA_i	Pb_A	V_I	Pb_i	MA_I	Pb_I
A	0.23	0.28	0.81	0.29	1.96	1.53	1.39	2.93	1.87	4.24	3.31	5.44
B	0.83	1.15	1.28	1.62	3.01	3.45	0.93	2.51	1.27	2.91	2.25	3.62
C	1.42	1.47	2.01	2.68	4.34	5.10	0.20	1.74	0.67	1.85	0.93	1.97

DownLoad: CSV

[1]	Huang J, Shao Y, Dong Q 2015 J. Phys. Chem. Lett. 6 3218 Google Scholar
[2]	Nazeeruddin M K, Snaith H 2015 Mrs. Bull. 40 641 Google Scholar
[3]	Lin Q, Armin A, Nagiri R C R, Burn P L, Meredith P 2015 Nat. Photon. 9 106
[4]	Gong J, Darling S B, You F 2015 Energy Environ. Sci. 8 1953 Google Scholar
[5]	Nrel. gov https://www.nrel.gov/pv/assets/images/efficiency-chart.png [2019-6-27]
[6]	Leo K 2015 Nat. Nanotechnol. 10 574 Google Scholar
[7]	Zhao X, Park N G 2015 Photonics 2 1139 Google Scholar
[8]	Shahbazi M, Wang H 2016 Sol. Energy 123 74 Google Scholar
[9]	Yang B, Dyck O, Ming W, Du M H, Das S, Rouleau C M, Duscher G, Geohegan D B, Xiao K 2016 CS Appl. Mater. Inter. 8 32333 Google Scholar
[10]	Park N G, Grätzel M, Miyasaka T, Zhu K, Emery K 2016 Nat. Energy 1 16152 Google Scholar
[11]	Leijtens T, Eperon G E, Pathak S, Abate A, Lee M M, Snaith H J 2013 Nat. Commun. 4 2885 Google Scholar
[12]	Cao D H, Stoumpos C C, Farha O K, Hupp J T, Kanatzidis M G 2015 J. Am. Chem. Soc. 137 7843 Google Scholar
[13]	Smith I C, Hoke E T, Solis-Ibarra D, McGehee M D, Karunadasa H I 2014 Angew. Chem. Int. Edit. 53 11232 Google Scholar
[14]	Gao P, Bin Mohd Yusoff A R, Nazeeruddin M K 2018 Nat. Commun. 9 5028 Google Scholar
[15]	Zheng F, Saldana-Greco D, Liu S, Rappe A M 2015 J. Phys. Chem. Lett. 6 4862 Google Scholar
[16]	Berry J, Buonassisi T, Egger D A, Hodes G, Kronik L, Loo Y L, Lubomirsky I, Marder S R, Mastai Y, Miller J S, Mitzi D B, Paz Y, Rappe A M, Riess I, Rybtchinski B, Stafsudd O, Stevanovic V, Toney M F, Zitoun D, Kahn A, Ginley D, Cahen D 2015 Adv. Mater. 27 5102 Google Scholar
[17]	Zhao Y, Liang C, Zhang H, Li D, Tian D, Li G, Jing X, Zhang W, Xiao W, Liu Q, Zhang F, He Z 2015 Energy Environ. Sci. 8 1256 Google Scholar
[18]	Egger D A, Edri E, Cahen D, Hodes G 2015 J. Phys. Chem. Lett. 6 279 Google Scholar
[19]	Shao Y, Xiao Z, Bi C, Yuan Y, Huang J 2014 Nat. Commun. 5 5784 Google Scholar
[20]	Snaith H J, Abate A, Ball J M, Eperon G E, Leijtens T, Noel N K, Stranks S D, Wang J T W, Wojciechowski K, Zhang W 2014 J. Phys. Chem. Lett. 5 1511 Google Scholar
[21]	Tress W, Marinova N, Moehl T, Zakeeruddin S M, Nazeeruddin M K, Graetzel M 2015 Energy Environ. Sci. 8 995 Google Scholar
[22]	Unger E L, Hoke E T, Bailie C D, Nguyen W H, Bowring A R, Heumueller T, Christoforo M G, McGehee M D 2014 Energy Environ. Sci. 7 3690 Google Scholar
[23]	Son D Y, Kim S G, Seo J Y, Lee S H, Shin H, Lee D, Park N G 2018 J. Am. Chem. Soc. 140 1358 Google Scholar
[24]	Kim H S, Jang I H, Ahn N, Choi M, Guerrero A, Bisquert J, Park N G 2015 J. Phys. Chem. Lett. 6 4633 Google Scholar
[25]	Wei J, Zhao Y, Li H, Li G, Pan J, Xu D, Zhao Q, Yu D 2014 J. Phys. Chem. Lett. 5 3937 Google Scholar
[26]	Kang D H, Park N G 2019 Adv. Mater. 1805214 Google Scholar
[27]	Liu P, Wang W, Liu S, Yang H, Shao Z 2019 Adv. Energy Mater. 9 1803017 Google Scholar
[28]	Jeon N J, Noh J H, Kim Y C, Yang W S, Ryu S, Seok S I 2014 Nat. Mater. 13 897 Google Scholar
[29]	Wei J, Li H, Zhao Y, Zhou W, Fu R, Leprince-Wang Y, Yu D, Zhao Q 2016 Nano Energy 26 139 Google Scholar
[30]	Zhao Y, Zhou W, Tan H, Fu R, Li Q, Lin F, Yu D, Walters G, Sargent E H, Zhao Q 2017 J. Phys. Chem. C 121 14517 Google Scholar
[31]	Jung H J, Kim D, Kim S, Park J, Dravid V P, Shin B 2018 Adv. Mater. 30 e1802769 Google Scholar
[32]	Wang Q, Shao Y, Dong Q, Xiao Z, Yuan Y, Huang J 2014 Energy Environ. Sci. 7 2359 Google Scholar
[33]	Kim H S, Park N G 2014 J. Phys. Chem. Lett. 5 2927 Google Scholar
[34]	Eames C, Frost J M, Barnes P R, O'Regan B C, Walsh A, Islam M S 2015 Nat. Commun. 6 7497 Google Scholar
[35]	Yuan Y, Wang Q, Shao Y, Lu H, Li T, Gruverman A, Huang J 2016 Adv. Energy Mater. 6 1501803 Google Scholar
[36]	Yang D, Ming W, Shi H, Zhang L, Du M H 2016 Chem. Mater. 28 4349 Google Scholar
[37]	Shao Y, Fang Y, Li T, Wang Q, Dong Q, Deng Y, Yuan Y, Wei H, Wang M, Gruverman A, Shield J, Huang J 2016 Energy Environ. Sci. 9 1752 Google Scholar
[38]	Calado P, Telford A M, Bryant D, Li X, Nelson J, O’Regan B C, Barnes P R F 2016 Nat. Commun. 7 13831 Google Scholar
[39]	Zhang Y, Liu M, Eperon G E, Leijtens T C, McMeekin D, Saliba M, Zhang W, de Bastiani M, Petrozza A, Herz L M, Johnston M B, Lin H, Snaith H J 2015 Mater. Horiz. 2 315 Google Scholar
[40]	Azpiroz J M, Mosconi E, Bisquert J, de Angelis F 2015 Energy Environ. Sci. 8 2118 Google Scholar
[41]	Mizusaki J, Arai K, Fueki K 1983 Solid State Ionics 11 203 Google Scholar
[42]	Xiao Z, Yuan Y, Shao Y, Wang Q, Dong Q, Bi C, Sharma P, Gruverman A, Huang J 2015 Nat. Mater. 14 193 Google Scholar
[43]	Yuan Y, Chae J, Shao Y, Wang Q, Xiao Z, Centrone A, Huang J 2015 Adv. Energy Mater. 5 1500615 Google Scholar
[44]	Zhang Y, Wang Y, Xu Z Q, Liu J, Song J, Xue Y, Wang Z, Zheng J, Jiang L, Zheng C, Huang F, Sun B, Cheng Y B, Bao Q 2016 ACS Nano 10 7031 Google Scholar
[45]	Almora O, Zarazua I, Mas-Marza E, Mora-Sero I, Bisquert J, Garcia-Belmonte G 2015 J. Phys. Chem. Lett. 6 1645 Google Scholar
[46]	Yang J H, Yin W J, Park J S, Wei S H 2016 J. Mater. Chem. A 4 13105 Google Scholar
[47]	Deng X, Wen X, Lau C F J, Young T, Yun J, Green M A, Huang S, Ho-Baillie A W Y 2016 J. Mater. Chem. C 4 9060 Google Scholar
[48]	Haruyama J, Sodeyama K, Han L, Tateyama Y 2015 J. Am. Chem. Soc. 137 10048 Google Scholar
[49]	Zhang T, Chen H, Bai Y, Xiao S, Zhu L, Hu C, Xue Q, Yang S 2016 Nano Energy 26 620 Google Scholar
[50]	Egger D A, Kronik L, Rappe A M 2015 Angew. Chem. Int. Edit. 54 12437 Google Scholar
[51]	Yin W J, Shi T, Yan Y 2014 Appl. Phys. Lett. 104 063903 Google Scholar
[52]	Xiao Z, Du K Z, Meng W, Wang J, Mitzi D B, Yan Y 2017 J. Am. Chem. Soc. 139 6054 Google Scholar
[53]	Polman A, Knight M, Garnett E C, Ehrler B, Sinke W C 2016 Science 35 aad4424
[54]	Ansari M I H, Qurashi A, Nazeeruddin M K 2018 J. Photoch. Photobio. C 35 1 Google Scholar
[55]	Nakazaki J, Segawa H 2018 J. Photoch. Photobio. C 35 74 Google Scholar
[56]	Chakraborty S, Xie W, Mathews N, Sherburne M, Ahuja R, Asta M, Mhaisalkar S G 2017 ACS Energy Lett. 2 837 Google Scholar
[57]	Sun J, Yang J, Lee J I, Cho J H, Kang M S 2018 J. Phys. Chem. Lett. 9 1573 Google Scholar
[58]	Zhang M, Lyu M, Chen P, Hao M, Yun J H, Wang L 2016 Asia-Pac. J. Chem. Eng. 11 392 Google Scholar
[59]	Liu C, Li W, Fan J, Mai Y 2018 J. Energy Chem. 27 1054 Google Scholar
[60]	Liang L, Gao P 2018 Adv. Sci. 5 1700331 Google Scholar
[61]	Pazoki M, Edvinsson T 2018 Sustain. Energ. Fuels 2 1430 Google Scholar
[62]	Ganose A M, Savory C N, Scanlon D O 2017 Chem. Commun. 53 20
[63]	Chatterjee S, Pal A J 2018 J. Mater. Chem. A 6 3793 Google Scholar
[64]	Yang B, Pan W, Wu H, Niu G, Yuan J H, Xue K H, Yin L, Du X, Miao X S, Yang X, Xie Q, Tang J 2019 Nat. Commun. 10 1989 Google Scholar
[65]	Li Q, Yin L, Chen Z, Deng K, Luo S, Zou B, Wang Z, Tang J, Quan Z 2019 Inorg. Chem. 58 1621 Google Scholar
[66]	Cheng Y, Li H W, Qing J, Yang Q D, Guan Z, Liu C, Cheung S H, So S K, Lee C S, Tsang S W 2016 J. Mater. Chem. A 4 12748 Google Scholar
[67]	Dhar J, Sil S, Dey A, Sanyal D, Ray P P 2017 J. Phys. Chem. C 121 5515
[68]	Kuku T A 1998 Thin Solid Films 325 246 Google Scholar
[69]	Leijtens T, Hoke E T, Grancini G, Slotcavage D J, Eperon G E, Ball J M, De Bastiani M, Bowring A R, Martino N, Wojciechowski K, McGehee M, Snaith H J, Petrozza A 2015 Adv. Energy Mater. 5 1500962 Google Scholar
[70]	Li C, Tscheuschner S, Paulus F, Hopkinson P E, Kiessling J, Kohler A, Vaynzof Y, Huettner S 2016 Adv. Mater. 28 2446 Google Scholar
[71]	de Bastiani M, Dell'Erba G, Gandini M, D'Innocenzo V, Neutzner S, Kandada A R S, Grancini G, Binda M, Prato M, Ball J M, Caironi M, Petrozza A 2016 Adv. Energy Mater. 6 1501453 Google Scholar
[72]	Zhang H M, Lin H, Liang C J, Liu H, Liang J J, Zhao Y, Zhang W G, Sun M J, Xiao W K, Li H, Polizzi S, Li D, Zhang F J, He Z Q, Choy W C H 2015 Adv. Funct. Mater. 25 7226 Google Scholar
[73]	Xu J, Buin A, Ip A H, Li W, Voznyy O, Comin R, Yuan M, Jeon S, Ning Z, McDowell J J, Kanjanaboos P, Sun J P, Lan X, Quan L N, Kim D H, Hill I G, Maksymovych P, Sargent E H 2015 Nat. Commun. 6 7081 Google Scholar
[74]	Liu N, Yam C 2018 Phys. Chem. Chem. Phys. 20 6800 Google Scholar
[75]	Zhao Y, Zhou W, Ma W, Meng S, Li H, Wei J, Fu R, Liu K, Yu D, Zhao Q 2016 ACS Energy Lett. 1 266 Google Scholar
[76]	Tian Y, Peter M, Unger E, Abdellah M, Zheng K, Pullerits T, Yartsev A, Sundström V, Scheblykin I G 2015 Phys. Chem. Chem. Phys. 17 24978 Google Scholar
[77]	Chen S, Wen X, Sheng R, Huang S, Deng X, Green M A, Ho-Baillie A 2016 ACS Appl. Mater. Inter. 8 5351 Google Scholar
[78]	Zhang W, Burlakov V M, Graham D J, Leijtens T, Osherov A, Bulović V, Snaith H J, Ginger D S, Stranks S D 2016 Nat. Commun. 7 11683 Google Scholar
[79]	Hu M, Bi C, Yuan Y, Bai Y, Huang J 2016 Adv. Sci. 3 1500301 Google Scholar
[80]	Walsh A, Scanlon D O, Chen S, Gong X, Wei S H 2015 Angew. Chem. 127 1811 Google Scholar
[81]	Johnston M B, Herz L M 2016 Accounts Chem. Res. 49 146
[82]	Xiao Z, Yuan Y, Wang Q, Shao Y, Bai Y, Deng Y, Dong Q, Hu M, Bi C, Huang J 2016 Mater. Sci. Engin. R-Reports 101 1 Google Scholar
[83]	Stranks S D, Nayak P K, Zhang W, Stergiopoulos T, Snaith H J 2015 Angew. Chem. Int. Edit. 54 3240 Google Scholar
[84]	Richardson G, O'Kane S E, Niemann R G, Peltola T A, Foster J M, Cameron P J, Walker A B 2016 Energy Environ. Sci. 9 1476 Google Scholar
[85]	van Reenen S, Kemerink M, Snaith H J 2015 J. Phys. Chem. Lett. 6 3808 Google Scholar
[86]	Hoke E T, Slotcavage D J, Dohner E R, Bowring A R, Karunadasa H I, McGehee M D 2015 Chem. Sci. 6 613 Google Scholar
[87]	Hentz O, Zhao Z, Gradecak S 2016 Nano Lett. 16 1485 Google Scholar
[88]	Bag M, Renna L A, Adhikari R Y, Karak S, Liu F, Lahti P M, Russell T P, Tuominen M T, Venkataraman D 2015 J. Am. Chem. Soc. 137 13130
[89]	Bae S, Kim S, Lee S W, Cho K J, Park S, Lee S, Kang Y, Lee H S, Kim D 2016 J. Phys. Chem. Lett. 7 3091 Google Scholar
[90]	Yuan Y, Huang J 2016 Accounts Chem. Res. 49 286 Google Scholar
[91]	Lee H, Ko D, Lee C 2019 ACS Appl. Mater. Inter. 11 11667 Google Scholar
[92]	Zhang H, Fu X, Tang Y, Wang H, Zhang C, Yu W W, Wang X, Zhang Y, Xiao M 2019 Nat. Commun. 10 1088 Google Scholar
[93]	Leijtens T, Eperon G E, Barker A J, Grancini G, Zhang W, Ball J M, Kandada A R S, Snaith H J, Petrozza A 2016 Energy Environ. Sci. 9 3472 Google Scholar
[94]	Zhang T, Meng X, Bai Y, Xiao S, Hu C, Yang Y, Chen H, Yang S 2017 J. Mater. Chem. A 5 1103 Google Scholar
[95]	Yuan H, Debroye E, Janssen K, Naiki H, Steuwe C, Lu G, Moris M, Orgiu E, Uji I H, de Schryver F, Samori P, Hofkens J, Roeffaers M 2016 J. Phys. Chem. Lett. 7 561 Google Scholar
[96]	Yang T Y, Jeon N J, Shin H W, Shin S S, Kim Y Y, Seo J 2019 Adv. Sci. 1900528 Google Scholar
[97]	Fedwa El-Mellouhi S N R, Marzouk A, Kabalan L, Belaidi A, Merzougui B, Tabet N, Alharbi F H 2019 J. Mater. Chem. C 7 5299 Google Scholar
[98]	Jiang L, Lu J, Raga S R, Sun J, Lin X, Huang W, Huang F, Bach U, Cheng Y B 2019 Nano Energy 58 687 Google Scholar
[99]	Wu Q, Wu Z Y, Rudd P N, Shao Y C, Dai X Z, Wei H T, Zhao J J, FangY J, Wang Q, Liu Y, Deng Y H, Xiao X, Feng Y X, Huang J S 2019 Sci. Adv. 5 eaav8925 Google Scholar
[100]	Ferdani D W, Pering S R, Ghosh D, Kubiak P, Walker A B, Lewis S E, Johnson A L, Baker P J, Islam M S, Cameron P J 2019 Energy Environ. Sci.Google Scholar
[101]	Fu W, Liu H, Shi X, Zuo L, Li X, Jen A K Y 2019 Adv. Funct. Mater. 29 1900221
[102]	Huang F, Jiang L, Pascoe A R, Yan Y, Bach U, Spiccia L, Cheng Y B 2016 Nano Energy 27 509 Google Scholar
[103]	Shi J, Xu X, Zhang H, Luo Y, Li D, Meng Q 2015 Appl. Phys. Lett. 107 163901 Google Scholar
[104]	Nie W, Blancon J C, Neukirch A J, Appavoo K, Tsai H, Chhowalla M, Alam M A, Sfeir M Y, Katan C, Even J, Tretiak S, Crochet J J, Gupta G, Mohite A D 2016 Nat. Commun. 7 11574 Google Scholar
[105]	Yang T Y, Gregori G, Pellet N, Gratzel M, Maier J 2015 Angew. Chem. 54 7905 Google Scholar
[106]	Jeangros Q, Duchamp M, Werner J, Kruth M, Dunin-Borkowski R E, Niesen B, Ballif C, Hessler-Wyser A 2016 Nano Lett. 16 7013 Google Scholar
[107]	Akbulatov A F, Frolova L A, Griffin M P, Gearba I R, Dolocan A, Vanden Bout D A, Tsarev S, Katz E A, Shestakov A F, Stevenson K J, Troshin P A 2017 Adv. Energy Mater. 7 1700476 Google Scholar
[108]	Carrillo J, Guerrero A, Rahimnejad S, Almora O, Zarazua I, Mas-Marza E, Bisquert J, Garcia-Belmonte G 2016 Adv. Energy Mater. 6 1502246 Google Scholar
[109]	Zohar A, Kedem N, Levine I, Zohar D, Vilan A, Ehre D, Hodes G, Cahen D 2016 J. Phys. Chem. Lett. 7 191
[110]	Kato Y, Ono L K, Lee M V, Wang S, Raga S R, Qi Y 2015 Adv. Mater. Interf. 2 1500195 Google Scholar
[111]	Zhao J, Zheng X, Deng Y, Li T, Shao Y, Gruverman A, Shield J, Huang J 2016 Energy Environ. Sci. 9 3650 Google Scholar
[112]	Dong X, Fang X, Lü M, Lin B, Zhang S, Ding J, Yuan N 2015 J. Mater. Chem. A 3 5360 Google Scholar
[113]	Soe Chan Myae M, Nie W, Stoumpos Constantinos C, Tsai H, Blancon J C, Liu F, Even J, Marks Tobin J, Mohite Aditya D, Kanatzidis Mercouri G 2018 Adv. Energy Mater. 8 1700979
[114]	Jiang Q, Zhang X, You J 2018 Small 14 e1801154 Google Scholar
[115]	Chen Q, de Marco N, Yang Y, Song T B, Chen C C, Zhao H, Hong Z, Zhou H, Yang Y 2015 Nano Today 10 355 Google Scholar
[116]	Yun J S, Seidel J, Kim J, Soufiani A M, Huang S, Lau J, Jeon N J, Seok S I, Green M A, Ho-Baillie A 2016 Adv. Energy Mater. 6 1600330 Google Scholar
[117]	Zhang T, Long M, Yan K, Qin M, Lu X, Zeng X, Cheng C M, Wong K S, Liu P, Xie W, Xu J 2017 Adv. Energy Mater. 7 1700118 Google Scholar
[118]	Meggiolaro D, Mosconi E, de Angelis F 2019 ACS Energy Lett. 4 779 Google Scholar
[119]	Xing J, Wang Q, Dong Q, Yuan Y, Fang Y, Huang J 2016 Phys.Chem. Chem. Phys. 18 30484 Google Scholar
[120]	Xiao Z, Dong Q, Bi C, Shao Y, Yuan Y, Huang J 2014 Adv. Mater. 26 6503 Google Scholar
[121]	Yang M, Zhang T, Schulz P, Li Z, Li G, Kim D H, Guo N, Berry J J, Zhu K, Zhao Y 2016 Nat. Commun. 7 12305 Google Scholar
[122]	Guo P, Ye Q, Yang X, Zhang J, Xu F, Shchukin D, Wei B, Wang H 2019 J. Mater. Chem. A 7 2497 Google Scholar
[123]	Xie C, Zhou C, Yang B, Shen L, Ke L, Ding L, Yuan Y 2019 Appl. Phys. Express 12 064006 Google Scholar
[124]	Bi C, Shao Y, Yuan Y, Xiao Z, Wang C, Gao Y, Huang J 2014 J. Mater. Chem. A 2 18508 Google Scholar
[125]	Zhao Y, Zhao Y, Zhou W, Li Q, Fu R, Yu D, Zhao Q 2018 ACS Appl. Mater. Inter. 10 33205 Google Scholar
[126]	Li X, Zhang W, Wang Y C, Zhang W, Wang H Q, Fang J 2018 Nat. Commun. 9 3806 Google Scholar
[127]	Wei D, Ma F, Wang R, Dou S, Cui P, Huang H, Ji J, Jia E, Jia X, Sajid S, Elseman A M, Chu L, Li Y, Jiang B, Qiao J, Yuan Y, Li M 2018 Adv. Mater. 30 e1707583 Google Scholar
[128]	Pan W, Wu H, Luo J, Deng Z, Ge C, Chen C, Jiang X, Yin W J, Niu G, Zhu L, Yin L, Zhou Y, Xie Q, Ke X, Sui M, Tang J 2017 Nat. Photon. 11 726 Google Scholar
[129]	Meloni S, Moehl T, Tress W, Franckevicius M, Saliba M, Lee Y H, Gao P, Nazeeruddin M K, Zakeeruddin S M, Rothlisberger U, Graetzel M 2016 Nat. Commun. 7 10334 Google Scholar
[130]	Shi E, Gao Y, Finkenauer B P, Akriti, Coffey A H, Dou L 2018 Chem. Soc. Rev. 47 6046 Google Scholar
[131]	Mosconi E, de Angelis F 2016 ACS Energy Lett. 1 182 Google Scholar
[132]	Eperon G E, Stranks S D, Menelaou C, Johnston M B, Herz L M, Snaith H J 2014 Energy Environ. Sci. 7 982 Google Scholar
[133]	Pang S, Hu H, Zhang J, Lü S, Yu Y, Wei F, Qin T, Xu H, Liu Z, Cui G 2014 Chem. Mater. 26 1485 Google Scholar
[134]	Lan C, Zhao S, Luo J, Fan P 2018 Phys. Chem. Chem. Phys. 20 24339 Google Scholar
[135]	Zhou W, Zhao Y, Zhou X, Fu R, Li Q, Zhao Y, Liu K, Yu D, Zhao Q 2017 J. Phys. Chem. Lett. 8 4122 Google Scholar
[136]	Li Z, Yang M, Park J S, Wei S H, Berry J J, Zhu K 2016 Chem. Mater. 28 284
[137]	Binek A, Hanusch F C, Docampo P, Bein T 2015 J. Phys. Chem. Lett. 6 1249 Google Scholar
[138]	Liao Y, Liu H, Zhou W, Yang D, Shang Y, Shi Z, Li B, Jiang X, Zhang L, Quan L N, Quintero-Bermudez R, Sutherland B R, Mi Q, Sargent E H, Ning Z 2017 J. Am. Chem. Soc. 139 6693
[139]	Jackson P, Wuerz R, Hariskos D, Lotter E, Witte W, Powalla M 2016 Phys. Status Solidi-R. 10 583 Google Scholar
[140]	Chirila A, Reinhard P, Pianezzi F, Bloesch P, Uhl A R, Fella C, Kranz L, Keller D, Gretener C, Hagendorfer H, Jaeger D, Erni R, Nishiwaki S, Buecheler S, Tiwari A N 2013 Nat. Mater. 12 1107 Google Scholar
[141]	Bu T, Liu X, Zhou Y, Yi J, Huang X, Luo L, Xiao J, Ku Z, Peng Y, Huang F, Cheng Y B, Zhong J 2017 Energy Environ. Sci. 10 2509 Google Scholar
[142]	Nam J K, Chai S U, Cha W, Choi Y J, Kim W, Jung M S, Kwon J, Kim D, Park J H 2017 Nano Lett. 17 2028 Google Scholar
[143]	Liu X, Zhang Y, Shi L, Liu Z, Huang J, Yun J S, Zeng Y, Pu A, Sun K, Hameiri Z, Stride J A, Seidel J, Green M A, Hao X 2018 Adv. Energy Mater. 8 1800138
[144]	Wang P, Wang J, Zhang X, Wang H, Cui X, Yuan S, Lu H, Tu L, Zhan Y, Zheng L 2018 J. Mater. Chem. A 6 15853 Google Scholar
[145]	Li Y, Duan J, Yuan H, Zhao Y, He B, Tang Q 2018 Solar. Rrl. 2 1800164 Google Scholar
[146]	Tsai H, Nie W, Blancon J C, Stoumpos C C, Asadpour R, Harutyunyan B, Neukirch A J, Verduzco R, Crochet J J, Tretiak S, Pedesseau L, Even J, Alam M A, Gupta G, Lou J, Ajayan P M, Bedzyk M J, Kanatzidis M G, Mohite A D 2016 Nature 536 312 Google Scholar
[147]	Wang Z, Lin Q, Chmiel F P, Sakai N, Herz L M, Snaith H J 2017 Nat. Energy 2 17135 Google Scholar
[148]	Grancini G, Roldán-Carmona C, Zimmermann I, Mosconi E, Lee X, Martineau D, Narbey S, Oswald F, de Angelis F, Graetzel M, Nazeeruddin M K 2017 Nat. Commun. 8 15684 Google Scholar
[149]	Chao L, Niu T, Xia Y, Ran X, Chen Y, Huang W 2019 J. Phys. Chem. Lett. 10 1173 Google Scholar
[150]	Ye T, Bruno A, Han G, Koh T M, Li J, Jamaludin N F, Soci C, Mhaisalkar S G, Leong W L 2018 Adv. Funct. Mater. 28 1801654 Google Scholar
[151]	Liu G, Zheng H, Xu X X, Zhu L, Alsaedi A, Hayat T, Pan X, Dai S 2018 J. Mater. Chem. A 6 18067 Google Scholar
[152]	Koh T M, Shanmugam V, Guo X T, Lim S S, Filonik O, Herzig E M, Müller-Buschbaum P, Swamy V, Chien S T, Mhaisalkar S G, Mathews N 2018 J. Mater. Chem. A 6 2122−2128 Google Scholar
[153]	Lin Y, Bai Y, Fang Y, Wang Q, Deng Y, Huang J 2017 ACS Energy Lett. 2 1571 Google Scholar
[154]	Xiao X, Dai J, Fang Y, Zhao J, Zheng X, Tang S, Rudd P N, Zeng X C, Huang J 2018 ACS Energy Lett. 3 684 Google Scholar
[155]	Song J, Li J, Li X, Xu L, Dong Y, Zeng H 2015 Adv. Mater. 27 7162 Google Scholar
[156]	Wang N, Cheng L, Ge R, Zhang S, Miao Y, Zou W, Yi C, Sun Y, Cao Y, Yang R 2016 Nat. Photon. 10 699 Google Scholar
[157]	Shang Q, Wang Y, Zhong Y, Mi Y, Qin L, Zhao Y, Qiu X, Liu X, Zhang Q 2017 J. Phys. Chem. Lett. 8 4431 Google Scholar
[158]	Zou W, Li R, Zhang S, Liu Y, Wang N, Cao Y, Miao Y, Xu M, Guo Q, Di D, Zhang L, Yi C, Gao F, Friend R H, Wang J, Huang W 2018 Nat. Commun. 9 608 Google Scholar
[159]	Yang X, Zhang X, Deng J, Chu Z, Jiang Q, Meng J, Wang P, Zhang L, Yin Z, You J 2018 Nat. Commun. 9 570 Google Scholar
[160]	Yan J, Qiu W, Wu G, Heremans P, Chen H 2018 J. Mater. Chem. A 6 11063 Google Scholar
[161]	Zhang X, Munir R, Xu Z, Liu Y, Tsai H, Nie W, Li J, Niu T, Smilgies D M, Kanatzidis M G, Mohite A D, Zhao K, Amassian A, Liu S F 2018 Adv. Mater. 30 e1707166 Google Scholar
[162]	Liu G, Zheng H, Xu X, Xu S, Zhang X, Pan X, Dai S 2019 Adv. Funct. Mater. 1807565 Google Scholar
[163]	Zheng H, Liu G, Zhu L, Ye J, Zhang X, Alsaedi A, Hayat T, Pan X, Dai S 2018 Adv. Energy. Mater. 8 1800051 Google Scholar
[164]	Cho Y, Soufiani A M, Yun J S, Kim J, Lee D S, Seidel J, Deng X, Green M A, Huang S, Ho-Baillie A W Y 2018 Adv. Energy Mater. 8 1703392
[165]	Li M H, Yeh H H, Chiang Y H, Jeng U S, Su C J, Shiu H W, Hsu Y J, Kosugi N, Ohigashi T, Chen Y A, Shen P S, Chen P, Guo T F 2018 Adv. Mater. 30 e1801401 Google Scholar
[166]	Wang F, Jiang X, Chen H, Shang Y, Liu H, Wei J, Zhou W, He H, Liu W, Ning Z 2018 Joule 2 2732 Google Scholar
[167]	Peng W, Yin J, Ho K T, Ouellette O, de Bastiani M, Murali B, El Tall O, Shen C, Miao X, Pan J, Alarousu E, He J H, Ooi B S, Mohammed O F, Sargent E, Bakr O M 2017 Nano Lett. 17 4759 Google Scholar
[168]	Liu M, Johnston M B, Snaith H J 2013 Nature 501 395 Google Scholar

[1]	Zhong Ting-Ting, Hao Hui-Ying. Component control and additive engineering of all-inorganic perovskite films and carbon-based solar cells under ambient air environment. Acta Physica Sinica, 2024, 73(23): 238101. doi: 10.7498/aps.73.20241439
[2]	Liu Si-Wen, Ren Li-Zhi, Jin Bo-Wen, Song Xin, Wu Cong-Cong. Preparation of two-dimensional perovskite layer by solution method for improving stability of FAPbI₃ perovskite solar cells. Acta Physica Sinica, 2024, 73(6): 068801. doi: 10.7498/aps.73.20231678
[3]	Wang Jing, Gao Shan, Duan Xiang-Mei, Yin Wan-Jian. Influence of defect in perovskite solar cell materials on device performance and stability. Acta Physica Sinica, 2024, 73(6): 063101. doi: 10.7498/aps.73.20231631
[4]	Juan Ting, Xing Jia-He, Zeng Fan-Cong, Zheng Xin, Xu Lin. Performance of perovskite solar cells based on SnO₂:DPEPO hybrid electron transport layer. Acta Physica Sinica, 2024, 73(19): 198401. doi: 10.7498/aps.73.20240827
[5]	Wang Gui-Qiang, Bi Jia-Yu, Liu Jie-Qiong, Lei Miao, Zhang Wei. Enhancing quality of CsPbIBr₂ inorganic perovskite via cellulose acetate addition for high-performance perovskite solar cells. Acta Physica Sinica, 2022, 71(1): 018802. doi: 10.7498/aps.71.20211074
[6]	Luo Yuan, Zhu Cong-Tan, Ma Shu-Peng, Zhu Liu, Guo Xue-Yi, Yang Ying. Low-temperature preparation of SnO₂ electron transport layer for perovskite solar cells. Acta Physica Sinica, 2022, 71(11): 118801. doi: 10.7498/aps.71.20211930
[7]	Zhang Ao, Zhang Chun-Xiu, Zhang Chun-Mei, Tian Yi-Min, Yan Jun, Meng Tao. Effects of CH₃NH₃ polymer formation on performance of organic-inorganic hybrid perovskite solar cell. Acta Physica Sinica, 2021, 70(16): 168801. doi: 10.7498/aps.70.20210353
[8]	Yan Jia-Hao, Chen Si-Xuan, Yang Jian-Bin, Dong Jing-Jing. Improving efficiency and stability of organic-inorganic hybrid perovskite solar cells by absorption layer ion doping. Acta Physica Sinica, 2021, 70(20): 206801. doi: 10.7498/aps.70.20210836
[9]	Li Jia-Sen, Liang Chun-Jun, Ji Chao, Gong Hong-Kang, Song Qi, Zhang Hui-Min, Liu Ning. Improvement in performance of carbon-based perovskite solar cells by adding 1, 8-diiodooctane into hole transport layer 3-hexylthiophene. Acta Physica Sinica, 2021, 70(19): 198403. doi: 10.7498/aps.70.20210586
[10]	Wu Hai-Yan, Tang Jian-Xin, Li Yan-Qing. Efficient and stable blue perovskite light emitting diodes based on defect passivation. Acta Physica Sinica, 2020, 69(13): 138502. doi: 10.7498/aps.69.20200566
[11]	Fan Qin-Hua, Zu Yan-Qing, Li Lu, Dai Jin-Fei, Wu Zhao-Xin. Research progress of stability of luminous lead halide perovskite nanocrystals. Acta Physica Sinica, 2020, 69(11): 118501. doi: 10.7498/aps.69.20191767
[12]	Wang Ji-Ming, Chen Ke, Xie Wei-Guang, Shi Ting-Ting, Liu Peng-Yi, Zheng Yi-Fan, Zhu Rui. Research progress of solution processed all-inorganic perovskite solar cell. Acta Physica Sinica, 2019, 68(15): 158806. doi: 10.7498/aps.68.20190355
[13]	Fu Peng-Fei, Yu Dan-Ni, Peng Zi-Jian, Gong Jin-Kang, Ning Zhi-Jun. Perovskite solar cells passivated by distorted two-dimensional structure. Acta Physica Sinica, 2019, 68(15): 158802. doi: 10.7498/aps.68.20190306
[14]	Xia Jun-Min, Liang Chao, Xing Gui-Chuan. Inkjet printed perovskite solar cells: progress and prospects. Acta Physica Sinica, 2019, 68(15): 158807. doi: 10.7498/aps.68.20190302
[15]	Cao Ru-Nan, Xu Fei, Zhu Jia-Bin, Ge Sheng, Wang Wen-Zhen, Xu Hai-Tao, Xu Run, Wu Yang-Lin, Ma Zhong-Quan, Hong Feng, Jiang Zui-Min. Temperature-dependent time response characteristic of photovoltaic performance in planar heterojunction perovskite solar cell. Acta Physica Sinica, 2016, 65(18): 188801. doi: 10.7498/aps.65.188801
[16]	Yuan Huai-Liang, Li Jun-Peng, Wang Ming-Kui. Recent progress in research on solid organic-inorganic hybrid solar cells. Acta Physica Sinica, 2015, 64(3): 038405. doi: 10.7498/aps.64.038405
[17]	Yang Xu-Dong, Chen Han, Bi En-Bing, Han Li-Yuan. Key issues in highly efficient perovskite solar cells. Acta Physica Sinica, 2015, 64(3): 038404. doi: 10.7498/aps.64.038404
[18]	Xia Xiang, Liu Xi-Zhe. Effects of CH3NH3I on fabricating CH3NH3PbI(3-x)Clx perovskite solar cells. Acta Physica Sinica, 2015, 64(3): 038104. doi: 10.7498/aps.64.038104
[19]	Zhang Dan-Fei, Zheng Ling-Ling, Ma Ying-Zhuang, Wang Shu-Feng, Bian Zu-Qiang, Huang Chun-Hui, Gong Qi-Huang, Xiao Li-Xin. Factors influencing the stability of perovskite solar cells. Acta Physica Sinica, 2015, 64(3): 038803. doi: 10.7498/aps.64.038803
[20]	Xiang Jun, Li Li-Ping, Su Wen-Hui. Preparation and characterization of a new perovskite-type oxide ion conductor KN b1-xMgxO3-δ. Acta Physica Sinica, 2003, 52(6): 1474-1478. doi: 10.7498/aps.52.1474

Catalog

Vol. 68, Issue 15 - 2019-08-05

Metrics

Abstract views: 36127
PDF Downloads: 1535
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板