In this paper, the highly ordered periodic silver nanosphere arrays are fabricated by vacuum evaporation based on anodic aluminum oxide (AAO) template. The diameter and spacing of silver nanosphere in the arrays are adjusted just by controlling the thickness of evaporation. Furthermore, this can effectively modulate the absorption peaks and bandwidths in ultraviolet-visible-near-infrared regions. The measurement results of absorption spectra show that the nano-arrays have obvious electromagnetic wave absorption characteristics in the ultraviolet, visible and near-infrared bands. The finite-difference time-domain theoretical simulation combined with experiments is used to analyze the physical mechanism of light absorption characteristics in different wavebands. The ultraviolet strong absorption is due to the Fano resonance induced by asymmetric dielectric environment of silver and aluminum; the visible absorption originates from local surface plasmon resonance of silver nanoparticles; the near-infrared strong absorption is attributed to the surface lattice resonance of silver nanosphere arrays.
-
Keywords:
- localized surface plasmon /
- nano arrays /
- anodic aluminum oxide /
- absorption peak-position
[1] Wang S Q, Xu L P, Wen Y Q, Du H W, Wang S T, Zhang X J 2013 Nanoscale 5 4284
Google Scholar
[2] Shipway A N, Katz E, Willner I 2000 ChemPhysChem 1 18
Google Scholar
[3] Prakash J, Harris R A, Swart H C 2016 Int. Rev. Phys. Chem. 35 353
Google Scholar
[4] Fuku K, Hayashi R, Takakura S, Kamegawa T, Mori K, Yamashita H 2013 Angew. Chem. Int. Ed. 52 7446
Google Scholar
[5] Yan B, Yang X X, Fang J Y, Huang Y D, Qin H, Qin S Q 2015 Chin. Phys. B 24 15203
Google Scholar
[6] 张喆, 柳倩, 祁志美 2013 物理学报 62 060703
Google Scholar
Zhang Z, Liu Q, Qi Z M 2013 Acta Phys. Sin. 62 060703
Google Scholar
[7] Offermans P, Schaafsma M C, Rodriguez S R K, Zhang Y C, Crego-Calama M, Brongersma S H, Rivas J G 2015 ACS Nano 5 5151
[8] Ren K, Yin P, Zhou Y, Cao X, Dong C, Cui L, Liu H, Du X 2017 Small 13 1700867
Google Scholar
[9] Mi Y, Wen L Y, Xu R, Wang Z J, Cao D W, Fang Y G, Lei Y 2016 Adv. Energy Mater. 6 1501496
Google Scholar
[10] 叶松, 王向贤, 侯宜栋, 张志友, 杜惊雷 2014 物理学报 65 087802
Google Scholar
Ye S, Wang X, Hou Y D, Zhang Z Y, Du J L 2014 Acta Phys. Sin. 65 087802
Google Scholar
[11] Zhang J, Dong L, Yu S H 2015 Sci. Bull. 60 785
Google Scholar
[12] Khan Y, Li A R, Chang L, Li L D 2018 Sens. Actuator, B 255 1298
Google Scholar
[13] Xiong B, Zhou R, Hao J R, Jia Y H, He Y, Yeung E S 2013 Nat. Commun. 4 1708
Google Scholar
[14] Jung H Y, Yeo I S, Kim T U, Ki H C, Gu H B 2018 Appl. Surf. Sci. 432 266
Google Scholar
[15] Wu K, Li T, Schmidt M S, Rindzevicius T, Boisen A, Ndoni S 2018 Adv. Funct. Mater. 28 1704818
Google Scholar
[16] Zhan Z B, Xu R, Mi Y, Zhao H P, Lei Y 2015 ACS Nano 9 4583
Google Scholar
[17] Ji N, Ruan W D, Li Z S, Wang C X, Yang Z, Zhao B 2013 J. Raman Spectrosc. 44 1
Google Scholar
[18] King N S, Liu L F, Yang X, Cerjan B, Everitt H O, Nordlander P, Halas N J 2015 ACS Nano 9 10628
Google Scholar
[19] Zhan Z B, Xu R, Zheng X Z, Fu Q, Wu M H, Lei Y 2016 Nanotechnol. 27 445301
Google Scholar
[20] Minamimoto H, Oikawa S, Hayashi T, Shibazaki A, Li X W, Murakoshi K 2018 J. Phys. Chem. C 122 14162
Google Scholar
[21] Zhang C, Wu K, Ling B, Li X F 2016 J. Photonics Energy 6 042502
Google Scholar
[22] González-Rubio G, Díaz-Núñez P, Rivera A, Prada A, Tardajos G, González-Izquierdo J, Bañares L, Llombart P, Macdowell L G, Palafox M A, Liz-Marzán L M, Peña-Rodríguez O, Guerrero-Martínez A 2017 Science 358 640
Google Scholar
[23] Wang L C, Liu Z Q, Yi X Y, Zhang Y Y, Li H J, Li G M, Wang G H 2016 J. Appl. Phys. 119 1685
Google Scholar
[24] Gromov D G, Pavlova L M, Savitsky A I, Trifonov A Y 2015 Appl. Phys. A 118 1297
Google Scholar
[25] Liu Z H, Ye J 2016 Nanoscale 8 17665
Google Scholar
[26] Marimuthu A, Zhang J W, Linic S 2013 Science 339 1590
Google Scholar
[27] Ji N, Ruan W D, Wang C X, Lu C, Zhao B 2009 Langmuir 25 11869
Google Scholar
[28] Zhang S P, Bao K, Halas N J, Xu H X, Nordlander P 2011 Nano Lett. 11 1657
Google Scholar
[29] 屈炜, 李静 2017 新技术新工艺 5 15
Google Scholar
Qu W, Li J 2017 New Technol. New Process 5 15
Google Scholar
[30] Zhan Y H, Lei D Y, Li X F, Maier S A 2014 Nanoscale 6 4705
Google Scholar
[31] 张佳, 牧凯军, 王俊俏, 范春珍, 梁二军 2017 光散射学报 29 1007
Google Scholar
Zhang J, Mu K J, Wang J X, Fan C Z, Liang E J 2017 J. Light Scatt. 29 1007
Google Scholar
[32] Knight M W, Wu Y P, Lassiter J B, Nordlander P, Halas N J 2009 Nano Lett. 9 2188
Google Scholar
[33] Wu Y P, Nordlander P 2010 J. Phys. Chem. C 114 7302
Google Scholar
[34] Benjamin G, Olivier Martin J F 2011 ACS Nano 5 8999
Google Scholar
[35] Wang M S, Krasnok A, Zhang T Y, Scarabelli L, Liu H, Wu Z L, Luis M, Marzán L, Terrones M, Alù A, Zheng Y B 2018 Adv. Mater. 3 1705779
Google Scholar
[36] Sherry L J, Chang S H, Schatz G C, Van Duyne R P, Wiley B J, Xia Y 2005 Nano Lett. 5 2034
Google Scholar
[37] Yin J, Zang Y S, Xu B B, Li S P, Kang J Y, Fang Y Y, Wu Z H, Li J 2014 Nanoscale 6 3934
Google Scholar
[38] Catchpole K R, Polman A 2008 Opt. Express 16 21793
Google Scholar
[39] 黄昕乾, 姚若河 2018 真空科学与技术学报 38 791
Google Scholar
Huang X Q, Yao R H 2018 Chin. J. Vacuum Sci. Technol. 38 791
Google Scholar
[40] Cristiano M, Christoph H, Luis G P J, Judith L, Agustín M, Luis M, Liz M 2018 ACS Nano 12 8531
Google Scholar
-
图 1 AAO纳米碗阵列和Ag纳米球阵列制备过程示意图 (a) 高纯铝片; (b) AAO纳米管阵列; (c) AAO纳米碗阵列; (d) Ag纳米颗粒; (e) Ag纳米球阵列
Figure 1. Schematic diagram of the preparation procedure for fabricating patterned aluminum templates and Ag nanosphere arrays: (a) Purity aluminum; (b) AAO nanotube arrays after the first anodization; (c) AAO nanobowl arrays after the removal of the porous alumina layer; (d) Ag nanoparticles; (e) Ag nanosphere arrays.
图 2 真空蒸镀实验仪器示意图
Figure 2. Schematic diagram of vacuum evaporation apparatus.
图 3 FDTD Solutions仿真模型 (a) x-y视图; (b) x-z视图
Figure 3. View of simulation model in FDTD Solution (a) x-y; (b) x-z.
图 4 (a) AAO纳米碗阵列SEM图; (b) Ag纳米球周期性阵列SEM图
Figure 4. SEM images of the (a) AAO nanobowl arrays and (b) periodic arrays of Ag nanospheres.
图 5 不同粒径(D) Ag纳米球周期性阵列/不同厚度(T) Ag膜的SEM图 (a)−(n)及相应的粒径分布直方图(i)−(x) (a) D = 73.5 nm; (b) D = 78.2 nm; (c) D = 83.2 nm; (d) D = 85.5 nm; (e) D = 87.7 nm; (f) D = 90.1 nm; (g) D = 91.3 nm; (h) D = 91.7 nm; (i) D = 93.1 nm; (j) D = 94.2 nm; (k) T = 17.5; (l) T =18.2 nm; (m) T = 19.0 nm; (n) T = 19.7 nm
Figure 5. (a)−(n) SEM images of Ag nanosphere arrays/Ag film and (i)−(x) their related size distribution histograms: (a) D = 73.5 nm; (b) D = 78.2 nm; (c) D = 83.2 nm; (d) D = 85.5 nm; (e) D = 87.7 nm; (f) D = 90.1 nm; (g) D = 91.3 nm; (h) D = 91.7 nm; (i) D = 93.1 nm; (j) D = 94.2 nm; (k) T = 17.5 nm; (l) T = 18.2 nm; (m) T = 19.0 nm; (n) T = 19.7 nm.
图 6 (a) 沉积在AAO纳米碗上不同粒径Ag纳米球阵列UV-vis-NIR实验所得吸收光谱; (b) 不同衬底制备的银复合结构的吸收光谱
Figure 6. Experimental UV-vis-NIR absorption spectra of (a) Ag nanosphere arrays deposited on AAO-nanobowl with different sizes; (b) silver composite structure fabricated on different substrates.
图 7 (a) UV-Vis波段不同粒径Ag纳米球阵列实验所得吸收光谱和(b) FDTD模拟吸收光谱
Figure 7. UV-Vis absorption spectra of Ag nanosphere arrays with different sizes: (a) Experimental results; (b) FDTD simulation results
图 8 (a)紫外波段Ag纳米颗粒实验测得吸收光谱(黑色虚线), 以及根据(3)式拟合得到的吸收光谱(红色); (b) Ag纳米球阵列在437 nm波长下x-y平面(z = 0)的极化电场分布
Figure 8. (a) UV absorption spectra of Ag nanosphere arrays (black dashed line is experimental results; red line corresponds to σt obtained by fitting the Eq. (3); (b) polarized field distributions on the x-y plane (z = 0) of the Ag nano-sphere array excited 437 nm.
图 9 (a) NIR波段不同粒径Ag纳米球阵列实验所得吸收光谱和(b) FDTD理论模拟吸收光谱
Figure 9. NIR absorption spectra of Ag nanosphere arrays with different sizes: (a) Experimental results; (b) FDTD simulation results.
-
[1] Wang S Q, Xu L P, Wen Y Q, Du H W, Wang S T, Zhang X J 2013 Nanoscale 5 4284
Google Scholar
[2] Shipway A N, Katz E, Willner I 2000 ChemPhysChem 1 18
Google Scholar
[3] Prakash J, Harris R A, Swart H C 2016 Int. Rev. Phys. Chem. 35 353
Google Scholar
[4] Fuku K, Hayashi R, Takakura S, Kamegawa T, Mori K, Yamashita H 2013 Angew. Chem. Int. Ed. 52 7446
Google Scholar
[5] Yan B, Yang X X, Fang J Y, Huang Y D, Qin H, Qin S Q 2015 Chin. Phys. B 24 15203
Google Scholar
[6] 张喆, 柳倩, 祁志美 2013 物理学报 62 060703
Google Scholar
Zhang Z, Liu Q, Qi Z M 2013 Acta Phys. Sin. 62 060703
Google Scholar
[7] Offermans P, Schaafsma M C, Rodriguez S R K, Zhang Y C, Crego-Calama M, Brongersma S H, Rivas J G 2015 ACS Nano 5 5151
[8] Ren K, Yin P, Zhou Y, Cao X, Dong C, Cui L, Liu H, Du X 2017 Small 13 1700867
Google Scholar
[9] Mi Y, Wen L Y, Xu R, Wang Z J, Cao D W, Fang Y G, Lei Y 2016 Adv. Energy Mater. 6 1501496
Google Scholar
[10] 叶松, 王向贤, 侯宜栋, 张志友, 杜惊雷 2014 物理学报 65 087802
Google Scholar
Ye S, Wang X, Hou Y D, Zhang Z Y, Du J L 2014 Acta Phys. Sin. 65 087802
Google Scholar
[11] Zhang J, Dong L, Yu S H 2015 Sci. Bull. 60 785
Google Scholar
[12] Khan Y, Li A R, Chang L, Li L D 2018 Sens. Actuator, B 255 1298
Google Scholar
[13] Xiong B, Zhou R, Hao J R, Jia Y H, He Y, Yeung E S 2013 Nat. Commun. 4 1708
Google Scholar
[14] Jung H Y, Yeo I S, Kim T U, Ki H C, Gu H B 2018 Appl. Surf. Sci. 432 266
Google Scholar
[15] Wu K, Li T, Schmidt M S, Rindzevicius T, Boisen A, Ndoni S 2018 Adv. Funct. Mater. 28 1704818
Google Scholar
[16] Zhan Z B, Xu R, Mi Y, Zhao H P, Lei Y 2015 ACS Nano 9 4583
Google Scholar
[17] Ji N, Ruan W D, Li Z S, Wang C X, Yang Z, Zhao B 2013 J. Raman Spectrosc. 44 1
Google Scholar
[18] King N S, Liu L F, Yang X, Cerjan B, Everitt H O, Nordlander P, Halas N J 2015 ACS Nano 9 10628
Google Scholar
[19] Zhan Z B, Xu R, Zheng X Z, Fu Q, Wu M H, Lei Y 2016 Nanotechnol. 27 445301
Google Scholar
[20] Minamimoto H, Oikawa S, Hayashi T, Shibazaki A, Li X W, Murakoshi K 2018 J. Phys. Chem. C 122 14162
Google Scholar
[21] Zhang C, Wu K, Ling B, Li X F 2016 J. Photonics Energy 6 042502
Google Scholar
[22] González-Rubio G, Díaz-Núñez P, Rivera A, Prada A, Tardajos G, González-Izquierdo J, Bañares L, Llombart P, Macdowell L G, Palafox M A, Liz-Marzán L M, Peña-Rodríguez O, Guerrero-Martínez A 2017 Science 358 640
Google Scholar
[23] Wang L C, Liu Z Q, Yi X Y, Zhang Y Y, Li H J, Li G M, Wang G H 2016 J. Appl. Phys. 119 1685
Google Scholar
[24] Gromov D G, Pavlova L M, Savitsky A I, Trifonov A Y 2015 Appl. Phys. A 118 1297
Google Scholar
[25] Liu Z H, Ye J 2016 Nanoscale 8 17665
Google Scholar
[26] Marimuthu A, Zhang J W, Linic S 2013 Science 339 1590
Google Scholar
[27] Ji N, Ruan W D, Wang C X, Lu C, Zhao B 2009 Langmuir 25 11869
Google Scholar
[28] Zhang S P, Bao K, Halas N J, Xu H X, Nordlander P 2011 Nano Lett. 11 1657
Google Scholar
[29] 屈炜, 李静 2017 新技术新工艺 5 15
Google Scholar
Qu W, Li J 2017 New Technol. New Process 5 15
Google Scholar
[30] Zhan Y H, Lei D Y, Li X F, Maier S A 2014 Nanoscale 6 4705
Google Scholar
[31] 张佳, 牧凯军, 王俊俏, 范春珍, 梁二军 2017 光散射学报 29 1007
Google Scholar
Zhang J, Mu K J, Wang J X, Fan C Z, Liang E J 2017 J. Light Scatt. 29 1007
Google Scholar
[32] Knight M W, Wu Y P, Lassiter J B, Nordlander P, Halas N J 2009 Nano Lett. 9 2188
Google Scholar
[33] Wu Y P, Nordlander P 2010 J. Phys. Chem. C 114 7302
Google Scholar
[34] Benjamin G, Olivier Martin J F 2011 ACS Nano 5 8999
Google Scholar
[35] Wang M S, Krasnok A, Zhang T Y, Scarabelli L, Liu H, Wu Z L, Luis M, Marzán L, Terrones M, Alù A, Zheng Y B 2018 Adv. Mater. 3 1705779
Google Scholar
[36] Sherry L J, Chang S H, Schatz G C, Van Duyne R P, Wiley B J, Xia Y 2005 Nano Lett. 5 2034
Google Scholar
[37] Yin J, Zang Y S, Xu B B, Li S P, Kang J Y, Fang Y Y, Wu Z H, Li J 2014 Nanoscale 6 3934
Google Scholar
[38] Catchpole K R, Polman A 2008 Opt. Express 16 21793
Google Scholar
[39] 黄昕乾, 姚若河 2018 真空科学与技术学报 38 791
Google Scholar
Huang X Q, Yao R H 2018 Chin. J. Vacuum Sci. Technol. 38 791
Google Scholar
[40] Cristiano M, Christoph H, Luis G P J, Judith L, Agustín M, Luis M, Liz M 2018 ACS Nano 12 8531
Google Scholar
DownLoad:
Catalog
Metrics
- Abstract views: 12398
- PDF Downloads: 153
- Cited By: 0