Based on the electromagnetic loading device CQ-4, an experimental method of simultaneously measuring the refractive index and high pressure sound velocity of transparent material is established. The ramp wave compression experiment of PMMA is carried out under a pressure of 14 GPa. The velocity history curves of PMMA sample rear surface are obtained by dual laser heterodyne velocimetry (DLHV). The velocity curve shows obvious double wave structure, which indicates the elastic-plastic transition. The refractive index particle velocity optical characteristics and Lagrangian sound velocity particle velocity dynamic characteristics of PMMA are obtained simultaneously with the experimental data processing.
-
Keywords:
- polymethyl methacrylate /
- refractive index /
- lagrange sound speed /
- ramp wave loading
[1] Hall C A, Asay J R, Knudson M D, Stygar W A, Spielman R B, Pointon T D, Reisman D B, Toor A, Cauble R C 2001 Rev. Sci. Instrum. 72 3587
Google Scholar
[2] Hayes D B 2001 J. Appl. Phys. 89 648
Google Scholar
[3] Hayes D B, Hall C A, Asay J R, Knudson M D 2003 J. Appl. Phys. 94 2331
Google Scholar
[4] Fratanduono D E, Boehly T R, Barrios M A, Meyer-hofer D D, Eggert J H, Smith R F, Hicks D G, Celliers P M, Braun D G, Collins G W 2011 J. Appl. Phys. 109 123521
Google Scholar
[5] Fratanduono D E, Eggert J H, Akin M C, Chau R, Holmes N C 2013 J. Appl. Phys. 114 043518
Google Scholar
[6] Nazarov D V, Mikhailov A L, Fedorov A V, Manachkin S F, Urlin V D, Men’ shikh A V, Finyushin S A, Davy-dov V A, Filinov E V 2006 Combust. Explo. Shock 42 351
Google Scholar
[7] 张旭平, 罗斌强, 种涛, 王桂吉, 谭福利, 赵剑衡, 孙承纬, 刘仓理 2016 物理学报 64 046201
Google Scholar
Zhang X P, Luo B Q, Chong T, Wang G J, Tan F L, Zhao J H, Sun C W, Liu C L 2016 Acta Phys. Sin. 64 046201
Google Scholar
[8] Mulliken A D, Boyce M C 2006 Int. J. Solids. Struct. 46 2320
[9] Cheng W M, Manson J A 1990 J. Mater. Sci. 25 31
[10] Richeton J, Schlatter G, Vecchio K S, Remond Y, Ahzi S 2005 Polymer 46 8195
[11] Richeton J, Ahzi S, Vecchio K S, Jiang F C, Makradi A 2007 Int. J. Solids. Struct. 44 7940
[12] Chen W, Lu F 2002 Polym. Test. 21 114
[13] Jo C, Fu J, Naguib H E 2005 Polymer 46 11897
[14] Forquin P, Nasraoui M, Rusinek A, Siad L 2012 Int. J. Impact Eng. 40 46
[15] Pélissier J L, Partouche-Sebban D 2005 Physica B 364 14
Google Scholar
[16] Chhabildas L C, Asay J R 1979 J. Appl. Phys. 50 2749
Google Scholar
[17] 郝龙, 王翔, 王青松, 康强, 黄金 2017 高压物理学报 5 579
Google Scholar
Hao L, Wang X, Wang Q S, Kang Q, Hang J 2017 Chin. J. High Pressure Phys. 5 579
Google Scholar
[18] Wang G J, Luo B Q, Zhang X P, Zhao J H, Sun C W, Tan F L, Chong T, Mo J J, Wu G, TaO Y H 2013 Rev. Sci. Instrum. 84 015117
Google Scholar
[19] 种涛, 王桂吉, 谭福利, 赵剑衡, 唐志平 2018 物理学报 67 070204
Google Scholar
Chong T, Wang G J, Tan F L, Zhao J H, Tang A P 2018 Acta Phys. Sin. 67 070204
Google Scholar
[20] 罗斌强, 张红平, 种涛, 王桂吉, 谭福利, 赵剑衡, 孙承纬 2017 高压物理学报 31 295
Google Scholar
Luo B Q, Zhang H P, Chong T, Wang G J, Tan F L, Zhao J H, Sun C W 2017 Chin. J. High Pressure Phys. 31 295
Google Scholar
[21] 陶天炯, 翁继东, 王翔 2011 光电工程 38 39
Tao T J, Weng J D, Wang X 2011 Opto-Electron. Eng. 38 39
[22] LaLone B M, Fat’yanov O V, Asay J R, Gupta Y M 2008 J. Appl. Phys. 103 093505
Google Scholar
[23] Barker L M, Hollenbach R E 1970 J. Appl.Phys. 41 4208
Google Scholar
[24] Ao T, Knudson M D, Asay J R, Davis J P 2009 J. Appl.Phys. 106 103507
Google Scholar
[25] 种涛2012 硕士学位论文 (绵阳: 中国工程物理研究院)
Chong T 2012 M. S. Thesis (Mianyang: China Academy of Engineering Physics) (in Chinese)
[26] 蔡进涛 2018 博士学位论文 (绵阳: 中国工程物理研究院)
Cai J T 2018 Ph. D. Dissertation (Mianyang: China Academy of Engineering Physics) (in Chinese)
[27] 姬忠涛, 田德 2006 农业工程学报 32 98
Google Scholar
Ji Z T, Tian D 2006 Trans. Chin. Soc. Agric. Eng. 32 98
Google Scholar
-
图 1 磁驱动加载原理及样品布局
Figure 1. Schematic diagram of magnetically driven ramp wave loading and layout of the samples.
图 2 实验速度曲线
Figure 2. Experimental velocity curve.
图 3 表观速度-原位粒子速度关系
Figure 3. ua-up relationship of PMMA.
图 4 原位粒子速度波形
Figure 4. true particle velocity waveforms.
图 5 拉氏声速-原位粒子速度关系
Figure 5. Lagrange sound speed- true particle velocity relationship.
表 1 实验条件
Table 1. Experimental condition.
实验编号 位置 材料 尺寸/(mm × mm) shot163 ch1 纯铝 1.006 × 10.0 (厚 × 宽) PMMA Ф10.0 × 1.485 PMMA Ф10.0 × 4.000 ch2 纯铝 1.002 × 10.0 (厚 × 宽) PMMA Ф10.0 × 1.483 ch3 纯铝 1.007 × 10.0 (厚 × 宽) PMMA Ф10.0 × 1.263 PMMA Ф10.0 × 3.987 ch4 纯铝 1.008 × 10.0 (厚 × 宽) LiF Ф10.0 × 3.601 
DownLoad: CSV
-
[1] Hall C A, Asay J R, Knudson M D, Stygar W A, Spielman R B, Pointon T D, Reisman D B, Toor A, Cauble R C 2001 Rev. Sci. Instrum. 72 3587
Google Scholar
[2] Hayes D B 2001 J. Appl. Phys. 89 648
Google Scholar
[3] Hayes D B, Hall C A, Asay J R, Knudson M D 2003 J. Appl. Phys. 94 2331
Google Scholar
[4] Fratanduono D E, Boehly T R, Barrios M A, Meyer-hofer D D, Eggert J H, Smith R F, Hicks D G, Celliers P M, Braun D G, Collins G W 2011 J. Appl. Phys. 109 123521
Google Scholar
[5] Fratanduono D E, Eggert J H, Akin M C, Chau R, Holmes N C 2013 J. Appl. Phys. 114 043518
Google Scholar
[6] Nazarov D V, Mikhailov A L, Fedorov A V, Manachkin S F, Urlin V D, Men’ shikh A V, Finyushin S A, Davy-dov V A, Filinov E V 2006 Combust. Explo. Shock 42 351
Google Scholar
[7] 张旭平, 罗斌强, 种涛, 王桂吉, 谭福利, 赵剑衡, 孙承纬, 刘仓理 2016 物理学报 64 046201
Google Scholar
Zhang X P, Luo B Q, Chong T, Wang G J, Tan F L, Zhao J H, Sun C W, Liu C L 2016 Acta Phys. Sin. 64 046201
Google Scholar
[8] Mulliken A D, Boyce M C 2006 Int. J. Solids. Struct. 46 2320
[9] Cheng W M, Manson J A 1990 J. Mater. Sci. 25 31
[10] Richeton J, Schlatter G, Vecchio K S, Remond Y, Ahzi S 2005 Polymer 46 8195
[11] Richeton J, Ahzi S, Vecchio K S, Jiang F C, Makradi A 2007 Int. J. Solids. Struct. 44 7940
[12] Chen W, Lu F 2002 Polym. Test. 21 114
[13] Jo C, Fu J, Naguib H E 2005 Polymer 46 11897
[14] Forquin P, Nasraoui M, Rusinek A, Siad L 2012 Int. J. Impact Eng. 40 46
[15] Pélissier J L, Partouche-Sebban D 2005 Physica B 364 14
Google Scholar
[16] Chhabildas L C, Asay J R 1979 J. Appl. Phys. 50 2749
Google Scholar
[17] 郝龙, 王翔, 王青松, 康强, 黄金 2017 高压物理学报 5 579
Google Scholar
Hao L, Wang X, Wang Q S, Kang Q, Hang J 2017 Chin. J. High Pressure Phys. 5 579
Google Scholar
[18] Wang G J, Luo B Q, Zhang X P, Zhao J H, Sun C W, Tan F L, Chong T, Mo J J, Wu G, TaO Y H 2013 Rev. Sci. Instrum. 84 015117
Google Scholar
[19] 种涛, 王桂吉, 谭福利, 赵剑衡, 唐志平 2018 物理学报 67 070204
Google Scholar
Chong T, Wang G J, Tan F L, Zhao J H, Tang A P 2018 Acta Phys. Sin. 67 070204
Google Scholar
[20] 罗斌强, 张红平, 种涛, 王桂吉, 谭福利, 赵剑衡, 孙承纬 2017 高压物理学报 31 295
Google Scholar
Luo B Q, Zhang H P, Chong T, Wang G J, Tan F L, Zhao J H, Sun C W 2017 Chin. J. High Pressure Phys. 31 295
Google Scholar
[21] 陶天炯, 翁继东, 王翔 2011 光电工程 38 39
Tao T J, Weng J D, Wang X 2011 Opto-Electron. Eng. 38 39
[22] LaLone B M, Fat’yanov O V, Asay J R, Gupta Y M 2008 J. Appl. Phys. 103 093505
Google Scholar
[23] Barker L M, Hollenbach R E 1970 J. Appl.Phys. 41 4208
Google Scholar
[24] Ao T, Knudson M D, Asay J R, Davis J P 2009 J. Appl.Phys. 106 103507
Google Scholar
[25] 种涛2012 硕士学位论文 (绵阳: 中国工程物理研究院)
Chong T 2012 M. S. Thesis (Mianyang: China Academy of Engineering Physics) (in Chinese)
[26] 蔡进涛 2018 博士学位论文 (绵阳: 中国工程物理研究院)
Cai J T 2018 Ph. D. Dissertation (Mianyang: China Academy of Engineering Physics) (in Chinese)
[27] 姬忠涛, 田德 2006 农业工程学报 32 98
Google Scholar
Ji Z T, Tian D 2006 Trans. Chin. Soc. Agric. Eng. 32 98
Google Scholar
DownLoad:
Catalog
Metrics
- Abstract views: 4325
- PDF Downloads: 52
- Cited By: 0