Application of <i>in</i>-<i>situ</i> characterization techniques  in all-solid-state lithium batteries

Lu Jing-Yu; Ke Cheng-Zhi; Gong Zheng-Liang; Li De-Ping; Ci Li-Jie; Zhang Li; Zhang Qiao-Bao

doi:10.7498/aps.70.20210531

Abstract

In recent years, mobile consumer electronics and electric vehicles have been developing rapidly, and they have been hunting for lithium batteries with high energy density, high safety and stability, to alleviate the range anxiety and improve their stability over long term operations. These make all-solid-state lithium batteries very attractive and they have been under intense investigations. However, the development of high-performance all-solid-state lithium batteries requires an in-depth understanding of their charge and discharge mechanism, their degradation process, along with the evolution of the microstructures, phase compositions, chemical states and their distributions, etc., inside the battery and at the interface. This paper summarizes the basic principles, functions, and the representative advances in investigation of the dynamics and failure mechanism of electrode materials and interfaces in solid-state lithium batteries under working conditions, with typical in-situ characterization techniques, including in-situ microscopy (in-situ scanning electron microscopy (SEM), in-situ transmission electron microscopy (TEM)), in-situ X-ray techniques (in-situ X-ray diffraction (XRD)), in-situ X-ray photoelectron spectroscopy (XPS), in-situ near-edge structure X-ray absorption spectroscopy (XANES), in-situ X-ray tomography), in-situ neutron techniques (in-situ neutron diffraction (ND), in-situ neutron depth profiling (NDP)) and in-situ spectroscopies (in-situ Raman spectroscopy, in-situ nuclear magnetic resonance (NMR) and in-situ nuclear magnetic resonance imaging (MRI)), etc. We also discussed the application of future advanced in-situ characterization techniques in the investigation of all-solid-state lithium batteries.

Keywords:

Authors and contacts

1.
School of Science, Harbin Institute of Technology (Shenzhen), Shenzhen 518055, China
2.
College of Materials, Xiamen University, Xiamen 361005, China
3.
College of Energy, Xiamen University, Xiamen 361005, China
4.
School of Materials, Harbin Institute of Technology (Shenzhen), Shenzhen 518055, China
5.
College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005, China

Corresponding author: Li De-Ping, lideping@hit.edu.cn ; Ci Li-Jie, cilijie@hit.edu.cn ; Zhang Qiao-Bao, zhangqiaobao@xmu.edu.cn

Funds: Project supported by the Scientific Research Starting Foundation of Harbin Institute of Technology (Shenzhen), China (Grant Nos. DD29100027, DD45001022, University 20210028), the Shenzhen Steady Support Plan (Grant No. GXWD20201230155427003-20200824103000001), and the National Natural Science Foundation of China (Grant Nos. 52002094, 52122211, 52072323, 21935009, 21875196)

FullText HTML : translate this paragraph

References

[1]	An W, Gao B, Mei S, Xiang B, Fu J, Wang L, Zhang Q, Chu P K, Huo K 2019 Nat. Commun. 10 1447 Google Scholar
[2]	Lu J Y, Xu C 2020 Chem 6 3165 Google Scholar
[3]	Manthiram A, Yu X, Wang S 2017 Nat. Rev. Mater. 2 16103 Google Scholar
[4]	Randau S, Weber D A, Kötz O, Koerver R, Braun P, Weber A, Ivers-Tiffée E, Adermann T, Kulisch J, Zeier W G, Richter F H, Janek J 2020 Nat. Energy 5 259 Google Scholar
[5]	Zuo J H, Gong Y J 2020 Tungsten 2 134 Google Scholar
[6]	Zhao C, Xu G L, Yu Z, Zhang L, Hwang I, Mo Y X, Ren Y, Cheng L, Sun C J, Ren Y, Zuo X, Li J T, Sun S G, Amine K, Zhao T 2021 Nat. Nanotechnol. 16 166 Google Scholar
[7]	Cao Z J, Zhang Y Z, Cui Y L S, Li B, Yang S B 2020 Tungsten 2 162 Google Scholar
[8]	Lu J, Dey S, Temprano I, Jin Y, Xu C, Shao Y, Grey C P 2020 ACS Energy Lett. 5 3681 Google Scholar
[9]	Liu T, Vivek J P, Zhao E W, Lei J, Garcia-Araez N, Grey C P 2020 Chem. Rev. 120 6558 Google Scholar
[10]	Guo H, Hou G, Dai L, Yao Y, Wei C, Liang Z, Si P, Ci L 2020 J. Phys. Chem. Lett. 11 172 Google Scholar
[11]	Kato Y, Hori S, Saito T, Suzuki K, Hirayama M, Mitsui A, Yonemura M, Iba H, Kanno R 2016 Nat. Energy 1 16030 Google Scholar
[12]	Zhou L, Park K H, Sun X, Lalère F, Adermann T, Hartmann P, Nazar L F 2019 ACS Energy Lett. 4 265 Google Scholar
[13]	Ji X, Hou S, Wang P, He X, Piao N, Chen J, Fan X, Wang C 2020 Adv. Mater. 32 2002741 Google Scholar
[14]	Zhao Q, Stalin S, Zhao C Z, Archer L A 2020 Nat. Rev. Mater. 5 229 Google Scholar
[15]	Xu L, Li J, Deng W, Shuai H, Li S, Xu Z, Li J, Hou H, Peng H, Zou G, Ji X 2021 Adv. Energy Mater. 11 2000648 Google Scholar
[16]	Lilu Liu, Fan Wu, Hong Li, Chen L 2019 J. Chin. Ceramic Soc. 47 1367
[17]	Chung H, Kang B 2017 Chem. Mater. 29 8611 Google Scholar
[18]	Han F, Zhu Y, He X, Mo Y, Wang C 2016 Adv. Energy Mater. 6 1501590 Google Scholar
[19]	Zhang S N, Zeng Z, Zhai W, Hou G M, Chen L N, Ci L J 2021 Adv. Mater. Interfaces. 8 2100072 Google Scholar
[20]	拱越, 谷林 2020 物理学报 69 226801 Google Scholar Gong Y, Gu L 2020 Acta Phys. Sin. 69 226801 Google Scholar
[21]	冯吴亮, 王飞, 周星, 吉晓, 韩福东, 王春生 2020 物理学报 69 228206 Google Scholar Feng W L, Wang F, Zhou X, Ji X, Han F D, Wang C S 2020 Acta Phys. Sin. 69 228206 Google Scholar
[22]	Banerjee A, Wang X, Fang C, Wu E A, Meng Y S 2020 Chem. Rev. 120 6878 Google Scholar
[23]	Symington A R, Molinari M, Dawson J A, Statham J M, Purton J, Canepa P, Parker S C 2021 J. Mater. Chem. A 9 6487 Google Scholar
[24]	Grey C P, Tarascon J M 2017 Nat. Mater. 16 45 Google Scholar
[25]	Cheng Y, Zhang L, Zhang Q, Li J, Tang Y, Delmas C, Zhu T, Winter M, Wang M S, Huang J 2021 Mater. Today 42 137 Google Scholar
[26]	Li W, Lutz D M, Wang L, Takeuchi K J, Marschilok A C, Takeuchi E S 2021 Joule 5 77 Google Scholar
[27]	李文俊, 郑杰允, 谷林, 李泓 2015 电化学 21 99 Li W J, Zheng J Y, Gu L, Li H 2015 J. Electrochem. 21 99
[28]	潘弘毅, 禹习谦, 李泓, 李泉 2021 物理化学学报 37 2008090 Pan H Y, Yu X Q, Li H, Li Q 2021 Acta Phys. Sin. 37 2008090
[29]	Romanenko K, Jin L, Howlett P, Forsyth M 2016 Chem. Mater. 28 2844 Google Scholar
[30]	Ishikawa R, Jimbo Y, Terao M, Nishikawa M, Ueno Y, Morishita S, Mukai M, Shibata N, Ikuhara Y 2020 Microscopy 69 240 Google Scholar
[31]	Hou P, Chu G, Gao J, Zhang Y, Zhang L 2016 Chin. Phys. B 25 016104 Google Scholar
[32]	余启鹏, 刘琦, 王自强, 李宝华 2020 物理学报 69 228805 Google Scholar Yu Q P, Liu Q, Wang Z Q, Li B H 2020 Acta Phys. Sin. 69 228805 Google Scholar
[33]	曹文卓, 李泉, 王胜彬, 李文俊, 李泓 2020 物理学报 69 228204 Google Scholar Cao W Z, Li Q, Wang S B, Li W J, Li H 2020 Acta Phys. Sin. 69 228204 Google Scholar
[34]	Sagane F, Shimokawa R, Sano H, Sakaebe H, Iriyama Y 2013 J. Power Sources 225 245 Google Scholar
[35]	Motoyama M, Ejiri M, Iriyama Y 2015 J. Electrochem. Soc. 162 A7067 Google Scholar
[36]	Zheng H, Xiao D, Li X, Liu Y, Wu Y, Wang J, Jiang K, Chen C, Gu L, Wei X, Hu Y S, Chen Q, Li H 2014 Nano Lett. 14 4245 Google Scholar
[37]	柯承志, 肖本胜, 李苗, 陆敬予, 何洋, 张力, 张桥保 2021 储能科学与技术 10 1219 Google Scholar Ke C Z, Xiao B S, Li M, Lu J Y, He Y, Zhang L, Zhang Q B 2021 Energy Storage Sci. Technol. 10 1219 Google Scholar
[38]	Nomura Y, Yamamoto K, Fujii M, Hirayama T, Igaki E, Saitoh K 2020 Nat. Commun. 11 2824 Google Scholar
[39]	Zhu J, Zhao J, Xiang Y, Lin M, Wang H, Zheng B, He H, Wu Q, Huang J Y, Yang Y 2020 Chem. Mater. 32 4998 Google Scholar
[40]	梁宇皓, 范丽珍 2020 物理学报 69 226201 Google Scholar Liang Y H, Fan L Z 2020 Acta Phys. Sin. 69 226201 Google Scholar
[41]	Zhang L, Yang T, Du C, Liu Q, Tang Y, Zhao J, Wang B, Chen T, Sun Y, Jia P, Li H, Geng L, Chen J, Ye H, Wang Z, Li Y, Sun H, Li X, Dai Q, Tang Y, Peng Q, Shen T, Zhang S, Zhu T, Huang J 2020 Nat. Nanotechnol. 15 94
[42]	Wang Z, Tang Y, Zhang L, Li M, Shan Z, Huang J 2020 Small 16 2001899
[43]	Lu P, Yan P, Romero E, Spoerke E D, Zhang J G, Wang C M 2015 Chem. Mater. 27 1375 Google Scholar
[44]	Lin F, Markus I M, Doeff M M, Xin H L 2014 Sci. Rep. 4 5694
[45]	Shim J H, Kang H, Lee S, Kim Y M 2021 J. Mater. Chem. A 9 2429 Google Scholar
[46]	Wang X, Li Y, Meng Y S 2018 Joule 2 2225 Google Scholar
[47]	Li Y, Li Y, Pei A, Yan K, Sun Y, Wu C L, Joubert L M, Chin R, Koh A L, Yu Y, Perrino J, Butz B, Chu S, Cui Y 2017 Science 358 506 Google Scholar
[48]	Llewellyn A V, Matruglio A, Brett D J L, Jervis R, Shearing P R 2020 Condens. Matter 5 75 Google Scholar
[49]	Xu C, Märker K, Lee J, Mahadevegowda A, Reeves P J, Day S J, Groh M F, Emge S P, Ducati C, Layla Mehdi B, Tang C C, Grey C P 2021 Nat. Mater. 20 84 Google Scholar
[50]	Bak S M, Hu E, Zhou Y, Yu X, Senanayake S D, Cho S J, Kim K B, Chung K Y, Yang X Q, Nam K W 2014 ACS Appl. Mater. Interfaces 6 22594 Google Scholar
[51]	Safanama D, Sharma N, Rao R P, Brand H E A, Adams S 2016 J. Mater. Chem. A 4 7718 Google Scholar
[52]	Li W, Liang J, Li M, Adair K R, Li X, Hu Y, Xiao Q, Feng R, Li R, Zhang L, Lu S, Huang H, Zhao S, Sham T K, Sun X 2020 Chem. Mater. 32 7019 Google Scholar
[53]	Bartsch T, Kim A Y, Strauss F, de Biasi L, Teo J H, Janek J, Hartmann P, Brezesinski T 2019 Chem. Commun. 55 11223 Google Scholar
[54]	Goonetilleke D, Sharma N, Kimpton J, Galipaud J, Pecquenard B, Le Cras F 2018 Front. Energy Res. 6 64 Google Scholar
[55]	刘丽露, 吴凡, 李泓, 陈立泉 2019 硅酸盐学报 47 1367 Liu L L, Wu F, Li H, Chen L Q 2019 J. Chin. Ceram. Soc. 47 1367
[56]	张桥保, 龚正良, 杨勇 2020 物理学报 69 228803 Google Scholar Zhang Q B, Gong Z L, Yang Y 2020 Acta Phys. Sin. 69 228803 Google Scholar
[57]	Wenzel S, Randau S, Leichtweiß T, Weber D A, Sann J, Zeier W G, Janek J 2016 Chem. Mater. 28 2400 Google Scholar
[58]	Wenzel S, Weber D A, Leichtweiss T, Busche M R, Sann J, Janek J 2016 Solid State Ionics 286 24 Google Scholar
[59]	Wu J, Liu S, Han F, Yao X, Wang C 2021 Adv. Mater. 33 2000751 Google Scholar
[60]	Endo R, Ohnishi T, Takada K, Masuda T 2020 J. Phys. Chem. Lett. 11 6649 Google Scholar
[61]	张念, 任国玺, 章辉, 周櫈, 刘啸嵩 2020 物理学报 69 228806 Google Scholar Zhang N, Ren G X, Zhang H, Zhou D, Liu X G 2020 Acta Phys. Sin. 69 228806 Google Scholar
[62]	蔡明俐, 姚柳, 靳俊, 温兆银 2021 物理化学学报 37 2009006 Cai L, Yao L, Qi J, Wen Z 2021 Acta Phys. -Chim. Sin. 37 2009006
[63]	赵宁, 穆爽, 郭向欣 2020 物理学报 69 228804 Google Scholar Zhao N, Mu S, Guo X X 2020 Acta Phys. Sin. 69 228804 Google Scholar
[64]	Connell J G, Fuchs T, Hartmann H, Krauskopf T, Zhu Y, Sann J, Garcia-Mendez R, Sakamoto J, Tepavcevic S, Janek J 2020 Chem. Mater. 32 10207 Google Scholar
[65]	Liu Z, Li G, Borodin A, Liu X, Li Y, Endres F 2019 J. Solid State Electrochem. 23 2107 Google Scholar
[66]	Li X, Ren Z, Norouzi Banis M, Deng S, Zhao Y, Sun Q, Wang C, Yang X, Li W, Liang J, Li X, Sun Y, Adair K, Li R, Hu Y, Sham T K, Huang H, Zhang L, Lu S, Luo J, Sun X 2019 ACS Energy Lett. 4 2480 Google Scholar
[67]	Gonzalez Malabet H J, Juarez Robles D, de Andrade V, Mukherjee P P, Nelson G J 2020 J. Electrochem. Soc. 167 40523 Google Scholar
[68]	Lou S, Liu Q, Zhang F, Liu Q, Yu Z, Mu T, Zhao Y, Borovilas J, Chen Y, Ge M, Xiao X, Lee W K, Yin G, Yang Y, Sun X, Wang J 2020 Nat. Commun. 11 5700 Google Scholar
[69]	Wood V 2018 Nat. Rev. Mater. 3 293 Google Scholar
[70]	Pietsch P, Wood V 2017 Annu. Rev. Mater. Res. 47 451 Google Scholar
[71]	Wu X, Billaud J, Jerjen I, Marone F, Ishihara Y, Adachi M, Adachi Y, Villevieille C, Kato Y 2019 Adv. Energy Mater. 9 1901547 Google Scholar
[72]	Madsen K E, Bassett K L, Ta K, Sforzo B A, Matusik K E, Kastengren A L, Gewirth A A 2020 Adv. Mater. Interfaces 7 2000751 Google Scholar
[73]	Sun F, Dong K, Osenberg M, Hilger A, Risse S, Lu Y, Kamm P H, Klaus M, Markötter H, García-Moreno F, Arlt T, Manke I 2018 J. Mater. Chem. A 6 22489 Google Scholar
[74]	Lewis J A, Cortes F J Q, Liu Y, Miers J C, Verma A, Vishnugopi B S, Tippens J, Prakash D, Marchese T S, Han S Y, Lee C, Shetty P P, Lee H W, Shevchenko P, De Carlo F, Saldana C, Mukherjee P P, McDowell M T 2021 Nat. Mater. 20 503 Google Scholar
[75]	Kimura Y, Tomura A, Fakkao M, Nakamura T, Ishiguro N, Sekizawa O, Nitta K, Uruga T, Okumura T, Tada M, Uchimoto Y, Amezawa K 2020 J. Phys. Chem. Lett. 11 3629 Google Scholar
[76]	Kimura Y, Fakkao M, Nakamura T, Okumura T, Ishiguro N, Sekizawa O, Nitta K, Uruga T, Tada M, Uchimoto Y, Amezawa K 2020 ACS Appl. Energy Mater. 3 7782 Google Scholar
[77]	Wang J, Karen Chen-Wiegart Y C, Eng C, Shen Q, Wang J 2016 Nat. Commun. 7 12372 Google Scholar
[78]	Xiang Y, Li X, Cheng Y, Sun X, Yang Y 2020 Mater. Today 36 139 Google Scholar
[79]	Liang G, Didier C, Guo Z, Pang W K, Peterson V K 2020 Adv. Mater. 32 1904528 Google Scholar
[80]	郑国瑞, 向宇轩, 杨勇 2021 物理化学学报 37 2008094 Zheng G R, Xiang Y X, Yang Y 2021 Acta Phys. -Chim. Sin. 37 2008094
[81]	Kaup K, Zhou L, Huq A, Nazar L F 2020 J. Mater. Chem. A 8 12446 Google Scholar
[82]	Li Q, Yi T, Wang X, Pan H, Quan B, Liang T, Guo X, Yu X, Wang H, Huang X, Chen L, Li H 2019 Nano Energy 63 103895 Google Scholar
[83]	Wang C, Gong Y, Dai J, Zhang L, Xie H, Pastel G, Liu B, Wachsman E, Wang H, Hu L 2017 J. Am. Chem. Soc. 139 14257 Google Scholar
[84]	赵亮, 胡勇胜, 李泓, 王兆翔, 徐红星, 黄学杰, 陈立泉 2011 电化学 17 12 Zhao L, Hu Y S, Li H, Wang Z X, Xu H X, Huang X J, Chen L Q 2011 J. Electrochem. 17 12
[85]	孙姝纬, 赵慧玲, 郁彩艳, 白莹 2019 储能科学与技术 5 975 Sun S W, Zhao H L, Yu C Y, Bai Y 2019 Energy Storage Sci. Technol. 5 975
[86]	Matsuda Y, Kuwata N, Okawa T, Dorai A, Kamishima O, Kawamura J 2019 Solid State Ionics 335 7 Google Scholar
[87]	Wang C, Liang J, Jiang M, Li X, Mukherjee S, Adair K, Zheng M, Zhao Y, Zhao F, Zhang S, Li R, Huang H, Zhao S, Zhang L, Lu S, Singh C V, Sun X 2020 Nano Energy 76 105015 Google Scholar
[88]	Zhou Y, Doerrer C, Kasemchainan J, Bruce P G, Pasta M, Hardwick L J 2020 Batteries & Supercaps 3 647
[89]	耿福山, 胡炳文 2019 储能科学与技术 8 1017 Geng F S, Hu B W 2019 Energy Storage Sci. Technol. 8 1017
[90]	傅日强, 刘湘思, 向宇轩, 钟贵明, 李琦, 郑时尧, 杨勇 2019 电源技术 43 5 Google Scholar Fu R Q, Liu X S, Xiang Y X, Zhong G M, Li Q, Zheng S R, Yang Y 2019 Chin. J. Power Sources 43 5 Google Scholar
[91]	Huo H, Lin Z, Wu D, Zhong G, Shao J, Xu X, Xie B, Ma Y, Dai C, Du C, Zuo P, Yin G, Peng L 2019 ACS Appl. Energy Mater. 2 3692 Google Scholar
[92]	Kitada K, Pecher O, Magusin P C M M, Groh M F, Weatherup R S, Grey C P 2019 J. Am. Chem. Soc. 141 7014 Google Scholar
[93]	Bhattacharyya R, Key B, Chen H, Best A S, Hollenkamp A F, Grey C P 2010 Nat. Mater. 9 504 Google Scholar
[94]	Forse Alexander C, Griffin John M, Merlet C, Carretero-Gonzalez J, Raji A-Rahman O, Trease Nicole M, Grey Clare P 2017 Nat. Energy 2 16216 Google Scholar
[95]	Xiang Y, Zheng G, Liang Z, Jin Y, Liu X, Chen S, Zhou K, Zhu J, Lin M, He H, Wan J, Yu S, Zhong G, Fu R, Li Y, Yang Y 2020 Nat. Nanotechnol. 15 883 Google Scholar
[96]	Zhao E W, Liu T, Jónsson E, Lee J, Temprano I, Jethwa R B, Wang A, Smith H, Carretero-González J, Song Q, Grey C P 2020 Nature 579 224 Google Scholar
[97]	Liu X, Wang D, Wan L 2015 Sci. Bull. 60 839 Google Scholar
[98]	Deng X, Liu X, Yan H, Wang D, Wan L 2014 Sci. China Chem. 57 178 Google Scholar
[99]	Zhu J, Feng J, Lu L, Zeng K 2012 J. Power Sources 197 224 Google Scholar
[100]	Liu T, Lin L, Bi X, Tian L, Yang K, Liu J, Li M, Chen Z, Lu J, Amine K, Xu K, Pan F 2019 Nat. Nanotechnol. 14 50 Google Scholar
[101]	Wan J, Hao Y, Shi Y, Song Y X, Yan H J, Zheng J, Wen R, Wan L J 2019 Nat. Commun. 10 3265 Google Scholar
[102]	Bartsch T, Strauss F, Hatsukade T, Schiele A, Kim A Y, Hartmann P, Janek J, Brezesinski T 2018 ACS Energy Lett. 3 2539 Google Scholar
[103]	Yamagishi Y, Morita H, Nomura Y, Igaki E 2021 ACS Appl. Mater. Interfaces 13 580 Google Scholar
[104]	Marceau H, Kim C S, Paolella A, Ladouceur S, Lagacé M, Chaker M, Vijh A, Guerfi A, Julien C M, Mauger A, Armand M, Hovington P, Zaghib K 2016 J. Power Sources 319 247 Google Scholar
[105]	Wan M, Kang S, Wang L, Lee H W, Zheng G W, Cui Y, Sun Y 2020 Nat. Commun. 11 829 Google Scholar
[106]	Otoyama M, Sakuda A, Hayashi A, Tatsumisago M 2018 Solid State Ionics 323 123 Google Scholar
[107]	Nishikawa K, Munakata H, Kanamura K 2013 J. Power Sources 243 630 Google Scholar
[108]	Sethuraman V A, Chon M J, Shimshak M, Van Winkle N, Guduru P R 2010 Electrochem. Commun. 12 1614 Google Scholar

Cited By

图 1 典型表征技术的空间(x轴)与时间及能量(y轴)分辨率^[31]

Figure 1. Spatial (x-axis) and time/energy (y-axis) resolution of typical characterization techniques^[31].

DownLoad: Full-Size Img PowerPoint

图 2 (a) 原位电化学扫描电子显微镜电池示意图^[34]; 在电流密度为50 μA·cm^–2下, 锂电池在沉积反应过程中的原位SEM图像 (b) 0 s; (c) 30 s; (d) 60 s; (e) 150 s; (f) 300 s; (g) 900 s; (h) 1800 s; (i) 3600 s^[34]

Figure 2. (a) Schematic diagram of the battery design for in situ electrochemical SEM^[34]; in situ SEM images of the Cu working electrode acquired at (b) 0, (c) 30, (d) 60, (e) 150, (f) 300, (g) 900, (h) 1800 and (i) 3600 s, during Li plating at the current density of 50 μA·cm^–2^[34].

DownLoad: Full-Size Img PowerPoint

图 3 (a) 原位电化学扫描电子显微镜电池示意图^[35]; (b) 在锂电沉积过程中间隔5 min的连续SEM图像^[35]; (c) 在(b)虚线方格区域内锂电沉积过程中间隔200 s的连续SEM图像^[35]; (d) 锂棒冲破Cu CC膜的生长示意图^[35]; (e) 用蒸馏水除去电沉积锂后Cu CC膜的SEM图像^[35]

Figure 3. (a) Electrochemical cell design for the in situ SEM observation^[35]; sequential SEM images taken (b) every 5 min, and (c) every 200 s of the region in the dashed region in Figure (b)^[35]; (d) illustration of the breaking of the Cu CC film by the growth of a Li rod^[35]; (e) SEM image of the Cu CC film after removing the plated lithium with distilled water^[35].

DownLoad: Full-Size Img PowerPoint

图 4 (a) 用于原位SEM观测的微型全固态Li-O₂电池示意图^[36]; 在锂氧电池的(b)放电和(c)充电过程中的原位SEM照片^[36]

Figure 4. (a) Schematic view of a microscale all solid-state Li-O₂ battery for in situ SEM observation^[36]; in situ SEM images of the cathode surface during the (b) discharge and (c) charge process^[36].

DownLoad: Full-Size Img PowerPoint

图 5 (a) 固态电池中正极与固体电解质LASGTP界面附近的ADF-STEM图像^[38]; (b) 为(a)中正极在充放电过程中锂平均浓度的变化^[38]; (c), (d)分别在1−3点和4−6点锂浓度的变化^[38]; (e)−(j)在阶段A (3−18 nA·h)、阶段B (39−53 nA·h)和阶段C(充放电反应间30 min开路状态)锂分布的变化^[38]

Figure 5. (a) ADF-STEM image of the interfacial region between the cathode and solid electrolyte LASGTP in the solid-state battery^[38]; (b) evolution of the average Li concentration in the entire cathode film in Figure (a)^[38]; (c), (d) evolution of Li concentrations at points 1−3 and 4−6, respectively; (e)−(j) evolution of the Li maps at stages A (3−18 nA·h), B (39−53 nA·h), and C (open-circuit state for 30 min between the charge and discharge reactions), respectively^[38].

DownLoad: Full-Size Img PowerPoint

图 6 (a)−(d) LATP与锂金属反应的原位TEM图^[39]; 与金属锂反应前(e)和后(f)LATP的SAED图^[39]; 在无人工层(g)和有保护层(h)下LATP|Li界面的化学-机械失效机制^[39]

Figure 6. (a)−(d) In situ TEM images of the reaction between a LATP wire and a Li metal^[39]; SAED pattern of LATP before (e) and after (f) reaction with the lithium metal^[39]; illustration of the chemomechanical failure mechanism at the LATP|lithium interface: (g) without an artificial layer^[39]; (h) with the protection layer^[39].

DownLoad: Full-Size Img PowerPoint

图 7 (a) AFM–ETEM装置示意图^[41]; (b) TEM图像显示一个AFM悬臂梁接近锂金属的对电极^[41]; (c) TEM图像显示碳纳米管附着在扁平的AFM尖端上^[41]; (d), (e), (g) 锂晶须生长的延时TEM图像^[41]; (f) 不同生长方向锂晶须的最大应力σ_m与等效直径的关系图^[41]; (h) 8个锂晶须测试的临界压应力(当锂晶须停止生长时)与施加电压的关系^[41]

Figure 7. (a) Schematic diagram of the AFM–ETEM set-up^[41]; (b) TEM image showing an AFM cantilever approaching the counter electrode of Li metal^[41]; (c) TEM image showing a CNT attached to a flattened AFM tip^[41]; (d), (e), (g) time-lapse TEM images of Li whisker growth^[41]; (f) plot of the maximum stress σ_m versus equivalent diameter for Li whiskers with different growth directions^[41]; (h) critical compressive stress (when the growth of a Li whisker stops) versus applied voltage for eight Li whiskers tested^[41].

DownLoad: Full-Size Img PowerPoint

图 8 用于进行(a)反射式^[48]与(b)透射式^[49]原位XRD测试的典型电池装置示意图; (c) 在一个充电-放电循环中, 利用同步辐射X光进行原位XRD表征所获得的NCM811正极XRD图谱^[49]; (d) 在指定数目的充放电循环中, 同步辐射原位XRD在1.3 Å^–1附近所获得的图谱^[49]; (e) 基于(d)中数据进行精修与物相分析所获得的各物相含量变化^[49]

Figure 8. Schematic diagram of typical setup for in situ XRD of batteries in (a) reflection mode^[48], and (b) transmission mode^[49]; (c) the in situ XRD pattern of a NCM811 cathode during a charge-discharge cycle, with the synchrotron X-ray, with local zoom in view at around 1.3 Å^–1 shown in Figure (d)^[49]; (e) evolution of relative concentration of different phases calculated based on data in Figure (d)^[49].

DownLoad: Full-Size Img PowerPoint

图 9 (a) 典型用于原位XPS的固态电池^[60]及(b) 原位XPS系统^[57]示意图; 在Li₁₀GeP₂S₁₂ (LGPS)固体电解质上通过电化学沉积31 nm锂金属过程中, 原位XPS所检测的(c) S 2p谱、(d) Ge 3d谱, 以及(e) P 2p/Ge 3p谱, 及(f)各谱峰对应组分的相对摩尔含量随时间的变化, 包括Li₃P, Li₂S和Li–Ge合金等^[57]; (c)−(e) 中, 渐变色竖条代表典型组分的能谱峰区^[57]

Figure 9. (a) Typical solid-state battery for in situ XPS characterization^[60], and (b) Diagram of in situ XPS system^[57]; during the electrochemical deposition of 31 nm thick Li metal on LGPS solid electrolyte, evolution of the (c) S 2p spectra, (d) Ge 3d spectra, (e) P 2p/Ge 2p spectra, and (f) the evolution of relative molar concentration of phases, including Li₃P, Li₂S, and Li–Ge alloy, etc^[57]; the color stripes in Figure (c)−(e) indicate binding energy regions of typical compositions^[57].

DownLoad: Full-Size Img PowerPoint

图 10 (a) 典型原位XANES系统^[52]及(b)对应电池结构设计示意图^[52]; 在(c)干燥空气和湿气混合物中, (d)干燥空气中, 及(e) 氩气和湿气混合物中, 120 min内对固体电解质Li₃InCl₆的原位XANES的Cl K-边谱图^[52]; (f) 对全固态电池NMC811-LGPS的原位工况XANES S K-边谱图及其(g)微分投影图^[66]; (h) Ni K-边谱以及(i)电池的充电/放电曲线^[66]

Figure 10. (a) Diagram of a typical in situ XANES system^[52], and (b) the corresponding battery structure design^[52]; Cl K-edge XANES spectra of the solid electrolyte Li₃InCl₆ acquired during its exposure for120 min in (c) mixture of dry air and moisture, (d) dry air, and (e) mixture of Ar and moisture^[52]; (f) operando S K-edge spectra with (g) first derivative mapping, and (h) Ni K-edge of a NCM811-LGPS solid state battery during a full cycle, with the charge/discharge profile shown in Figure (i)^[66]

DownLoad: Full-Size Img PowerPoint

图 11 (a) XANES对Cu₆Sn₅负极的原位成像过程^[67]; 原位二维TXM-XANES对(b)全固态锂电池、及(c)传统基于液体电解质的锂离子电池对正极材料NCM622颗粒在充电过程中的实时成像及状态示意图^[68]

Figure 11. (a) Image formation process based on in situ XANES investigation of a Cu₆Sn₅ anode^[67]; in operando 2D TXM-XANES mapping of a NCM622 cathode particle during its charging process in (b) a solid-state battery, and (c) a Li-ion battery based on a conventional liquid electrolyte, with the corresponding schematic view included^[68].

DownLoad: Full-Size Img PowerPoint

图 12 (a) X射线层析成像原理示意图^[70]. 相干X射线光源穿透位于可旋转台上的样品后被闪烁体转换为可见光, 光学放大后被CMOS相机拍摄成像, 然后样品旋转一个小角度进行成像, 最后对不同角度采集的投影照片重构为三维结构; (b) 原位X射线层析成像对Li|LGPS|Li电池在循环过程中LGPS片表面形貌实时监测所获得的三维结构^[72]; 原位X射线层析成像监测下, (c) 在1 mA·cm^–2电流下Li|LSPS界面随时间的变化, 其中蓝色区域表示锂金属, 棕红色区域代表界面, 黄色区域代表LSPS固体电解质^[74]; (d) Li|LSPS界面及两电极在此电流下的体积变化^[74]; (e) 电流中实际用于锂氧化的比率随界面层厚度的变化曲线^[74]; (f) Li|LSPS界面孔隙在脱锂过程中的演变过程^[74]

Figure 12. (a) Schematic diagram of the X-ray tomography process^[70]. Coherent X-rays are transmitted through the sample mounted on a rotating stage and then converted into visible light via a scintillator, the image is then optically magnified and recorded by a CMOS detector. The projected imaging process was continued during the gradual rotation of the sample, finally the data set is reconstructed into a 3D structure; (b) 3D morphology renderings of a LGPS pellet during the cycling of a Li|LGPS|Li battery with operando X-ray tomography^[72]; (c) operando X-ray tomography detected 3D growth of the Li|LSPS interface at 1 mA·cm^–2 current, with blue region indicates Li metal, brown for the interface, and yellow for LSPS solid electrolyte^[74]; (d) volumetric evolution of Li|LSPS interface and the Li at the two electrodes based on Figure (c)^[74]; (e) profile of the fraction of total current due to Li oxidation vs the thickness of the interface^[74]; (f) evolution of the voids at the Li|LSPS interface region during the stripping process^[74].

DownLoad: Full-Size Img PowerPoint

图 13 (a) 原位3D CT-XANES测试示意图^[76]; (b) 对复合电极(LiCoO₂∶Li_2.2Co_0.8O₃ = 8∶2)在充放电过程中的原位3D CT-XANES扫描^[76]; LiFePO₄颗粒在充电过程中的(c)物相变化及(d)物相比率变化^[77]

Figure 13. (a) Schematic diagram of the operando CT-XANES system^[76]; (b) 3D mapping of the composite electrode (LiCoO₂∶Li_2.2Co_0.8O₃ = 8∶2) during the charge process^[76]; the evolution of (c) phases and (d) phase volume fraction in the LiFePO₄ particle during the charge process^[77].

DownLoad: Full-Size Img PowerPoint

图 14 (a) NDP系统示意图^[83]; (b) 用于NDP检测非对称电池的结构设计; 对称电池中只需将此电池中的CNT正极更改为Li金属^[83]; (c) 典型Li|LLZO|Li对称电池的原位NDP谱图^[83]; (d) 为其中一个镀锂-脱锂循环过程中的NDP谱图^[83]; (e) 循环过程中对电池每5 min采集一次NDP谱后的二维(2D)投影图^[83]; (f) 在前期循环过程中, 及(g)在动态短路过程中, 用于诊断对称电池中锂枝晶短路的原位NDP谱图, 图中蓝色线表示电压, 绿色线是电量曲线, 红色线为NDP信号积分值; (h)为”动态短路”机理示意图^[83]

Figure 14. Schematic of the (a) NDP system, and (b) asymmetric battery design for NDP measurement; while only the CNT cathode needs to be replaced by Li metal in symmetric cells^[83]; typical in situ NDP spectra of a Li|LLZO|Li symmetric cell (c) at different times, and (d) during a plating-stripping cycle^[83]; (e) 2D projection of the NDP spectra acquired every 5 min during the cycling process of the symmetric cell^[83]; in situ NDP measurement for diagnosing short-circuit of a symmetric cell during the (f) predicted and (g) “dynamic short-circuit” stage of the cycling process, with blue for voltage, green for charge, and red for NDP counts, respectively^[83]; (h) schematic of the “dynamic short-circuit” mechanism^[83].

DownLoad: Full-Size Img PowerPoint

图 15 用于进行原位拉曼检测LiCoO₂ 电极的(a)正面和(b)背面的电池示意图^[86]; 对Li_xCoO₂正极正面在(c)充电与(d)放电过程中进行原位拉曼检测的拉曼光谱^[86]

Figure 15. Schematic diagram of the battery design for in situ Raman measurement of the LiCoO₂ electrode at (a) the front side and (b) the backside^[86]; in situ Raman spectra acquired at front side of the Li_xCoO₂ cathode during (c) charging and (d) discharging process^[86].

DownLoad: Full-Size Img PowerPoint

图 16 (a) 典型原位固态NMR电池的组成, 包括集流体、电极、隔膜以及三个由聚醚醚酮PEEK制成的电池支撑结构^[92]; (b) 组装后的原位固态NMR电池及(c)在NMR探头里的照片^[92]; 用于进行原位固态MRI而采用(d)平行线形与(e)圆盘电极的电池示意图^[92].; 对基于(f)纯硅与(g)无定形SiO (a-SiO)电极的半电池进行的 ⁷Li原位NMR波普及电压随时间的变化曲线^[92]. 对由含有锂涂层的铜圆盘电极片组成的对称电池进行的原位¹H SPRITE (T1加权单点攀升成像, 即single point ramped imaging with T1 enhancement) MRI成像图片: (h) 初始状态^[29]; 在10 μA电流下运行(i) 17, (j) 34, (k) 51 h后^[29]; 该电池在反向电流下运行 (l) 6, (m) 40, (n) 57, 及 (o) 77 h后^[29]

Figure 16. (a) Components of a typical battery for solid state NMR measurement, including current collector, electrodes, separator, and the plastic cell capsule consisting of 3 PEEK structures^[92]; (b) a NMR battery after assembly^[92]; (c) a photo of the battery in the NMR probe^[92]; schematic of symmetric cells with (d) parallel wire, and (e) disk electrodes^[92]; ⁷Li in situ NMR spectra and cell voltage during the cycling of the half-cell based on (f) pure Si, and (g) a-SiO electrode^[92]; in situ ¹H SPRITE MRI images of the lithium coated copper disk electrodes in a symmetric cell: (h) At initial state, after operation at +10 μA for (i) 17, (j) 34 and (k) 51 h; and after operation at –10 μA current for (l) 6, (m) 40 and (o) 77 h^[29].

DownLoad: Full-Size Img PowerPoint

[1]	An W, Gao B, Mei S, Xiang B, Fu J, Wang L, Zhang Q, Chu P K, Huo K 2019 Nat. Commun. 10 1447 Google Scholar
[2]	Lu J Y, Xu C 2020 Chem 6 3165 Google Scholar
[3]	Manthiram A, Yu X, Wang S 2017 Nat. Rev. Mater. 2 16103 Google Scholar
[4]	Randau S, Weber D A, Kötz O, Koerver R, Braun P, Weber A, Ivers-Tiffée E, Adermann T, Kulisch J, Zeier W G, Richter F H, Janek J 2020 Nat. Energy 5 259 Google Scholar
[5]	Zuo J H, Gong Y J 2020 Tungsten 2 134 Google Scholar
[6]	Zhao C, Xu G L, Yu Z, Zhang L, Hwang I, Mo Y X, Ren Y, Cheng L, Sun C J, Ren Y, Zuo X, Li J T, Sun S G, Amine K, Zhao T 2021 Nat. Nanotechnol. 16 166 Google Scholar
[7]	Cao Z J, Zhang Y Z, Cui Y L S, Li B, Yang S B 2020 Tungsten 2 162 Google Scholar
[8]	Lu J, Dey S, Temprano I, Jin Y, Xu C, Shao Y, Grey C P 2020 ACS Energy Lett. 5 3681 Google Scholar
[9]	Liu T, Vivek J P, Zhao E W, Lei J, Garcia-Araez N, Grey C P 2020 Chem. Rev. 120 6558 Google Scholar
[10]	Guo H, Hou G, Dai L, Yao Y, Wei C, Liang Z, Si P, Ci L 2020 J. Phys. Chem. Lett. 11 172 Google Scholar
[11]	Kato Y, Hori S, Saito T, Suzuki K, Hirayama M, Mitsui A, Yonemura M, Iba H, Kanno R 2016 Nat. Energy 1 16030 Google Scholar
[12]	Zhou L, Park K H, Sun X, Lalère F, Adermann T, Hartmann P, Nazar L F 2019 ACS Energy Lett. 4 265 Google Scholar
[13]	Ji X, Hou S, Wang P, He X, Piao N, Chen J, Fan X, Wang C 2020 Adv. Mater. 32 2002741 Google Scholar
[14]	Zhao Q, Stalin S, Zhao C Z, Archer L A 2020 Nat. Rev. Mater. 5 229 Google Scholar
[15]	Xu L, Li J, Deng W, Shuai H, Li S, Xu Z, Li J, Hou H, Peng H, Zou G, Ji X 2021 Adv. Energy Mater. 11 2000648 Google Scholar
[16]	Lilu Liu, Fan Wu, Hong Li, Chen L 2019 J. Chin. Ceramic Soc. 47 1367
[17]	Chung H, Kang B 2017 Chem. Mater. 29 8611 Google Scholar
[18]	Han F, Zhu Y, He X, Mo Y, Wang C 2016 Adv. Energy Mater. 6 1501590 Google Scholar
[19]	Zhang S N, Zeng Z, Zhai W, Hou G M, Chen L N, Ci L J 2021 Adv. Mater. Interfaces. 8 2100072 Google Scholar
[20]	拱越, 谷林 2020 物理学报 69 226801 Google Scholar Gong Y, Gu L 2020 Acta Phys. Sin. 69 226801 Google Scholar
[21]	冯吴亮, 王飞, 周星, 吉晓, 韩福东, 王春生 2020 物理学报 69 228206 Google Scholar Feng W L, Wang F, Zhou X, Ji X, Han F D, Wang C S 2020 Acta Phys. Sin. 69 228206 Google Scholar
[22]	Banerjee A, Wang X, Fang C, Wu E A, Meng Y S 2020 Chem. Rev. 120 6878 Google Scholar
[23]	Symington A R, Molinari M, Dawson J A, Statham J M, Purton J, Canepa P, Parker S C 2021 J. Mater. Chem. A 9 6487 Google Scholar
[24]	Grey C P, Tarascon J M 2017 Nat. Mater. 16 45 Google Scholar
[25]	Cheng Y, Zhang L, Zhang Q, Li J, Tang Y, Delmas C, Zhu T, Winter M, Wang M S, Huang J 2021 Mater. Today 42 137 Google Scholar
[26]	Li W, Lutz D M, Wang L, Takeuchi K J, Marschilok A C, Takeuchi E S 2021 Joule 5 77 Google Scholar
[27]	李文俊, 郑杰允, 谷林, 李泓 2015 电化学 21 99 Li W J, Zheng J Y, Gu L, Li H 2015 J. Electrochem. 21 99
[28]	潘弘毅, 禹习谦, 李泓, 李泉 2021 物理化学学报 37 2008090 Pan H Y, Yu X Q, Li H, Li Q 2021 Acta Phys. Sin. 37 2008090
[29]	Romanenko K, Jin L, Howlett P, Forsyth M 2016 Chem. Mater. 28 2844 Google Scholar
[30]	Ishikawa R, Jimbo Y, Terao M, Nishikawa M, Ueno Y, Morishita S, Mukai M, Shibata N, Ikuhara Y 2020 Microscopy 69 240 Google Scholar
[31]	Hou P, Chu G, Gao J, Zhang Y, Zhang L 2016 Chin. Phys. B 25 016104 Google Scholar
[32]	余启鹏, 刘琦, 王自强, 李宝华 2020 物理学报 69 228805 Google Scholar Yu Q P, Liu Q, Wang Z Q, Li B H 2020 Acta Phys. Sin. 69 228805 Google Scholar
[33]	曹文卓, 李泉, 王胜彬, 李文俊, 李泓 2020 物理学报 69 228204 Google Scholar Cao W Z, Li Q, Wang S B, Li W J, Li H 2020 Acta Phys. Sin. 69 228204 Google Scholar
[34]	Sagane F, Shimokawa R, Sano H, Sakaebe H, Iriyama Y 2013 J. Power Sources 225 245 Google Scholar
[35]	Motoyama M, Ejiri M, Iriyama Y 2015 J. Electrochem. Soc. 162 A7067 Google Scholar
[36]	Zheng H, Xiao D, Li X, Liu Y, Wu Y, Wang J, Jiang K, Chen C, Gu L, Wei X, Hu Y S, Chen Q, Li H 2014 Nano Lett. 14 4245 Google Scholar
[37]	柯承志, 肖本胜, 李苗, 陆敬予, 何洋, 张力, 张桥保 2021 储能科学与技术 10 1219 Google Scholar Ke C Z, Xiao B S, Li M, Lu J Y, He Y, Zhang L, Zhang Q B 2021 Energy Storage Sci. Technol. 10 1219 Google Scholar
[38]	Nomura Y, Yamamoto K, Fujii M, Hirayama T, Igaki E, Saitoh K 2020 Nat. Commun. 11 2824 Google Scholar
[39]	Zhu J, Zhao J, Xiang Y, Lin M, Wang H, Zheng B, He H, Wu Q, Huang J Y, Yang Y 2020 Chem. Mater. 32 4998 Google Scholar
[40]	梁宇皓, 范丽珍 2020 物理学报 69 226201 Google Scholar Liang Y H, Fan L Z 2020 Acta Phys. Sin. 69 226201 Google Scholar
[41]	Zhang L, Yang T, Du C, Liu Q, Tang Y, Zhao J, Wang B, Chen T, Sun Y, Jia P, Li H, Geng L, Chen J, Ye H, Wang Z, Li Y, Sun H, Li X, Dai Q, Tang Y, Peng Q, Shen T, Zhang S, Zhu T, Huang J 2020 Nat. Nanotechnol. 15 94
[42]	Wang Z, Tang Y, Zhang L, Li M, Shan Z, Huang J 2020 Small 16 2001899
[43]	Lu P, Yan P, Romero E, Spoerke E D, Zhang J G, Wang C M 2015 Chem. Mater. 27 1375 Google Scholar
[44]	Lin F, Markus I M, Doeff M M, Xin H L 2014 Sci. Rep. 4 5694
[45]	Shim J H, Kang H, Lee S, Kim Y M 2021 J. Mater. Chem. A 9 2429 Google Scholar
[46]	Wang X, Li Y, Meng Y S 2018 Joule 2 2225 Google Scholar
[47]	Li Y, Li Y, Pei A, Yan K, Sun Y, Wu C L, Joubert L M, Chin R, Koh A L, Yu Y, Perrino J, Butz B, Chu S, Cui Y 2017 Science 358 506 Google Scholar
[48]	Llewellyn A V, Matruglio A, Brett D J L, Jervis R, Shearing P R 2020 Condens. Matter 5 75 Google Scholar
[49]	Xu C, Märker K, Lee J, Mahadevegowda A, Reeves P J, Day S J, Groh M F, Emge S P, Ducati C, Layla Mehdi B, Tang C C, Grey C P 2021 Nat. Mater. 20 84 Google Scholar
[50]	Bak S M, Hu E, Zhou Y, Yu X, Senanayake S D, Cho S J, Kim K B, Chung K Y, Yang X Q, Nam K W 2014 ACS Appl. Mater. Interfaces 6 22594 Google Scholar
[51]	Safanama D, Sharma N, Rao R P, Brand H E A, Adams S 2016 J. Mater. Chem. A 4 7718 Google Scholar
[52]	Li W, Liang J, Li M, Adair K R, Li X, Hu Y, Xiao Q, Feng R, Li R, Zhang L, Lu S, Huang H, Zhao S, Sham T K, Sun X 2020 Chem. Mater. 32 7019 Google Scholar
[53]	Bartsch T, Kim A Y, Strauss F, de Biasi L, Teo J H, Janek J, Hartmann P, Brezesinski T 2019 Chem. Commun. 55 11223 Google Scholar
[54]	Goonetilleke D, Sharma N, Kimpton J, Galipaud J, Pecquenard B, Le Cras F 2018 Front. Energy Res. 6 64 Google Scholar
[55]	刘丽露, 吴凡, 李泓, 陈立泉 2019 硅酸盐学报 47 1367 Liu L L, Wu F, Li H, Chen L Q 2019 J. Chin. Ceram. Soc. 47 1367
[56]	张桥保, 龚正良, 杨勇 2020 物理学报 69 228803 Google Scholar Zhang Q B, Gong Z L, Yang Y 2020 Acta Phys. Sin. 69 228803 Google Scholar
[57]	Wenzel S, Randau S, Leichtweiß T, Weber D A, Sann J, Zeier W G, Janek J 2016 Chem. Mater. 28 2400 Google Scholar
[58]	Wenzel S, Weber D A, Leichtweiss T, Busche M R, Sann J, Janek J 2016 Solid State Ionics 286 24 Google Scholar
[59]	Wu J, Liu S, Han F, Yao X, Wang C 2021 Adv. Mater. 33 2000751 Google Scholar
[60]	Endo R, Ohnishi T, Takada K, Masuda T 2020 J. Phys. Chem. Lett. 11 6649 Google Scholar
[61]	张念, 任国玺, 章辉, 周櫈, 刘啸嵩 2020 物理学报 69 228806 Google Scholar Zhang N, Ren G X, Zhang H, Zhou D, Liu X G 2020 Acta Phys. Sin. 69 228806 Google Scholar
[62]	蔡明俐, 姚柳, 靳俊, 温兆银 2021 物理化学学报 37 2009006 Cai L, Yao L, Qi J, Wen Z 2021 Acta Phys. -Chim. Sin. 37 2009006
[63]	赵宁, 穆爽, 郭向欣 2020 物理学报 69 228804 Google Scholar Zhao N, Mu S, Guo X X 2020 Acta Phys. Sin. 69 228804 Google Scholar
[64]	Connell J G, Fuchs T, Hartmann H, Krauskopf T, Zhu Y, Sann J, Garcia-Mendez R, Sakamoto J, Tepavcevic S, Janek J 2020 Chem. Mater. 32 10207 Google Scholar
[65]	Liu Z, Li G, Borodin A, Liu X, Li Y, Endres F 2019 J. Solid State Electrochem. 23 2107 Google Scholar
[66]	Li X, Ren Z, Norouzi Banis M, Deng S, Zhao Y, Sun Q, Wang C, Yang X, Li W, Liang J, Li X, Sun Y, Adair K, Li R, Hu Y, Sham T K, Huang H, Zhang L, Lu S, Luo J, Sun X 2019 ACS Energy Lett. 4 2480 Google Scholar
[67]	Gonzalez Malabet H J, Juarez Robles D, de Andrade V, Mukherjee P P, Nelson G J 2020 J. Electrochem. Soc. 167 40523 Google Scholar
[68]	Lou S, Liu Q, Zhang F, Liu Q, Yu Z, Mu T, Zhao Y, Borovilas J, Chen Y, Ge M, Xiao X, Lee W K, Yin G, Yang Y, Sun X, Wang J 2020 Nat. Commun. 11 5700 Google Scholar
[69]	Wood V 2018 Nat. Rev. Mater. 3 293 Google Scholar
[70]	Pietsch P, Wood V 2017 Annu. Rev. Mater. Res. 47 451 Google Scholar
[71]	Wu X, Billaud J, Jerjen I, Marone F, Ishihara Y, Adachi M, Adachi Y, Villevieille C, Kato Y 2019 Adv. Energy Mater. 9 1901547 Google Scholar
[72]	Madsen K E, Bassett K L, Ta K, Sforzo B A, Matusik K E, Kastengren A L, Gewirth A A 2020 Adv. Mater. Interfaces 7 2000751 Google Scholar
[73]	Sun F, Dong K, Osenberg M, Hilger A, Risse S, Lu Y, Kamm P H, Klaus M, Markötter H, García-Moreno F, Arlt T, Manke I 2018 J. Mater. Chem. A 6 22489 Google Scholar
[74]	Lewis J A, Cortes F J Q, Liu Y, Miers J C, Verma A, Vishnugopi B S, Tippens J, Prakash D, Marchese T S, Han S Y, Lee C, Shetty P P, Lee H W, Shevchenko P, De Carlo F, Saldana C, Mukherjee P P, McDowell M T 2021 Nat. Mater. 20 503 Google Scholar
[75]	Kimura Y, Tomura A, Fakkao M, Nakamura T, Ishiguro N, Sekizawa O, Nitta K, Uruga T, Okumura T, Tada M, Uchimoto Y, Amezawa K 2020 J. Phys. Chem. Lett. 11 3629 Google Scholar
[76]	Kimura Y, Fakkao M, Nakamura T, Okumura T, Ishiguro N, Sekizawa O, Nitta K, Uruga T, Tada M, Uchimoto Y, Amezawa K 2020 ACS Appl. Energy Mater. 3 7782 Google Scholar
[77]	Wang J, Karen Chen-Wiegart Y C, Eng C, Shen Q, Wang J 2016 Nat. Commun. 7 12372 Google Scholar
[78]	Xiang Y, Li X, Cheng Y, Sun X, Yang Y 2020 Mater. Today 36 139 Google Scholar
[79]	Liang G, Didier C, Guo Z, Pang W K, Peterson V K 2020 Adv. Mater. 32 1904528 Google Scholar
[80]	郑国瑞, 向宇轩, 杨勇 2021 物理化学学报 37 2008094 Zheng G R, Xiang Y X, Yang Y 2021 Acta Phys. -Chim. Sin. 37 2008094
[81]	Kaup K, Zhou L, Huq A, Nazar L F 2020 J. Mater. Chem. A 8 12446 Google Scholar
[82]	Li Q, Yi T, Wang X, Pan H, Quan B, Liang T, Guo X, Yu X, Wang H, Huang X, Chen L, Li H 2019 Nano Energy 63 103895 Google Scholar
[83]	Wang C, Gong Y, Dai J, Zhang L, Xie H, Pastel G, Liu B, Wachsman E, Wang H, Hu L 2017 J. Am. Chem. Soc. 139 14257 Google Scholar
[84]	赵亮, 胡勇胜, 李泓, 王兆翔, 徐红星, 黄学杰, 陈立泉 2011 电化学 17 12 Zhao L, Hu Y S, Li H, Wang Z X, Xu H X, Huang X J, Chen L Q 2011 J. Electrochem. 17 12
[85]	孙姝纬, 赵慧玲, 郁彩艳, 白莹 2019 储能科学与技术 5 975 Sun S W, Zhao H L, Yu C Y, Bai Y 2019 Energy Storage Sci. Technol. 5 975
[86]	Matsuda Y, Kuwata N, Okawa T, Dorai A, Kamishima O, Kawamura J 2019 Solid State Ionics 335 7 Google Scholar
[87]	Wang C, Liang J, Jiang M, Li X, Mukherjee S, Adair K, Zheng M, Zhao Y, Zhao F, Zhang S, Li R, Huang H, Zhao S, Zhang L, Lu S, Singh C V, Sun X 2020 Nano Energy 76 105015 Google Scholar
[88]	Zhou Y, Doerrer C, Kasemchainan J, Bruce P G, Pasta M, Hardwick L J 2020 Batteries & Supercaps 3 647
[89]	耿福山, 胡炳文 2019 储能科学与技术 8 1017 Geng F S, Hu B W 2019 Energy Storage Sci. Technol. 8 1017
[90]	傅日强, 刘湘思, 向宇轩, 钟贵明, 李琦, 郑时尧, 杨勇 2019 电源技术 43 5 Google Scholar Fu R Q, Liu X S, Xiang Y X, Zhong G M, Li Q, Zheng S R, Yang Y 2019 Chin. J. Power Sources 43 5 Google Scholar
[91]	Huo H, Lin Z, Wu D, Zhong G, Shao J, Xu X, Xie B, Ma Y, Dai C, Du C, Zuo P, Yin G, Peng L 2019 ACS Appl. Energy Mater. 2 3692 Google Scholar
[92]	Kitada K, Pecher O, Magusin P C M M, Groh M F, Weatherup R S, Grey C P 2019 J. Am. Chem. Soc. 141 7014 Google Scholar
[93]	Bhattacharyya R, Key B, Chen H, Best A S, Hollenkamp A F, Grey C P 2010 Nat. Mater. 9 504 Google Scholar
[94]	Forse Alexander C, Griffin John M, Merlet C, Carretero-Gonzalez J, Raji A-Rahman O, Trease Nicole M, Grey Clare P 2017 Nat. Energy 2 16216 Google Scholar
[95]	Xiang Y, Zheng G, Liang Z, Jin Y, Liu X, Chen S, Zhou K, Zhu J, Lin M, He H, Wan J, Yu S, Zhong G, Fu R, Li Y, Yang Y 2020 Nat. Nanotechnol. 15 883 Google Scholar
[96]	Zhao E W, Liu T, Jónsson E, Lee J, Temprano I, Jethwa R B, Wang A, Smith H, Carretero-González J, Song Q, Grey C P 2020 Nature 579 224 Google Scholar
[97]	Liu X, Wang D, Wan L 2015 Sci. Bull. 60 839 Google Scholar
[98]	Deng X, Liu X, Yan H, Wang D, Wan L 2014 Sci. China Chem. 57 178 Google Scholar
[99]	Zhu J, Feng J, Lu L, Zeng K 2012 J. Power Sources 197 224 Google Scholar
[100]	Liu T, Lin L, Bi X, Tian L, Yang K, Liu J, Li M, Chen Z, Lu J, Amine K, Xu K, Pan F 2019 Nat. Nanotechnol. 14 50 Google Scholar
[101]	Wan J, Hao Y, Shi Y, Song Y X, Yan H J, Zheng J, Wen R, Wan L J 2019 Nat. Commun. 10 3265 Google Scholar
[102]	Bartsch T, Strauss F, Hatsukade T, Schiele A, Kim A Y, Hartmann P, Janek J, Brezesinski T 2018 ACS Energy Lett. 3 2539 Google Scholar
[103]	Yamagishi Y, Morita H, Nomura Y, Igaki E 2021 ACS Appl. Mater. Interfaces 13 580 Google Scholar
[104]	Marceau H, Kim C S, Paolella A, Ladouceur S, Lagacé M, Chaker M, Vijh A, Guerfi A, Julien C M, Mauger A, Armand M, Hovington P, Zaghib K 2016 J. Power Sources 319 247 Google Scholar
[105]	Wan M, Kang S, Wang L, Lee H W, Zheng G W, Cui Y, Sun Y 2020 Nat. Commun. 11 829 Google Scholar
[106]	Otoyama M, Sakuda A, Hayashi A, Tatsumisago M 2018 Solid State Ionics 323 123 Google Scholar
[107]	Nishikawa K, Munakata H, Kanamura K 2013 J. Power Sources 243 630 Google Scholar
[108]	Sethuraman V A, Chon M J, Shimshak M, Van Winkle N, Guduru P R 2010 Electrochem. Commun. 12 1614 Google Scholar

[1]	Liu Chao, Zhang Ai-Bing, Sun Yue-Qiang, Kong Ling-Gao, Wang Wen-Jing, Guan Yi-Bing, Wang Yong-Song, Zheng Xiang-Zhi, Tian Zheng, Gao Jun. Plasma in-situ imaging detection technology on China’s Space Station Wentian module. Acta Physica Sinica, 2023, 72(4): 049401. doi: 10.7498/aps.72.20221759
[2]	Yang Yuan, Hu Nai-Fang, Jin Yong-Cheng, Ma Jun, Cui Guang-Lei. Research advance of lithium-rich cathode materials in all-solid-state lithium batteries. Acta Physica Sinica, 2023, 72(11): 118801. doi: 10.7498/aps.72.20230258
[3]	Hu Xiao-Hua, Lu Xiao-Tong, Zhang Xiao-Fei, Chang Hong. Density shift measurement and synchronous frequency comparison based on in situ imaging technique. Acta Physica Sinica, 2022, 71(17): 173401. doi: 10.7498/aps.71.20220600
[4]	Zhou Hai-Tao, Xiong Xi-Ya, Luo Fei, Luo Bing-Wei, Liu Da-Bo, Shen Cheng-Min. Graphene enforced copper matrix composites fabricated by in-situ deposition technique. Acta Physica Sinica, 2021, 70(8): 086201. doi: 10.7498/aps.70.20201943
[5]	Liang Yu-Hao, Fan Li-Zhen. Mechanical failures in solid-state lithium batteries and their solution. Acta Physica Sinica, 2020, 69(22): 226201. doi: 10.7498/aps.69.20200713
[6]	Zhao Ning, Mu Shuang, Guo Xiang-Xin. Physical issues in solid garnet batteries. Acta Physica Sinica, 2020, 69(22): 228804. doi: 10.7498/aps.69.20201191
[7]	Yu Qi-Peng, Liu Qi, Wang Zi-Qiang, Li Bao-Hua. Anode interface in all-solid-state lithium-metal batteries: Challenges and strategies. Acta Physica Sinica, 2020, 69(22): 228805. doi: 10.7498/aps.69.20201218
[8]	Cui Long-Fei, Ju Jiang-Wei, Cui Guang-Lei. Three-dimensional porous ceramic framework reinforcing composite electrolyte. Acta Physica Sinica, 2020, 69(22): 228203. doi: 10.7498/aps.69.20201552
[9]	Zhang Nian, Ren Guo-Xi, Zhang Hui, Zhou Deng, Liu Xiao-Song. Research progress of interface problems and optimization of garnet-type solid electrolyte. Acta Physica Sinica, 2020, 69(22): 228806. doi: 10.7498/aps.69.20201533
[10]	Zhang Bao-Bao, Zhang Cheng-Yun, Zhang Zheng-Long, Zheng Hai-Rong. Surface plasmon mediated chemical reaction. Acta Physica Sinica, 2019, 68(14): 147102. doi: 10.7498/aps.68.20190345
[11]	Jin Xin, Yang Chun-Ming, Hua Wen-Qiang, Li Yi-Wen, Wang Jie. Temperature dependence of spherical micelles of PS3000-b-PAA5000 studied by in-situ small angle X-ray scattering. Acta Physica Sinica, 2018, 67(4): 048301. doi: 10.7498/aps.67.20172167
[12]	Wang Qi-Yu, Wang Shuo, Zhou Ge, Zhang Jie-Nan, Zheng Jie-Yun, Yu Xi-Qian, Li Hong. Progress on the failure analysis of lithium battery. Acta Physica Sinica, 2018, 67(12): 128501. doi: 10.7498/aps.67.20180757
[13]	Li Chao, Yao Yuan, Yang Yang, Shen Xi, Gao Bin, Huo Zong-Liang, Kang Jin-Feng, Liu Ming, Yu Ri-Cheng. In situ transmission electron microscopy studies on nanomaterials and HfO2-based storage nanodevices. Acta Physica Sinica, 2018, 67(12): 126802. doi: 10.7498/aps.67.20180731
[14]	Li Jun, Chen Xiao-Hui, Wu Qiang, Luo Bin-Qiang, Li Mu, Yang Qing-Guo, Tao Tian-Jiong, Jin Ke, Geng Hua-Yun, Tan Ye, Xue Tao. Experimental investigation on dynamic lattice response by in-situ Xray diffraction method. Acta Physica Sinica, 2017, 66(13): 136101. doi: 10.7498/aps.66.136101
[15]	Zeng Xian, Yang Zhao-Hui, Zhang Xiao-Hua. Characterization tools for polymer thin films. Acta Physica Sinica, 2016, 65(17): 176801. doi: 10.7498/aps.65.176801
[16]	Zhang Kun, Liu Fang-Yang, Lai Yan-Qing, Li Yi, Yan Chang, Zhang Zhi-An, Li Jie, Liu Ye-Xiang. In situ growth and characterization of Cu2ZnSnS4 thin films by reactive magnetron co-sputtering for solar cells. Acta Physica Sinica, 2011, 60(2): 028802. doi: 10.7498/aps.60.028802
[17]	Luo Yu-Feng, Zhong Cheng, Zhang Li, Yan Xue-Jian, Li Jin, Jiang Yi-Ming. An in situ method for characterizing the kinetics of the oxidation process of copper thin films via sheet resistance. Acta Physica Sinica, 2007, 56(11): 6722-6726. doi: 10.7498/aps.56.6722
[18]	BAI HAI-YANG, CHEN HONG, ZHANG YUN, WANG WEN-KUI. STUDY ON SOLID STATE REACTION INTERDIFFUSION OF Fe-Ti MULTILAYER MODULATED FILMS WITH DYNAMIC IN SITU X-RAY DIFFRACTION. Acta Physica Sinica, 1993, 42(7): 1134-1140. doi: 10.7498/aps.42.1134
[19]	Bai Hai-yang;Vhen Hong; Zhang Yun;Wang Wen-kui. STUDY ON SOLID STATE REACTION INTERDIFFUSION OF Fe一Ti MULTILAYER MODULATED FILMS WITH DYNAMIC IN SITU X一RAY DIFFRACTION. Acta Physica Sinica, 1991, 40(7): 1134-1140. doi: 10.7498/aps.40.1134
[20]	GUO CHANG-LIN, LU CHANG-WEI, SHEN DING-KUN, YU ZHI-ZHONG. STUDIES ON THE STRUCTURE OF AMORPHOUS MoS3 AS CATHODE MATERIALS IN LITHIUM BATTERIES. Acta Physica Sinica, 1985, 34(10): 1336-1341. doi: 10.7498/aps.34.1336

Catalog

Vol. 70, Issue 19 - 2021-10-05

Metrics

Abstract views: 23709
PDF Downloads: 1166
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Application of in-situ characterization techniques in all-solid-state lithium batteries

Abstract

Authors and contacts

Corresponding author: Li De-Ping, lideping@hit.edu.cn ; Ci Li-Jie, cilijie@hit.edu.cn ; Zhang Qiao-Bao, zhangqiaobao@xmu.edu.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板

Application of in-situ characterization techniques in all-solid-state lithium batteries

Abstract

Authors and contacts

Corresponding author: Li De-Ping, lideping@hit.edu.cn ; Ci Li-Jie, cilijie@hit.edu.cn ; Zhang Qiao-Bao, zhangqiaobao@xmu.edu.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Publishing process

Authors

Referees

About Journal

About