Mechanism of grain refinement in Al-Cu alloy by adding trace La and Al-5Ti-1B

Yang Lin-Jie; Zhang Li-Li; Jiang Hong-Xiang; He Jie; Zhao Jiu-Zhou

doi:10.7498/aps.72.20222334

Abstract

Grain refinement of aluminium alloys can not only reduce the defects (such as segregation and hot tearing) but also improve the mechanical properties. Adding Al-5Ti-1B master alloy to the melt has become a common method to refine the solidification microstructure of aluminium alloys. A lot of researches have been carried out to uncover the grain refining mechanisms as well as to show the microstructure formation under the effect of grain refiner. These researches demonstrated that the grain refining efficiency is closely related to the number density of TiB₂ particles as well as the solute Ti concentration in the melt. However, there exist still problems to be resolved, such as the limited grain refinement potency of Al-5Ti-1B master alloy. Recently, the addition of trace La to the melt has attracted much attention to control the microstructure of aluminium alloys. The Al-Cu alloys are widely applied to the automobile and aerospace fields due to their high strength, good ductility and high temperature properties. It has been reported that Cu can segregate to Al/TiB₂ interface in the Al-Cu melt inoculated with Al-5Ti-1B master alloy. But the effect of Cu segregation on the grain refinement result is not clear yet. Meanwhile, whether the grain refinement effect of Al-5Ti-1B master alloy on Al-Cu alloy can be improved by the addition of trace La has not been reported.Solidification experiments are carried out for Al-2Cu alloy with the addition of Al-5Ti-1B master alloy+ trace La. The synergistic effect of trace La and Al-5Ti-1B on the solidification microstructure of Al-2Cu alloy is investigated. It is found that trace La can effectively enhance the refinement result of Al-2Cu alloy and further diminish the nucleation undercooling. Experimental and calculated results demonstrate that solute Cu segregates to the Al/TiB₂ interface and thus increases the interatomic spacing mismatch between Ti (0001) plane of the TiB₂ particles and the interfacial monolayer, while La segregation reduces the interatomic spacing mismatch. The trace La addition reduces the interfacial energy between α-Al and TiB₂ particles, improves the potency of TiB₂ particles to nucleate α-Al, and thus enhances the grain refinement result of Al-5Ti-1B master alloy.

Keywords:

Authors and contacts

1.
Shi-changxu Innovation Centre for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China
2.
School of Materials Science and Engineering, University of Science and Technology of China, Shenyang 110016, China

Corresponding author: Zhang Li-Li, llzhang@imr.ac.cn ; Zhao Jiu-Zhou, jzzhao@imr.ac.cn

Funds: Project supported by the National Key R&D Program of China (Grant No. 2021YFA0716303), the China Manned Space Station Project, and the National Natural Science Foundation of China (Grant Nos. 51901231, 51971227).

FullText HTML : translate this paragraph

References

[1]	张丽丽 2017 博士学位论文 (沈阳: 中国科学院大学) Zhang L L 2017 Ph. D. Dissertation (Shenyang: University of Chinese Academy of Sciences) (in Chinese)
[2]	Greer A L, Bunn A M, Tronche A, Evans P V, Bristow D J 2000 Acta Mater. 48 2823 Google Scholar
[3]	Quested T E, Greer A L 2004 Acta Mater. 52 3859 Google Scholar
[4]	Quested T E, Greer A L 2005 Acta Mater. 53 4643 Google Scholar
[5]	Easton M A, StJohn D H 2001 Acta Mater. 49 1867 Google Scholar
[6]	Easton M A, StJohn D H 2005 Metall. Mater. Trans. A 36 1911 Google Scholar
[7]	Easton M A, StJohn D H 2008 Mater. Sci. Eng. A 486 8 Google Scholar
[8]	Fan Z, Wang Y, Zhang Y, Qin T, Zhou X R, Thompson G E, Pennycook T, Hashimoto T 2015 Acta Mater. 84 292 Google Scholar
[9]	Cibula A 1951 J. Inst. Met. 80 1
[10]	Crossley F A, Mondolfo L F 1951 JOM. 3 1143 Google Scholar
[11]	Jones G P, Jones H 1987 Solidification Processing (Sheffield: University of Sheffield) p496
[12]	Mohanty P S, Gruzleski J E 1995 Acta Metall. Mater. 43 2001 Google Scholar
[13]	Fan Z Y 2013 Metall. Mater. Trans. A 44 1409 Google Scholar
[14]	Maxwell I, Hellawell A 1975 Acta Metall. 23 229 Google Scholar
[15]	Zhang L L, Zheng Q J, Jiang H X, Zhao J Z 2019 Scr. Mater. 160 25 Google Scholar
[16]	Li J H, Hage F S, Ramasse Q M, Schumacher P 2021 Acta Mater. 206 116652 Google Scholar
[17]	吴俊子, 贾锦玉, 姜佳鑫 2018 稀土信息 2 30 Wu J Z, Jia J Y, Jiang J X 2018 Rare Earth Inform. 2 30
[18]	韩延峰 2007 博士学位论文 (上海: 上海交通大学) Han Y F 2007 Ph. D. Dissertation (Shanghai: Shanghai Jiao Tong University) (in Chinese)
[19]	Zhang Z, Bian X, Wang Y, Liu, X 2003 Mater. Sci. Eng. A 352 8 Google Scholar
[20]	李克, 饶磊, 闫洪, 王俊, 孙宝德 2006 铸造 9 894 Li K, Rao L, Yan H, Wang J, Sun B D 2006 Foundry 9 894
[21]	董天顺, 崔春翔, 刘双进, 刘福才 2008 稀有金属材料与工程 1 29 Dong T S, Cui C X, Liu S J, Liu F C 2008 Rare Metal Mater. Eng. 1 29
[22]	Wang Z J, Si N C 2015 Rare Metal Mater. Eng. 44 2970 Google Scholar
[23]	Ma T F, Chen Z Y, Nie Z R, Huang H 2013 J. Rare Earths 31 622 Google Scholar
[24]	Wang K, Cui C X, Wang Q, Liu S, Gu C 2012 Mater. Lett. 85 153 Google Scholar
[25]	Wang K, Cui C X, Wang Q, Zhao L, Hu Y 2013 J. Rare Earths 31 313 Google Scholar
[26]	Zhang L L, Song Y, Yang L J, Zhao J Z, He J, Jiang H X 2022 Materials 15 600 Google Scholar
[27]	Zhang M X, Kelly P M, Easton M A, Taylor J A 2005 Acta Mater. 53 1427 Google Scholar
[28]	Wang Y, Fang C M, Zhou L, Hashimoto T, Fan Z 2018 Acta Mater. 164 428 Google Scholar
[29]	Iida T, Guthrie R I L 1993 The Physical Properties of Liquid Metals (Oxford: Clarendon Press) p71
[30]	Fan T X, Yang G, Zhang D 2005 Metall. Mater. Trans. A 36 225 Google Scholar
[31]	Dinsdale A T 1991 Calphad. 15 317 Google Scholar
[32]	李淑波, 杜文博, 王旭东, 刘轲, 王朝辉 2018 金属学报 54 911 Google Scholar Li S B, Du W B, Wang X D, Liu K, Wang C H 2018 Acta Metall. Sin. 54 911 Google Scholar
[33]	Zhang L L, Jiang H X, He J, Zhao J Z 2020 Scr. Mater. 179 99 Google Scholar
[34]	Okamoto H 2013 J. Phase Equilib. Diffus. 34 493 Google Scholar
[35]	Elliott R P, Shunk F A 1981 Bull. Alloy Phase Diagrams 2 219 Google Scholar

Cited By

图 1 Al-2Cu和不同La添加量下经0.4% Al-5Ti-1B中间合金细化处理的Al-2Cu合金晶粒平均尺寸和微观组织的OM像

Figure 1. Average size of α-Al grains and OM images of the Al-2Cu alloys without addition of inoculant, inoculated with 0.4% Al-5Ti-1B and inoculated with 0.4% Al-5Ti-1B + 0.08% La.

DownLoad: Full-Size Img PowerPoint

图 2 添加1% Al-5Ti-1B的Al-2Cu合金的TEM像及元素分布图　(a) 低倍TEM像; (b)—(e) 元素Al (b), Cu (c), Ti (d), B (e)分布图; (f) TiB₂粒子的高倍TEM像, 其中插图为元素Al, Cu和Ti在蓝框内的平均电子能量损失谱线

Figure 2. TEM image and elemental maps in the Al-2Cu alloy inoculated by 1% Al-5Ti-1B: (a) TEM image at low magnification; (b)–(e) elemental maps of Al (b), Cu (c), Ti (d), B (e); (f) TEM image at high magnification of TiB₂ particles, where inset shows the electron energy loss spectroscopy line profiles of elements Al, Cu and Ti averaged over the area indicated in Fig. (f) by blue box

DownLoad: Full-Size Img PowerPoint

图 3 (a) 添加1% Al-5Ti-1B + 0.08% La的Al-2Cu合金的高倍TEM像; (b)—(e) 元素Al (b), Cu (c), Ti (d), La (e)的X射线能量散谱图; (f) Al, Cu, Ti和La元素的电子能量损失谱线

Figure 3. (a) TEM image at high magnification in Al-2Cu alloy inoculated by 1% Al-5Ti-1B + 0.08% La; (b)–(e) energy dispersive X-ray spectroscopy maps of Al (b), Cu (c), Ti (d), La (e); (f) electron energy loss spectroscopy line profiles of elements Al, Cu, Ti and La averaged over the area indicated in (a) by pink box of TiB₂ particles.

DownLoad: Full-Size Img PowerPoint

图 4 添加1% Al-5Ti-1B + 0% La (a)和1% Al-5Ti-1B +0.08% La (b)的Al-2Cu合金HRTEM像; (c) TiB₂粒子中Ti (0001)面与界面单原子层间界面示意图

Figure 4. HRTEM images showing the basal plane (0001) of TiB₂ in Al-2Cu alloy inoculated with 1% Al-5Ti-1B + 0% La (a) and 1% Al-5Ti-1B +0.08%La (b), respectively; (c) schematic illustration of interface between the Ti (0001) plane of TiB₂ surface and the monolayer

DownLoad: Full-Size Img PowerPoint

图 5 经0.4% Al-5Ti-1B细化处理的Al-2Cu合金的DTA升温(虚线)和冷却(实线)曲线, 其中T_m 和T_n分别为合金的熔点和开始形核温度, T_m = 926.2K; 插图为α-Al的形核过冷度ΔT_Heter

Figure 5. DTA heating (dashed line) and cooling (solid line) curves for the Al-2Cu alloys with the addition of 0.4% Al-5Ti-1B master alloy. T_n and T_m = 926.2K are respectively the nucleation temperature of α-Al and the melting point temperature of Al. Inset shows the undercooling ΔT_Heter.

DownLoad: Full-Size Img PowerPoint

图 6 微量La添加量对经0.4%Al-5Ti-1B细化处理的Al-2Cu合金生长限制因子的影响

Figure 6. Effect of trace La addition on the growth restriction factor of Al-2Cu alloy inoculated with 0.4% Al-5Ti-1B master alloy.

DownLoad: Full-Size Img PowerPoint

表 1 (13)式中涉及的参数

Table 1. Parameters used in Eq. (13).

i k_i m_i/(K·%^–1) $ {c'_{{\text{S}}i}}/\% $ $ {c'_{{\text{L}}i}}/\% $ Reference

Ti 7.8 33.3 — — [12]
Cu 0.17 –3.4 5.69 32.5 [34]
La 0.004 –1.71 0.05 11.7 [35]

DownLoad: CSV

[1]	张丽丽 2017 博士学位论文 (沈阳: 中国科学院大学) Zhang L L 2017 Ph. D. Dissertation (Shenyang: University of Chinese Academy of Sciences) (in Chinese)
[2]	Greer A L, Bunn A M, Tronche A, Evans P V, Bristow D J 2000 Acta Mater. 48 2823 Google Scholar
[3]	Quested T E, Greer A L 2004 Acta Mater. 52 3859 Google Scholar
[4]	Quested T E, Greer A L 2005 Acta Mater. 53 4643 Google Scholar
[5]	Easton M A, StJohn D H 2001 Acta Mater. 49 1867 Google Scholar
[6]	Easton M A, StJohn D H 2005 Metall. Mater. Trans. A 36 1911 Google Scholar
[7]	Easton M A, StJohn D H 2008 Mater. Sci. Eng. A 486 8 Google Scholar
[8]	Fan Z, Wang Y, Zhang Y, Qin T, Zhou X R, Thompson G E, Pennycook T, Hashimoto T 2015 Acta Mater. 84 292 Google Scholar
[9]	Cibula A 1951 J. Inst. Met. 80 1
[10]	Crossley F A, Mondolfo L F 1951 JOM. 3 1143 Google Scholar
[11]	Jones G P, Jones H 1987 Solidification Processing (Sheffield: University of Sheffield) p496
[12]	Mohanty P S, Gruzleski J E 1995 Acta Metall. Mater. 43 2001 Google Scholar
[13]	Fan Z Y 2013 Metall. Mater. Trans. A 44 1409 Google Scholar
[14]	Maxwell I, Hellawell A 1975 Acta Metall. 23 229 Google Scholar
[15]	Zhang L L, Zheng Q J, Jiang H X, Zhao J Z 2019 Scr. Mater. 160 25 Google Scholar
[16]	Li J H, Hage F S, Ramasse Q M, Schumacher P 2021 Acta Mater. 206 116652 Google Scholar
[17]	吴俊子, 贾锦玉, 姜佳鑫 2018 稀土信息 2 30 Wu J Z, Jia J Y, Jiang J X 2018 Rare Earth Inform. 2 30
[18]	韩延峰 2007 博士学位论文 (上海: 上海交通大学) Han Y F 2007 Ph. D. Dissertation (Shanghai: Shanghai Jiao Tong University) (in Chinese)
[19]	Zhang Z, Bian X, Wang Y, Liu, X 2003 Mater. Sci. Eng. A 352 8 Google Scholar
[20]	李克, 饶磊, 闫洪, 王俊, 孙宝德 2006 铸造 9 894 Li K, Rao L, Yan H, Wang J, Sun B D 2006 Foundry 9 894
[21]	董天顺, 崔春翔, 刘双进, 刘福才 2008 稀有金属材料与工程 1 29 Dong T S, Cui C X, Liu S J, Liu F C 2008 Rare Metal Mater. Eng. 1 29
[22]	Wang Z J, Si N C 2015 Rare Metal Mater. Eng. 44 2970 Google Scholar
[23]	Ma T F, Chen Z Y, Nie Z R, Huang H 2013 J. Rare Earths 31 622 Google Scholar
[24]	Wang K, Cui C X, Wang Q, Liu S, Gu C 2012 Mater. Lett. 85 153 Google Scholar
[25]	Wang K, Cui C X, Wang Q, Zhao L, Hu Y 2013 J. Rare Earths 31 313 Google Scholar
[26]	Zhang L L, Song Y, Yang L J, Zhao J Z, He J, Jiang H X 2022 Materials 15 600 Google Scholar
[27]	Zhang M X, Kelly P M, Easton M A, Taylor J A 2005 Acta Mater. 53 1427 Google Scholar
[28]	Wang Y, Fang C M, Zhou L, Hashimoto T, Fan Z 2018 Acta Mater. 164 428 Google Scholar
[29]	Iida T, Guthrie R I L 1993 The Physical Properties of Liquid Metals (Oxford: Clarendon Press) p71
[30]	Fan T X, Yang G, Zhang D 2005 Metall. Mater. Trans. A 36 225 Google Scholar
[31]	Dinsdale A T 1991 Calphad. 15 317 Google Scholar
[32]	李淑波, 杜文博, 王旭东, 刘轲, 王朝辉 2018 金属学报 54 911 Google Scholar Li S B, Du W B, Wang X D, Liu K, Wang C H 2018 Acta Metall. Sin. 54 911 Google Scholar
[33]	Zhang L L, Jiang H X, He J, Zhao J Z 2020 Scr. Mater. 179 99 Google Scholar
[34]	Okamoto H 2013 J. Phase Equilib. Diffus. 34 493 Google Scholar
[35]	Elliott R P, Shunk F A 1981 Bull. Alloy Phase Diagrams 2 219 Google Scholar

[1]	Dai Yu-Jia, Li Ming-Liang, Song Chao, Gao Xun, Hao Zuo-Qiang, Lin Jing-Quan. Accuracy improvement of Fe element in aluminum alloy by laser induced breakdown spectroscopy under spatial confinement combined with gradient descent. Acta Physica Sinica, 2021, 70(20): 205204. doi: 10.7498/aps.70.20210792
[2]	Song Yan, Jiang Hong-Xiang, Zhao Jiu-Zhou, He Jie, Zhang Li-Li, Li Shi-Xin. Numerical simulations of solidification microstructure evolution process for commercial-purity aluminum alloys inoculated by Al-Ti-B refiner. Acta Physica Sinica, 2021, 70(8): 086402. doi: 10.7498/aps.70.20201431
[3]	Guo Zhi-Chao, Li Ping-Lin. Grain refinement influence on the critical current density of the MgB2 superconductor sample. Acta Physica Sinica, 2014, 63(6): 067401. doi: 10.7498/aps.63.067401
[4]	Guan Ren-Guo, Zhao Zhan-Yong, Huang Hong-Qian, Lian Chao, Chao Run-Ze, Liu Chun-Ming. Theoretical study on boundary distributions and flow-metal heat transfer during melt treatment by cooling sloping plate. Acta Physica Sinica, 2012, 61(20): 206602. doi: 10.7498/aps.61.206602
[5]	Zhang Hui, Wu Di, Zhang Guo-Ying, Xiao Ming-Zhu. Study of the influence mechanism of additional elements on the corrosion behavior of bulk Cu-based amorphous alloys. Acta Physica Sinica, 2010, 59(1): 488-493. doi: 10.7498/aps.59.488
[6]	Sun Dui-Xiong, Su Mao-Gen, Dong Chen-Zhong, Wang Xiang-Li, Zhang Da-Cheng, Ma Xin-Wen. Quantitative analysis of element concentration in Al alloy by using laser-induced breakdown spectroscopy. Acta Physica Sinica, 2010, 59(7): 4571-4576. doi: 10.7498/aps.59.4571
[7]	Wang Na, Tang Bi-Yu. Structural，elastic and electronic properties of L12 aluminum phases from first principles calculation. Acta Physica Sinica, 2009, 58(13): 230-S234. doi: 10.7498/aps.58.230
[8]	Fan Fei, Ban Chun-Yan, Wang Yang, Ba Qi-Xian, Cui Jian-Zhong. The resistivity evolution with temperature of 7050 aluminium alloy by different casting methods. Acta Physica Sinica, 2009, 58(1): 638-643. doi: 10.7498/aps.58.638
[9]	Liu Gui-Li. Electron-theoretical study of grain refining mechanism of Mg alloys. Acta Physica Sinica, 2009, 58(5): 3319-3323. doi: 10.7498/aps.58.3319
[10]	Liu Gui-Li. The electronic structure of the microstructure of Mg-Zr alloys. Acta Physica Sinica, 2008, 57(2): 1043-1047. doi: 10.7498/aps.57.1043
[11]	Zhang Da-Cheng, Ma Xin-Wen, Zhu Xiao-Long, Li Bin, Zu Kai-Ling. Application of laser-induced breakdown spectroscopy in analyzing microelements in three kinds of fruit samples. Acta Physica Sinica, 2008, 57(10): 6348-6353. doi: 10.7498/aps.57.6348
[12]	Zheng Li-Ping, Li Dou-Xing, Xu Zi-Jian, Zhu Zhi-Yuan. The dual-species model study of co-enrichment of trace elements and Ni at Ni3Al grain boundary. Acta Physica Sinica, 2007, 56(3): 1520-1525. doi: 10.7498/aps.56.1520
[13]	Zhang Guo-Ying, Zhang Hui, Liu Chun-Ming, Zhou Yong-Jun. The grain boundary segregation of microalloying elements and the ultra-refinement of steel. Acta Physica Sinica, 2006, 55(3): 1369-1373. doi: 10.7498/aps.55.1369
[14]	Pang Xue-Jun, Wang Qiang, Wang Chun-Jiang, Wang Ya-Qin, Li Ya-Bin, He Ji-Cheng. Effects of high magnetic fields on the distribution of solute elements in Al-alloys. Acta Physica Sinica, 2006, 55(10): 5129-5134. doi: 10.7498/aps.55.5129
[15]	Peng Kai-Ping, Chen Wen-Zhe, Qian Kuang-Wu. Study of an anomalous serrated yielding phenomenon in 3004 aluminum alloy. Acta Physica Sinica, 2006, 55(7): 3569-3575. doi: 10.7498/aps.55.3569
[16]	Wu Han-Hua, Long Bei-Hong, Lü Xian-Yi, Wang Jian-Bo, Jin Zeng-Sun. Study on the electrical parameter variation during microarc oxidation of alumini um alloys. Acta Physica Sinica, 2005, 54(4): 1697-1701. doi: 10.7498/aps.54.1697
[17]	Zhang Guo-Ying, Zhang Hui, Liu Chun-Ming, Zhou Yong-Jun. The study on the ultrafine mechanism of steels: strain-induced phase-transform ation form austenite to ferrite. Acta Physica Sinica, 2005, 54(4): 1771-1776. doi: 10.7498/aps.54.1771
[18]	Zhu Bo, Cai Xun, Wang Cheng-Guo, Cai Hua-Su. Studies on the relationship between acoustic emission characteristics and fractu re toughness of materials. Acta Physica Sinica, 2003, 52(8): 1960-1964. doi: 10.7498/aps.52.1960
[19]	Zhang Qin, Ban Chun-Yan, Cui Jian-Zhong, Ba Qi-Xian, Lu Gui-Min, Zhang Bei-Jiang. The forced solution mechanism of alloying agents of 7075 alloy as-cast ingot und er the effects of electromagnetic field. Acta Physica Sinica, 2003, 52(10): 2642-2648. doi: 10.7498/aps.52.2642
[20]	WANG ZHEN-XIA, PAN JI-SHENG, ZHANG JI-PING, TAO ZHEN-LAN. EFFECT OF SURFACE LOCAL ENRICHMENT ON PREFEREN-TIAL SPUTTERIONG OF ALLOY. Acta Physica Sinica, 1992, 41(10): 1722-1727. doi: 10.7498/aps.41.1722

Catalog

Vol. 72, Issue 8 - 2023-04-20

Metrics

Abstract views: 3256
PDF Downloads: 54
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板