Temperature sensing with nitrogen vacancy center in diamond

Lin Hao-Bin; Zhang Shao-Chun; Dong Yang; Zheng Yu; Chen Xiang-Dong; Sun Fang-Wen

doi:10.7498/aps.71.20211822

Abstract

Temperature is the most intuitive and widespread in various physical quantities. Violent changes in temperature usually implies the appearing of fluctuations in physical properties of an object. Therefore, temperature is often an important indicator. With the development of science and technology, the scales in many fields are being more and more miniaturized. However, there are no mature temperature measurement systems in the case where the spatial scale is less than 10 μm. In addition to the requirement for spatial resolution, the sensor ought to exert no dramatic influence on the object to be measured. The nitrogen vacancy (NV) center in diamond is a stable luminescence defect. The measurements of its spectrum and spin state can be used to obtain the information about physical quantities near the color center, such as temperature and electro-magnetic field. Owing to its stable chemical properties and high thermal conductivity, the NV center can be applied to the noninvasive detection for nano-scale researches. It can also be used in the life field because it is non-toxic to cells. Moreover, combined with different techniques, such as optical fiber, scanning thermal microscopy, NV center can be used to measure the local temperatures in different scenarios. This review focuses on the temperature properties, the method of measuring temperature, and relevant applications of NV centers.

Keywords:

Authors and contacts

Chinese Academy of Sciences Key Laboratory of Quantum Information, University of Science and Technology of China, Hefei 230026, China

Corresponding author: Sun Fang-Wen, fwsun@ustc.edu.cn

Funds: Project supported by the National Key Research and Development Program of China (Grant No. 2017YFA0304504), the National Natural Science Foundation of China (Grant Nos. 91850102, 12005218), and the Science Fund for Distinguished Young Scholars of Heibei Province, China (Grant No. F2019516002).

FullText HTML : translate this paragraph

References

[1]	van Oort E, Manson N B, Glasbeek M 1988 J. Phys. C: Solid State Phys. 21 4385 Google Scholar
[2]	Gruber A 1997 Science 276 2012 Google Scholar
[3]	Jelezko F, Gaebel T, Popa I, Domhan M, Gruber A, Wrachtrup J 2004 Phys. Rev. Lett. 93 130501 Google Scholar
[4]	Fuchs G D, Dobrovitski V V, Hanson R, Batra A, Weis C D, Schenkel T, Awschalom D D 2008 Phys. Rev. Lett. 101 117601 Google Scholar
[5]	Neumann P, Kolesov R, Jacques V, Beck J, Tisler J, Batalov A, Rogers L, Manson N B, Balasubramanian G, Jelezko F, Wrachtrup J 2009 New J. Phys. 11 013017 Google Scholar
[6]	Childress L, Hanson R 2013 MRS Bull. 38 134 Google Scholar
[7]	Chen X, Zou C, Gong Z, Dong C, Guo G, Sun F 2015 Light Sci. Appl. 4 e230 Google Scholar
[8]	Han K Y, Kim S K, Eggeling C, Hell S W 2010 Nano Lett. 10 3199 Google Scholar
[9]	Arroyo-Camejo S, Adam M P, Besbes M, Hugonin J P, Jacques V, Greffet J J, Roch J F, Hell S W, Treussart F 2013 ACS Nano 7 10912 Google Scholar
[10]	Maze J R, Stanwix P L, Hodges J S, Hong S, Taylor J M, Cappellaro P, Jiang L, Dutt M V G, Togan E, Zibrov A S, Yacoby A, Walsworth R L, Lukin M D 2008 Nature 455 644 Google Scholar
[11]	Dolde F, Fedder H, Doherty M W, Nbauer T, Rempp F, Balasubramanian G, Wolf T, Reinhard F, Hollenberg L C L, Jelezko F, Wrachtrup J 2011 Nat. Phys. 7 459 Google Scholar
[12]	Ovartchaiyapong P, Lee K W, Myers B A, Jayich A C B 2014 Nat. Commun. 5 4429 Google Scholar
[13]	Acosta V M, Bauch E, Ledbetter M P, Waxman A, Bouchard L S, Budker D 2010 Phys. Rev. Lett. 104 070801 Google Scholar
[14]	Chen X D, Dong C H, Sun F W, Zou C L, Cui J M, Han Z F, Guo G C 2011 Appl. Phys. Lett. 99 161903 Google Scholar
[15]	Hayashi T, Fukuda N, Uchiyama S, Inada N 2015 PLoS One 10 e0117677 Google Scholar
[16]	Jaque D, del Rosal B, Rodrguez E M, Maestro L M, Haro-Gonzlez P, Sol J G 2014 Nanomedicine 9 1047 Google Scholar
[17]	Somero G N 1995 Annu. Rev. Physiol. 57 43 Google Scholar
[18]	Suzuki M, Tseeb V, Oyama K, Ishiwata S I 2007 Biophys. J. 92 2 Google Scholar
[19]	Zohar O, Ikeda M, Shinagawa H, Inoue H, Nakamura H, Elbaum D, Alkon D L, Yoshioka T 1998 Biophys. J. 74 82 Google Scholar
[20]	Astakhov V P, Outeiro J 2019 Importance of Temperature in Metal Cutting and Its Proper Measurement/Modeling (Cham: Springer International Publishing) pp1–47
[21]	Shi L, Dames C, Lukes J R, Reddy P, Duda J, Cahill D G, Lee J, Marconnet A, Goodson K E, Bahk J H, Shakouri A, Prasher R S, Felts J, King W P, Han B, Bischof J C 2015 Nanoscale and Microscale Thermophys. Eng. 19 127 Google Scholar
[22]	Brites C D S, Balabhadra S, Carlos L D 2019 Adv. Opt. Mater. 7 1801239 Google Scholar
[23]	Doherty M W, Acosta V M, Jarmola A, Barson M S J, Manson N B, Budker D, Hollenberg L C L 2014 Phys. Rev. B 90 041201 Google Scholar
[24]	Li C C, Gong M, Chen X D, Li S, Zhao B W, Dong Y, Guo G C, Sun F W 2017 Diamond Relat. Mater. 74 119 Google Scholar
[25]	Schirhagl R, Chang K, Loretz M, Degen C L 2014 Annu. Rev. Phys. Chem. 65 83 Google Scholar
[26]	Toyli D M, Christle D J, Alkauskas A, Buckley B B, Van de Walle C G, Awschalom D D 2012 Phys. Rev. X 2 031001 Google Scholar
[27]	Toyli D M, de las Casas C F, Christle D J, Dobrovitski V V, Awschalom D D 2013 Proc. Natl. Acad. Sci. 110 8417 Google Scholar
[28]	Neumann P, Jakobi I, Dolde F, Burk C, Reuter R, Waldherr G, Honert J, Wolf T, Brunner A, Shim J H, Suter D, Sumiya H, Isoya J, Wrachtrup J 2013 Nano Lett. 13 2738 Google Scholar
[29]	Kucsko G, Maurer P C, Yao N Y, Kubo M, Noh H J, Lo P K, Park H, Lukin M D 2013 Nature 500 54 Google Scholar
[30]	Fedotov I V, Blakley S, Serebryannikov E E, Safronov N A, Velichansky V L, Scully M O, Zheltikov A M 2014 Appl. Phys. Lett. 105 261109 Google Scholar
[31]	Kraus H, Soltamov V A, Fuchs F, Simin D, Sperlich A, Baranov P G, Astakhov G V, Dyakonov V 2015 Sci. Rep. 4 5303 Google Scholar
[32]	Plakhotnik T, Aman H, Chang H C 2015 Nanotechnology 26 245501 Google Scholar
[33]	Laraoui A, Aycock-Rizzo H, Gao Y, Lu X, Riedo E, Meriles C A 2015 Nat. Commun. 6 8954 Google Scholar
[34]	Jelezko F, Wrachtrup J 2006 Phys. Status Solidi A 203 3207 Google Scholar
[35]	Wojciechowski A M, Karadas M, Osterkamp C, Jankuhn S, Meijer J, Jelezko F, Huck A, Andersen U L 2018 Appl. Phys. Lett. 113 013502 Google Scholar
[36]	Tzeng Y K, Tsai P C, Liu H Y, Chen O Y, Hsu H, Yee F G, Chang M S, Chang H C 2015 Nano Lett. 15 3945 Google Scholar
[37]	Wang J, Feng F, Zhang J, Chen J, Zheng Z, Guo L, Zhang W, Song X, Guo G, Fan L, Zou C, Lou L, Zhu W, Wang G 2015 Phys. Rev. B 91 155404 Google Scholar
[38]	Konzelmann P, Rendler T, Bergholm V, Zappe A, Pfannenstill V, Garsi M, Ziem F, Niethammer M, Widmann M, Lee S Y, Neumann P, Wrachtrup J 2018 New J. Phys. 20 123013 Google Scholar
[39]	Plakhotnik T, Doherty M W, Cole J H, Chapman R, Manson N B 2014 Nano Lett. 14 4989 Google Scholar
[40]	Zhang S C, Li S, Du B, Dong Y, Zheng Y, Lin H B, Zhao B W, Zhu W, Wang G Z, Chen X D, Guo G C, Sun F W 2019 Opt. Mater. Express 9 4634 Google Scholar
[41]	Wang N, Liu G Q, Leong W H, Zeng H, Feng X, Li S H, Dolde F, Fedder H, Wrachtrup J, Cui X D, Yang S, Li Q, Liu R B 2018 Phys. Rev. X 8 011042 Google Scholar
[42]	Liu C F, Leong W H, Xia K, Feng X, Finkler A, Denisenko A, Wrachtrup J, Li Q, Liu R B 2021 National Science Review 8 nwaa194 Google Scholar
[43]	Hayashi K, Matsuzaki Y, Taniguchi T, Shimo-Oka T, Nakamura I, Onoda S, Ohshima T, Morishita H, Fujiwara M, Saito S, Mizuochi N 2018 Phys. Rev. Appl. 10 034009 Google Scholar
[44]	Vetrone F, Naccache R, Zamarrn A, Juarranz de la Fuente A, Sanz-Rodrguez F, Martinez Maestro L, Martn Rodriguez E, Jaque D, Garca Sol J, Capobianco J A 2010 ACS Nano 4 3254 Google Scholar
[45]	Ermakova Y G, Lanin A A, Fedotov I V, Roshchin M, Kelmanson I V, Kulik D, Bogdanova Y A, Shokhina A G, Bilan D S, Staroverov D B, Balaban P M, Fedotov A B, Sidorov-Biryukov D A, Nikitin E S, Zheltikov A M, Belousov V V 2017 Nat. Commun. 8 15362 Google Scholar
[46]	Yukawa H, Fujiwara M, Kobayashi K, Kumon Y, Miyaji K, Nishimura Y, Oshimi K, Umehara Y, Teki Y, Iwasaki T, Hatano M, Hashimoto H, Baba Y 2020 Nanoscale Adv. 2 1859 Google Scholar
[47]	Simpson D A, Morrisroe E, McCoey J M, Lombard A H, Mendis D C, Treussart F, Hall L T, Petrou S, Hollenberg L C L 2017 ACS Nano 11 12077 Google Scholar
[48]	Fujiwara M, Sun S, Dohms A, Nishimura Y, Suto K, Takezawa Y, Oshimi K, Zhao L, Sadzak N, Umehara Y, Teki Y, Komatsu N, Benson O, Shikano Y, Kage-Nakadai E 2020 Sci. Adv. 6 eaba9636 Google Scholar
[49]	Tsai P C, Epperla C P, Huang J S, Chen O Y, Wu C C, Chang H C 2017 Angew.Chem. Int. Ed. 56 3025 Google Scholar
[50]	Mamaluy D, Gao X 2015 Appl. Phys. Lett. 106 193503 Google Scholar
[51]	Yue Y, Wang X 2012 Nano Rev. 3 11586 Google Scholar
[52]	Foy C, Zhang L, Trusheim M E, Bagnall K R, Walsh M, Wang E N, Englund D R 2020 ACS Appl. Mater. Interfaces 12 26525 Google Scholar
[53]	Andrich P, Li J, Liu X, Heremans F J, Nealey P F, Awschalom D D 2018 Nano Lett. 18 4684 Google Scholar
[54]	Zhang S C, Dong Y, Du B, Lin H B, Li S, Zhu W, Wang G Z, Chen X D, Guo G C, Sun F W 2021 Rev. Sci. Instrum. 92 044904 Google Scholar
[55]	Tetienne J P, Lombard A, Simpson D A, Ritchie C, Lu J, Mulvaney P, Hollenberg L C L 2016 Nano Lett. 16 326 Google Scholar

Cited By

图 1 不同温度零场劈裂. 横坐标为施加的微波频率, 纵坐标为归一化的荧光强度, 两条曲线代表不同的温度^[13]

Figure 1. Zero-field splitting with different temperatures. The horizontal coordinate is the applied microwave frequency, while the vertical coordinate is the normalized fluorescence intensity^[13].

DownLoad: Full-Size Img PowerPoint

图 2 光学探测磁共振谱和零声子线随温度的变化^[14]

Figure 2. Temperature dependent ODMR and zero-phonon line^[14].

DownLoad: Full-Size Img PowerPoint

图 3 三点快速测温法. 根据图中的3个点—f₁, f₂, f₃拟合出1个完整的ODMR曲线. 前提是整个ODMR曲线的形状变化不大^[36]

Figure 3. Three-point fast thermometry. A complete ODMR curve can be fitted according to the three points in the figure—f₁, f₂, f₃^[36]

DownLoad: Full-Size Img PowerPoint

图 4 利用自旋操作消除磁场相位的影响提高温度的灵敏度. 图(b)中的$ \pi/2 $用于产生叠加态, 3个$ \pi $脉冲用于改变相位的符号, 去除磁相位的影响^[28]

Figure 4. Spin operation is used to improve the temperature sensitivity by removing the effect of the magnetic field. The $ \pi/2 $ pulse in the panel (b) is used to generate the superposition state, and three $ \pi $ pulses are used to change the sign of the phase and remove the effect of the magnetic phase^[28]

DownLoad: Full-Size Img PowerPoint

图 5 各种体系的温度灵敏度与尺寸大小. 横坐标为传感器尺寸, 纵坐标为温度灵敏度^[29]

Figure 5. Temperature sensitivity versus size for various systems. The horizontal coordinate is the sensor size and the vertical coordinate is the temperature sensitivity^[29].

DownLoad: Full-Size Img PowerPoint

图 6 细胞内测温^[29]　(a)共聚焦下的荧光图, 虚线部分是细胞膜, 白色叉的部分表示金纳米颗粒的位置, 用来加热细胞. 圆圈表示纳米金刚石的位置. 旁边的颜色条是荧光的计数率. (b)不同金纳米颗粒的荧光条件下, 金刚石的温度差

Figure 6. Intracellular thermometry^[29]. (a) Fluorescence with confocal microscopy. The dashed part shows the cell membrane. The cross shows the position of gold nanoparticles, which is used to heat the cell. The circle shows the position of nanodiamond. The color bar next to it shows the count rate of fluorescence. (b) Temperature difference of diamond under different fluorescence conditions of gold nanoparticles

DownLoad: Full-Size Img PowerPoint

图 7 一体化细胞测温^[48]　(a)线虫示意图; (b)测量的样品室, 集成了微波、NV色心和细胞生活环境; (c)下半幅图为药物刺激下的温度变化反应, 上半幅图为对应的荧光强度; (d) 对照组

Figure 7. Integrated cellular thermometry^[48]: (a) Schematic diagram of Caenorhabditis elegans worms; (b) sample chamber: integrated microwave, NV color center and cell living environment; (c) the lower half shows the temperature change response to drug stimulation, and the upper half shows the corresponding fluorescence intensity; (d) the control

DownLoad: Full-Size Img PowerPoint

图 8 利用金刚石控制细胞的存活^[49]　(a)绿色的是蛋白质, 红色的是与金纳米颗粒混合的荧光纳米金刚石; (b)利用功率为330 μW的594 nm激光照射6 s后产生的结果: 细胞的膜隧道纳米管破裂了

Figure 8. Using diamond to control cell survival^[49]: (a) The green is protein and the red is fluorescent nanodiamond mixed with gold nanoparticles; (b) obtained results after a 594 nm laser irradiation at a power of 330 μW for 6 s: the membrane tunneling nanotubes of the cell ruptured

DownLoad: Full-Size Img PowerPoint

图 9 NV色心对材料的温度和磁场进行表征^[52]　(a)测量装置示意图, 插图的红色小点为纳米金刚石; (b)氮化镓高电子迁移率晶体管成像示意图; (c) 高分辨率磁场测量(功率为290 mW); (d), (e) 功率为1和1.73 W下沟道阻挡层的温度分布

Figure 9. Characterizing the temperature and magnetic field of the material with NV center^[52]: (a) Schematic diagram of the measurement device, and the red dots in the inset are nanodiamonds; (b) imaging schematic of a gallium nitride high-electron mobility transistor; (c) high-resolution magnetic field measurement (290 mW); (d), (e) temperature distribution of the channel stop at different powers of 1 and 1.73 W

DownLoad: Full-Size Img PowerPoint

图 10 利用PDMS进行局部测温^[53]　(a)纳米金刚石转移到PDMS上的微纳加工工艺; (b)通过ODMR拟合提取出温度信息, 并对温度进行重建之后的温度分布图

Figure 10. Local temperature measurement with PDMS^[53]: (a) Processing of nanodiamond transferred to PDMS; (b) temperature distribution after extracting the temperature information by ODMR fitting and reconstructing the temperature

DownLoad: Full-Size Img PowerPoint

图 11 利用光纤传感对芯片温度分布进行测量^[54]　(a)测量的系统, 结合了锁相放大系统与光纤系统; (b)色心传感装置示意图, 红色的螺旋线表示微波天线; (c), (d)芯片未通电与通电时的温度分布图; (e)对应于图(c)和图(d)的红色虚线测量值

Figure 11. Chip temperature distribution is measured using fiber optic sensing^[54]: (a) System of measurement, combining the phase-locked amplification system with the fiber optic system; (b) schematic diagram of the color center sensing device, with the red spiral lines indicating the microwave antenna; (c), (d) temperature distribution of the chip when it is powered off and on; (e) corresponds to the red dashed line measurements in panel (c) and (d)

DownLoad: Full-Size Img PowerPoint

图 12 对材料热导率进行测量^[33]　(a)实验装置, 电流沿着AFM的悬梁臂, 通过加热悬梁臂间接加热粘在上面的金刚石色心. 色心发出的荧光通过一个高数值孔径的显微镜收集. (b)与不同介质接触后金刚石的温度, 横坐标为加热的温度, 纵坐标为金刚石的温度

Figure 12. Measuring the thermal conductivity of materials^[33]. (a) Experimental setup, where current is flowing along the cantilever arm of the AFM and indirectly heats a diamond color center attached to it by heating the cantilever arm. The fluorescence emitted from NV center is collected through a microscope in a high numerical aperture. (b) Temperature of the diamond contact with different mediums. The horizontal coordinate is the temperature of heating and the vertical coordinate is the temperature of the diamond

DownLoad: Full-Size Img PowerPoint

表 1 NV色心的测量灵敏度

Table 1. Measurement sensitivity with NV color centers.

温度灵敏度/$({\rm{mK} }\cdot{ {\rm{Hz}^{-1/2} } })$	方法	样品	NV色心浓度或者碳含量	参考文献
0.43	利用自旋锁相结合ODMR	块状	0.1—1 × 10⁶ (99.99% ${ }^{12} {\rm{C}}$)	[35]
0.76	增加NV色心的浓度	块状	2.84 × 10⁶	[43]
1.6	借助磁场消磁测量温度	块状	0.15 × 10⁶	[40]
5	对自旋能级进行相干操控	块状	99.995% ${ }^{12} {\rm{C}}$	[28]
9	对自旋能级进行相干操控	块状	99.99% ${ }^{12}{\rm{ C}}$	[29]
10	对自旋能级进行相干操控	块状	1.1% ¹³C	[27]
10.1	利用多脉冲进行相干操控	块状	1.1% ¹³C	[37]
11	利用居里温度下磁场的改变推算出温度	100 nm	500个NV	[41]
0.076	利用居里温度下磁场的改变推算出温度	金刚石立柱	单个NV	[42]
130	对自旋能级进行相干操控	50 nm	无相关数据	[28]
300	NV色心电子态的超精细结构	50 nm	100个NV	[32]

DownLoad: CSV

[1]	van Oort E, Manson N B, Glasbeek M 1988 J. Phys. C: Solid State Phys. 21 4385 Google Scholar
[2]	Gruber A 1997 Science 276 2012 Google Scholar
[3]	Jelezko F, Gaebel T, Popa I, Domhan M, Gruber A, Wrachtrup J 2004 Phys. Rev. Lett. 93 130501 Google Scholar
[4]	Fuchs G D, Dobrovitski V V, Hanson R, Batra A, Weis C D, Schenkel T, Awschalom D D 2008 Phys. Rev. Lett. 101 117601 Google Scholar
[5]	Neumann P, Kolesov R, Jacques V, Beck J, Tisler J, Batalov A, Rogers L, Manson N B, Balasubramanian G, Jelezko F, Wrachtrup J 2009 New J. Phys. 11 013017 Google Scholar
[6]	Childress L, Hanson R 2013 MRS Bull. 38 134 Google Scholar
[7]	Chen X, Zou C, Gong Z, Dong C, Guo G, Sun F 2015 Light Sci. Appl. 4 e230 Google Scholar
[8]	Han K Y, Kim S K, Eggeling C, Hell S W 2010 Nano Lett. 10 3199 Google Scholar
[9]	Arroyo-Camejo S, Adam M P, Besbes M, Hugonin J P, Jacques V, Greffet J J, Roch J F, Hell S W, Treussart F 2013 ACS Nano 7 10912 Google Scholar
[10]	Maze J R, Stanwix P L, Hodges J S, Hong S, Taylor J M, Cappellaro P, Jiang L, Dutt M V G, Togan E, Zibrov A S, Yacoby A, Walsworth R L, Lukin M D 2008 Nature 455 644 Google Scholar
[11]	Dolde F, Fedder H, Doherty M W, Nbauer T, Rempp F, Balasubramanian G, Wolf T, Reinhard F, Hollenberg L C L, Jelezko F, Wrachtrup J 2011 Nat. Phys. 7 459 Google Scholar
[12]	Ovartchaiyapong P, Lee K W, Myers B A, Jayich A C B 2014 Nat. Commun. 5 4429 Google Scholar
[13]	Acosta V M, Bauch E, Ledbetter M P, Waxman A, Bouchard L S, Budker D 2010 Phys. Rev. Lett. 104 070801 Google Scholar
[14]	Chen X D, Dong C H, Sun F W, Zou C L, Cui J M, Han Z F, Guo G C 2011 Appl. Phys. Lett. 99 161903 Google Scholar
[15]	Hayashi T, Fukuda N, Uchiyama S, Inada N 2015 PLoS One 10 e0117677 Google Scholar
[16]	Jaque D, del Rosal B, Rodrguez E M, Maestro L M, Haro-Gonzlez P, Sol J G 2014 Nanomedicine 9 1047 Google Scholar
[17]	Somero G N 1995 Annu. Rev. Physiol. 57 43 Google Scholar
[18]	Suzuki M, Tseeb V, Oyama K, Ishiwata S I 2007 Biophys. J. 92 2 Google Scholar
[19]	Zohar O, Ikeda M, Shinagawa H, Inoue H, Nakamura H, Elbaum D, Alkon D L, Yoshioka T 1998 Biophys. J. 74 82 Google Scholar
[20]	Astakhov V P, Outeiro J 2019 Importance of Temperature in Metal Cutting and Its Proper Measurement/Modeling (Cham: Springer International Publishing) pp1–47
[21]	Shi L, Dames C, Lukes J R, Reddy P, Duda J, Cahill D G, Lee J, Marconnet A, Goodson K E, Bahk J H, Shakouri A, Prasher R S, Felts J, King W P, Han B, Bischof J C 2015 Nanoscale and Microscale Thermophys. Eng. 19 127 Google Scholar
[22]	Brites C D S, Balabhadra S, Carlos L D 2019 Adv. Opt. Mater. 7 1801239 Google Scholar
[23]	Doherty M W, Acosta V M, Jarmola A, Barson M S J, Manson N B, Budker D, Hollenberg L C L 2014 Phys. Rev. B 90 041201 Google Scholar
[24]	Li C C, Gong M, Chen X D, Li S, Zhao B W, Dong Y, Guo G C, Sun F W 2017 Diamond Relat. Mater. 74 119 Google Scholar
[25]	Schirhagl R, Chang K, Loretz M, Degen C L 2014 Annu. Rev. Phys. Chem. 65 83 Google Scholar
[26]	Toyli D M, Christle D J, Alkauskas A, Buckley B B, Van de Walle C G, Awschalom D D 2012 Phys. Rev. X 2 031001 Google Scholar
[27]	Toyli D M, de las Casas C F, Christle D J, Dobrovitski V V, Awschalom D D 2013 Proc. Natl. Acad. Sci. 110 8417 Google Scholar
[28]	Neumann P, Jakobi I, Dolde F, Burk C, Reuter R, Waldherr G, Honert J, Wolf T, Brunner A, Shim J H, Suter D, Sumiya H, Isoya J, Wrachtrup J 2013 Nano Lett. 13 2738 Google Scholar
[29]	Kucsko G, Maurer P C, Yao N Y, Kubo M, Noh H J, Lo P K, Park H, Lukin M D 2013 Nature 500 54 Google Scholar
[30]	Fedotov I V, Blakley S, Serebryannikov E E, Safronov N A, Velichansky V L, Scully M O, Zheltikov A M 2014 Appl. Phys. Lett. 105 261109 Google Scholar
[31]	Kraus H, Soltamov V A, Fuchs F, Simin D, Sperlich A, Baranov P G, Astakhov G V, Dyakonov V 2015 Sci. Rep. 4 5303 Google Scholar
[32]	Plakhotnik T, Aman H, Chang H C 2015 Nanotechnology 26 245501 Google Scholar
[33]	Laraoui A, Aycock-Rizzo H, Gao Y, Lu X, Riedo E, Meriles C A 2015 Nat. Commun. 6 8954 Google Scholar
[34]	Jelezko F, Wrachtrup J 2006 Phys. Status Solidi A 203 3207 Google Scholar
[35]	Wojciechowski A M, Karadas M, Osterkamp C, Jankuhn S, Meijer J, Jelezko F, Huck A, Andersen U L 2018 Appl. Phys. Lett. 113 013502 Google Scholar
[36]	Tzeng Y K, Tsai P C, Liu H Y, Chen O Y, Hsu H, Yee F G, Chang M S, Chang H C 2015 Nano Lett. 15 3945 Google Scholar
[37]	Wang J, Feng F, Zhang J, Chen J, Zheng Z, Guo L, Zhang W, Song X, Guo G, Fan L, Zou C, Lou L, Zhu W, Wang G 2015 Phys. Rev. B 91 155404 Google Scholar
[38]	Konzelmann P, Rendler T, Bergholm V, Zappe A, Pfannenstill V, Garsi M, Ziem F, Niethammer M, Widmann M, Lee S Y, Neumann P, Wrachtrup J 2018 New J. Phys. 20 123013 Google Scholar
[39]	Plakhotnik T, Doherty M W, Cole J H, Chapman R, Manson N B 2014 Nano Lett. 14 4989 Google Scholar
[40]	Zhang S C, Li S, Du B, Dong Y, Zheng Y, Lin H B, Zhao B W, Zhu W, Wang G Z, Chen X D, Guo G C, Sun F W 2019 Opt. Mater. Express 9 4634 Google Scholar
[41]	Wang N, Liu G Q, Leong W H, Zeng H, Feng X, Li S H, Dolde F, Fedder H, Wrachtrup J, Cui X D, Yang S, Li Q, Liu R B 2018 Phys. Rev. X 8 011042 Google Scholar
[42]	Liu C F, Leong W H, Xia K, Feng X, Finkler A, Denisenko A, Wrachtrup J, Li Q, Liu R B 2021 National Science Review 8 nwaa194 Google Scholar
[43]	Hayashi K, Matsuzaki Y, Taniguchi T, Shimo-Oka T, Nakamura I, Onoda S, Ohshima T, Morishita H, Fujiwara M, Saito S, Mizuochi N 2018 Phys. Rev. Appl. 10 034009 Google Scholar
[44]	Vetrone F, Naccache R, Zamarrn A, Juarranz de la Fuente A, Sanz-Rodrguez F, Martinez Maestro L, Martn Rodriguez E, Jaque D, Garca Sol J, Capobianco J A 2010 ACS Nano 4 3254 Google Scholar
[45]	Ermakova Y G, Lanin A A, Fedotov I V, Roshchin M, Kelmanson I V, Kulik D, Bogdanova Y A, Shokhina A G, Bilan D S, Staroverov D B, Balaban P M, Fedotov A B, Sidorov-Biryukov D A, Nikitin E S, Zheltikov A M, Belousov V V 2017 Nat. Commun. 8 15362 Google Scholar
[46]	Yukawa H, Fujiwara M, Kobayashi K, Kumon Y, Miyaji K, Nishimura Y, Oshimi K, Umehara Y, Teki Y, Iwasaki T, Hatano M, Hashimoto H, Baba Y 2020 Nanoscale Adv. 2 1859 Google Scholar
[47]	Simpson D A, Morrisroe E, McCoey J M, Lombard A H, Mendis D C, Treussart F, Hall L T, Petrou S, Hollenberg L C L 2017 ACS Nano 11 12077 Google Scholar
[48]	Fujiwara M, Sun S, Dohms A, Nishimura Y, Suto K, Takezawa Y, Oshimi K, Zhao L, Sadzak N, Umehara Y, Teki Y, Komatsu N, Benson O, Shikano Y, Kage-Nakadai E 2020 Sci. Adv. 6 eaba9636 Google Scholar
[49]	Tsai P C, Epperla C P, Huang J S, Chen O Y, Wu C C, Chang H C 2017 Angew.Chem. Int. Ed. 56 3025 Google Scholar
[50]	Mamaluy D, Gao X 2015 Appl. Phys. Lett. 106 193503 Google Scholar
[51]	Yue Y, Wang X 2012 Nano Rev. 3 11586 Google Scholar
[52]	Foy C, Zhang L, Trusheim M E, Bagnall K R, Walsh M, Wang E N, Englund D R 2020 ACS Appl. Mater. Interfaces 12 26525 Google Scholar
[53]	Andrich P, Li J, Liu X, Heremans F J, Nealey P F, Awschalom D D 2018 Nano Lett. 18 4684 Google Scholar
[54]	Zhang S C, Dong Y, Du B, Lin H B, Li S, Zhu W, Wang G Z, Chen X D, Guo G C, Sun F W 2021 Rev. Sci. Instrum. 92 044904 Google Scholar
[55]	Tetienne J P, Lombard A, Simpson D A, Ritchie C, Lu J, Mulvaney P, Hollenberg L C L 2016 Nano Lett. 16 326 Google Scholar

[1]	Shen Yuan-Yuan, Wang Bo, Ke Dong-Qian, Zheng Dou-Dou, Li Zhong-Hao, Wen Huan-Fei, Guo Hao, Li Xin, Tang Jun, Ma Zong-Min, Li Yan-Jun, Igor Vladimirovich Yaminsky, Liu Jun. High-frequency resolution diamond nitrogen-vacancy center wide-spectrum imaging technology. Acta Physica Sinica, 2024, 73(6): 067601. doi: 10.7498/aps.73.20231833
[2]	Liu Hui-Gang, Zhang Xiang-Yu, Nan Xue-Ying, Zhao Er-Gang, Liu Hai-Tao. All-dielectric metasurface two-parameter sensor based on quasi-bound states in continuum. Acta Physica Sinica, 2024, 73(4): 047802. doi: 10.7498/aps.73.20231514
[3]	Wu Bo, Lin Yi, Wu Feng-Chuan, Chen Xiao-Zhang, An Qiang, Liu Yi, Fu Yun-Qi. Quantum microwave electric field measurement technology based on enhancement electric filed resonator. Acta Physica Sinica, 2023, 72(3): 034204. doi: 10.7498/aps.72.20221582
[4]	Wu Jian-Dong, Cheng Zhi, Ye Xiang-Yu, Li Zhao-Kai, Wang Peng-Fei, Tian Chang-Lin, Cheng Hong-Wei. Coherent electrical control of a single electron spin in diamond nitrogen-vacancy centers. Acta Physica Sinica, 2022, 0(0): . doi: 10.7498/aps.71.20220410
[5]	Wu Jian-Dong, Cheng Zhi, Ye Xiang-Yu, Li Zhao-Kai, Wang Peng-Fei, Tian Chang-Lin, Chen Hong-Wei. Coherent electrical control of single electron spin in diamond nitrogen-vacancy center. Acta Physica Sinica, 2022, 71(11): 117601. doi: 10.7498/aps.70.20220410
[6]	Liu Gang-Qin. Diamond spin quantum sensing under extreme conditions. Acta Physica Sinica, 2022, 71(6): 066101. doi: 10.7498/aps.71.20212072
[7]	Yang Zhi-Ping, Kong Xi, Shi Fa-Zhan, Du Jiang-Feng. Phase transition observation of nanoscale water on diamond surface. Acta Physica Sinica, 2022, 71(6): 067601. doi: 10.7498/aps.71.20211348
[8]	. Temperature sensing with NV center in diamond. Acta Physica Sinica, 2021, (): . doi: 10.7498/aps.70.20211822
[9]	Zhao Peng-Ju, Kong Fei, Li Rui, Shi Fa-Zhan, Du Jiang-Feng. Nanoscale zero-field detection based on single solid-state spins in diamond. Acta Physica Sinica, 2021, 70(21): 213301. doi: 10.7498/aps.70.20211363
[10]	. Phase Transition Observation of Nanoscale Water on Diamond Surface. Acta Physica Sinica, 2021, (): . doi: 10.7498/aps.70.20211348
[11]	Shen Xiang, Zhao Li-Ye, Huang Pu, Kong Xi, Ji Lu-Min. Atomic spin and phonon coupling mechanism of nitrogen-vacancy center. Acta Physica Sinica, 2021, 70(6): 068501. doi: 10.7498/aps.70.20201848
[12]	Feng Yuan-Yao, Li Zhong-Hao, Zhang Yang, Cui Ling-Xiao, Guo Qi, Guo Hao, Wen Huan-Fei, Liu Wen-Yao, Tang Jun, Liu Jun. Optimization of optical control of nitrogen vacancy centers in solid diamond. Acta Physica Sinica, 2020, 69(14): 147601. doi: 10.7498/aps.69.20200072
[13]	Li Xue-Qin, Zhao Yun-Fang, Tang Yan-Ni, Yang Wei-Jun. Entanglement of quantum node based on hybrid system of diamond nitrogen-vacancy center spin ensembles and superconducting quantum circuits. Acta Physica Sinica, 2018, 67(7): 070302. doi: 10.7498/aps.67.20172634
[14]	Peng Shijie, Liu Ying, Ma Wenchao, Shi Fazhan, Du Jiangfeng. High-resolution magnetometry based on nitrogen-vacancy centers in diamond. Acta Physica Sinica, 2018, 67(16): 167601. doi: 10.7498/aps.67.20181084
[15]	Liu Gang-Qin, Xing Jian, Pan Xin-Yu. Quantum control of nitrogen-vacancy center in diamond. Acta Physica Sinica, 2018, 67(12): 120302. doi: 10.7498/aps.67.20180755
[16]	Dong Yang, Du Bo, Zhang Shao-Chun, Chen Xiang-Dong, Sun Fang-Wen. Solid quantum sensor based on nitrogen-vacancy center in diamond. Acta Physica Sinica, 2018, 67(16): 160301. doi: 10.7498/aps.67.20180788
[17]	Liu Dong-Qi, Chang Yan-Chun, Liu Gang-Qin, Pan Xin-Yu. Electron spin studies of nitrogen vacancy centers in nanodiamonds. Acta Physica Sinica, 2013, 62(16): 164208. doi: 10.7498/aps.62.164208
[18]	Miao Yin-Ping, Yao Jian-Quan. Temperature sensitivity of microstructured optical fiber filled with ferrofluid. Acta Physica Sinica, 2013, 62(4): 044223. doi: 10.7498/aps.62.044223
[19]	Zhang Chun-Shu, Kai Gui-Yun, Wang Zhi, Wang Chao, Sun Ting-Ting, Zhang Wei-Gang, Liu Yan-Ge, Liu Jian-Fei, Yuan Shu-Zhong, Dong Xiao-Yi. Temperature and strain sensing property of grapefruit microstructure fiber Bragg grating. Acta Physica Sinica, 2005, 54(6): 2758-2763. doi: 10.7498/aps.54.2758
[20]	Qiao Xue-Guang, Jia Zhen-An, Fu Hai-Wei, Li Ming, Zhou Hong. Theory and experiment about in-fiber Bragg grating temperature sensing. Acta Physica Sinica, 2004, 53(2): 494-497. doi: 10.7498/aps.53.494

Catalog

Vol. 71, Issue 6 - 2022-03-20

Metrics

Abstract views: 6071
PDF Downloads: 365
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板