Structure and magnetic properties of CoPt(FePt)-C nanocomposite films

Zhao Zi-Qiang Wang Hao Yang Fu-Jun Xue Shuang-Xi Cao Xin Wang Jun-An Gu Hao-Shuang

Structure and magnetic properties of CoPt(FePt)-C nanocomposite films

Zhao Zi-Qiang, Wang Hao, Yang Fu-Jun, Xue Shuang-Xi, Cao Xin, Wang Jun-An, Gu Hao-Shuang
PDF
Get Citation
Metrics
  • Abstract views:  3151
  • PDF Downloads:  884
  • Cited By: 0
Publishing process
  • Received Date:  05 July 2004
  • Accepted Date:  30 July 2004
  • Published Online:  17 March 2005

Structure and magnetic properties of CoPt(FePt)-C nanocomposite films

  • 1. (1)北京大学物理学院重离子物理教育部重点实验室,北京100871; (2)湖北大学物理学与电子技术学院,武汉430062

Abstract: CoPt(FePt)C nanocomposite thin films were prepared by a pulsed filtered vacuum arc deposition technique. Thermal annealing was performed in vacuum at various temperatures. The dependence of the magnetic properties on the carbon fraction and annealing temperature was studied. Both xray diffraction and magnetic force microscopy analyses confirmed the formation of nanocrystallites of facecenteredtetragonal phase of CoPt or FePt in the carbon matrix after annealing at a sufficiently high temperature. For the film with particular compositions of Co24Pt31C45 and Fe43Pt35C22,the coercivity and the grain size were observed to increase with increasing annealing temperature. For the Co24Pt31C45 film at an annealing temperature of 700℃, the coercivity was 2.1×105 A/m and the grain size was about 17nm. For the Fe43Pt35C22 film at an annealing temperature of 650℃, the values were 2.8×105 A/m and 105nm,respectively.