Nuclear fusion energy is a clean and safe energy resource with huge potential. Tungsten is the primary candidate for plasma facing materials (PFMs) in future nuclear reactors because of its high melting point, high thermal conductivity and high resistance to sputtering and erosion. However, the interaction between tungsten and helium plasma generated by deuterium-tritium nuclear reactions will result in the degeneration of tungsten through helium blistering in tungsten. The solubility of helium in tungsten is low, and it tends to aggregate at grain boundary, phase boundary, vacancies and dislocations, thus forming helium bubbles. These bubbles will lead to microstructure changes of surface and bulk phases, as well as a decrease in mechanical properties, which seriously affects the service life of material. Limited by experimental techniques, some basic problems for the growth of helium bubbles in tungsten are not clear, for instance, how the helium clusters migrate, and nucleation mechanisms. The study of complex helium bubble formation, evolution and its underlying mechanism in tungsten PFM necessitates advanced experimental techniques. Traditional methods such as ion implantation, scanning electron microscope and transmission electron microscope are inadequate for this task. Therefore, we propose the helium ion microscope method to investigate the aforementioned several aspects of helium in tungsten in situ and real-time. Here, a helium irradiation experiment is performed by helium ion microscope (HIM), featuring nanostructure fabrication, ion implantation and microscopic imaging. The HIM can generate an ion beam with energy in a range of 0.5−35 keV and an flux upto 1025 ions/m2/s. In the process of helium ion implantation, we observe in situ and real time the helium blistering and the morphological evolution on tungsten surface, in order to capture the helium implantation-induced microscopic damage evolution on tungsten surface and subsurface. From the results of in situ HIM experiments, it is believed that a strong orientation dependence of blistering is observed with the blister occurring preferentially on the surface of grains with normal direction close to (111), and surface blistering of tungsten is directly related to cracks immediately below the surface. The present study demonstrates that the HIM is a powerful tool for investigating the helium blistering behavior in tungsten and provides valuable experimental data and reference for designing PFMs.
-
Keywords:
- tungsten /
- helium behavior /
- helium ion microscope /
- real-time analysis of in situ
[1] Bolt H, Barabash V, Federici G, Linke J, Loate A, Roth J, Sato K 2002 J. Nucl. Mater. 43 307
[2] Lässer R, Baluc N, Boutard J L, Diegele E, Dudarev S, Möslang A, Pippan R, Riccardi B, Van der Schaaf B 2007 Fusion Eng. Des. 82 511
Google Scholar
[3] Wilson W D, Bisson C L, Baskes M L 1981 Phys. Rev. B. 24 5618
[4] Shahram S, Akiyuki T, Koji N, Nasr G 2009 J. Nucl. Mater. 389 203
Google Scholar
[5] Alimov V K, Wang Y W, Liang T R, Yu Q Z, Jia X J 2017 Fusion Eng. Des. 125 479
Google Scholar
[6] Zhou H B, Li Y H, Lu G H 2016 Comp. Mater. Sci. 112 487
Google Scholar
[7] Chen Z, Han W J, Yu J G, Laszlo K, Zhu K G , Wei Q M 2016 J. Nucl. Mater. 479 418
Google Scholar
[8] Al-Ajlony A, Tripathi J K, Hassanein A 2017 J. Nucl. Mater. 488 1
Google Scholar
[9] Wang L, Hao T, Zhao B L, Zhang T, Fang Q F, Liu C S, Wang X P, Cao L 2018 J. Nucl. Mater. 508 107
Google Scholar
[10] Chen Z, Niu L L, Wang Z L, Tian L F, Laszlo K, Zhu K G, Wei Q M 2018 Acta Materialia 147 100
Google Scholar
[11] Nishijima D, Ye M.Y, Ohno N 2004 J. Nucl. Mater. 329—333 1029
[12] Yang X, Hassanein A 2013 J. Nucl. Mater. 434 1
Google Scholar
[13] Ananth M, Scipioni L , Notte J 2008 Am. Lab. 40 42
[14] Economou N P, Notte J A, Thompson W B 2011 Scanning 33 1
Google Scholar
[15] Hlawacek G, Veligura V, Van Gastel R, Poelsema B 2014 J. Vac. Sci. Technol. B 32 020801
[16] Bergner F, Heintze C 2018 J. Nucl. Mater. 505 267
Google Scholar
[17] Hasenhuetl E, Zhang Z X, Kiyohiro Y, Peng S, Akihiko K 2017 Nucl. Instrum. Methods Phys. Res. Sect. B 397 11
Google Scholar
[18] Valles G, Panizo-Laiz M, Gonz_alez C, Martin-Bragado I, Gonz_alez-Arrabal R, Gordillo N, Iglesias R, Guerrero C L, Perlado J M 2017 Fusion Eng. Des. 125 479
Google Scholar
[19] Fukumoto M, Kashiwagi H, Ohtsuka Y, Ueda Y, Nobuta Y, Yagyu J, Arai T, Taniguchi M, Inoue T, Sakamoto K 2009 J. Nucl. Mater. 386—388 768
[20] Miyamoto M, Mikami S, Nagashima H, Iijima N, Nishijima D, Doerner R P, Yoshida N, Watanabe H , Ueda Y, Sagara A 2015 J. Nucl. Mater. 463 333
Google Scholar
[21] Liu F S, Rui H T, Peng S X, Zhu K G 2014 Nucl. Instrum. Methods Phys. Res. Sect. B 333 120
Google Scholar
[22] Gilliam S B, Gidcumb S M, Forsythe D 2005 Nucl. Instrum. Methods Phys. Res. Sect. B 241 491
Google Scholar
[23] Lindig S, Balden M, Kh Alimov V 2009 Phys. Scripta T 138 014040
[24] Smirnov R D, Krasheninnikov S I, Guterl J 2015 J. Nucl. Mater. 463 359
Google Scholar
-
图 1 HIM整体结构及其工作原理图 (a)整体结构; (b)工作原理
Figure 1. Schematic diagram and working principle diagram of HIM: (a) Schematic diagram; (b) working principle diagram.
图 2 W样品的EBSD衍射花样和表面微观形貌 (a)EBSD衍射花样; (b)表面微观形貌; (c)注入区域
Figure 2. EBSD map and surface micrograph of tungsten: (a) EBSD map of tungsten; (b) surface micrograph of tungsten; (c) the irradiated area of tungsten.
图 3 He泡生长过程的原位在线监测 (a) 120 s; (b) 240 s; (c) 360 s; (d) 480 s; (e) 600 s; (f) 720 s; (g) 840 s; (h) 960 s; (i) 1080 s; (j) 1200 s; (k) 1320 s; (l) 1440 s; (m) 1560 s; (n) 1680 s; (o) 1800 s; (p) 1920 s; (q) 2040 s; (r) 2160 s
Figure 3. In-situ observation of helium bubble growth during helium implantation: (a) 120 s; (b) 240 s; (c) 360 s; (d) 480 s; (e) 600 s; (f) 720 s; (g) 840 s; (h) 960 s; (i) 1080 s; (j) 1200 s; (k) 1320 s; (l) 1440 s; (m) 1560 s; (n) 1680 s; (o) 1800 s; (p) 1920 s; (q) 2040 s; (r) 2160 s.
图 4 He泡生长过程的在线监测 (a) 1100 s; (b) 1120 s; (c) 1140 s; (d) 1160 s; (e) 1180 s; (f) 1200 s; (g) 1220 s; (h) 1240 s
Figure 4. In-situ observation of helium bubble growth during helium implantation: (a) 1100 s; (b) 1120 s; (c) 1140 s; (d) 1160 s; (e) 1180 s; (f) 1200 s; (g) 1220 s; (h) 1240 s.
图 5 He泡生长过程的在线监测 (a) 120 s; (b) 240 s; (c) 360 s; (d) 480 s; (e) 600 s; (f) 720 s; (g) 840 s; (h) 960 s
Figure 5. In-situ observation of helium bubble growth during helium implantation: (a) 120 s; (b) 240 s; (c) 360 s; (d) 480 s; (e) 600 s; (f) 720 s; (g) 840 s; (h) 960 s.
图 6 He泡和裂纹的大小测量 (a)He泡; (b)裂纹
Figure 6. Measurement of the helium bubble and crack size: (a) Helium bubble; (b) crack.
图 7 氦泡横截面微观形貌
Figure 7. Cross-section of helium bubbles microstructure.
-
[1] Bolt H, Barabash V, Federici G, Linke J, Loate A, Roth J, Sato K 2002 J. Nucl. Mater. 43 307
[2] Lässer R, Baluc N, Boutard J L, Diegele E, Dudarev S, Möslang A, Pippan R, Riccardi B, Van der Schaaf B 2007 Fusion Eng. Des. 82 511
Google Scholar
[3] Wilson W D, Bisson C L, Baskes M L 1981 Phys. Rev. B. 24 5618
[4] Shahram S, Akiyuki T, Koji N, Nasr G 2009 J. Nucl. Mater. 389 203
Google Scholar
[5] Alimov V K, Wang Y W, Liang T R, Yu Q Z, Jia X J 2017 Fusion Eng. Des. 125 479
Google Scholar
[6] Zhou H B, Li Y H, Lu G H 2016 Comp. Mater. Sci. 112 487
Google Scholar
[7] Chen Z, Han W J, Yu J G, Laszlo K, Zhu K G , Wei Q M 2016 J. Nucl. Mater. 479 418
Google Scholar
[8] Al-Ajlony A, Tripathi J K, Hassanein A 2017 J. Nucl. Mater. 488 1
Google Scholar
[9] Wang L, Hao T, Zhao B L, Zhang T, Fang Q F, Liu C S, Wang X P, Cao L 2018 J. Nucl. Mater. 508 107
Google Scholar
[10] Chen Z, Niu L L, Wang Z L, Tian L F, Laszlo K, Zhu K G, Wei Q M 2018 Acta Materialia 147 100
Google Scholar
[11] Nishijima D, Ye M.Y, Ohno N 2004 J. Nucl. Mater. 329—333 1029
[12] Yang X, Hassanein A 2013 J. Nucl. Mater. 434 1
Google Scholar
[13] Ananth M, Scipioni L , Notte J 2008 Am. Lab. 40 42
[14] Economou N P, Notte J A, Thompson W B 2011 Scanning 33 1
Google Scholar
[15] Hlawacek G, Veligura V, Van Gastel R, Poelsema B 2014 J. Vac. Sci. Technol. B 32 020801
[16] Bergner F, Heintze C 2018 J. Nucl. Mater. 505 267
Google Scholar
[17] Hasenhuetl E, Zhang Z X, Kiyohiro Y, Peng S, Akihiko K 2017 Nucl. Instrum. Methods Phys. Res. Sect. B 397 11
Google Scholar
[18] Valles G, Panizo-Laiz M, Gonz_alez C, Martin-Bragado I, Gonz_alez-Arrabal R, Gordillo N, Iglesias R, Guerrero C L, Perlado J M 2017 Fusion Eng. Des. 125 479
Google Scholar
[19] Fukumoto M, Kashiwagi H, Ohtsuka Y, Ueda Y, Nobuta Y, Yagyu J, Arai T, Taniguchi M, Inoue T, Sakamoto K 2009 J. Nucl. Mater. 386—388 768
[20] Miyamoto M, Mikami S, Nagashima H, Iijima N, Nishijima D, Doerner R P, Yoshida N, Watanabe H , Ueda Y, Sagara A 2015 J. Nucl. Mater. 463 333
Google Scholar
[21] Liu F S, Rui H T, Peng S X, Zhu K G 2014 Nucl. Instrum. Methods Phys. Res. Sect. B 333 120
Google Scholar
[22] Gilliam S B, Gidcumb S M, Forsythe D 2005 Nucl. Instrum. Methods Phys. Res. Sect. B 241 491
Google Scholar
[23] Lindig S, Balden M, Kh Alimov V 2009 Phys. Scripta T 138 014040
[24] Smirnov R D, Krasheninnikov S I, Guterl J 2015 J. Nucl. Mater. 463 359
Google Scholar
-
[1] Qi Chao, Ma Yu-Tian, Qi Yan-Fei, Xiao Shan-Qu, Wang Bo. Influence of microstructure on thermal fatigue effect of W-PFM with laminated structure. Acta Physica Sinica, 2024, 0(0): . doi: 10.7498/aps.73.20240007 [2] Qin Meng-Fei, Wang Ying-Min, Zhang Hong-Yu, Sun Ji-Zhong. Molecular dynamics simulation of dynamic migration of $\boldsymbol {\langle 100\rangle} $ interstitial dislocation loops under (010) surfaces of pure W and W containing helium impurity. Acta Physica Sinica, 2023, 72(24): 245204. doi: 10.7498/aps.72.20230651[3] Zhang Guo-Shuai, Yin Chao, Wang Zhao-Fan, Chen Ze, Mao Shi-Feng, Ye Min-You. Simulation of neutron irradiation-induced recrystallization of tungsten. Acta Physica Sinica, 2023, 72(16): 162801. doi: 10.7498/aps.72.20230531 [4] Xu Chi, Wan Fa-Rong. Analysis of dislocation characteristics and inside-outside contrasts in irradiated and annealed tungsten as a fusion reactor material. Acta Physica Sinica, 2023, 72(5): 056801. doi: 10.7498/aps.72.20222124 [5] Huang Wen-Jun, Qiao Jun-Wei, Chen Shun-Hua, Wang Xue-Jiao, Wu Yu-Cheng. Preparation, structures and properties of tungsten-containing refractory high entropy alloys. Acta Physica Sinica, 2021, 70(10): 106201. doi: 10.7498/aps.70.20201986 [6] Zhu Te, Cao Xing-Zhong. Research progress of hydrogen/helium effects in metal materials by positron annihilation spectroscopy. Acta Physica Sinica, 2020, 69(17): 177801. doi: 10.7498/aps.69.20200724 [7] Zhou Liang-Fu, Zhang Jing, He Wen-Hao, Wang Dong, Su Xue, Yang Dong-Yang, Li Yu-Hong. The nucleation and growth of Helium hubbles at grain boundaries of bcc tungsten: a molecular dynamics simulation. Acta Physica Sinica, 2020, 69(4): 046103. doi: 10.7498/aps.69.20191069 [8] Guo Hong-Yan, Xia Min, Yan Qing-Zhi, Guo Li-Ping, Chen Ji-Hong, Ge Chang-Chun. Microstructure of medium energy and high density helium ion implanted tungsten. Acta Physica Sinica, 2016, 65(7): 077803. doi: 10.7498/aps.65.077803 [9] Huang Yan, Sun Ji-Zhong, Sang Chao-Feng, Ding Fang, Wang De-Zhen. Numerical study of the erosion of the EAST tungsten divertor targets caused by edge localized modes. Acta Physica Sinica, 2014, 63(3): 035204. doi: 10.7498/aps.63.035204 [10] Wang Xin-Xin, Zhang Ying, Zhou Hong-Bo, Wang Jin-Long. Effects of niobium on helium behaviors in tungsten：a first-principles investigation. Acta Physica Sinica, 2014, 63(4): 046103. doi: 10.7498/aps.63.046103 [11] Guo Long-Ting, Sun Ji-Zhong, Huang Yan, Liu Sheng-Guang, Wang De-Zhen. Molecular dynamics simulation of low-energy hydrogen atoms bombarding tungsten (001) surface at different angles and their depth distribution. Acta Physica Sinica, 2013, 62(22): 227901. doi: 10.7498/aps.62.227901 [12] Liu Wang, Wu Qi-Qi, Chen Shun-Li, Zhu Jing-Jun, An Zhu, Wang Yuan. Helium effect on the stability of the interface of Cu/W nanomultilayer. Acta Physica Sinica, 2012, 61(17): 176802. doi: 10.7498/aps.61.176802 [13] Wang Jun, Zhang Bao-Ling, Zhou Yu-Lu, Hou Qing. Molecular dynamics simulation of helium behavior in tungsten matrix. Acta Physica Sinica, 2011, 60(10): 106601. doi: 10.7498/aps.60.106601 [14] Wang Jun, Hou Qing. Molecular dynamics simulation of helium cluster growth in titanium. Acta Physica Sinica, 2009, 58(9): 6408-6412. doi: 10.7498/aps.58.6408 [15] Zhang Hong-Hua, Zhang Chong-Hong, Li Bing-Sheng, Zhou Li-Hong, Yang Yi-Tao, Fu Yun-Chong. Optical properties revealing annealing behavior of high-temperature He-implantation induced defects in silicon carbide. Acta Physica Sinica, 2009, 58(5): 3302-3308. doi: 10.7498/aps.58.3302 [16] Liu Shi, Zheng Hua, Zhao Yue, Xiong Liang-Yue, Wang Long-Bao, Yang Xun. The occupying activities of helium in ball-milled hydrogen-storage alloys. Acta Physica Sinica, 2003, 52(3): 756-760. doi: 10.7498/aps.52.756 [17] Fang Ye, Wei Ying, Zhong Fa-Peng, Bai Li-Chun, Tang You-Qi. . Acta Physica Sinica, 1995, 44(4): 599-605. doi: 10.7498/aps.44.599 [18] YANG CUI-YING, ZHANG DAO-FAN, WU XING, ZHOU YU-QING, FENG GUO-GUANG. ANALYTICAL ELECTRON MICROSCOPY OF DEFECTS IN PHOTOREFRACTIVE BaTiO3 CRYSTAL. Acta Physica Sinica, 1989, 38(12): 2003-2007. doi: 10.7498/aps.38.2003 [19] Cheng Wan-rong, Wu Zi-qin. THE TEM AND SEM OBSERVATIONS OF THE HIGH TEMPERATURE BEHAVIOURS OF COPPER ALLOY FILMS. Acta Physica Sinica, 1982, 31(10): 1387-1394. doi: 10.7498/aps.31.1387 [20] LIAO QIAN-CHU, WANG YUN, WANG HONG-JUN, LAN FEN-LAN. ANOMOLOUS PATTERNS OF TUNGSTEN SAMPLES OBSERVED WITH SCANNING ELECTRON MICROSCOPE. Acta Physica Sinica, 1980, 29(1): 131-137. doi: 10.7498/aps.29.131
DownLoad:
Catalog
Metrics
- Abstract views: 6518
- PDF Downloads: 85
- Cited By: 0