Preparation and temperature sensing properties of Tm3+, Yb3+ co-doped Bi2WO6 upconversion luminescent materials

Arepati Xiakeer; Wang Lin-Xiang; Li Qing; Bai Yun-Feng; Munire Maimaiti

doi:10.7498/aps.72.20222143

Abstract

Tm³⁺ and Yb³⁺, with different concentrations, co-doped Bi₂WO₆ up-conversion luminescence materials are prepared by high temperature solid state method. The microstructure, upconversion emission spectra, and optical temperature sensing properties of the synthesized powders are characterized and analyzed. The X-ray diffraction results show that the doping of Tm³⁺ and Yb³⁺ ions has little effect on the orthorhombic structure of Bi₂WO₆ matrix material. Under the 980 nm excitation, the maximum emission intensity of Tm³⁺ ions is obtained when the doping concentration of Tm³⁺ and Yb³⁺ are 1% and 6%, respectively. The intensities of four emission peaks of Tm³⁺ in 1%Tm³⁺, 6%Yb³⁺:Bi₂WO₆ sample increase with the excitation pump power increasing from 199 to 400 mW. With the excitation power of 199–400 mW, the sample light intensity I and the excitation power Pⁿ show a linear relationship. The relationship between the excitation pump power and the emission intensity of Tm³⁺ in this range is investigated. The four emission peaks of Tm³⁺ at 478, 650, 685 and 705 nm correspond to the n values of 1.01, 1.34, 1.77 and 1.75, respectively, indicating that the above emission peaks are derived from two-photon absorption. Under 980 nm excitation (power 379 mW), when the temperature increases from 298 to 573 K, the thermal coupling energy levels of Tm³⁺ in 1%Tm³⁺, 6%Yb³⁺:Bi₂WO₆ samples produce 705 and 685 nm emission whose intensities are increased by 28.4 times and 31.6 times, respectively. The relationship between the fluorescence intensity ratio of the thermal coupling energy levels (³F₃, ³F₂) of Tm³⁺ in the sample and the temperature is fitted. The maximum absolute temperature sensitivity of the sample is 0.00254 K^–1 at 298 K, and the maximum relative temperature sensitivity is 0.00144 K^–1. Under the same conditions, the relationship between the fluorescence intensity ratio of 705 and 650 nm produced by the non-thermal coupling energy level pair (³F₃, ¹G₄) and the temperature is fitted, and the maximum absolute temperature sensitivity is calculated to be 0.167 K^–1 at 573 K. The maximum relative temperature sensitivity is 0.0378 K^–1 at 298 K, which is 26 times higher than the relative maximum temperature sensitivity S_r of the thermal coupling level (³F₃, ³F₂).

Keywords:

Authors and contacts

1.
School of Physics and Electronic Engineering, Xinjiang Normal University, Urumqi 830054, China
2.
Xinjiang Key Laboratory for Luminescence Minerals and Optical Functional Materials, Xinjiang Normal University, Urumqi 830054, China

Corresponding author: Wang Lin-Xiang, wanglinxiang23@126.com

Funds: Project supported by the National Natural Science Foundation of China (Grant No. 12164048) and the Project of Key Laboratory Of Xinjiang Normal University, China (Grant No. KWFG202204).

FullText HTML : translate this paragraph

References

[1]	Ruiz D, Rosal B, Acebrón M, et al. 2017 Adv. Funct. Mater. 27 1604629 Google Scholar
[2]	周慧丽, 吴锋, 张志宏, 张雁, 叶林华 2022 发光学报 43 192 Google Scholar Zhou H L, Wu F, Zhang Z H, Zhang Y, Ye L H 2022 Chin. J. Lumin. 43 192 Google Scholar
[3]	谢宇 2016 硕士学位论文 (沈阳: 辽宁大学) Xie Y 2016 M. S. Thesis (Shenyang: Liaoning University) (in Chinese)
[4]	吴中立, 吴红梅, 唐立丹, 李煜, 郭宇, 姚震 2017 光子学报 46 0916003 Google Scholar Wu Z L, Wu H M, Tang L D, Li Y, Guo Y, Yao Z 2017 Acta Photonica Sin. 46 0916003 Google Scholar
[5]	Xing J H, Shang F, Chen G H 2021 J. Non-Cryst. Solids 569 120989 Google Scholar
[6]	Saidi K, Dammak M, Soler-Carracedo K, Martín I 2022 Dalton Trans. 51 5108 Google Scholar
[7]	Meng M Z, Zhang R, Fa X M, et al. 2022 CrystEngComm 24 1752 Google Scholar
[8]	Zhuang Y F, Wang D W, Yang Z P 2022 Opt. Mater. 126 112167 Google Scholar
[9]	Zheng T, Runowski M, Stopikowska N, Skwierczyńska M, Lis S, Du P, Luo L H 2021 J. Alloys Compd. 890 161830 Google Scholar
[10]	蒙铭周, 张瑞, 法信蒙, 杨江华, 欧俊 2021 发光学报 42 1763 Google Scholar Meng M Z, Zhang R, Fa X M, Yang J H, Ou J 2021 Chin. J. Lumin. 42 1763 Google Scholar
[11]	郑龙江, 李雅新, 刘海龙, 徐伟, 张志国 2013 物理学报 62 240701 Google Scholar Zheng L J, Li Y X, Liu H L, Xu W, Zhang Z G 2013 Acta Phys. Sin. 62 240701 Google Scholar
[12]	Wu Z L, Zhang Y P, Bao D M, Li H Q, Hou X Q, Wang J L 2022 J. Lumin. 245 118766 Google Scholar
[13]	Lü H C, Du P, Li W P, Luo L H 2022 ACS Sustainable Chem. Eng. 10 2450 Google Scholar
[14]	Gao Z L, Wang J R, Yu D C, Pun E Y B, Lin H 2022 Adv. Mater. Interfaces 9 2101869 Google Scholar
[15]	张志宏, 周慧丽, 吴锋, 张雁, 叶林华 2021 发光学报 42 1872 Google Scholar Zhang Z H, Zhou H L, Wu F, Zhang Y, Ye L H 2021 Chin. J. Lumin. 42 1872 Google Scholar
[16]	Wang T W, Zhao S L, Lei R S, Huang L H, Xu S Q 2022 J. Non-Cryst. Solids 579 121379 Google Scholar
[17]	Tong X, Zhou X, Tang X Z, Min Y G, Li X L, Wang W G, Qian Y N 2022 CrystEngComm 24 1407 Google Scholar
[18]	Wang X F, Liu Q, Bu Y Y, Liu C S, Liu T, Yan X H 2015 RSC Adv. 5 86219 Google Scholar
[19]	Liu Z H, Long S W, Zhu Y Z, Wang W J, Wang B 2020 J. Alloys Compd. 867 158986 Google Scholar
[20]	Sun Z, Liu G F, Fu Z L, et al. 2018 Dyes Pigm. 151 287 Google Scholar

Cited By

图 1 (a) xTm³⁺, 6%Yb³⁺:Bi₂WO₆的XRD图谱(x = 0.5%, 1%, 1.5%, 2%); (b) 1%Tm³⁺, yYb³⁺:Bi₂WO₆ (y = 4%, 6%, 8%, 10%)的XRD图谱

Figure 1. (a) XRD patterns of xTm³⁺, 6%Yb³⁺:Bi₂WO₆ (x = 0.5%, 1%, 1.5%, 2%); (b) XRD patterns of 1%Tm³⁺, yYb³⁺:Bi₂WO₆ (y = 4%, 6%, 8%, 10%).

DownLoad: Full-Size Img PowerPoint

图 2 980 nm激光(379 mW)激发下Tm³⁺, Yb³⁺共掺Bi₂WO₆的上转换发射光谱　(a) xTm³⁺, 6%Yb³⁺:Bi₂WO₆; (b) 1%Tm³⁺, yYb³⁺:Bi₂WO₆

Figure 2. Upconversion emission spectra of Tm³⁺, Yb³⁺ co-doped Bi₂WO₆ excited by 980 nm laser (379 mW): (a) xTm³⁺, 6%Yb³⁺:Bi₂WO₆; (b) 1%Tm³⁺, yYb³⁺:Bi₂WO₆.

DownLoad: Full-Size Img PowerPoint

图 3 Yb³⁺敏化Tm³⁺的上转换发光过程

Figure 3. Upconversion luminescence process of Yb³⁺ sensitized Tm³⁺.

DownLoad: Full-Size Img PowerPoint

图 4 980 nm激光激发下, 不同泵浦功率时1%Tm³⁺, 6%Yb³⁺:Bi₂WO₆的上转换光谱

Figure 4. Upconversion spectra of 1%Tm³⁺, 6%Yb³⁺:Bi₂WO₆ excited by 980 nm laser at different pump powers.

DownLoad: Full-Size Img PowerPoint

图 5 1%Tm³⁺, 6%Yb³⁺:Bi₂WO₆的上转换发射强度与泵浦功率的关系

Figure 5. Relationship between upconversion luminescence intensity and pump power of 1%Tm³⁺, 6% Yb³⁺:Bi₂WO₆.

DownLoad: Full-Size Img PowerPoint

图 6 (a) 不同温度下1%Tm³⁺, 6%Yb³⁺:Bi₂WO₆的上转换发射谱; (b) 红色荧光强度的变化(685, 705 nm)

Figure 6. (a) Upconversion emission spectra of 1%Tm³⁺, 6%Yb³⁺:Bi₂WO₆ at different temperatures; (b) change of red fluorescence intensity (685, 705 nm).

DownLoad: Full-Size Img PowerPoint

图 7 Tm³⁺热耦合能级对³F₃/³F₂产生的705和685 nm处荧光强度比与温度的关系

Figure 7. Relationship between the fluorescence intensity ratio at 705 and 685 nm and the absolute temperature for ³F₃/³F₂ produced by Tm³⁺ thermal coupling energy level.

DownLoad: Full-Size Img PowerPoint

图 8 样品的热耦合能级对³F₃/³F₂表征温度时对应的(a)绝对灵敏度和(b)相对测温灵敏度

Figure 8. (a) Absolute temperature sensitivity and (b) relative temperature sensitivity of samples characterized by thermal coupling energy level ³F₃/³F₂.

DownLoad: Full-Size Img PowerPoint

图 9 非热耦合能级对³F₃/¹G₄产生的705和650 nm处荧光强度比与温度的关系

Figure 9. Temperature dependence of fluorescence intensity ratio at 705 and 650 nm produced by ³F₃/¹G₄ at non-thermal coupling level.

DownLoad: Full-Size Img PowerPoint

图 10 非热耦合能级对³F₃/¹G₄表征温度时的绝对测温灵敏度(a)和相对测温灵敏度(b)

Figure 10. Absolute temperature sensitivity (a) and relative temperature sensitivity (b) of ³F₃/¹G₄ at characterization temperature by non-thermal coupling level.

DownLoad: Full-Size Img PowerPoint

图 11 298和573 K下R_FIR1 (a)以及R_FIR2 (b)稳定性测试

Figure 11. Stability test of R_FIR1 (a) and R_FIR2 (b) at 298 and 573 K .

DownLoad: Full-Size Img PowerPoint

表 1 800 ℃下煅烧3 h合成不同浓度Tm³⁺, Yb³⁺共掺Bi₂WO₆材料

Table 1. Synthesis of Tm³⁺, Yb³⁺ co-doped Bi₂WO₆ materials with different doping concentration at the sintering temperature and time of 800 ℃ and 3 h.

Sample No.	Mole fraction of Tm³⁺/%	Mole fraction of Yb³⁺/%	Mole fraction of Bi₂WO₆/%
1	0.5	6	93.5
2	1	6	93
3	1.5	6	92.5
4	2	6	92
5	1	4	95
6	1	8	91
7	1	10	89

DownLoad: CSV

表 2 不同基质材料中Tm³⁺温度传感性能

Table 2. Temperature sensing performance of Tm³⁺ in various host materials.

Host material	Energy level	Temperature range/K	Relative temperature measurement sensitivity/K^–1	Ref.
SiO₂@Tm³⁺:NaYbF₄	³F_{2, 3}, ³H₄→³H₆	100—700	Max = 0.00054@298 K	[18]
Tm³⁺, Yb³⁺:LuYO₃	³F₂, ³F₃→³H₆	223—723	Max = 0.00461@516.3 K	[15]
Tm³⁺, Yb³⁺:LiNbO₃	¹G₄→³F₄, ³H₄→³H₆	80—260	Max = 0.0125@80 K	[19]
Tm³⁺, Yb³⁺:Bi_3.84W_0.16O_6.24	³H₄₍₁₎, ³H₄₍₂₎→³H₆	323—573	Max = 0.00068@323 K	[20]
Li⁺, Tm³⁺, Yb³⁺:Bi_3.84W_0.16O_6.24	³H₄₍₁₎, ³H₄₍₂₎→³H₆	323—573	Max = 0.00103@323 K
Mg²⁺, Tm³⁺, Yb³⁺:Bi_3.84W_0.16O_6.24	³H₄₍₁₎, ³H₄₍₂₎→³H₆	323—573	Max = 0.00070@323 K
Tm³⁺, Yb³⁺:Bi₂WO₆	³F₂, ₃→³H₆	298—573	Max = 0.00144@298 K	This work
	³F₂, ₃→³H₆	313	0.0013 K^–1
	³F₂, ₃→³H₆	323	0.0012 K^–1
	³F₃→³H₆, ¹G₄→³F₄	298—573	Max = 0.0378@298 K
	³F₃→³H₆, G₄→³F₄	313	0.0343 K^–1
	³F₃→³H₆, ¹G₄→³F₄	323	0.0322 K^–1

DownLoad: CSV

[1]	Ruiz D, Rosal B, Acebrón M, et al. 2017 Adv. Funct. Mater. 27 1604629 Google Scholar
[2]	周慧丽, 吴锋, 张志宏, 张雁, 叶林华 2022 发光学报 43 192 Google Scholar Zhou H L, Wu F, Zhang Z H, Zhang Y, Ye L H 2022 Chin. J. Lumin. 43 192 Google Scholar
[3]	谢宇 2016 硕士学位论文 (沈阳: 辽宁大学) Xie Y 2016 M. S. Thesis (Shenyang: Liaoning University) (in Chinese)
[4]	吴中立, 吴红梅, 唐立丹, 李煜, 郭宇, 姚震 2017 光子学报 46 0916003 Google Scholar Wu Z L, Wu H M, Tang L D, Li Y, Guo Y, Yao Z 2017 Acta Photonica Sin. 46 0916003 Google Scholar
[5]	Xing J H, Shang F, Chen G H 2021 J. Non-Cryst. Solids 569 120989 Google Scholar
[6]	Saidi K, Dammak M, Soler-Carracedo K, Martín I 2022 Dalton Trans. 51 5108 Google Scholar
[7]	Meng M Z, Zhang R, Fa X M, et al. 2022 CrystEngComm 24 1752 Google Scholar
[8]	Zhuang Y F, Wang D W, Yang Z P 2022 Opt. Mater. 126 112167 Google Scholar
[9]	Zheng T, Runowski M, Stopikowska N, Skwierczyńska M, Lis S, Du P, Luo L H 2021 J. Alloys Compd. 890 161830 Google Scholar
[10]	蒙铭周, 张瑞, 法信蒙, 杨江华, 欧俊 2021 发光学报 42 1763 Google Scholar Meng M Z, Zhang R, Fa X M, Yang J H, Ou J 2021 Chin. J. Lumin. 42 1763 Google Scholar
[11]	郑龙江, 李雅新, 刘海龙, 徐伟, 张志国 2013 物理学报 62 240701 Google Scholar Zheng L J, Li Y X, Liu H L, Xu W, Zhang Z G 2013 Acta Phys. Sin. 62 240701 Google Scholar
[12]	Wu Z L, Zhang Y P, Bao D M, Li H Q, Hou X Q, Wang J L 2022 J. Lumin. 245 118766 Google Scholar
[13]	Lü H C, Du P, Li W P, Luo L H 2022 ACS Sustainable Chem. Eng. 10 2450 Google Scholar
[14]	Gao Z L, Wang J R, Yu D C, Pun E Y B, Lin H 2022 Adv. Mater. Interfaces 9 2101869 Google Scholar
[15]	张志宏, 周慧丽, 吴锋, 张雁, 叶林华 2021 发光学报 42 1872 Google Scholar Zhang Z H, Zhou H L, Wu F, Zhang Y, Ye L H 2021 Chin. J. Lumin. 42 1872 Google Scholar
[16]	Wang T W, Zhao S L, Lei R S, Huang L H, Xu S Q 2022 J. Non-Cryst. Solids 579 121379 Google Scholar
[17]	Tong X, Zhou X, Tang X Z, Min Y G, Li X L, Wang W G, Qian Y N 2022 CrystEngComm 24 1407 Google Scholar
[18]	Wang X F, Liu Q, Bu Y Y, Liu C S, Liu T, Yan X H 2015 RSC Adv. 5 86219 Google Scholar
[19]	Liu Z H, Long S W, Zhu Y Z, Wang W J, Wang B 2020 J. Alloys Compd. 867 158986 Google Scholar
[20]	Sun Z, Liu G F, Fu Z L, et al. 2018 Dyes Pigm. 151 287 Google Scholar

[1]	Mu Li-Peng, Zhou Yao, Zhao Jian-Xing, Wang Li, Jiang Li, Zhou Jian-Hong. Enhancement of NaYF₄:Yb³⁺/Er³⁺ up-conversion luminescence based on anodized alumina template. Acta Physica Sinica, 2024, 73(3): 037803. doi: 10.7498/aps.73.20231405
[2]	Chen Gui-Ling, Ma Jia-Jia, Sun Jia-Shi, Zhang Jin-Su, Li Xiang-Ping, Xu Sai, Zhang Xi-Zhen, Cheng Li-Hong, Chen Bao-Jiu. Preparation and upconversion luminescence properties of GdTaO₄:RE/Yb(RE=Tm, Er) phosphor through experimental optimization design. Acta Physica Sinica, 2022, 71(16): 163301. doi: 10.7498/aps.71.20220474
[3]	Gao Wei, Sun Ze-Yu, Guo Li-Chun, Han Shan-Shan, Chen Bin-Hui, Han Qing-Yan, Yan Xue-Wen, Wang Yong-Kai, Liu Ji-Hong, Dong Jun. Upconversion luminescence characteristics of Ho³⁺ ion doped single-particle fluoride micron core-chell structure. Acta Physica Sinica, 2022, 71(3): 034207. doi: 10.7498/aps.71.20211719
[4]	. Upconversion luminescence characteristics of Ho3+ ion doped single-particle fluoride micron core-chell structure. Acta Physica Sinica, 2021, (): . doi: 10.7498/aps.70.20211719*
[5]	Gao Wei, Wang Bo-Yang, Han Qing-Yan, Han Shan-Shan, Cheng Xiao-Tong, Zhang Chen-Xue, Sun Ze-Yu, Liu Lin, Yan Xue-Wen, Wang Yong-Kai, Dong Jun. Building vertical gold nanorod arrays to enhance upconversion luminescence of β-NaYF₄: Yb³⁺/Er³⁺ nanocrystals. Acta Physica Sinica, 2020, 69(18): 184213. doi: 10.7498/aps.69.20200575
[6]	Gao Wei, Wang Bo-Yang, Sun Ze-Yu, Gao Lu, Zhang Chen-Xue, Han Qing-Yan, Dong Jun. Tuning upconversion emissions of Ho³⁺ through changing excitation conditions. Acta Physica Sinica, 2020, 69(3): 034207. doi: 10.7498/aps.69.20191333
[7]	Liu Bei, Lu Xi-Jian, Liu Xiao-Ning, Wu Yi-Pin, Zou Bin. Hot injection synthesis of core-shell upconversion nanoparticles for bioimaging application. Acta Physica Sinica, 2020, 69(14): 147801. doi: 10.7498/aps.69.20200347
[8]	Yang Jian-Zhi, Qiu Jian-Bei, Yang Zheng-Wen, Song Zhi-Guo, Yang Yong, Zhou Da-Cheng. Preparation and upconversion luminescence properties of Ba5SiO4Cl6: Yb3+, Er3+, Li+ phosphors. Acta Physica Sinica, 2015, 64(13): 138101. doi: 10.7498/aps.64.138101
[9]	Mao Xin-Guang, Wang Jun, Shen Jie. Upconversion luminescence properties in Er3+/Yb3+ codoped TiO2 films prepared by magnetron sputtering. Acta Physica Sinica, 2014, 63(8): 087803. doi: 10.7498/aps.63.087803
[10]	Zheng Long-Jiang, Li Ya-Xin, Liu Hai-Long, Xu Wei, Zhang Zhi-Guo. Up-conversion luminescence and temperature characteristics of Tm3+, Yb3+ co-doped CaWO4 polycrystal material. Acta Physica Sinica, 2013, 62(24): 240701. doi: 10.7498/aps.62.240701
[11]	Sun Yu, Yang Chun-Hui, Jiang Zhao-Hua, Meng Xiang-Bin. Room temperature absorption spectra analysis of Er3+/Yb3+-doped Hydrothermal Epitaxial Layer on LiNbO3 and LiTaO3 Single Crystal Substrates. Acta Physica Sinica, 2012, 61(12): 127801. doi: 10.7498/aps.61.127801
[12]	Peng Yong, Xing Ming-Ming, Luo Xi-Xian, Wang Li-Qiang. Synthesis and characteristic research of nanoparticles KY3F10: Yb, RE (RE=Er, Ho, Tm) by thermal decomposition. Acta Physica Sinica, 2012, 61(13): 137201. doi: 10.7498/aps.61.137201
[13]	Wang Da-Gang, Zhou Ya-Xun, Wang Xun-Si, Dai Shi-Xun, Shen Xiang, Chen Fei-Fei, Wang Sen. Upconversion luminescence of Tm3+/Ho3+/Yb3+ codoped tellurite glass used for white light emission. Acta Physica Sinica, 2010, 59(9): 6256-6260. doi: 10.7498/aps.59.6256
[14]	Yuan Ning-Yi, Chen Xiao-Shuang, Ding Jian-Ning, He Ze-Jun, Li Feng, Lu Wei. Quantum effect and up-conversion luminescence of ZnO-SiO2 composite films synthesized by sol-gel technique. Acta Physica Sinica, 2009, 58(4): 2649-2653. doi: 10.7498/aps.58.2649
[15]	Gan Zong-Song, Yu Hua, Li Yan-Ming, Wang Ya-Nan, Chen Hui, Zhao Li-Juan. Investigation on up-conversion luminescence of Tm3+ and Yb3+ codoped oxy-fluorosilicate glass ceramics. Acta Physica Sinica, 2008, 57(9): 5699-5704. doi: 10.7498/aps.57.5699
[16]	Jin Zhe, Nie Qiu-Hua, Xu Tie-Feng, Dai Shi-Xun, Shen Xiang, Zhang Xiang-Hua. Energy transfer and upconversion luminescence of Tm3+/Yb3+ co-doped lanthanum-zinc-lead-tellurite glasses. Acta Physica Sinica, 2007, 56(4): 2261-2267. doi: 10.7498/aps.56.2261
[17]	Wen Lei, Zhang Li-Yan, Yang Jian-Hu, Wang Guo-Nian, Chen Wei, Hu Li- Li. Upconversion emission properties of Er3+ in fluoride (halide) phosphate tellurite glasses. Acta Physica Sinica, 2006, 55(3): 1486-1490. doi: 10.7498/aps.55.1486
[18]	Wen Lei, Yang Jian-Hu, Hu Li-Li. Determination of upconversion state lifetime and upconversion mechanisms of Er3+ in tellurite glasses. Acta Physica Sinica, 2004, 53(12): 4378-4381. doi: 10.7498/aps.53.4378
[19]	Chen Xiao-Bo, Liu Kai, Zhang Jian, Wang Guo-Wen, Chen Chang-Tian. . Acta Physica Sinica, 2002, 51(3): 690-695. doi: 10.7498/aps.51.690
[20]	Zhao Li-Juan, Sun Ling-Dong, Xu Jing-Jun, Zhang Guang-Yin. . Acta Physica Sinica, 2001, 50(1): 63-67. doi: 10.7498/aps.50.63

Catalog

Vol. 72, Issue 6 - 2023-03-20

Metrics

Abstract views: 7019
PDF Downloads: 93
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Preparation and temperature sensing properties of Tm³⁺, Yb³⁺ co-doped Bi₂WO₆ upconversion luminescent materials

Abstract

Authors and contacts

Corresponding author: Wang Lin-Xiang, wanglinxiang23@126.com

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板