Proton irradiation induced damage effects in CH3NH3PbI3-based perovskite solar cells

Xue Bin-Tao; Zhang Li-Min; Liang Yong-Qi; Liu Ning; Wang Ding-Ping; Chen Liang; Wang Tie-Shan

doi:10.7498/aps.72.20222100

Abstract

Perovskite solar cells (PSCs) have a great potential for space applications due to their high specific power, low cost and high defect tolerance. PSCs used in space will be subjected to high-energy particle irradiation, especially proton irradiation, resulting in the decline of photovoltaic (PV) performance. However, the research on proton irradiation effects in PSCs is still in its infancy stage. In this work, the CH₃NH₃PbI₃ (MAPbI₃) thin films and their PSCs are irradiated by protons with energy of 0.1, 2, 10, 20 MeV, etc. Irradiation-induced changes in PV parameters of the PSCs are studied as a function of proton fluence. The structural and surface morphological changes of the irradiated MAPbI₃ films and Au electrode layers of PSCs are characterized by X-ray diffraction and scanning electron microscopy. In addition, UV spectrophotometer is also employed to analyze the transmission loss in glass substrate induced by proton irradiation. It is found that PSCs exhibit superior resistance against proton irradiation. The PV properties of the PSCs don’t degrade after 0.1 MeV (2 MeV) proton irradiation up to a fluence of 1×10¹³ p/cm² (1×10¹⁴ p/cm²). The irradiation-induced damage in the charge transport layers may be the main cause for the performance degradation of PSCs. The gaseous products (NH₃ and CH₃I) of perovskite decomposition eventually lead to exfoliation of the top Au electrode from the PSCs. Regarding 10 and 20 MeV proton irradiation with larger projected ion ranges, the irradiations create color center defects in glass substrate of PSCs, which results in a decrease in light transmission of visible spectrum. However, the color center defects, specifically non-bridging oxygen hole centers, will be partly annealed at room temperature or 100 ℃, reducing the transmission loss in glass. The reported results may help predict the performance degradation of PSCs in space irradiation environment.

Keywords:

Authors and contacts

1.
School of Nuclear Science and Technology, Lanzhou University, Lanzhou 730000, China
2.
Key Laboratory of Advanced Catalysis of Gansu Province, College of Chemistry and Chemical Engineering, Lanzhou University, Lanzhou 730000, China

Corresponding author: Zhang Li-Min, zhanglm@lzu.edu.cn

Funds: Project supported by the Fund of National Innovation Center of Radiation Application (Grant No. KZFC2020020201) and the National Natural Science Foundation of China (Grant No. U20B2008).

FullText HTML : translate this paragraph

References

[1]	Kojima A, Techima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[2]	Jeon N J, Noh J H, Yang W S, Kim Y C, Ryu S, Seo J, Seok S I 2015 Nature 517 476 Google Scholar
[3]	Saliba M, Matsui T, Seo J Y, Domanski K, Correa-Baena J P, Nazeeruddin M K, Zakeeruddin S M, Tress W, Abate A, Hagfeldt Anders, Grätzel M 2016 Energy Environ. 9 1989 Google Scholar
[4]	Min H, Lee D Y, Kim J, Kim G, Lee K S, Kim J, Paik M J, Kim Y K, Kim K S, Kim M G, Shin T J, Seok S I 2021 Nature 598 444 Google Scholar
[5]	Kang S, Jeong J, Cho S, Yoon Y J, Park S, Lim S, Kim J Y, Ko H 2019 J. Mater. Chem. A 7 1107 Google Scholar
[6]	AZUR SPACE. http://www.azurspace.com/index.php/en/ [2022-09-14]
[7]	Kheraj V, Simond B J, Toshniwal A, Misra S, Peroncik P, Zhang C, Vardeny Z V, Scarpulla M A 2018 J. Lumin. 194 353 Google Scholar
[8]	Tu Y, Wu J, Xu G, Yang X, Cai R, Gong Q, Zhu R, Huang W 2021 Adv. Mater. 33 2006545 Google Scholar
[9]	Yang J, Bao Q, Shen L, Ding L 2020 Nano Energy 76 105019 Google Scholar
[10]	Miyazawa Y, Ikegami M, Chen H W, Ohshima T, Imaizumi M, Hirose K, Miyasaka T 2018 iScience 2 148 Google Scholar
[11]	Xiong G, Qin Z, Li B, Wang L, Zhang X, Zheng Z, Zhu H, Zhao S, Gao J, Li B, Yang J, Li X, Luo J, Han Z, Liu X, Zhao F 2021 J. Mater. Chem. C 9 2095 Google Scholar
[12]	Durant B K, Afshari H, Singh S, Rout B, Eperon G E, Sellers I R 2021 ACS Energy Lett. 6 2362 Google Scholar
[13]	Barbé J, Hughes D, Wei Z, Pockett A, Lee H K H, Heasman K C, Carnie M J, Watson T M, Tsoi W C 2019 Sol. Rrl. 3 1900219 Google Scholar
[14]	Brus V V, Lang F, Bundesmann J, Seidel S, Denker A, Rech B, Landi G, Neitzert H C, Rappich J, Nickel N H 2017 Adv. Electron. Mater. 3 1600438 Google Scholar
[15]	Boldyreva A G, Frolova L A, Zhidkov I S, Gutsev L G, Kurmaev E Z, Ramachandran B R, Petrov V G, Stevenson K J, Aldoshin S M, Troshin P A 2020 J. Phys. Chem. Lett. 11 2630 Google Scholar
[16]	Boldyreva A G, Akbulatov A F, Tsarev S A, Luchkin S Y, Zhidkov I S, Kurmaev E Z, Stevenson K J, Petrov V G, Troshin P A 2019 J. Phys. Chem. Lett. 10 813 Google Scholar
[17]	Tu Y, Xu G, Yang X, Zhang Y, Li Z, Su R, Luo D, Yang W, Miao Y, Cai R, Jiang L, Du X, Yang Y, Liu Q, Yang G, Zhao S, Huang W, Gong Q, Zhu R 2019 Sci. China-Phys. Mech. Astron. 62 7 Google Scholar
[18]	Kirmani A R, Durant B K, Grandidier J, Haegel N M, Kelzenberg M D, Lao Y M, McGehee M D, McMillon-Brown L, Ostrowski D P, Peshek T J, Rout B, Sellers I R, Steger M, Walker D, Wilt D M, VanSant K T, Luther J M 2022 Joule 6 1015 Google Scholar
[19]	Ziegler J F, Ziegler M D, Biersack J P 2010 Nucl. Instrum. Methods. Phys. Res. B 268 1818 Google Scholar
[20]	Xue B, Zhang L, Li Z, Jiang W, Liang Y, Liu N, Pan C, Chen L, Wang T 2022 Nucl. Instrum. Methods. Phys. Res. B 526 29 Google Scholar
[21]	Serge T G, Bernard Z, Bruno K, Boubacar S, Mahamadi S, Martial Z, Issa Z 2019 Int. J. Photoenergy 2019 8306492 Google Scholar
[22]	Ohshima T, Sato S, Imaizumi M, Nakamura T, Sugaya T, Matsubara K, Niki S 2013 Sol. Energy Mater Sol. Cells 108 263 Google Scholar
[23]	Jacobsson T J, Correa-Baena J P, Anaraki E H, Philippe B, Stranks S D, Bouduban M E F, Tress W, Schenk K, Teuscher J, Moser J E, Rensmo H, Hagfeldt A 2016 J. Am. Chem. Soc. 138 10331 Google Scholar
[24]	Yang J, Hong Q, Yuan Z, Xu R, Guo X, Xiong S, Liu X, Braun S, Li Y, Tang J, Duan C, Fahlman M, Bao Q 2018 Adv. Optical Mater. 12 1800262 Google Scholar
[25]	Chaudhary B, Kulkarni A, Jena A K, Ikegami M, Miyasaka T 2020 Energy Technol. 8 1900990 Google Scholar
[26]	Jena A K, Ikegami M, Miyasaka T 2017 ACS Energy Lett. 2 1760 Google Scholar
[27]	Kim S, Bae S, Lee S, Cho K, Lee K D, Kim H, Park S, Kwon G, Ahn S W, Lee H M, Kang Y, Lee H S, Kim D 2017 Sci. Rep. 7 1200 Google Scholar
[28]	Mejri A, Farah K, Eleuch H, Ouada H B 2008 Radiat. Meas. 43 1372 Google Scholar
[29]	Sheng J W, Kadono K, Yazawa T 2002 Appl. Radiat. Isot. 57 813 Google Scholar
[30]	Acha C, Sanca G A, Barella M, Alurralde M, Marlasca F G, Huhtinen H, Paturi P, Golmar F, Levy P 2021 Radiat. Phys. Chem. 183 109404 Google Scholar

Cited By

图 1 PSCs样品的结构示意图(a), 截面SEM图像(b)和实物图(c)

Figure 1. Sketch (a), cross-section SEM image (b) and photograph (c) of PSCs sample.

DownLoad: Full-Size Img PowerPoint

图 2 SRIM预测的注量为1×10¹⁴ p/cm²的0.1 MeV质子(黑色与红色实线)和注量为2.2×10¹⁵ p/cm²的2 MeV质子(黑色与红色虚线)在PSCs样品中产生的注入H原子浓度(a)和离位损伤与电子能量沉积分布(b)

Figure 2. SRIM-predicted depth profiles of implanted H atomic concentrations (a) and atomic displacement damage and electronic energy deposition (b) in PSCs irradiated with 0.1 MeV protons to 1×10¹⁴ p/cm² (black and red solid line) and 2 MeV protons to 2.2×10¹⁵ p/cm² (black and red dotted line).

DownLoad: Full-Size Img PowerPoint

图 3 质子辐照PSCs的PV参数随质子注量的变化　(a) 0.1 MeV; (b) 2 MeV

Figure 3. PV parameters versus proton fluence for PSCs irradiated with protons: (a) 0.1 MeV; (b) 2 MeV.

DownLoad: Full-Size Img PowerPoint

图 4 质子辐照前后钙钛矿薄膜的XRD谱　(a) 0.1 MeV; (b) 2 MeV

Figure 4. XRD patterns of perovskite thin films before and after proton irradiations: (a) 0.1 MeV; (b) 2 MeV.

DownLoad: Full-Size Img PowerPoint

图 5 2 MeV质子辐照前(a)和辐照后(b)钙钛矿薄膜的SEM图像(质子注量为2.2×10¹⁵ p/cm²)

Figure 5. SEM images of perovskite thin films before (a) and after (b) 2 MeV proton irradiation (Proton fluence is 2.2 × 10¹⁵ p/cm²).

DownLoad: Full-Size Img PowerPoint

图 6 质子辐照前后PSCs Au电极表面的SEM图像　(a) 辐照前; (b) 0.1 MeV质子辐照后; (c), (d) 2 MeV质子辐照后. (e) SnO₂/FTO/玻璃基底的透射谱

Figure 6. SEM images of the Au electrode surface of PSCs before and after proton irradiations: (a) Before irradiations; (b) after irradiations with 0.1 MeV proton; (c), (d) after irradiations with 2 MeV proton. (e) Transmittance spectra of SnO₂/FTO/glass substrates.

DownLoad: Full-Size Img PowerPoint

图 7 SRIM预测的2, 10和20 MeV质子在PSCs玻璃基底中产生的电子能量沉积分布(10和20 MeV质子的注量为1×10¹² p/cm², 2 MeV质子的注量为2.2×10¹⁵ p/cm²)

Figure 7. SRIM-predicted depth profiles of electronic energy deposition in the glass substrates of PSCs irradiated with 2, 10 and 20 MeV protons (10 and 20 MeV proton fluences are 1×10¹² p/cm², and 2 MeV proton fluence is 2.2×10¹⁵ p/cm²)

DownLoad: Full-Size Img PowerPoint

图 8 质子辐照PSCs的PV参数随质子注量的变化　(a) 10 MeV; (b) 20 MeV

Figure 8. PV parameters versus proton fluence for PSCs irradiated with protons: (a) 10 MeV; (b) 20 MeV.

DownLoad: Full-Size Img PowerPoint

图 9 质子辐照前后钙钛矿薄膜的XRD谱　(a) 10 MeV; (b) 20 MeV

Figure 9. XRD patterns of perovskite thin films before and after proton irradiations: (a) 10 MeV; (b) 20 MeV.

DownLoad: Full-Size Img PowerPoint

图 10 质子(注量均为1×10¹² p/cm²)辐照前后PSCs Au电极表面的SEM图像　(a) 辐照前; (b), (c) 分别为10和20 MeV质子辐照后. (d), (e) SnO₂/FTO/玻璃基底透射谱

Figure 10. SEM images of Au electrode surface of PSCs before and after irradiations with 10 and 20 MeV proton (Proton fluences are 1×10¹² p/cm²): (a) Before irradiations; (b), (c) after irradiations with 10 and 20 MeV proton, respectively; (d), (e) Transmittance spectra of SnO₂/FTO/glass substrates.

DownLoad: Full-Size Img PowerPoint

表 1 用于质子辐照实验的原生PSCs样品的PV参数

Table 1. PV parameters of as-prepared PSCs sample used for proton irradiation experiments.

质子能量/MeV	V_OC/V	J_SC/(mA·cm^–2)	FF	PCE/%
0.1	1.02 ± 0.04	18.40 ± 0.72	0.68 ± 0.03	12.75 ± 0.63
2.0	1.04 ± 0.04	18.88 ± 0.58	0.71 ± 0.03	14.08 ± 1.18
10.0	1.08 ± 0.02	18.10 ± 0.41	0.75 ± 0.02	14.66 ± 0.82
20.0	1.08 ± 0.02	18.37 ± 0.39	0.74 ± 0.02	14.58 ± 0.68

DownLoad: CSV

表 2 不同能量质子辐照实验的注量率和注量范围

Table 2. Flux and fluence for proton irradiations with different proton energies.

质子能量 /MeV	注量率 /(10⁸ p·cm^–2·s^–1)	注量范围 /(p·cm^–2)
0.1	5000	1×10¹²—1×10¹⁴
2.0	10⁴	1×10¹²—2.2×10¹⁵
10.0 和 20.0	1	3×10⁹—1×10¹²

DownLoad: CSV

[1]	Kojima A, Techima K, Shirai Y, Miyasaka T 2009 J. Am. Chem. Soc. 131 6050 Google Scholar
[2]	Jeon N J, Noh J H, Yang W S, Kim Y C, Ryu S, Seo J, Seok S I 2015 Nature 517 476 Google Scholar
[3]	Saliba M, Matsui T, Seo J Y, Domanski K, Correa-Baena J P, Nazeeruddin M K, Zakeeruddin S M, Tress W, Abate A, Hagfeldt Anders, Grätzel M 2016 Energy Environ. 9 1989 Google Scholar
[4]	Min H, Lee D Y, Kim J, Kim G, Lee K S, Kim J, Paik M J, Kim Y K, Kim K S, Kim M G, Shin T J, Seok S I 2021 Nature 598 444 Google Scholar
[5]	Kang S, Jeong J, Cho S, Yoon Y J, Park S, Lim S, Kim J Y, Ko H 2019 J. Mater. Chem. A 7 1107 Google Scholar
[6]	AZUR SPACE. http://www.azurspace.com/index.php/en/ [2022-09-14]
[7]	Kheraj V, Simond B J, Toshniwal A, Misra S, Peroncik P, Zhang C, Vardeny Z V, Scarpulla M A 2018 J. Lumin. 194 353 Google Scholar
[8]	Tu Y, Wu J, Xu G, Yang X, Cai R, Gong Q, Zhu R, Huang W 2021 Adv. Mater. 33 2006545 Google Scholar
[9]	Yang J, Bao Q, Shen L, Ding L 2020 Nano Energy 76 105019 Google Scholar
[10]	Miyazawa Y, Ikegami M, Chen H W, Ohshima T, Imaizumi M, Hirose K, Miyasaka T 2018 iScience 2 148 Google Scholar
[11]	Xiong G, Qin Z, Li B, Wang L, Zhang X, Zheng Z, Zhu H, Zhao S, Gao J, Li B, Yang J, Li X, Luo J, Han Z, Liu X, Zhao F 2021 J. Mater. Chem. C 9 2095 Google Scholar
[12]	Durant B K, Afshari H, Singh S, Rout B, Eperon G E, Sellers I R 2021 ACS Energy Lett. 6 2362 Google Scholar
[13]	Barbé J, Hughes D, Wei Z, Pockett A, Lee H K H, Heasman K C, Carnie M J, Watson T M, Tsoi W C 2019 Sol. Rrl. 3 1900219 Google Scholar
[14]	Brus V V, Lang F, Bundesmann J, Seidel S, Denker A, Rech B, Landi G, Neitzert H C, Rappich J, Nickel N H 2017 Adv. Electron. Mater. 3 1600438 Google Scholar
[15]	Boldyreva A G, Frolova L A, Zhidkov I S, Gutsev L G, Kurmaev E Z, Ramachandran B R, Petrov V G, Stevenson K J, Aldoshin S M, Troshin P A 2020 J. Phys. Chem. Lett. 11 2630 Google Scholar
[16]	Boldyreva A G, Akbulatov A F, Tsarev S A, Luchkin S Y, Zhidkov I S, Kurmaev E Z, Stevenson K J, Petrov V G, Troshin P A 2019 J. Phys. Chem. Lett. 10 813 Google Scholar
[17]	Tu Y, Xu G, Yang X, Zhang Y, Li Z, Su R, Luo D, Yang W, Miao Y, Cai R, Jiang L, Du X, Yang Y, Liu Q, Yang G, Zhao S, Huang W, Gong Q, Zhu R 2019 Sci. China-Phys. Mech. Astron. 62 7 Google Scholar
[18]	Kirmani A R, Durant B K, Grandidier J, Haegel N M, Kelzenberg M D, Lao Y M, McGehee M D, McMillon-Brown L, Ostrowski D P, Peshek T J, Rout B, Sellers I R, Steger M, Walker D, Wilt D M, VanSant K T, Luther J M 2022 Joule 6 1015 Google Scholar
[19]	Ziegler J F, Ziegler M D, Biersack J P 2010 Nucl. Instrum. Methods. Phys. Res. B 268 1818 Google Scholar
[20]	Xue B, Zhang L, Li Z, Jiang W, Liang Y, Liu N, Pan C, Chen L, Wang T 2022 Nucl. Instrum. Methods. Phys. Res. B 526 29 Google Scholar
[21]	Serge T G, Bernard Z, Bruno K, Boubacar S, Mahamadi S, Martial Z, Issa Z 2019 Int. J. Photoenergy 2019 8306492 Google Scholar
[22]	Ohshima T, Sato S, Imaizumi M, Nakamura T, Sugaya T, Matsubara K, Niki S 2013 Sol. Energy Mater Sol. Cells 108 263 Google Scholar
[23]	Jacobsson T J, Correa-Baena J P, Anaraki E H, Philippe B, Stranks S D, Bouduban M E F, Tress W, Schenk K, Teuscher J, Moser J E, Rensmo H, Hagfeldt A 2016 J. Am. Chem. Soc. 138 10331 Google Scholar
[24]	Yang J, Hong Q, Yuan Z, Xu R, Guo X, Xiong S, Liu X, Braun S, Li Y, Tang J, Duan C, Fahlman M, Bao Q 2018 Adv. Optical Mater. 12 1800262 Google Scholar
[25]	Chaudhary B, Kulkarni A, Jena A K, Ikegami M, Miyasaka T 2020 Energy Technol. 8 1900990 Google Scholar
[26]	Jena A K, Ikegami M, Miyasaka T 2017 ACS Energy Lett. 2 1760 Google Scholar
[27]	Kim S, Bae S, Lee S, Cho K, Lee K D, Kim H, Park S, Kwon G, Ahn S W, Lee H M, Kang Y, Lee H S, Kim D 2017 Sci. Rep. 7 1200 Google Scholar
[28]	Mejri A, Farah K, Eleuch H, Ouada H B 2008 Radiat. Meas. 43 1372 Google Scholar
[29]	Sheng J W, Kadono K, Yazawa T 2002 Appl. Radiat. Isot. 57 813 Google Scholar
[30]	Acha C, Sanca G A, Barella M, Alurralde M, Marlasca F G, Huhtinen H, Paturi P, Golmar F, Levy P 2021 Radiat. Phys. Chem. 183 109404 Google Scholar

[1]	Luo Pan, Li Xiang, Sun Xue-Yin, Tan Xiao-Hong, Luo Jun, Zhen Liang. Effect of electron irradiation on perovskite films and devices for novel space solar cells. Acta Physica Sinica, 2024, 73(3): 036102. doi: 10.7498/aps.73.20231568
[2]	Li Pei, Xu Jie, He Chao-Hui, Liu Jia-Xin. Experimental study on irradiation of perovskite solar cells. Acta Physica Sinica, 2023, 72(12): 126101. doi: 10.7498/aps.72.20230230
[3]	Fu Jing, Cai Yu-Long, Li Yu-Dong, Feng Jie, Wen Lin, Zhou Dong, Guo Qi. Single event transient effect of frontside and backside illumination image sensors under proton irradiation. Acta Physica Sinica, 2022, 71(5): 054206. doi: 10.7498/aps.71.20211838
[4]	Liu Ye, Guo Hong-Xia, Ju An-An, Zhang Feng-Qi, Pan Xiao-Yu, Zhang Hong, Gu Zhao-Qiao, Liu Yi-Tian, Feng Ya-Hui. Data inversion and erroneous annealing of floating gate cell under proton radiation. Acta Physica Sinica, 2022, 71(11): 118501. doi: 10.7498/aps.71.20212405
[5]	Li Zhe-Fu, Jia Yan-Yan, Liu Ren-Duo, Xu Yu-Hai, Wang Guang-Hong, Xia Xiao-Bin, Shen Wei-Zu. Effect of proton irradiation on microstructure evolution of permanent magnet. Acta Physica Sinica, 2018, 67(1): 016104. doi: 10.7498/aps.67.20172025
[6]	Li Zhe-Fu, Jia Yan-Yan, Liu Ren-Duo, Xu Yu-Hai, Wang Guang-Hong, Xia Xiao-Bin. Irradiation effect of Sm2Co17 type permanent magnets. Acta Physica Sinica, 2017, 66(22): 226101. doi: 10.7498/aps.66.226101
[7]	Zhang Ning, Zhang Xin, Yang Ai-Xiang, Ba De-Dong, Feng Zhan-Zu, Chen Yi-Feng, Shao Jian-Xiong, Chen Xi-Meng. Damage effects of proton beam irradiation on single layer graphene. Acta Physica Sinica, 2017, 66(2): 026103. doi: 10.7498/aps.66.026103
[8]	Zeng Jun-Zhe, Li Yu-Dong, Wen Lin, He Cheng-Fa, Guo Qi, Wang Bo, Maria, Wei Yin, Wang Hai-Jiao, Wu Da-You, Wang Fan, Zhou Hang. Effects of proton and neutron irradiation on dark signal of CCD. Acta Physica Sinica, 2015, 64(19): 194208. doi: 10.7498/aps.64.194208
[9]	Wen Lin, Li Yu-Dong, Guo Qi, Ren Di-Yuan, Wang Bo, Maria. Analysis of ionizing and department damage mechanism in proton-irradiation-induced scientific charge-coupled device. Acta Physica Sinica, 2015, 64(2): 024220. doi: 10.7498/aps.64.024220
[10]	Zeng Jun-Zhe, He Cheng-Fa, Li Yu-Dong, Guo Qi, Wen Lin, Wang Bo, Maria, Wang Hai-Jiao. Particle transport simulation and effect analysis of CCD irradiated by protons. Acta Physica Sinica, 2015, 64(11): 114214. doi: 10.7498/aps.64.114214
[11]	Yang Jian-Qun, Li Xing-Ji, Ma Guo-Liang, Liu Chao-Ming, Zou Meng-Nan. Effect of 170 keV proton irradiation on structure and electrical conductivity of multi-walled carbon nanotubes film. Acta Physica Sinica, 2015, 64(13): 136401. doi: 10.7498/aps.64.136401
[12]	Lü Ling, Zhang Jin-Cheng, Li Liang, Ma Xiao-Hua, Cao Yan-Rong, Hao Yue. Effects of 3 MeV proton irradiations on AlGaN/GaN high electron mobility transistors. Acta Physica Sinica, 2012, 61(5): 057202. doi: 10.7498/aps.61.057202
[13]	Wang Zu-Jun, Tang Ben-Qi, Xiao Zhi-Gang, Liu Min-Bo, Huang Shao-Yan, Zhang Yong. Experimental analysis of charge transfer efficiency degradation of charge coupled devices induced by proton irradiation. Acta Physica Sinica, 2010, 59(6): 4136-4142. doi: 10.7498/aps.59.4136
[14]	Jin Yu-Zhe, Hu Yi-Pei, Zeng Xiang-Hua, Yang Yi-Jun. Gamma radiation effect on GaN-based blue light-emitting diodes with multi-quantum well. Acta Physica Sinica, 2010, 59(2): 1258-1262. doi: 10.7498/aps.59.1258
[15]	Zhang Lin, Han Chao, Ma Yong-Ji, Zhang Yi-Men, Zhang Yu-Ming. Gamma-ray radiation effect on Ni/4H-SiC SBD. Acta Physica Sinica, 2009, 58(4): 2737-2741. doi: 10.7498/aps.58.2737
[16]	Zhao Hui-Jie, He Shi-Yu, Sun Yan-Zheng, Sun Qiang, Xiao Zhi-Bin, Lü Wei, Huang Cai-Yong, Xiao Jing-Dong, Wu Yi-Yong. Effect of 100 keV proton irradiation on photoemission of GaAs/Ge space solar cells. Acta Physica Sinica, 2009, 58(1): 404-410. doi: 10.7498/aps.58.404
[17]	Qiao Hui, Liao Yi, Hu Wei-Da, Deng Yi, Yuan Yong-Gang, Zhang Qin-Yao, Li Xiang-Yang, Gong Hai-Mei. Real-time study of γ irradiation on Hg1-xCdxTe focal plane photodiodes. Acta Physica Sinica, 2008, 57(11): 7088-7093. doi: 10.7498/aps.57.7088
[18]	Fan Xian-Hong, Chen Bo, Guan Qing-Feng. The influence of proton irradiation on the microstructure of pure Al films. Acta Physica Sinica, 2008, 57(3): 1829-1833. doi: 10.7498/aps.57.1829
[19]	Wei Qiang, Liu Hai, He Shi-Yu, Hao Xiao-Peng, Wei Long. Slow positron annihilation study of Al film reflector after proton irradiation. Acta Physica Sinica, 2006, 55(10): 5525-5530. doi: 10.7498/aps.55.5525
[20]	ZHANG TING-QING, LIU CHUAN-YANG, LIU JIA-LU, WANG JIAN-PING, HUANG ZHI, XU NA-JUN, HE BAO-PING, PENG HONG-LUN, YAO YU-JUAN. RADIATION EFFECTS OF MOS DEVICE AT LOW DOSE RATE AND LOW TEMPERATURE. Acta Physica Sinica, 2001, 50(12): 2434-2438. doi: 10.7498/aps.50.2434

Catalog

Vol. 72, Issue 13 - 2023-07-05

Metrics

Abstract views: 1913
PDF Downloads: 63
Cited By: 0

姓名
邮箱
手机号码
标题
留言内容
验证码

Search

Article

留言板

Proton irradiation induced damage effects in CH₃NH₃PbI₃-based perovskite solar cells

Abstract

Authors and contacts

Corresponding author: Zhang Li-Min, zhanglm@lzu.edu.cn

FullText HTML : translate this paragraph

References

Cited By

Catalog

Metrics

Authors

Referees

About Journal

About

Search

Article

留言板